Catalytic composition

BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to catalytic compositions, and more particularly to catalytic compositions which exhibit a marked catalytic effect on the formation of unsaturated nitriles by vapor-phase reaction of an olefin, ammonia and oxygen or an oxygen-containing gas, particularly on the formation of acrylonitrile by vapor-phase reaction of propylene, ammonia and oxygen or an oxygen-containing gas.
2. Description of the Prior Art
Various catalysts have heretofore been proposed for the production of acrylonitrile by vapor-phase catalytic ammoxidation of propylene. It is known in the art that a catalyst comprising molybdenum and bismuth as primary components and further containing iron, phosphorus and the like can be used industrially. Upon further study there is developed a catalyst, for example, comprising molybdenum, bismuth, iron, phosphorus and metallic elements such as nickel and cobalt. However, such a catalyst is not satisfactory in suppressing side reactions, and when such a catalyst is used under the conditions where the gaseous materials are fed into the catalyst bed at a high space velocity and where the conversion of propylene is increased, the selectivity of the catalyst is so decreased that it becomes difficult to achieve a satisfactorily good yield of acrylonitrile. Furthermore, these catalyst are not completely satisfactory with respect to catalyst life.
SUMMARY OF THE INVENTION
Upon our further study, we have found that a further improved yield of acrylonitrile can be attained by use of a catalyst comprising molybdenum, bismuth, lead, antimony, iron and/or chromium, and oxygen within a certain range of composition or a catalyst comprising further tungsten, cerium, magnesium potassium and/or lithium within a certain range of composition, and accomplished this invention.
It is an object of this invention to provide an improved catalytic composition having long life which can be used in commercial production of unsaturated nitriles including acrylonitrile to advantage.
In accordance with the present invention, the above-mentioned objective is accomplished by a catalyst composition having the formula:
(Mo).sub.a (W).sub.b (Bi).sub.c (Pb).sub.d (Sb).sub.e (A).sub.f (B).sub.g (C).sub.h (P).sub.m (O).sub.n
in which A is iron and/or chromium, B is cerium and/or magnesium and C is potassium and/or lithium; and a, b, c, d, e, f, g, h, m and n stand for the numbers of atoms for molybdenum, tungsten, bismuth, lead, antimony, A, B, C, phosphorus and oxygen elements respectively, wherein, given that a+b=12,
0.ltoreq.b.ltoreq.7, 0.4.ltoreq.c.ltoreq.7, 2.ltoreq.d.ltoreq.12,
0.1/22.ltoreq.e/a.ltoreq.25/22, 0.05/22.ltoreq.f/a.ltoreq.3/22,
0.ltoreq.g/a.ltoreq.2/22, 0.ltoreq.h/a.ltoreq.3/22,
0.ltoreq.m/a.ltoreq.7/22, and
n is the numbers of oxygen necessary to satisfy the valences of atoms for the individual constituent elements other than oxygen.
DESCRIPTION OF THE PREFERRED EMBODIMENT
As mentioned above, the catalytic compositions of this invention are represented by the formula:
(Mo).sub.a (W).sub.b (Bi).sub.c (Pb).sub.d (Sb).sub.e (A).sub.f (B).sub.g (C).sub.h (P).sub.m (O).sub.n
in which A is iron and/or chromium, B is cerium and/or magnesium and C is potassium and/or lithium; and a, b, c, d, e, f, g, h, m, n stand for the numbers of atoms for molybdenum, tungsten, bismuth, lead, antimony, A, B, C, phosphorus and oxygen elements respectively, wherein, given that a+b=12,
0.ltoreq.b.ltoreq.7, 0.4.ltoreq.c.ltoreq.7, 2.ltoreq.d.ltoreq.12,
0.1/22.ltoreq.e/a.ltoreq.25/22, 0.05/22.ltoreq.f/a.ltoreq.3/22,
0.ltoreq.g/a.ltoreq.2/22, 0.ltoreq.h/a.ltoreq.3/22,
0.ltoreq.m/a.ltoreq.7/22, and
n is the numbers of oxygen necessary to satisfy the valences of atoms for the individual constituent elements other than oxygen.
In these formulae, it is preferred in order to improve the selectivity of the catalyst toward the desired unsaturated nitriles that the numbers of atoms for the individual constituent elements (i.e., values, a to h and m) satisfy the following equations: given that a+b=12,
0.ltoreq.b.ltoreq.5.5, 0.6.ltoreq.c.ltoreq.6, 2.6.ltoreq.d.ltoreq.11,
1/22.ltoreq.e/a.ltoreq.10/22, 0.05/22.ltoreq.f/a.ltoreq.2/22,
0.ltoreq.g/a.ltoreq.1/22, 0.ltoreq.h/a.ltoreq.2/22
0.ltoreq.m/a.ltoreq.2/22
Preferable combinations of the atoms of the catalytic composition are as follows:
Mo-W-Bi-Pb-Sb-Fe-O
Mo-W-Bi-Pb-Sb-Fe-Cr-O
Mo-W-Bi-Pb-Sb-Fe-Mg-O
Mo-W-Bi-Pb-Sb-Fe-P-O
Mo-W-Bi-Pb-Sb-Fe-Li,K-P-O
MO-W-Bi-Pb-Sb-Fe-Mg-Li,K-O
Mo-W-Bi-Pb-Sb-Fe-Ce-O
Mo-W-Bi-Pb-Sb-Fe-Ce-P-O
Mo-W-Bi-Pb-Sb-Fe-Ce-Li,K-P-O
Mo-W-Bi-Pb-Sb-Fe-Fe-Cr-Mg-O
MO-W-Bi-Pb-Sb-Fe-Cr-Mg-Li,K-O
Mo-W-Bi-Pb-Sb-Fe-Cr-Mg-Li,K-P-O
Mo-W-Bi-Pb-Sb-Fe-Cr-Ce-O
Mo-W-Bi-Pb-Sb-Fe-Cr-Ce-Li,K-O
Mo-W-Bi-Pb-Sb-Fe-Cr-Ce-Li,K-P-O
Mo-W-Bi-Pb-Sb-Fe-Cr-Li,K-O
Mo-W-Bi-Pb-Sb-Fe-Cr-Li,K-P-O
Mo-W-Bi-Pb-Sb-Fe-Mg-P-O
Mo-W-Bi-Pb-Sb-Fe-Mg-Li,K-P-O
The catalytic composition of this invention may be shaped with or without a carrier material such as silica, titania, alumina, silicon carbide or the like. The size and geometry of the shaped catalyst are not critical and the catalytic composition may be shaped into catalyst particles of any size and geometry (e.g., pellets, tablets, granules, etc.) depending on the conditions under which it is used.
Molybdenum compounds useful for the preparation of the catalytic composition of this invention include molybdenum oxides such as molybdenum trioxide, molybdic acid and its salts, and phosphomolybdic acid and its salts. Preferably molybdates such as ammonium paramolybdate are used. Useful tungsten compounds include tungsten oxides such as tungsten trioxide, tungstic acid and condensed tungstic acid and their salts such as ammonium paratungstate, and phosphotungstic acid and its salts, Bismuth compounds that can be used include bismuth salts such as bismuth nitrate and bismuth sulfate and various oxides and hydroxides of bismuth. Useful lead compounds include lead salts such as lead nitrate and lead sulfate and various oxides and hydroxides of lead. useful antimony compounds include oxides such as antimony trioxide, chlorides such as antimony trichloride and metallic antimony. Useful iron compounds include iron salts such as iron nitrate and iron sulfate and various oxides and hydroxides of iron. Useful chromium compounds include chromium salts such as chromium nitrate, chromium sulfate and ammonium dichromate and various oxides and hydroxides of chromium. Useful cerium compounds include cerium salts such as cerium nitrate and cerium sulfate and various oxides and hydroxides of cerium. Useful magnesium compounds include magnesium salts such as magnesium nitrate and magnesium chloride and various oxides and hydroxides of magnesium.
Lithium and potassium compounds that can be used include carbonates such as lithium carbonate and potassium carbonate and nitrates such as lithium nitrate and potassium nitrate and hydroxides such as lithium hydroxide and potassium hydroxide. Useful phosphorus compounds include phosphoric acids such as orthophosphoric acid and metaphosphoric acid and phosphates such as ammonium phosphate, and oxides such as phosphorus pentaoxide and phosphorus chloride oxide and heteropolyphosphoric acids such as phosphomolybdic acid and phosphotungstic acid, salts of these acids, and organophosphorus compounds.
The catalytic composition can be prepared from the appropriate combination of these raw materials by dissolving or suspending the compounds of the constituent elements in water to form a uniform aqueous slurry or solution. In some cases, a sol of a carrier material such as silica sol or alumina sol or carrier particles such as titania powder may be suspended in the slurry or solution. The resulting uniform slurry or solution is then evaporated to dryness and shaped in separate steps or in a single step by spray drying and finally calcined in a stream of air to prepare a catalyst. When shaping is made by spray drying, the catalyst having improved impact strength can be obtained by controlling the pH of the material slurry between 1 and 6 before spray drying. In preparation of the catalyst, when ammonium paramolybdate and/or ammonium paratungstate is used as the molybdenum and/or tungsten source, respectively, a dissolution accelerator such as ammonia is preferably added to the aqueous medium in order to increase the solubility of these compounds. In the case where bismuth nitrate or bismuth sulfate is employed as the bismuth source, it is preferably dissolved in a water acidified with nitric acid or sulfuric acid correspondingly. When antimony trioxide is used as the antimony source, it may be added after it has been dissolved in an aqueous solution of an organic acid such as tartaric acid, or otherwise it may be added directly in the form of powdered antimony trioxide. In the latter case, the resulting final slurry containing all the catalytic components including the antimony trioxide powder can be uniformly stirred, adjusted to pH 7 or less and heated at 40.degree. C. or higher for 1 to 8 hours to further improve the selectivity of the finally obtained catalytic composition toward unsaturated nitriles. In this case, iron compounds may be added after heating if desired. Following the shaping step, the shaped particles are usually calcined for 5 minutes to 5 hours at a temperature in the range of 400.degree. to 800.degree. C., preferably in the range of 500.degree. to 750.degree. C., although the temperature and duration of the calcination step are not critical.
The catalytic compositions of this invention can be used in the following way. The following description is limited to the production of acrylonitrile, it is to be understood that the catalytic compositions can be used for the production of other unsaturated nitriles as well. In order to produce acrylonitrile, propylene, ammonia and oxygen or an oxygen-containing gas are contacted in the vapor phase in the presence of a catalyst according to this invention (e.g., one prepared in any of the following Examples). It is not always necessary that the starting propylene gas is of high purity, and the propylene gas may contain a substantial amount of other gas which is substantially inert to the reaction, for example, a saturated hydrocarbon such as propane. The oxygen used may be either pure oxygen gas or diluted with other gas or gases inert to the reaction. In a commercial operation air is usually employed as the oxygen-containing gas. The molar ratio of oxygen to propylene fed to the reaction zone are usually in the range of 0.8:1 to 4:1. Ammonia is fed in an amount of 0.8 to 2.5 moles, preferably 0.9 to 1.5 moles per mole of propylene. The vapor-phase reaction is usually conducted at atmospheric pressure, but it may be carried out at a subatmospheric or superatmospheric pressure as required. The reaction temperature is usually from 360.degree. to 540.degree. C., preferably from 400.degree. to 500.degree. C. The space velocity at which the gaseous reactants are fed may suitably be selected from the range of 100 to 3,000 hr.sup.-1, preferably 200 to 2,000 hr.sup.-1.
The catalytic compositions of this invention may be used either in the fixed or fluidized bed system.
As previously mentioned, the catalytic compositions of this invention are capable of formation of acrylonitrile with high selectivity even at an increased conversion of the starting gaseous material and hence they can be employed in the commercial production of acrylonitrile to advantage.

Having generally described the invention, a more complete understanding can be obtained by reference to certain examples which are provided herein for purposes of illustration only and are not intended to be limiting in any manner.
The terms "conversion", "selectivity" and "yield of acrylonitrile" used herein, particularly in the examples are defined by the following equations: ##EQU1##
EXAMPLE 1
To a solution of 0.0392 g of ammonium paratungstate [(NH.sub.4).sub.10 W.sub.12 O.sub.41.5H.sub.2 O] in 2 ml of aqueous 1 wt. % ammonia was added with stirring 15.54 g of 20 wt. % silica sol, and the following solutions were added with stirring in that order: a solution of 3.030 g of lead nitrate in 5.9 ml of water; a solution of 2.225 g of ammonium paramolybdate [(NH.sub.4).sub.6 Mo.sub.7 O.sub.24.4H.sub.2 O] in 11.5 ml of aqueous 5 wt. % ammonia; a solution of 1.164 g of bismuth nitrate in 1.8 ml of aqueous 10 wt. % nitric acid; one tenth of a solution of 2.08 g of commercially available antimony trioxide powder dissolved under heating in a mixture of 8.6 ml of water, 1.7 ml of aqueous 25 wt. % ammonia and 3.2 g of tartaric acid; and a solution of 0.0242 g of iron (III) nitrate [Fe(NO.sub.3).sub.3.9H.sub.2 O] in 0.5 ml of water. An aqueous 10 wt. % nitric acid solution was then added to the resulting slurry to adjust the pH of the slurry to 2.2, and then heated with stirring on a hot plate until the evolution of NO.sub.2 ceased, and the heating was continued until the slurry was evaporated to dryness. The solid residue was compressed into tablets of 6 mm in diameter and 3 mm in thickness, which were calcined at 700.degree. C. for 2 hours in a stream of air and then crushed to give a catalyst in the form of granules of 16 to 24 mesh (Tyler) in size. The catalyst thus obtained had the composition: Mo.sub.11.86 W.sub.0.14 Bi.sub.2.26 Pb.sub.8.61 Sb.sub.1.35 Fe.sub.0.056 O.sub.50.11 which was supported on a carrier comprising silica. The weight ratio of silica to total catalytic components was 40:60.
A pyrex reactor of 4 mm inner diameter was packed with 0.5 ml of the supported catalyst was prepared above. A mixed gas of propylene, ammonia and air having a molar ratio of propylene to ammonia to air of 1:1.2:10 was passed at a space velocity of 1,000 hr.sup.-1 through the catalyst bed in tubular reactor held at 470.degree. C. to produce acrylonitrile. The reaction was carried out for 1.5 hours. The results were 94.4% conversion of propylene and 88.0% selectivity toward acrylonitrile (with 83.0% yield of acrylonitrile).
EXAMPLES 2-6
Following the procedure described in Example 1, various catalysts of composition indicated in Table 1 were prepared and used in the ammoxidation of propylene at temperatures indicated in Table 1. The results are also reported in Table 1.
EXAMPLE 7
To a suspension of 0.5247 g of commercially available antimony trioxide powder in 13 ml of water was added a solution of 0.0392 g of ammonium paratungstate [(NH.sub.4).sub.10 W.sub.12 O.sub.41.5H.sub.2 O] in 2 ml of aqueous 1 wt. % ammonia, followed by 16.79 g of 20 wt. % silica sol with stirring. Thereafter the following solutions were added successively with stirring: a solution of 3.030 g of lead nitrate in 5.9 ml of water; a solution of 2.225 g of ammonium paramolybdate [(NH.sub.4).sub.6 Mo.sub.7 O.sub.24.4H.sub.2 O] in 11.5 ml of aqueous 5 wt. % ammonia; a solution of 1.164 g of bismuth nitrate in 1.8 ml of aqueous 10 wt. % nitric acid; and a solution of 0.3232 g of iron (III) nitrate [Fe(NO.sub.3).sub.3.9H.sub.2 O] in 6 ml of water. The resulting slurry was adjusted to pH 2.2 with an aqueous 10 wt. % nitric acid solution, and then heated with stirring on a hot plate until the evolution of NO.sub.2 ceased, whereupon it was evaporated to dryness. The solid residue was compressed into tablets of 6 mm in diameter and 3 mm in thickness, which were calcined at 650.degree. C. for 2 hours in a stream of air and then crushed to give a catalyst in the form of granules of 16 to 24 mesh (Tyler).
Using 1 ml of the catalyst, the ammoxidation of propylene was carried out using the same reactor as in Example 1 and using a mixed gas of the same composition in Example 1, which was passed at a space velocity of 500 hr.sup.-1. The reaction was carried out for 1.5 hours. The composition of the catalyst and the results of the ammoxidation reaction are shown in Table 2.
EXAMPLE 8
The procedure of Example 7 was repeated except that the catalyst was prepared from a slurry which further contained 0.0132 g of aqueous 85 wt. % orthophosphoric acid. The composition of the catalyst and the results of the reaction are shown in Table 2.
EXAMPLE 9
To a suspension of 0.3498 g of commercially available antimony trioxide powder in 8.7 ml of water was added a solution of 0.0392 g of ammonium paratungstate [(NH.sub.4).sub.10 W.sub.12 O.sub.41.5H.sub.2 O] in 2 ml of aqueous 1 wt. % ammonia, followed by 16.21 g of 20 wt. % silica sol with stirring. Thereafter the following solutions were added successively with stirring: a solution of 3.030 g of lead nitrate in 5.9 ml of water; a solution of 2.225 g of ammonium paramolybdate [(NH.sub.4).sub.6 Mo.sub.7 O.sub.24.4H.sub.2 O] in 11.5 ml of aqueous 5 wt. % ammonia; and a solution of 1.164 g of bismuth nitrate in 1.8 ml of aqueous 10 wt. % nitric acid. The resulting slurry was adjusted to pH 2.8 with an aqueous 10 wt. % nitric acid solution, and was placed in a three-necked flask and heated under reflux for 3 hours at 100.degree. C. During this heating, the pH of the slurry rose from 2.8 to 3.6 and it was readjusted to 2.2. To this slurry a solution of 0.03232 g of iron (III) nitrate [Fe(NO.sub.3).sub.3.9H.sub.2 O] in 6 ml of water was added and the pH of the slurry was readjusted to 2.2, and then heated with stirring on a hot plate until the evolution of NO.sub.2 ceased, whereupon it was evaporated to dryness. The solid residue was compressed into tablets of 6 mm in diameter and 3 mm in thickness, which were calcined at 700.degree. C. for 2 hours in a stream of air and then crushed to give a catalyst in the form of granules of 16 to 24 mesh (Tyler).
Using 1 ml of the catalyst, the ammoxidation of propylene was carried out under the same conditions as in Example 8. The composition of the catalyst and the results of the ammoxidation reaction are shown in Table 2.
EXAMPLES 10-12
The procedure of Example 9 was repeated except that the heating of the slurry under reflux at 100.degree. C. was omitted. The composition of the catalyst and the results of the ammoxidation reaction are shown in Table 2.
EXAMPLE 13
The procedure of Example 12 was repeated except that the catalyst was prepared from a slurry which further contained a solution of the precipitate of potassium phosphotungstate (P.sub.2 O.sub.5.24WO.sub.3.42H.sub.2 O). This solution was obtained by adding a solution of 6.9 mg of potassium carbonate (K.sub.2 CO.sub.3) in 0.3 ml of water to a solution of 107.7 mg of commercially available phosphotungstic acid (P.sub.2 O.sub.5.24WO.sub.3.42H.sub.2 O) in 5 ml of water.
The composition of the catalyst and the results of the reaction are shown in Table 2.
COMPARATIVE EXAMPLE 1
The procedure of Example 1 was repeated except that iron (III) nitrate [Fe(NO.sub.3).sub.3.9H.sub.2 O] was not used. The composition of the catalyst and the results of the reaction are shown in Table 1.
COMPARATIVE EXAMPLE 2
The procedure of Example 1 was repeated except that antimony trioxide was not used. The composition of the catalyst and the results of the reaction are shown in Table 1.
EXAMPLE 14
To a solution of 0.0392 g of ammonium paratungstate [(NH.sub.4).sub.10 W.sub.12 O.sub.41.5H.sub.2 O] in 2 ml of aqueous 1 wt. % ammonia was added with stirring 16.14 g of 20 wt. % silica sol, and the following solutions were added with stirring in that order: a solution of 3.030 g of lead nitrate in 5.9 ml of water; a solution of 2.225 g of ammonium paramolybdate [(NH.sub.4).sub.6 Mo.sub.7 O.sub.24.4H.sub.2 O] in 11.5 ml of aqueous 5 wt. % ammonia; a solution of 1.164 g of bismuth nitrate in 1.8 ml of aqueous 10 wt. % nitric acid; one tenth of a solution of 3.43 g of commercially available antimony trioxide powder dissolved under heating in a mixture of 14.2 ml of water, 2.80 ml of aqueous 25 wt. % ammonia and 5.3 g of tartaric acid; a solution of 0.115 g of iron (III) nitrate [Fe(NO.sub.3).sub.3.9H.sub.2 O] in 3 ml of water; and a solution of 0.138 g of chromium nitrate [Cr(NO.sub.3).sub.3.9H.sub.2 O] in 3 ml of water. An aqueous 10 wt. % nitric acid solution was then added to the resulting slurry to adjust the pH of the slurry to 2.2, and then heated with stirring on a hot plate until the evolution of NO.sub.2 ceased, and the heating was continued until the slurry was evaporated to dryness. The solid residue was compressed into tablets of 6 mm in diameter and 3 mm in thickness, which were calcined at 700.degree. C. for 2 hours in a stream of air and then crushed to give a catalyst in the form of granules of 16 to 24 mesh (Tyler) in size. The catalyst thus obtained had the composition: Mo.sub.11.86 W.sub.0.14 Bi.sub.2.26 Pb.sub.8.61 Sb.sub.2.21 Fe.sub.0.27 Cr.sub.0.32 O.sub.52.20 which was supported on a carrier comprising silica. The weight ratio of silica to total catalytic components was 40:60.
A pyrex reactor of 4 mm inner diameter was packed with 1 ml of supported catalyst as prepared above. A mixed gas of propylene, ammonia and air having a molar ratio of propylene to ammonia to air of 1:1.2:10 was passed at a space velocity of 500 hr.sup.-1 through the catalyst bed in tubular reactor held at 460.degree. C. to produce acrylonitrile. The reaction was carried out for 1.5 hours. The results were 98.6% conversion of propylene and 86.2% selectivity toward acrylonitrile (with 85.0% yield of acrylonitrile).
EXAMPLES 15-19
Following the procedure described in Example 14, various catalysts of composition indicated in Table 3 were prepared and used in the ammoxidation of propylene at temperatures indicated in Table 3. The results are also reported in Table 3.
COMPARATIVE EXAMPLE 3
The procedure of Example 14 was repeated except that iron (III) nitrate [Fe(NO.sub.3).sub.3.9H.sub.2 O] was not used and the amount of chromium nitrate [Cr(NO.sub.3).sub.3.9H.sub.2 O] was increased. The composition of the catalyst and the results of the reaction are shown in Table 3.
COMPARATIVE EXAMPLE 4
The procedure of Example 16 was repeated except that antimony trioxide was not used.
The composition of the catalyst and the results of the reaction are shown in Table 3.
EXAMPLE 20
The procedure of Example 14 was repeated except that iron (III) nitrate [Fe(NO.sub.3).sub.3.9H.sub.2 O] was not used and the amount of chromium nitrate [Cr(NO.sub.3).sub.3.9H.sub.2 O] was increased. The composition of the catalyst and the results of the reacton are shown in Table 3.
TABLE 1__________________________________________________________________________Composition of Catalyst Reaction(Atomic Ratio) Temp. % Conversion % Selectivity % YieldEx. No. Mo w Bi Pb Sb Fe O (.degree.C.) of Propylene toward AN* of AN*__________________________________________________________________________1 11.86 0.14 2.26 8.61 1.35 0.056 50.11 470 94.4 88.0 83.12 11.86 0.14 2.26 8.61 1.46 0.11 50.36 470 95.0 87.5 83.13 11.86 0.14 2.26 8.61 1.73 0.27 51.00 470 95.0 87.0 82.74 11.86 0.14 2.26 8.61 1.91 0.43 51.51 470 95.1 87.1 82.85 11.86 0.14 2.26 8.61 2.10 0.59 52.04 470 96.3 86.0 82.86 11.86 0.14 2.26 8.61 1.73 0.43 51.24 470 97.5 86.2 84.0Comp. Ex. 11.86 0.14 2.26 8.61 1.08 49.62 470 91.4 88.0 80.4Comp. Ex. 11.86 0.14 2.26 8.61 0.05 48.08 470 95.7 79.8 76.42__________________________________________________________________________ *AN = Acrylonitrile (Reaction Time: 1.5 hours)
TABLE 2__________________________________________________________________________ % Reaction Conversion %Composition of Catalyst (Atomic Ratio) Temp. of Selectivity % YieldEx. No. Mo W Bi Pb Sb Fe P K O (.degree.C.) Propylene toward AN* of AN*__________________________________________________________________________7 11.86 0.14 2.26 8.61 3.40 0.75 54.23 450 98.5 85.1 83.88 11.86 0.14 2.26 8.61 3.40 0.75 0.11 54.50 460 98.4 86.2 84.89 11.86 0.14 2.26 8.61 2.26 0.75 52.52 460 98.6 85.6 84.410 11.86 0.14 2.26 8.61 2.26 0.75 52.52 460 99.1 84.6 83.811 11.78 0.22 3.49 6.76 1.71 0.16 50.80 460 99.1 86.0 85.212 11.86 0.14 2.26 8.61 1.88 0.75 51.95 460 99.5 83.4 83.013 11.49 0.51 2.19 8.34 1.83 0.73 0.03 0.09 51.59 460 99.1 84.6 83.8__________________________________________________________________________ *AN = Acrylonitrile (Reaction Time: 1.5 hours)
TABLE 3__________________________________________________________________________ Reaction %Composition of Catalyst (Atomic Ratio) Temp. % Conversion Selectivity % YieldEx. No. Mo W Bi Pb Sb Fe Cr O (.degree.C.) of Propylene toward AN* of AN*__________________________________________________________________________14 11.86 0.14 2.26 8.61 2.21 0.27 0.32 52.50 460 98.6 86.2 85.015 11.86 0.14 2.26 8.61 1.94 0.27 0.16 51.56 460 98.9 85.8 84.916 11.86 0.14 2.26 8.61 2.32 0.38 0.22 52.38 460 98.5 86.0 84.717 11.86 0.14 2.26 8.61 2.21 0.43 0.16 52.20 450 97.5 86.5 84.318 11.85 0.15 1.67 9.53 2.26 0.30 0.36 52.42 460 98.7 85.6 84.519 11.87 0.13 2.76 7.88 2.00 0.25 0.30 51.85 460 98.6 85.7 84.520 11.86 0.14 2.26 8.61 2.21 0.59 52.20 460 99.5 84.4 84.0Comp. Ex. 11.86 0.14 2.26 8.61 2.21 2.70 55.37 470 99.5 75.9 75.5Comp. Ex. 11.86 0.14 2.26 8.61 0.38 0.22 48.9 470 100 74.3 74.34__________________________________________________________________________ *AN = Acrylonitrile (Reaction Time: 1.5 hours)
EXAMPLE 21
Using 1 ml of the same catalyst of Example 3, the ammoxidation of propylene was carried out at 460.degree. C. using the same reactor as in Example 1 and using a mixed gas of the same composition in Example 1, which was passed at a space velocity of 500 hr.sup.-1.
The results of the reaction after 1.5 hours are shown in Table 4. The continuous reaction was carried out for further 15 hours, and the selectivity toward acrylonitrile was increased to a fixed value shown in Table 4.
EXAMPLE 22
The procedure of Example 21 was repeated except that a mixed gas of propylene, ammonia and air having a molar ratio of propylene to ammonia to air of 1:1.1:10 was used.
The results obtained after the reaction was carried out for 16.5 hours are shown in Table 4.
EXAMPLES 23 AND 24
The procedures of Examples 21 and 22 were repeated using the same catalyst of Example 5. The results are summarized in Table 4.
EXAMPLE 25
The procedure of Example 22 was repeated except that the catalyst was prepared as in Example 3 from a slurry which further contained 1 ml of aqueous cerium nitrate [Ce(NO.sub.3).sub.3.6H.sub.2 O] solution contaning 0.1 atom cerium per liter.
The composition of the catalyst and the results of the reaction are shown in Table 5.
EXAMPLE 26
The procedure of Example 25 was repeated except that the catalyst was prepared from a slurry which further contained 1. ml of aqueous potassium carbonate (K.sub.2 CO.sub.3) solution containing 0.1 atom potassium per liter.
The composition of the catalyst and the results of the reaction are shown in Table 5.
EXAMPLE 27
The procedure of Example 26 was repeated except that the catalyst was prepared from a slurry which further contained 0.0132 g of aqueous 85 wt. % orthophosphoric acid. The composition of the catalyst and the results of the reaction are shown in Table 5.
EXAMPLE 28
The procedure of Example 24 was repeated except that the catalyst was prepared as in Example 5 from a slurry which further contained 1.1 ml of aqueous magnesium nitrate [Mg(NO.sub.3).sub.2.6H.sub.2 O] solution containing 0.1 atom magnesium per liter.
The composition of the catalyst and the results of the reaction are shown in Table 5.
EXAMPLE 29
The procedure of Example 28 was repeated except that the catalyst was prepared from a slurry which further contained 1.7 ml of aqueous lithium nitrate (LiNO.sub.3) solution containing 0.1 atom lithium per liter.
The composition of the catalyst and the results of the reaction are shown in Table 5.
EXAMPLE 30
The procedure of Example 29 was repeated except that the catalyst was prepared from a slurry which further contained 0.01 g of aqueous 85 wt. % orthophosphoric acid. The composition of the catalyst and the results of the reaction are shown in Table 5.
EXAMPLE 31
The procedure of Example 14 was repeated except that continuous reaction was carried out for 16.5 hours. The results are shown in Table 6.
EXAMPLE 32
The procedure of Example 31 was repeated except that a mixed gas of propylene, ammonia and air having a molar ratio of propylene to ammonia to air of 1:1.1:10 was used. The continuous reaction was carried out for 16.5 hours. The results are shown in Table 6.
EXAMPLE 33
The procedure of Example 32 was repeated except that the catalyst was prepared as in Example 14 from a slurry which further contained 0.55 ml of aqueous potassium carbonate (K.sub.2 CO.sub.3) solution containing 0.1 atom potassium per liter. The composition of the catalyst and the results of the reaction are shown in Table 6.
EXAMPLE 34
The procedure of Example 33 was repeated except that the catalyst was prepared from a slurry which further contained 0.55 ml of aqueous orthophosphoric acid solution containing 0.1 atom phosphorus per liter. The composition of the catalyst and the results of the reaction are shown in Table 6.
EXAMPLE 35
The procedure of Example 32 was repeated except that the catalyst was prepared from a slurry which further contained 1.1 ml of aqueous magnesium nitrate [Mg(NO.sub.3).sub.2.6H.sub.2 O] solution containing 0.1 atom magnesium per liter. The composition of the catalyst and the results of the reaction are shown in Table 6.
EXAMPLE 36
The procedure of Example 35 was repeated except that the catalyst was prepared from a slurry which further contained 1.1 ml of aqueous potassium carbonate (K.sub.2 CO.sub.3) solution containing 0.1 atom potassium per liter. The composition of the catalyst and the results of the reaction are shown in Table 6.
EXAMPLE 37
The procedure of Example 36 was repeated except that the catalyst was prepared from a slurry which further contained 1.1 ml of aqueous orthophosphoric acid solution containing 0.1 atom phosphorus per liter. The composition of the catalyst and the results of the reaction are shown in Table 6.
EXAMPLE 38
The procedure of Example 32 was repeated except that the catalyst was prepared from a slurry which further contained 1 ml of aqueous cerium nitrate [Ce(NO.sub.3).sub.3.6H.sub.2 O] solution containing 0.1 atom cerium per liter. The composition of the catalyst and the results of the reaction are shown in Table 6.
EXAMPLE 39
The procedure of Example 38 was repeated except that the catalyst was prepared from a slurry which further contained 1.1 ml of aqueous potassium carbonate (K.sub.2 CO.sub.3) solution containing 0.1 atom potassium per liter. The composition of the catalyst and the results of the reaction are shown in Table 6.
EXAMPLE 40
The procedure of Example 39 was repeated except that the catalyst was prepared from a slurry which further contained 1.1 ml of aqueous orthophosphoric acid solution containing 0.1 atom phosphorus per liter.
The composition of the catalyst and the results of the reaction are shown in Table 6.
TABLE 4__________________________________________________________________________ Composition of Raw Material Gas Reaction Reaction (molar ratio) Time Temp. % Conversion % Selectivity % YieldEx. No. PPY*/NH.sub.3 /Air (hr) (.degree.C.) of Propylene toward AN* of AN*__________________________________________________________________________21 1/1.2/10 1.5 460 98.1 85.8 84.2 1/1.2/10 16.5 460 98.1 86.7 85.122 1/1.1/10 16.5 460 98.1 84.7 83.123 1/1.2/10 1.5 460 98.2 85.8 84.3 1/1.2/10 16.5 460 98.0 87.1 85.424 1/1.1/10 16.5 460 98.0 85.6 83.9__________________________________________________________________________ *PPY = Propylene *AN = Acrylonitrile
TABLE 5__________________________________________________________________________ Reaction % Conver- %Ex. Composition of Catalyst (Atomic Ratio) Temp. sion of Selectivity % YieldNo. Mo W Bi Pb Sb Fe Ce Mg Li K P O (.degree.C.) Propylene toward of__________________________________________________________________________ AN*22 11.86 0.14 2.26 8.61 1.73 0.27 51.0 460 98.1 84.7 83.125 11.86 0.14 2.26 8.61 1.73 0.27 0.09 51.14 460 98.2 85.7 84.226 11.86 0.14 2.26 8.61 1.73 0.27 0.09 0.11 51.20 460 98.0 86.4 84.727 11.86 0.14 2.26 8.61 1.73 0.27 0.09 0.11 0.11 51.48 460 97.5 87.6 85.424 11.86 0.14 2.26 8.61 2.1 0.59 52.04 460 98.0 85.6 83.928 11.86 0.14 2.26 8.61 2.1 0.59 0.11 52.15 460 99.1 85.8 85.029 11.86 0.14 2.26 8.61 2.1 0.59 0.11 0.16 52.23 460 98.9 86.7 85.730 11.86 0.14 2.26 8.61 2.1 0.59 0.11 0.16 0.08 52.43 460 98.5 87.5 86.2__________________________________________________________________________ *AN = Acrylonitrile
TABLE 6__________________________________________________________________________ Re- % action % Conver- SelectivityEx. Composition of Catalyst (Atomic Ratio) Temp. sion of toward % YieldNo. Mo W Bi Pb Sb Fe Cr Ce Mg Li K P O (.degree.C.) Propylene AN*.sup.2 of__________________________________________________________________________ AN*.sup.231*.sup.1 11.86 0.14 2.26 8.61 2.21 0.27 0.32 52.2 460 98.5 87.3 86.032 11.86 0.14 2.26 8.61 2.21 0.27 0.32 52.2 460 98.5 86.4 85.133 11.86 0.14 2.26 8.61 2.21 0.27 0.32 0.05 52.23 460 98.0 87.2 85.534 11.86 0.14 2.26 8.61 2.21 0.27 0.32 0.05 0.05 52.35 460 97.6 88.1 86.035 11.86 0.14 2.26 8.61 2.21 0.27 0.32 0.11 52.31 460 99.0 87.1 86.236 11.86 0.14 2.26 8.61 2.21 0.27 0.32 0.11 0.11 52.37 460 98.8 87.7 86.637 11.86 0.14 2.26 8.61 2.21 0.27 0.32 0.11 0.11 0.11 52.64 460 98.3 88.6 87.138 11.86 0.14 2.26 8.61 2.21 0.27 0.32 0.05 52.28 460 98.5 87.1 85.839 11.86 0.14 2.26 8.61 2.21 0.27 0.32 0.05 0.05 52.31 460 98.2 87.8 86.240 11.86 0.14 2.26 8.61 2.21 0.27 0.32 0.05 0.05 0.05 52.44 460 97.9 88.8 86.9__________________________________________________________________________ *.sup.1 Ex. 31 PPY/NH.sub.3 /Air = 1/1.2/10 Ex. 32-40 PPY/NH.sub.3 /Air = 1/1.1/10 *.sup.2 AN = Acrylonitrile
EXAMPLE 41
The catalyst of the same composition as in Example 3 was prepared as follows:
To a solution of 78.4 g of ammonium paratungstate [(NH.sub.4).sub.10 W.sub.12 O.sub.41.5H.sub.2 O] in 1 l of aqueous 1 wt. % ammonia was added with stirring 31.08 Kg of 20 wt. % silica sol, and the following solutions were added with stirring in that order: a solution of 6.06 Kg of lead nitrate in 11.3 l of water; a solution of 4.450 Kg of ammonium paramolybdate [(NH.sub.4).sub.6 Mo.sub.7 O.sub.24.4H.sub.2 O] in 8.5 l of aqueous 5 wt. % ammonia; a solution of 2.328 Kg of bismuth nitrate in 2.70 l of aqueous 10 wt. % nitric acid; a solution of 554.7 g of commercially available antimony trioxide powder dissoled under heating in a mixture of 2.3 l of water, 453 ml of aqueous 25 wt. % ammonia and 850 g of tartaric acid; and a solution of 242 g of iron (III) nitrate [Fe(NO.sub.3).sub.3.9H.sub.2 O] in 2.75 l of water. An aqueous 67 wt. % nitric acid solution was then added to the resulting slurry to adjust the pH of the slurry to 2.2. The resulting slurry was homogenized by the homogenizer and spray dried in usual way using the spray dryer having rotating disk and calcined at 715.degree. C. at a residence time of 14 minutes continuously using rotary calcination kiln and the catalyst of 57.mu. diameter was obtained. A fluidized bed reactor of 2.5 inch inner diameter was packed with 1,850 g of the supported catalyst as prepared above. A mixed gas of propylene, ammonia and air having a molar ratio of propylene to ammonia to air of 1:1.1:12.7 was passed at a 0.068 hr.sup.-1 feed of propylene per 1 g of catalyst in the reactor held at 480.degree. C. and 0.85 kg/cm.sup.2 G to produce acrylonitrile.
The variation of catalytic activity with time was investigated. The results are shown in Table 7 below.
COMPARATIVE EXAMPLE 5
To a solution of 261 g of ammonium paratungstate [(NH.sub.4).sub.10 W.sub.12 O.sub.41.5H.sub.2 O] in 3.3 l of aqueous 1 wt. % ammonia was added with stirring 350 g of commercially available antimony trioxide powder and 32.6 kg of 20 wt. % silica sol, and the following solutions were added with stirring in that order: a solution of 6.29 kg of lead nitrate in 11.7 l of water; a solution of 4.450 kg of ammonium paramolybdate [(NH.sub.4).sub.6 Mo.sub.7 O.sub.24.4H.sub.2 O] in 8.5 l of aqueous 5 wt. % ammonia; and a solution of 2.328 kg of bismuth nitrate in 2.7 l of aqueous 10 wt. % nitric acid. An aqueous 67 wt. % nitric acid solution was then added to the resulting slurry to adjust the pH of the slurry to 4.2. Separately a solution of 13.8 g of potassium carbonate (K.sub.2 CO.sub.3) in 500 ml of water was added to a solution of 215.4 g of phosphotungstic acid (P.sub.2 O.sub.5.24WO.sub.3.42H.sub.2 O) in 1 l of water. This mixture solution was added to the above slurry and the resulting slurry was placed in a three-necked flask and heated under reflux for 3 hours at 100.degree. C. During this heating, the pH of the slurry rose from 4.2 to 5.0 and it was readjusted to 4.2.
The resulting slurry was homogenized by the homogenizer and spray dried in usual way using the spary dryer having rotating disk and calcined at 685.degree. C. at a residence time of 14 minutes continuously using the rotary calcination filn and the catalyst of 50.mu. diameter was obtained. The catalyst thus obtained had the composition: Mo.sub.11.2 W.sub.0.8 Bi.sub.2.1 Pb.sub.8.4 Sb.sub.1.07 K.sub.0.09 P.sub.0.03 O.sub.49.28 which was supported on a carrier comprising silica. The weight ratio of silica to toal catalytic components was 40:60. Using 1,850 g of the catalyst ammoxidation was carried out in the same way as in Example 41.
TABLE 7______________________________________ Reaction Time % Conversion % Selectivity % YieldRun (hr) of Propylene toward AN* of AN*______________________________________1 20 98.1 81.0 79.52 100 97.0 82.0 79.53 150 96.4 82.5 79.54 200 96.2 82.6 79.5______________________________________
TABLE 8______________________________________ Reaction Time % Conversion % Selectivity % YieldRun (hr) of Propylene toward AN* of AN*______________________________________1 20 98.7 79.1 78.12 100 97.2 80.2 78.03 150 95.7 80.6 77.14 200 94.3 81.0 76.4______________________________________ *AN = Acrylonitrile
Having now fully described the invention, it will be apparent to one of ordinary skill in the art that many changes and modifications can be made thereto without departing from the spirit or scope of the invention as set forth herein.

Number	Name	Date
4035418	Okada et al.	Jul 1977
4113770	Okiyama et al.	Sep 1978
4155938	Yamamoto et al.	May 1979
4259211	Krabetz et al.	Mar 1981
4280928	Kirch et al.	Jul 1981
4290922	Amemura et al.	Sep 1981
4341659	Kogeyama et al.	Jul 1982

Number	Date	Country
2626	Dec 1978	EPX
564	Jul 1979	EPX
1497589	Jan 1978	GBX

Catalytic composition

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (7)

Foreign Referenced Citations (3)