Catalyst system for deodorization and apparatus for deodorization using the same

Abstract

A catalyst system for deodorization and an apparatus for deodorization, each of which comprises a pretreating catalyst and a noble metal catalyst, the pretreating catalyst converting a sulfur atom of low oxidation state which deactivates the noble metal catalyst into a sulfur atom of high oxidation state which has little deactivation effects there on, the noble metal catalyst oxidizing aldehyde, etc., wherein a material to be deodorized is brought into contact with the pretreating catalyst prior to being brought into contact with the noble metal catalyst. As the pretreating catalyst, a catalyst comprising at least one selected from the group consisting of vanadium, chromium, manganese, iron, cobalt, nickel, copper and oxides thereof is used, while as the noble metal catalyst, a catalyst comprising at least one selected from the group consisting of ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum and gold is used. According to the catalyst system, a striking deodorizing-effect is provided to, in particular, a mixture of sulfur compounds of low oxidation state and compounds such as aldehydes or alcohols.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a catalyst for deodorization and a deodorizing apparatus using the same catalyst is used and in particular, relates to a catalyst for deodorization which provides an excellent deoderization effect to a mixture of sulfur compounds and compounds such as aldehydes, alcohols or hydrocarbon compounds, and an apparatus for deodorization using the same.

[0003] 2. Prior Art

[0004] Hitherto, noble metal catalysts in which platinum, palladium, or both platinum and palladium are supported on a proper support have been used as a catalyst for deodorization. These catalysts promote a reaction wherein a gas to be deodorized is oxidized and decomposed by oxygen in air so as to provide a deodorization effect, which are, in particular, effective on aldehydes, alcohols and hydrocarbon compounds.

[0005] However, These catalyst are deactivated by materials to be deodorized which contain sulfur compounds of low oxidation state such as dimethyl sulfide or methanethiol. Therefore, when such materials to be deodorized are contained, it is difficult to use these catalyst as the deordorization catalyst.

[0006] In case of materials to be deodorized which contain sulfur compounds, catalysts having an oxide of cobalt, manganese, etc. as an active component, which have relatively strong resistance against such materials are used. For example, Japanese Patent KOKAI(Laid-Open) No.31128/94 discloses a deodorant which comprises an oxide of cobalt and/or manganese, and zeolite. Furthermore, in Japanese Patent KOKAI Nos.47645/96 and 284670/95, a catalyst containing an activated manganese dioxide, a copper-supporting zeolite and copper oxide as an effective component is used so as to attempt a deodorization thereby. However, all of such catalysts provide some effects on the sulfur compounds, while insufficient or no effects on aldehydes, alcohols and the like.

[0007] On the other hand, gases, which are emitted from crude waste disposal machines, contain aldehydes, amines, alcohols and the like as well as we sulfur compounds, and therefore, it was impossible to treat such gases, with the conventional cataysts mentioned above.

SUMMARY OF THE INVENTION

[0008] It is, because a sulfur atom of dimethylsulfide or the like strongly adsorbs on active sites of the noble metal catalysts mentioned above, that these catalysts are deactivated by dimethylsulfide or the like. It has been found that the effect that the catalyst is deactivated by such an adsorption is remarkable in compounds which have a sulfur atom of low oxidation state, while such effect is little observed in a sulfur compound of high oxidation state. The present inventor has been found that prolongation of life of the noble metal catalyst and a high-efficient oxidative decomposition are realized by using in a combination of the noble metal catalyst and a catalyst which oxidizes compounds having a sulfur atom of low oxidation state such as dimethylsulfide to a high oxidation state such as sulfons.

[0009] It is an object of the present invention to provide a catalyst system which has an effective deodorization effect on materials to be deordorized which contain a compound such as aldehydes, alcohols, amines or hydrocarbon compounds, as well as sulfur compounds of low oxidation state.

[0010] It is another object of the present invention to provide an apparatus in which a catalyst system is arranged so that the catalyst system has an effective deodorization effect on materials to be deordorized which contain compounds such as aldehydes, alcohols, amines or of hydrocarbon compounds, as well as sulfur compounds of low oxidation state.

[0011] According to one aspect of the present invention, there is provided a catalyst system for deordorization, which comprises a pretreating catalyst and a noble metal catalyst, the pretreating catalyst being a catalyst for converting a sulfur compound of low oxidation state which is included in materials to be deordorized into a sulfur compound of high oxidation state, wherein the materials to be deordorized are brought into contact with the pretreating catalyst prior to being brought into contact with the noble metal catalyst.

[0012] According to another aspect of the present invention, there is provided an apparatus for deordorization which is provided with a catalyst tower inside which the pretreating catalyst is positioned upstream of channels for a gas to be deodorized, and the noble metal catalyst is positioned downstream of the channels, wherein the pretreating catalyst is the one for converting the sulfur compound of low oxidation state which is included in the gas to be deodorized into the sulfur compound of high oxidation state.

[0013] Furthermore, the catalyst system for drozination of the present invention is characterized by comprising the pretreating catalyst and the noble metal catalyst, the pretreating catalyst comprising at least one selected from the group consisting of vanadium, chromium, manganese, iron, cobalt, nickel, copper and oxides thereof, and the noble metal catalyst comprising at least one selected from the group consisting of ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum and gold.

[0014] In particular, the catalyst system for deordorization of the present invention preferably comprises the pretreating catalyst which contains manganese oxide(IV) and/or vanadium oxide(V), and the noble metal catalyst which contains palladium and/or platinum.

[0015] Further another aspect of the present invention relates to a use of the catalyst system which comprises the noble metal catalyst and the pretreating catalyst for deodorizing a malodorous gas containing materials which provides a deactivation effect on the noble metal catalyst, wherein the use comprises the steps of: bringing the gas to be deodorized which contains materials which provides the deactivation effect on the noble metal catalyst into contact with the pretreating catalyst prior to bringing the gas into contact with the noble metal catalyst so as to convert the gas into other materials having less deactivation effect; and then, bringing the gas into contact with the noble metal catalyst.

BRIEF EXPLANATION OF THE DRAWINGS

[0016] FIG. 1 is an explanation drawing which illustrates an example of the apparatus for deodorization of the present invention; and

[0017] FIG. 2 is an explanation drawing which illustrates another example of the apparatus for deodorization of the present invention.

PREFFERED MODES OF EMBODIMENT

[0018] As the pretreating catalyst in the present invention, a catalyst which comprises at least one selected from the group consisting of vanadium, chromium, manganese, iron, cobalt, nickel, copper, and oxides thereof is suitably used. The pretreating catalyst is constituted by an oxidation catalyst which has relatively strong resistance against compounds having a sulfur atom of low oxidation state, which takes a part to oxidize compounds containing a sulfur atom of low oxidation state such as disulfides to materials of high oxidation state such as sulfones. At this time, it is necessary to control the oxidation power thereof so that the compound can be requisitely and sufficiently oxidized to sulfone. According to the catalyst for deodorization of the present invention, the metals and their oxides which are included in the above group can be suitably selected or combined together depending upon the composition of a gas to be deodorized so as to control the oxidation power thereof. It is effective to use manganese oxide(IV) and/or vanadium oxide(V), in particular, when the pretreating catalyst comprising manganese oxide(IV) and 5 to 20% by weight of vanadium oxide(V) (the whole catalyst is represented as 100% by weight) is used, a catalyst which is effective on many gases to be deodorized can be realized. A manganese oxide(IV)-vanadium oxide(V) can be prepared according to various methods, for example, as follows. Namely, manganese oxide(IV) which is obtained by decomposing potassium permanganate with nitric acid and vanadium oxide(V) which is obtained by decomposing ammonium metavanadate at a temperature of 500° C. in an air flow are mixed in desired amounts, and said mixture is fired at a temperature of 200° C. in an oxygen flow so as to obtain a manganese oxide(IV)-vanadium oxide(V) of the present invention. Incidentally, a support is not necessary for this catalyst except special occasions. Furthermore, depending upon the use of the catalyst, the form of an apparatus, the flow rate of a gas to be deodorized or the like, the shape of the catalyst may be suitably selected from tablets, fine particles, honeycombs and the like.

[0019] The noble metal catalyst takes a part to oxidize aldehydes, alcohols, amines and hydrocarbon compounds, which is preferably selected from the group consisting of ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum and gold. Then the compound having sulfur atom of low oxidation state which causes the deactivation of the noble metal catalyst is oxidized by the pretreating catalyst so as to be converted into compounds having sulfur atom of high oxidation state such as sulfones which have little deactivation effects. Therefore the prolongation of life of the noble metal catalyst and a high-efficient oxidative decomposition can be realized. The noble metal catalyst can be suitably selected from metals which are contained in the group mentioned above, or can be obtained by a combination of said metals so as to increase deordorization efficiency. In particular, it has been confirmed that a catalyst which is effective to many different kinds of gases to be deodorized is realized by using platinum or gold. Furthermore, although a support for the noble metal catalyst is not particularly limited, for example, γ-alumina or the like can be used.

[0020] Thus, as a catalyst system for deororization is in combination of the pretreating catalyst to oxidize compounds containing sulfur atom of low oxidation state into sulfones, and the noble metal catalyst to oxidize aldehydes into carbon dioxide and water, the prolongation of life of the noble metal catalyst and a high-efficient oxidative decomposition can be realized, wherein as the use mode of the catalyst for deordorization of the present invention, the pretreating catalyst is desirably positioned upstream of channels for a gas to be deodorized, and the noble metal catalyst is desirably positioned downstream of the channels, because the compound including sulfur atom of low oxidation state can be effectively converted into sulfones by such an arrangement.

[0021] The catalyst system for deordorization of the present invention is effective on aldehydes, alcohols, amines, and hydrocarbon compounds, and furthermore effective on compounds which contain a sulfur atom of low oxidation state such as sulfides, disulfides or alkylthiols. In particular, the catalyst is effective on a mixture of the aldehyde compound and the sulfur compound.

[0022] The apparatus for deodorization of the present invention is characterized in that the pretreating catalyst and the pecious metal catalyst as mentioned above are arranged in series inside a catalytic reaction tower, wherein the pretreating catalyst is positioned upsteam of channels for a gas to be deodorized, while the pecious metal catalyst is positioned downsteam of the channels. If such conditions are satisfied, the form of a general catalytic reaction tower which has been used hitherto can be used as it is. As shown in FIG. 1, pretreating catalyst bed (5) is positioned upstream of gas to be deodorized (2) as shown by arrows, while noble metal catalyst bed (6) is positioned downstream thereof, wherein the catalyst beds (5) and (6) are properly spaced, provided that both catalysts are not mixed with each other, and a space between the catalyst beds (5) and (6) is not specifically limited. Heater (3) is positioned in the jacket of reaction tower (1). After treatment, deodorized gas (4) is removed.

[0023] Furthermore, as shown in FIG. 2, the pretreating catalyst bed (5) and the noble metal catalyst bed (6) can be arranged by bringing both catalyst beds (5) and (6) into contact with each other not to be mixed with each other. When a pellet-shaped catalyst is used, the boundary of both catalyst beds is preferably comparted by, for example, a wire netting. On the other hand, when at least one of both catalysts is a monolithic catalyst, for example, a catalyst which was formed in the shape of a honeycomb, the compartment therebetween is unnecessary because there is no possibility of both catalysts to be mixed with each other. Incidentally, the shape of the catalyst tower (1) does not specifically matter. Such a structure of the catalytic reaction tower can provide effective treatment on compounds including sulfur of low oxidation state which deactivate the noble metal catalyst, and furthermore can achieve the high efficiency of the catalyst and the prolongation of the life thereof.

[0024] Conditions for deodorizing the gas by using the catalyst for deodorization of the present invention are suitably selected according to the kind of the gas to be deodorized; for example, preferably the reaction temperature is in the range of 200° C. to 400° C. , and the space velocity (SV) is in the range of about 1000 to 10000 h−1. Furthermore, a contact system for bringing the gas to be deodorized into contact with the catalyst is preferably a fixed bed, while the contact system in which a fluidized bed or a moving bed is employed can be also used under such conditions that the pretreating catalyst and the noble metal catalyst are not mixed with each other.

EXAMPLES

[0025] Hereinafter, the present invention will be more specifically explained by the following examples.

Example 1

[0026] A catalyst system for deodorization of the present invention which comprises a pretreating catalyst and a noble metal catalyst was used, wherein the pretreating catalyst comprises manganese oxide(IV) and vanadium oxide(V) in an amount of 5% by weight (in which all of said catalysts was represented as 100% by weight), and the noble metal catalyst comprises a platinum-supporting alumina catalyst in which 1% of platinum is supported; and an apparatus for deodorization of the present invention is shown in FIG. 1, wherein a silica tube(having an inner diameter of 16 mm and a length of 500 mm) as catalyst tower (1), pretreating catalyst bed (5) and noble metal catalyst bed (6) are provided, wherein the silica tube was filled with the pretreating catalyst bed (5) having a volume of 10 cm3 and the noble metal catalyst bed (6) having a volume of 5 cm3, the pretreating catalyst bed (5) and the noble metal catalyst bed (6) being spaced about 2 cm apart; and thereby a simulated malodorous air including 10 ppm of dimethylsulfide and ethanal(acetaldehyde) having the same concentration was treated at a temperature of 3000 C under the condition of Sv/h−130000. 96% of Dimethylsulfide and 100% of ethanal were oxidized and removed, respectively. Although the treatment was carried on for a period of 100 hours, no deterioration in activation was observed.

Comparative Example 1

[0027] A treatment was carried out under the same conditions as that in Example 1 except that only the platinum-supporting alumina catalyst in which 1% of platinum is supported was used instead of the atalyst system for deodorization of the present invention. In the early stage of reaction, the removal ratio of dimethylsulf ide was 34%, while that of ethanal was 63%. According to measurements after the simulated malodorous air was passed through for a period of 100 hours, the removal ratio of dimethylsulfide was 2%, while that of ethanal was 9%.

Example 2

[0028] The same apparatus for deodorization as that used in Example 1 was filled with a catalyst system for deodorization of the present invention which comprises a pretreating catalyst and a noble metal catalyst, wherein the pretreating catalyst comprises manganese oxide(IV) and vanadium oxide(V ) in an amount of 20% by weight, the noble metal catalyst compris a platinum-palladium supporting alumina catalyst in which platinum and palladium were supported by 1.5%, respectively; and then a simulated malodorous air which includes 100 ppm of methanal(formaldehyde), trimethylamine in an amount of the same concentration, and 10 ppm of methanethiol was treated at a temperature of 300° C. under the condition of SV/h−1=30000. 99% of Methanal, 94% of trimethylamine and 97% of Methanethiol were oxidized and removed. Although the treatment was carried on for a period of 100 hours, no deterioration in activation was observed.

Example 3

[0029] The same apparatus for deodorization as that in Example 1 was filled with a catalyst system for deodorization of the present invention which comprises a pretreating catalyst and a noble metal catalyst, wherein the pretreating catalyst comprises manganese oxide(IV) and vanadium oxide(V) in an amount of 5% by weight, the noble metal catalyst comprises a palladium-supporting alumina catalyst in which 1.5% of palladium was supported; and then a simulated malodorous air which includes 330 ppm of acetic acid and 480 ppm of ethanal was treated at a temperature of 380° C. under the condition of SV/h−1=10000. Both acetic acid and ethanal were removed by 100%, respectively.

Comparative Example 2

[0030] When a treatment was carried out under the same conditions as that in Example 3 except that only manganese oxide(IV) containing 5% by weight of vanadium oxide(V) was used instead of the catalyst system of the present invention, the removal ratio of acetic acid was 61%, while that of ethanal was 48%. Furthermore, when the treatment was carried out under the same conditions as that in Example 3 except that only a palladium-supporting alumina catalyst in which 1.5% of palladium was supported was used instead of the catalyst system of the present invention, the removal ratio of acetic acid was 68% while that of ethanal was 78%. From these results, assuming that there is no synergistic effect of both catalysts, the removal ratio of acetic acid comes to about 88%, while that of ethanal comes to about 89%. On the other hand, since according to the catalyst system of the present invention, the removal ratios of acetic acid and ethanal are 100%, respectively, it is clear that a catalyst system of the present invention provides more excellent effects as compared with a mere combination of the effect of each individual catalyst, which shows that a material which provides a deactivation effect to the noble metal catalyst is converted into another material, thereby the deodorization efficiency of the noble metal catalyst is strikingly improved.

Example 4

[0031] The same apparatus for deodorization as that in Example 1 was filled with the catalyst system for deodorization of the present invention which comprises the pretreating catalyst and the noble metal catalyst, wherein the pretreating catalyst comprises manganese oxide(IV), 1% by weight of nickel oxide(II), and 5% by weight of vanadium oxide(V), the noble metal catalyst comprises a platinum-ruthenium supporting alumina catalyst in which platinum and ruthenium were supported by 2%, respectively; and then a simulated malodorous air which includes 100 ppm of dimethylsulfide, 100 ppm of methanethiol, 100 ppm of limonene and 100 ppm of ethanal was treated at a temperature of 400° C. under the condition of SV/h−1=10000. 98% of Dimethylsulfide, 93% of methanethiol, 99% of limonene and 99% of ethanal were treated, respectively. Although this treatment was carried on for a period of 100 hours, no deterioration in activation was observed.

Example 5

[0032] The same simulated malodorous air as that in Example 4 was treated under the same conditions as those in Example 4 except that the catalyst system for deodorization of the present invention which comprises a pretreating catalyst and a noble metal catalyst was used, wherein the pretreating catalyst comprises manganese oxide(IV), 1% by weight of nickel oxide(II), and 10% by weight of vanadium oxide(V), the noble metal catalyst comprises a rhodium-palladium supporting alumina catalyst in which rhodium and palladium were supported by 1% by weight, respectively. 95% of Dimethylsulfide, 96% of methanethiol, 100% of limonene and 96% of ethanal were treated, respectively. Although this treatment was carried on for a period of 100 hours, no deterioration in activation was observed.

Example 6

[0033] The same simulated malodorous air as that in Example 5 was treated under the same conditions as those in Example 5 except that manganese oxide(IV) and 5% by weight of vanadium oxide(V) are used as the pretreating catalyst. 96% of Dimethylsulfide, 97% of methanethiol, 98% of limonene and 97% of ethanal were treated, respectively. Although this treatment was carried on for a period of 100 hours, no deterioration in activation was observed.

[0034] As mentioned above, the catalyst system for deodorization of the present invention can effectively decompose and/or deodorize a gas to be deodorized which includes aldehydes, sulfur compounds of low oxidation state, or other compounds. Furthermore, it is also possible to preponderantly remove a material to be removed with top priority by suitably selecting the kind of a catalyst.

[0035] Effects of the Invention:

[0036] As mentioned above, according to the present invention, the pretreating catalyst and the noble metal catalyst are used, and a gas to be deodorized is brought into contact with the pretreating catalyst priot to being brought into contact with the noble metal catalyst, wherein the pretreating catalyst can convert a sulfur atom of low oxidation state by which the noble metal catalyst is deactivated, into a sulfur atom the high oxidation state which has little deactivation effects, and the noble metal catalyst can oxidize aldehydes; and thereby the catalyst system for deodorization which shows a high deodorization on to a mixture of compounds such as aldehydes and sulfur compounds, and has high resistance against the same, is provided.

[0037] On the other hand, in the apparatus for deodorization of the present invention, the pretreating catalyst is positioned upstream of the channels of a gas to be deodorized, while the noble metal catalyst is positioned downstream thereof, and therefore, compounds containing a sulfur atom of low oxidation state have been effectively converted into sulfur compounds of high oxidation state such as sulfone through the pretreating catalyst, and thereafter the deodorization treatment is carried out through the noble metal catalyst, and thereby the prolongation of life of the noble metal catalyst and a high-efficient oxidative decomposition can be realized.

Claims

1. A catalyst system for deodorization, comprising a pretreating catalyst for converting sulfur compounds of low oxidation state which are contained in materials to be deodorized, into sulfur compounds of high oxidation state and a noble metal catalyst, wherein said material to be deodorized is brought into contact with said pretreating catalyst prior to being brought into contact with said noble metal catalyst.

2. The catalyst system for deodorization according to claim 1, wherein said pretreating catalyst is a catalyst comprising at least one selected from the group consisting of vanadium, chromium, manganese, iron, cobalt, nickel, copper and oxides thereof, while said noble metal catalyst is a catalyst comprising at least one selected from the group consisting of ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum and gold.

3. An apparatus for deodorization which is provided with a catalytic reaction tower inside which channels for a gas to be deodorized are provided, wherein a pretreating catalyst bed for converting sulfur compounds of low oxidation state which are contained in said gas into sulfur compounds of high oxidation state is positioned upstream of said channels for said gas, while a noble metal bed is positioned downstream of said channels.

4. The apparatus for deodorization according to claim 3, wherein said pretreating catalyst is a catalyst comprising at least one selected from the group consisting of vanadium, chromium, manganese, iron, cobalt, nickel, copper and oxides thereof, while said noble metal catalyst is a catalyst comprising at least one selected from the group consisting of ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum and gold.

5. The apparatus for deodorization according to claim 3, wherein inside the catalytic reaction tower, said pretreating catalyst bed is upstream positioned, and said noble metal catalyst bed is downstream positioned, wherein said pretreating catalyst bed and said noble metal catalyst bed are positioned in series at desired space.

6. The apparatus for deodorization according to claim 3, wherein inside the catalytic reaction column, said pretreating catalyst bed is upstream positioned, and said noble metal catalyst bed is downstream positioned, wherein said pretreating catalyst bed and said noble metal catalyst bed are not mixed with each other, and are kept in contact with each other.

7. A use of a catalytic system comprising a pretreating catalyst and a noble metal catalyst for deodorizing a gas which contains materials having a deactivation effect on the noble metal catalyst, wherein said use comprises the steps of: bringing said gas to be deodorized into contact with said pretreating catalyst prior to bringing said gas into contact with said noble metal catalyst so as to convert said gas into another material having less deactivation effect; and then, bringing said gas into contact with-said noble metal catalyst.

8. The use of a catalytic system according to claim 7, wherein said pretreating catalyst is a catalyst comprising at least one selected from the group consisting of vanadium, chromium, manganese, iron, cobalt, nickel, copper and oxides thereof; and said noble metal catalyst is a catalyst comprising at least one selected from the group consisting of ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum and gold.