Patent Grant
11794178
The ring-expansion metathesis polymerization of cycloalkenes has received significant attention. This polymerization is documented, for example in Bielawski et al., Science 2002, 297, 2041-44. Recently, Veige et al. U.S. Patent Application Publication No. 2014/0309389 discloses tridentate pincer ligand supported metal complex of a group 5-7 transition metals that initiate polymerization of alkynes in high yield to macrocyclic polyalkynes. Metal complexes that polymerize alkenes to yield cyclic polyalkenes are desirable. Cyclic norbornene-based macromonomers were polymerized via REMP using cyclic ruthenium catalysts, as described by Boydston et al., J. Am. Chem. Soc. 2008, 130, 12775-82. However, control over both tacticity and the cis/trans ratio is either not reported or is absent. Hence, effective catalysts for the preparation of polymers by stereo-controlled ring-expansion metathesis polymerization are desirable.
An embodiment of the invention is directed toward a tetraanionic pincer ligand metal-oxo-alkylidene complex of the structure:
where: Z is independently O or S; R comprises, independently, H, methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl t-butyl, or larger alkyl; R′ is methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, t-butyl, C5-C22 alkyl, phenyl, naphthyl, or C13-C22 aryl; X is O, N, S, P, or Se; R″, independently, is methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, t-butyl, C5-C22, phenyl, naphthyl, C13-C22 aryl, or two R″ is a C4-C6 alkylene combined with a single X as a heterocycle; n is 1 to 3; and M is a group 5-7 transition metal. A representative tetraanionic pincer ligand metal-oxo-alkylidene complex has the structure:
The tetraanionic pincer ligand metal-oxo-alkylidene complex can be prepared from the reaction of a trianionic OCO pincer ligand supported metal-alkylidyne complex with carbon dioxide or carbon disulfide.
In embodiments of the invention, the tetraanionic OCO pincer ligand metal-oxo-alkylidene complex, a trianionic OCO pincer ligand metal complex, or a trianionic ONO pincer ligand metal complex can be combined with a plurality of cyclic alkene monomers to yield a plurality of cyclic poly(alkene).
In an embodiment of the invention the trianionic OCO pincer ligand metal complex has the structure:
In another embodiment of the invention, the trianionic ONO pincer ligand metal complex has the structure:
Cyclic monomers that can be employed are unsubstituted or substituted cyclopropene, cyclobutene, cyclopentene, cycloheptene, and cyclooctene, norbomene, dicyclopentadiene, norbomene anhydride, diester from norbornene anhydride, imide from norbornene anhydride, oxanorbornene, oxanorbornene anhydride, ester of oxanorbornene anhydride, and imide of oxanorbornene anhydride, or any combination thereof, wherein the ester is from a C1-C10 alkyl or aryl alcohol, the imides is from C1-C10 alkyl or aryl amine; wherein substituents can be C1-C10 alkyl, aryl, C1-C10 alkoxy, aryloxy, C1-C10 carboxylic acid ester, or carboxylic acid amide, optionally substituted one or two times with C1-C10 alkyl or aryl.
Polymerization by ring expansion metathesis polymerization can result in stereorandom or stereoregular cyclic polymers. A stereoregular cyclic polynorbornene can be formed with repeating units having greater than 95% cis content and greater than 95 percent syndiotactic content.
An embodiment of the invention is directed to tetraanionic pincer ligand metal-oxo-alkylidene complexes of the structure:
where: Z is independently O or S; R is, independently, H, methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl t-butyl, or larger alkyl, or any other substituent that does not inhibit formation of the tetraanionic pincer ligand supported metal-alkylidyne complex; R′ is methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, t-butyl, C5-C22 alkyl, phenyl, naphthyl, or C13-C22 aryl; X, independently, can be O, N, S, P, or Se; R″, independently, is methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, t-butyl, C5-C22, phenyl, naphthyl, C13-C22 aryl, or two R″ is a C4-C6 alkylene combined with a single X as a heterocycle; n is 1 to 3 depending on X; and M is a group 5-7 transition metal.
The OCO pincer ligand contains three anionic donor atoms that complex the metal ion. The tetraanionic pincer ligand metal-oxo-alkylidene complex is generated by the addition of carbon dioxide, carbon disulfide, or, effectively, cabonoxidesulfide to a trianionic pincer ligand supported metal-alkylidyne complex where the trianionic pincer ligand results from a precursor with the structure:
where R groups at carbons 3, 4, 5, 6, 4′, 5′, 6′, 3″, 4″, 5″ and 6″ of the 1,1′:3′,1″ terphenyl assembly can be H, or substituted, with an alkyl group, such as methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, t-butyl, or larger alkyl group, for example C5-C20, or any other substituents that do not compete for the formation of an M≡C bond of a synthetic precursor trianionic pincer ligand supported metal-alkylidyne complex. For example, a substituent that can form a chelate toward the metal, alone or in combination with one of the OH groups of the OCO pincer ligand can be included. Among the other substituents on the OCO pincer ligand, R may be groups that permit the attachment of the OCO pincer ligand, a precursor trianionic pincer ligand supported metal-alkylidyne complex prepared therefrom, or a trianionic pincer ligand metal-oxo-alkylidene complex prepared therefrom to a polymer or resin, for example a carboxylic acid, carboxylic ester, amine, thiol, epoxy, haloalkyl, hydroxy, or other reactive group in the 4, 5, 5′, 4″, or 5″ positions. Large R groups at carbons 6, 4′, 6′, and 6″ of the OCO pincer ligand precursor can oblige the aromatic rings to be out of plane to a significant degree and inhibit the formation of the desired precursor trianionic pincer ligand supported metal-alkylidyne complex, and, generally, are not appropriate for preparation of the trianionic pincer ligand supported metal-oxo-alkylidene complexes, according to embodiments of the invention.
In an exemplary embodiment of the invention, as shown in Scheme 1, below, a tetraanionic OCO pincer ligand tungsten-oxo-alkylidene complex 2 and a dinuclear species 3 are synthesized from a trianionic pincer ligand supported tungsten-alkylidyne complex 1 upon reaction with carbon dioxide in a 9:2 ratio.
Complex 2 crystallizes preferentially in C6D6, resulting in single crystals amenable to X-ray diffraction. The tungsten ion in complex 2, as shown in
Complex 3 results from complex 2 by the loss of CO and tetrahydrofuran (THF). Upon extensive heating of the reaction mixture, complete conversion of 2 to 3 is possible. Slow evaporation of a concentrated solution of 3 in a pentane/Et2O mixture yields single crystals suitable for X-ray diffraction, as shown in
In an embodiment of the invention, complex 2 is employed as catalyst for ring-expansion metathesis polymerization of cycloalkenes. In an embodiment of the invention, complex 3 is employed as catalyst for ring-expansion metathesis polymerization of cycloalkenes to generate a cyclic polyalkene. In other embodiments of the invention, a trianionic pincer-supported metal alkylidyne, where the metal is a group 5-7 transition metal, is employed as a catalyst in a method for ring-expansion metathesis polymerization of cycloalkenes. The trianionic pincer ligand precursor has the structure:
where R groups at carbons 3, 4, 5, 6, 4′, 5′, 6′, 3″, 4″, 5″ and 6″ of the 1,1′:3′,1″ terphenyl assembly can be H, or substituted, with an alkyl group, such as methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, t-butyl, or larger alkyl group, for example C5-C20, or any other substituents that do not compete for the formation of an M≡C bond of a synthetic precursor trianionic pincer ligand supported metal-alkylidyne complex. The trianionic pincer ligand can be an OCO3− pincer ligand, as in 1, or, in an embodiment of the invention, an ONO3− pincer ligand. The ONO3− pincer ligand can be of the structure derived from the protonated precursor:
R groups and R′ groups where X is C are independently H, C1-C30 alkyl, C2-C30 alkenyl, C2-C30 alkynyl, C6-C14 aryl, C7-C30 arylalkyl, C8-C30, C3-C30 polyether, C3-C30 polyetherester, C3-C30 polyester, or arylalkenyl, C8-C30 arylalkynyl, C1-C30 alkoxy, C6-C14 aryloxy, C7-C30 arylalkyloxy, C2-C30 alkenyloxy, C2-C30 alkynyloxy, C8-C30 arylalkenyloxy, C8-C30 arylalkynyloxy, C2-C3 alkylester, C5-C15 arylester, C8-C30 alkylarylester, C3-C30 alkenylester, C3-C30 alkynylesterperfluorinated, partially fluorinated, and/or otherwise substituted variations thereof.
According to an embodiment of the invention, cyclic poly(cycloalkene)s can be homopolymers or copolymers of a plurality of cyclic alkene monomers where the catalyst functions as the initiator of the polymerization. Cyclic polymers can be prepared from a wide variety of cycloalkene monomers, including, but not limited to, monocyclic alkenes, such as, but not limited to cyclopropene, cyclobutene, cyclopentene, cycloheptene, and cyclooctene, and substituted variations thereof, bicycloalkenes, such as, but not limited to, norbornene, dicyclopentadiene, norbornene anhydride, esters from norbornene anhydride, imides from norbornene anhydride, oxanorbornene, oxanorbornene anhydride, esters of oxanorbornene anhydride, and imides of oxanorbornene anhydride. The imides can be imides from alkyl or aryl amines, which can be substituted or unsubstituted. Substituents can be C1-C10 alkyl, aryl, alkoxy, carboxylic acid ester, carboxylic acid amide, where the amide is optionally substituted one or two times with an alkyl or aryl. Cyclic polymers can be prepared that are copolymers of two or more monomers. The molecular weight of the cyclic polymers can be small, equivalent to oligomers of three to ten repeating units, or the molecular weights can be of any size up to tens and hundreds of thousands in molecular weight. The cyclic poly(cycloalkene)s can be used as prepared or converted into cyclic poly(cycloalkane)s upon reduction of the double bonds of the cyclic poly(cycloalkene)s polymer. The cyclic poly(cycloalkene)s can be converted to substituted cyclic poly(cycloalkane)s by addition reaction at the alkene groups of the cyclic poly(cycloalkene)s, for example the addition of halogens, alcohols, amines, or any other olefin addition reactions. The macrocyclic polymers can find many applications, such as part of motor oil additives or other lubricants.
Depending on the catalyst employed, the stereochemistry of polymerization varies. For example, the cyclic polymer can be atactic in monomer placement with approximately 61% cis content with catalyst 4 but in excess of 99% cis content and more than 95% syndiotactic when complex 1 or complex 2 is employed as the catalytic initiator, according to embodiments of the invention.
In an exemplary polymerization, as shown in
A mixture of 2 and 3 maintains the selectivity of 2 when treated with norbornene, suggesting initiation with catalyst 2 and propagation of the monomer are much faster than initiation by the more hindered complex 3. Evidence for fast propagation relative to initiation comes from a sealed NMR tube polymerization experiment. Combining norbornene and 2 in C6D6 results in polymer formation but the 1H NMR spectrum of the reaction mixture exhibits signals attributable to unreacted catalyst 2. Cyclic polynorbornene produced with catalyst 2 is syndiotactic (>98%), as determined by a comparison to 13C NMR data of previously reported syndiotactic linear polynorbornene.
[a]The appropriate amount of a 1 mg/mL solution of catalyst dissolved in toluene is added to 40 mg of norbornene dissolved in toluene and stirred for 7 h at room temperature.
[b]mol · L−1.
[c]Determined by 1H NMR spectroscopy.
[d]Determined by size exclusion chromatography.
Size exclusion chromatography (SEC) equipped with multi-angle light scattering (MALS) and viscosity detectors provide compelling data for a cyclic topology for polynorbornene from complex 2. Cyclic polymers have lower intrinsic viscosities and smaller hydrodynamic volumes than their linear analogs. Catalyst that produce linear polynorbornene with high cis selectivity (>95%) and syndiotacticity (>95%) are known, and a sample was synthesized utilizing Grubbs catalyst Ru(NHC(Ad)(Mes)(═CH(PhOiPr))(η2-NO3) (6).
[a]Absolute molecular weights determined by SEC-MALS.
[b]Determined by 1H NMR spectroscopy.
[c]Determined by 13C NMR spectroscopy.
A plot of log of molar mass versus elution volume is shown in
Tethering an alkylidene to a substitutionally inert ancillary ligand is an effective design for creating catalysts capable of REMP, as with catalyst 2, according to an embodiment of the invention. Unique to this system, CO2 cleavage across the metal-carbon triple bond of complex 1 leads to the tethered alkylidene catalyst 2. Complex 2 is the first group VI alkylidene complex to function as a REMP catalyst. This catalyst produces cyclic polynorbornene with extremely high stereocontrol.
In another embodiment of the invention, complex 4 reacts slowly with norbornene to give non-stereoselective cyclic polynorbornene, as indicated in
[a]The appropriate amount of a 1 mg/mL solution of catalyst dissolved in toluene is added to 30 mg of norbornene dissolved in toluene and stirred for 30 min at room temperature.
[b]mol · L−1.
[c]Determined by 1H NMR
[d]Determined by gel permeation chromatography (GPC) using THF as the mobile phase at 35° C.
[e]Determined gravimetrically.
Linear polynorbornene, as indicated in Table 4, below, with a similarly high cis selectivity (95%) and syndiotacticity (>95%) was synthesized using the known ruthenium Grubbs catalyst 6, as shown in
[a]Determined by gel permeation chromatography (GPC) using THF as the mobile phase at 35° C.
[b]Determined by 1H NMR.
[c]Confirmed by 1H-1H COSY NMR.
A Mark-Houwink-Sakurada (MHS) plot (log [η] versus log M, where [η] is the intrinsic viscosity and M is the viscosity-average molecular weight, is shown in
calculated over the range is within reasonable error limits of the theoretical value of 0.5, as indicated in
Differential Scanning Calorimetry (DSC) analyses of cyclic poly(NBE) synthesized by 1 (B) and linear poly(NBE) synthesized by 6 (A) were performed and the results indicate nearly identical glass transition temperatures (Tg) for the cyclic and linear poly(NBE). The similar thermal properties are the result of the relatively high molecular weights (>100,000 g/mol) of these polymers, which minimizes the potential end group effects.
In summary, OCO3− pincer ligands as in 1, or an ONO3− pincer ligand as with 4 can produce cyclic polymers by REMP, but with vastly different degrees of stereo-control. Table 5 below summarizes these differences.
1 (cyclic)
4(cyclic)
[a]Determined by gel permeation chromatography (GPC) using THF as the mobile phase at 35° C.
[b]Determined by 1H NMR.
[c]Confirmed by 1H-1H COSY NMR.
Unless otherwise specified, all manipulations were performed under an inert atmosphere using glove-box techniques. C6D6(Cambridge Isotopes) was dried over sodium-benzophenone ketyl, distilled or vacuum transferred and stored over 4 Å molecular sieves. Norbornene was refluxed over sodium, distilled and stored under argon. The tungsten-alkylidyne [OCO]W(═CtBu)(THF)2 1 was prepared according to Veige et al. US Patent Application Publication No. 2014/0309389. The tungsten complexes [CF3—ONO]W≡CtBu(THF)2 4 and [CF3—ONO]W═CHtBu(OtBu) 5 were prepared according to Patent Application Publication No. 2014/0073800 and the monomer chiral dicarbomenthoxynorbornadiene (DCMNBD) was prepared according to Gonsales et al., Journal of the American Chemical Society 2016, 138, 4996-99. Linear cis-syndiotactic-polynorbornene (cis-poly(NBE)) was synthesized using the commercially available Grubbs catalyst purchased from Sigma-Aldrich (CAS 1352916-84-7) and used as received. Bromination of poly(NBE) was carried out according to the method of Hyvl et al., Macromolecules 2015, 48, 3148-52. 1H and 13C NMR spectra were obtained on Varian INOVA spectrometer (500 MHz), or a Mercury spectrometer (400 MHz and 300 MHz for proton). Chemical shifts, reported in δ (ppm), were referenced on the solvent, on the TMS scale for 1H and 13C. Elemental analyses were performed at Complete Analysis Laboratory Inc., Parsippany, New Jersey Size-exclusion chromatography was performed in THF at 35° C. and a flow rate of 1.0 mL/min (Agilent isocratic pump, degasser, and autosampler; columns: three PLgel 5 μm MIXED-D mixed bed columns, molecular weight range 200-400,000 g/mol). Detection consisted of a Wyatt Optilab rEX refractive index detector operating at 658 nm, a Wyatt miniDAWN Treos light scattering detector operating at 656 nm, and a Wyatt ViscoStar-II viscometer. Absolute molecular weights and molecular weight distributions were calculated using the Wyatt ASTRA software. Electrospray ionization mass spectrometry (ESI-MS) spectra were collected by direct injection into an Agilent 6120 TOF spectrometer at a gas temperature of 350° C. with fragmentation voltage of 120 V. The sample was prepared in an argon glovebox and transported in Hamilton gastight syringes. Gas chromatography electron ionization mass spectrometry (GC/EI-MS) to identify CO was performed using a Restek Corp. Rxi-5MS column (30 m×0.25 mm i.d. and 0.25 μm df). A Finnigan Trace GC Ultra chromatograph was employed using split injection mode, with a split flow rate of 30 mL/min and a GC carrier gas flow of 1 mL/min, vacuum compensated. Temperature at the injection port was of 250° C., MS transfer line was at 225° C., and a temperature program of 35° C. Isothermal was utilized. A ThermoFinnigan (San Jose, CA) Finnigan Trace DSQ mass spectrometer was used with electron ionization (EI) of 70 eV, and ion source temperature of 250° C.
Acetylene dicarboxylic acid (1.00 g, 8.77 mmol), (−)-menthol (3.43 g, 21.9 mmol, 2.50 equiv), p-toluenesulfonic acid (0.167 mg, 0.877 mmol, 0.100 equiv), and toluene (25 mL) were charged in a round-bottomed flask equipped with a Dean-Stark apparatus. The solution was heated under reflux for 18 h. The solution was cooled to rt, washed with water (20 mL×2) and brine (20 mL), dried (Na2SO4), filtered, and concentrated, and the crude material was purified by column chromatography (hexanes:EtOAc 40:1, Rf=0.2) to give the product dimenthyl acetylenedicarboxylate A as a white solid (1.72 g, 4.40 mmol, 50%), as indicated in
Freshly prepared cyclopentadiene (0.42 mL, 5.1 mmol, 2.0 equiv) was added to a stirred solution of A (1.00 g, 2.56 mmol) in DCM (4 mL) at rt. After 14 h the solution was concentrated, and the crude material was purified by column chromatography (hexanes:EtOAc 20:1, Rf=0.3) and recrystallization (MeOH) to give BMCNBD as a white solid (935 mg, 2.04 mmol, 80%).
A J-Young NMR tube was charged with tungsten alkylidyne [OCO]W≡CC(CH3)3(THF)2 (1) (0.050 g, 0.065 mmol) in C6D6. After performing a freeze-pump-thaw procedure to evacuate the headspace of the tube, 1 atm of CO2 was admitted into it. Heating up the reaction up to 55° C. for 12 h generates the tungsten oxo alkylidene 2, along with complex 3 in a 9:2 ratio, respectively, and as indicated in the proton NMR spectrum shown in
To a 20 mL glass vial charged with norbornene (0.038 g, 4.1×10−4 mol, 100 equiv.) in 1 mL of toluene were added 3 mL of a 1 mg/mL solution of 2 in toluene (3 mg, 4.1×10−6 mol, 1 equiv.). The reaction was allowed to stir for 7 h at room temperature. After this period the reaction vessel was brought outside the glovebox and the reaction mixture was added dropwise to stirring methanol. Polynorbornene precipitates out and is isolated by filtration, and dried overnight under vacuum. Yield (0.035 g, 92%). 1H and 13C NMR spectral assignments were consistent with literature reports.
Tacticity of the polynorbornene is consistent with the results of the post-functionalization of polynorbornene via bromination, as recently described by Schrock and coworkers. The brominated polymer exhibits two doublets at 3.84 ppm (J=11.2 Hz) and 3.81 ppm (J=10.3 Hz). Consistent with reported cis, syndiotactic polynorbornene, irradiating the methine protons at 2.61 ppm results in two singlets. Further evidence for high syndiotacticity comes from polymerization of the chiral monomer, bis((menthyloxy)carbonyl)norbornadiene (BMCNBD). COSY NMR is able to distinguish between isotactic and syndiotactic poly(BMCNBD). In the case of a cis isotactic sample, the olefinic protons are inequivalent, and therefore couple in a COSY NMR spectrum. However, a cis syndiotactic poly(BMCNBD) contains equivalent olefinic protons related by a C2 axis, and thus do not couple. Poly(BMCNBD) produced by 2 does not exhibit any coupling between the olefinic protons, indicating the polymer is syndiotactic.
To a 20 mL glass vial charged with norbornene (0.019 g, 2.0×10−4 mol, 100 equiv.) in 1 mL of toluene was added 3 (2.6 mg, 2.0×10−4 mol, 1 equiv.) in 1 mL of toluene. The reaction was allowed to stir for 7 h at room temperature. After this period the reaction vessel was brought outside the glovebox and the reaction mixture was added dropwise to stirring methanol. Polynorbonene precipitates out and is isolated by filtration, and dried overnight under vacuum. Yield (0.008 g, 42%). A mixture of cis and tram polynorbornene was obtained. Tacticity was not determined.
A solution of norbornene (0.580 g, 6.16×10−3 mol, 1000 equiv.) in 30 mL of THF was added to a 100 mL round bottom flask containing a stirring bar. This solution was cooled to −40° C. and 50 μl, of a stock solution (0.039 g in 0.5 mL of THF) of complex 6 (6.15×106 mol, 1 equiv.) were added to it. The reaction was allowed to stir for 1 h at −40° C. After this period 0.1 mL of ethyl vinyl ether was used to quench the reaction, which was then added dropwise to stirring methanol. Polynorbornene precipitates out and is isolated by filtration, and dried under vacuum. Yield (0.221 g, 38%). 1H and 13C NMR spectral assignments were consistent with literature reports.
In a nitrogen filled glovebox, norbornene (32 mg, 3.4×10−4 mol, 12 equiv) was dissolved in 1 ml of C6D6 and transferred to a scaled NMR tube. In another vial 4 (26 mg, 2.8×10−5 mol, 1.0 equiv) was dissolved in 1 mL of C6D6 and is added to the NMR tube. After 5 h the mixture was dissolved in a small amount of toluene (3 mL) and was added dropwise to stirring methanol. The mixture was allowed to stir for 30 min. Polynorbonene precipitates as a white solid and was isolated by filtration, and dried overnight under vacuum. (28 mg, 88%). 1H and 13C NMR spectral assignments were consistent with literature reports.
In a nitrogen filled glovebox, a 20 mL glass vial was charged with norbornene (30.0 mg, 3.19×10−4 mol, 400 equiv) and dissolved in 5.76 mL of toluene. To the first solution a 1.0 mg/L solution of 1 (0.61 mL, 7.94×10−7 mol, 1.0 equiv) was added. The reaction was stirred for 30 min at room temperature. After this period the reaction vessel was brought outside the glovebox and the reaction mixture was added dropwise to stirring methanol. The mixture was allowed to stir for 30 minutes. Polynorbornene precipitated as a white solid and was isolated by filtration and dried overnight under vacuum. Yield (29 mg, 97%). 1H and 13C NMR spectral assignments were consistent with literature reports. Other polymerization results are tabulated in Table 5, below.
[a]The appropriate amount of a 1 mg/mL solution of catalyst dissolved in toluene is added to 30 mg of norbornene dissolved in toluene and stirred for 30 min at room temperature.
[b]mol · L−1.
[c]Determined by 1H NMR
[d]Determined by gel permeation chromatography (GPC) using THF as the mobile phase at 35° C.
[e]Determined gravimetrically.
In a nitrogen filled glovebox, norbornene (35 mg, 3.7×10 mol, 15 equiv) was dissolved in 1 ml of C6D6 and transferred to a sealable NMR tube. In another vial, 5 (21 mg, 2.5×10−5 mol, 1.0 equiv.) was dissolved in 1 mL of C6D6 and was added to the NMR tube. After 5 h the mixture was dissolved in a small amount of toluene (3 mL) and added dropwise to a stirring methanol solution. The polymer was then recovered by filtration (30 mg, 86%). 1H and 13C NMR spectral assignments were consistent with literature reports.
All patent applications, and publications referred to or cited herein are incorporated by reference in their entirety, including all figures and tables, to the extent they are not inconsistent with the explicit teachings of this specification.
It should be understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application.
This application is a U.S. Divisional patent application of Ser. No. 16/806,054, filed Mar. 2, 2020, now issued as U.S. Pat. No. 11,241,681 which in turn is a U.S. Divisional patent application of Ser. No. 15/760,730, filed Mar. 16, 2018, now issued as U.S. Pat. No. 10,639,620, which in turn is a U.S. national stage application of International patent application No. PCT/US2016/052437, filed Sep. 19, 2016, which claims the benefit of U.S. Provisional Application Ser. No. 62/220,569, filed Sep. 18, 2015, the disclosures of which is are hereby incorporated by reference in their entireties, including all figures, tables and drawings.
This invention was made with government support under CHE-1265993 awarded by the National Science Foundation. The government has certain rights in the invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 10639620 | Veige | May 2020 | B2 |
| 10730972 | Veige | Aug 2020 | B2 |
| 11241681 | Veige | Feb 2022 | B2 |
| 20140073800 | Veige et al. | Mar 2014 | A1 |
| 20140309389 | Veige et al. | Oct 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 2004013198 | Feb 2004 | WO |
| 2013085707 | Jun 2013 | WO |
| Entry |
|---|
| Vestenamer 8012 (Evonik Industries); product bulletin, 2017. (Year: 2017). |
| Bailey, B. C. et al., “Snapshots of an Alkylidyne for Nitride Triple-Bond Metathesis,” J. Am. Chem. Soc., 2007, 129, No. 8, pp. 2234-2235. |
| Bielawski, C. W. et al., “An “Endless” Route to Cyclic Polymers,” Science, Sep. 20, 2002, vol. 297, No. 5589, pp. 2041-2044. |
| Bielawski, C. W. et al., “Synthesis of Cyclic Polybutadiene via Ring-Opening Metathesis Polymerization: The Importantance of Removing Trace Linear Contaminants,” J. Am. Chem. Soc., 2003, vol. 125, No. 28, pp. 8424-8425. |
| Boydston, A. J. et al., “Cyclic Ruthenium-Alkylidene Catalysts for Ring-Expansion Metathesis Polymerization,” J. Am. Chem. Soc., Sep. 24, 2008, vol. 130, No. 38, pp. 12775-12782. |
| Ciszewski, J. T. et al., “Synthesis and structure of an imido-tethered Schrock carbene of molybdenum,” Dalton Transactions, 2003, pp. 4226-4227. |
| Floros et al., Ring opening metathesis polymerization of norborene and derivatives by the triply bonded di tungsten complex Na[W2( μ-Cl)3Cl4(THF)2](THF)3, Polymers, 4 (4):1657-1673 (2012). |
| Geyer, A. M. et al., “Catalytic Nitrile-Alkyne Cross-Metathesis,” J. Am. Chem. Soc., 2007, vol. 129, pp. 3800-3801. |
| Gonsales et al., Fast “wittig-like” react ions as a consequence of the inorganic enamine effect, Journal of the American Chemical Society, 137(14):4840-4845 (2015). |
| Gonsales, S. A. et al., “Highly Tactic Cyclic Polynorbommene: Stereoselective Ring Expansion Metathesis Polymerization of Norbornene Catalyzed by a New Tethered Tungsten-Alkylidene Catalyst,” J. Am. Chem. Soc., 2016, 138, 4996-99. |
| Hyvl et al., “Proof of Tacticity of Stereoregular ROMP Polymers through Post Polymerization Modification,” 5 Macromolecules,, 2015, vol. 48, pp. 3148-3152. |
| International Application No. PCT/US2016/052437, International Preliminary Report on Patentability, dated Mar. 29, 2018. |
| International Application No. PCT/US2016/052437, International Search Report and Written Opinion, dated Jan. 3, 2017. |
| Jan, M. T. et al., “Synthesis and characterization of a trianionic pincer supported Mo-alkylidene anion and alkyne insertion into a Mo(IV)-C.sub.pincer bond to form metallocyclopropene (n.sup.2-vinyl) complexes,” J. Organomet. Chem., 2011, vol. 696, pp. 4079-4089. |
| Katz, T. J. et al., “Polymerization of Acetylenes and Cyclic Olefins Induced by Metal Carbynes,” J. Am. Chem. Soc., 1984, vol. 106, pp. 2659-2668. |
| Kuppuswamy, S. et al., “Synthesis and Characterization of Tungsten(VI) Alkylidene Complexes Supported by an [OCO].sub.3 Trianionic Pincer Ligand: Progress towards the [.sup.tBuOCO]W.ident.CC(CH.sub.3).sub.3 Fragment,” Organometallics, 2010, vol. 29, pp. 4227-4233. |
| Lokare, K. S. et al., Synthesis, Properties, and Structure of Tethered Molybdenum Alkylidenes, Organometallics, 2008, vol. 27, No. 19, pp. 5130-5138. |
| Meng et al., Vinyl and ring-opening metathesis polymerization of norbornene with novel half-sandwich iridium (III) complexes bearing hydroxyindanimine ligands, Chemical Communications, 27:3178-3180 (2008). |
| Mortreaux, A. et al. “Reactions of W(CCMe.sub.3) (OCMe.sub.3).sub.3 with terminal alkynes: metathesis and polymerization,” Journal of Molecular Catalysis A: Chemical, 1995, vol. 96, pp. 95-105. |
| Nadif, S. S. et al., Introducing “ynene” metathesis: ring-expansion metathesis polymerization (REMP) leads to highly cis and syndiotactic cyclic polymers or norbornene, J. Am. Chem. Soc., 2016, vol. 138, pp. 6408-6411. |
| Sarkar, et al., An OC03-trianionic pincer tungsten (VI) alkylidyne: rational design of a highly active alkyne polymerization catalyst, Journal of the American Chemical Society, 134(10):4509-4512 (2012). |
| Sarkar, S. et al., “Additional of Mild Electrophiles to a Mo.ident.N Triple Bond and Nitrile Systhesis via Metal-Mediated N-Atom Transfer to Acid Chlorides,” J. Am. Chem. Soc., 2008, vol. 130, pp. 16128-16129. |
| Sarkar, S. et al., “Synthesis, Characterization, and Reactivity of a d.sup.2, Mo(IV) Complex Supported by a New OCO-Trianionic Pincer Ligand,” J. Am. Chem. Soc., 2008, vol. 130, pp. 1116-1117. |
| Number | Date | Country | |
|---|---|---|---|
| 20220258146 A1 | Aug 2022 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62220569 | Sep 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16806054 | Mar 2020 | US |
| Child | 17577510 | US | |
| Parent | 15760730 | US | |
| Child | 16806054 | US |