Claims
- 1. A process for converting feedstock hydrocarbon compounds to product hydrocarbon compounds having a lower molecular weight than the feedstock hydrocarbon compounds which comprises contacting said feedstock at conversion conditions with a catalyst composition comprising catalyst manufactured by the method comprising the steps of:
- forming a first slurry comprising clay and a source of phosphorus;
- mixing said first slurry with an acid stable zeolite component to form a second slurry; and
- spray drying said second slurry at a pH of below 3.
- 2. The process of claim 1 wherein said second slurry is spray dried at a pH of less than or equal to 2.
- 3. The process of claim 1 wherein the contact time between said clay and said source of phosphorus prior to said mixing step is less than 30 minutes.
- 4. The process of claim 1 wherein the contact time between said clay and said source of phosphorus prior to said mixing step is less than 15 minutes.
- 5. The process of claim 1 wherein the catalyst composition is calcined prior to said contacting.
- 6. The process of claim 1 wherein said acid stable zeolite has a SiO.sub.2 /Al.sub.2 O.sub.3 molar ratio of at least about 23/1.
- 7. The process of claim 1 wherein said source of phosphorus is selected from the group consisting of phosphoric acid, ammonium dihydrogen phosphate, ammonium monohydrogen phosphate, triammonium phosphate, ammonium hypophosphate, ammonium orthophosphate, ammonium dihydrogen orthophosphate, ammonium monohydrogen orthophosphate, ammonium hypophosphite, ammonium dihydrogen orthophosphite, and mixtures thereof.
- 8. The process of claim 1 wherein said source of phosphorus is phosphoric acid.
- 9. The process of claim 1 wherein said clay comprises Kaolin.
- 10. The process of claim 1 wherein said acid stable zeolite component comprises crystalline material having the structure of ZSM-5.
- 11. The process of claim 1 wherein said conversion conditions include temperature of from about 400.degree. C. to about 650.degree. C. and a pressure of from atmospheric to about 5 atmospheres.
- 12. The process of claim 1 wherein said conversion conditions include an average reactor temperature of from about 450.degree. C. to about 540.degree. C., a catalyst/oil volume ratio of from about 2 to about 7, and a space volume hourly velocity of from about 1 to about 5.
- 13. The process of claim 1 wherein said conversion conditions include a riser top temperature of from about 500.degree. C. to about 595.degree. C., a catalyst/oil weight ratio of from about 3 to about 12, and a catalyst residence time of from about 0.5 to about 15 seconds.
- 14. The process of claim 1 wherein said acid-stable zeolite component comprises a large-pore molecular sieve material having pore openings of greater than about 7 Angstroms.
- 15. The process of claim 14 wherein the large-pore molecular sieve material is selected from the group consisting of zeolites REY, USY, REUSY, dealuminated Y, ultrahydrophobic Y, silicon-enriched dealuminated Y, ZSM-20, Beta, L, silicoaluminophosphates SAPO-5, SAPO-37, SAPO-40, MCM-9, metalloaluminophosphate MAPO-36, aluminophosphate VPI-5, and mesoporous crystalline MCM-41.
- 16. The process of claim 15 wherein the large-pore molecular sieve material comprises REY, USY, or REUSY.
- 17. The process of claim 1 wherein said feedstock comprises a gas oil having an initial boiling point above about 204.degree. C. and an end point of at least about 315.degree. C.
- 18. The process of claim 1 wherein said feedstock comprises deep cut gas oil, vacuum gas oil, thermal oil, residual oil, cycle stock, whole top crude, tar sand oil, shale oil, or a
- 19. The process of claim 18 wherein said feedstock comprises residual oil or deep cut gas oil.
- 20. The process of claim 1 wherein said catalyst composition further comprises from about 0.01 ppm to about 100 ppm by weight of an oxidation promoter selected from the group consisting of platinum, palladium, iridium, osmium, rhodium, ruthenium, rhenium, and combination thereof.
- 21. A process for cracking feedstock hydrocarbon compounds to product comprising gasoline and olefins of 3 to 4 carbon atoms which comprises contacting said feedstock at cracking conditions including a temperature of from about 400.degree. C. to about 650.degree. C. with a catalyst composition comprising catalyst manufactured by the method comprising the steps of:
- forming a first slurry comprising clay and a source of phosphorus;
- mixing said first slurry with an acid stable zeolite component to form a second slurry; and
- spray drying said second slurry at a pH of below 3.
- 22. The process of claim 21 wherein said zeolite component comprises crystalline material having the structure of ZSM-5.
- 23. The process of claim 21 wherein said zeolite component comprises a large-pore molecular sieve material having pore openings of greater than about 7 Angstroms.
- 24. The process of claim 23 wherein the large-pore molecular sieve material comprises REY, USY, or REUSY.
- 25. The process of claim 21 wherein said catalyst composition further comprises from about 0.01 ppm to about 100 ppm by weight of an oxidation promoter selected from the group consisting of platinum, palladium, iridium, osmium, rhodium, ruthenium, rhenium, and combination thereof.
- 26. A process for converting feedstock hydrocarbon compounds to product hydrocarbon compounds having a lower molecular weight than the feedstock hydrocarbon compounds which comprises contacting said feedstock at conversion conditions with a catalyst composition comprising catalyst manufactured by the method comprising the steps of:
- forming a slurry comprising clay, a source of phosphorus, and an acid stable zeolite component; and
- spray drying said slurry at a pH of below 3.
- 27. A process for cracking feedstock hydrocarbon compounds to product comprising gasoline and olefins of 3 to 4 carbon atoms which comprises contacting said feedstock at cracking conditions including a temperature of from about 200.degree. C. to about 870.degree. C. with a catalyst composition comprising catalyst manufactured by the method comprising the steps of:
- forming a slurry comprising clay, a source of phosphorus, and an acid stable zeolite component; and
- spray drying said slurry at a pH of below 3.
CROSS-REFERENCE TO RELATED APPLICATION
This is a continuation-in-part of application Ser. No. 07/667,854, filed Mar. 12, 1991, now U.S. Pat. No. 5,231,064.
US Referenced Citations (11)
Foreign Referenced Citations (1)
Number |
Date |
Country |
0358261 |
Mar 1990 |
EPX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
667854 |
Mar 1991 |
|