Claims
- 1. A process for activating a reducing catalyst comprising the sequential steps:
- (a) reducing said catalyst by heating the catalyst in the presence of hydrogen at a temperature sufficient to partially activate the catalyst;
- (b) contacting said partially active catalyst in the presence of hydrogen with a reactant feed which undergoes an exothermic reaction in the presence of said partially activated catalyst at conditions whereby said reaction occurs, said conditions including temperatures at least greater than the temperatures at which the catalyst is partially activated; and
- (c) continuing said contacting for a time sufficient to convert said partially activated catalyst to a high activity catalyst.
- 2. The process of claim 1 wherein the heating in step (a) is in the range from about 210.degree. to less than about 235.degree. C.
- 3. The process of claim 1 wherein said reducing catalyst is comprised of nickel.
- 4. The process of claim 1 wherein said reducing catalyst is comprised of nickel and silica.
- 5. The process of claim 1 wherein said reducing catalyst is comprised of nickel and silica and capable of having a reduced nickel surface area ranging from 55 to about 100 m.sup.2 /g and a B.E.T. total surface area ranging from 150 to about 300 m.sup.2 /g.
- 6. The process of claim 5 wherein said catalyst additionally includes copper.
- 7. The process of claim 1 wherein said reactant feed comprises an unsaturated hydrocarbon or oxygenated derivative thereof.
- 8. The process of claim 7 wherein said unsaturated hydrocarbon is a C.sub.6 to C.sub.20 aromatic hydrocarbon.
- 9. The process of claim 7 wherein said unsaturated hydrocarbon is a C.sub.2 to C.sub.20 olefinic hydrocarbon.
- 10. A process for activating a reducing catalyst comprised of nickel and silica and capable of having a reduced nickel surface area ranging from about 55 to about 100 m.sup.2 /g and a total surface area ranging from about 150 to about 300 m.sup.2 /g, comprising the steps:
- (a) reducing the catalyst by heating the catalyst in increments in the presence of hydrogen at a temperature sufficient to partially activate the catalyst;
- (b) contacting said partially active catalyst in the presence of hydrogen with a reactant feed which undergoes an exothermic reaction in the presence of said partially activated catalyst at conditions whereby said reaction occurs, said conditions including a temperature ranging from about 235.degree. to about 275.degree. C.; and
- (c) continuing said contacting for a time sufficient to convert said partially activated catalyst to a high activity catalyst.
- 11. The process of claim 10 wherein said heating in step (a) is conducted until a temperature in the range from about 210.degree. to less than about 235.degree. C. is attained.
- 12. The process of claim 10 wherein said catalyst additionally includes copper.
- 13. The process of claim 10 wherein said reactant feed comprises an unsaturated hydrocarbon or oxygenated derivative thereof.
- 14. The process of claim 13 wherein said unsaturated hydrocarbon is a C.sub.6 to C.sub.20 aromatic hydrocarbon.
- 15. The process of claim 13 wherein said unsaturated hydrocarbon is C.sub.2 to C.sub.20 olefinic hydrocarbon.
- 16. A process for activating a massive nickel reducing catalyst, said catalyst comprising copper, nickel and silica, and said catalyst being characterized as capable of having a reduced nickel surface area ranging from 55 to about 100 m.sup.2 /g and a B.E.T. total surface area ranging from 150 to about 300 m.sup.2 /g, comprising the steps:
- (a) reducing said catalyst by heating the catalyst in increments in the presence of hydrogen until said catalyst attains temperatures ranging from about 210.degree. to less than about 235.degree. C. and maintaining said temperatures for a time sufficient to yield a partially activated catalyst;
- (b) contacting said partially active catalyst in the presence of hydrogen with a reactant feed which undergoes an exothermic reaction in the presence of said partially activated catalyst at conditions whereby said reaction occurs, said conditions including temperatures ranging from about 235.degree. C. to about 275.degree. C., whereby the temperatures at the catalyst surface exceeds the temperature of the catalyst bed; and
- (c) continuing said contacting for a time sufficient to convert said partially activated catalyst to a high activity catalyst.
- 17. The process of claim 16 wherein said catalyst is prepared by contacting a porous support with a solution of nickel, copper and silicate ions at conditions whereby said ions are coprecipitated onto said support to yield a composite comprising nickel, copper and silica precursors supported on said porous support.
- 18. The process of claim 17 wherein said porous support is a particulate support.
- 19. The process of claim 18 wherein said support is selected from the group consisting of silica and kieselguhr.
- 20. The process of claim 18 wherein said feed comprises an unsaturated hydrocarbon or oxygenated derivative thereof.
- 21. The process of claim 20 wherein said unsaturated hydrocarbon is a C.sub.6 to C.sub.20 aromatic hydrocarbon.
- 22. The process of claim 20 wherein said unsaturated hydrocarbon is C.sub.2 to C.sub.20 olefinic hydrocarbon.
- 23. The process of claim 18 wherein said (a) is continued at temperatures ranging from about 210.degree. C. to less than about 235.degree. C. for a time sufficient to yield a catalyst having an activity ranging from 10 to 75% of the fully activated catalyst.
- 24. The process of claim 23 wherein step (b) is carried out at conditions sufficient to yield a catalyst with an activity of greater than 75% of the fully activated catalyst.
CROSS REFERENCE TO RELATED APPLICATIONS
This application is a continuation-in-part of U.S. application Ser. No. 654,693, filed Feb. 2, 1976 and now abandoned.
US Referenced Citations (5)
Foreign Referenced Citations (1)
Number |
Date |
Country |
1,158,418 |
Jul 1969 |
UK |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
654693 |
Feb 1976 |
|