Catalyst for the preparation of elastomeric ethylene-propylene copolymers

Information

  • Patent Grant
  • 5578540
  • Patent Number
    5,578,540
  • Date Filed
    Monday, February 5, 1996
    28 years ago
  • Date Issued
    Tuesday, November 26, 1996
    28 years ago
Abstract
Solid component of a catalyst for the synthesis of elastomeric Ethylene-Propylene copolymers typically amorphous, basically consisting of a Titanium compound supported on a solid component mainly consisting of MgCl.sub.2, prepared by a process which comprises putting a solution (I), basically consisting of an organometallic compound of Aluminium diluted with aliphatic hydrocarbons, in contact with a solution (II) containingan anhydrous Magnesium halide in a composition of solvents selected from halohydrocarbons and aromatic hydrocarbons and relative mixtures, in the presence of an Aluminium trihalide;a tetravalent Titanium compound having general formula Ti(OR).sub.4-n X.sub.n.
Description

BACKGROUND OF THE INVENTION
The present invention relates to solid catalytic components of the Ziegler-Natta type, suitable for the synthesis of elastomeric copolymers having a high purity and to the process for their preparation.
The present invention also relates to the use of these catalytic components in the synthesis of elastomeric copolymers of ethylene with propylene, prevalently amorphous and with a high purity.
DESCRIPTION OF THE PRIOR ART
It is known in the art that prevalently amorphous polymers of ethylene with propylene can be advantageously produced using Ziegler-Natta type catalysts, as described in G. Natta, G. Mazzanti et al., Journal of Polymer Science Vol. 51 (1961) page 411, and in Fr-A-2,027457.
These catalysts consist of at least two components:
a) a salt of a transition metal belonging to a group from IV to VIII of the periodic table,
b) an organometallic compound of a metal belonging to a group from I to IV of the periodic table.
To obtain copolymers characterized by a low crystallinity, sufficiently narrow distribution of molecular weights and composition, a Vanadium compound is preferred as the transition metal salt: in this case the complete catalytic system comprises a third component (c) capable of raising the polymerization productivity expressed as Kg of polymer produced per gram of Vanadium per hour.
Type "a" components particularly used are salts of Vanadium with a valence of from 3 to 5, such as for example Vanadium halides, Vanadium oxyhalides, Vanadium or Vanadyl alcoholates and Vanadium acetylacetonate.
Preferred type "b" components are organometallic compounds of Aluminium such as Aluminium trialkyls, Aluminium alkylhalides.
The type "c" components are generally halogenated organic compounds of the chloroalkane or chloroester type such as for example CHCl.sub.3, CCl.sub.4, ethyltrichloroacetate or n-butyl perchlorocrotonate.
For the production of ethylene-propylene elastomeric copolymers, both solution and suspension processes are used.
The solution processes are characterized in that both the monomers and the polymers are dissolved in a hydrocarbon medium whereas in the suspension processes the polymerization is carried out in a medium in which the elastomer is substantially insoluble. This latter process generally comprises liquid propylene as suspending medium and has considerable economical advantages with respect to the solution, in particular:
i) high concentrations of polymer can be used in the reactor without causing great increases in viscosity in the reaction medium;
ii) no solvents or suspending agents are used which are extraneous to the polymerization and whose recycling would result in a considerable waste of energy;
iii) the reaction heat can be very efficiently removed by evaporation of the liquid monomers and their subsequent condensation before recharging them into the reactor.
For suspension processes, when the operating temperatures are not higher than 50.degree. C., a particularly advantageous catalytic system consists of Vanadium triacetylacetonate (component "a"), Aluminium diethylmonochloride (component "b") and n-butyl perchlorocrotonate (component "c"); with this system a wide range of copolymers can be obtained, having satisfactory mechanical and elastic properties to be used for a variety of applications both as raw and vulcanized polymers.
Catalysts based on Vanadium salts however have the disadvantage of giving a low productivity. In addition, if the process does not comprise a final washing step, considerable quantities of catalytic residues can be present in the polymer, in particular chlorinated compounds resulting from the reaction of the Vanadium salt with the organometallic co-catalyst.
Catalysts which are suitable for the copolymerization of ethylene with propylene having a much higher productivity than that given by systems containing Vanadium compounds are described in patents U.S. Pat. No. 3,789,036, U.S. Pat. No. 4,013,823, U.S. Pat. No. 4,331,561, GB-A-2.099.836, GB-A-1.293.814, EP-A-301.894. The catalyts described in the above documents consist, in the preferred embodiment, of:
A) a solid obtained by putting a Titanium compound having the formula Ti(OR).sub.n X.sub.4-n (wherein R is an aliphatic, cycloaliphatic or aromatic radical containing a number of carbon atoms of between 1 and 20, X is a halogen atom and n is an integer of between 0 and 4) in contact with a Magnesium compound selected from the halides, alkoxyhalides or adducts between MgCl.sub.2 and alcohols;
B) at least one organometallic compound of aluminium having the general formula Al(Z.sub.3-m)X.sub.m or Al.sub.2 Z.sub.t X.sub.p wherein Z is an alkyl group, X is a halogen, m represents an integer of between 0 and 2, t and p represent integers between 1 and 5 with p+t=6.
Examples of type (B) compounds which can be used together with component (A) for the synthesis of polyolefins are: Al(C.sub.2 H.sub.5).sub.2 Cl, Al(i-C.sub.4 H.sub.9).sub.3, Al(C.sub.2 H.sub.5).sub.3, Al.sub.2 (C.sub.2 H.sub.5).sub.3 Cl.sub.3 etc.
Examples of Magnesium compounds suitable for the preparation of the solid (A) are MgCl.sub.2, MgCl(O-C.sub.4 H.sub.9), MgCl.sub.2.m(n-HOC.sub.4 H.sub.9).
An example of a type (A) compound is described in Italian patent application IT-A-MI 91 A001935. This compound can be represented by the formula: M.sub.1 Mg.sub.(0.3-20) X.sub.(2-60) Al.sub.(0-6) (R-COO).sub.(0.1-3) wherein: M can be Ti, V, Zr or Hf; X is a halogen; R is a hydrocarbon radical containing at least 4 carbon atoms. According to a procedure described in the above patent application, the Titanium compound to be reacted is Titanium chloride 2-ethylhexanoate and the magnesium compound is magnesium chloride 2-ethyl-hexanoate.
For the preparation of an active solid compound (A) in the polymerization of ethylene and alpha-olefins various very effective processes are known in the art. Some of them comprise for example treatment with the Titanium compound of a solid support having a high surface area comprising the Magnesium compound, as described for example in EP-A-202.550 which discloses the preparation of a solid catalytic component (A) having a high productivity in the synthesis of polyolefins and which is prepared by grinding MgCl.sub.2 together with Ethylbenzoate and subsequently treating the solid thus obtained with TiCl.sub.4 in excess.
According to the disclosure of U.S. Pat. No. 4,843,049 the solid component (A) can be prepared for example with the following process: a) spray-drying of an ethanol solution of MgCl.sub.2 to obtain a solid granular substrate; b) treatment of the substrate with Ti(n-OC.sub.4 H.sub.9).sub.4 in n-decane; c) addition of Al(C.sub.2 H.sub.5).sub.2 Cl. The critical phase for the above method is in the preparation of the support based on Magnesium, particularly in the operations necessary for bringing the surface area to sufficiently high values to allow absorption of the Titanium compound: this phase is generally expensive and technologically very complex. Alternative processes which simplify the preparation of the support consist in: (a) treating a Magnesium compound previously brought into solution with a Titanium compound, (b) separating the solid (A) by treatment with a suitable precipitant.
According to an example of patent JP 56004608, the solid catalytic component (A) is prepared by adding butanol to a solution of MgCl.sub.2 and Titanium tetrabutoxide in heptane, and then adding AlCl.sub.3, TiCl.sub.4 and methylhydropolysiloxane.
IT-A-19473/84 discloses how a solid component (A) can be obtained by reacting a Titanium compound (i) dissolved in a hydrocarbon (such as Ti(O-C.sub.4 H.sub.9).sub.4 dissolved in anhydrous n-hexane) with a liquid complex (ii), having general formula MX.sub.2.n(AlRX.sub.2).pAlX.sub.3, (wherein for example: M is Mg, X is Chlorine, R is the C.sub.2 H.sub.5 radical; "n" and "p" are integers varying from 1 to 4 and from 0 to 1 respectively), and finally adding an electron-donor compound (iii) such as for example n-butyl ether or anisole. With this method the separation of the solid (A) takes place directly after the reaction between components (i) and (ii) without the use of further precipitants.
JP-A-158871 discloses that component (A) can be prepared by putting TiCl.sub.4 in contact with a solid obtained by precipitation from a solution of anhydrous MgCl.sub.2 in propylchloride in the presence of AlCl.sub.3.
SUMMARY OF THE INVENTION
It has now been found, in accordance with the present invention, that the supporting of a Titanium compound on solid crystalline MgCl.sub.2 can be advantageously carried out with a new simplified process.
On the basis of what is specified above, the present invention relates to a catalyst for the synthesis of prevalently amorphous elastomeric Ethylene-Propylene copolymers, consisting of a Titanium compound supported on a solid mainly consisting of MgCl.sub.2, characterized in that it is prepared with a process which comprises:
i) putting a solution (I), basically consisting of an organometallic compound of Aluminium diluted with aliphatic hydrocarbons, in contact with a solution (II) prepared by means of the following steps:
a) dissolution of an anhydrous Magnesium halide in a composition of solvents selected from halohydrocarbons and aromatic hydrocarbons and relative mixtures, in the presence of an Aluminium trihalide;
b) treatment of the solution prepared in step (a) with a tetravalent Titanium compound having general formula Ti(OR).sub.4-n X.sub.n, wherein R is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical containing from 1 to 20 carbon atoms, X is a halogen and n is an integer from 0 to 4;
c) possible treatment with an electron-donor compound selected from the group of esters of carboxylic acids and alkyl or aryl or arylalkyl ethers, contemporaneously with or following treatment with the Titanium compound of step (b);
ii) separation and possible purification of the solid catalytic component thus formed.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
In a preferred embodiment, solution (II) is obtained by treating anhydrous MgCl.sub.2 and AlCl.sub.3 with a mixture of 1,2-dichlorethane and toluene, or with a mixture of n-butylchloride and 1,2-dichloroethane, at a temperature of between 10.degree. and 90.degree. C., and subsequently adding, after cooling to a temperature of between 10.degree. and 40.degree. C., TiCl.sub.4, Ti (O-nC.sub.4 H.sub.9).sub.4 or TiCl(O-C.sub.4 H.sub.9).sub.3 and an electron-donor compound of the group of ethers or esters, preferably ethyl benzoate, di-n-butyl ether or anisole.
In both cases the ingredients are reacted in the following molar ratios:
AlCl.sub.3 /MgCl.sub.2 from 1 to 5; 1,2-dichloroethane (or n-butylchloride)/AlCl.sub.3 not less than 0.1; MgCl.sub.2 /Ti from 0.5 to 5; 1,2-dichloroethane/toluene from 0.05 to 5; electron-donor compound/Ti not more than 5. The concentration of MgCl.sub.2, expressed with respect to the mixture (1,2-dichloroethane plus toluene or n-butylchloride and 1,2-dichloroethane) is preferably between 1 and 7 g/100 ml; the temperature at which the contact between the ingredients takes place is between 10.degree. and 90.degree. C. and the duration is between 0.5 and 8 hours.
Solution (I) basically consists of an organometallic compound of Aluminium having general formula Al(Z.sub.3-m)X.sub.m or Al.sub.2 Z.sub.t X.sub.p, wherein Z is an alkyl group, X a halogen, m an integer from 1 to 3, t and p represent integers between 1 and 5 with p+t=6, dissolved in a hydrocarbon solvent at a concentration of from 5 to 15 g/l. The molar ratio between the Aluminium alkyl of (I) and Titanium of (II) is preferably between 3 and 20. The mixing temperature of the two solutions is between 30.degree. and 60.degree. C.
The contact between solution (I) and (II) gives rise to the formation of the solid (A) which can be separated and washed with the conventional techniques.
In another form of embodiment, the precipitation of the catalytic component can be also carried out by prepolymerization with ethylene or propylene both in a hydrocarbon solution or suspension of liquid monomer, in the presence of one or more Aluminium alkyls, preferably Al(C.sub.2 H.sub.5).sub.3, Al(i-C.sub.4 H.sub.9).sub.3 or their mixtures; the concentration of Aluminium alkyl, before the prepolymerization, is preferably between 1 and 10 g/l; the molar ratio between Aluminium alkyl and Titanium is preferably from 2 to 25; the weight ratio between the prepolymer and dissolved solid component of liquid (II) consisting of AlCl.sub.3, MgCl.sub.2 and Titanium compound is preferably from 1 to 10.
Alternatively liquid (I) and liquid (II) can be fed directly into the polymerization reactor; in this case the catalytic component is generated in situ in the reactor.
Liquid (II) is preferably previously put in contact with the organometallic compound of Aluminium (I) dissolved in hydrocarbon; in this case the catalytic solid is generated immediately before the polymerization reaction without carrying out any operation to separate the solid (A).
The following examples provide a better illustration of the invention.
The preparation of the polymers was carried out in a 3-liter autoclave using the following procedure:
Cleansing with propylene containing Aluminium triisobutyl at 5% weight/volume, is carried out with subsequent washing with fresh propylene. 1.8 liter of liquid propylene "polymerization grade" at room temperature, are fed, at 23.degree. C., the autoclave is then brought to the polymerization temperature and gases of hydrogen and ethylene are introduced through an immersed tube in the pre-established ratio and in such a way as to reach the partial pressures desired.
The catalyst is prepared as follows:
A solution of Aluminium alkyl in hexane at a concentration of from 2 to 4% weight/volume (component "B"); is prepared in a glass funnel maintained under a nitrogen atmosphere; 50% of this solution is poured into a 50 ml glass flask, equipped with a lower tap and maintained under a nitrogen atmosphere, into which solid component "A" in a hexane suspension, or directly a quantity of liquid (II), is immediately fed. The catalytic suspension thus obtained is poured into a steel barrel placed above the autoclave, and the pouring is completed by washing the flask with the remaining 50% of the solution containing the organometallic compound. The content of the barrel is then immediately and rapidly fed into the autoclave using an overpressure of nitrogen. The pressure of the autoclave is kept constant during the test by feeding ethylene from a cylinder with controlled weight. At the end of the experiment the residual monomers are degassed and the autoclave is emptied.
The polymer is finally homogenized with a roll mixer and characterized.
Examples 1 and 2 refer to catalysts obtained with a process which comprises the dissolution of Magnesium chloride in a mixture of 1,2-dichloroethane and toluene, whereas in examples 6 to 22 this dissolution takes place in a mixture of 1,2-dichloroethane and n-butyl chloride.
In particular, for the synthesis of the ethylene-propylene copolymers solid catalytic components were used containing respectively: titanium tetra n-butylate (examples 1 and 2) and titanium tetra n-butylate together with anisole (examples 3 to 5).
Examples 6, 7 and 8 refer to liquid catalytic components fed directly into the polymerization reactor, without the previous separation of a solid and which also form the precursors of the solid catalysts described in examples 9 to 16; they contain respectively Titanium tetra n-butylate, Titanium tetrachloride, Titanium chloro tri-isopropylate.
Examples 9 to 16 refer to prepolymerized solid catalysts, examples 17 to 22 refer to solid catalysts containing Ti tetra n-butylate.





EXAMPLES
Examples 1 and 2
Dissolution of Magnesium Chloride in 1,2-Dichloroethane and Toluene
The following products are charged in order into a 250 ml flask with a flat bottom and breakwater, equipped with a stirrer, reflux cooler and pumped with anhydrous nitrogen: 44.2 grams of anhydrous AlCl.sub.3, 10.5 grams of anhydrous MgCl.sub.2 flakes, 142 ml of toluene and 17.3 ml of 1,2 dichloroethane both anhydrified on molecular sieves. The suspension is then heated and the mixture of liquids brought to boiling point in 1 hour and maintained as such for 2 hours.
During the treatment the development of acid gas is observed. At the end of the reaction a dark-brown solution is obtained which on filtration leaves only traces of solid. The solution is characterized by the following molar ratios: Al/Mg=3, 1,2-dichloroethane/Mg=2, Toluene/Mg=12.
Preparation of the Liquid (II)
50 ml of the solution of MgCl.sub.2 in 1,2-dichloroethane plus toluene prepared as described above, 30 ml of anhydrous 1,2-dichloroethane and 7.15 ml of Titanium tetra-n-butylate diluted in 10 ml of 1,2-dichloroethane are charged into a large 100 ml test-tube with magnetic stirrer and pumped with nitrogen; after the addition of the Titanium compound there is a development of heat. The solution obtained is characterized by the molar ratios Mg/Ti=1.5; TIBA/Ti=6.
Preparation of the Solid Catalytic Component Precipitate Containing Titanium Tetra-n-butylate
250 ml of a solution consisting of Aluminium triisobutyl (TIBA) at 10% weight/volume in hexane are charged into a pear-shaped flask, with stirrer, reflux cooler and pumped with nitrogen; 87 ml of the liquid (II) prepared as described above are then fed in 1 minute. After the addition of the liquid (II) there is a development of heat and immediate formation of a dark solid. The mixture is heated in 30 minutes to 50.degree. C. and then left under stirring for 2 hours. After filtration using a funnel with a porous septum in a nitrogen environment, the precipitate is washed 3 times with anhydrous hexane at room temperature and is dried under vacuum. The solid obtained weighs 7.4 grams and has the following analytical weight composition:
Total Ti=11.7% Mg=7.85% Al=2.7%, Cl=55.35%, (O-n-C.sub.4 H.sub.9) group=0.9.
The evaluation of the behaviour in polymerization is carried out operating under the conditions shown in Table 1.
TABLE I__________________________________________________________________________Ex- Molar ratio Pressures Duration Compon- TIBA (1) Molar Polymer Yield Yieldam- Temp. Ethyl./Propyl. Ethylene Hydrogen Total time ent "A" (mmol./ ratio obtained Kg polym./ (Kg polym./ple (.degree.C.) liquid phase (bar) (bar) (bar) (hrs.) quantity It) Al/Ti (grams) g. catal.) g.__________________________________________________________________________ Ti)1 40 0.0526 2.5 0.1 18.2 1 0.0058 g 2.1 267 146 25.2 2152 40 0.0753 3.5 0.5 19.6 1 0.008 g 2.1 193 138 17.3 147.43 40 0.0526 2.5 0.1 18.2 1 (*) 0.15 cc 4.2 430 137 -- 488.54 40 0.0723 3.5 0.5 19.6 1 (*) 0.10 cc 2.8 645 145 -- 775.45 40 0.163 7.1 3. 25.6 1 (*) 0.07 cc 1.4 1383 107 -- 817.46 40 0.0526 2.5 0.1 18.2 1 1.11 cc 2.8 406 230 3877 40 0.0526 2.5 0.1 18.2 1 0.08 cc 2.8 539 221 4938 40 0.0526 2.5 0.1 18.2 1 0.1 cc 4.2 842 167 3889 40 0.0526 2.5 0.1 18.2 1 0.0255 g 2.8 -- 261 10.2 --10 40 0.163 7.1 3.5 26.2 1 0.0103 g 1.4 86 8.311 50 0.124 6.2 3.6 29.6 1 0.0129 g 1.4 191 14.812 40 0.0526 2.5 0.1 18.2 0.5 0.0247 g 2.8 -- 249 10.1 --13 40 0.163 7.1 3.5 26.2 1 0.0084 g 1.4 126 1514 40 0.124 6.2 3.6 29.6 0.5 0.012 g 1.4 127 10.615 40 0.0526 2.5 0.1 18.3 1 0.0160 g 2.8 190 11.916 40 0.0526 2.5 0.5 18.8 1 0.0161 g 2.8 187 11.617 40 0.0526 2.5 0.1 18.2 1 0.0102 g 2.8 313 231 22.6 30018 40 0.0753 3.5 0.5 19.7 1 0.0081 g 2.1 296 162 20 264.919 40 0.163 7.1 3.5 26.2 1 0.0059 g 1.4 271 110 18.6 246.920 40 0.0526 2.5 0.1 18.2 1 0.0055 g 2.8 405 128 23.3 214.521 40 0.0753 3.5 0.5 19.6 1 0.0065 g 2.1 257 106 16.3 150.322 50 0.0753 3.9 0.1 23.7 0.83 0.0054 g 2.1 309 202 37.4 344.8__________________________________________________________________________ (1) Aluminium triisobutyl (*) Solid catalytic component suspended in anhydrous heptane; concentration in Ti = 0.187% weight/volume
Examples 3-5
Preparation of the Solid Catalytic Component Precipitate Containing Titanium Tetra-n-butylate and Anisole
The following products are charged in order and under stirring into a 100 ml large test-tube with mechanical stirrer and pumped with nitrogen:
70 ml of the solution of MgCl.sub.2 in 1,2-dichloroethane and toluene prepared as described in examples 1 and 2;
30 ml of anhydrous 1,2-dichloroethane;
9.54 grams of anisole diluted in 10 ml of 1,2-dichloroethane (in 15 minutes);
10 grams of Titanium tetra-n-butylate diluted in 10 ml of 1,2-dichloroethane (in 15 minutes).
After 1.5 hours at room temperature, the mixture is fed in 30 seconds into a 1 liter flask equipped with stirrer, cooler, pumped with nitrogen and containing 350 ml of a hexane solution of TIBA at 10% weight/volume. After the addition of the liquid (II) there is a development of heat and immediate formation of a dark solid. The mixture is heated in 30 minutes to 50.degree. C. and then left under stirring for 2 hours. After filtration using a funnel with a porous septum in a nitrogen environment, the precipitate is washed 3 times with anhydrous hexane at room temperature and is dried under vacuum at 55.degree. C. for 2 hours. The solid obtained weighs 11 grams and has the following analytical weight composition:
Total Ti=10.3%, Ti.sup.3+ =10%; Mg=8.65%, Al=1.4%, Cl=52.8%, (O-n-C.sub.4 H.sub.9) group=3.3%; Anisole=2.8%.
Example 6
Dissolution of Magnesium chloride in 1,2-dichloroethane: The following products are charged in order into a 250 ml flask with a flat bottom and breakwater, equipped with a stirrer, reflux cooler and pumped with anhydrous nitrogen: 14.9 grams of anhydrous AlCl.sub.3, 3.55 grams of anhydrous MgCl.sub.2 flakes and 74 ml of 1,2 dichloroethane anhydrified on molecular sieves; 12 ml of n-butyl chloride are then added in 15 minutes, at room temperature. During the dripping of the alkylhalide, there is a development of acid gas.
The suspension is then heated to a temperature of 80.degree. C. in 0.5 hours and maintained as such for 1.5 hours.
At the end of the reaction a dark-brown solution is obtained which on filtration leaves only traces of solid.
The solution is characterized by the following molar ratios: Al/Mg=3, Al/n-butylchloride=1.
Preparation of the liquid catalytic component containing Titanium tetra n-butylate:
25 ml of the solution of MgCl.sub.2 in 1,2-dichloroethane prepared as described above and 1 ml of Titanium tetra n-butylate are charged into a 50 ml test-tube with magnetic stirring and pumped with nitrogen; after the addition of the Titanium compound there is a development of heat. The solution obtained is characterized from a molar ratio Mg/Ti=4.
Example 7
A liquid catalytic component containing Titanium tetrachloride is prepared: the same procedure is used as in example 6 using TiCl.sub.4 as Titanium compound.
Example 8
A liquid catalytic component containing Titanium chloro-tri-isopropylate is prepared: the same procedure is used as in example 6 using Titanium chloro-triisopropylate as Titanium compound.
Examples 9-11
Preparation of the prepolymerized solid catalytic component containing Titanium tetra-n-butylate:
150 ml of anhydrous hexane, 4.5 grams of aluminium triisobutyl (diluted at 10% weight in hexane) and 13 ml of solution containing Titanium tetra n-butylate prepared as described in example 6 are charged into a 500 ml flask thermostat-regulated and equipped with a reflux cooler; the temperature is then brought under stirring to 50.degree. C.; "polymerization grade" ethylene is fed up to a constant pressure of 75 mmHg and the prepolymerization is continued for 3.5 hours. At the end the liquid part is removed by decanting, the polymer is washed three times with anhydrous hexane and the solid is dried under vacuum. The preparation produces 2.4 grams of powder.
Examples 12-14
Preparation of the prepolymerized solid catalytic component containing Titanium tetrachloride:
The same procedure is used as in examples 9 to 11, using the solution containing Titanium tetrachloride prepared as described in example 7.
Examples 15-16
Preparation of the prepolymerized solid catalytic component containing Titanium chloro tri-isopropylate:
The same procedure is used as in examples 9 to 11, using the solution containing Titanium chloro tri-isopropylate prepared as described in example 8.
Examples 17-19
Preparation of the solid catalytic component precipitate containing Titanium tetra-n-butylate:
50 ml of the solution of MgCl.sub.2 in 1,2-dichloroethane, prepared as described in example 6, and 2.1 grams of Titanium tetra-n-butylate (molar ratio Mg/Ti=3.5) are charged into a 100 ml test-tube with magnetic stirring and pumped with nitrogen; after the addition of the Titanium compound the solution is left to mature for 2 hours at the same temperature; the liquid thus obtained is rapidly fed into a 500 ml thermostat-regulated flask, equipped with a reflux cooler, magnetic stirrer and pumped with nitrogen, containing 184 ml of a hexane solution of aluminium triisobutyl (TIBA) at 10% weight; the molar ratio TIBA/Ti is thus equal to 15. After the mixing there is a development of heat and immediate formation of a dark solid. The suspension is then heated to 50.degree. C. for 1.5 hours, the precipitate is filtered and washed 3 times with anhydrous hexane.
The solid after drying under vacuum has the following analytical weight composition: Total Ti=7.55%; Mg=12%; Al=2.45%; Cl=57.55%; (O-n-C.sub.4 H.sub.9) group: less than 0.1%.
Examples 20 to 22
Preparation of the solid catalytic component precipitate containing Titanium tetra-n-butylate:
The same procedure is used as described in examples 17 to 19, but the quantities of Titanium compound and TIBA are modified in order to bring the molar ratio Mg/Ti to 1.5 and the molar ratio TIBA/Ti to 6.3. The solid obtained after drying under vacuum has the following analytical weight composition:
Total Ti=10.85%; Ti.sup.3+ =10.65%; Mg=6.75%; al=2.5%; Cl=46.6%; (O-n-C.sub.4 H.sub.9) group=0.93%.
Table 1 indicates the copolymerization conditions of ethylene with propylene for all the catalysts in the examples and also the polymerization yields.
A comparison between the results of the polymerization tests relating to examples 3, 4 and 5 with those relating to examples 1 and 2, shows that the introduction of anisole as electron-donor compound in the preparation of catalytic component "A", produces a considerable increase in the yield with the same molar ratio ethylene/propylene in the feeding.
Examples 1 and 2 also show that an increase in the partial hydrogen pressure causes a decrease in the catalytic activity even though it is associated with an increase in the concentration of ethylene; on the contrary when component "A" contains anisole a contemporaneous increase in the concentrations of hydrogen and ethylene produce an increase in the yield.
Examples 6, 7 and 8 show that a solid component containing the supported Titanium compound, having a high catalytic activity, can be generated in situ in the polymerization reactor by directly feeding solution (II).
As is shown in examples 9 to 16, the prepolymerization of the liquid components described in examples 6-8, enables high catalytic activities to be obtained.
Examples 17 to 19, compared with examples 20 and 21, show that an increase in the Titanium content in the solid component cause a reduction in the catalytic yield calculated with respect to the Titanium itself.
A comparison between example 21 and example 22 shows that by increasing the polymerization temperature there is a considerable increase in the productivity of the catalytic system.
PHYSICAL MECHANICAL ANALYSES AND CHARACTERIZATIONS
The following measurements were carried out on the polymers obtained:
Propylene content via IR on the polymers in the form of 0.2 mm thick films; using a Perkin-Elmer model 1760 FTIR spectrophotometer.
The method consists in measuring the ratio between the band absorbances at 4390 and 4255 cm.sup.-1 and using a calibration curve calibrated with standard polymers.
Intrinsic viscosity.
The measurements were carried out in Orthodichlorobenzene at 135.degree. C. using an Ubbelhode-type Viscosimeter; the fall times of the solvent and solutions with increasing concentration of the polymer being tested were measured. The extrapolation of the reduced viscosity and that referring to concentration zero gave the intrinsic viscosity value.
Molecular weight distribution.
These analyses were carried out with gel permeation chromatography in orthodichlorobenzene at 135.degree. C., using an ALC/GPC 150 "WATERS" device equipped with a refraction index detector and a set of 10 micron PL GEL columns with porosity in Angstrom of 10.sup.3, 10.sup.4, 10.sup.5, 10.sup.6.
The calibration curve used for the calculation was obtained by using standard monodispersed samples of polystyrene applying the equation of Mark-Houwink valid for linear polyethylene and polypropylene; the molecular weights were corrected in accordance with the composition by the equation of Scholte (Th. G. Scholte, N. L. J. Meijerink and others: J. Appl. Polym. Sci., 1984, 29, 3763-3782).
The results of these analyses are shown in Table 2.
TABLE II__________________________________________________________________________Propylene Intrinsic Molecular Weight average Mooneycontent Viscosity weight distrib. molecul. weight ViscosityExample (% w/w) (dl/g) (Mw/Mn) (Mw .times. 0.001) ML(1 + 4.100) ML(1 + 4.125)__________________________________________________________________________1 55.2 1.7 22.5 224 232 45.1 1.5 19. 226 303 47.7 -- 25 279 654 42.8 1.7 14.4 221 365 26.8 1.5 15.1 153 366 52.8 1.8 6.8 185 247 52.4 1.4 9.3 143 138 47 1.55 14 177 369 53.1 2.2 18.4 234 3010 33.1 1.5 14.8 151 3611 43.8 1 20 99 1212 54.1 1.8 22 192 3813 29.2 1.6 9.3 115 4114 42.5 1.1 10 102 1715 53 2.3 -- -- 4816 51.7 1.95 21 265 4617 50.8 2.1 21 303 5118 41.2 1.9 21.8 250 4419 28.6 1.0 13.4 169 3620 53.2 1.9 12.1 290 4721 42.3 1.8 13.7 194 3222 45 2.0 26.5 301 40__________________________________________________________________________
With the liquid components described in examples 6 to 8, M.sub.w /M.sub.n values are obtained which are lower than or at least very close to those obtained with all the other catalytic components in the examples and in particular with the corresponding prepolymerized catalysts (examples 9 to 16).
The results relating to examples 1 to 6 compared to those of examples 17 to 22, show that the different ways of dissolving the Magnesium chloride or introducing the anisole together with the Titanium compound, enable the synthesis of copolymers of the same type, characterized by ample polydispersity, the M.sub.w /M.sub.n values being between 10 and 30.
Vulcanization and preparation of the samples for physical-mechanical characterization.
The mixtures to be vulcanized were prepared using the formulations shown in table 3.
TABLE 3______________________________________Ingredients Parts by weight______________________________________Polymer 100Fef carbon black (1) 55ZnO 5Peroximon F40 Mg (2) 5Sulphur 0.37Eil 570 Oil (3) 30______________________________________ (1) High Abrasion Furnace low structure carbon black of Cabot; (2) bis(tert-butylperoxy-isopropyl benzene, masterbatch at 40% in EP copolymer, produced by Atochem; (3) paraffin oil having a specific weight of 0.88 of Exxon
The vulcanizability of the copolymers was determined according to the method ASTM D2084-86, with a Monsanto MDR 100-S Rheometer, at a temperature of 160.degree. C. with an oscillation frequency of the rotor of 50 min.sup.-1, deformation angle 0.2.degree., gap 0.2 mm. The following measurements were carried out: time necessary for reaching 2% of the maximum twisting moment (t02); time necessary for reaching 90% of the maximum twisting moment (t90); maximum vulcanizing rate.
Mechanical characteristics of the vulcanized copolymers.
The characteristics of the vulcanized copolymers were measured according to the ASTM methods shown in table 4, using samples taken from plates moulded in a plate-press at 165.degree. C. for 40 minutes and at 18 MPa.
TABLE 4______________________________________Characteristic Method______________________________________Ultimate tensile stress D 412-68Ultimate elongation D 412-68Tension set at 200% D 412-68Shore A Harness D 2240-68______________________________________
Table 5 shows the results of the characterizations carried out on the copolymers obtained with the physico-mechanical measurements before and after vulcanization. These results show that all the catalysts produce easily cross-linkable copolymers, with good final mechanical and elastic properties.
TABLE V__________________________________________________________________________Mooney Viscosity Vulcanization Ultimate Elongation Tension set of the blend t02 t90 V max. tensile stress to break 200%; 25.degree. C. Shore AExample ML(1 + 4.100) (min.) (min.) (N m/min) (MPa) (%) (%) hardness__________________________________________________________________________1 24 0.9 22.2 0.008 7.25 500 12 462 29 0.8 21.9 0.011 7.45 500 14 523 52 -- -- -- 6.45 640 18 494 33 0.7 21.7 0.014 9.8 510 13 525 41 -- -- -- 9 660 68 676 34 0.7 21.3 0.012 9.7 540 8 467 22 0.73 21.9 0.0097 7.3 510 10 468 33 0.8 23.7 0.012 8.4 500 10 489 43 0.73 20.6 0.014 10.5 560 8 4710 39 0.83 21.2 0.011 9.2 560 10 4716 46 0.75 21 0.013 12.2 560 12 4917 46.5 0.8 20.7 0.0145 12.8 580 10 4618 41 0.77 20.4 0.017 14.5 580 14 5119 40 0.8 21.6 0.017 15.9 588 54 6420 36 0.8 20.4 0.011 12.54 660 10 4621 33 0.75 21.3 0.015 9.2 470 13 52__________________________________________________________________________
Claims
  • 1. A process for the preparation of a solid component of a catalyst for the synthesis of an elastomeric ethylene-propylene copolymer prevalently amorphous, comprising a titanium compound supported on a solid consisting essentially of MgCl.sub.2, and said process consisting essentially of the steps of:
  • i) contacting a solution (I) consisting substantially of an organometallic compound of aluminum diluted with aliphatic hydrocarbons, with a solution (II) prepared by the following steps:
  • a) dissolving an anhydrous magnesium halide in a composition of solvents said solvents being halohydrocarbons, aromatic hydrocarbons or mixtures thereof, in the presence of an aluminum trihalide;
  • b) treating said solution (a) with a tetravalent titanium compound having general formula Ti(OR).sub.4-n X.sub.n, wherein R is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical containing from 1 to 20 carbon atoms, X is a halogen and n is an integer from 0 to 4; and
  • ii) separating the solid catalytic component thus formed.
  • 2. The process of claim 1, characterized in that the liquid (II) is obtained by treating anhydrous MgCl.sub.2 and AlCl.sub.3 with a mixture of 1,2-dichloroethane and toluene, or with a mixture of n-butylchloride and 1,2-dichloroethane, at a temperature of between 10.degree. and 90.degree. C., subsequently adding, after cooling to a temperature of between 10.degree. and 40.degree. C., a Titanium compound selected from TiCl.sub.4, Ti(O-n-C.sub.4 H.sub.9).sub.4, TiCl(O-n-C.sub.4 H.sub.9).sub.3.
  • 3. The process of claim 1, wherein said magnesium halide is MgCl.sub.2, said halohydrocarbon is n-butylchloride, and said aluminum trihalide is AlCl.sub.3, and in the preparation of the liquid (II), the ingredients are reacted in the following molar ratios: AlCl.sub.3 /MgCl.sub.2 from 1 to 5; n-butylchloride/AlCl.sub.3 not less than 0.1; MgCl.sub.2 /Ti from 0.5 to 5.
  • 4. The process of claim 1, wherein said magnesium halide is MgCl.sub.2, said halohydrocarbon is 1,2-dichloroethane, and said aluminum trihalide is AlCl.sub.3, and in the preparation of the liquid (II) the ingredients are reacted in the following molar ratios: AlCl.sub.3 /MgCl.sub.2 from 1 to 5; 1,2-dichloroethane/AlCl.sub.3 not less than 0.1; MgCl.sub.2 /Ti from 0.5 to 5.
  • 5. The process of claim 1, characterized in that the reaction between the liquid (I) and liquid (II) takes place directly in the polymerization reactor and, the molar ratio between the organometallic component of Aluminum and the titanium compound is between 3 and 20.
  • 6. The process of claim 2, wherein the solid catalyst component is prepolymerized with ethylene, propylene, or their mixtures in the presence of at least one aluminum alkyl with a molar ratio aluminum alkyl/Ti of between 2 and 25 and characterized in that the weight ratio between the prepolymer and solid consisting of MgCl.sub.2 /AlCl.sub.3 and the titanium compound dissolved in liquid (II), is between 1 and 10.
  • 7. The process of claim 1, wherein step (b) is followed by the steps of:
  • (c) treating said solution with an electron-donor compound, said electron-donor compound being an ester of a carboxylic acid or an ether, and said ether being alkyl, aryl or arylalkyl ether, simultaneously with or following treatment with the titanium compound of step (b) to form a solid catalylic component; and separating and purifying the solid catalytic component thus formed.
Priority Claims (2)
Number Date Country Kind
MI93A2649 Dec 1993 ITX
MI94A0454 Nov 1994 ITX
Parent Case Info

This application is a continuation of application Ser. No. 08/348,120, filed on Nov. 28, 1994, now abandoned.

US Referenced Citations (4)
Number Name Date Kind
4186107 Wagner Jan 1980
4517307 Cuffiani et al. May 1985
4736002 Allen et al. Apr 1988
5037997 Zhukou et al. Aug 1991
Continuations (1)
Number Date Country
Parent 348120 Nov 1994