The present invention relates to a carbon purification method and a carbon product produced using the same.
Purification of carbon nanotubes (CNTs) by reduction of catalyst content and removal of impurities is a necessary step for obtaining pure carbon nanotubes. However, purification of carbon nanotubes remains a challenge despite extensive research having been done in this area. Amongst the issues faced is the use of oxidants such as hydrogen peroxide (H2O2) and potassium permanganate (KMnO4) to increase catalyst removal efficiency. The addition of oxidants causes some reactions with the surface of the carbon nanotubes, generating functional groups and destroying the surface of the carbon nanotubes. Other shortcomings of known purification methods include the use of large quantities of acids and long reflux durations. In view of the foregoing, it would be desirable to provide a carbon purification method that can mitigate at least some of these shortcomings.
Accordingly, in a first aspect, the present invention provides a carbon purification method. The carbon purification method includes providing a carbon product having a catalyst content and/or impurities, performing a hydrothermal acid digestion operation on the carbon product in an acid to dissolve the catalyst content and/or the impurities, and performing a filtering operation to separate the dissolved catalyst content and/or the dissolved impurities from the carbon product.
In a second aspect, the present invention provides a carbon product produced in accordance with the carbon purification method of the first aspect, the catalyst content of the carbon product being less than 5 wt %.
Other aspects and advantages of the invention will become apparent from the following detailed description, taken in conjunction with the accompanying drawings, illustrating by way of example the principles of the invention.
Embodiments of the invention will now be described, by way of example only, with reference to the accompanying drawings, in which:
The detailed description set forth below in connection with the appended drawings is intended as a description of presently preferred embodiments of the invention, and is not intended to represent the only forms in which the present invention may be practiced. It is to be understood that the same or equivalent functions may be accomplished by different embodiments that are intended to be encompassed within the scope of the invention.
Referring now to
The carbon product may be a plurality of carbon nanotubes. The carbon nanotubes may be grown from natural rubber precursors or hydrocarbon precursors. The as-synthesized carbon nanotubes may contain a catalyst and/or other non-carbon content.
The catalyst content and/or the impurities that are removed from the carbon nanotubes using hydrothermal acid treatment may include one or more of metal catalysts and stable oxide supports. More particularly, the catalyst content may include one or more of a metal and a metal oxide. In one embodiment, the catalyst content may include one or more of iron (Fe), nickel (Ni), aluminium oxide (Al2O3) and nickel aluminium oxide (NiAl2O4).
At step 14, a hydrothermal acid digestion operation is performed on the carbon product in an acid to dissolve the catalyst content and/or the impurities. The hydrothermal reaction may be used to remove Al2O3 and NiAl2O4 supports.
The hydrothermal acid digestion operation may be performed in the acid at a temperature that is higher than a boiling point of the acid. In one embodiment, the temperature at which the hydrothermal acid digestion operation is performed may be between about 130 degrees Celsius (° C.) and about 160° C.
All common inorganic mineral acids such as, for example, nitric, sulphuric and hydrochloric acids, may be applied to effectively remove the catalysts from the carbon nanotubes under hydrothermal acid treatment. Different types of inorganic mineral acids may be used standalone without the addition of oxidants for the removal of non-carbon species and/or catalysts on carbon nanotubes via hydrothermal treatment. The hydrothermal acid digestion operation may be performed without addition of an oxidant. In one embodiment, nitric acid may be used effectively alone.
The hydrothermal acid digestion operation may be performed at a pressure of between about 270,000 pascal (Pa) and about 650,000 Pa.
The described hydrothermal technique may be used to efficiently remove all non-carbon species in a shorter time. More particularly, the hydrothermal acid digestion operation may be performed for a period of between about 2 hours (h) and about 12 h.
The hydrothermal acid digestion operation may be performed in an acid solution having a concentration of between about 1 mole per litre (mol/L) and about 5 mol/L. In one embodiment, 30 millilitres (mL) of 5 moles per litre (mol/L) of acid may be used for every 0.5 gram (g) of as-synthesized carbon nanotubes.
The reaction may be carried out in a pressurized vessel, which allows temperature to be above the boiling point of the acid. More particularly, the hydrothermal treatment may be performed in an acid digester which allows the reaction to be pressurized and uses temperature higher than the boiling point of the acid. The hydrothermal acid treatment may be directly applied to the purification process using the acid digester. This provides more energy to the acids for reaction and hence, uses lesser amounts of acids. This also enhances the reaction rate between the acid and a metal or metal oxide containing compound and hence a full removal of catalysts may be achieved with a lesser amount of acid.
A filtering operation is performed at step 16 to separate the dissolved catalyst content and/or the dissolved impurities from the carbon product. Water alone may be used to wash out the remaining residue and to neutralize the purified carbon nanotubes (CNTs).
Between about 95 mass percent (wt %) and about 99 wt % of the catalyst content may be removed with the carbon purification method 10. Accordingly, the catalyst content of the carbon product produced in accordance with the carbon purification method 10 may be less than 5 wt %. The purified carbon nanotubes may have a purity of greater than about 95 mass percent (wt %).
The improved purification technique for carbon nanotubes using hydrothermal acid treatment significantly decreases the amount of acid and time used as compared to the common refluxing method. In particular, this method may significantly decrease the treatment time by four (4) fold as compared to the common refluxing method. The concentration of acid used may be as low as 1 mole per litre (mol/L). The carbon nanotubes may be effectively purified at a temperature of 140 degrees Celsius (° C.) in 8 hours (h), regardless of the type of acid used. In one embodiment, raw carbon nanotubes may be effectively purified to a purity of greater than about 95 wt % with 5M nitric acid at 160° C. for 4 hours using hydrothermal acid techniques.
The carbon purification method 10 may be applied as a purification treatment for carbon nanotubes and may be applicable to any carbon products containing metal and metal oxide catalysts.
0.5 grams (g) of as-grown carbon nanotubes (CNTs) was added to 30 millilitres (mL) of 5 molar (M) acid in an acid digester and placed at 140 degrees Celsius (° C.) for various durations. The mixture was then cooled down and filtered using 0.22 micron (μm) pore size filter paper. It was then washed with deionised (DI) water until the filtrate is neutral in pH. The solid was then collected and dried overnight at 120° C. in an oven.
For comparison, the refluxing method was performed as follows: 0.5 g of as-grown carbon nanotubes (CNTs) was added to 100 mL of 5 M acid and refluxed at 120° C. with stirring for 24 hours. The mixture was then cooled down and filtered using 0.22 μm pore size filter paper. It was then washed with DI water until the filtrate is neutral in pH. The solid was then collected and dried overnight at 120° C.
Referring now to
The same conclusion can also be gathered from the TGA results shown in
Table 1 below shows the percentage amount of residue remaining as analysed by TGA for various samples of carbon nanotubes obtained from different purification methods under different conditions. The residue was measured using TGA after various acid treatments. The hydrothermal treatment was carried out in an acid digester.
From Table 1 above, it can be concluded that hydrothermal treatment with nitric acid at 140° C. for 6 hours will have similar results as compared to that of refluxing at 100° C. for 24 hours. This shows that the duration of the purification process may be reduced by four (4) fold to obtain similar results. The experiments also demonstrate that all three (3) acids tested can effectively remove catalyst when used in a hydrothermal treatment process at 140° C. for 8 hours.
Referring now to
As is evident from the foregoing discussion, the present invention provides a carbon purification method that requires a shorter treatment time and uses a lower concentration of acid. The carbon purification method of the present invention may be used to remove 99 mass percent (wt %) of the catalyst. The present invention provides an efficient purification method for assynthesized carbon nanotubes through hydrothermal acid digestion or hydrothermal acid treatment. The method may be used for full separation or a complete removal of catalysts from carbon nanotubes. The method may be used to purify carbon nanotubes grown from natural rubber precursors or other hydrocarbon precursors from the catalyst.
While preferred embodiments of the invention have been described, it will be clear that the invention is not limited to the described embodiments only. Numerous modifications, changes, variations, substitutions and equivalents will be apparent to those skilled in the art without departing from the scope of the invention as described in the claims. The carbon purification method of the present invention may be applied to separation of carbon nanotubes with catalyst and purification of high quality carbon nanotubes.
Further, unless the context clearly requires otherwise, throughout the description and the claims, the words “comprise”, “comprising” and the like are to be construed in an inclusive as opposed to an exclusive or exhaustive sense; that is to say, in the sense of “including, but not limited to”.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10201803053W | Apr 2018 | SG | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/SG2019/050162 | 3/25/2019 | WO | 00 |