Patent Application
20140128653
The following specification particularly describes the invention and the manner in which it is to be performed:
The present application claims the benefit of Indian application No. 3443/DEL/2012 filed Nov. 7, 2012, the entire disclosure of which is hereby incorporated by reference.
The present invention related to catalyst for the selective dehydrogenation/oxidative dehydrogenation of ethane to ethylene. Particularly the present invention relates to a catalyst for the vapor phase dehydrogenation/oxidative dehydrogenation of ethane to ethylene under atmospheric pressure. More particularly, the present invention relates to a process future to produce ethylene from ethane with high conversion and selectivity in one single step. The present invention relates to an improved process for the preparation of Mo supported nanocrystalline TiO2; the catalyst can effectively produce ethylene without any deactivation in a longer run.
Ethylene is a very important chemical, which does not occur in nature but still represents the organic chemicals consumed in the greater quantity worldwide. It is mainly the raw material for a large no of industrial products, such as poly-ethylene, polyvinyl chloride, polystyrene, polyester etc. Despite of the economic uncertainty around the petrochemical industry, ethylene production and consumption scenario are expected to grow continuously. The global demand of ethylene is over 140 million tons per year with the future growth rate of 3.5% per year (www.technip.com/sites/default/files/technip/publications/attachments/-Ethylene_production—1.pdf). Industrially, ethylene is produced by steam cracking of ethane; reactors have to plug into a firebox as the cracking of ethane is endothermic in nature. In standard condition a steam cracker can achieve up to 60% of ethane conversion with maximum 80% ethylene selectivity. However, oxidative dehydrogenation (ODH) is one of the alternative processes mainly known. Since, oxidative dehydrogenation is exothermic so the reaction goes automatically as the catalyst is light off. While, ODH can offers high conversion with high ethylene selectivity, minimizing the contact time in milliseconds.
In this context, oxidative dehydrogenation (ODH) will have the clear future to replace steam cracker to produce ethylene. Although many researcher has reported oxidative dehydrogenation of ethane in resent past, but poor atom efficiency (called E-factor by R A Sheldon in Chemistry & Industry, 6 Jan. 1997, P 13) in respect to both conversion and selectivity restrict the successful commercialization of ODH process. Moreover, the use of pure oxygen in ODH process makes the process cost high; hence to deploy ODH reactor industry must put a costly gas separation tower first. In this context catalytic dehydrogenation is another possibility to replace the existing processes of ethylene production, as it can deliver ≧80% ethane conversion with ≧90% ethylene conversion. Uses of solid nanocrystalline metal oxides catalyst are very important as they offer larger active surface area with option to reuse.
There are many reports on the dehydration as well as oxidative dehydrogenation (ODH) of ethane over different solid catalyst, but to the best of our knowledge there is no reference available that can offer such atom efficiency for a prolonged reaction time.
Reference can be made to European patent EP 2165997 A1, 2010 wherein Han et al. provided a novel one step catalytic process of oxidative dehydrogenation of ethane for the production of ethylene and carbon dioxide using pure oxygen over Fe-manganese oxide or Fe—CaCO3 catalyst. But use of pure oxygen at a temperature≧600° C. is very much painful, because above 600° C., thermal cracking will come into effect. So use of pure oxygen at above 600° C. makes the process cost higher and unfavourable for commercialization.
Reference can be made to U.S. Pat. No. 4,250,346, 1981 by Young et al. In their patent application, they claimed gas phase oxidative dehydrogenation of ethane in presence or absence of H2O2 over mix-Molybdenum oxide catalyst (Moa Xb Yc) (where X=Cr, Mn, Nb, Ta, Ti, V, W and Y=Bi, Ce, Co, Cu, Fe, Mg, K, Ni, P etc.) at ≦500° C. The drawbacks of this process are the low conversion of butane (only 2 to 8% of ethane conversion was claimed) although the process operates at 1-30 atmosphere pressure. Again, the use of H2O rise the question of metal leaching from the solid catalyst, leads to rapid deactivation of catalyst.
Reference can be made to the article AIChE journal, 1997, 43, 1545-1550 in which Choudhary et al. studied non-catalytic thermal cracking of ethane in presence of oxygen in a space velocity of 2000-11000 h−1. But, the conversion of ethane is only 44.2% whereas in absence of oxygen is further decreases to 28.5%. Moreover, the selectivity of ethylene goes down as the side reaction product (such as CH4, C3H6, C3H8 etc.) are predominates at 800° C.
Reference can be made to the U.S. Pat. No. 4,524,236 by McCain et al. in which they developed one step low temperature oxidative dehydrogenation of ethane to produce ethylene over mixed oxide catalyst with 1: 1.2 oxygen to ethane as feed. The main drawback of the process is the low space velocity, loss of selectivity (about 11% selectivity decreased as the conversion goes up from 53% to 76%). The low space velocity makes the industrial difficult, as the industry need process which can give steady conversion and selectivity in a high space velocity in order to cut down the production cost.
Reference can be made to the J. Catal., 2010, 270, 67-75 wherein Lemoniou et al. reported low temperature oxidative dehydrogenation of ethane to ethylene over Ni—Me—O (where Me is the doped metal) as catalyst. Under the reported process 46% ethylene yield at 400° C. has been achieved with Ni—Nb—O catalyst.
Reference may also be made to Chem. Comm., 2003, 18, 2294-2295, in which partial oxidation of ethane was carried out via bromination followed by reaction with mix metal oxide. A product selectivity of ≧80% was achieved over Co2O4:ZrO2 catalyst. But main drawback is the use of bromine and double stage reactor setup to achieve such high product selectivity.
Another reference can be made to Ind. Eng. Chem. Res., 2011, 50, 8438-8442, by Leclerc et al. on the ODH of ethane over platinum catalyst. Wherein, silica supported platinum catalyst demonstrate the highest conversion of 76% with ethylene yield of 46% at 900° C. with C2H6/O2 ratio of 1.5.
Main object of the present invention is to provide a catalyst for the selective dehydrogenation/oxidative dehydrogenation of ethane to ethylene.
Another object of the present invention is to provide an improved process for the preparation of catalyst for the selective dehydrogenation/oxidative dehydrogenation of ethane to ethylene.
Yet another object of the present invention is to provide a process for the vapor phase dehydrogenation/oxidative dehydrogenation of ethane to ethylene under atmospheric pressure.
Yet another object of the present invention is to provide a process future to produce ethylene from ethane with high conversion and selectivity in one single step.
Yet another object of the present invention is to provide an efficient Mo supported nanocrystalline TiO2; the catalyst can effectively produce ethylene without any deactivation in a longer run.
Accordingly, present invention provides Mo—TiO2 nanocrystalline oxide catalyst wherein Mo is in the range of 5 to 15 wt % and TiO2 in the range of 85 to 95 wt % having particle size in the range of 80-150 nm.
In an embodiment of the present invention, Mo—TiO2 nanocrystalline oxide catalyst as claimed in claim 1, wherein said catalyst is useful for production of ethylene from ethane by vapor phase dehydrogenation/oxidative dehydrogenation in absence and presence of oxygen.
In an embodiment, present invention provides a process for the preparation of Mo—TiO2 nanocrystalline oxide catalyst as used in claim 1 and the said process comprising the steps of:
In another embodiment, present invention provides a process for the production of ethylene from ethane by vapor phase dehydrogenation/oxidative dehydrogenation in absence and presence of oxygen using Mo—TiO2 nanocrystalline oxide catalyst and the said process comprising the steps of:
In yet another embodiment of the present invention, reaction temperature is preferably in the range 650 to 800° C.
In yet another embodiment of the present invention, gas hourly space velocity (GHSV) is preferably in the range of 10000 to 50000 ml g−1 h−1.
In yet another embodiment of the present invention, the reaction time used is preferably in the range 3 to 20 h.
In yet another embodiment of the present invention, the conversion percentage of ethane is in the range of 65 to 96 mol %.
In yet another embodiment of the present invention, the selectivity of the ethylene obtained in the range of 88 to 100 mol %.
Present invention provides a catalyst consisting of Mo—TiO2 prepared hydrothermally and process to produce ethylene from ethane by gas phase dehydrogenation/oxidative dehydrogenation with and without O2 over Mo—TiO2 catalyst at atmospheric pressure, at a temperature range of 550 to 850° C. with a gas hourly space velocity (GHSV) in the range of 5000-70000 ml g−1 h−1 in the presence of Mo supported TiO2 catalyst with Mo to TiO2 weight ratio varied between 0.03 to 0.2 to obtain desired product ethylene for a period of 1-20 hours.
The present invention provides a process for the production of ethylene from ethane by vapor phase dehydrogenation/oxidative dehydrogenation in absence and presence of oxygen and Mo—TiO2 nanocrystalline oxide as the catalyst which involves the following steps:
The detailed steps of the process are:
The dehydrogenation of ethane was carried out in a fixed-bed down flow reactor at atmospheric pressure. Typically 200 mg of catalyst was placed in between two quartz wool plugged in the centre of the 6 mm quartz reactor and dehydrogenation of ethane was carried out in a temperature range of 650-800° C. The catalyst was reduced using 5% H2 balance He at 650° C. for 1 h before the reaction. The gas hourly space velocity (GHSV) was varied between 5000 ml g−1 h−1 to 50000 ml g−1 h−1 with a molar ratio of C2H6:O2:He of 1:1:8. The reaction products were analyzed using an online gas chromatography (Agilent 7890A) fitted with a FID & TCD detector using Al2O3/KCl column (to analyse C2H6, C2H4, CH4 etc.) and PoraPack-Q (for analyzing O2 and CO2).
An improved process for the preparation of Mo—TiO2 catalyst, wherein the said process comprising the steps of:
A process for gas phase dehydrogenation/oxidative dehydrogenation with and without O2 of ethane to produce ethylene using catalyst comprising the steps of:
Weight ratio of Mo to TiO2 of the catalyst varied in the range of 0.05 to 0.15.
Reactor pressure is preferably in the range of 1 atmosphere. Reaction temperature is preferably in the range 650 to 800° C. Gas hourly space velocity (GHSV) is preferably in the range of 1000 g ml−1 h−1 to 50000 g ml−1 h−1. Reaction time used is preferably in the range 3-20 h. Conversion (mol %) of ethane is in the range of 65 to 96%. Selectivity (mol %) of the ethylene obtained in the range of 78 to 100%.
The following examples are given by way of illustration and therefore should not be construed to limit the scope of the invention.
5 ml titanium isopropoxide was taken in 75 ml chilled ethanol to form a heterogeneous solution. Approximately 0.2 g octadecyldimethyl (3-trimethoxy silylpropyl) ammonium chloride was added drop wise under vigorous stirring. Then, the pH of the mixed solution was adjusted by 1(M) NaOH solution and pH of the mixed solution was fixed at 10. Finally, the mixed solution was heated at 80° C. and maintained for 2 h. The resultant mixture was autoclaved at 180° C. for 24 h for further crystallization. The white precipitate (TiO2) was collected by filtration, washed thoroughly with distilled water and ethanol and dried at 80° C. for 12 h. To remove the template the as-synthesized material was heated to 750° C. with a temperature ramp of 1.5° C./min under static air and kept at the same temperature for 4 h. This was used as a TiO2 support material.
Synthesis of Mo—TiO2 catalyst using ethanol (25 ml) medium taking the solution composition of 1.05 g of MoCl3, 0.5 g of cetyltrimethylammonium bromide, 0.2 g hydrazine (the molar ratio of Mo:CTAB:Hydrazine=1:1:0.01) and prepared 1.0 g of TiO2 was added to it such a way that the weight ratio of Mo to TiO2 was 0.05. The mixture was stirred for 3 h and the solid material was filtered out with 2 litre distilled water and it was dried in the oven at 110° C. for 16 h. Finally the calcination of the material was carried out at 750° C. for 6 h in air.
The X-ray diffraction pattern, Scanning Electron Microscope (SEM) images and Transmission Electron Microscope (TEM) images of this material are given below.
This example describes the dehydrogenation of ethane by gas phase reaction in He using Mo—TiO2 nanocrystalline oxide as the catalyst. (Table-1)
The dehydrogenation of ethane to ethylene was carried out in a fixed-bed down flow quartz reactor at atmospheric pressure. Typically 200 mg of catalyst was placed in between two quartz wool plugged in the center of the 6 mm quartz reactor and dehydrogenation of ethane was carried out in a temperature range of 650-800° C. The gas hourly space velocity (GHSV) was varied between 10000 ml g−1 h−1 to 30000 ml g−1 h−1 with a molar ratio of C2H6:He of 1:9.
Process Conditions
Mo: TiO2 wt % in the catalyst=5%
Pressure: 1 atmosphere
Total flow=33.3 ml/min (GHSV=10000)
Reaction time: 1 h
The example describes the effect of temperature on yield and selectivity ethylene. The product analysis presented in Table-2.
Process Conditions:
Mo: TiO2 wt % in the catalyst=5%
Pressure: 1 atmosphere
Total flow=33.3 ml/min (GHSV=10000)
Reaction time: 1 h
The example describes the effect of time on stream on yield and selectivity of ethylene. The product analysis presented in Table 3
Process Conditions:
Catalyst: 0.2 g, Mo: TiO2 wt % in the catalyst=5%
Pressure: 1 atmosphere
Total flow=33.3 ml/min (GHSV=10000)
Reaction temperature: 750° C.
The example describes the effect of gas hourly space velocity (GHSV) on yield and selectivity of ethylene. The product analysis presented in Table-3.
Process Conditions:
Mo: TiO2 wt % in the catalyst=5%
Pressure: 1 atmosphere
Reaction temperature: 750° C.
Reaction time: 1 h
The main advantages of the present invention are: