Claims
- 1. A catalyst for the steam reforming of normally liquid hydrocarbons to produce hydrogen and the oxides of carbon, which consists essentially of:
- (a) a low surface area refractory support consisting essentially of aluminum oxide in the alpha phase and having a surface area, as measured by nitrogen adsorption of less than 15 square meters per gram, and having catalytically active constituents impregnated thereon;
- (b) said catalytically active constituents consisting essentially of nickel oxide in a weight concentration, expressed as the metal, of from 5 to 30% by weight and the oxides of manganese and iron, in which the ratio of manganese to iron, expressed as the metal by weight, does not exceed 2:1;
- (c) the improvement wherein said catalytically active constituents are not chemically bound to said refractory support, having been impregnated on to said support from a heat decomposable water soluble solution of their metal salts, followed by calcination of said salts to convert said salts to their oxides by calcination at a temperature not in excess of 1200.degree. F.
- 2. The catalyst, as defined in claim 1, in which the manganese is present in a weight concentration, expressed as the metal, of from 0.5-5.0 percent by weight.
- 3. The catalyst, as defined in claim 1, in which the iron is present in a weight concentration, expressed as the metal, of from 0.5-10 percent.
- 4. A catalyst, as defined in claim 1,
- A. the further improvement of a promoter for said catalytically active constituents comprising barium oxide.
- 5. A process for preparing a catalyst for the steam reforming of normally liquid hydrocarbons for the production of hydrogen and the oxides of carbon, and which is resistent to the deposition of carbon thereon, which consists of the steps of:
- (a) forming an aqueous solution of the water soluble heat decomposable salts of nickel and of the heat decomposable salts of promotional amounts of manganese and iron in which the ratio of manganese to iron, expressed as the metal by weight, is not in excess of 2:1;
- (b) impregnating said solution on to a low surface area refractory support in catalytically active amounts, said support comprising a shaped carrier consisting essentially of aluminum oxide in the alpha phase and having a surface area, as measured by nitrogen adsorption of less than 15 square meters per gram; and
- (c) calcining said impregnated refractory support at a temperature of not in excess of 1200.degree. F. to convert each of these salts to the oxide.
- 6. A process for preparing a catalyst, as defined in claim 5, the improvement of adding a water soluble heat decomposable salt of barium to said aqueous solution.
- 7. A process for preparing a catalyst, as defined in claim 5, the improvement of:
- A. preparing a water solution of a heat decomposable barium salt;
- B. dipping the impregnated and calcined support into said solution.
- C. calcining said impregnated support at a temperature of not in excess of 1200 degrees F.
- 8. A process for preparing a catalyst for the steam reforming of normally liquid hydrocarbons for the production of hydrogen and the oxides of carbon, which consists of the steps of:
- (a) preparing a first solution of a heat decomposable salt of manganese,
- (b) preparing a second solution comprising the heat decomposable salts of nickel and iron;
- (c) dipping a low surface area refractory support consisting essentially of aluminum oxide in the alpha phase and having a surface area of less than 15 square meters per gram in said first solution to impregnate said manganese salt onto said support;
- (d) calcining said impregnated support to convert the salt to the oxide at a temperature not in excess of 1200.degree. F.;
- (e) dipping said calcined support in said second solution to impregnate thereon the salts of nickel and iron;
- (f) calcining said support at a temperature not in excess of 1200.degree. F. to convert said salts to the oxides.
- 9. The method of preparing a catalyst as defined in claim 8, the further improvement of
- A. controlling the concentration of the salts in said first and second solutions so that the concentration of manganese, expressed as the metal in said first solution does not exceed twice the concentration of the iron salt, expressed as the metal by weight, in the second solution.
- 10. A process of preparing a catalyst, as defined in claim 8, the further improvement of adding a water soluble, heat decomposable salt of barium of one to said solutions.
- 11. A process of preparing a catalyst, as defined in claim 8, the further improvement of:
- A. preparing a third aqueous solution of a water soluble heat decomposable salt of barium;
- B. dipping the calcined carrier into said third solution,
- C. calcining said carrier at a temperature not in excess of 1200 degrees F.
- 12. A process of preparing a catalyst for the steam reforming of hydrocarbons to produce hydrogen and the oxides or carbon, which consists of the steps of:
- (a) preparing an aqueous solution of a heat decomposable water-soluble salt of iron;
- (b) preparing a second aqueous solution of the water-soluble heat-decomposable salts of nickel and manganese;
- (c) dipping a low surface area refractory support, consisting essentially of aluminum oxide in the alpha phase and having a surface area, as measured by nitrogen adsorption, in the range of less than 15 square meters per gram, into said first solution to impregnate a salt of iron thereon;
- (d) calcining said support at a temperature not in excess of 1200.degree. F. to convert said salt to the oxide;
- (e) dipping said salt into said second solution to impregnate thereon the salts of nickel and manganese;
- (f) calcining said support to convert the salts of manganese and nickel to the oxide at a temperature not in excess of 1200.degree. F.
- 13. A process of preparing a catalyst, as defined in claim 12, the improvement of controlling the concentration of manganese in said second solution relative to the concentration of iron, expressed as the metal, in said first solution so that concentration of manganese, expressed as the metal, in said second solution does not exceed twice the concentration of iron, expressed as the metal, in the first solution.
- 14. A process of preparing a catalyst, as defined in claim 12, the further improvement of adding a water soluble, heat decomposable salt of barium to one of said solutions.
- 15. A process of preparing a catalyst, as defined in claim 12, the further impovement of:
- A. preparing a third aqueous solution of a water soluble heat decomposable salt of barium;
- B. dipping the calcined carrier into said third solution;
- C. calcining said carrier at a temperature not in excess of 1200 degrees F.
CROSS REFERENCE TO RELATED APPLICATION
This application is a continuation in part of our copending application for CATALYST AND PROCESS FOR STEAM REFORMING OF HYDROCARBONS, Ser. No. 638,505, filed Dec. 8, 1975.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
3507811 |
Davies et al. |
Apr 1970 |
|
3645915 |
Stiles |
Feb 1972 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
460801 |
Feb 1937 |
GBX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
638505 |
Dec 1975 |
|