Patent Application
20210229993
Embodiments of the disclosure relate to catalyst carrier compositions for use in reforming processes. In particular, certain embodiments of the disclosure relate to catalyst carrier compositions for and methods of steam reforming.
Steam reforming of natural gas is a method of producing commercial bulk hydrogen. Methane and steam are used to produce carbon monoxide and hydrogen (synthesis gas or syngas). In addition, more hydrogen is produced through the water-gas shift reaction. Equation 1 shows the general chemical equation for steam reforming and Equation 2 shows the general chemical equation for the water-gas shift reaction.
CH4+H2O CO+3H2 Eq. 1
CO+H2O CO2+H2 Eq. 2
One challenge in steam reforming is the high thermodynamic potential for coke formation on catalysts. Other challenges include high energy consumption and CO2 emissions. Nickel catalysts with aluminum oxide and magnesium oxide as supports are used in steam reforming. Catalyst support type and catalytic additives affect the coking tendency of catalysts during steam reforming.
Present catalyst technology is insufficient in some processes to provide cost-effective and durable means for steam reforming.
Applicant has recognized a need for catalyst carrier compositions comprising red mud to be applied in systems and processes for steam reforming. Red mud catalyst carrier compositions for use in steam reforming are disclosed. The red mud catalyst carrier compositions in some embodiments contain Fe, Al, Si, Na, Ca, and Ti oxides from red mud, and the compositions act as a base support for catalytically active compositions, for example added metals and metal oxides. A factor in designing suitable reforming catalysts is the catalyst support or base material (carrier), which can have an active catalytic role in a catalytic reaction or be merely inert. In embodiments of the present disclosure, red mud acts as a catalyst carrier. Disclosed compositions are useful as a catalyst carrier in steam reforming processes for the conversion of methane to syngas, according to Equation 1 in addition to or alternative to Equation 2. Utilization of red mud in steam reforming processes provides the concurrent advantages of utilizing a waste material (red mud) and producing useful H2.
Red mud is a caustic waste material produced from bauxite ore processing for alumina extraction, and is utilized here as a catalyst carrier for a steam reforming process. Surprisingly and unexpectedly, without being specifically designed as a catalyst or carrier (for example using specific zeolitic structure), red mud waste material can be readily used as a catalyst carrier. Red mud generally includes a mixture of transition metals such as Ti, Fe, and Al, which make it an advantageous catalyst in addition to or alternative to catalyst carrier for steam reforming processes, for example once modified with nickel in addition to or alternative to other metals, such as transition metals and their oxides.
Embodiments disclosed here apply red mud as a catalyst support or base material, while offering some catalytic activity itself for steam reforming of methane. Optionally, the support material can be used in the water-gas shift reaction to produce additional H2 (Equation 2). Red mud compositions of the present disclosure can be used as an active catalyst support, promoter, in addition to or alternative to catalyst in either or both of Equations 1 and 2.
Therefore, disclosed here is a method for steam reforming with a red mud catalyst support composition, the method including providing a methane feed and a steam feed to react over the red mud catalyst support composition at increased temperature and increased pressure to produce synthesis gas comprising H2 and CO, the composition comprising: red mud material produced from an alumina extraction process from bauxite ore. In some embodiments, the composition further comprises at least one added catalytic metal, the added catalytic metal not being present in an unmodified form of the red mud material produced from the alumina extraction process from bauxite ore. Still in other embodiments, the at least one added catalytic metal is a Periodic Table Group 3-12 metal. In certain embodiments, the increased temperature is between about 500° C. to about 1000° C. In other embodiments, the increased temperature is between about 600° C. to about 800° C. In yet other embodiments, the increased temperature is between about 700° C. to about 750° C.
In other embodiments of the method, the increased pressure is between about 5 bar and about 20 bar. Still in certain other embodiments, the increased pressure is between about 7 bar and about 15 bar. In some embodiments, the increased pressure is about 14 bar. In some embodiments, the gas hourly space velocity of the methane feed and steam feed is between about 1000 to 10000 In some embodiments, the composition includes at least one component selected from the group consisting of: Fe2O3, Al2O3, SiO2, Na2O, CaO, and TiO2. Still in other embodiments, a majority of the particles of the composition have a particle size of less than about 70 μm. Some embodiments of the method include the step of carrying out a water-gas shift reaction on the syngas produced in the producing step. Still in other embodiments, the step of carrying out the water-gas shift reaction applies the red mud catalyst support composition as a catalyst support. In certain other embodiments, a molar ratio of the steam feed to the methane feed is between about 2:1 and about 4:1. In yet other embodiments, produced H2 is at least about 1.5 mol. % of produced products from the reaction for at least about 5 hours.
In some embodiments, the composition includes between about 20 wt. % and about 30 wt. % Al2O3, between about 5 wt. % and about 10 wt. % CaO, between about 15 wt. % and about 25 wt. % Fe2O3, between about 5 wt. % and about 15 wt. % Na2O, between about 15 wt. % and about 25 wt. % SiO2, and between about 5 wt. % and about 10 wt. % TiO2.
These and other features, aspects, and advantages of the present disclosure will become better understood with regard to the following descriptions, claims, and accompanying drawing. It is to be noted, however, that the drawing illustrates only several embodiments of the disclosure and is therefore not to be considered limiting of the disclosure's scope as it can admit to other equally effective embodiments.
So that the manner in which the features and advantages of the embodiments of compositions of red mud along with systems and methods for steam reforming with such compositions, may be understood in more detail, a more particular description of the embodiments of the present disclosure briefly summarized previously may be had by reference to the embodiments thereof, which are illustrated in the appended drawing, which form a part of this specification. It is to be noted, however, that the drawing illustrates only various embodiments of the disclosure and are therefore not to be considered limiting of the present disclosure's scope, as it may include other effective embodiments as well.
As noted, red mud is a caustic waste material generated during alumina extraction from bauxite ore. Red mud includes a mixture of transition metals, for example as listed in Table 1.
In one embodiment, a Saudi Arabian red mud sample was evaluated for steam reforming activities at 750° C. and 14 bar, as shown in
Saudi Arabian red mud from Ma'aden Aluminium Company, based at Ras Al Khair, Saudi Arabia was used in the test runs. Table 2 shows the weight percent for certain components in the Saudi Arabian red mud composition.
The red mud was tested as-is without further treatment, for example acid or base treatment, for use as a catalyst support with a Brunauer-Emmett-Teller (BET) surface area of about 16 m2/g.
Several tests on red mud support catalytic activity and MgO support catalytic activity for steam reforming were experimentally conducted. Saudi Arabian red mud was tested as received as a catalyst support without any modifications, and it was placed in a Micromeritics® PID Eng & Tech brand microactivity reactor designed for catalyst activity and selectivity analysis, and similar tests were performed for the MgO catalyst support. The results are compared, for example, in
Hydrogen production illustrated in
The singular forms “a,” “an,” and “the” include plural referents, unless the context clearly dictates otherwise. The term “about” when used with respect to a value or range refers to values including plus and minus 5% of the given value or range.
In the drawings and specification, there have been disclosed example embodiments of the present disclosure, and although specific terms are employed, the terms are used in a descriptive sense only and not for purposes of limitation. The embodiments of the present disclosure have been described in considerable detail with specific reference to these illustrated embodiments. It will be apparent, however, that various modifications and changes can be made within the spirit and scope of the disclosure as described in the foregoing specification, and such modifications and changes are to be considered equivalents and part of this disclosure.