Claims
- 1. A water dealkylation catalyst for an aromatic hydrocarbon consisting essentially of from 0.1 to 5% by weight of (A) one or two metals selected from the group consisting of rhodium, platinum, palladium and iridium or (B) Rh with at least one metal selected from the group consisting of Pt, Pd, Ir and Mn deposited on a gamma alumina carrier, said catalyst having improved properties of activity, selectivity and stability wherein said catalyst is prepared by:
- (a) pretreating said gamma alumina carrier in an aqueous medium for 15 minutes to 78 hours, at a pH from 1 to 10, at a temperature of 0.degree. to 100.degree. C.;
- (b) impregnating the pretreated gamma alumina carrier with an aqueous or acid solution of a salt of the metal, to a total concentration of metal in the carrier of from 0.1 to 5% by weight;
- (c) drying said impregnated carrier;
- (d) calcining said dried impregnated carrier in air;
- (e) reducing the calcined impregnated carrier in a hydrogen current at 400.degree.-500.degree. C.;
- (f) treating the reduced impregnated carrier with a water vapor current at 400.degree. to 600.degree. C. for a period of 5 minutes to 15 hours whereby the catalyst is formed.
- 2. A catalyst according to claim 1, wherein said carrier is a gamma alumina of spinel or pseudo-spinel structure of a specific surface of 50 to 350 m.sup.2 g.sup.-1, a total porous volume of 0.3 to 1.3 cm.sup.3 g.sup.-1, a grain diameter of from 0.01 to 5 mm, and a residual sulfate content of 0.5 to 2000 ppm.
- 3. A catalyst according to claim 1 or 2, wherein said carrier is pre-treated in the presence of deionized water.
- 4. A bimetallic catalyst according to claim 1, wherein the relative proportions of the two metals is from 1:10 to 10:1.
- 5. A bimetallic catalyst according to claim 4, containing 0.05% rhodium and 0.1% iridium.
- 6. A bimetallic catalyst according to claim 1, containing 0.6% rhodium and 1% manganese.
- 7. A catalyst according to claim 1 wherein the total concentration of metals in the impregnated carrier vary between 0.2 to 2% by weight.
- 8. A catalyst according to claim 2 wherein the carrier is a gamma alumina of spinel or pseudo-spinel structure of a specific surface of 150 to 350 m.sup.2 g.sup.-1.
- 9. A catalyst according to claim 2 wherein the grain diameter of the carrier varies from 0.05 to 2 mm.
- 10. A catalyst according to claim 2 wherein the total porous volume of the carrier varies from 0.4 to 0.80 cm.sup.3 g.sup.-1.
- 11. A catalyst according to claim 2 wherein the residual sulfate content of the carrier varies from 0.5 to 1000 ppm.
- 12. A catalyst according to claim 4 wherein the total concentration of metals on the impregnated carrier varies from 0.1 to 2% by weight.
- 13. A catalyst according to claim 1 wherein the total concentration of metals deposited on the impregnated carrier varies from 0.1 to 2% by weight.
- 14. The catalyst of claim 1 wherein the metal is Rh or a mixture of Rh with at least one metal selected from the group consisting of Pt, Pd, Ir and Mn.
Priority Claims (1)
Number |
Date |
Country |
Kind |
78 06424 |
Mar 1978 |
FRX |
|
Parent Case Info
This is a continuation of application Ser. No. 17,328, filed Mar. 5, 1979, now abandoned.
US Referenced Citations (4)
Foreign Referenced Citations (1)
Number |
Date |
Country |
792645 |
Apr 1958 |
GBX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
17328 |
Mar 1979 |
|