Claims
- 1. A catalyst comprising:
- (a) a support having initially a surface area ranging from about 350 to about 500 m.sup.2 /g, a total pore volume of about 1.0 to about 2.5 cc/g, not more than about 0.2 cc/g of said pore volume being in pores having a diameter of more than about 400 Angstroms, said support comprising agglomerates of alumina and silica, said silica comprising less than about 10 weight percent of said support, said agglomerates having been prepared in an agglomeration zone, under agglomeration conditions, including maintaining the heat introduced into said agglomeration zone in the range of about 10,000 to about 25,000 British thermal units per hour per pound of said alumina, and
- (b) a hydrogenation component selected from the group consisting of elemental metal, metal oxide, metal sulfide of a Group VIB metal and an elemental metal, metal oxide and metal sulfide of a Group VII metal and mixtures thereof of the Periodic Table of Elements.
- 2. The catalyst of claim 1, wherein said heat introduced into said agglomeration zone ranges from about 10,000 to about 20,000 British thermal units per hour per pound of said alumina.
- 3. The catalyst of claim 1 wherein said hydrogenation component is present in said agglomeration zone during the preparation of said agglomerates and wherein said heat introduced into said agglomeration zone ranges from about 20,000 to about 25,000 British thermal units per hour per pound of said alumina.
- 4. The catalyst of claim 1 wherein said pores having diameters above about 400 Angstroms comprise from about 0.05 to about 0.20 cc/g of the pore volume of said catalyst.
- 5. The catalyst of claim 1 wherein said silica comprises from about 1 to about 6 weight percent of said support.
- 6. The catalyst of claim 1 wherein said silica comprises from about 1 to about 4 weight percent of said support.
- 7. The catalyst of claim 1 wherein said catalyst comprises from about 1 to about 6 weight percent of at least one of said Group VIII metals and from about 5 to about 25 weight percent of said Group VIB metals, calculated as the oxides thereof, based on the total catalyst.
- 8. The catalyst of claim 1 wherein said hydrogenation component is selected from the group consisting of nickel, nickel oxide, nickel sulfide, molybdenum, molybdenum oxide, molybdenum sulfide, tungsten, tungsten oxide, tungsten sulfide, cobalt, cobalt oxide, cobalt sulfide, and mixtures thereof.
- 9. The catalyst of claim 1 wherein said catalyst has a surface area ranging from about 250 to about 450 m.sup.2 /g, a pore volume ranging from about 0.9 to about 2.0 cc/g and not more than about 0.2 cc/g of said pore volume being in pores having a diameter of more than about 400 Angstroms.
CROSS REFERENCE TO RELATED APPLICATIONS
This application is a continuation-in-part of U.S. patent application Ser. No. 066,572 filed Aug. 15, 1979 and now abandoned, the teachings of which are hereby incorporated by reference.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
4159969 |
Mone et al. |
Jul 1979 |
|
4175118 |
Wassermann et al. |
Nov 1979 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
66572 |
Aug 1979 |
|