Catalyst for steam cracking reactions and related preparation process

Abstract

Catalyst for steam cracking reactions consisting of pure mayenite having the general formula:

Description

[0001] The present invention relates to a catalyst for steam cracking reactions and the related preparation process.

[0002] The most widely-used method for the production of light olefins, in particular ethylene and propylene, is the steam cracking process, in which a hydrocarbon charge is heated, in the presence of water vapor, in specific ovens to produce a gaseous stream rich in olefins. Steam cracking is a thermal process which is carried out on an industrial scale without catalysts. The setting up of a catalytic system which allows an increase in the yields to the desired products would provide important advantages; owing to the large volumes of products in question (for example the world-wide production of ethylene is over 70 Mton/year), even small percentage increases in the yield would have a great impact on process economy.

[0003] The use of catalysts for steam cracking reactions has not been widely studied, even if various companies and research groups have occasionally worked in this area since the 70s'. In some cases a process has been defined but industrial applications are not known at the moment.

[0004] Among the most significant references are the following, which identify calcium-aluminate compounds in which the 12CaO.7Al2O3 (mayenite) phase prevails, as the most active materials for the catalysis of naphtha cracking:

[0005] A. A. Lemonidou, I. A. Vasalos, Applied Catalysis, 54 (1989), 119-138;

[0006] A. A. Lemonidou, I. A. Vasalos, Proc. 1987 AIChE Spring National Meeting, Houston, Mar. 29-Apr. 2, 1987;

[0007] K. Kikuchi, T. Tomita, T. Sakamoto, T. Ishida, Chemical & Engineering Progress, 81 (1985) 6, 54.

[0008] B. Basu, D. Kunzru, Industrial & Engineering Chemistry Res., 1992, 31, 146-155.

[0009] Another reference has also demonstrated the good performance of materials consisting of Ca-aluminate mixtures:

[0010] S. Nowak, G. Zimmermann, H. Gushel, K. Anders, in “Catalysis in Petroleum Refining 1989” (D. L. Trimm et al. Eds.), Elsevier Science Publishers B. V., 1990.

[0011] As far as studies relating to industrial development are concerned, mention can be made of Asahi Chemical which claims a process, almost ready for commercialization, for steam cracking in a circulating bed, using a catalyst based on ZSM-5 and ZSM-11 zeolites, charged with metals such as Fe, Mg and/or Ib metals. This process partially increases the yield to ethylene, but the reaction is mainly directed towards the production of propylene and aromatics. Recent information (PERP Report 96/97S12-Chem Systems, September 1997) reveals that the process still has several problems of a technological nature to be solved, among which many aspects relating to the catalyst (activity, regeneration, duration), before it can be actually commercialized. More or less the same situation also applies to the Russian process of Vniios (Research Institute for organic syntheses) which uses potassium vanadate supported on corindone/mullite as catalyst, with the addition of promoters. Exxon has patented a process using an inert solid as heat transporter or catalysts based on mixed oxides of Mg, Ca, Mn, Be, Sr, Ce, V, Cs (W. Serrand et al., WO 97/31083). This process however is preferably designed for heavy charges (e.g.>500° C.) and comprises, in fact, a particular type of horizontal moving bed reactor with two rotating screws which help the movement of the charge.

[0012] A technology which seems closer to a possible industrial application is the Pyrocat process, set up by Veba Oel and Linde (M. Wyrosteck, M. Rupp, D. Kaufmann, H. Zimmermann, Proc. 15th World Petroleum Congress, Beijing, Oct. 12-16, 1997). This technology comprises implementation of steam cracking plants without modifying the design of the ovens. The idea is based on coating the inside of the cracking tubes with a solid layer having a catalytic effect and which inhibits the formation of coke, thus prolonging the times between subsequent stoppages for decoking operations. The catalyst is based on Al2O3/CaO and contains, as gasification promoter, compounds of alkaline metals. The technology however can only be applied to conventional cracking plants, operating with conventional charges.

[0013] It can therefore be seen from literature that catalysts based on calcium aluminates can be used in steam cracking reactions for the production of ethylene and propylene. The calcium aluminates which can be formed are the following, in increasing order of calcium content: CaO.6Al2O3, CaO.2Al2O3, 3CaO.5Al2O3, CaO.Al2O3, 5CaO.3Al2O3, 12CaO.7Al2O3, 2CaO.Al2O3 and 3CaO.Al2O3 but it is not disclosed in literature which is the preferred crystalline phase for steam cracking reactions. In fact, according to Lemonidou (A. A. Lemonidou, I. A. Vasalos, Applied Catalysis, 54 (1989), 119-138) the most effective catalyst is a mixture of calcium-aluminates in which the prevalent compound is mayenite (12CaO.7Al2O3); S. Nowak, on the other hand, has patented a catalyst (DD-243 647 of 1987) in which the preferred phases have a lower content of calcium oxide: CaO.Al2O3 and CaO.2Al2O3.

[0014] The preparation of these catalysts is generally effected by the mechanical mixing of the oxides or their aluminum and calcium precursors and subsequent calcination at a high temperature. This process generally leads to the formation of materials in which there are several phases, even if in some cases one phase may be distinctly prevalent with respect to the others. No information is provided however in scientific literature with respect to this type of catalyst, on the production of pure calcium-aluminate materials by means of the syntheses described.

[0015] We have now found a process for obtaining pure mayenite (12CaO.7Al2O3), which surprisingly allows better results to be obtained in terms of yield to light olefins in the field of naphtha steam cracking reactions with respect to mixtures containing mayenite and other calcium-aluminates either pure or mixed with each other.

[0016] The catalyst for steam cracking reactions, object of the present invention, is characterized in that it consists of pure mayenite having the general formula:

12CaO.7Al2O3

[0017] which has, in its calcined form, an X-ray diffraction spectrum, registered by means of a vertical goniometer equipped with an electronic impulse count system and using CuKα radiation (λ=1.54178 Å), containing the main reflections indicated in Table 1 (wherein d indicates the interplanar distance) and in FIG. 1.

[0018] The process for the preparation of the catalyst, i.e. pure mayenite described above, is characterized in that it comprises the following steps:

[0019] dissolution of salts containing calcium and aluminum with water;

[0020] complexing of the dissolved salts by means of polyfunctional organic hydroxyacids;

[0021] drying of the solution resulting from the complexing in order to obtain a solid precursor product;

[0022] calcination of the solid precursor product at a temperature ranging from 1300 to 1400° C., preferably ranging from 1330 to 1370° C., for at least 2 hours, preferably for at least 5 hours.

[0023] The polyfunctional organic hydroxyacids can be selected from citric acid, maleic acid, tartaric acid, glycolic acid and lactic acid: citric acid is preferred.

[0024] The salts containing calcium are preferably selected from calcium acetate and calcium nitrate.

[0025] Aluminum nitrate is the preferred salt containing aluminum.

[0026] It is advisable for the preparation process to be carried out with a molar ratio polyfunctional hydroxyacids/salts containing calcium and alumina ranging from 1.5 to 1.

[0027] A further object of the invention relates to the process for the production of light olefins by means of the steam cracking reaction of hydrocarbon charges selected from naphtha, in particular virgin naphtha, kerosene, atmospheric gas oil, vacuum gas oil, alone or mixed with each other, in the presence of a catalyst according to claim 1, which is effected preferably operating at a temperature ranging from 720 to 800° C., at a pressure ranging from 1.1 to 1.8 absolute Atm and for a contact time ranging from 0.07 to 0.2 sec.

[0028] Some examples are provided for a better illustration of the invention, but which should not be considered as limiting the scope of the present invention.

EXAMPLE 1

[0029] Preparation of the catalyst.

[0030] A synthesis method in homogeneous phase was used.

[0031] This method comprises the use of citric acid or polyfunctional hydroxyacids which have the function of complexing metal salts in aqueous solution. After dehydration of the aqueous solution an amorphous solid precursor is obtained, which, after thermal treatment at a high temperature, produces the desired product.

[0032] The main advantages of this technique are the following:

[0033] homogeneous mixing on an atomic scale

[0034] good stoichiometric control

[0035] production of mixed oxides using commercial chemical products

[0036] short process times

[0037] A solution of aluminum nitrate, 378.2 g of Al(NO3)3.9H2O (1.008 moles) in 470 g of water was first added to a solution of calcium acetate, obtained by dissolving at room temperature 152.2 g of (CH3COO)2Ca.H2O (0.864 moles) in 450 g of H2O, followed by a solution of citric acid: 393.1 g (1.872 moles) in 375 g of water. The homogeneous solution obtained was dried by means of a spray-dryer. The desired product 12CaO.7Al2O3 (Mayenite) was obtained in pure form after calcination at 1350° C. for 5 h.

[0038] In order to obtain a catalyst formed by means of tableting, a lubricating agent (2 wt % of stearic acid) was added; after tableting, the catalyst was subjected to an additional calcination step.

[0039] The composition of the catalyst obtained was verified by means of X-ray diffractometry, which showed the presence of the single pure 12CaO.7Al2O3 phase.

[0040] (See Table 1 and FIG. 1 mentioned above).

EXAMPLE 2 (COMPARATIVE)

[0041] In this example the sol-gel method was used.

[0042] 327.62 g of aluminum secbutoxide (1.33 moles) in 327.9 g of n-butanol (4.431 moles) were charged into a 2 liter three-necked flask. A solution of 200.8 g of (CH3COO)2Ca.H2O (1.14 moles) in 598 g of H2O was added, at 80° C., under vigorous magnetic stirring, by means of a drip funnel. The gel formed was left to age for a night and then dried. The composition of the product obtained, after calcination at 1350° C. for 5 h, determined by means of X-ray diffraction, is the following: 21% 6 CaO.Al2O3, 7% CaO.2Al2O3, 3% 3CaO.Al2O3, 69% 12CaO.7Al2O3.

[0043] In order to obtain a catalyst formed by means of tableting, a lubricating agent (2 wt % of stearic acid) was added; after tableting, the catalyst was subjected to an additional calcination step.

[0044] From Table II and FIG. 2 it can be seen that in addition to the mayenite phase, there are also the diffraction lines relating to the calcium-aluminates specified above.

EXAMPLE 3 (COMPARATIVE)

[0045] A solution of aluminum nitrate, 577.7 g of Al(NO3)3.9H2O (1.540 moles) in 720 g of water was first added to a solution of calcium acetate, obtained by dissolving at room temperature 67.83 g of (CH3COO)2Ca.H2O (0.385 moles) in 200 g of H2O, followed by a solution of citric acid: 404.3 g (1.925 moles) in 380 g of water. The homogeneous solution obtained was dried by means of a spray-dryer. The desired product CaO.2Al2O3 was obtained in pure form after calcination at 1350° C. for 5 h.

[0046] In order to obtain a catalyst formed by means of tableting, a lubricating agent (2 wt % of stearic acid) was added; after forming, the catalyst was subjected to an additional calcination step.

[0047] The composition of the catalyst obtained was verified by means of X-ray diffractometry, which showed the presence of the single pure CaO.2Al2O3 phase.

EXAMPLES 4-7

[0048] Steam cracking reaction effected in a laboratory plant in continuous with a fixed bed reactor having a diameter of ½″.

[0049] Operating conditions:

[0050] Charge=Virgin Naphtha

[0051] T=775° C.

[0052] H2O/charge=0.8 by weight

[0053] Residence time=0.1 s

[0054] 4 tests were effected using the following materials:

[0055] quartz in granules, or inert material as reference for evaluating the catalyst performances (Example 4: comparative);

[0056] mixture of calcium aluminates prepared as described in Example 2 (Example 5: comparative);

[0057] pure CaO.2Al2O3 prepared as described in Example 3 (Example 6: comparative);

[0058] pure mayenite prepared as described in Example 1 (Example 7).

[0059] From the results provided in Table A, it can be seen that all the calcium-aluminate materials give higher performances than quartz with respect to yield to C2, C3, C4 olefins (butenes and butadiene); pure mayenite (12CaO.7Al2O3) however provides the best result, producing the highest yield, without increasing the formation of undesired products such as coke and carbon monoxides.

	TABLE A
	Example
		5
		69% 12CaO · 7Al2O3	6	7
		21% CaO · Al2O3	Pure	Pure
	4	7% CaO · 2Al2O3	CaO ·	12CaO ·
Yield (w %)	quartz	3% 3CaO · Al2O3	2Al2O3	7Al2O3
Hydrogen	0.80	0.98	0.92	0.94
Methane	9.78	11.35	10.70	11.14
Ethylene	22.26	25.45	24.90	26.27
Ethane	2.23	2.54	2.41	2.52
Propylene	15.12	17.24	15.94	17.60
Propane	0.35	0.41	0.40	0.48
Butanes	1.31	1.52	1.19	2.04
Butenes	5.77	6.67	5.41	7.35
Butadiene	3.96	4.81	3.80	5.03
CO + CO2	0.11	0.62	0.16	0.03
Tot. GAS	61.7	71.6	65.8	73.4
Coke	0.8	0.8	0.7	0.4
Tot. C2,C3,C4	47.11	54.17	50.05	56.25
olefins

[0060]

TABLE I
X-ray diffraction spectrum of the pure Mayenite phase
2θ (CuKα) (°) d (Å)
18.18         4.88
21.02         4.22
23.52         3.78
27.89         3.196
29.87         2.989
33.48         2.675
35.17         2.550
36.77         2.442
38.33         2.347
41.31         2.184
44.10         2.052
46.76         1.941
49.30         1.847
51.76         1.765
52.96         1.728
54.14         1.693
55.30         1.660
56.44         1.629
57.56         1.600
60.87         1.521
61.95         1.497
62.98         1.475
67.19         1.392
69.23         1.356

[0061]

TABLE II
X-ray diffraction spectrum of a sample consisting of May-
enite (main phase) and Ca3Al2O6, CaAl2O4 and CaAl4O7.
	2θ (CuKα) (°)	d (Å)	2θ (CuKα) (°)	d (Å)
	12.94	6.84	43.19	2.093
	14.32	6.18	44.14	2.050
	16.06	5.52	44.80	2.021
	16.40	5.40	45.36	1.998
	18.18	4.88	46.39	1.956
	19.01	4.66	46.81	1.939
	19.99	4.44	47.24	1.923
	21.02	4.22	47.69	1.906
	21.98	4.04	48.07	1.891
	22.80	3.899	48.85	1.863
	23.53	3.777	49.37	1.844
	23.99	3.707	49.60	1.836
	24.71	3.601	50.65	1.801
	25.42	3.501	51.83	1.763
	26.06	3.416	53.02	1.726
	27.00	3.299	54.20	1.691
	27.92	3.193	55.36	1.658
	28.24	3.158	56.51	1.627
	29.00	3.077	57.63	1.598
	29.23	3.053	59.32	1.557
	29.90	2.986	59.50	1.552
	30.10	2.967	60.40	1.531
	31.21	2.864	60.96	1.519
	32.14	2.782	61.99	1.496
	32.59	2.745	62.17	1.492
	33.22	2.695	63.09	1.472
	33.52	2.671	63.28	1.468
	34.55	2.594	63.82	1.457
	35.20	2.548	64.22	1.449
	35.70	2.513	65.19	1.430
	36.83	2.438	65.65	1.421
	37.44	2.400	66.44	1.406
	38.37	2.344	67.29	1.390
	38.71	2.324	67.48	1.387
	39.75	2.266	68.34	1.372
	41.02	2.198	69.31	1.355
	41.35	2.182	69.55	1.351
	42.35	2.133

Claims

1. A catalyst for steam cracking reactions characterized in that it consists of pure mayenite having the general formula:

2. A process for the preparation of the catalyst according to claim 1, characterized in that it comprises the following steps: dissolution of salts containing calcium and aluminum with water; complexing of the dissolved salts by means of polyfunctional organic hydroxyacids; drying of the solution resulting from the complexing in order to obtain a solid precursor product; calcination of the solid precursor product at a temperature ranging from 1300 to 1400° C. for at least two hours.

3. The process according to claim 2, wherein the calcination is effected at a temperature ranging from 1330 to 1370° C. for at least 5 hours.

4. The process according to claim 2, wherein the salts containing calcium are selected from calcium acetate and calcium nitrate.

5. The process according to claim 2, wherein the salt containing aluminum is aluminum nitrate.

6. The process according to claim 2, wherein the polyfunctional hydroxyacid is citric acid.

7. The process according to claim 2, wherein the molar ratio polyfunctional hydroxyacids/salts containing calcium and alumina ranges from 1.5 to 1.

8. A process for the production of light olefins by means of the steam cracking reaction of hydrocarbon charges selected from naphtha, kerosene, atmospheric gas oil, vacuum gas oil, alone or mixed with each other, in the presence of a catalyst according to claim 1, operating at a temperature ranging from 720 to 800° C., at a pressure ranging from 1.1 to 1.8 absolute Ate. and for a contact time ranging from 0.07 to 0.2 sec.

9. The process according to claim 8, wherein the naphtha is virgin naphtha.