The present invention relates to a catalyst for treating exhaust gas having a denitration activity and a mercury oxidation activity.
Among methods for treating exhaust gas in which NOx is removed from exhaust gas in a reduction denitration unit and then SO2 is removed in a wet desulfurization unit using an alkaline absorbing solution as an absorbent, there has been studied a method for treating metallic mercury and a mercury compound (hereinafter, collectively referred to as mercury, unless otherwise stated) in exhaust gas while performing denitration and desulfurization at the same time.
Mercury in flue gas exists in forms of metallic mercury which is insoluble in water and mercury chloride which is soluble in water. When in the form of metallic mercury, mercury is hardly dissolved in water. When mercury is in the metallic form, the efficiency of removing mercury by a wet desulfurization unit is lowered. Meanwhile, when mercury is in the form of HgCl or HgCl2, HgCl or HgCl2 in exhaust gas is dissolved in water through the gas-liquid contact in the wet desulfurization unit, and thereby mercury can be removed. In other words, if metallic mercury can be converted into mercury chloride in the presence of a catalyst such as a denitration catalyst, mercury can be removed in the desulfurization unit located in the downstream.
An example of such a conventional method for treating exhaust gas utilizing this scheme will be described with reference to
However, in a case of a coal with a low Cl content, a large amount of a mercury-chlorinating agent such as HCl needs to be supplied into exhaust gas to maintain the rate of conversion to mercury chloride. Moreover, in order to vaporize HCl, a large amount of a high-temperature heat source, steam, or the like is needed. Furthermore, in addition to NH3, which is considered hazardous in power plants, highly corrosive HCl is used, which induces material corrosion, thereby presenting problems of increased utility and storage costs.
Accordingly, an object of the present invention is to provide a method and an apparatus for treating exhaust gas which are capable of reducing the amount of a highly corrosive mercury-halogenating agent such as a mercury-chlorinating agent to be added in an exhaust gas treatment with the mercury-removing efficiency kept high.
In order to achieve the above object, according to the present invention, a catalyst for treating exhaust gas in which nitrogen oxide in the exhaust gas is removed upon contact with ammonia serving as a reducing agent, and in which mercury is oxidized using a halogen as an oxidant includes: TiO2 as a support; an oxide of at least one selected from the group consisting of V, W and Mo, which is supported as an active component on the support; and at least one selected from the group consisting of Bi, P, and compounds containing Bi and/or P, which is supported as a co-catalyst component on the support. The halogen as the oxidant for mercury is preferably a compound containing chlorine (Cl) such as NH4Cl besides HCl or a compound containing bromine (Br). Moreover, the co-catalyst component can be used in forms as follows.
(a) in a form of only a Bi element.
(b) in a form of only a P element.
(c) in a form of containing both a Bi element and a P element.
(d) in a form of a compound of Bi and P.
(e) in a form of a compound containing Bi.
(f) in a form of a compound containing P.
(g) in a form of a compound containing Bi and P.
According to another aspect of the present invention, in the catalyst for treating exhaust gas, the co-catalyst component is formed of any one of P and a compound containing P.
According to yet another aspect of the present invention, in the catalyst for treating exhaust gas, the co-catalyst component is formed of any one of Bi and a compound containing Bi.
The present invention provides a catalyst for treating exhaust gas capable of reducing the amount of a highly corrosive mercury-chlorinating agent to be added while keeping the mercury oxidation efficiency high in an exhaust gas treatment.
Hereinafter, a catalyst for treating exhaust gas according to the present invention will be described in further details with reference to an embodiment thereof.
A support of the catalyst for treating exhaust gas according to the present invention is formed of TiO2. As the catalyst support, generally, at least one selected from the group consisting of TiO2, SiO2, ZrO2, Al2O3, complex oxides thereof, and zeolite can be used.
Moreover, the catalyst for treating exhaust gas according to the present invention supports an oxide of at least one selected from the group consisting of V, W and Mo as an active component on such a support.
Furthermore, the catalyst for treating exhaust gas according to the present invention supports at least one selected from the group consisting of Bi, P, and compounds containing Bi and/or P as a co-catalyst component on the support. The co-catalyst component exists preferably in the form of an oxide, complex oxide or heteropoly acid. Since the compound containing Bi or P is in the form of a compound having a different oxidation number, the oxidation of mercury can be promoted owing to the effect of the oxidation-reduction cycle. Bi can form a complex oxide with Mo, and thus functions as a co-catalyst. Meanwhile, P can form a heteropoly acid having a considerably strong oxidizing power by combining with Mo or W. Both Bi and P do not exist independently and they are an element that can form a compound. Thus, Bi and P function as a co-catalyst.
The compounding ratio of the co-catalyst component with respect to the active component is as follows.
For example, suppose a case where V oxide is used as the active component and a heteropoly acid containing P (molybdophosphoric acid) is used as the co-catalyst component. In this case, the ratio of the number of V atoms contained, the number of Mo atoms contained and the number of P atoms contained is preferably 32:12:1 to 10:12:1.
As another example, suppose a case where V oxide is used as the active component and a compound containing Bi is used as the co-catalyst component. In this case, the ratio of the number of V atoms contained, the number of Mo atoms contained and the number of Bi atoms contained is preferably 1:3:0.1 to 1:10:1.5.
In the above cases, preferably 0.1 to 2 mass % of the active component is supported per 100 g of the support.
Schematically, the catalyst for treating exhaust gas according to the present invention is produced as follows.
(1) For example, a catalyst paste containing a support component and an active component is molded into a honeycomb shape and fired.
(2) The honeycomb is impregnated with a co-catalyst component and fired.
A specific mode of preparing Bi2O3(1.5)-MoO3(7)-V2O5/TiO2 will be described in Example 1 below.
A specific mode of preparing P—MoO3(7)-V2O5(0.5)/TiO2 will be described in Example 2 below.
A TiO2-V2O5-based denitration catalyst (TiO2:V2O5=95.5:0.5 (mass ratio)) was prepared as follows.
Ammonia water with a NH3 content of 25% was added to 3600 g of a metatitanic acid slurry (TiO2 content: 30 mass %), and the pH was adjusted to 6.5, followed by wet-kneading for 2 hours, drying, and furthermore firing at 550° C. for 5 hours. Thereby, a titanium oxide powder was obtained. To the powder, an ammonium metavanadate aqueous solution and an ammonium molybdate aqueous solution were added so as to make the V2O5 and MoO3 contents be 0.5 mass % and 7 mass %, respectively, and then were sufficiently mixed with the powder. Thereafter, the mixture was dried and fired at 450° C. for 4 hours. Thereby, a powder (A) formed of titanium oxide [TiO2]-vanadium oxide [V2O5]-molybdenum oxide [MoO3] was obtained. To 1000 g of the powder (A), 25 g of carboxymethyl cellulose and 12.5 g of polyethylene oxide were put and kneaded together in a kneader for 30 minutes with an adequate amount of water being added thereto, followed by extrusion into a honeycomb shape with 30 mm2, drying and then firing at 500° C. for 5 hours. A bismuth nitrate aqueous solution was further prepared, and the honeycomb was impregnated therewith so as to make the Bi2O3 content be 1.5 mass %. The resultant was fired at 500° C. for 3 hours. Thus, a Bi2O3(1.5)-MoO3(7)-V2O5/TiO2 catalyst was prepared.
The honeycomb-shaped catalysts 1 for treating exhaust gas prepared as described above were provided at three stages, each catalyst having 4 conduits×7 conduits in 500-mm length as shown in
Exhaust gas samples having the following O2 to NOx features shown in Table 1 were allowed to flow under the conditions in the same Table 1, and the mercury oxidation activity of the catalyst 1 for treating exhaust gas was tested. Note that symbols in the table represent the following meanings.
Ugs: superficial velocity
AV: the amount of gas to be treated based on gas-contact area
The exhaust gas samples were extracted at positions S1 and S2 in
Table 2 shows the test result. As seen from the result in Table 2, it is understood that, by using the catalyst 1 for treating exhaust gas according to the present invention, 79.8% of mercury was oxidized after passing through the three stages.
A TiO2-V2O5-based denitration catalyst (TiO2:V2O5=95.5:0.5 (mass ratio)) was prepared as follows.
Ammonia water with a NH3 content of 25% was added to 3600 g of a metatitanic acid slurry (TiO2 content: 30 mass %), and the pH was adjusted to 6.5, followed by wet-kneading for 2 hours, drying, and furthermore firing at 550° C. for 5 hours. Thereby, a titanium oxide powder was obtained. To the powder, an ammonium metavanadate aqueous solution was added so as to make the V2O5 content be 0.5 mass %, and then was sufficiently mixed with the powder. Thereafter, the mixture was dried and fired at 450° C. for 4 hours. Thereby, a powder (A) formed of titanium oxide [TiO2]-vanadium oxide [V2O5] was obtained. To 1000 g of the powder (A), 25 g of carboxymethyl cellulose and 12.5 g of polyethylene oxide were put and kneaded together in a kneader for 30 minutes with an adequate amount of water being added thereto, followed by extrusion into a honeycomb shape with 30 mm2, drying and then firing at 500° C. for 5 hours. A phosphomolybdic acid aqueous solution was further prepared, and the honeycomb was impregnated therewith so as to make the MoO3 content be 7 mass %. The resultant was fired at 500° C. for 3 hours. Thus, a P—MoO3(7)-V2O5(0.5)/TiO2 catalyst was prepared.
As in the case of Example 1, the honeycomb-shaped catalysts 2 for treating exhaust gas prepared as described above were provided at three stages, each catalyst having 4 conduits×7 conduits in 500-mm length as shown in
Exhaust gas samples having the same O2 to NOx features as those shown in Table 1 were allowed to flow under the conditions in Table 3, and the mercury oxidation activity of the catalyst 2 for treating exhaust gas was tested.
Table 4 shows the test result. As seen from the result in Table 4, it is understood that, by using the catalyst 2 for treating exhaust gas according to the present invention, 89.1% of mercury was oxidized after passing through the three stages.
A TiO2-V2O5-based denitration catalyst (TiO2:V2O5=95.5:0.5 (mass ratio)) was prepared as follows.
Ammonia water with a NH3 content of 25% was added to 3600 g of a metatitanic acid slurry (TiO2 content: 30 mass %), and the pH was adjusted to 6.5, followed by wet-kneading for 2 hours, drying, and furthermore firing at 550° C. for 5 hours. Thereby, a titanium oxide powder was obtained. To the powder, an ammonium metavanadate aqueous solution and an ammonium molybdate aqueous solution were added so as to make the V2O5 and MoO3 contents be 0.5 mass % and 7 mass %, respectively, and then where sufficiently mixed with the powder. Thereafter, the mixture was dried and fired at 450° C. for 4 hours. Thereby, a powder (A) formed of titanium oxide [TiO2]-vanadium oxide [V2O5]-molybdenum oxide [MoO3] was obtained. To 1000 g of the powder (A), 25 g of carboxymethyl cellulose and 12.5 g of polyethylene oxide were put and kneaded together in a kneader for 30 minutes with an adequate amount of water being added thereto, followed by extrusion into a honeycomb shape with 30 mm2, drying and then firing at 500° C. for 5 hours. Thus, a MoO3(7)-V2O5/TiO2 catalyst of Comparative Example was prepared.
As in the case of Example 1, the comparative honeycomb-shaped catalysts for treating exhaust gas prepared as described above were provided at three stages, each catalyst having 4 conduits×7 conduits in 500-mm length as shown in
Exhaust gas samples having the same O2 to NOx features as those shown in Table 1 were allowed to flow, and the mercury oxidation activity of the comparative catalyst for treating exhaust gas was tested.
Table 5 shows the test result. As seen from the result in Table 5, it is understood that, by using the comparative catalyst for treating exhaust gas according to the present invention, 79.5% of mercury was oxidized after passing through the three stages.
As seen from the results of Example 1, Example 2 and Comparative Example, by using a catalyst for treating exhaust gas according to the present invention, the amount of a highly corrosive mercury-chlorinating agent to be added can be reduced with the mercury oxidation efficiency kept high.
When the catalyst for treating exhaust gas according to the present invention is used, only an addition of a considerably small amount of mercury oxidant suffices for an HCl/HBr spray unit or an NH4Cl supply unit for oxidizing mercury. For this reason, flue corrosion due to highly corrosive HCl can be reduced.
Moreover, when exhaust gas contains several tens ppm of HCl originating from coal, it is not necessary to install an HCl spray unit. In that case, the facility cost for safety control measure of HCl requiring care in handling can be greatly reduced.
Therefore, the catalyst for treating exhaust gas according to the present invention can be used in the method for treating exhaust gas described in
| Number | Date | Country | Kind |
|---|---|---|---|
| 2008-045818 | Feb 2008 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2009/053573 | 2/26/2009 | WO | 00 | 4/28/2010 |