Catalysts for the hydrotreatment of hydrocarbons and their utilization

Information

  • Patent Grant
  • 4039477
  • Patent Number
    4,039,477
  • Date Filed
    Tuesday, July 22, 1975
    49 years ago
  • Date Issued
    Tuesday, August 2, 1977
    47 years ago
Abstract
Catalysts particularly useful for hydroreforming and isomerization of hydrocarbons formed of a refractory mineral oxide carrier having a halogen in combined form and the following metals in free or combined state:A. A metal from the platinum group (0.02 to 2%);B. tin (0.02 to 2%); andC. at least one metal selected from the group of scandium, yttrium, thorium, uranium, and the rare earths metals (0.01 to 5%) -- said percentages being based upon the total weight of the catalyst, said catalyst preferably having platinum and chlorine. Also the use of said catalyst in the aforementioned hydrotreatments.
Description

The present invention relates to new catalysts for the hydrotreatment of hydrocarbons. More particularly, it relates to their utilization in the hydroreforming and isomerization of hydrocarbons.
Catalytic hydrotreating processes are treatments applied to hydrocarbon charges in the presence of hydrogen and of a catalyst which entail, separately or simultaneously, hydrogenation, dehydrogenation, isomerization, cyclization, dehydrocyclization and aromatization reactions.
An example of a process in which these reactions occur simultaneously is catalytic hydroreforming, a process that is employed particularly in the treatment of petroleum fractions intended for the production of gasolines for the purpose of raising the octane rating of these fractions. In this process it is sought to promote the dehydrocyclization reactions which convert paraffins and naphthenes to high-octane aromatic hydrocarbons. This process has come into wide use on account of the current demand for gasoline as engine fuel. Moreover, the current trend toward reduction of atmospheric pollution by automotive vehicles calls for the production of gasolines which may be used directly, without tetraethyllead being added for the purpose of raising the octane rating.
In catalytic hydroreforming, the conditions of treatment are selected so that cracking reactions are minimized and dehydrocylization, dehydrogenation and isomerization promoted.
These conditions generally are as follows: Temperature ranges approximately from 450.degree. to 550.degree. C. Total relative pressure ranges approximately from 10 to 40 bars. The space velocity per hour of the charge of hydrocarbons (usually naphtha), measured in the liquid state, is in the neighborhood of 1 to 2 and generally is comprised between 0.5 and 5. Moreover, the operation is carried out in the presence of hydrogen, the molar ratio of hydrogen to hydrocarbons being comprised between 2 and 10.
Particularly when paraffins and naphthenes are used as starting materials, the dehydrocyclization and dehydrogenation reactions result in the formation of aromatic hydrocarbons which, apart from being of interest as fuels by reason of their high octane rating, are also suited for use as raw materials in the petrochemical industry.
Another example of a catalytic hydrotreating process is the process for isomerization of hydrocarbons. This process may be applied particularly to saturated aliphatics, olefinic or aromatic hydrocarbons. In the case of aromatic hydrocarbons, for example, it may be employed to increase the yield of paraxylene, which is a particularly useful raw material in the manufacture of polyesters.
The isomerization of alkylaromatic hydrocarbons is an operation that is carried out at a temperature slightly below the temperature employed in hydroreforming - generally below 500.degree. C. and above 350.degree. C. -- for example, between 430.degree. and 480.degree. C. -- and at a pressure on the order of 25 to 35 bars. The space velocity per hour of the hydrocarbon charge, measured in the liquid state, generally is in the neighborhood of 1 to 2. The operation is carried out in the presence of hydrogen, the molar ratio of hydrogen to hydrocarbons varying approximately between 8 and 10.
The most widely used catalysts are those containing a platinum-group metal, usually platinum, supported on a refractory mineral oxide of large specific surface, such as alumina. The price of platinum being very high, bi- or tri-metallic catalysts have come into use which permit the amount of platinum deposted on the carrier to be reduced.
It is known that rare earths may be added to the platinum in hydrotreating catalysts. U.S. Pat. No. 3,776,860, for example, relates to catalysts containing platinum and a metal selected from the group consisting of neodymium, praseodymium, samarium and ytterbium. However, these catalysts have the drawback of promoting cracking reactions which result in the formation of light hydrocarbons detrimental to the octane rating of the effluent.
Catalysts containing tin and platinum are also known. For example, U.S. Pat. No. 3,700,588 and the addition thereto, U.S. Pat. No. 3,822,221, which are owned by the applicants' assignee, describe catalysts containing at least one element from the platinum group, for example, platinum, and possibly iridium, and at least one element from the group consisting of lead and tin.
For the isomerization of alkylaromatic hydrocarbons, a great many catalysts are known. Many of these include a porous alumina or aluminosilicate carrier in which is deposited a so-called noble metal such as platinum, whether or not associated with other metals, among them iridium, tin, rhenium, lead and germanium. It is also known that one or more "non-noble" metals may be associated on such a carrier, such as the metals of groups Ib, IIb, Vb or VIb of the periodic table of elements.
The applicants have found that the stability of catalysts containing at least one platinum-group metal and tin may be improved by the addition of a metal selected from the group consisting of scandium, yttrium, thorium, uranium and the rare earths metals.
It has further found that, surprisingly, these catalysts do not promote cracking reactions.
It is thus the object of the present invention to provide highly stable hydrotreating catalysts which result in effluents having a very good octane rating, give a better liquid-hydrocarbon yield, and possess good isomerizing properties.
The present invention has as a first preferred embodiment catalysts for the hydrotreatment of hydrocarbons comprising a refractory mineral oxide carrier and a halogen element present in combined form, said catalysts being characterized by the fact that they comprise, in combination, in free or combined form:
a. Form 0.02 to 2%, and preferably from 0.10 to 0.70%, based on the total weight of the catalyst, of at least one platinum-group metal.
b. From 0.02 to 2%, and preferably from 0.05 to 0.60%, based on the total catalyst weight, of tin.
c. From 0.01 to 5%, and preferably from 0.02 to 1%, based on the total catalyst weight, of at least one metal selected from the group consisting of scandium, yttrium, thorium, uranium and the rare earths metals.
In this definition of the invention and throughout the present application, the term "platinum-group metal" means one of the following metals: Ruthenium, rhodium, palladium, osmium, iridium, and platinum.
A second preferred embodiment of the present invention are catalysts for the hydrotreatment of hydrocarbons comprising a refractory mineral oxide carrier and a halogen element present in combined form, said catalysts being characterized by the fact that they comprise, in combination, in the free or combined state:
a. From 0.02 to 2%, and preferably from 0.10 to 0.70%, based on the total wieght of the catalyst, of at least one platinum-group metal.
b. From 0.02 to 2%, and preferably from 0.05 to 0.60%, based on the total catalyst weight, of tin.
c. From 0.01 to 5%, and preferably from 0.02 to 1%, based on the total catalyst weight, of at least one metal from the group consisting of yttrium, thorium, uranium, praseodymium, cerium, lanthanum, neodymium, samarium, dysprosium and gadolinium.
More particularly, the invention relates to catalysts as defined above in which:
a. The carrier has a specific surface greater than 15 m.sup.2 per gram and a specific pore volume greater than 0.1 cc per gram, and
b. The halogen content, determined in the elemental form, and based on the total catalyst weight, is comprised between 0.5 and 3%, and preferably between 0.6 and 1.6%.
A third preferred embodiment of the present invention is the utilization of the catalysts defined above in the hydroreforming of a petroleum fraction containing less than 10 ppm, and preferably less than 1 ppm, of sulfur and whose boiling temperature at atmospheric pressure is comprised between 35.degree. and 250.degree. C.
A fourth preferred embodiment of the invention is the utilization of the catalysts in accordance with the invention in the isomerization of hydrocarbons in the presence of hydrogen.
The carriers of the catalysts in accordance with the invention should be refractory substances having an adequate surface and specific pore volume. The specific surface is comprised between 15 and 350 m.sup.2 /gram, and preferably between 100 and 350 m.sup.2 /gram, the specific pore volume being greater than 0.1 cc per gram. Moreover, the substances must have a rather pronounced acid character since it is known that the isomerization reactions occur on acid sites. Both alumina and aluminosilicates, for example, are well suited for use as such carriers.
The most advantageous carriers are those whose platinum-group metal content, based on the total catalyst weight, is comprised between 0.02 and 2%. To give satisfactory catalytic properties, said content should peferably be greater than 0.10%; however, for reasons of catalyst cost, it is preferably limited to 0.70%.
The tin content, based on the total catalyst weight, is comprised between 0.02 and 2%; since below 0.02% and above 2% the improvement in catalytic properties in relation to a catalyst containing no platinum is negligible.
The applicants have further found that the most efficacious contents are those comprised between 0.02 and 0.60%.
The same is ture of the content of the metal selected from the group consisting of yttrium, thorium, uranium, samarium, dysprosium, gadolinium, praseodymium, cerium, lanthanum and neodymium, which, based on the total catalyst weight, is comprised between 0.01 and 5%, and preferably between 0.02 and 1%.
The halogen content, based on the total catalyst weight, may be comprised between 0.3 and 3%, and preferably between 0.6 and 1.6%. The halogen present in the catalysts in accordance with the invention is preferably chlorine. It may be introduced into the catalyst composition in the manner known in the field, for example, during preparation of the carrier or while the metallic elements are being deposited, by means of solutions of metal chlorides, for example.
The catalysts in accordance with the invention may be prepared by conventional carrier impregnation methods using solutions containing the elements to be deposited.
The impregnation of the carrier may be carried out:
a. by means of at least one solution containing the three elements to be deposited; or
b. by means of at least two solutions, one containing two elements to be deposited, and the other the third; or
c. by means of at least three solutions, each containing one of the elements to be deposited.
The deposition of the tin may be effected from solutions of stannous chloride, stannic chloride or any other soluble tin salt, for example.
The deposition of the metal selected from the group containing yttrium, thorium, praseodymium, cerium, uranium, lanthanum, neodymium, samarium, dysprosium and gadolinium may be effected from solutions of their soluble salts, as, for example, the nitrates, the chlorides or the acetates.
The impregnating solution containing at least one metal selected from the group consisting of praseodymium, cerium, lanthanum, neodymium, samarium, dysprosium and gadolinium may be prepared from a natural mixture of these elements. Impregnation may take place before the addition, between additions or after the addition of tin and at least one of the platinum-group metals.
After the metals have been deposited, the solid obtained is calcined at a temperature which, in the case of the metals other than the platinum-group metals, is comprised between 400.degree. and 700.degree. C. and preferably is 600.degree. C. or less, and which in the case of the platinum-group metals is 550.degree. C. or less.
The acidity of the carrier may be altered prior to deposition of the elements, during such deposition, or between depositions when the latter are not simultaneous, by an acid treatment with hydrochloric acid, for example.
The catalyst may be activated during the hydrotreatment by incorporating in the charge a soluble halogenated compound (a chloride, for example). It may also be advantageous to presulfurize the catalyst with a stream of sulfurized hydrogen, for example, with a view to minimizing the cracking reactions which tend to occur at the start of the treatment.
As will be seen from the examples which follow, and which are in no wise limitative, the applicants have obtained highly interesting results with the catalysts in accordance with the invention.
Examples 1, 2 and 3 relate more particularly to the hydroreforming of a charge of normal heptane. The nature of this charge does not constitute a limitation of the field of application of said catalysts since such a charge is customarily used in performance tests on hydroreforming catalysts. The results obtained may therefore be extended to the case where the charge is a fraction intended for the manufacture of a high-octane gasoline whose boiling temperature is comprised between 35 and 250.degree. C. and whose sulfur content is under 10 ppm. and preferably under 1 ppm.
Examples 4 and 5 relate to the isomerization of a charge consisting of ethylbenzene.





EXAMPLE 1
This example relates to the preparation of
1. a control catalyst T1 consisting of platinum and alumina;
2. control catalysts A1, B1, C1, D1, E1, F1, G1, H1, I1, and J1 consisting of alumina, platinum and a metal selected from the group consisting of yttrium, thorium, uranium, praseodymium, cerium, lanthanum, neodymium, samarium, dysprosium, and gadolinium; and
3. catalysts A2, B2, C2, C3, D2, E2, F2, G2, H2, I2 and J2 in accordance with the invention; which are then submitted to catalytic tests consisting of the hydroreforming of normal heptane.
An alumina is used in the form of extrusions whose characteristics are as follows:
______________________________________Average diameter of extrusions 1.5 mmSpecific surface 190 m.sup.2 /gPore volume 0.51 cc/gChlorine content 0.5% by weight of(measured by x-ray fluorescence) the alumina______________________________________
This alumina is calcined for four hours at 600.degree. C. and is used as the carrier for the catalysts prepared and tested in this example. It will hereinafter be referred to as the alumina carrier.
PREPARATION OF CONTROL CATALYST T1
100 g of the alumina carrier is immersed in 250 cc of an N/10 solution of hydrochloric acid. This alumina is then dewatered at ambient temperature and then contacted with a circulating solution of hexachlorplatinic acid (H.sub.2 PtCl.sub.6.sup.. 6H.sub.2 O) of such concentration that the final catalyst contains from 0.35 to 0.40% by weight of platinum. After dewatering followed by drying at 120.degree. C. for 16 hours, the catalyst is calcined for 2 hours at 530.degree. C. in a muffle kiln. The catalyst so obtained contains 0.35% by weight of platinum and 1.34% by weight of chlorine.
PREPARATION OF CATALYSTS A1, B1, C1, D1, E1, F1, G1, H1, I1, AND J1
100 g of the alumina carrier is placed in a rotary evaporator with 250 cc of a solution containing 20 cc hydrochloric acid RP and a certain amount of a compound of the metal selected from the group consisting of yttrium, samarium, thorium, uranium, praseodymium, cerium, lanthanum, neodymium, dysprosium and gadolinium.
Said amount and the compound are given in Table I for every one of the catalysts prepared.
TABLE I______________________________________ Quantity (in grams) Metal to be De- of com-CA- posited, other pound forTA- than platinum 100 g ofLYST and tin COMPOUND alumina______________________________________A1 OxideA2 Praseodymium Pr.sub.6 O.sub.11 0.2868B1 Cerium NitrateB2 Ce (NO.sub.3).sub.3 . 6 H.sub.2 O 0.7318C1 OxideC2 Yttrium Y.sub.2 O.sub.3 0.1902C3D1 NitrateD2 Lanthanum La (NO.sub.3).sub.3 . 6 H.sub.2 O 0.7296E1 OxideE2 Neodymium Nd.sub.2 O.sub.3 0.2834F1 AcetateF2 Uranium UO.sub.2 (CH.sub.3 COO).sub.2 . 2 H.sub.2 O 0.7146G1 Nitrate Thorium 0.9300G2 Th (NO.sub.3).sub.4 . 4 H.sub.2 OH1 Samarium OxideH2 Sm.sub.2 O.sub.3 0.2964I1 Dysprosium OxideI2 Dy.sub.2 O.sub.3 0.2738J1 Gadolinium OxideJ2 Gd.sub.2 O.sub.3 0.3054______________________________________
After evaporation of the liquid phase, the alumina is dried at 120.degree. C. for 16 hours, then calcined at 500.degree. C. for 2 hours.
The alumina is then immersed in 250 cc of an N/10 solution of hydrochloric acid which is circulated for 2 hours.
After dewatering, the alumina is immersed in 250 cc of a hexachloroplatinic acid solution containing 1.4 g per liter of platinum. This solution is circulated for 16 hours.
Following dewatering, the alumina is dried at 120.degree. C. for 16 hours, then calcined at 530.degree. C. for 2 hours.
The compositions of the catalysts obtained are given in Table II.
TABLE II______________________________________ Compositon of catalyst in weight per cent Metal other Metal otherCATA- than thanLYST platinum Platinum platinum Chlorine______________________________________A1 Praseodymium 0.35 0.06 1.37B1 Cerium 0.35 0.12 1.38C1 Yttrium 0.35 0.06 1.30D1 Lanthanum 0.35 0.04 1.32E1 Neodymium 0.35 0.06 1.40F1 Uranium 0.35 0.30 1.28G1 Thorium 0.35 0.48 1.37H1 Samarium 0.35 0.14 1.36I1 Dysprosium 0.35 0.10 1.43J1 Gadolinium 0.35 0.105 1.26______________________________________
PREPARATION OF CATALYSTS A2, B2, C2, C3, D2, E2, F2, G2, H2, I2 and J2
100 g of the alumina carrier is placed in a rotary evaporator with 250 cc of a solution containing 20 cc hydrochloric acid RP and a certain amount of a compound of the metal selected from the group consisting of yttrium, thorium, uranium, praesodymium, cerium, lanthanum, neodymium, samarium, dysprosium and gadolinium.
Said amount and the compound are likewise given in Table I for every one of the catalysts prepared.
After evaporation of the liquid phase, the alumina is dried at 120.degree. C. for 16 hours, then calcined at 600.degree. C. for 2 hours.
The alumina is then placed in a rotary evaporator with 250 cc of a solution containing 20 cc of hydrochloric acid RP and 0.380 g of stannous chloride, SnCl.sub.2.sup.. 2H.sub.2 O.
After evaporation of the liquid phase, drying at 120.degree. C. for 16 hours and calcination at 600.degree. C. for 2 hours, the alumina is immersed in 250 cc of an N/10 solution of hydrochloric acid which is circulated for 2 hours.
After dewatering, the alumina is immersed in 250 cc of a hexachloroplatinic acid solution containing 1.4 g per liter of platinum. This solution is circulated for 16 hours.
Following dewatering, the alumina is dried at 120.degree. C. for 16 hours, then calcined at 530.degree. C. for 2 hours.
The compositions of the catalysts obtained are given in Table III.
TABLE III______________________________________Metal other Composition of catalyst in wt. % than Metal otherCATA- platinum or Plati- than plati-LYST tin num num or tin Tin Chlorine______________________________________A2 Praseodymium 0.35 0.07 0.20 1.35B2 Cerium 0.35 0.13 0.20 1.36C2 Yttrium 0.35 0.06 0.20 1.24C3 Yttrium 0.35 0.06 0.20 1.24D2 Lanthanum 0.35 0.05 0.20 1.26E2 Neodymium 0.35 0.07 0.20 1.35F2 Uranium 0.35 0.30 0.20 1.37G2 Thorium 0.35 0.45 0.20 1.45H2 Samarium 0.35 0.16 0.20 1.26I2 Dysprosium 0.35 0.12 0.20 1.26J2 Gadolinium 0.35 0.12 0.20 1.16______________________________________
The catalysts T1, A1, A2, B1, B2, C1, C2, C3, D1, D2, E1, E2, F1, F2, G1, G2, H1, H2, I1, I2, J1 and J2 are submitted to the following catalytic test: 2 cc of the catalyst is placed in a small reactor which is maintained at a constant temperature. That temperature is 520.degree. C. for all tests, except for catalyst C3, for which the temperature is 460.degree. C. A hydrogen gas stream saturated with normal heptane (by bubbling the hydrogen in the heptane at 20.degree. C.) is passed over the catalyst at atmospheric pressure. The sulfur content of the normal heptane is less than 1 ppm. The space velocity per hour of the gas mixture (that is to say, the volume of gas passing over a unit volume of catalyst per hour) is 80.
The proportion of heptane in the gas stream is 2.5%. The reactor effluent is analyzed in the gaseous phase by chromatography.
The results obtained with the catalysts T1, A1, A2, B1, B2, C1, C2, C3, D1, D2, E1, E2, F1, F2, G1, G2, H1, H2, I1, I2, J1 and J2 are presented in Table IV.
That table gives, for each catalyst and after different operating times, the weight percent in the effluent of -
a. the hydrocarbons with four or fewer carbon atoms (C.sub.1 to C.sub.4), this value being representative of the cracking of the charge;
b. the normal heptane (nC.sub.7), the complement to 100 being a measure of the conversion of the charge;
c. the hydrocarbons with five or more carbon atoms other than the unconverted normal heptane (C.sub.5 +); and
d. the aromatic hydrocarbons (benzene and toluene), this value being particularly representative of the activity of the catalysts for the hydroreforming of hydrocarbons, aromatic hydrocarbons having a high octane rating.
TABLE IV______________________________________Characteristicvalues ofCATA- effluent (wt. Operating times (hours)LYST % of charge) 1/4 1 3 5 71/2______________________________________ C.sub.1 - C.sub.4 63 54.8 44.6 44.3 38.9 n C.sub.7 -- 0.2 2.3 6.9 11.2 C.sup.+.sub.5 (otherT1 than n C.sub.7) 0.1 1.1 4.1 6.0 6.1 Aromatics (benzene + 36.8 43.9 49.0 42.8 43.8 toluene) C.sub.1 - C.sub.4 64.4 54.1 51.3 52.1 -- n C.sub.7 -- -- 0.4 1.4 -- C.sup.+.sub.5 (otherA1 than n C.sub.7) -- 0.9 3.1 5.3 -- Aromatics (benzene + 35.6 45.0 45.2 41.2 -- toluene) C.sub.1 - C.sub.4 23.5 16.7 10.8 14.4 14.6 n C.sub.7 -- -- -- -- -- C.sup.+.sub.5 (otherA2 than n C.sub.7) 1.7 2.2 2.9 2.7 2.7 Aromatics (benzene + 74.8 81.1 86.3 82.9 82.7 toluene) C.sub.1 - C.sub.4 53.6 43.9 39.8 44.9 -- n C.sub.7 -- -- 0.3 0.3 -- C.sup.+.sub.5 (otherB1 than n C.sub.7) 0.9 4.3 10.4 13.0 -- Aromatics (benzene + 45.5 51.8 49.5 41.8 -- toluene) C.sub.1 - C.sub.4 13.1 11.2 10.7 10.5 -- n C.sub.7 -- -- -- -- -- C.sup.+.sub.5 (otherB2 than n C.sub.7) 0.8 1.1 1.6 1.5 -- Aromatics (benzene + 86.1 87.7 87.7 88.0 -- toluene) C.sub.1 - C.sub.4 62.2 46.4 43.8 42.5 -- n C.sub.7 -- 1.5 2.9 6.6 -- C.sup.+.sub.5 (otherC1 than n C.sub. 7) 1.1 5.1 8.6 10.7 -- Aromatics (benzene + 36.7 47.0 44.7 40.2 -- toluene) C.sub.1 - C.sub.4 15.8 10.8 9.1 9.3 9.9 n C.sub.7 -- -- -- -- -- C.sup.+.sub.5 (otherC2 than n C.sub.7) 1.2 1.4 1.8 1.8 1.9 Aromatics (benzene + 83.0 87.8 89.1 88.9 88.2 toluene) C.sub.1 - C.sub.4 23.7 22.7 23.2 24.5 24.5 n C.sub.7 -- -- 0.5 0.4 1.0 C.sup.+.sub.5 (otherC3 than n C.sub.7) 6.7 7.4 9.2 10.0 11.2 Aromatics (benzene + 69.6 69.9 67.1 65.1 63.3 toluene) C.sub.1 - C.sub.4 56.9 45.7 47.8 46.2 -- n C.sub.7 0.4 0.9 2.1 3.5 -- C.sup.+.sub.5 (otherD1 than n C.sub.7) 1.2 3.7 6.0 9.3 -- Aromatics (benzene + 41.5 49.7 44.1 41.0 -- toluene) C.sub.1 - C.sub.4 21.1 15.6 13.7 14.9 12.2 n C.sub.7 -- -- -- 0.3 0.7 C.sup.+.sub.5 (otherD2 than n C.sub.7) 2.7 3.4 3.3 3.8 3.9 Aromatics (benzene + 76.2 81.0 83.0 81.0 83.2 toluene) C.sub.1 - C.sub.4 52.0 49.4 49.0 49.2 -- n C.sub.7 -- -- 0.4 1.1 -- C.sup.+.sub.5 (otherE1 than n C.sub.7) -- 1.3 4.7 6.8 -- Aromatics (benzene + 48.0 49.3 45.9 42.9 -- toluene)C.sub.1 - C.sub.4 16.2 13.5 13.8 11.3 11.4 n C.sub.7 -- -- -- -- -- C.sup.+.sub.5 (otherE2 than n C.sub.7) 0.4 1.2 1.7 2.2 1.8 Aromatics (benzene + 83.4 85.3 84.5 86.5 86.8 toluene) C.sub.1 - C.sub.4 57.0 45.2 45.2 44.4 -- n C.sub.7 -- -- 0.6 1.2 -- C.sup.+.sub.5 (otherF1 than n C.sub.7) 0.4 2.3 5.8 7.6 -- Aromatics (benzene + 42.6 52.5 48.4 46.8 -- toluene) C.sub.1 - C.sub.4 16.2 11.5 11.1 10.1 -- n C.sub.7 -- -- -- -- -- C.sup.+.sub.5 (otherF2 than n C.sub.7) 0.5 1.4 1.6 1.6 -- Aromatics (benzene + 83.3 87.1 87.3 88.3 -- toluene) C.sub.1 - C.sub.4 50.7 48.1 46.2 46.0 -- n C.sub.7 -- 0.4 1.3 2.9 -- C.sup.+.sub.5 (otherG1 than n C.sub.7) 0.6 2.8 5.6 8.1 -- Aromatics (benzene + 48.7 48.7 46.9 43.0 -- toluene) C.sub.1 - C.sub.4 16.3 13.4 11.1 11.3 10.4 n C.sub.7 -- -- -- -- -- C.sup.+.sub.5 (otherG2 than n C.sub.7) 0.5 1.1 1.6 1.7 2.1 Aromatics (benzene + 83.2 85.5 87.3 87.0 87.5 toluene) C.sub.1 - C.sub.4 33.2 28.7 33.4 35.4 36.3 n C.sub.7 -- 2.2 2.6 3.8 4.0 C.sup.+.sub.5 (otherH1 than C.sub.7) 4.4 6.2 7.1 8.0 8.2 Aromatics (benzene + 62.4 62.9 56.9 52.8 51.5 toluene) C.sub.1 - C.sub.4 13.3 10.7 11.0 11.1 10.6 n C.sub.7 -- -- 0.1 0.4 0.4 C.sup.+.sub.5 (otherH2 than n C.sub.7) 1.8 2.1 2.4 2.5 2.5 Aromatics (benzene + 84.9 87.2 86.5 86.0 86.5 toluene) C.sub.1 - C.sub.4 49.4 41.3 39.6 38.1 44.3 n C.sub.7 -- -- -- -- -- C.sup.+.sub.5 (otherI1 than n C.sub.7) -- -- 0.1 0.6 1.0 Aromatics (benzene + 50.6 58.7 60.3 61.3 54.7 toluene) C.sub.1 - C.sub.4 16.9 13.9 12.0 10.8 12.1 n C.sub.7 -- -- -- -- -- C.sup.+.sub.5 (otherI2 than n C.sub.7) 1.6 2.5 2.6 2.0 2.6 Aromatics (benzene + 81.5 83.6 85.4 87.2 85.3 toluene) C.sub.1 - C.sub.4 36.7 29.2 32.8 31.9 34.2 n C.sub.7 4.9 9.3 15.7 22.4 23.3 C.sup.+.sub.5 (otherJ1 than n C.sub.7 6.4 8.6 9.4 10.1 10.3 Aromatics (benzene + 52.0 52.9 42.1 35.6 32.2 toluene) C.sub.1 - C.sub.4 18.3 14.3 12.4 12.2 11.1 n C.sub.7 -- -- -- -- -- C.sup.+.sub.5 (otherJ2 than n C.sub.7 2.5 3.9 3.6 3.8 3.6 Aromatics (benzene + 79.2 81.8 84.0 84.0 85.3 toluene)______________________________________
It is apparent from Table IV that catalysts which contain no tin give results closely similar to those obtained with a catalysts containing only platinum and alumina. With these catalysts, the percentage of hydrocarbons with four or fewer carbon atoms is particularly high.
On the other hand, the percentage of aromatic hydrocarbons obtained with the catalysts in accordance with the invention is about double that obtained with catalysts containing no tin. Catalyst C3, tested at 460.degree. C., exhibits a remarkable activity, the percentage of aromatic hydrocarbons obtained being close to 70 wt.%.
Thus the catalysts in accordance with the invention are good hydroreforming catalysts.
EXAMPLE 2
In this example, a catalyst T2 consisting of alumina, platinum and tin is prepared.
This catalyst, along with catalysts B2 and D2, is then submitted to catalytic tests under hydrogen pressure.
PREPARATION OF CATALYST T2
100 g of the alumina carrier is immersed for 4 hours in 250 cc of a solution containing 20 cc of hydrochloric acid RP and 0.380 g of stannous chloride, SnCl.sub.2.sup.. 2H.sub.2 O. After drying at 120.degree. C. for 16 hours and calcination for 2 hours, the alumina is immersed in 250 cc of an N/10 solution of hydrochloric acid which is circulated for 24 hours.
Following dewatering, the alumina is immersed for 16 hours in 250 cc of a hexachloroplatinic acid solution containing 0.350 g of platinum.
The impregnated alumina is then dried for 16 hours at 120.degree. C. and calcined for 2 hours at 530.degree. C.
The catalyst so prepared contains 0.35 wt.% of platinum, 0.20 wt.% of tin and 1.20 wt.% of chlorine.
CATALYTIC TEST
25 cc of catalyst is placed in a stainless-steel reactor. A pure and dry hydrogen stream is then passed over the catalyst for 2 hours, its temperature being maintained to about 500.degree. C. and the pressure in the reactor being maintained at 7 bars. The charge consisting of normal heptane is then introduced at a space velocity per hour of 2 and a ratio of moles of hydrogen introduced to moles of normal heptane introduced of 5.
Samples taken from the reactor effluent permit determination, on the one hand, of the liquid yield, by simple weighing, and, on the other hand, of the equivalent octane number of the liquid, by applying to the chromatographic analyses of said liquid the ASTM blend numbers appearing in the graphs with which those skilled in the art are familiar.
The tests are performed at a fixed octane number, that is to say, as soon as a decrease in octane number is observed, the reactor temperature is raised in order to bring the octane number again to the level originally selected, which in this example is 103.
The variation of the reactor temperature as a function of time closely resembles a straight line whose slope is measured. The milder the slope of the straight line, the better the catalyst, as the temperature then needs to be adjusted only very slighly in the course of time to secure the desired octane number. The time required to reach the limiting temperature of use then is extended, which is a decided advantage in industrial applications.
Table V shows the results of the catalytic tests performed under pressure on catalysts T2, B2, and D2.
TABLE V______________________________________ INITIAL SLOPE OF TEMPERATURE CURVECATALYSTS (.degree. C.) T = f (time)______________________________________T2 520.5 0.0690B2 509.7 0.0324D2 499.2 0.0493______________________________________
It is apparent from that table that for a given constant octane number:
1. the initial temperature is lower for the catalysts B2 and D2 in accordance with the invention than for catalyst T2 which contains only alumina, platinum and tin, and
2. the slope of the curve is milder in the case of catalysts B2 and D2, which translates into less rapid degradation of the catalyst.
The catalysts in accordance with the invention thus exhibit better stability than a catalysts containing only alumina, platinum and tin.
EXAMPLE 3
This example illustrates the catalytic hydroreforming tests performed under pressure for about 200 hours on various catalysts in accordance with the invention which have been prepared by the impregnation techniques described in example 1.
The various catalytic composition tested are summarized in Table VI, which also shows the composition of two control catalysts, T3 and T4, which contain only platinum and only platinum and tin, respectively, and have been prepared by the same impregnation techniques as the catalysts in accordance with the invention.
TABLE VI______________________________________ Composition of Catalyst, wt. % Metal other Metal otherCATA- than Platinum Plati- than plati-LYST or tin num num or tin Tin Chlorine______________________________________ T3 -- 0.37 -- -- 0.97 T4 -- 0.37 -- 0.21 0.86K Cerium 0.35 0.55 0.20 0.88L " 0.35 0.09 0.20 0.93M " 0.31 1.66 0.21 0.90N Lanthanum 0.36 0.05 0.20 1.26O " 0.36 0.06 0.21 0.92Q Dysprosium 0.36 0.10 0.20 0.93S Yttrium 0.36 0.03 0.23 1.04U Thorium 0.35 0.45 0.20 0.84V Uranium 0.36 0.29 0.21 0.85W Praseodymium 0.37 0.04 0.22 0.95X Neodymium 0.37 0.03 0.21 0.86Y Gadolinium 0.36 0.12 0.20 0.90Z Samarium 0.36 0.16 0.24 0.88______________________________________
The catalytic test under pressure is similar to that described in example 2. The test conditions are as follows:
______________________________________Quantity of catalyst in the reactor 25 ccPressure 7 barsCharge n-heptaneSpace velocity per hour (measured inthe liquid state) 2Molar ratio of hydrogen introducedto n-heptane introduced 5Octane number selected 103______________________________________
All catalysts are reduced by a stream of pure hydrogen for several hours at 500.degree. C. prior to introduction of the n-heptane.
The drops in octane number are compensated by a rise in the reaction temperature, as in example 2.
The results of these tests are reported in Table VII for a duration of about 200 hours. The table shows the equation of the curve representing the variation of temperature as a function of time as well as the average liquid yield, calculated for the entire duration of the test.
The liquid yield indicates the percentage of high-octane hydrocarbons with five or more carbon atoms contained in the effluent, exclusive of the unconverted normal heptane.
TABLE VII______________________________________ Initial Slope of curve Average liquidCATALYST Temperature T = f (time) yield, %______________________________________ T3 507 0.127 *59.7 - 0.036 t T4 514 0.073 59.4K 515.5 0.010 56L 504 0.066 58.9M 507 0.098 59.0N 508.8 0.039 57.4O 511.4 0.063 59.0Q 514 0.103 59.3S 509.4 0.044 57.8U 515.6 0.083 59.5V 514.3 0.083 59.2W 503.2 0.078 59.1X 514.8 0.089 59.9Y 514.3 0.081 58.6Z 511 0.062 59.3______________________________________ *With respect to this catalyst, a rather substantial drop in liquid yield with time was observed, which means that the stability of this catalyst i rather poor. (The liquid yield is expressed as a function of time t.) For the other catalytic formulas, the liquid yield is stable with time, and i is apparent from this table that the catalysts in accordance with the invention compare favorably with the control catalysts prepared and teste under the same conditions.
EXAMPLE 4
In this example, the catalysts B1 and B2 prepared in example 1 are submitted to catalytic tests for isomerization of the ethylbenzene.
25 cc of catalyst is placed in a stainless-steel reactor, and a pure and dry hydrogen stream is passed over the catalyst for 2 hours, its temperature being maintained at about 435.degree. C. and the pressure in the reactor being maintained at 10 bars. The charge consisting of ethylbenzene is then introduced at a spaced velocity per hour of 2 and a ratio of moles of hydrogen introduced to moles of ethylbenzene introduced to 3.
Samples taken from the reactor effluent permit determination, on the one hand, of the liquid yield, by simple weighing, and, on the other hand, of the yields of aromatic hydrocarbons, by chromatographic analysis of said liquid.
The results of the tests run on catalysts B1 and B2 are reported in Table VIII.
TABLE VIII__________________________________________________________________________Operating time 3 5 7 (hours)Catalyst B1 B2 B1 B2 B1 B2Liquid yield 100 96.8 100 92.4 96.53 100 (wt. %)Ethylbenzene 13.37 21.03 15.22 24.25 17.42 17.60conversion (%) Benzene 1.43 1.06 1.22 0.92 0.95 1.10Yield Toluene 1.06 0.25 0.69 0.18 0.51 0.29in Paraxylene 1.93 3.47 2.72 3.05 2.71 3.34wt. Metaxylene 4.03 6.15 4.30 5.46 4.28 5.86% of Orthoxylene 2.59 4.82 2.71 4.41 2.83 4.24Selectivity for xylene 63.3 68.7 63.9 53.3 56.4 76.4__________________________________________________________________________
In this table, the selectivity for xylenes is the ratio of percent of xylenes formed to percent of ethylbenzene converted.
As may be seen from this table, catalyst B2 in accordance with the invention has greater activity and greater selectivity in the isomerization of ethylbenzene than catalyst B1 which contains no tin.
EXAMPLE 5
This example, like the preceding one, illustrates the utilization of catalysts in accordance with the invention in the isomerization of aromatic hydrocarbons.
In this example, the isomerization of ethylbenzene is carried out under the following conditions:
______________________________________Quantity of catalyst in the reactor 40 ccPressure 30 barsMolar ratio of hydrogen introducedto ethylbenzene introduced 5Space velocity per hour,measured in the liquid state 2Reaction temperature 450.degree. C.Duration of test About 6 hr.______________________________________
For each catalyst tested, Table IX shows -
the composition of the catalyst;
the ethylbenzene conversion (that is to say, the molar ratio of ethylbenzene converted to ethylbenzene introduced);
the selectivity for xylenes S.sub.x (molar ratio of xylenes produced to ethylbenzene converted);
The overall selectivity ##EQU1## the precursors of xylenes being intermediate products such as ethylcyclohexane, dimethylcyclohexanes, methylethylcyclopentanes, etc; and
TABLE IX______________________________________ Composition of catalyst(Wt. %)Plati- conver- Sx S.sub.Tnum Tin Cerium Chlorine sion % % %______________________________________*0.30 -- -- 1.39 60.5 46.0 76.3*0.35 0.20 -- 1.40 47.3 58.3 82.70.35 0.21 0.10 1.27 71.2 59.9 85.30.36 0.20 0.13 1.57 74.7 65.15 85.70.35 0.05 0.15 1.37 82.0 50.9 78.30.36 0.10 0.15 1.32 73.1 58.7 82.250.35 0.15 0.18 1.29 66.0 64.5 87.9*0.35 -- 0.18 1.34 65.3 40.2 65.00.35 0.20 0.55 1.31 42.5 52.4 87.50.31 0.21 1.66 1.42 37.0 49.7 85.1*0.32 -- 1.95 1.39 51.35 44.2 73.5______________________________________ *Control catalysts containing only platinum, or platinum and tin, or platinum and cerium prepared under the same conditions as the catalysts i accordance with the invention tested in this table.
The results presented in this table show that the catalysts in accordance with the invention are good catalysts for the isomerization of aromatic hydrocarbons. (Refer to the selectivities for xylene S.sub.x or the overall selectivities S.sub.T.)
Claims
  • 1. A catalyst for the hydrotreatment of hydrocarbons comprising a refractory mineral oxide carrier, a halogen element present in combined form, and containing metals in a free or combined state on said carrier as follows:
  • a. From 0.02 to 2% of at least one metal from the platinum group;
  • b. From 0.02 to 2% of tin; and
  • c. From 0.01 to 5% of scandium;
  • said percentages, determined relative to the respective elemental form, being based upon the total catalyst weight.
  • 2. A catalyst according to claim 1, wherein its halogen content, based on the total catalyst weight, is between 0.5 and 3%.
  • 3. A catalyst according to claim 2, wherein said metal percentages comprise:
  • a. from 0.10% to 0.70%;
  • b. from 0.05% to 0.60%; and
  • c. from 0.02% to 1%; respectively.
  • 4. A catalyst according to claim 2, wherein the platinum-group metal is platinum.
  • 5. A catalyst according to claim 4, wherein the halogen is chlorine.
  • 6. A process for preparing a catalyst as defined in claim 1, by the method comprising an impregnation of the porous carrier with a solution containing hydrochloric acid and a compound of scandium evaporating the liquid phase, drying and calcining the impregnated carrier at between 400.degree. and 700.degree. C.; a further impregnation of the porous carrier with a solution containing hydrochloric acid and a soluble tin salt, evaporation of the liquid phase, drying and calcining at between 400.degree. and 700.degree. C.; immersion of the resulting product in hydrochloric acid; de-watering the carrier and thereafter impregnating with hexachloroplatinic acid followed by drying and then calcining at a temperature of between 400.degree. and 550.degree. C.
  • 7. A catalyst according to claim 1, wherein said metal percentages comprise:
  • a. from 0.10% to 0.70%;
  • b. from 0.05% to 0.60%; and
  • c. from 0.02% to 1%;
  • respectively; said carrier has a specific surface greater than 15 m.sup.2 per gram and a specific pore volume greater than 0.1 cc per gram; and said platinum-group metal is platinum.
  • 8. A catalyst for the hydrotreatment of hydrocarbons comprising a refractory mineral oxide carrier, a halogen element present in combined form, and containing metals in a free or combined state on said carrier as follows:
  • a. From 0.02 to 2% of at least one metal from the platinum group;
  • b. From 0.02 to 2% of tin; and
  • c. From 0.01 to 5% of yttrium;
  • said percentages, determined relative to the respective elemental form, being based upon the total catalyst weight.
  • 9. A catalyst according to claim 8, wherein said metal percentages comprise:
  • a. from 0.10 to 0.70%;
  • b. from 0.05 to 0.60%; and
  • c. from 0.02 to 1%; respectively.
  • 10. A catalyst according to claim 8 wherein said carrier has a specific surface greater than 15 m.sup.2 per gram and a specific pore volume greater than 0.1 cc per gram.
  • 11. A catalyst according to claim 10 wherein its halogen content, based on the total catalyst weight, is between 0.5 and 3%.
  • 12. A catalyst according to claim 11, wherein the platinum-group metal is platinum.
  • 13. A catalyst according to claim 12, wherein the carrier is alumina whose specific surface is between 15 and 350 m.sup.2 per gram.
  • 14. A catalyst according to claim 13, wherein said carrier is substantially acid in character giving its acid sites which favor isomerization.
  • 15. A catalyst according to claim 13, wherein the halogen is chlorine.
  • 16. A catalyst according to claim 15, wherein its halogen content, based on the total catalyst weight, is between 0.6 and 1.6%.
  • 17. A process for preparing a catalyst as defined in claim 8, by the method comprising impregnation of the porous carrier with at least one solution containing at least one of the elements selected from the group consisting of tin, yttrium, and at least one of the platinum-group metals, and at least one of said solutions contains the element yttrium, said carrier being calcined, after deposition of the metals other than those from the platinum group, at a temperature comprised between 400.degree. and 700.degree. C., and, after deposition of at least one platinum-group metal, calcined at a temperature of between 400.degree. and not more than 550.degree. C.
  • 18. A catalyst according to claim 8, wherein said metal percentages comprise:
  • a. from 0.10 to 0.70%;
  • b. from 0.05 to 0.60%; and
  • c. from 0.02 to 1%;
  • respectively; said carrier has a specific surface greater than 15 m.sup.2 per gram and a specific pore volume greater than 0.1 cc per gram; and said platinum-group metal is platinum.
  • 19. A catalyst for the hydrotreatment of hydrocarbons comprising a refractory mineral oxide carrier, a halogen element present in combined form, and containing metals in a free or combined state on said carrier as follows:
  • a. From 0.02 to 2% of at least one metal from the platinum group;
  • b. From 0.02 to 2% of tin; and
  • c. From 0.01 to 5% of thorium;
  • said percentages, determined relative to the respective elemental form, being based upon the total catalyst weight.
  • 20. A process for preparing a catalyst as defined in claim 19, by the method comprising impregnation of the porous carrier with at least one solution containing at least one of the elements selected from the group consisting of tin, thorium, and at least one of the platinum-group metals, and at least one of said solutions contains the element thorium, said carrier being calcined after deposition of the metals other than those from the platinum group, at a temperature comprised between 400.degree. and 700.degree. C., and, after deposition of at least one platinum-group metal, calcined at a temperature of between 400.degree. and not more than 550.degree. C.
  • 21. A catalyst according to claim 19, wherein said metal percentages comprise:
  • a. from 0.10 to 0.70%;
  • b. from 0.05 to 0.60%; and
  • c. from 0.02 to 1%;
  • respectively.
  • 22. A catalyst according to claim 19 wherein said carrier has a specific surface greater than 15 m.sup.2 per gram and a specific pore volume greater than 0.01 cc per gram.
  • 23. A catalyst according to claim 22 wherein its halogen content, based on the total catalyst weight, is between 0.5 and 3%.
  • 24. A catalyst according to claim 23, wherein the platinum-group metal is platinum.
  • 25. A catalyst according to claim 24, wherein the carrier is alumina whose specific surface is between 15 and 350 m.sup.2 per gram.
  • 26. A catalyst according to claim 25, wherein said carrier is substantially acid in character giving it acid sites which favor isomerization.
  • 27. A catalyst according to claim 25, wherein the halogen is chlorine.
  • 28. A catalyst according to claim 19, wherein said metal percentages comprise:
  • a. from 0.10 to 0.70%;
  • b. from 0.05 to 0.60%; and
  • c. from 0.02 to 1%;
  • respectively; said carrier has a specific surface greater than 15 m.sup.2 per gram and a specific pore volume greater than 0.1 cc per gram; and said platinum-group metal is platinum.
  • 29. A catalyst for the hydrotreatment of hydrocarbons comprising a refractory mineral oxide carrier, a halogen element present in combined form, and containing metals in a free or combined state on said carrier as follows:
  • a. from 0.02 to 2% of at least one metal from the platinum group;
  • b. From 0.02 to 2% of tin; and
  • c. From 0.01 to 5% of uranium;
  • said percentages, determined relative to the respective elemental form, being based upon the total catalyst weight.
  • 30. A process for preparing a catalyst as defined in claim 29, by the method comprising impregnation of the porous carrier with at least one solution containing at least one of the elements selected from the group consisting of tin, uranium, and at least one of the platinum-group metals, and at least one of said solutions contains the element uranium, said carrier being calcined after deposition of the metals other than those from the platinum group, at a temperature comprised between 400.degree. and 700.degree. C., and, after deposition of at least one platinum-group metal, calcined at a temperature of between 400.degree. and not more than 550.degree. C.
  • 31. A catalyst according to claim 29, wherein said metal percentages comprise:
  • a. from 0.10 to 0.70%;
  • b. from 0.05 to 0.60%; and
  • c. from 0.02 to 1%;
  • respectively.
  • 32. A catalyst according to claim 31, wherein its halogen content, based on the total catalyst weight, is between 0.5 and 3%.
  • 33. A catalyst according to claim 32, wherein the platinum-group metal is platinum.
  • 34. A catalyst according to claim 33, wherein the carrier is alumina whose specific surface is between 15 and 350 m.sup.2 per gram.
  • 35. A catalyst according to claim 34, wherein said carrier is substantially acid in character giving it acid sites which favor isomerization.
  • 36. A catalyst according to claim 29, wherein said metal percentages comprise:
  • a. from 0.10 to 0.70%;
  • b. from 0.05 to 0.60%; and
  • c. from 0.02 to 1%;
  • respectively; said carrier has a specific surface greater than 15 m.sup.2 per gram and a specific pore volume greater than 0.1 cc per gram; and said platinum-group metal is platinum.
Priority Claims (1)
Number Date Country Kind
74.26490 Jul 1974 FR
US Referenced Citations (11)
Number Name Date Kind
3207808 Bajars Sep 1965
3402210 Hiser Sep 1968
3661768 Davis et al. May 1972
3686340 Patrick et al. Aug 1972
3694348 Bursian et al. Sep 1972
3700588 Weisang et al. Oct 1972
3776860 Rai Dec 1973
3788977 Dolbear et al. Jan 1974
3852215 Duhaut et al. Dec 1974
3894110 Drehman Jul 1975
3915845 Antos Oct 1975