Patent Application
20070212591
The present invention relates to a catalyst layer for a solid polymer electrolyte fuel cell, to a method of producing the catalyst layer for a solid polymer electrolyte fuel cell, and to a solid polymer electrolyte fuel cell.
A solid polymer electrolyte fuel cell is expected to be a future energy-generation apparatus because the solid polymer electrolyte fuel cell has high energy conversion efficiency, is clean, and produces very little noise. In particular, the solid polymer electrolyte fuel cell has recently been used not only as a generator for automobiles and homes, but has also been installed into small electrical instruments such as cellular phones, laptop computers, and digital cameras because of its high energy density to possibly operate for a longer period of time than a conventional secondary battery, and has been attracting attention. However, cost reduction is required for a solid polymer electrolyte fuel cell used as a generator for automobiles and homes, and a catalyst usage is desirably reduced as a way for cost reduction. Practical application of a solid polymer electrolyte fuel cell as a generator for small electrical instruments requires a compact total system and improved power generation efficiency.
Conventionally, an attempt has been made at forming a catalyst into fine particles and supporting the catalyst on carbon particles or the like for three-dimensional dispersion, to thereby increase a surface area and improve catalyst utilization.
Meanwhile, another attempt has been made at forming a catalyst layer into a very small thickness of about several μm, to thereby facilitate substance transport. Further, a catalyst layer was gathered in a vicinity of an electrolyte membrane, to thereby increase an effective surface area of the catalyst.
In particular, in a case where a fuel cell is installed into small electrical instruments, the fuel cell itself needs to be small, and air is often supplied to an air electrode from air holes through natural diffusion (air breathing system) without use of a pump or a blower.
In this case, substance transport at the air electrode often becomes a reaction rate-limiting factor, and thickness reduction of a catalyst layer seems to be effective means. An example of a method of forming a thin catalyst layer involves deposition of Pt or the like on a surface of an electrolyte membrane through sputtering (see S. Y. Cha and W. M. Lee, “J. Electrochem. Soc.”, 146, 4055 (1999).
However, the membrane described in the above-mentioned publication is dense and has poor gas permeability. Further, an increased thickness presumably causes cracks in the catalyst layer through expansion and shrinkage of the electrolyte membrane. Attempts have been made at forming a catalyst layer on a surface of a carbon electrode through sputtering or metal plating. However, a rough surface of the carbon electrode inhibits numerous catalysts from becoming in contact with an electrolyte membrane, and high performance has not yet been obtained.
The present invention has been made in view of the above circumstances, and it is an object of the present invention to provide: a catalyst layer for a solid polymer electrolyte fuel cell having improved catalytic activity, and catalyst utilization by forming a dendritic structure in the catalyst layer, and improved substance transport performance in the catalyst layer; and a method of producing the same.
Further, another object of the present invention is to provide a solid polymer electrolyte fuel cell having stable characteristics at lost cost by using the catalyst layer having improved catalytic activity and catalyst utilization.
The present invention has been made through extensive studies for attaining the above-described objects, and has the following constructions.
That is, according to one aspect of the present invention, there is provided a catalyst layer for a solid polymer electrolyte fuel cell including: a solid polymer electrolyte membrane; an electrode; and a catalyst layer provided between the solid polymer electrolyte membrane and the electrode, characterized in that the catalyst layer includes: a catalyst with a dendritic structure; or a catalyst with a multilayer structure having at least one layer with the dendritic structure.
According to another aspect of the present invention, there is provided a catalyst layer for a solid polymer electrolyte fuel cell, characterized in that the catalyst with a dendritic structure or the catalyst with a multilayer structure having at least one layer with the dendritic structure is: platinum oxide; a composite oxide of platinum oxide and an oxide of a metal element except platinum; platinum obtained through reduction treatment of platinum oxide or the composite oxide; a multicomponent metal containing platinum; a-mixture of platinum and an oxide of a metal element except platinum; or a mixture of a multicomponent metal containing platinum and an oxide of a metal element except platinum.
According to another aspect of the present invention, there is provided a catalyst layer for a solid polymer electrolyte fuel cell, characterized in that the metal element except platinum is at least one metal selected from the group consisting of Al, Si, Ti, V, Cr, Fe, Co, Ni, Cu, Zn, Ge, Zr, Nb, Mo, Ru, Rh, Pd, Ag, In, Sn, Hf, Ta, W, Os, Ir, Au, La, Ce, and Nd.
According to another aspect of the present invention, there is provided a catalyst layer for a solid polymer electrolyte fuel cell, characterized in that the catalyst with a dendritic structure has a branch or branched piece with a width of 5 nm or more and 200 nm or less in a shorter direction.
According to another aspect of the present invention, there is provided a catalyst layer for a solid polymer electrolyte fuel cell, characterized in that the catalyst with a dendritic structure has a porosity of 30% or more and less than 95%.
According to another aspect of the present invention, there is provided a catalyst layer for a solid polymer electrolyte fuel cell, characterized in that the catalyst with a dendritic structure is preferably arranged on a catalyst support, and the catalyst support is one member selected from the group consisting of: a carbon support; a platinum-supported carbon support; platinum alloy-supported carbon (where, platinum alloy refers to alloy composed of platinum and at least one metal element selected from the group consisting of Ru, Co, Cr, Ni, Cu, Fe, V, Sn, Rh, In, Pd, and Ru); platinum black; a platinum fine particle layer; or a gold fine particle layer.
According to another aspect of the present invention, there is provided a method of producing the catalyst layer for a solid polymer electrolyte fuel cell, characterized by including forming a catalyst with a dendritic structure through reactive vacuum deposition.
According to another aspect of the present invention, there is provided a solid polymer electrolyte fuel cell, including: a solid polymer electrolyte membrane; a pair of electrodes; and catalyst layers each provided between the solid polymer electrolyte and the respective electrode, characterized in that at least one catalyst layer includes a catalyst with a dendritic structure, or a catalyst with a multilayer structure having at least one layer with the dendritic structure.
The present invention allows improvements on catalytic activity and catalyst utilization by forming a characteristic dendritic fine structure in a catalyst layer, and improvement on substance transport performance in the catalyst layer by reducing a thickness of the catalyst layer. Further, the present invention can provide a fuel cell at an advantageous manufacturing cost through a simple manufacturing method of reactive vacuum deposition such as reactive sputtering, reactive electron beam evaporation, or reactive ion plating.
According to the present invention, there is provided a catalyst layer for a solid polymer electrolyte fuel cell having improved catalytic activity and catalyst utilization by forming in the catalyst layer a dendritic structure or a multilayer structure having at least one layer with the dendritic structure, and improved substance transport performance in the catalyst layer.
Further, the present invention can provide a solid polymer electrolyte fuel cell having stable characteristics at lost cost by using the above-described catalyst layer.
In addition, a method of producing a catalyst layer, according to the present invention, can realize a catalyst layer for a solid polymer electrolyte fuel cell through a simple process at low cost and good reproducibility. The catalyst layer has a dendritic structure or a multilayer structure having at least one layer with the dendritic structure, and thus hardly cracks.
Hereinafter, preferable embodiments of a catalyst layer for a solid polymer electrolyte fuel cell of the present invention and a method of producing the catalyst layer for a solid polymer electrolyte fuel cell of the present invention will be specifically described with reference to the drawings. The materials, sizes, shapes, relative positions, and the like of component members described in the embodiments do not limit the scope of the present invention unless otherwise noted specifically. Similarly, a manufacturing method described below does not limit the scope of the present invention.
The catalyst layer 3 with a dendritic structure or with a multilayer structure having at least one layer with the dendritic structure is constituted by: a catalyst 4 with a dendritic structure or with a multilayer structure having at least one layer with the dendritic structure; and a catalyst support 5 for supporting the catalyst 4. An anode gas diffusion layer 6 and an anode (fuel electrode) 8 are arranged on an outer side of the anode catalyst layer 2.
A cathode gas diffusion layer 7 and a cathode (air electrode) 9 are arranged on an outer side of the cathode catalyst layer 3 with a dendritic structure or with a multilayer structure having at least one layer with the dendritic structure.
The solid polymer electrolyte membrane 1 may preferably employ a perfluorosulfonic acid polymer with a structure in which a side chain having a sulfonic group on a terminal is bonded to a fluorocarbon skeleton. For example, a polymer in which a sulfonic group is bonded to Teflon (trade name) may preferably be used. To be specific, Nafion (trade name) may preferably be used.
The perfluorosulfonic acid polymer has no crosslinked fluorocarbon skeletons, and the skeletons are bonded together by van der Waals force to form a crystal. Further, several sulfonic groups are aggregated to form a reversed micelle structure, which serves as a proton H+ conduction channel.
In a case where protons H+ migrate through the electrolyte membrane toward the cathode, the protons H+ migrate using water molecules as a medium and the electrolyte membrane must have a function of holding water molecules. Thus, the solid polymer electrolyte membrane must have functions of: transferring protons H+ generated by the anode to the cathode; inhibiting passage of unreacted reaction gases (hydrogen and oxygen); and holding water to a predetermined level. An arbitrary electrolyte membrane may be selected and used as long as the above conditions are satisfied.
The gas diffusion layers 6 and 7 each serve to: supply a fuel gas or air to an electrode reaction region in the catalyst layer of the fuel electrode or air electrode sufficiently and uniformly across the surface of electrode reaction region; emit charges generated through an anode reaction out of the unit cell; and efficiently discharge reaction product water or unreacted gas out of the unit cell. An example of the gas diffusion layer that can preferably be used includes a porous member having electrical conductivity such as carbon cloth or carbon paper.
The catalyst support 5 serves to improve catalytic activity as a promoter, retain a form of the catalyst 4 with a dendritic structure, secure an electron conduction channel, increase a specific surface area, and the like. Examples of the catalyst support 5 that can preferably be used include carbon black, platinum-supported carbon, platinum alloy-supported carbon (where, platinum alloy refers to alloy composed of platinum and at least one metal element selected from the group consisting of Ru, Co, Cr, Ni, Cu, Fe, V, Sn, Rh, In, Pd, and Ru), platinum black, a platinum fine particle layer, and a gold fine particle membrane layer.
In general, an interface between a catalyst and an electrolyte must be sufficiently large and passage of electrode reaction substances (reaction gas, hydrogen gas, and electrons) must be favorable, that is, a three-phase interface must be formed effectively for obtaining a high performance catalyst layer. The catalyst 4 with a dendritic structure of the present invention has such features in that: an electrolyte channel and an electron conduction channel are secured while pores are formed along a direction of the electron conduction channel by providing a dendritic form to the catalyst; and a sufficient gas channel can be secured.
A branch or branched piece of the catalyst with a dendritic structure has such a feature in that its length is 5 nm or more and 200 nm or less in a shorter direction. Here, the length in a shorter direction refers to the minimum size of the branch or branched piece. Note that, the branch or branched piece does not necessarily need to be in a form of a branch or piece, and refers to a basic unit structure constituting a dendritic shape having branch points.
The catalyst 4 with a dendritic structure or with a multilayer structure having at least one layer with the dendritic structure has such a feature in that its porosity is 30% and more and less than 95%, preferably 55% to 75%. Note that, the porosity is calculated by (1-(actual volume of catalyst with dendritic structure)/(volume of space between electrolyte membrane and catalyst support)).
Further, the catalyst support-has a thickness of 200 nm or less, preferably 50 nm or less.
In
Increase in substrate temperature during deposition accelerates crystallization of platinum oxide during deposition to reduce a branch density of the dendritic form, resulting in long branches or pieces of the individual dendritic structures. The porosity and pore size of the dendritic catalyst layer may be controlled by using the phenomenon. In particular, the branch or piece of the dendritic structure tends to extend significantly at 85° C. or higher, corresponding to ⅕ of a melting point of platinum oxide. In order to obtain the desired dendritic structure, the substrate temperature may be maintained constant during deposition or may be varied during deposition. To be specific, an operation involving varying of the substrate temperature during deposition, that is, an operation involving deposition at about room temperature once and then increase in substrate temperature to 85° C. or higher, or an operation involving simultaneous annealing from 85° C. or higher and deposition may be performed appropriately. Thus, the pore size and porosity of the catalyst layer may have a desired distribution with respect to a thickness direction.
The catalyst with a dendritic structure shown in
The catalyst 4 with a dendritic structure is composed of: platinum oxide; a composite oxide of platinum oxide and an oxide of a metal element except platinum; platinum obtained through reduction treatment of platinum oxide or the composite oxide; a multicomponent metal containing platinum; a mixture of platinum and an oxide of a metal element except platinum; or a mixture of a multicomponent metal containing platinum and an oxide of a metal element except platinum. The metal element except platinum may be at least one metal selected from the group consisting of Al, Si, Ti, V, Cr, Fe, Co, Ni, Cu, Zr, Nb, Mo, Ru, Rh, Pd, Ag, In, Sn, Hf, Ta, W, Os, Ir, Au, La, Ce, and Nd.
The upper limit and lower limit of a composition ratio between platinum and the metal element except platinum cannot be defined uniquely, but improvement in catalytic activity can be confirmed with a content of the metal element except platinum of about 1 atomic %. A content thereof is preferably 3 to 80 atomic %, and significant reduction in catalytic activity is confirmed with a content thereof exceeding 80 atomic %.
In a case where a catalyst layer of the present invention is composed of a composite oxide of platinum oxide and an oxide of a metal element except platinum, platinum obtained through reduction treatment of the composite oxide, a multicomponent metal containing platinum, a mixture of platinum and an oxide of a metal element except platinum, or a mixture of a multicomponent metal containing platinum and an oxide of a metal element except platinum, the deposition preferably involves: an operation (1) for providing a layer of platinum oxide; and then an operation (2) for providing a composite layer, multicomponent metal layer, or mixture layer repeated at least once. In this way, a dendritic form may preferably be formed in the catalyst layer. A deposition time for each of the operations (1) and (2), and a ratio of the deposition times may be arbitrarily controlled, to thereby obtain the desired dendritic catalyst layer.
The catalyst 4 with a dendritic structure may be produced easily through vapor evaporation in a broad sense such as reactive sputtering, reactive electron beam evaporation, or reactive ion plating. For example, in order to produce platinum oxide PtOx with a dendritic structure through reactive sputtering, Ar and O2 gases are introduced for sputtering a platinum target, to thereby form platinum oxide with a dendritic structure.
Further, in order to produce a composite oxide PtMlx1M2x2 . . . MnxnOy (Σn=1 . . . n=0.3 to 0.8) with a dendritic structure containing platinum, Ar and O2 gasses are introduced for sputtering a platinum-M1- . . . -Mn alloy target, to thereby form a composite oxide with a dendritic structure containing platinum.
The reasons for formation of a dendritic structure in platinum oxide or in a composite oxide of platinum oxide and an oxide of a metal element except platinum relate to both deposition conditions such as oxygen partial pressure, input power, and substrate temperature, and surface roughness of the substrate. A case where those conditions are not satisfied results in a plate structure, an aggregated form of fine particles, or a dense columnar structure with substantially no pores.
In the present invention, the surface roughness of the substrate is preferably in a 0.1 to 10 micron order. The level of the surface roughness of the substrate is more preferably in an order of 0.1 to 10 times that of the thickness of platinum oxide or composite oxide of platinum oxide and an oxide of a metal element except platinum to be formed.
Various methods may be employed as a method of producing a solid polymer electrolyte fuel cell having a catalyst layer containing a catalyst with a dendritic structure of the present invention or with a multilayer structure having at least one layer with the dendritic structure. Hereinafter, a method of producing a solid polymer electrolyte fuel cell having a construction shown in
(1) A cathode dendritic catalyst layer is prepared.
Au as a catalyst support is deposited through electron beam evaporation on a polytetrafluoroethylene (PTFE) sheet as a transfer layer to a solid polymer electrolyte membrane. Then, a platinum oxide catalyst with a dendritic structure is formed thereon through reactive sputtering. Subsequently, the platinum oxide catalyst with a dendritic structure is subjected to hydrogen reduction treatment, to thereby obtain a platinum/gold catalyst layer with a dendritic structure.
Then, a mixed suspension of PTFE and Nafion (trade name: Nafion, available from Dupont) is applied onto the platinum/gold catalyst layer with a dendritic structure for effective formation of an electrolyte channel on a catalyst surface and appropriate water repellent treatment.
(2) An anode catalyst layer is prepared.
A platinum-supported carbon catalyst is formed in the same manner as in the step (1) on a PTFE sheet by using a doctor blade. A catalyst slurry to be used here is a kneaded product of platinum-supported carbon (trade name: HiSPEC 4000, available from Johnson Matthey Plc), Nafion, PTFE, IPA (2-ethanol), and water.
(3) A solid polymer electrolyte membrane (trade name: Nafion 112, available from Dupont) is sandwiched by a pair of catalyst layers produced in the steps (1) and (2) such that the PTFE sheets are on the outer sides, and the whole is subjected to hot pressing. Then, the) PTFE sheets are peeled off, resulting in an assembly of the electrolyte membrane and the pair of catalyst layers obtained by transferring the pair of catalyst layers onto the solid polymer electrolyte membrane and assembling the electrolyte membrane and the pair of catalyst layers.
(4) The assembly is sandwiched by a carbon cloth (trade name: LT1400-W, available from E-TEK Div. of De Nora N.A., Inc.) as gas diffusion layers, and further sandwiched by a fuel electrode and an air electrode, to thereby produce a unit cell.
The present invention is not limited to a solid polymer electrolyte fuel cell having a construction of a unit cell as described above, and also includes a solid polymer electrolyte fuel cell having a construction produced by stacking a plurality of unit cells.
Next, the present invention will be described in more detail with reference to specific examples.
Example 1 shows an example of manufacturing a solid polymer electrolyte fuel cell having a construction shown in
Hereinafter, detailed description will be made of manufacturing steps of the solid polymer electrolyte fuel cell according to Example 1.
(Step 1)
In Step 1, a dendritic catalyst layer of the present invention was produced.
A gold fine particle layer as a catalyst support was formed to a thickness of 50 nm through electron beam evaporation on a PTFE sheet (NITOFLON, available from Nitto Denko Corporation) as a transfer layer to a polymer electrolyte membrane. Further, a platinum oxide catalyst with a dendritic structure was formed thereon to a thickness of 1,000 nm through reactive sputtering. The platinum oxide catalyst had a porosity of 55%. At this time, an amount of Pt supported was 0.34 mg/cm2. The reactive sputtering was performed under the conditions of: a total pressure of 4 Pa; an oxygen flow ratio (QO2/(QAr+QO2)) of 70%; a substrate temperature of 80° C.; and an input power of 4.9 W/cm2.
A mixed suspension of PTFE and Nafion was applied thereon for effective formation of an electrolyte channel on a catalyst surface and appropriate water repellent treatment.
(Step 2)
In Step 2, a platinum-supported carbon catalyst layer was produced as a catalyst layer pairing with the catalyst layer with a dendritic structure produced in Step 1.
A platinum-supported carbon catalyst was formed on a PTFE sheet as a transfer layer to a polymer electrolyte membrane by using a doctor blade. A catalyst slurry to be used here was a kneaded product of platinum-supported carbon (trade name: HiSPEC 4000, available from Johnson Matthey Plc), Nafion, PTFE, IPA, and water. At this time an amount of Pt supported was 0.35 mg/cm2. The platinum-supported carbon catalyst layer had a thickness of about 30 μm.
(Step 3)
A solid polymer electrolyte membrane (Nafion 112, available from Dupont) was sandwiched by the pair of catalyst layers produced in Steps 1 and 2, and the whole was subjected to hot pressing under pressing conditions of 8 MPa, 150° C., and 1 minute.
The PTFE sheets were peeled off, resulting in transfer of the pair of catalyst layers onto the polymer electrolyte membrane and assembly of the electrolyte membrane and the pair of catalyst layers.
(Step 4)
The dendritic catalyst layer of the present invention was used as a cathode catalyst layer, and the platinum-supported carbon catalyst layer was used as an anode catalyst layer. The assembly was sandwiched by a carbon cloth (trade name: LT1200-W, available from E-TEK Div. of De Nora N.A., Inc.) as gas diffusion layers, and further sandwiched by a fuel electrode and an air electrode, to thereby form a unit cell.
The unit cell produced through the above-described steps was subjected to characteristic evaluation by using evaluation equipment having a construction shown in
First, .a current density of the unit cells was compared at 900 mV, which falls within a reaction rate-limiting region, resulting in 4.5 mA/cm2 for Example 1 and 2.0 mA/cm2 for Comparative Example 1. The current density was divided by the amount of Pt supported, to provide a specific catalytic activity. The specific catalytic activity of the unit cells was compared, resulting in 13.2 A/g for Example 1 and 5.7 A/g for Comparative Example 1.
The current density of the unit cells was compared in a limiting current region, resulting in 600 mA/cm2 or more for Example 1 and 520.mA/cm2 for Comparative Example 1. That is, the catalyst layer of Example 1 had improved substance transport performance in the catalyst layer compared with that of the catalyst layer of Comparative Example 1, and thus deterioration of fuel cell characteristics due to diffusion polarization was significantly suppressed.
Example 2 shows an example of a solid polymer electrolyte fuel cell having a construction shown in
Hereinafter, detailed description will be made of only Step 1 of the manufacturing step of the solid polymer electrolyte fuel cell according to Example 2, which differs in construction and manufacturing method from those of Example 1.
(Step 1)
In Step 1, a dendritic catalyst layer of the present invention was produced.
A gold fine particle layer as a catalyst support was formed to a thickness of 50 nm through electron beam evaporation on a PTFE sheet (NITOFLON, available from Nitto Denko Corporation) as a transfer layer to a polymer electrolyte membrane. Further, a platinum oxide catalyst with a dendritic structure was formed thereon to a thickness of 1,000 nm through reactive sputtering. At this time, an amount of Pt supported was 0.27 mg/cm2. The reactive sputtering was performed under the conditions of: a total pressure of 4 Pa; an oxygen flow ratio (QO2/(QAr+QO2)) of 70%; a substrate temperature of 80° C.; and an input power of 4.9 W/cm2. Subsequently, the platinum oxide catalyst with a dendritic structure was subjected to reduction treatment at 120° C. for 30 minutes in a 2% H2/He atmosphere (1 atm), to thereby obtain a platinum/gold catalyst layer with a dendritic structure on a PTFE sheet.
Then, a mixed suspension of PTFE and Nafion was applied thereon for effective formation of an electrolyte channel on a catalyst surface and appropriate water repellent treatment.
The subsequent steps were performed in the same manner as in Example 1, to thereby form a unit cell.
The unit cell produced through the above-described steps was subjected to characteristic evaluation by using evaluation equipment having a construction shown in
First, a current density of the unit cells was compared at 900 mV, which falls within a reaction rate-limiting region, resulting in 6.8 mA/cm2 for Example 2 and 2.0 mA/cm2 for Comparative Example 1. The current density was divided by the amount of Pt supported, to provide a specific catalytic activity. The specific catalytic activity of the unit cells was compared, resulting in 25.3 A/g for Example 2 and 5.7 A/g for Comparative Example 1. That is, the catalyst layer of Example 2 had improved catalytic activity compared with-that of the catalyst layer of Comparative Example 1.
The current density of the unit cells was compared in a limiting current region, resulting in 600 mA/cm2 or more for Example 2 and 520 mA/cm2 for Comparative Example 1. That is, the catalyst layer of Example 2 had improved substance transport performance in the catalyst layer compared with that of the catalyst layer of Comparative Example 1, and thus deterioration of fuel cell characteristics due to diffusion polarization was significantly suppressed.
Example 3 shows an example of manufacturing a solid polymer electrolyte fuel cell having a construction shown in
Hereinafter, detailed description will be made of manufacturing steps of the solid polymer electrolyte fuel cell according to Example 3.
(Step 1)
In Step 1, a dendritic catalyst layer of the present invention was produced.
A platinum oxide catalyst with a dendritic structure was formed on a gas diffusion layer (LT1400-W, available from E-TEK Div. of De Nora N.A., Inc.) having carbon black applied thereon in advance. An anode catalyst was formed to a thickness of 20 nm, and a cathode catalyst was-formed to a thickness of 1,000 nm. At this time, an amount of Pt supported was 0.01 mg/cm2 for the anode catalyst, and 0.34 mg/cm2 for the cathode catalyst. The reactive sputtering was performed under the conditions of: a total pressure of 4 Pa; an oxygen flow ratio (QO2/(QAr+QO2)) of 70%; and an input power of 4.9 W/.cm2. Subsequently, the platinum oxide catalyst with a dendritic structure was subjected to reduction treatment at 120° C. for 30 minutes in a 2% H2/He atmosphere (1 atm), to thereby obtain a platinum catalyst layer with a dendritic structure on a gas diffusion layer.
Then, the resultant was impregnated with a mixed suspension of PTFE and Nafion for effective formation of an electrolyte channel on a catalyst surface and appropriate water repellent treatment. (Step 2)
A solid polymer electrolyte membrane (Nafion 112, available from Dupont) was sandwiched by the pair of gas diffusion layers each having a dendritic catalyst produced in Step 1, and the whole was subjected to hot pressing under pressing conditions of 3 MPa, 150° C., and 1 minute, to thereby produce a polymer electrolyte membrane-catalyst electrode assembly including the gas diffusion layers.
(Step 3)
The membrane-electrode assembly produced in Step 2 was sandwiched by a fuel electrode and an air electrode, to thereby form a unit cell.
The unit cell produced through the above-described steps was subjected to characteristic evaluation by using evaluation equipment having a construction shown in
First, a current density of the unit cells was compared at 900 mV, which falls within a reaction rate-limiting region, resulting in 4.1 mA/cm2 for Example 3 and 2.0 mA/cm2 for Comparative Example 1. The current density was divided by the amount of Pt supported, to provide a specific catalytic activity. The specific catalytic activity of the unit cells was compared, resulting in 12.1 A/g for Example 3 and 5.7 A/g for Comparative Example 1.
The current density of the unit cells was compared in a limiting current region, resulting in 600 mA/cm2 or more for Example 3 and 520 mA/cm2 for Comparative Example 1. That is, in the catalyst layer of Example 3 deterioration of fuel cell characteristics due to resistance polarization and diffusion polarization was significantly suppressed compared with that in the catalyst layer of Comparative Example 1.
Example 4 shows an example of a solid polymer electrolyte fuel cell having a construction shown in
Hereinafter, detailed description will be made of only Step 1 and Step 2 of the manufacturing steps of the solid polymer electrolyte fuel cell according to Example 1 as Step 1 of Example 4, which differ in construction and manufacturing method from those of Example 1.
(Step 1)
In Step 1, a dendritic catalyst layer of the present invention was produced.
A platinum oxide catalyst with a dendritic structure was formed on a PTFE sheet having a platinum-supported carbon catalyst (20% Pt on Vulcan XC-72, available from available from E-TEK Div. of De Nora N.A., Inc.) applied thereon. An anode catalyst was formed to a thickness of 20 nm, and a cathode catalyst was formed to a thickness of 1,000 nm. At this time, an amount of Pt supported was 0.01 mg/cm2 for the anode catalyst, and 0.54 mg/cm2 for the cathode catalyst. The reactive sputtering was performed under the conditions of: a total pressure of 4 Pa.; an oxygen flow ratio (QO2/(QAr+QO2)) of 70%;. and an input power of 4.9 W/cm2. Subsequently, the platinum oxide catalyst with a dendritic structure was subjected to reduction treatment at 120° C. for 30 minutes in a 2% H2/He atmosphere (1 atm), to thereby obtain a platinum catalyst layer with a dendritic structure on a PTFE sheet.
Then, the resultant was impregnated with a mixed suspension of PTFE and Nafion for effective formation of an electrolyte channel on a catalyst surface and appropriate water repellent treatment.
The unit cell produced through the above-described steps was subjected to characteristic evaluation by using evaluation equipment having a construction shown in
First, a current density of the unit cells was compared at 900 mV, which falls within a reaction rate-limiting region, resulting in 6.5 mA/cm2 for Example 4 and 2.0 mA/cm for Comparative Example 1. The current density was divided by the amount of Pt supported, to provide a specific catalytic activity. The specific catalytic activity of the unit cells was compared, resulting in 12.0 A/g for Example 4 and 5.7 A/g for Comparative Example 1.
The current density of the unit cells was compared in a limiting current region, resulting in 600 mA/cm2 or more for Example 4 and 520 mA/cm2 for Comparative Example 1. That is, in the catalyst layer of Example 4 deterioration of fuel cell characteristics due to resistance polarization and diffusion polarization was significantly suppressed compared with that in the catalyst layer of Comparative Example 1.
Example 5 shows an example of manufacturing a solid polymer electrolyte fuel cell having a construction shown in
(Step 1)
In Step 1, a dendritic catalyst layer of the present invention was produced.
A gold thin film was formed to a thickness of 50 nm through electron beam vacuum evaporation on a PTFE sheet (NITOFLON, available from Nitto Denko Corporation) as a transfer layer to a polymer electrolyte membrane. Further, a platinum oxide catalyst with a dendritic structure shown in
Subsequently, the catalyst with a dendritic structure was subjected to reduction treatment at 120° C. for 30 minutes in a 2% H2/He atmosphere at 0.1 MPa (1 atm), to thereby obtain a dendritic catalyst layer having a structure shown in
Then, an appropriate amount of a Nafion solution (5 wt %, available from Wako Pure Chemical Industries, Ltd.) was dropped onto the obtained catalyst layer, and a solvent was evaporated in vacuum, to thereby form an electrolyte channel on a catalyst surface.
(Step 2)
In Step 2, a platinum black catalyst layer was produced as a catalyst layer pairing with the catalyst layer produced in Step 1.
A platinum black catalyst layer was formed on a PTFE sheet as a transfer layer to a polymer electrolyte membrane by using a doctor blade. A catalyst slurry to be used here is a kneaded product of platinum black (trade name: HiSPEC 1000, available from Johnson Matthey Plc), Nafion, IPA, and water. At this time, an amount of Pt supported was 4.96 mg/cm2, and the catalyst layer had a thickness of about 30 μm.
The subsequent steps were performed in the same manner as in Example 1, to thereby form a unit cell.
The unit cell produced through the above-described steps was subjected to characteristic evaluation by using evaluation equipment having a construction shown in
First, a current density of the unit cells was compared at 900 mV, which falls within a reaction rate-limiting region, resulting in 6.0 mA/cm2 for Example 5 and 2.0 mA/cm2 for Comparative Example 2. The current density was divided by the amount of Pt supported, to provide a specific catalytic activity. The specific catalytic activity of the unit cells was compared, resulting in 17.1 A/g for Example 5 and 5.7 A/g for Comparative Example 2. That is, the catalyst layer of Example 5 had improved catalytic activity compared with that of the catalyst layer of Comparative Example 2.
The current density of the unit cells was compared in a limiting current region, resulting in 980 mA/cm2 or more for Example 5 and 520 mA/cm2 for Comparative Example 2.
That is, the catalyst layer of Example 5 had large pores as shown in
Example 6 shows an example of a solid polymer electrolyte fuel cell having a construction shown in
Hereinafter, detailed description will be made of only Step 1 of the manufacturing step of the solid polymer electrolyte fuel cell according to Example 6, which differs in construction and manufacturing method from those of Example 1.
(Step 1)
In Step 1, a catalyst layer with a multilayer structure having at least one layer with a dendritic structure of the present invention was produced.
A gold fine particle layer as a catalyst support was formed to a thickness of 50 nm through electron beam evaporation on a PTFE sheet (NITOFLON, available from Nitto Denko Corporation) as a transfer layer to a polymer electrolyte membrane. Further, a platinum oxide catalyst layer with a dendritic structure was formed thereon to a thickness of 500 nm through reactive sputtering. Furthermore, a composite oxide layer of platinum oxide and copper oxide was formed thereon to a thickness of 500 nm through simultaneous reactive sputtering of platinum and copper to an atomic % ratio of platinum to copper of 93:7. At this time, a total amount of Pt supported was, 0.34 mg/cm2. The reactive sputtering was performed under the conditions of: a total pressure of 4 Pa for each layer; an oxygen flow ratio (QO2/(QAr+QO2)) of 70%; a substrate temperature of 80° C.; and an input power of 4.9 W/cm2. Subsequently, the obtained two-layer platinum oxide catalyst having one layer with a dendritic structure was subjected to reduction treatment at 120° C. for 30 minutes in a 2% H2/He atmosphere.(1 atm), to thereby obtain a platinum-copper oxide/platinum/gold catalyst layer having one layer with a dendritic structure on a PTFE sheet.
Then, a mixed suspension of PTFE and Nafion was applied thereon for effective formation of an electrolyte channel on a catalyst surface and appropriate water repellent treatment.
The subsequent steps were performed in the same manner as in Example 1, to thereby form a unit cell.
The unit cell produced through the above-described steps was subjected to characteristic evaluation by using evaluation equipment having a construction shown in
First, a current density of the unit cells was compared at 900 mV, which falls within a reaction rate-limiting region, resulting in 6.8 mA/cm2 for Example 6 and 2.0 mA/cm for Comparative Example 1. The current density was divided by the amount of Pt supported, to provide a specific catalytic activity. The specific catalytic activity of the unit cells was compared, resulting in 20.0 A/g for Example 6 and 5.7 A/g for Comparative Example 1. That is, the catalyst layer of Example 6 had improved catalytic activity compared with that of the catalyst layer of Comparative Example 1.
The current density of the unit cells was compared in a limiting current region, resulting in 600 mA/cm2 or more for Example 6 and 520 mA/cm2 for Comparative Example 1 That is, the catalyst layer of Example 6 had improved substance transport performance in the catalyst layer compared with that in the catalyst layer of Comparative Example 1, and thus deterioration of fuel cell characteristics due to diffusion polarization was significantly suppressed.
Example 7 shows an example of manufacturing a solid polymer electrolyte fuel cell having a construction shown in
Hereinafter, detailed description will be made of only step of the manufacturing step of the solid polymer electrolyte fuel cell according to Example 7, which differ in construction and manufacturing method from those of Example 5.
(Step 1)
In Step 1, a composite oxide catalyst layer with a dendritic structure of the present invention was produced.
A gold thin film was formed to a thickness of 50 nm through electron beam vacuum evaporation on a PTFE sheet (NITOFLON, available from Nitto Denko Corporation) as a transfer layer to a polymer electrolyte membrane. Further, a platinum oxide layer and a platinum oxide-copper oxide composite layer were alternatively and repeatedly deposited thereon through reactive sputtering, to thereby form a dendritic composite oxide catalyst layer having a thickness of 4.2 μm. Each platinum oxide layer was deposited to a thickness of 10 nm, and each composite oxide layer was deposited to a thickness of 30 nm. The reactive sputtering was performed under the conditions of: a total pressure of 5 Pa; an oxygen flow ratio (QO2/(QAr+QO2)) of 70%; a substrate temperature of 25° C.; an RF input power for the Pt cathode of 3.6 W/cm2; and an RF input power for the Cu cathode of 8.7 W/cm2. The results of XPS and EDX analyses confirmed that the dendritic composite oxide catalyst was composed of a composite of platinum oxide and CuO with a molecule number ratio of about 77 to 23.
Subsequently, the dendritic composite oxide catalyst was subjected to reduction treatment at 120° C. for 30 minutes in a 2% H2/He atmosphere at 0.1 MPa (1 atm), to thereby obtain a dendritic composite metal catalyst layer having a structure shown in
Then, an appropriate amount of a Nafion solution (5 wt %, available from Wako Pure Chemical Industries, Ltd.) was dropped onto the obtained catalyst layer, and a solvent was evaporated in vacuum, to thereby form an electrolyte channel on a catalyst surface.
The subsequent steps were performed in the same manner as in Example 5, to thereby form a unit cell.
The unit cell produced through the above-described steps was subjected to characteristic evaluation by using evaluation equipment having a construction shown in
First, a current density of the unit cells was compared at 900 mV, which falls within a reaction rate-limiting region, resulting in 14.2 mA/cm2 for Example 7 and 8.1 mA/cm2 for Comparative Example 3. The current density was divided by the amount of Pt supported, to provide a specific catalytic activity. The specific catalytic activity of the unit cells was compared, resulting in 8.87 A/g for Example 7 and 1.63 A/g for Comparative Example 3. That is, in the dendritic composite metal catalyst layer of Example 7, deterioration of fuel cell characteristics due to activation polarization was significantly suppressed compared with that in the catalyst layer of Comparative Example 3. Further, the dendritic composite metal catalyst layer of Example 7 had improved catalyst utilization compared with that of the catalyst layer of Comparative Example 3. Thus, comparable current was obtained with the dendritic composite metal catalyst layer of Example 7 although an amount of Pt supported was about ⅓ of that of Comparative Example 3.
The current density of the unit cells was compared in a limiting current region, resulting in 650 mA/cm2 or more for Example 7, which was comparable to that of Comparative Example 3.
Example 8 shows an example of a solid polymer electrolyte fuel cell having a construction shown in
Hereinafter, detailed description will be made of only step of the manufacturing step of the solid polymer electrolyte fuel cell according to Example 8, which differs in construction and manufacturing method from those of Example 5.
(Step 1)
A gold thin film was formed to a thickness of 50 nm through electron beam vacuum evaporation on a PTFE sheet (NITOFLON, available from Nitto Denko Corporation) as a transfer layer to a polymer electrolyte membrane. Further, a platinum oxide layer and a platinum oxide-copper oxide composite layer were alternatively and repeatedly deposited thereon through reactive sputtering, to thereby form a dendritic composite oxide-catalyst layer shown in
Subsequently, the dendritic composite oxide catalyst was subjected to reduction treatment at 120° C. for 30 minutes in a 2% H2/He atmosphere at 0.1 MPa (1 atm), to thereby obtain a dendritic composite metal catalyst layer on a PTFE sheet. No great changes were observed before and after the reduction treatment. The results of XPS and EDX analyses confirmed that the dendritic composite metal catalyst was composed of a composite metal of Pt and Cu with an atom number ratio of about 73 to 27. An amount of Pt supported was 0.36 mg/cm2, and the catalyst layer had a porosity of 76.5%. Then, an appropriate amount of a Nafion solution (5 wt %, available from Wako Pure Chemical Industries, Ltd.) was dropped onto the obtained catalyst layer, and a solvent was evaporated in vacuum, to thereby form an electrolyte channel on a catalyst surface.
The subsequent steps were performed in the same manner as in Example 5, to thereby form a unit cell.
The unit cell produced through the above-described steps was subjected to characteristic evaluation by using evaluation equipment having a construction shown in
First, a current density of the unit cells was compared at 900 mV, which falls within a reaction rate-limiting region, resulting in 7.5 mA/cm2 for Example 8 and 2.0 mA/cm2 for Comparative Example 2. The current density was divided by the amount of Pt supported, to provide a specific catalytic activity. The specific catalytic activity of the unit cells was compared, resulting in 20.7 A/g for Example 8 and 5.7 A/g for Comparative Example 2. That is, the catalyst layer of Example 8 had improved catalytic activity compared with that of the catalyst layer of Comparative Example 2.
The current density of the unit cells was compared in a limiting current region, resulting in 600 mA/cm2 or more for Example 8, and 520 mA/cm2 for that of Comparative Example 2.
That is, the catalyst layer of Example 8 had improved substance transport performance in the catalyst layer compared with that of the catalyst layer of Comparative Example 2, and thus deterioration of fuel cell characteristics due to diffusion polarization was significantly suppressed.
Example 9 shows an example of a solid polymer electrolyte fuel cell having a construction shown in
Hereinafter, detailed description will be made of only Step 1 of the manufacturing step of the solid polymer electrolyte fuel cell according to Example 9, which differs in construction and manufacturing method from those of Example 1.
(Step 1)
In Step 1, a dendritic catalyst layer of the present invention was produced.
A gold fine particle layer as catalyst support was formed to a thickness of 50 nm through electron beam evaporation on a PTFE sheet (NITOFLON, available from Nitto Denko Corporation) as a transfer layer to a polymer electrolyte membrane. Further, a platinum oxide catalyst with a dendritic structure shown in
Then, a mixed suspension of PTFE and Nafion was applied thereon for effective formation of an electrolyte channel on a catalyst surface and appropriate water repellent treatment.
The subsequent steps were performed in the same manner as in Example 1, to thereby form a unit cell.
The unit cell produced through the above-described steps was subjected to characteristic evaluation by using evaluation equipment having a construction shown in
First, a current density of the unit cells was compared at 900 mV, which falls within a reaction rate-limiting region, resulting in 6.9 in A/cm2 for Example 9 and 2.0 mA/cm2 for Comparative Example 1. The current density was divided by the amount of Pt supported, to provide a specific catalytic activity. The specific catalytic activity of the unit cells was compared, resulting in 19.2 A/g for Example 9 and 5.7 A/g for Comparative Example 1. That is, the catalyst layer of Example 9 had improved catalytic activity compared with that of the catalyst layer of Comparative Example 1.
The current density of the unit cells was compared in a limiting current region, resulting in 800 mA/cm2 or more for Example 9 and 520 mA/cm2 for Comparative Example 1. That is, the catalyst layer of the Example 9 had improved substance transport performance in the catalyst layer compared with that in the catalyst layer of Comparative Example 1, and thus deterioration of fuel cell characteristics due to diffusion polarization was significantly suppressed.
As shown in Examples, a dendritic catalyst layer or catalyst layer with a multilayer structure having at least one layer with a dendritic structure of the present invention was used as a catalyst layer for a solid polymer electrolyte fuel cell, to thereby obtain a fuel cell having excellent fuel cell characteristics with improved catalytic activity and catalyst utilization, and improved substance transport performance. Further, a method of producing a dendritic catalyst layer or catalyst layer with a multilayer structure having at least one layer with a dendritic structure of the present invention involves a simple process at low cost and good reproducibility, to thereby realize a solid polymer electrolyte fuel cell having stable characteristics at low cost.
The dendritic catalyst layer or catalyst layer with a multilayer structure having at least one layer with the dendritic structure of the present invention has improved catalytic activity and catalyst utilization, and improved substance transport performance in the catalyst layer, and thus can be used as a catalyst layer for a solid polymer electrolyte fuel cell.
The solid polymer electrolyte fuel cell having the dendritic catalyst layer of the present invention can be used as a fuel cell for small electrical instruments such as cellular phones, laptop computers, and digital cameras.
This application claims priority from Japanese Patent Application Nos. 2004-194791 filed on Jun. 30, 2004 and 2005-158097 filed on May 30, 2005, which are hereby incorporated by reference herein.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2004-194791 | Jun 2004 | JP | national |
| 2005-158097 | May 2005 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP05/12163 | 6/24/2005 | WO | 12/4/2006 |