Cathode electrode material and lithium sulfur battery using the same

Information

  • Patent Grant
  • 10333147
  • Patent Number
    10,333,147
  • Date Filed
    Monday, January 15, 2018
    6 years ago
  • Date Issued
    Tuesday, June 25, 2019
    5 years ago
Abstract
A cathode electrode material and a lithium sulfur battery are disclosed. The cathode electrode material includes the cathode binder. The cathode binder includes a polymer obtained by polymerizing a dianhydride monomer with a diamine monomer. At least one of the dianhydride monomer and the diamine monomer includes a silicon-containing monomer. The lithium sulfur battery includes an anode electrode, an electrolyte, and the cathode electrode, the cathode electrode includes a sulfur containing cathode active material, a conducting agent, and the cathode binder.
Description
FIELD

The present disclosure relates to cathode electrode materials and sulfur batteries using the same.


BACKGROUND

For a long time, people have been committed to the research and development of new energy storage systems. Among them, lithium sulfur secondary batteries are considered the most attractive battery system. Sulfur has the highest theoretical specific energy (2800 Wh/kg) and theoretical specific capacity (1675 Ah/kg) compared to other battery systems.


However, lithium sulfur batteries generate polysulfides during charge-discharge cycles. The polysulfides dissolve in organic electrolytes, resulting in irreversible loss of active material and decay of capacity. Moreover, with the insertion and extraction of lithium ions during the charge-discharge cycle, the sulfur cathode electrode has a volumetric expansion and contraction. As the cycling number increases, the cathode electrode structure collapses and the cathode electrode material spalls, causing a rapid decay of the capacity.


Experiments have shown that a commonly used oily binder such as polyvinylidene fluoride (PVDF) has a deteriorated cycling performance for lithium sulfur batteries. An aqueous binder such as polyacrylic acid or polyacrylate is used in the lithium-sulfur battery system. However, during the manufacturing of the electrode, the cathode active material, such as sulfur, is mixed with the conducting agent and the binder through in a solvent to form an electrode slurry, which is coated on the surface of the current collector and then dried to remove the solvent. For oily binders, volatile organic solvents can be used to make electrode slurries that are easier to dry. For aqueous binder, a relatively long time is needed to thoroughly dry water in the slurry at a relatively low temperature, during which the cathode active material may be oxidized.





SUMMARY
Brief Description of the Drawings

Implementations are described by way of example only with reference to the attached FIGURE.


The FIGURE is a graph showing cycling performances of Example 5 and Comparative Example 1 of lithium sulfur batteries.





DETAILED DESCRIPTION

A detailed description with the above drawing is made to further illustrate the present disclosure.


One embodiment of a cathode binder is provided. The cathode binder is a polymer obtained by polymerizing a dianhydride monomer with a diamine monomer. At least one of the dianhydride monomer and the diamine monomer comprises a monomer containing a silicon atom.


In one embodiment, the dianhydride monomer comprises the silicon-containing monomer, and the silicon containing dianhydride monomer can be represented by formula I.




embedded image


In another embodiment, the diamine monomer comprises the silicon-containing monomer, and the silicon-containing diamine monomer can be represented by formula II.




embedded image


R1 in formula I and R2 in formula II are both silicon-containing bivalent organic substituents, which can be independently selected from




embedded image



wherein n=1 to 6; R5, R6, R7, and R8 can be independently selected from an alkyl group with 1 to 6 carbon atoms, an alkoxy group with 1 to 6 carbon atoms, a monovalent alicyclic group, a monovalent substituted alicyclic group, a monovalent aromatic group, a monovalent substituted aromatic group, —C(O)R, —RS(O)R, —RNH2R, wherein R is an alkyl group with 1 to 6 carbon atoms. A hydrogen atom of the monovalent alicyclic group or the monovalent aromatic group can be substituted by a halogen atom or an alkyl group with 1 to 6 carbon atoms to form the monovalent substituted alicyclic group or the monovalent substituted aromatic group. The monovalent substituted aromatic group or the monovalent aromatic group can have 1 or 2 benzene rings, and in some embodiments can be a phenyl group, methyl phenyl group, or dimethyl phenyl group. R5, R6, R7, and R8 can be the same or different.


In some embodiments, R1 in formula I and R2 in formula II can be independently selected from




embedded image


When the diamine monomer comprises the silicon-containing monomer, the dianhydride monomer does not need to contain silicon atom, and can be represented by formulas III, IV, or V.




embedded image


In formula V, R3 is a bivalent organic substituent containing no silicon atoms, which can be —(CH2)n—, —O—, —S—, —CH2—O—CH2—,




embedded image



wherein n=1 to 6; R5, R6, R7, and R8 can be independently selected from an H atom, an alkyl group with 1 to 6 carbon atoms, an alkoxy group with 1 to 6 carbon atoms, a monovalent alicyclic group, a monovalent substituted alicyclic group, a monovalent aromatic group, a monovalent substituted aromatic group, —C(O)R, —RS(O)R, —RNH2R, wherein R is an alkyl group with 1 to 6 carbon atoms. A hydrogen atom of the monovalent alicyclic group or the monovalent aromatic group can be substituted by a halogen atom or an alkyl group with 1 to 6 carbon atoms to form the monovalent substituted alicyclic group or the monovalent substituted aromatic group. The monovalent substituted aromatic group or the monovalent aromatic group can have 1 or 2 benzene rings, and in some embodiments can be a phenyl group, methyl phenyl group, or dimethyl phenyl group.


When the dianhydride monomer comprises the silicon-containing monomer, the diamine monomer does not need to contain a silicon atom, and comprises a monomer represented by formula VI below.




embedded image


In formula VI, R4 is a bivalent organic substituent containing no silicon atom, which can be —(CH2)n-, —O—, —S—, —CH2—O—CH2—, —CH(NH)—(CH2)n—,




embedded image



wherein n=1 to 6; R5, R6, R7, and R8 can be independently selected from H atom, an alkyl group with 1 to 6 carbon atoms, an alkoxy group with 1 to 6 carbon atoms, a monovalent alicyclic group, a monovalent substituted alicyclic group, a monovalent aromatic group, and a monovalent substituted aromatic group, —C(O)R, —RS(O)R, —RNH2R, wherein R is an alkyl group with 1 to 6 carbon atoms. A hydrogen atom of the monovalent alicyclic group or the monovalent aromatic group can be substituted by a halogen atom or an alkyl group with 1 to 6 carbon atoms to form the monovalent substituted alicyclic group or the monovalent substituted aromatic group. The monovalent substituted aromatic group or the monovalent aromatic group can have 1 or 2 benzene rings, and in some embodiments can be a phenyl group, methyl phenyl group, or dimethyl phenyl group.


When the diamine monomer comprises the silicon-containing monomer, the diamine monomer can further comprise a silicon-free monomer, which can be a monomer represented by formula VI.


When the dianhydride monomer comprises the silicon-containing monomer, the dianhydride monomer can further comprise a silicon-free monomer, which can be a monomer represented by formula III, IV, or V.


When the diamine monomer and the dianhydride monomer both comprise the silicon-containing monomers, the diamine monomer and the dianhydride monomer can further comprise a silicon-free monomer, which can be a monomer represented by formula VI and a monomer represented by formula III, IV, or V.


A molar ratio of a total amount of the silicon-containing monomer (the silicon-containing diamine monomer and/or the silicon-containing dianhydride monomer) to a total amount of the silicon-free monomer (the diamine monomer containing no silicon atom and/or the dianhydride monomer containing no silicon atom) can be 1:100 to 10:1, such as 1:20 to 1:1.


In one embodiment, the diamine monomer and the dianhydride monomer both only comprise the silicon-containing monomers.


A molar ratio of all the dianhydride monomer to all the diamine monomer can be 1:10 to 10:1, and in some embodiments can be 1:2 to 4:1.


A molecular weight of the polymer obtained by polymerizing the dianhydride monomer with the diamine monomer can be in a range from about 10000 to about 600000.


One embodiment of a method for making the cathode binder comprises a step of polymerizing the dianhydride monomer with the diamine monomer, which specifically can comprise:


mixing the dianhydride monomer and the diamine monomer in an organic solvent to form a mixture, and heating and stirring the mixture to fully carry the reaction thereby obtaining the cathode binder.


The diamine monomer can be dissolved in an organic solvent to form a diamine solution. A mass ratio of the diamine monomer to the organic solvent in the diamine solution can be 1:100 to 1:1, and can be 1:10 to 1:2 in some embodiments.


The dianhydride monomer can be dissolved in an organic solvent to form a dianhydride solution. A mass ratio of the dianhydride monomer to the organic solvent in the dianhydride solution can be 1:100 to 1:1, and can be 1:10 to 1:2 in some embodiments.


The organic solvent can dissolve the diamine monomer and the dianhydride monomer, such as m-cresol, N,N-dimethylformamide, N,N-dimethylacetamide, propylene carbonate, and N-methyl-2-pyrrolidone (NMP).


A pump can be used to deliver the dianhydride solution into the diamine solution at a certain speed or deliver the diamine solution into the dianhydride solution at a certain speed. After the delivery, the stirring can continue for a period of time to form a complete reaction. The stirring can last for about 2 hours to about 72 hours, and can last for about 12 hours to about 24 hours in some embodiments. The temperature of the polymerizing can be at about 160° C. to about 200° C.


During the polymerizing, a catalyst can be added. The catalyst can be at least one of benzoic acid, benzenesulfonic acid, phenylacetic acid, pyridine, quinoline, pyrrole, and imidazole. A mass percentage of the catalyst to a sum of the dianhydride monomer and the diamine monomer can be about 0.5% to about 5%.


First, the dianhydride monomer and the diamine monomer can be completely dissolved in the organic solvent, and then heated to a temperature of about 30° C. to about 60° C. at which the mixture is stirred for about 1 hour to about 10 hours, and 2 hours to 4 hours in some embodiments. The catalyst is then added to the mixture followed by heating the mixture to a temperature of about 160° C. to about 200° C. at which the mixture is stirred for about 6 hours to about 48 hours, and 12 hours to 24 hours in some embodiments, to obtain the polymer.


After the reaction, the cathode binder can be purified by washing the obtained polymer with a cleaning solvent, and dried. The catalyst and the organic solvent are soluble to the cleaning solvent, and the cathode binder is insoluble to the cleaning solvent to form a precipitate. The cleaning solvent can be water, methanol, ethanol, a mixture of methanol and water, or a mixture of ethanol and water (a concentration of the methanol or the ethanol can be 5 wt % to 99 wt %).


One embodiment of a cathode electrode material comprises a sulfur containing cathode active material, a conducting agent, and the above-described cathode binder, which are uniformly mixed with each other. A mass percentage of the cathode binder in the cathode electrode material can be in a range from about 0.01% to about 50%, such as from about 5% to about 20%.


The sulfur containing cathode active material can be at least one of elemental sulfur and sulfur based polymer. The sulfur based polymer is a product formed from a pyrolysis reaction, dehydrogenation and carbonation reaction, dehydration reaction, dehydrochlorination reaction, or deamination reaction of a mixture of conducting polymer and elemental sulfur. The sulfur based polymer can be at least one of sulfurized poly(pyridinopyridine), sulfurized polystyrene, sulfurized polyoxyethylene, sulfurized polyvinyl alcohol, sulfurized poly(vinylidene chloride), sulfurized poly(vinylidene difluoride), sulfurized polyvinylchloride, sulfurized polyvinyl fluoride, sulfurized poly(1,2-dichloroethylene), sulfurized poly(1,2-difluoroethylene), sulfurized polymethyl methacrylate, and sulfurized phenolic resin.


The conducting agent can be carbonaceous materials, such as at least one of carbon black, conducting polymers, acetylene black, carbon fibers, carbon nanotubes, and graphite.


Since the cathode binder is oily and is soluble in an oily solvent, the cathode binder can be used in combination with an oily organic solvent commonly used in the preparation of electrode slurry of the lithium sulfur battery, such as N-methylpyrrolidone. The oily organic solvent can be rapidly and effectively removed during the drying process of the electrode slurry to avoid an adverse effect of the drying process on the electrode and the battery performance.


One embodiment of a lithium sulfur battery comprises a cathode electrode, an anode electrode, and an electrolyte located between the cathode electrode and the anode electrode. The cathode electrode can comprise the above-described cathode electrode material. The cathode electrode can further comprise a cathode current collector. The cathode electrode material can be located on a surface of the cathode current collector. The anode can comprise an anode electrode material, and can further comprise an anode current collector. The anode electrode material can be located on a surface of the anode current collector. The anode electrode material can be lithium metal. The electrolyte can be a solid electrolyte or an electrolyte liquid. In one embodiment, the electrolyte is the electrolyte liquid, the lithium sulfur battery can further comprise a separator, and the anode electrode material and the cathode electrode material are opposite to each other and spaced by the separator. In another embodiment, the electrolyte is the solid electrolyte having a film shape, and the anode electrode material and the cathode electrode material are spaced from each other by the film shaped solid electrolyte.


The separator can be polyolefin microporous membrane, modified polypropylene fabric, polyethylene fabric, glass fiber fabric, superfine glass fiber paper, vinylon fabric, or composite membrane of nylon fabric, and wettable polyolefin microporous membrane composited by welding or bonding.


The electrolyte liquid comprises a lithium salt and a non-aqueous solvent. The non-aqueous solvent can comprise at least one of cyclic carbonates, chain carbonates, cyclic ethers, chain ethers, nitriles, amides and combinations thereof, such as ethylene carbonate (EC), diethyl carbonate (DEC), propylene carbonate (PC), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), butylene carbonate, gamma-butyrolactone, gamma-valerolactone, dipropyl carbonate, N-methyl pyrrolidone (NMP), N-methylformamide, N-methylacetamide, N,N-dimethylformamide, N,N-diethylformamide, diethyl ether, acetonitrile, propionitrile, anisole, succinonitrile, adiponitrile, glutaronitrile, dimethyl sulfoxide, dimethyl sulfite, vinylene carbonate, ethyl methyl carbonate, dimethyl carbonate, diethyl carbonate, fluoroethylene carbonate, chloropropylene carbonate, acetonitrile, succinonitrile, methoxymethylsulfone, tetrahydrofuran, 2-methyltetrahydrofuran, epoxy propane, methyl acetate, ethyl acetate, propyl acetate, methyl butyrate, ethyl propionate, methyl propionate, 1,3-dioxolane, 1,2-diethoxyethane, 1,2-dimethoxyethane, and 1,2-dibutoxy.


The lithium salt can comprise at least one of lithium chloride (LiCl), lithium hexafluorophosphate (LiPF6), lithium tetrafluoroborate (LiBF4), lithium methanesulfonate (LiCH3SO3), lithium trifluoromethanesulfonate (LiCF3SO3), lithium hexafluoroarsenate (LiAsF6), lithium hexafluoroantimonate (LiSbF6), lithium perchlorate (LiClO4), Li[BF2(C2O4)], Li[PF2(C2O4)2], Li[N(CF3SO2)2], Li[C(CF3SO2)3], lithium bisoxalatoborate (LiBOB), and lithium bis(trifluoromethanesulphonyl)imide (LiTFSI).


Example 1

In molar ratio, 0.4 parts of bis(4-aminophenoxy)dimethylsilane, 0.6 parts of 4,4′-oxydianiline (ODA), and m-cresol as the organic solvent are added in a triple-neck flask (a solid content of the solution is about 10%), stirred at room temperature to dissolve completely. 1 part of 2,3,3′,4′-diphenyl ether tetracarboxylic dianhydride is then added and dissolved completely. The solution is heated to about 50° C. and reacted for about 4 hours followed by adding 1.5 mL of benzoic acid as the catalyst. Then the solution is heated to about 180° C. and reacted for about 24 hours. Finally, the reaction is terminated and the solution is precipitated in methanol to obtain the cathode binder, which is a fiber shaped polymer represented by formula VII.




embedded image


Example 2

In molar ratio, 0.4 parts of bis(4-aminophenoxy)diphenylsilane, 0.6 parts of 4,4′-oxydianiline (ODA), and m-cresol as the organic solvent are added in a triple-neck flask (a solid content of the solution is about 10%), stirred at room temperature to dissolve completely. 1 part of 2,3,3′,4′-diphenyl ether tetracarboxylic dianhydride is then added and dissolved completely. The solution is heated to about 50° C. and reacted for about 4 hours followed by adding 1.5 mL of benzoic acid as the catalyst. Then the solution is heated to about 180° C. and reacted for about 24 hours. Finally, the reaction is terminated and the solution is precipitated in methanol to obtain the cathode binder, which is a fiber shaped polymer represented by formula VIII.




embedded image


Example 3

In molar ratio, 0.4 parts of bis(4-aminophenoxy)dimethylsilane, 0.6 parts of 4,4′-oxydianiline (ODA), and m-cresol as the organic solvent are added in a triple-neck flask (a solid content of the solution is about 10%), stirred at room temperature to dissolve completely. 1 part of bis(dimethylsilyl)benzotetracarboxylic dianhydride




embedded image



is then added and dissolved completely. The solution is heated to about 50° C. and reacted for about 4 hours followed by adding 1.5 mL of benzoic acid as the catalyst. Then the solution is heated to about 180° C. and reacted for about 24 hours. Finally, the reaction is terminated and the solution is precipitated in methanol to obtain the cathode binder, which is a fiber shaped polymer represented by formula IX.




embedded image


Example 4

In molar ratio, 0.4 parts of 2,2′-bis(4-aminophenoxyphenyl)propane (BAPP), 0.6 parts of 4,4′-oxydianiline (ODA), and m-cresol as the organic solvent are added in a triple-neck flask (a solid content of the solution is about 10%), stirred at room temperature to dissolve completely. 1 part of bis(dimethylsilyl)benzotetracarboxylic dianhydride




embedded image



is then added and dissolved completely. The solution is heated to about 50° C. and reacted for about 4 hours followed by adding 1.5 mL of benzoic acid as the catalyst. Then the solution is heated to about 180° C. and reacted for about 24 hours. Finally, the reaction is terminated and the solution is precipitated in methanol to obtain the cathode binder, which is a fiber shaped polymer represented by formula X.




embedded image


Example 5

70% of sulfur-carbon cathode electrode material, 10% of the cathode binder obtained in Example 1, and 20% of the conducting graphite by mass percent are mixed and dispersed by the NMP to form a slurry. The slurry is coated on an aluminum foil and vacuum dried at about 60° C. for about 24 hours to obtain the cathode electrode. The counter electrode is lithium metal. The electrolyte liquid is 1 M of LiTFSI dissolved in a solvent mixture of DOL/DME=1/1 (v/v). The counter electrode, the cathode electrode, and the electrolyte liquid are assembled to form a 2032 coin-type battery.


Example 6

70% of sulfur-carbon cathode electrode material, 10% of the cathode binder obtained in Example 2, and 20% of the conducting graphite by mass percent are mixed and dispersed by the NMP to form a slurry. The slurry is coated on an aluminum foil and vacuum dried at about 60° C. for about 24 hours to obtain the cathode electrode. The counter electrode is lithium metal. The electrolyte liquid is 1 M of LiTFSI dissolved in a solvent mixture of DOL/DME=1/1 (v/v). The counter electrode, the cathode electrode, and the electrolyte liquid are assembled to form a 2032 coin-type battery.


Comparative Example 1

70% of sulfur-carbon cathode electrode material, 10% of PVDF as the binder, and 20% of the conducting graphite by mass percent are mixed and dispersed by the NMP to form a slurry. The slurry is coated on an aluminum foil and vacuum dried at about 60° C. for about 24 hours to obtain the cathode electrode. The counter electrode is lithium metal. The electrolyte liquid is 1 M of LiTFSI dissolved in a solvent mixture of DOL/DME=1/1 (v/v). The counter electrode, the cathode electrode, and the electrolyte liquid are assembled to form a 2032 coin-type battery.


The above-described Examples and Comparative Example adopt the same sulfur-carbon cathode electrode material formed by mixing the elemental sulfur with the conductive carbon.


Cycling Performance Test of Batteries


The test conditions are as follows: in the voltage range of 1 V to 3 V, the batteries are charged and discharged at a constant current rate (C-rate) of 0.1 C. Referring to the FIGURE and Table 1, the cycling performance of the lithium sulfur batteries in Example 5 and Comparative Example 1 is shown in FIG. 1. The discharge specific capacity of the first cycle, the discharge specific capacity at the 30th cycle, and the capacity retention at the 30th cycle of the lithium sulfur batteries in Examples 5, 6, and Comparative Example 1 are shown in Table 1. It can be seen that the cycling performances of the lithium sulfur batteries using the polyimide binder is greatly improved compared with that of the lithium sulfur battery using PVDF as the binder.













TABLE 1







Discharge
Discharge
Capacity



specific capacity
specific capacity
retention



(mAh/g) at
(mAh/g) at
(%) at



1st cycle
30th cycle
30th cycle



















Example 5
1080.3
606.8
56.2%


Example 6
1105.6
635.5
57.5%


Comparative
1039.0
417.5
40.2%


Example 1









Binding Force Test


The binding force tests are carried out for the cathode electrodes of Examples 5, 6 and Comparative Example 1, respectively. Adhesive tape having a width of 20 mm±1 mm is used. First, 3 to 5 outer layers of the adhesive tape are peeled off, and then more than 150 mm long of the adhesive tape is taken. The adhesive tape does not contact a hand or any other object. One end of the adhesive tape is adhered to the cathode electrode, and the other end of the adhesive tape is connected to a holder. A roller under its own weight is rolled on the cathode electrode at a speed of about 300 mm/min back and forth over the entire length of the cathode electrode about three times. The test is carried out after resting the cathode electrode in the test environment for about 20 minutes to about 40 minutes. The adhesive tape is peeled from the cathode electrode by a testing machine at a speed of about 300 mm/min±10 mm/min. The test results are shown in Table 2, revealing that the cathode binders of Examples 5 and 6 have a stronger binding force than Comparative Example 1.














TABLE 2








Sample
Sample
Maximum



Sample
Thickness/μm
Width/mm
load/N









Example 5
58 ± 2
20
5.2



Example 6
58 ± 2
20
5.8



Comparative
58 ± 2
20
1.8



Example 1










Finally, it is to be understood that the above-described embodiments are intended to illustrate rather than limit the present disclosure. Variations may be made to the embodiments without departing from the spirit of the present disclosure as claimed. Elements associated with any of the above embodiments are envisioned to be associated with any other embodiments. The above-described embodiments illustrate the scope of the present disclosure but do not restrict the scope of the present disclosure.

Claims
  • 1. A cathode electrode material comprising a sulfur containing cathode active material, a conducting agent, and a cathode binder, wherein the cathode binder comprises a polymer obtained by polymerizing a dianhydride monomer with a diamine monomer, wherein at least one of the dianhydride monomer and the diamine monomer comprises a silicon-containing monomer.
  • 2. The cathode electrode material of claim 1, wherein the dianhydride monomer comprises a first monomer represented by a formula I,
  • 3. The cathode electrode material of claim 2, wherein R1 is selected from the group consisting of
  • 4. The cathode electrode material of claim 2, wherein R1 is selected from the group consisting of
  • 5. The cathode electrode material of claim 1, wherein the diamine monomer comprises a second monomer represented by a formula II,
  • 6. The cathode electrode material of claim 5, wherein R2 is selected from the group consisting of
  • 7. The cathode electrode material of claim 5, wherein R2 is selected from the group consisting of
  • 8. The cathode electrode material of claim 5, wherein the dianhydride monomer comprises a third monomer represented by formulas III, IV, or V,
  • 9. The cathode electrode material of claim 8, wherein the diamine monomer comprises a fourth monomer represented by a formula VI,
  • 10. The cathode electrode material of claim 1, wherein at least one of the dianhydride monomer and the diamine monomer comprises a silicon-free monomer, a molar ratio of a total amount of the silicon-containing monomer to a total amount of the silicon-free monomer is in a range from 1:100 to 10:1.
  • 11. The cathode electrode material of claim 1, wherein at least one of the dianhydride monomer and the diamine monomer comprises a silicon-free monomer, a molar ratio of all of the silicon-containing monomer to all of the silicon-free monomer is in a range from 1:20 to 1:1.
  • 12. The cathode electrode material of claim 1, wherein a molar ratio of all of the dianhydride monomer to all of the diamine monomer is in a range from 1:2 to 4:1.
  • 13. The cathode electrode material of claim 1, wherein a molecular weight of the polymer obtained by polymerizing the dianhydride monomer with the diamine monomer is in a range from about 10000 to about 600000.
  • 14. The cathode electrode material of claim 1, wherein the sulfur containing cathode active material is at least one of elemental sulfur and sulfur based polymer, and the sulfur based polymer is selected from the group consisting of sulfurized poly(pyridinopyridine), sulfurized polystyrene, sulfurized polyoxyethylene, sulfurized polyvinyl alcohol, sulfurized poly(vinylidene chloride), sulfurized poly(vinylidene difluoride), sulfurized polyvinylchloride, sulfurized polyvinyl fluoride, sulfurized poly(1,2-dichloroethylene), sulfurized poly(1,2-difluoroethylene), sulfurized polymethyl methacrylate, sulfurized phenolic resin, and combinations thereof.
  • 15. A lithium sulfur battery comprising: a cathode electrode;an electrolyte; andan anode electrode,wherein the cathode electrode comprises a sulfur containing cathode active material, a conducting agent, and a cathode binder, wherein the cathode binder comprises a polymer obtained by polymerizing a dianhydride monomer with a diamine monomer, and at least one of the dianhydride monomer and the diamine monomer comprises a silicon-containing monomer.
  • 16. A cathode electrode material comprising a sulfur containing cathode active material, a conducting agent, and a cathode binder, wherein the cathode binder comprises a polymer obtained by polymerizing a dianhydride monomer with a diamine monomer, wherein the dianhydride monomer comprises a silicon-containing monomer.
  • 17. The cathode electrode material of claim 16, wherein the dianhydride monomer comprises a first monomer represented by a formula I,
  • 18. The cathode electrode material of claim 17, wherein R1 is selected from the group consisting of
  • 19. The cathode electrode material of claim 17, wherein R1 is selected from the group consisting of
  • 20. The cathode electrode material of claim 16, wherein the diamine monomer containing no silicon atom, a molar ratio of all of the silicon-containing monomer to all of silicon-free monomer is in a range from 1:20 to 1:1.
Priority Claims (1)
Number Date Country Kind
2015 1 0426550 Jul 2015 CN national
CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims all benefits accruing under 35 U.S.C. § 119 from China Patent Application No. 201510426550.4, filed on Jul. 20, 2015 in the State Intellectual Property Office of China, the content of which is hereby incorporated by reference. This application is a continuation under 35 U.S.C. § 120 of international patent application PCT/CN2016/090256 filed on Jul. 18, 2016, the content of which is also hereby incorporated by reference.

US Referenced Citations (9)
Number Name Date Kind
20090269597 Bito et al. Oct 2009 A1
20120168688 Nakayama Jul 2012 A1
20120241667 Moriuchi et al. Sep 2012 A1
20130260020 Tomikawa Oct 2013 A1
20140272597 Mikhaylik Sep 2014 A1
20140377649 Fukui Dec 2014 A1
20150303483 Kikuchi et al. Oct 2015 A1
20180047987 He Feb 2018 A1
20180053938 He Feb 2018 A1
Foreign Referenced Citations (4)
Number Date Country
101466774 Jun 2009 CN
102484254 May 2012 CN
102934268 Feb 2013 CN
WO2014080853 Jan 2017 WO
Non-Patent Literature Citations (1)
Entry
International Search Report of PCT/CN2016/090256.
Related Publications (1)
Number Date Country
20180138510 A1 May 2018 US
Continuations (1)
Number Date Country
Parent PCT/CN2016/090256 Jul 2016 US
Child 15871094 US