Catalytic polymerization process

Abstract

This invention relates to a process for controlling the architecture of copolymers of at least two unsaturated monomers, made by free radical polymerization in the presence of a cobalt-containing chain transfer agent, including the control of molecular weight degree of branching and vinyl end group termination, by varying at least one of the variables of molar ratio of monomers, their relative chain transfer constants, polymerization temperature and degree of conversion and amount of cobalt chain transfer agent; and polymers made thereby.

Description

BACKGROUND OF THE INVENTION

Catalytic chain transfer is an effective way to control the molecular weight of polymers of methacrylates and styrenes. It is known that chain transfer catalysis (CTC) products contain a terminal vinylidene bond. This feature makes these products attractive as macromonomers for a variety of applications. However, CTC has not been known to be applicable for reduction of molecular weight in the polymerizations of other vinylic monomers such as acrylates.

Copolymerizations of methacrylate monomers with monosubstituted monomers in the presence of cobalt have been described in the art. However, the monosubstituted monomer is almost always present as a minor component. U.S. Pat. No. 4,680,354 describes molecular weight reduction using various Co(II) complexes in MMA-BA, MMA-EA and MMA-BA-St copolymerizations, wherein the abbreviations represent:

• • MMA=methyl methacrylate
  • BA=butyl acrylate
  • EA=ethyl acrylate
  • St=styrene.

U.S. Pat. No. 5,324,879 describes molecular weight reduction with Co(III) complexes in EA, St, and vinyl acetate (VAc) polymerizations, and MMA-EA copolymerization.

U.S. Pat. No. 4,680,352 describes molecular weight reduction and macromonomer (polymers or copolymers with unsaturated end-groups) synthesis in copolymerizations with acrylates and styrene with various Co(II) complexes. Various terpolymerizations are cited therein; however, no evidence of the nature or existence of terminal double bonds is given.

Gruel et al., Polymer Preprints, 1991, 32, p. 545, reports the use of Co(II) cobaloximes in low conversion St-MMA copolymerizations at low temperatures with end group analysis.

The references cited above cover the copolymerization of acrylates and styrene with methacrylate monomers, but do not disclose synthetic conditions for production of high purity macromonomers based on acrylates and styrene, nor branching of the resulting products. The conditions disclosed are unlikely to yield high purity macromonomers for systems composed predominantly of monosubstituted monomers. Disclosed temperatures of less than 80° C. are likely to provide substantial amounts of undesired graft copolymer at high conversion rates.

SUMMARY OF THE INVENTION

This invention concerns an improvement in a process for the free-radical polymerization of at least two unsaturated monomers to form a polymer whose molecular architecture comprises properties of molecular weight, branching, and vinyl-terminated end groups, the monomers having the formula CH₂═CXY wherein

• • X is selected from the group consisting of H, CH₃, and CH₂OH;
  • Y is selected from the group consisting of OR, O₂CR, halogen, CO₂H, COR, CO₂R, CN, CONH₂, CONHR, CONR₂ and R′;
  • R is selected from the group consisting of substituted and unsubstituted alkyl, substituted and unsubstituted aryl, substituted and unsubstituted heteroaryl, substituted and unsubstituted aralkyl, substituted and unsubstituted alkaryl, and substituted and unsubstituted organosilyl, the substituents being the same or different and selected from the group consisting of carboxylic acid, carboxylic ester, epoxy, hydroxyl, alkoxy, primary amino, secondary amino, tertiary amino, isocyanato, sulfonic acid and halogen; and the number of carbons in said alkyl groups is from 1 to 12; and
  • R′ is selected from the aromatic group consisting of substituted and unsubstituted aryl, substituted and unsubstituted heteroaryl, the substituents being the same or different and selected from the group consisting of carboxylic acid, carboxylic ester, epoxy, hydroxyl, alkoxy, primary amino, secondary amino, tertiary amino, isocyanato, sulfonic acid, substituted and unsubstituted alkyl, substituted and unsubstituted aryl, substituted and unsubstituted olefin and halogen;
  • by contacting said monomers with a cobalt-containing chain transfer agent and a free radical initiator at a temperature from about 80′ to 170° C.;
  • the improvement which comprises controlling polymer architecture by introducing into the presence of the chain transfer agent at least one each of monomers A and B in the molar ratio of A:B, said molar ratio lying in the range of about 1,000:1 to 2:1, wherein for monomer A X is H and for monomer B X is methyl or hydroxymethyl; by one or more of the following steps:
  • I decreasing the ratio of A:B from about 1,000:1 toward 2:1;
  • II increasing the temperature from above 80° C. toward 170° C.;
  • III increasing the conversion of monomer to polymer toward 100% from less than about 50%;
  • IV decreasing the ratio of the chain transfer constant of A:B to below 1; and
  • V increasing the concentration of cobalt chain transfer agent; whereby:
  • to effect lower molecular weight, employ at least one of steps I, II, IV and V;
  • to effect a higher degree of vinyl-terminated end groups, employ at least one of steps I, II, IV, and V; and
  • to effect increased branching, employ at least one of steps I, II, IV, and V with step III.

The nature of the derived products changes as a function of time. In the initial stages, linear macromonomers with one monomer-A in the terminal position can be obtained as essentially the only product. If the cobalt CTC catalyst levels are relatively low then CTC does not occur after every B-monomer insertion and the product mixture can include monomer-B units in the polymer chain as well as in the terminal position.

Cobalt chain transfer agent is employed in the form of cobalt complexes. Their concentrations are provided in the Examples in terms of ppm by weight of total reaction mass. Concentration will vary from 10 ppm to 1,500 ppm, preferably 10 to 1,000 ppm.

Later in the course of the reaction, when the concentration of the two above products is increased, then they can be reincorporated into a growing polymer chain. Thus, mono-branched product is obtained in the later stages of the reaction, usually around 90% conversion. At conversions above 95%, branches begin to appear on the branches, and the polymer becomes hyperbranched as conversions approach 100%.

Preferred monomers A are selected from the group consisting of acrylates, acrylonitrile and acrylamides;

and preferred monomers B are selected from the group:

• • a) substituted or unsubstituted α-methylstyrenes;
  • b) substituted or unsubstituted alkyl methyacrylates, where alkyl is C₁-C₁₂;
  • c) methacrylonitrile;
  • d) substituted or unsubstituted methacrylamide:
  • e) 2-chloropropene,
  • f) 2-fluoropropene,
  • g) 2-bromopropene,
  • h) methacrylic acid,
  • i) itaconic acid,
  • j) itaconic anhydride, and
  • k) substituted or unsubstituted styrenics.

If branched polymers are the desired product, it is possible to initiate the described process in the presence of preformed macromonomers. They can be of the type described in this patent. They can also be macromonomers based entirely upon methacrylates or the related species described previously in U.S. Pat. No. 4,680,354. Such a process would lead to products fitting the description above, but would allow for greater control over the polymer end-groups.

The branched polymers made by said process are polymers of this invention having the formula:

• Y is as earlier defined;
• n=1-20, m=1-5, p=1-20, and n+m+p≧3, and
• Z is selected from the group CH₂CHYCH₃, CH₂CMeYCH₃, and, optionally,
• m′=0-5, p′=0-20; n+m′+p′≧2;
• and if m or m′>1, the m or m′ insertions respectively are not consecutive.

This invention also concerns a process comprising selecting A and B so the ratio of their chain transfer constants is less than 1, whereby functionality derived from Monomer B will be located on the vinyl-terminated end of the polymer.

This invention also concerns an improved process for the free-radical polymerization of at least two unsaturated monomers having the formula CH₂═CXY wherein

• • X is selected from the group consisting of H, CH₃, and CH₂OH;
  • Y is selected from the group consisting of OR, O₂CR, halogen, CO₂H, CO₂R, CN, CONH₂, CONHR, CONR₂, COR and R′;
  • R is selected from the group consisting of substituted and unsubstituted alkyl, substituted and unsubstituted aryl, substituted and unsubstituted heteroaryl, substituted and unsubstituted aralkyl, substituted and unsubstituted alkaryl, and substituted and unsubstituted organosilyl, the substituents being the same or different and selected from the group consisting of carboxylic acid, carboxylic ester, epoxy, hydroxyl, alkoxy, primary amino, secondary amino, tertary amino, isocyanato, sulfonic acid and halogen, and the number of carbons in said alkyl groups is from 1 to 12; and
  • R′ is selected from the aromatic group consisting of substituted and unsubstituted aryl, substituted and unsubstituted heteroaryl, the substituents being the same or different and selected from the group consisting of carboxylic acid, carboxylic ester, epoxy, hydroxyl, alkoxy, primary amino, secondary amino, tertiary amino, substituted and unsubstituted alkyl, substituted and unsubstituted aryl, substituted and unsubstituted olefin and halogen;
  • by contacting said monomers with a cobalt-containing chain transfer agent and a free radical initiator at a temperature from about 80° C. to 170° C.;
  • the improvement which comprises controlling molecular weight of the polymer architecture by introducing into the presence of the chain transfer agent at least one each of monomers C and D in the molar ratio of C:D in the range of about 1,000:1 to 2:1, in which for monomer C, X is H and Y≠R′ and for monomer D, X is H and Y=R′ by:
  • decreasing the ratio of C:D from about 1,000:1 toward 2:1; or
  • increasing the temperature from above 80° C. toward 170° C.

Preferred monomers A are selected from the group consisting of acrylates, acrylonitrile and acrylamides;

• • and preferred monomers B are substituted and unsubstituted styrenics.

The polymers made by said process improvement are polymers of this invention having the formula: where Y≠R′ and n≧1.

This invention also concerns a process improvement for polymerizing monomer(s) in the presence of an excess of a nonpolymerizable olefin, Y¹Y²C═CY³Y⁴. The product in the initial stages of the polymerization will be composed primarily of wherein:

• • Y¹ and Y³, and optionally Y² and Y⁴, are each independently selected from the group consisting of —CH(O), —CN, —C(O)OR⁵, —C(O)NR⁶R⁷, —CR⁸(O), alkyl, aryl, substituted alkyl, substituted aryl; or
  • where Y¹ and Y³ or Y² and Y⁴ are combined in a cyclic structure which includes any of the above functionalities, or can be —C(O)—(CH₂)_x—, —C(O)—O—(CH₂)_x—, —C(O)O—C(O)—, —C(O)(CH₂)_x—, —C(O)NR⁹—(CH₂)_x—, wherein x=1-12, R⁵, R⁶, R⁷, R⁸, or R⁹ are hydrogen, alkyl, aryl, substituted alky, or substituted aryl; and where at least one of Y¹ and Y³ is selected from the group consisting of —CH(O), —CN, —C(O)OR⁵, —C(O)NR⁶R⁷, —CR⁸(O), aryl, substituted aryl; and the remaining of Y² and Y⁴ are —H.

The polymers made by said process improvement are polymers of this invention produced at later stages of the polymerization process having the formula:

• • where Z=H, CH₃, CH₂CHYCH₃, CH₂CMeYCH₃, or
  • k=0 or 1, n=0-20, m=0-5, p=0-20; and k+n+m+p≧2; if m>1, then it is not intended to imply that the m insertions are consecutive;
  • Y is selected from the group consisting of OR, O₂CR, halogen. CO₂H, COR, CO₂R, CN, CONH₂, CONHR, CONR₂ and R′; and
  • Y¹ to Y⁴ and R, and R′ are as defined above.

DETAILS OF THE INVENTION

We have discovered that, with addition of small amounts of an α-methylvinyl monomer and appropriate choice of reaction conditions, polymerization of monosubstituted monomers in the presence of a metal complex can provide high yield of macromonomers. These macromonomers can subsequently be used for the synthesis of a wide range of block and graft copolymers.

This invention concerns a method for the synthesis of ω unsaturated macromonomers composed predominantly of monosubstituted monomers. The macromonomers are prepared by polymerizing a monosubstituted monomer as the major component (for example styrene) in the presence of a disubstituted α-methylvinyl monomer (for example, α-methylstyrene, herein also referred to as “AMS”) and a catalytic amount of a cobalt complex [for example, Co(II)(DMG-BF2)2] called CoII in Scheme 1. Reaction Scheme 1 illustrates the process where monomer A=styrene and monomer B=α-methylstyrene. The process is applicable to a wide range of monosubstituted monomers (for example acrylate esters, vinyl acetate (VAc)) and other non-α-methylvinyl monomers.

In Scheme 1, “Ph” represents a phenyl group, and “m” designates the number of monomer units in the polymer, and is ≧1.

The key features of the invention are the addition of small amounts of α-methylvinyl monomers and the use of high reaction temperatures in the presence of chain transfer catalysts.

The incorporation of α-methylvinyl monomers into the recipe allows formation of the desired macromonomer end group. In the absence of the α-methylvinyl monomer, polymerization of monosubstituted monomers give polymers with internal double bonds (styrenic monomer) or a stable alkyl-cobalt species (acrylate monomers) as chain ends.

The use of high reaction temperatures (>100° C.) favors the formation of pure linear macromonomers from monosubstituted monomers (for example acrylates, vinyl esters, and styrene). At lower temperatures we have shown that the formed macromonomers can react further by copolymerization to give branched polymers. Even though the macromonomers can undergo further reaction, at reaction temperatures >100° C., the radicals so formed do not propagate to give branched polymers. Rather, they fragment to give back a macromonomer. It is possible that this chemistry will also reduce the polydispersity of the final product.

The invention also provides a route to block or graft copolymers as illustrated in Scheme 2. The product derived by copolymerization of the macromonomer in the presence of monomers can be determined by appropriate choice of the monomer and the reaction conditions. In Scheme 2, “Ph” represents a phenyl group; “m”, “n” and “o” designate the number of monomer units in the polymer; and X and Y are as defined above.

We have demonstrated that styrene macromonomers prepared by the above mentioned copolymerization route give chain transfer (by an addition fragmentation mechanism) and have acceptable chain transfer constants at temperatures >100° C. They should therefore be useful in the preparation of block copolymers.

One further aspect of the invention is that by appropriate choice of the α-methylvinyl monomer the method is also a route to end-functional polymers. For example, use of a hydroxyethyl- or glycidyl-functional monomer would yield polymers with ω-hydroxy or ω-epoxy groups, respectively.

This method enables the versatility and robustness of the cobalt technology to be utilized to form macromonomers that are comprised predominantly of monosubstituted monomers. Additionally, it provides the key step in a new and less expensive route to end-functional and block or graft copolymers based on monosubstituted monomers. Copolymerizations of monosubstituted monomers with other α-methylvinyl monomers (for example α-methylstyrene) in the presence of cobalt are contemplated.

The choice of the α-methyvinyl comonomer is important in macromonomer synthesis. It must be chosen so that the reactivity towards cobalt (“catalytic chain transfer constant”) of the derived propagating species is substantially greater than that of the propagating species derived from the monosubstituted monomer.

Two factors influence this reactivity.

• • a) The rate of the chain transfer reaction between the propagating species and the cobalt complex;
  • b) The relative concentrations of the propagating species. This is determined not only by the monomer concentration but also by the propagation rate constants and reactivity ratios.

While methacrylate esters can be used as α-methylvinyl comonomers (see examples), in copolymerization with styrene, the values of the reactivity ratios and propagation rate constants will favor the formation of styryl chain ends. The product then has an internal rather than the desired terminal double bond. Methacrylate esters are acceptable comonomers in, for example, acrylate polymerizations.

Thus, the use of α-methylvinyl comonomers (for example, α-methylstyrene, methacrylonitrile) which have low propagation rate constants and high chain transfer rate constants are preferred.

There are substantial cost improvements over alternative technologies which involve the use of stoichiometric amounts of an organic transfer agent. The ability to use acrylate/styrenic rich macromonomers, in contexts similar to those developed for methacrylate monomers products by cobalt mediated processes, for example, in graft, star, block and branched copolymer syntheses, further extends the value of the process.

The nature of the derived products changes as a function of time. In the initial stages, the product can be obtained as essentially the only product. If the cobalt CTC catalyst levels are relatively low then CTC does not occur after every B-monomer insertion and the product mixture can include:

Later in the course of the reaction, when the concentration of the two above products is increased, they can be reincorporated into a growing polymer chain. Thus, the product where Z can include —H, —CH₃, CH₂CHYCH₃, CH₂CMeYCH₃, or is obtained. In the early stages of the reaction, Z is most often H, but as the reaction proceeds toward 90% conversion, Z begins to include more of the higher molecular weight species as branches. At conversions above 95%, branches begin to appear on the branches, and the polymer becomes hyperbranched as conversions approach 100%.

Metal complexes are those that give catalytic chain transfer with α-methylvinyl monomers. Examples include, but are not limited to, cobalt(II) and cobalt(III) chelates:

• • Co(II)(DPG-BF₂)₂ J=K=Ph, L=ligand
  • Co(II)(DMG-BF₂)₂ J=K=Me, L=ligand
  • Co(II)(EMG-BF₂)₂ J=Me, K=Et, L=ligand
  • Co(II)(DEG-BF₂)₂ J=K=Et, L=ligand
  • Co(II)(CHG-BF₂)₂ J=K=—(CH₂)₄—, L=ligand
  • QCo(III)(DPG-BF₂)₂ J=K=Ph, R=alkyl, L=ligand
  • QCo(III)(DMG-BF₂)₂ J=K=Me, R=alkyl, L=ligand
  • QCo(III)(EMG-BF₂)₂ J=Me, K=Et, R=alkyl, L=ligand
  • QCo(III)(DEG-BF₂)₂ J=K=Et, R=alkyl, L=ligand
  • QCo(III)(CHG-BF₂)₂ J=K=—(CH₂)₄—, R=alkyl, L=ligand
  • QCo(III)(DMG-BF₂)₂ J=K=Me, R=halogen, L=ligand

L can be a variety of additional neutral ligands commonly known in coordination chemistry. Examples include water, amines, ammonia, phosphines. The catalysts can also include cobalt complexes of a variety of porphyrin molecules such as tetraphenylporphyrin, tetraanisylporphyrin, tetramesitylporphyrin and other substituted species.

α-Methylvinyl monomers (B monomers) have the general structure where Y is as described above in the “Summary”. R is an optionally substituted alkyl (such as fluoroalkyl, hydroxyalkyl, or epoxyalkyl), organosilyl, or aryl group. Preferred examples of α-methylvinyl monomers (B monomers) include methacrylate esters, α-methylstyrene and methacrylonitrile.

“A” monomers have the general structure:

• • where Y is as described above in the “Summary”

The enhanced utility of the polymerization method discussed in this invention is that it extends each of these general CTC methodologies:

• • i) molecular weight control is extended from methacrylates and styrenes to include acrylates, vinyl esters, and other higher activity monomer species;
  • ii) macromonomer synthesis is extended to the monomers in (i) while retaining the desirable vinyl termination of the resulting species;
  • iii) end-functional polymer synthesis is also extended to the monomers in (i);
  • iv) the use of macromonomers as chain transfer agents is extended to include monomer classes heretofore unavailable through CTC technology; and
  • v) not only are a wider range of block and graft copolymers available through the use of CTC technology, but now it is possible to prepare branched and even hyperbranched species through single-pot reactions.

It is preferred to employ free-radical initiators and solvents in the process of this invention. The process can be run in batch, semi-batch, continuous, bulk, emulsion or suspension mode.

Most preferred A-monomers are:

methyl acrylate, ethyl acrylate, propyl acrylate (all isomers), butyl acrylate (all isomers), 2-ethylhexyl acrylate, isobornyl acrylate, acrylic acid, benzyl acrylate, phenyl acrylate, acrylonitrile, glycidyl acrylate. 2-hydroxyethyl acrylate, hydroxypropyl acrylate (all isomers), hydroxybutyl acrylate (all isomers), diethylaminoethyl acrylate, triethyleneglycol acrylate, N-tert-butyl acrylamide, N-n-butyl acrylamide, N-methyl-ol acrylamide, N-ethyl-ol acrylamide, trimethoxysilylpropyl acrylate, triethoxysilylpropyl acrylate, tributoxysilylpropyl acrylate, dimethoxymethylsilylpropyl acrylate, diethoxymethylsilylpropyl acrylate, dibutoxymethylsilylpropyl acrylate, diisopropoxymethylsilylpropyl acrylate, dimethoxysilylpropyl acrylate, diethoxysilylpropyl acrylate, dibutoxysilylpropyl acrylate, diisopropoxysilylpropyl acrylate, vinyl acetate, styrene, diethylamino styrene, P-methylstyrene, vinyl benzoic acid, vinylbeuzinsulfonic acid, vinyl propionate, vinyl butyrate, vinyl benzoate, vinyl chloride, vinyl fluoride, vinyl bromide.

Most preferred B-monomers are:

methyl methacrylate, ethyl methacrylate, propyl methacrylate (all isomers), butyl methacrylate (all isomers), 2-ethylhexyl methacrylate, isobornyl methacrylate, methacrylic acid, benzyl methacrylate, phenyl methacrylate, methacrylonitrile, alpha methyl styrene, trimethoxysilylpropyl methacrylate, triethoxysilylpropyl methacrylate, tributoxysilylpropyl methacrylate, dimethoxymethylsilylpropyl methacrylate, diethoxymethyl-silylpropylmethacrylate, dibutoxymethylsilylpropyl methacrylate, diisopropoxymethylsilylpropyl methacrylate, dimethoxysilylpropyl methacrylate, diethoxysilylpropyl methacrylate, dibutoxysilylpropyl methacrylate, diisopropoxysilylpropyl methacrylate, isopropenyl butyrate, isopropenyl acetate, isopropenyl benzoate, isopropenyl chloride, isopropenyl fluoride, isopropenyl bromideitaconic aciditaconic anhydridedimethyl itaconate, methyl itaconateN-tert-butyl methacrylamide, N-n-butyl methacrylamide, N-methyl-ol methacrylamide, N-ethyl-ol methacrylamide, isopropenylbenzoic acid (all isomers), diethylamino alphamethylstyrene (all isomers), para-methyl-alpha-methylstyrene (all isomers), diisopropenylbenzene (all isomers), isopropenylbenzene sulfonic acid (all isomers), methyl 2-hydroxymethylacrylate, ethyl 2-hydroxymethylacrylate, propyl 2-hydroxymethylacrylate (all isomers), butyl 2-hydroxymethylacrylate (all isomers), 2-ethylhexyl 2-hydroxymethylacrylate, isobornyl 2-hydroxymethylacrylate, and TMI® dimethyl Meta-Isopropenylbenzyl Isocyanate.

Preferred C monomers are those from the list of A monomers minus the styrenic family.

Preferred D monomers include the following styrenes:

styrene, vinyl benzoic acid (all isomers), diethylamino styrene (all isomers), para-methylstyrene (all isomers), and vinyl benzene sulfonic acid (all isomers),

Typical products of the reaction at lower conversions include the linear products from methyl acryjate and methyl methacrylate:

• • from butyl acrylate and alpha-methylstyrene:
  • from hydroxyethyl acrylate and alpha-methylstyrene:
  • from vinyl benzoate and butyl methacrylate:

Typical products of the reaction at lower conversions include the linear products from butyl acrylate and methyl methacrylate: from methyl acrylate and alpha-methylstyrene:

When the polymerization (for example butyl acrylate as A-monomer and methyl methacrylate as B-monomer) is carried out in the presence of a nonpolymerizable olefin such as 2-pentenenitrile, the product in the initial stages of the polymerization will be:

• • and later in the polymerization, the product will be:

It becomes impractical to draw schematics of any of the higher degrees of branching that are obtained as the conversion of the polymerization approaches 100%.

Oligomers, macromonomers and polymers made by the present process are useful in a wide variety of coating and molding resins. Other potential uses can include cast, blown, spun or sprayed applications in fiber, film, sheet, composite materials, multilayer coatings, photopolymerizable materials, photoresists, surface active agents, dispersants, adhesives, adhesion promoters, coupling agents, compatibilizers and others. End products taking advantage of available characteristics can include, for example, automotive and architectural coatings or finishes, including high solids, aqueous or solvent based finishes. Polymers, such as those produced in this invention, will find use in, for example, structured polymers for use in pigment dispersants.

K⁺IDS mass spectroscopy is an ionization method that produces pseudomolecular ions in the form of [M]K⁺ with little or no fragmentation. Intact organic molecules are desorbed by rapid heating. In the gas phase, the organic molecules are ionized by potassium attachment. Potassium ions are generated from an aluminosilicate matrix that contains K₂O. All of these experiments were performed on a Finnegan Model 4615 GC/MS quadrupole mass spectrometer (Finnegan MAT (ISA), San Jose, Calif.). An electron impact source configuration operating at 200° C. and a source pressure of <1×10⁻⁶ torr was used. MALDI was also performed on this instrument.

All MW and DP measurements were based on gel permeation chromatography (GPC) using styrene as a standard.

Definitions

The following abbreviations have been used and are defined as:

• TAPCo=meso-tetra(4-methoxyphenyl)porphyrin-Co; VAZO®-88=1,1′-azobis(cyclohexane-1-carbonitrile) (DuPont Co., Wilmington, Del.); VRO-110=2,2′-azobis(2,4,4-trimethylpentane) (Wako Pure Chemical Industries, Ltd., Osaka, Japan);
• DP=degree of polymerization. M_n is number average molecular weight and M_w is weight average molecular weight. AIBN is azoisobutyronitrile. THF is tetrahydrofuran. MA=methylacrylate.

EXAMPLES

Examples 1-9

Synthesis of Low Molecular Weight Styrene Macromonomers

AMS Comonomer

Feed Polymerization

Examples 1-3 and Control 1 show that molecular weight control is obtained in the absence of added α-methylstyrene. The products have structure 1 with an internal double bond and do not function as macromonomers.

Solution polymerization of styrene with α-methylstyrene (10:1) and iPrCo(III)(DMG-BF₂)₂ isopropylcobalt(III)(DMG) (100 ppm) in n-butyl acetate at 125° C.

	n-butyl acetate	20.04	g
	styrene (sty)	10.03	g
	α-methylstyrene	1.00	g
Shot:	iPrCo(III)(DMG-BF2)2	1.4	mg
	n-butyl acetate	5.00	g
Feed 1:	1,1′-azobis(4-cyclohexanecarbonitrile)	0.093	g
(0.063 mL/min	n-butyl acetate	6.73	g
over 120 min)	iPrCo(III)(DMG-BF2)2	4.6	mg
Feed 2:	styrene	13.57	g
(0.139 mL/min	α-methylstyrene	1.57	g
over 120 min)

The butyl acetate was degassed in a 5 neck 250 mL reactor, equipped with condenser, stirred, and N₂ purge. The monomers were added and degassed for a further 10 minutes. The reactor was heated to reflux (ca 125° C.) and the shot of iPrCo(III)(DMG-BF₂)₂/solvent added. The monomer and initiator feeds were started immediately. The reactor was sampled at regular intervals to monitor intermediate molecular weights (GPC, THF) and conversions (¹H NMR, CDCl₃). A sample of this low viscosity yellow liquid was precipitated into a twenty fold excess of methanol, and the macromonomer recovered as a fine white powder. {overscore (M)}_n 1270, {overscore (M)}_w/{overscore (M)}_n 1.43, 34% conversion. The precipitated samples were examined by ¹H NMR (200 MHz, CDCl₃) to establish the nature of the chain ends.

The unsaturated end groups give rise to signals as follows: styryl end group internal double bond (1): δ6.1 —CH(Ph)—CH═CH-Ph; δ3.1 CH(Ph)—CH═CH-Ph. Alpha methyl styrene- (AMS)-derived terminal methylene double bond (2): δ4.8 1H and δ5.2 1H, —C(Ph)=CH₂ (the ratio of the signals at δ6.1 and δ4.8 was found to give the best estimate of terminal double bond content. Although this utilises a signal on the fringe of the broad aromatic resonance δ7.6-7.2, a series of comparisons of the ¹H-NMR molecular weights calculated from the end groups with those obtained by GPC showed that this gave better results than the signal at δ3.1). This may be due to the internal double bond product being a mixture of (1) and (3).

TABLE 1.1
Polymerization of styrene in presence of AMS
and iPrCo(III) (DMG-BF2)2 at 125° C.
	Time	[Co(III)]	Sty:
Example	(min)	ppm	AMS	{overscore (M)}n	{overscore (M)}w	{overscore (M)}w/{overscore (M)} n	Conv.1 %	[2]2%
1	30	100	—	1050	2290	2.18
	60	100		1150	2540	2.21	3
	120	100		1100	2590	2.18	5
	ppt	100		1630		1.69		0
2	60	50	—	2010	4150	2.06	3
	120	50		1720	3980	2.30	5
	ppt	50		1940		2.03		0
3	60	25	—	3270	11153	3.41	3
	120	25		2710	9540	3.52	5
	ppt	25	—	2750		3.26		0
Control 1	60	0	—	32230	54760	1.70	2
	120	0		33830	59450	1.76	4
	180	0		38060	63750	1.68	5
	240	0		39510	67150	1.70	6
	300	0		37420	67630	1.81	7
	360	0		39420	67070	1.70	8	0
4	30	100	10:1	730	1840	2.38
	60	100		740	1670	2.25	1
	120	100		690	1430	2.06	3
	ppt	100		1270		1.43		32
5	60	50	10:1	1170	2540	2.17	2
	120	50		1040	2300	2.21	4
	ppt	50		1470		1.80		56
6	60	25	10:1	1370	2890	2.11	2
	120	25		1270	2690	2.11	3
	ppt	25		1660		1.89		65
Control 2	20	0	10:1	19696	50460	2.56	n.d
	40	0		14860	37950	2.55	n.d
	60	0		17060	38890	2.28	1
	120	0		24430	42040	1.72	3
	240			27440	51420	1.87	4
	360	0		29400	52930	1.80	6	0
7	60	100	5:1	380	930	2.45
	120	100		140	870	2.10
	ppt	100		1310		1.83		—
8	60	50	5:1	810	1670	2.06	1
	120	50		780	1530	1.96	2
	ppt	50		1180		1.53		68
9	60	25	5:1	1760	3480	1.98	2
	120	25		1640	3160	1.93	3
	ppt	25		2140		1.60		100
Control 3	60	0	5:1	16740	32450	1.94
	120	0		19540	35020	1.79
	ppt	0		19570		1.83		0
1Determined by 1H NMR
2%2, remainder is 1 and 3 estimated by 1H NMR

Examples 10-12

Synthesis of High Molecular Weight Styrene Macromonomers

AMS Comonomer

Feed Polymerization

These Examples were run according to the same procedure of Examples 1 through 3.

TABLE 1.2
Polymerization of styrene in presence of AMS
and iPrCo(III)(DMG-BF2)2 at 125° C.
	reaction	[Co(III)]					% terminal
Ex.	time (h)	(ppm)	Sty/AMS	{overscore (M)}nc	{overscore (M)}w/{overscore (M)}	% conv.	alkene
10	2	8	5/1	7455	(120)	2.4	14	—
		(0.13/0.37)3		9442	(ppt)	1.95		>705
114	1	8	5/1	4648	(60)	1.81	12	—
		(0.13/0.37)3		5160	(ppt)	1.64		>705
12	2	13	5/1	2660	(120)	1.87	20	—
		(0.25/0.75)3		3300	(ppt)	1.63		>705
Numbers in parenthesis indicate reaction times.
3amount, in mg, added in (shot/feed).
4rate of cobalt complex feed twice that for example 10.
5internal methylene was not visible in the 1H-nmr spectrum.

Examples 13-18

Control 4-6

Synthesis of Styrene Macromonomers

AMS Comonomer

Batch Polymerizations in Sealed Tube—Effect of Reaction Temperature

Batch polymerizations were conducted in sealed tubes to establish the effect of temperature on macromonomer purity (%2). Molecular weights and macromonomer purities are similar to those obtained in the feed polymerization experiments (refer Table 1.1).

A mixture of styrene (1.3 g, 12.5 mmol), α-methylstyrene (0.15 g, 1.27 mmol) (monomer ratio: 10/1), n-butyl acetate (3 g), VR®-110 (8.9×10⁻⁵ g, 20 ppm) and iPrCo(III)(DMG-BF₂)₂ (for concentrations see Table 1.3) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 125° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by H-nmr and GPC.

TABLE 1.3
Batch polymerization of styrene in presence of AMS and
iPrCo(III)(DMG-BF2)2 at 125° C. with VR ®-110 initiator
	Sty/AMS	[Co(III)]				% terminal
Example	ratio	ppm	{overscore (M)}n	{overscore (M)}w/{overscore (M)} n	% conv	AMS
Control 4	10/1	0	64547	1.72	5-9	—
Control 5	5/1	0	53498	1.77	4-7	—
13	10/1	100	445	1.61	1-4	36
14	10/1	50	751	1.76	4-6	39
15	10/1	25	1408	1.79	7-9	54

TABLE 1.4
Batch polymerization of styrene in presence
of AMS and iPrCo(III)(DMG-BF2)2 at 80° C.
with AIBN initiator.
						%
	Sty/AM	[Co(III)]				terminal
Example	ratio	ppm	{overscore (M)}n	{overscore (M)}w/{overscore (M)}n	% conv	AMS6
Control 6	10/1	0	32,600	1.97	4	0
16	10/1	100	660	1.30	5	22
17	10/1	50	1090	1.52	7	33
18	10/1	25	1456	1.63	7	45
6Calculated as [terminal AMS units]/[terminal AMS units + terminal Sty units] × 100. From 1NMR.

Examples 19-22

Control 7-9

Synthesis of Styrene Macromonomers

AMS Comonomer

Batch Polymerizations in Sealed Tube—Effect of Cobalt Complex

A mixture of styrene (1.0 g, 9.6 mmol), α-methylstyrene (0.12 g, 0.96 mmol) (monomer ratio: 10/1), n-butyl acetate (2 g), VR®-110 (3.12×10⁻⁴ g, 100 ppm) and the cobalt species (for all experiments 50 ppm, 2.44×10⁻⁷ mol of cobalt species was used) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 125° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

TABLE 1.5
Batch polymerization of styrene in presence of AMS and various cobalt
complexes at 125° C. with VR ® 110 initiator.
							% terminal
Example	Co species7	[Co] ppm	Mn	Mw	PD	% conv	AMS units8
Control 7	Co(III)DMG	0	58,288	104,916	1.8	13	0
19	″	50	1065	1730	1.62	19	71
Control 8	Co(III)DEG	0	72,284	125,129	1.73	15	0
20	″	50	1388	2368	1.7	19	85
Control 9	Co(II) DPG	0	71,869	122,098	1.7	12	0
21	″	50	1454	2532	1.74	23	91
22	Co(III)DMG	50	1470	—	1.8	39	74
	Feed Expt9
7Co(III)DMG = iPrCo(III)(DMG-BF2)2, Co(III)DEG = MeCo(III)(DEG-BF2)2, Co(IIIDPG Co(II)(DPG-BF2)2.
8Calculated as [terminal AMS units]/[terminal AMS units + terminal Sty units] × 100 from NMR.
9Data ex Table 1.1

Examples 23-24

Control 10

Synthesis of Styrene Macromonomers

Methacrylate Comonomer

Feed Polymerization

The polymerization recipe for examples 23-24 and their control was similar to that given for Examples 1-3 with the modification that BMA was used in place of AMS. Conversions obtained are similar. Good molecular weight control is observed however little specificity for formation of a terminal macromonomer double bond is observed.

TABLE 1.7
Polymerization of styrene in presence of BMA and iPrCo(III)(DMG-BF2)2 at
125° C. with 1,1′-azobis(4-cyclohexanecarbonitrile) as initiator
	Time	[Co(III)]
Sample	(min)	ppm	Sty:BMA10	{overscore (M)}n11	{overscore (M)}w	{overscore (M)}w/{overscore (M)}n	% Conv.12
Control 10	30	0	10:1	35870	60580	1.69	25
	60	0		34970	58090	1.66	35
	120	0		36360	61770	1.70	51
	ppt	0		35750		1.73
23	30	100	10:1	1170	2130	1.81	20
	60	100		1220	3410	1.82	37
	120	100		1190	2230	1.88	51
	ppt	100		1560		1.69
24	60	25	10:1	4800	9440	1.97	38
	120	25		3750	8290	2.21	53
	ppt	25		4190	8270	1.97
10Molar ratio of comonomers
11Determined by GPC calibrated with narrow polydispersity polystyrene standards.
12Determined by 1H NMR

Examples 25-30

Synthesis of Styrene Macromonomers

Isopropenyl Acetate Comonomer

Batch Polymerization

Sty/iPA macromonomer formation at 80° C.: A mixture of styrene (1 g, 9.6 mmol), isopropenyl acetate (0.19 g, 1.9 mmol) (monomer ratio: 5/1), n-butyl acetate (2 g), AIBN (3.19×10⁻⁴ g, 100 ppm) and isopropylcobalt(III)DMG (for concentrations see Table 1.8) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

¹H-nmr (d6-acetone): styryl end group internal double bond (1): δ6.1 —CH(Ph)—CH═CH-Ph; δ3.1 CH(Ph)—CH═CH-Ph.

TABLE 1.8
Sty/iPA macromonomer formation at 80° C.
for 2 h with AIBN and iPrCo(III)(DMG-BF2)2.
	Sty/iPA	Co(III)					% terminal
Example	ratio	ppm	Mn	Mw	PD	% conv	iPA units13
Control 11	5/1	0	57,425	91,753	1.6	6.00	0
25	5/1	400	338	364	1.07	4.00	0
26	5/1	100	698	1045	1.49	4.00	0
27	5/1	25	5188	11,611	2.24	6.00	0
Control 12	1/1	0	32,782	52,987	1.61	3.00	0
28	1/1	400	323	343	1.07	2.00	0
29	1/1	100	465	586	1.26	3.00	0
30	1/1	25	1560	2825	1.81	3.00	0
13No terminal alkene derived from iPA were detectable by 1H NMR.

Examples 31-45

Controls 13-16

Synthesis of Butyl Acrylate Macromonomers

AMS Comonomer at 80° C.

Batch Polymerization—Effect of Comonomer and Complex Concentration

A mixture of butyl acrylate (1.3 g, 10 mmol), a-methylstyrene (50 mg, 0.4 mmol) (monomer ratio: 25/1), n-butyl acetate (2 g), AIBN (3.74×10⁻⁴ g, 100 ppm) and isopropylcobalt(III)DMG (for concentration see Table 2.1) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

¹H-nmr (d6-acetone): d 0.9, CH₃; 1.25, CH₂; 1.5, CH₂; 1.95, CH; 2.3, backbone CH₂; 2.55, allyl CH₂; 3.95, OCH₂; 5.0, vinyl H; 5.2, vinyl H; 7.15-7.25, ArH.

TABLE 2.1
Polymerization of butyl acrylate in presence of
AMS and iPrCo(III)(DMG-BF2)2 at 80° C.
	BA/AM	Co(III)			%	% term.	% AMS	% term.
Ex.	S ratio	ppm	{overscore (M)}n14	PD	Conv	AMS units15	inc.16	alkene17
Ctrl 13	5/1	0	23,500	1.75	3	0	39	0
31	5/1	100	475	1.20	3	64	43	100
32	5/1	50	487	1.20	4	60	38	100
33	5/1	25	495	1.20	4	54	41	100
Ctrl 14	10/1	0	28,200	1.64	4	0	38	0
34	10/1	100	551	1.27	3	67	36	100
35	10/1	50	605	1.31	5	63	35	100
36	10/1	25	635	1.33	5	60	36	100
Ctrl 15	25/1	0	41,423	1.69	9	0	17	0
37	25/1	200	943	1.37	6	92	15	91
38	25/1	100	961	1.39	5	77	17	96
39	25/1	50	1062	1.42	6	71	18	100
40	25/1	25	1152	1.48	7	57	20	100
Ctrl 16	50/1	0	56,071	1.76	14	0	12	0
41	50/1	400	1168	1.64	10	78	9	80
42	50/1	200	1207	1.76	10	75	9	85
43	50/1	100	1481	1.80	13	61	9	91
44	50/1	50	1600	1.82	11	59	10	100
45	50/1	25	1876	1.96	11	45	10	100
14Polystyrene equivalents.
15Calculated as (terminal AMS units)/(total AMS units) × 100.
16Calculated as (total AMS units)/(total BA units + total AMS) × 100.
17Calculated as (terminal AMS units)/(terminal AMS units + terminal BA units) × 100.
A Value of 100% indicates that terminal BA could not be detected by 1H NMR.

Examples 46-54

Controls 17, 18

Synthesis of Butyl Acrylate Macromonomers

AMS Comonomer at 125° C.

Batch Polymerization—Effect of Reaction Temperature

A mixture of butyl acrylate (1.3 g, 10 mmol), α-methylstyrene (50 mg, 0.4 mmol) (monomer ratio: 25/1), n-butyl acetate (2 g), VR®-110 (3.74×10⁻⁴ g, 100 ppm) and iPrCo(III)(DMG-BF₂)₂ (for concentration see Table 2.2) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 125° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

TABLE 2.2
Polymerization of butyl acrylate in presence of
AMS and iPrCo(III)(DMG-BF2)2 at 125° C.
						% term.
	BA/AMS	Co(III)			%	AMS	% AMS	% terminal
Ex.	ratio	ppm	{overscore (M)}n	PD	conv	units18	inc.19	alkene20
Control 17	25/1	0	18,069	1.77	36	0	13	0
46	25/1	200	973	1.58	19	77	12	85
47	25/1	100	967	1.73	29	68	13	93
48	25/1	50	1402	1.68	32	57	13	100
49	25/1	25	2230	2.10	3	23	20	100
Control 18	50/1	0	18,891	1.85	6	0	5	0
50	50/1	400	1069	1.65	21	84	6	not calc.
51	50/1	200	1200	1.72	21	72	7	73
52	50/1	100	1624	1.81	30	58	6	77
53	50/1	50	1948	1.92	32	55	6	87
54	50/1	25	3463	2.10	43	32	5	100
18Calculated as (terminal AMS units)/(total AMS units) × 100.
19Calculated as (total AMS units)/(total BA units + total AMS) × 100.
20Calculated as (terminal AMS units)/(terminal AMS units + terminal BA units) × 100.

Examples 55-58

Control 19

Synthesis of Butyl Acrylate Macromonomers

AMS Comonomer at 80° C.

Batch Polymerization—Effect of Cobalt Complex

A mixture of butyl acrylate (1.3 g, 10 mmol), a-methylstyrene (24 mg, 0.2 mmol) (monomer ratio: 50/1), n-butyl acetate (2 g), AIBN (3.74×10⁻⁴ g, 100 ppm) and MeCo(1 μl)(DEG-BF₂)₂ (for concentration see table 2.3) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by 1H-nmr and GPC.

TABLE 2.3
Polymerization of butyl acrylate in presence of
AMS and MeCo(III)(DEG-BF2)2 at 80° C.
						% term.
	BA/AMS	Co(III)			%	AMS	% AMS	% terminal
Ex.	ratio	ppm	{overscore (M)}n	PD	conv	units21	inc.22	alkene23
Control 19	50/1	0	49,342	1.74	11	0	25	0
55	50/1	200	1128	1.57	4	79	12	100
56	50/1	100	1162	1.66	5	75	12	100
57	50/1	50	1647	1.70	10	57	12	100
58	50/1	25	2369	1.85	11	31	13	100

Examples 59-63

Control 20

BA/AMS Macromonomer Formation at 80° C. With Co(II)(DPG-BF₂)₂

A mixture of butyl acrylate (1.3 g, 10 mmol), α-methylstyrene (24 mg, 0.2 mmol) (monomer ratio: 50/1), n-butyl acetate (2 g), AIBN (3.74×10⁻⁴ g, 100 ppm) and Co(II)(DPG-BF) (for concentrations see Table 2.4) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced under vacuum to a residue which was analysed by ¹H-nmr and GPC.

TABLE 2.4
Polymerization of butyl acrylate in presence of
AMS (50/1) and Co(II)(DPG-BF2)2 at 80° C.
						% term.		%
	Co(II)				%	AMS	% AMS	terminal
Ex.	ppm	{overscore (M)}n	{overscore (M)}w	PD	conv	units24	inc.25	alkene26
Control 20	0	50,575	104,679	2.07	17	0	9	0
59	400	796	1262	1.58	1	79	11	89
60	200	864	1419	1.64	1	73	12	100
61	100	1064	1817	1.71	1	66	13	100
62	50	1126	1957	1.73	1	60	14	100
63	25	2076	5407	2.10	3	35	13	100
21Calculated as (terminal AMS units)/(total AMS units) × 100.
22Calculated as (total AMS units)/(total BA units + total AMS) × 100.
23Calculated as (terminal AMS units)/(terminal AMS units + terminal BA units) × 100.
24Calculated as (terminal AMS units)/(total AMS units) × 100.
25Calculated as (total AMS units)/(total BA units + total AMS) × 100.
26Calculated as (terminal AMS units)/(terminal AMS units + terminal BA units) × 100.

Examples 64-68

Control 21

Synthesis of Butyl Acrylate Macromonomers

MAN Comonomer at 80° C.—Batch polymerization

A mixture of butyl acrylate (1 g, 7.58 mmol), methacrylonitrile (51 mg, 0.758 mmol), n-butyl acetate (2 g), AIBN (3.54×10⁻⁴ g, 100 ppm) and iPrCo(II)(DMG-BF₂)₂ (for concentration see Table 2.5) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by 1H-nmr and GPC. ¹H-nmr (CDCl₃): d 0.95, CH₃; 1.35, CH₂; 1.65, CH₂; 1.95, CH; 2.3, backbone CH₂; 2.6, allyl CH₂; 4.0, OCH₂; 5.7, vinyl H; 5.85, vinyl H.

TABLE 2.5
Polymerization of butyl acrylate in presence of
MAN and iPrCo(III)(DMG-BF2)2 at 80° C.
	BA/MAN	[Co(III)]				%	% terminal
Ex.	Ratio	ppm	{overscore (M)}n	{overscore (M)}w	PD	conv.	methylene27
Control 21	10/1	0	9306	17,653	1.90	8	0
64	10/1	400	669	1004	1.50	6	86
65	10/1	200	802	1179	1.47	7	87
66	10/1	100	959	1432	1.49	8	80
67	10/1	50	1036	1676	1.62	8	76
68	10/1	25	1301	2008	1.54	8	81
27Calculated as (terminal MAN units)/(terminal MAN units + terminal BA units) × 100.

Examples 69-83

Controls 22 to 24

Synthesis of Butyl Acrylate Macromonomers

MMA Comonomer at 60-125° C.—Batch Polymerization

BA/MMA Macromonomer Formation at BA/MMA 10/1

A mixture of butyl acrylate (1 g, 7.58 mmol), methyl methacrylate (76 mg, 0.758 mmol), n-butyl acetate (2 g), initiator (see Table 2.6 for initiator type) and isopropylcobalt(III)DMG (for concentration see Table 2.6) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at the indicated temperature for either 2 or 3 hours. The ampoule was rapidly cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

1H-nmr (CDCl₃): d 0.9, CH₃; 1.35, CH₂; 1.65, CH₂; 1.85, CH; 2.25, backbone CH₂; 2.55, allyl CH₂; 3.6, OCH₃; 4.0, OCH₂; 5.5, vinyl H; 6.15, vinyl H.

TABLE 2.6
Polymerization of butyl acrylate in presence of MMA (10:1)
and iPrCo(III)(DMG-BF2)2 at various temperatures
									{overscore (M)}n
	Temp ° C.	React.	Co(III)				% term.	% MMA	cal
Ex.	(initiator)	Time h	ppm	{overscore (M)}n	PD	% conv	alkene28	incorp.292	ob
Ctrl 22	(AIBN)	3	0	170,754	2.08	25	0	19	—
69	60	3	400	891	1.55	6	83	18	1.04
70	60	3	200	1051	1.56	5	87	19	1.05
71	60	3	100	1567	1.70	4	91	20	0.83
72	60	3	50	2610	1.80	7	100	19	0.98
73	60	3	25	7702	1.87	16	100	18	1.0
Ctrl 23	(AIBN)	2	0	75,501	2.08	54	0	14	—
74	80	2	400	917	1.31	8	75	17	0.92
75	80	2	200	1196	1.43	10	86	17	0.93
76	80	2	100	1520	1.50	9	92	18	0.92
77	80	2	50	2602	1.66	21	94	17	1.00
78	80	2	25	12,117	1.82	53	100	14	1.09
Ctrl 24	(VR ®-110)	2	0	10,410	2.56	76	0	11	—
79	125	2	400	832	1.51	9	79	16	1.04
80	125	2	200	1032	1.73	15	87	17	1.00
81	125	2	100	1224	1.60	14	91	17	1.05
82	125	2	50	1994	1.70	32	92	15	1.01
83	125	2	25	3513	1.74	45	93	14	0.88
28Calculated as (terminal MMA units)/(terminal MMA units + terminal BA units) × 100.
29Calculated as (total MMA units)/(total MMA units + total BA units) × 100.

Examples 84-91

Control 25 and 26

Synthesis of Functional Butyl Acrylate Macromonomers

HEMA Comonomer at 80° C.—Batch Polymerization

A mixture of butyl acrylate (1.3 g; 10 mmol), 2-hydroxyethyl methacrylate, HEMA (65 mg; 0.5 mmol) (monomer ratio 20:1), n-butyl acetate (2 g), AIBN (3.74×10⁴ g, 100 ppm) and isopropylcobalt(III)DMG (for concentration see Table 2.7) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 1 or 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

¹H-nmr (CDCl₃): d 0.95, CH₃; 1.40, CH₂; 1.65, CH₂; 1.85, backbone CH; 2.25, backbone CH₂; 3.80, CH₂; 4.00, CH₂; 4.22, CH₂; 5.50, external vinyl*; 5.80, 5.90, E&Z internal vinyl*; 6.20, external vinyl*.

(*external vinyl signals due to HEMA derived vinyl end group and internal vinyl signals due to BA derived vinyl group).

TABLE 2.7
Polymerization of butyl acrylate in presence of HEMA
(20:1) and iPrCo(III)(DMG-BF2)2 at 80° C.
	Reaction						%
	Time	Co(III)				%	terminal
Example	(hours)	ppm	Mn	Mw	PD	conv	alkene30
Control 25	1	0	169,846	403,699	2.38	53	0
84	1	200	1695	3011	1.78	6	80
85	1	50	12,919	25,390	1.97	23	100
86	1	25	35,421	68,294	1.93	37	100
Control 26	2	0	58,522	200,100	3.42	98	0
87	2	400	1116	2144	1.92	13	71
88	2	200	1545	3207	2.08	19	73
89	2	100	2219	5215	2.35	24	78
90	2	50	21,852	46,133	2.11	79	a
91	2	25	38,369	95,492	2.49	97	a
a Terminal alkene protons were not visible in 1H-nmr spectrum.
30Calculated as (terminal HEMA units)/(terminal HEMA units + terminal BA units) × 100.

Examples 92-94

Control 27

Synthesis of Functional Acrylate Copolymer Macromonomers

AMS Comonomer at 80° C.—Batch Polymerization

A mixture of butyl acrylate (1.3 g; 10 mmol), 2-hydroxyethylacrylate, HEA (116 mg; 1 mmol), α-methylstyrene (26 mg; 2.2×10⁻⁴ mol) (monomer ratio 10/1/0.22), n-butyl acetate (2 g), AIBN (3.65×10⁻⁴ g, 100 ppm) and isopropylcobalt(III)DMG (for concentration see Table 2.8) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

¹H-nmr (CDCl₃): d 0.90, CH₃; 1.30, CH₂; 1.50, CH₂; 1.80, backbone CH; 2.22, backbone CH₂; 3.80, CH₂; 3.85, CH₂; 4.98, external vinyl*; 5.20, external vinyl*; 5.80, 5.85, internal vinyl*; 6.60-7.00, internal vinyl*; 7.30, ArH. (*external vinyl signals due to aMS derived vinyl end group and internal vinyl signals due to BA derived vinyl group).

TABLE 2.8
Copolymerization of butyl acrylate and hydroxyethyl acrylate
in presence of AMS and iPrCo(III)(DMG-BF2)2 at 80° C.
						%		%
						terminal	%	terminal
	BA/HEA/	Co(III)		PD	%	AMS	AMS	alkene33
Example	AMS ratio	ppm	Mn	(Mw/Mn)	conv	units31	inc.32	3
Control 27	10/1/0.22	0	66,642	1.96	30	0	9	0
92	10/1/0.22	200	1255	1.55	16	72	10	78
93	10/1/0.22	100	1712	1.76	22	19	8	100
94	10/1/0.22	50	1835	1.80	22	49	10	100
31Calculated as (terminal AMS units)/(total AMS units) × 100.
22Calculated as (total AMS units)/(total BA + total HEA units) × 100.
33Calculated as (terminal AMS units)/(terminal AMS units + terminal BA units) × 100.

Examples 95-100

Controls 28 and 29

Synthesis of Vinyl Benzoate Macromonomers

BMA Comonomer at 80° C.—Batch Polymerization

A mixture of vinyl benzoate, VB (1.3 g, 8.77 mmol), butyl methacrylate (0.125 g, 0.877 mmol) (monomer ratio: 10/1), n-butyl acetate (3 g), AIBN (4.43×10⁻⁴ g, 100 ppm) and isopropylcobalt(III)DMG (for concentration see Table 3.1) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

1H-nmr (d6-acetone): δ 0.9, CH₃; 1.35, CH₂; 1.65, CH₂; 1.95, CH; 2.25, backbone CH₂; 2.55, allyl CH₂; 4.0, OCH₂; 5.2, CH; 5.45, vinyl H; 6.15, vinyl H; 6.9-7.7, ArH.

TABLE 3.1
Polymerization of vinyl benzoate in presence of
BMA and iPrCo(III)(DMG-BF2)2 at 80° C.
	VB/BMA	[Co(III)]				%	% terminal
Example	ratio	ppm	{overscore (M)}n	{overscore (M)}w	PD	conv.	methylene34
Control 28	10/1	0	67,070	106,547	1.59	12	0
95	10/1	100	3168	4942	1.56	5	87
96	10/1	50	6679	12,475	1.87	7	85
97	10/1	25	12,344	24,349	1.97	8	63
Control 29	5/1	0	86,701	137,600	1.58	19	0
98	5/1	100	1720	2526	1.47	8	100
99	5/1	50	3464	6151	1.76	7	100
100	5/1	25	9094	16,155	1.78	9	86
aCalculated as (terminal BMA units)/(terminal BMA units + terminal VB units) × 100.
34Calculated as (terminal BMA units)/(terminal BMA units + terminal VB units) × 100.

Examples 101-108

Controls 30 and 31

Synthesis of Vinyl Acetate Macromonomers Methacrylate Comonomers at 80° C.—Butyl Methacrylate Comonomers at 80° C. Batch Polymerization

VAc/BMA Macromonomer Synthesis With Monomer Ratio of 10/1

A mixture of vinyl acetate (1 g; 11.6 mmol), butyl methacrylate (0.165 g; 1.16 mmol) (monomer ratio: 10/1), n-butyl acetate (2 g), AIBN (3.17×10⁻⁴ g, 100 ppm) and isopropylcobalt(III)DMG (for concentration see Table 3.2) was placed in an ampoule and degassed by 3 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

¹H-nmr (CDCl₃): d 0.95, CH₃; 1.30, CH₂; 1.60, CH₂; 3.90, CH₂; 5.40, 6.10, external vinyl CH₂*.

(* external vinyl signals due to BMA derived vinyl end group).

TABLE 3.2
Polymerization of vinyl benzoate in presence of BMA and
iPrCo(III)(DMG-BF2)2 at 80° C. (VAc:BMA = 10:1)
								{overscore (M)}n
	Co(III)			%	% BMA	BMA36	% term.	calc
Example	ppm	{overscore (M)}n	PD	conv	terminal35	(%)	alkene37	obs
Control 30	0	62,363	1.78	10	0	67	0	0
101	400	499	1.40	5	33	80	100	0.9
102	200	1917	1.37	6	16	69	100	0.55
103	100	2127	2.3	7	7	72	100	1.02
104	50	4435	3.0	7	4	73	100	1.03
105	25	10,331	2.88	10	1	71	100	1.3
35Calculated as [terminal BMA units]/[total BMA units incorporated] × 100.
36Calculated as (total BMA units)/(total VAc units + total BMA units) × 100.
37VAc derived internal alkene not detectable by 1H-nmr.

VAc/MMA Macromonomer Synthesis With Monomer Ratio of 5/1

A mixture of vinyl acetate (0.75 g; 8.77 mol), methyl methacrylate 0.175 g; 1.75 mmol) (monomer ratio: 511), n-butyl acetate (2 g), AIBN (2.93×10⁻⁴ g, 100 ppm) and isopropylcobalt(III)DMG (for concentration see Table 3.3) was placed in an ampoule and degassed by 3 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 80° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

¹H-nmr (d₆-acetone): δ 0.6-2.1, CH₃CO₂ and backbone CH₂; 3.60, COOCH₃; 4.80-5.30, multiplet, various methine signals; 5.42, 6.10 external vinyl CH₂*. (*external vinyl signal due to MMA derived vinyl end group).

TABLE 3.3
Polymerization of vinyl acetate in presence of MMA and
iPrCo(III)(DMG-BF2)2 at 80° C. (VAc:MMA = 5:1)
								{overscore (M)}n
	Co(III)				% MMA	% MMA	% term.	calc
Example	ppm	{overscore (M)}n	PD	% conv	terminal38	inc.39	alkene40	obs
Control 31	0	40,448	1.87	8	0	87	0	—
106	100	11,806	2.26	5	0.9	87	100	1.0
107	50	12,487	2.38	8	0.8	88	100	1.06
108	25	30,782	1.92	8	041	87	041	—
38Calculated as (terminal MMA units)/(total MMA units incorporated) × 100.
39Calculated as (total MMA units)/(total VAc units + total MMA units) × 100.
40Calculated as (terminal MMA units)/(terminal VAc units + terminal MMA units) × 100. VAc derived internal alkene not detectable by 1H-nmr.
41Terminal vinyl signals could not be detected by 1H-nmr.

Examples 109-116

Controls 32 and 33

Synthesis of Vinyl Acetate Macromonomers Isopropenyl Acetate, iPA Comonomer at 125° C.—Batch Polymerization

A mixture of vinyl acetate (1.0 g; 11.6 mmol), isopropenyl acetate (23 mg; 0.232 mmol) (monomer ratio: 50/1), n-butyl acetate (2 g), VR®-110 (3.4×10⁻⁴ g, 100 ppm) and isopropylcobalt(III)DMG (for concentration see Table 3.4) was placed in an ampoule and degassed by 3 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 125° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

¹H-nmr (CDCl₃): d 1.2-2.1, CH₂+CH₃CO; 4.7-5.2, multiplet, various backbone methine.

TABLE 3.4
Polymerization of vinyl acetate in presence of
iPA and iPrCo(III)(DMG-BF2)2 at 125° C.
	Vac/iPA	Co(III)					% term.
Example	ratio	ppm	Mn	Mw	PD	% conv	iPA
Control 32	5/1	0	11,964	21,818	1.82	47	0
109	5/1	200	502	983	1.40	2	b
110	5/1	100	696	1124	1.61	2	b
111	5/1	50	1240	2278	1.84	2	b
112	5/1	25	z 4781	11,189	2.34	9	b
Control 33	50/1	0	15,271	29,423	1.93	90	0
113	50/1	200	772	1329	1.72	2	a
114	50/1	100	1295	2517	1.94	3	a
115	50/1	50	2353	6484	2.76	5	b
116	50/1	25	13,518	23,737	1.76	16	b
a end group signals observed but reliable quantitation not possible.
b no end group signals detected.

Examples 117-128

Controls 34 to 36

Synthesis of Vinyl Acetate Macromonomers Isopropenyl Chloride Comonomer at 125° C.—Batch Polymerization

VAc/iPrCl macromonomer formation at 125° C. with VR®-110 and iPrCo(III)(DMG-BF)₂

A mixture of vinyl acetate (1 g, 11.6 mmol), isopropenyl chloride (0.18 g, 2.32 mmol) (monomer ratio: 5/1), n-butyl acetate (2 g), VR®-110 (3.18×10⁻⁴ g, 100 ppm) and iPrCo(III)(DMG-BF₂)₂ (for concentration see table 3.5) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 125° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

TABLE 3.5
Polymerization of vinyl acetate in presence of
iPCl and iPrCo(III)(DMG-BF2)2 at 125° C.
	VAc/	Co(III)				%
Example	iPrCl	ppm	Mn	Mw	PD	conv
Control 34	5/1	0	3969	7475	1.88	3
117	5/1	200	350	434	1.24	1
118	5/1	100	552	1323	2.40	<1
119	5/1	50	1355	3833	2.82	1
120	5/1	25	1791	5143	2.87	<1
Control 35	50/1	0	15,712	27,346	1.74	14
121	50/1	200	717	973	1.35	<1
122	50/1	100	1230	1843	1.49	<1
123	50/1	50	2692	4594	1.71	1
124	50/1	25	12,243	21,771	1.78	8

VAc/iPrCl Macromonomer Formation at 125° C. with VR®-110 and MRCo(III)(DEG-BF₂)

A mixture of vinyl acetate (1 g, 11.6 mmol), isopropenyl chloride (18 mg, 0.232 mmol) (monomer ratio: 50/1), n-butyl acetate (2 g), VRO®110 (3.15×10⁻⁴ g, 100 ppm) and MeCo(III)(DEG-BF₂)₂ (for concentration see table 3.6) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 125® for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by GPC.

TABLE 3.6
Polymerization of vinyl acetate in presence of
iPCl and MeCo(III)(DEG-BF2)2 at 125° C.
	VAc/
	iPrCl	Co(III)				%
Example	ratio	ppm	Mn	Mw	PD	conv
Control 36	50/1	0	13,984	24,811	1.77	46
125	50/1	200	935	1502	1.60	<1
126	50/1	100	1627	3001	1.84	1
127	50/1	50	10,605	19,522	1.84	6
128	50/1	25	12,740	22,831	1.79	10

Examples 129-132

Control 37

Synthesis of Functional Styrene Macromonomer

TMI®—Cytec Incorporated Comonomer

Feed Polymerization

A mixture of styrene (1 g, 9.6 mmol), TMI® (0.2 g, 0.96 mmol) (monomer ratio: 10/1), n-butyl acetate (2 g), VR®-110 (3.2×10⁻⁴ g, 100 ppm) and isopropylcobalt(III)DMG (at 0, 25, 50, 100 and 200 ppm) was placed in an ampoule and degassed by 4 freeze-thaw cycles. The ampoule was sealed and the mixture heated at 125° C. for 2 hours. The ampoule was cooled, opened and the reaction mixture reduced in vacuo to a residue which was analysed by ¹H-nmr and GPC.

¹H-nmr (d₆-acetone): δ 4.9, external vinyl*; 5.20, external vinyl*; 6.0-6.2, internal vinyl*; 6.6-7.4, ArH.

(*external vinyl signals due to TMI® derived vinyl end group and internal vinyl signals due to Sty derived vinyl end group).

TABLE 4.1
Polymerization of styrene in presence of TMI ® and
iPrCo(III)(DMG-BF2)2 at 125° C.
						%
	Sty/					terminal
	TMI ®	Co(III)				TMI ®
Example	ratio	ppm	Mn	Mw	PD	units42
Control 37	10/1	0	85,912	133,091	1.67	0
129	10/1	200	475	602	1.27	47
130	10/1	100	640	903	1.41	53
131	10/1	50	887	1373	1.55	60
132	10/1	25	1274	2155	1.73	75
42Calculated as (terminal TMI units)/(terminal TMI units + terminal Sty units).

Example 133

A mixture of 2.5 mL MA, 0.5 mL 2-chloro-2-propenol, 14 mg TAPCo, 20 mg VAZO-88 and 5 mL chloroform was degassed by three freeze-pump-thaw cycles. The reaction mixture was kept at 90° C. until 10-15% conversion was attained. GPC analysis showed Mn≈2150, PD=2.0.

Example 134

A mixture of 2.5 mL MA, 0.5 mL ethyl 2-hydroxymethylacrylate, 14 mg TAPCo, 20 mg VAZO-88 and 5 mL chloroform was degassed by three freeze-pump-thaw cycles. The reaction mixture was kept at 90° C. until 10-15% conversion was attained. GPC analysis showed Mn≈1600, PD=3.2.

Example 135

A mixture of 2.5 mL MA, 0.5 mL styrene. 14 mg TAPCO, 20 mg VAZO-88 and 5 mL chloroform was degassed by three freeze-pump-thaw cycles. The reaction mixture was kept at 90° C. until 10-15% conversion was attained. GPC analysis showed Mn≈700, PD=2.4.

Example 136

A mixture of 2.5 mL MA, 0.5 mL 2-hydroxyethyl methacrylate, 14 mg TAPCo, 20 mg VAZO-88 and 5 mL chloroform was degassed by three freeze-pump-thaw cycles. The reaction mixture was kept at 90° C. until 10-15% conversion was attained. GPC analysis showed Mn≈2150, PD=2.0.

Control 38

A mixture of 2.5 mL MA, 14 mg TAPCo, 20 mg VAZO®-88 and 5 mL chloroform was degassed by three freeze-pump-thaw cycles. The reaction mixture was kept at 90° C. until 10-15% conversion was attained. GPC analysis showns Mn≈21,700, PD=2.4.

Example 137

High Conversion Copolymerization of BA and MMA to Branched and HyperbranchedPolymers

The reincorporation of initially-formed macromonomers back into the growing polymer is demonstrated.

Identical solutions of 32 mg of VAZO®-88 and 4 mg Co(1)(DPG-BF₂)₂ in 7.7 mL of butyl acrylate (BA), 1.5 mL MMA and 8 mL of 1,2-dichloroethane were degassed and kept in a 90° C. oil bath. The samples were removed from the temperature bath at various times shown in Table 5.1. Then each reaction mixture was chilled and evaporated in high vacuum till constant weight. The results, shown in Table 5.1, indicates that MW increases sharply at the end of the polymerization process. Because most of the monomer had been consumed before the increase in molecular weight, the only way that it could occur is through reincorporation of the macromonomers formed at the beginning of the reaction. GPC and K⁺IDS data are consistent.

TABLE 5.1
Conversion	Mn	Mn/Mw
12%	540	2.08
20%	640	2.08
55%	890	2.06
93%	2270	2.84

The catalyst remained active during the course of the polymerization. Sudden inactivation of the catalyst at conversion >60% cannot account for an increase of the Mn from 890 at 55% conversion to 2270 at 93% conversion. Less than doubling of the conversion (93% vs 55%) cannot provide a 2.6 fold increase of the Mn (2270 vs 890) maintaining a unimodal distribution.

The linear macromonomers formed at 55% conversion were incorporated into the polymer at higher conversions. The incorporation of macromonomer into growing polymer chains provides branched polymer. With continuous termination of polymeric radicals by the cobalt catalyst, such an incorporation leads to polymer with a structure containing “branches-on-branches”—in the extreme, it is hyperbranched.

Confirmation of the macromonomer reincorporation into the polymer back-bone was provided by MALDI mass spectroscopy. As seen on the MALDI spectra, at conversions <50% the polymer contains from 1 to 5 MMA units per chain. For Mn≈900, it means that the polymer is enriched with MMA vs composition of the initial monomer solution. As a result, the concentration of unreacted MMA monomer in the solution decreases faster than that of BA. At 55% conversion, more than 70% of the original MMA is consumed.

Fewer MMA units are available to be incorporated into the high molecular weight polymer formed at conversions >60% then at lower conversions if polymer that forms at high conversion does not incorporate previously formed macromonomer. Incorporation of the previously-formed macromonomer would provide MMA to the high molecular weight polymer. The MALDI spectrum of the polymer at 93% conversion demonstrated this clearly. The MALDI spectrum of the polymer at 93% conversion becomes unresolved at masses >2500 due to the high levels of MMA incorporation.

Example 138

A reaction mixture containing 4 mg of the CTC-catalyst (COBF), 32 mg of VAZO®-88, 2 ml of butyl acrylate, 6 ml MMA-trimer, 0.2 ml of methyl methacrylate and 4 ml of 1,2-dichloroethane was degassed by three freeze-pump-thaw cycles and put into an oil bath at 90° C. Samples of the reaction mixture were taken after 1.5 hours, 3 hours, 7 hours and 22 hours. Initial GPC analysis shows that molecular weight of the polymeric product increases with time. Comparision of GPC data with that of KIDS and MALDI shows that in the first case the average measured MW are lower than expected in case of higher conversion samples. The first samples had readily observable quantities of vinylene protons (1H NMR spectra), indicating the formation of methacrylate-terminated polymer at the beginning of the CTC process. All of these observations are consistent with the proposed scheme.

Claims

1. In a process for the free-radical polymerization of at least two unsaturated monomers to form a polymer whose molecular architecture comprises properties of molecular weight, branching, and vinyl-terminated end groups, the monomers having the formula

2. A process according to claim 1 wherein the improvement comprises:

3. A process according to claim 1 wherein the improvement comprises polymerizing monomer(s) in the presence of an excess of a nonpolymerizable olefin, Y1Y2C═CY3Y4. The product in the initial stages of the polymerization will be composed primarily of

4. A process according to claim 1 comprising selecting A and B so the ratio of their chain transfer constants is less than 1, whereby functionality derived from monomer B will be located on the vinyl-terminated end of the polymer.

5. The process according to claim 1 in which monomer A is at least one member selected from the group substituted and unsubstituted alkyl acrylates, substituted and unsubstituted acrylaxnides, acrylonitrile, and vinyl esters; and monomer B is at least one of: a) substituted and unsubstituted α-methyl styrenes; b) alkyl methacrylates c) methacrylonitrile; d) substituted or unsubstituted methacrylamide; e) 2-chloropropene, f) 2-fluoropropene, g) 2-bromopropene h) methacrylic acid, i) itaconic acid, j) itaconic anhydride, k) substituted and unsubstituted styrenics, and l) isopropenyl esters; alkyl being C1 to C12 and substituents being selected from the group carboxylic acid, carboxylic ester, epoxy, hydroxyl, alkoxy, primary amino, secondary amino, tertiary amino, isocyananto, sulfonic acid and hydrogen.

6. A process according to claim 5 in which monomer A is at least one member selected from the group alkyl acrylate, acrylamide, acrylonitrile and vinyl ester.

7. A process according to claim 2 in which monomer A is at least one member selected from the group substituted and unsubstituted alkyl acrylates substituted and unsubstituted acrylamides, acrylonitrile, and vinyl esters; and monomer B is at least one of: a) substituted and unsubstituted α-methyl styrenes; b) alkyl methacrylates c) methacrylonitrile; d) substituted and unsubstituted methacrylamide; e) 2-chloropropene, f) 2-fluoropropene, g) 2-bromopropene h) methacrylic acid, i) itaconic acid, j) itaconic anhydride, k) substituted and unsubstituted styrenics, and l) isopropenyl esters; alkyl being C1 to C12 and substituents being selected from the group carboxylic acid, carboxylic ester, epoxy, hydroxyl, alkoxy, primary amino, secondary amino, tertiary amino, isocyananto, sulfonic acid and hydrogen.

8. A polymer having the formula:

9. A polymer having the formula:

10. A polymer having the formula: