Patent Application
20180331329
The present invention relates generally to the field of microsystem architectures and more particularly to a structure and composition of a cathode in a thin film flexible microbattery.
A synergy of advances in materials science, microfabrication technology, biological micro-electro-mechanical systems (bioMEMS), microfluidics, and microelectronics has fueled a rapid growth of the capabilities and applications of microsystems. For example, the advancing capabilities of microsystems with an increasingly mature understanding of biological processes have a potential to significantly advance the quality of healthcare. Tiny tissue-integrated microsystems that enhance or monitor biological functions (e.g., for diabetics) and can operate for months or years at a time are envisioned. Such integrated devices must be biocompatible, neurologically and cosmetically comfortable, and effective—and with excellent reliability and longevity, especially if surgically implanted or if responsible for life-critical functions. To achieve widespread application, they must be commercially viable and cost effective.
Embodiments of the present invention disclose a battery, comprising an anode comprising anode material in contact with a metal anode current collector. The battery also comprises a cathode comprising cathode material in contact with a cathode current collector comprising a transparent conducting oxide (TCO). The battery also comprises an electrolyte with a pH in a range of 3 to 7. Embodiments of the present invention also disclose a method for forming a battery. The method includes fabricating a cathode in a first cavity in a first dielectric element. The method further includes fabricating an anode in a second cavity in a second dielectric element. The method further includes joining the cathode and the anode in a complanate manner.
Detailed embodiments of the present invention are disclosed herein with reference to the accompanying drawings. It is to be understood that the disclosed embodiments are merely illustrative of potential embodiments of the present invention and may take various forms. In addition, each of the examples given in connection with the various embodiments is intended to be illustrative, and not restrictive. Further, the Figures are not necessarily to scale, some features may be exaggerated to show details of particular components. Therefore, specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a representative basis for teaching one skilled in the art to variously employ the present invention.
References in the specification to “one embodiment”, “an embodiment”, “an example embodiment”, etc., indicate that the embodiment described may include a particular feature, structure, or characteristic, but every embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an embodiment, it is submitted that it is within the knowledge of one skilled in the art to affect such feature, structure, or characteristic in connection with other embodiments whether or not explicitly described.
For purposes of the description hereinafter, the terms “upper”, “lower”, “right”, “left”, “vertical”, “horizontal”, “top”, “bottom”, and derivatives thereof shall relate to the disclosed present invention, as oriented in the drawing Figures. The terms “overlying”, “underlying”, “atop”, “on top”, “positioned on” or “positioned atop” mean that a first element, such as a first structure, is present on a second element, such as a second structure, wherein intervening elements, such as an interface structure may be present between the first element and the second element. The term “direct contact” means that a first element, such as a first structure, and a second element, such as a second structure, are connected without any intermediary conducting, insulating or semiconductor layers at the interface of the two elements.
Contact lenses are potentially an excellent microsystem platform for a multitude of general diagnostic and vision-related functions. However, microsystems that are integrated into a contact lens or an ocular environment (e.g., a corneal implant) to perform ophthalmological functions have constraints in addition to those associated with integration into other types of human tissue—a microsystem must have extremely small dimensions, and be thin and flexible. The quest for such materials that are both amenable to economic fabrication and have the requisite optical, electrical and biological properties are currently an active area of research.
A microsystem that is suitable for integration into a contact lens, which includes an energy source and accommodates a variety of bioMEM and microelectronic mechanisms and that is realizable with economic microfabrication technologies is beneficial. A variety of health-related augmentation, diagnostic, and monitoring functions could potentially be hosted in such an ecosystem, greatly decreasing individual development times and costs.
A need for energy is a common requirement of active microsystems. An energy requirement may be minimal in many situations thus enabling a microbattery to provide ample energy for a microsystem. For example, a microbattery may be efficacious for a system embedded in a contact lens. However, batteries often contain substances that are toxic to humans, may be dimensionally awkward, and are opaque and inflexible, so compatible battery technologies are sought for ophthalmological devices.
In an embodiment of the present invention, a microsystem that can serve as a platform and ecosystem for a variety of microsystems and that can be implanted into human tissue is presented. In an embodiment, the microsystem is fabricated, using well-known processes, in two halves, a top side and a bottom side, that are joined after the two halves are fabricated. Each side is individually fabricated in a “C” shape, after which the top side is aligned with and superimposed over the bottom side and joined with the bottom side. An arc shaped gap in a resulting “C” shape that is comprised of the top side superimposed on the bottom side, is forced to close, forming an annulus.
In an embodiment, the microsystem includes one or more thin silicon die, interconnect wiring, and a battery energy source that is composed of materials that are benign, thin, and flexible. One or more circuits and memories are customized on the one or more silicon die to perform one or more functions. The one or more circuits may be quantum, electrical, chemical, optical, mechanical, electromagnetic, microfluidic, biological, or a combination thereof. In an embodiment the microsystem can be incorporated into a contact lens with a periphery of an annulus of the microsystem aligning with a periphery of the contact lens and the center of the annulus aligning with a center of the contact lens. In another embodiment, the microsystem is embedded in a corneal implant.
The present invention will now be described in detail with reference to the Figures, in accordance with an embodiment of the present invention.
In an embodiment, a side of a battery, a cathode side, is fabricated in microsystem top component 106 and the other side of the battery, an anode side, is fabricated in microsystem bottom component 105. In another embodiment, the anode side is fabricated in microsystem top component 106 and the cathode side is fabricated in microsystem bottom component 105. The cathode side of the battery and the anode side of the battery are superimposed and joined when the two halves of the single microsystem are joined.
In an embodiment, top polymer flex substrate 201 is a flex polymer material, e.g., polyethylene, or Kapton® (Kapton® is a registered trademark of DuPont Corporation), that is deposited on temporary support wafer 103 to provide a support matrix material for a creation of one or more structures in microsystem top component 106. Cavity 212 is etched into top polymer flex substrate 201 to accommodate a possible protuberance caused by one or more dies and pads on microsystem bottom component 105 to enable microsystem top component 106 to be joined with microsystem bottom component 105 in a complanate manner. The term complanate is defined as “made level” and as “put into or on one plane”.
Cavity 203 is etched into polymer flex substrate 201 to accommodate battery material 204 and polymer bondable seal material 202. In an embodiment, an etching of cavity 203 is accomplished by masking a photoresist in combination with reactive-ion etching (RIE). RIE is an etching technology that uses chemically reactive plasma to remove material deposited on wafers. In other embodiments the etching is accomplished by using a metal mask and a laser. Those skilled in the art understand there are many ways to etch cavity 203 and that polymer bondable seal material 202 is a photopatterned polymer bondable seal material that is photo-definable.
In an embodiment, rabbet joint adhesive 208 adheres to a substantially similar rabbet joint adhesive on microsystem bottom component 105 (rabbet joint adhesive 308 in
Silicon die 206 is a processing and/or memory element that is operable on quantum, electrical, chemical, optical, mechanical, microfluidic, electromagnetic, or biological principles and phenomena, or a combination thereof that provides a customizable functionality to an assembled microsystem. In an embodiment, one or more silicon dies substantially similar to silicon die 206 are attached to top polymer flex substrate 201. In an embodiment, silicon die 206 is between 20 μm and 100 μm in thickness.
Polymer bondable seal material 213 seals a portion of a surface of microsystem top component 106. Those skilled in the art understand that polymer bondable seal material 213 is a photopatterned polymer bondable seal material. Wiring trace 210 is an electrical conductor from battery material 204 to silicon die 206. Pads 209 are electrical contacts that provide electrical connections to silicon die 206 via wiring trace 214. In an embodiment, wiring trace 210 and wiring trace 214 are comprised of indium tin oxide (ITO) on a blend of titanium and tungsten (TiW). In an embodiment, hole 207 provides a path for one or more connective wires from pads 209 to one or more mechanisms that are external to microsystem top component 106. Conductive adhesive 211 adheres to a substantially similar conductive adhesive on microsystem bottom component 105 to bond microsystem top component 106 with microsystem bottom component 105. Conductive adhesive 211 is an electrical conductor and, in an embodiment, provides for an electrical connection between microsystem top component 106 and microsystem bottom component 105. In an embodiment, the electrical connection enables one or more batteries in a microsystem to be connected in series or parallel and/or enables signals to propagate between two or more locations in the microsystem.
In an embodiment, plane 205 depicts a cross-sectional view of a cathode side of a microbattery, the fabrication of which is discussed in reference to
In an embodiment, bottom polymer flex substrate 301 is a flex polymer material, e.g., Kapton® or polyethylene, which is deposited on temporary support wafer 104 to provide structural support for microsystem bottom component 105. Cavity 312 is etched into bottom polymer flex substrate 301 to accommodate a protuberance caused by silicon die 206 and pads 209 on microsystem top component 106 so that microsystem top component 106 can be joined with microsystem bottom component 105 in a complanate manner.
Cavity 303 is etched into bottom polymer flex substrate 301 to accommodate battery material 304 and polymer bondable seal material 302. In an embodiment, an etching of cavity 303 can be accomplished with photoresist in combination with reactive-ion etching. In other embodiments, the etching is accomplished with a metal mask and a laser. Those skilled in the art understand that there are many ways to etch cavity 303 and that polymer bondable seal material 302 is a photopatterned polymer bondable seal material that is photo-definable. In an embodiment, rabbet joint adhesive 308 adheres to rabbet joint adhesive 208 on microsystem top component 106 to bond the ends of a microsystem in a “C” or arc shape together into a shape of a closed annulus.
Silicon die 306 is a processing and/or memory element that is operable on quantum, electrical, chemical, optical, mechanical, microfluidic, electromagnetic, or biological principles and phenomena, or a combination thereof that provides a customizable functionality to an assembled microsystem. In an embodiment, one or more silicon dies substantially similar to silicon die 306 are attached to bottom polymer flex substrate 301. In an embodiment, silicon die 306 is between 20 μm and 100 μm in thickness.
Polymer bondable seal material 313 seals a portion of a surface of microsystem bottom component 105. Those skilled in the art understand that polymer bondable seal material 313 is a photopatterned polymer bondable seal material that is photo-definable. Wiring trace 310 is an electrical conductor from battery material 304 to silicon die 306. In other embodiments, a plurality of wiring traces distributes energy to energy consuming components such as silicon die 306. Pads 309 are electrical contacts that provide electrical connections to silicon die 306 via wiring trace 314. In an embodiment, wiring trace 310 and wiring trace 314 are comprised of indium tin oxide (ITO) on a blend of titanium and tungsten (TiW). In an embodiment, hole 307 provides a path for one or more connective wires from pads 309 to one or more mechanisms that are external to microsystem bottom component 105. Conductive adhesive 311 adheres to conductive adhesive 211 on microsystem top component 106 to bond microsystem top component 106 with microsystem bottom component 105. Conductive adhesive 311 is an electrical conductor and in an embodiment, provides for an electrical connection between microsystem top component 106 and microsystem bottom component 105. In an embodiment, the electrical connection enables one or more batteries in a microsystem to be connected in series or parallel and enables signals to propagate between two or more locations in a microsystem.
In an embodiment, plane 305 depicts a cross-sectional view of an anode side of a microbattery, the fabrication of which is discussed in reference to
Embodiments of the present invention recognize that microsystem 600 is capable of being incorporated into a contact lens. If microsystem 600 is incorporated into a contact lens, its shape and dimensions are defined by the shape of the human eye. The inner radius of the cone shape achieved after closing the gap in “C” shaped microsystem 500 is constrained by the need to have a sufficient visual opening. A minimum radius of about 3 mm for the inner radius is practical, and a larger radius is desirable. The outer radius of the cone shape is limited by the size of the cornea and the contact lens material around the cone shape of microsystem 600. The outer radius is less than about 9 mm.
The cone slope (as measured from the central axis of the cone) is a function of the inner and outer radii and is fabricated so that the cone slope approximates the slope of the eye surface between the inner and outer radius, within a range that is bounded by the contact lens thickness. Desired cone surface angles depend the range of eye dimensions that are envisioned as application targets for microsystem 600. If a corneal radius of curvature is R (about 8 mm), then for an inner cone radius of ri and outer cone radius of ro, a reasonable median cone angle A, is determined using Formula (1).
This is the angle between a surface of a cone and a central axis of the cone. The central axis of the cone is also collinear with the radius of a sphere (e.g., an eye) that the cone penetrates with the apex of the cone at the center of the sphere. The cone angle can be adjusted from cone angle A if the contact lens is not spherical. Typical cone angles are likely to be between about 15 and about 40 degrees. A cone thus described can be cut and flattened into a flat arc of inner radius ri/cos A, outer radius ro/cos A, and with an arc angle, cos A*360 degrees.
In an embodiment, microsystem 600 incorporates a microbattery to provide energy for one or more functions realized in microsystem 600. In an embodiment, a cathode of a microbattery is fabricated on microsystem top component 106 and an anode of the microbattery is fabricated on microsystem bottom component 105. The completed microbattery is formed when the cathode is placed in contact with the anode during a fabrication process.
In an embodiment, microsystem 600 comprises one or more of the following: one or more thermal, pressure, chemical, and biochemical sensors; one or more medicine delivery mechanisms for release and/or controlled release of liquids and/or bioactive chemicals, one or more light based sensors, indicators and/or displays; one or more radio frequency, visible light, infrared, and audio transmitters and/or receivers. In an embodiment, micro system 600 comprises one or more tactile indicators, vibrators, photonic, particle, image, and/or tactile sensors. In an embodiment, microsystem 600 is embedded in a contact lens or is a corneal implant wherein microsystem 600 enhances and/or enables vision. In an embodiment, microsystem 600 is embedded in a contact lens and adjusts a focal length of the contact lens using an electro-optical mechanism on microsystem 600 or controlled by microsystem 600. Examples of an electro-optical mechanism are described in U.S. Patent Publication No. 2015/0029424 filed concurrently with this application, the entirety of which is incorporated by reference herein. In an embodiment, microsystem 600 comprises a heating element. In an embodiment, microsystem 600 comprises a microfluidic or micromechanical mechanism such as a gyroscope or motion sensor. In an embodiment, microsystem 600 comprises a scene, and/or facial, and/or movement (e.g., gate) recognition mechanism. In an embodiment, microsystem 600 is embedded in each of two contact lenses, one contact lens in each of two eyes, and a microsystem 600 in a contact lens in an eye communicates with another microsystem 600 that is in another contact lens that is in another eye of a same person or in an eye of another person.
In an embodiment, transparent conducting oxide 802 is indium tin oxide (ITO), however, those skilled in the art understand that other transparent conducting oxides can be used, such as indium zinc oxide (IZO), Al-doped zinc oxide (AZO), or Ga-doped zinc oxide (GZO). Transparent conducting oxide 802 serves as a cathode current collector. In an embodiment, a combination of ITO, IZO, AZO, and GZO can be used. In an embodiment, transparent conducting oxide 802 can be replaced with titanium (Ti), gold (Au), carbon-coated Ti or carbon-coated Au. In an embodiment, transparent conducting oxide 802 can be thin, with a thickness of between 20 nm and 200 nm, which provides for a mechanically flexible battery and consumes less space than a material requiring a thicker layer for the cathode current collector. A mechanically flexible battery facilitates a use of the battery in a system that can conform to a biological shape in a living tissue, for example. In an embodiment, the battery has a flexibility defined by a radius of curvature of between about 4 mm and 20 mm.
Having described embodiments of a cathode (which are intended to be illustrative and not limiting), it is noted that modifications and variations may be made by persons skilled in the art in light of the above teachings. It is therefore to be understood that changes may be made in the particular embodiments disclosed which are within the scope of the present invention as outlined by the appended claims.
In an embodiment of the present invention, anode material 1601 is electroplated in a bath in an electroplating tank that contains In in a concentration in a range of 100 ppm to 1000 ppm, Bi in a concentration in a range of 100 ppm to 1000 ppm, with In in a nominal concentration of 300 ppm+/−200 ppm and Bi in a nominal concentration of 300 ppm+/−200 ppm, and Zn. In an embodiment of the present invention, the electroplating tank has sufficient convection to keep the electroplated composition of anode material 1601 uniform independent of its thickness and/or the current used in the electroplating process. The current used electroplating process is pulsed to keep the electroplated composition of anode material 1601 uniform independent of its thickness.
In another embodiment, the component elements of anode material 1601 are electroplated on the exposed surface of seed metal 1302 in separate layers, one component element per layer, in separate electroplating steps and then the separate layers are annealed to create a single homogeneous layer.
Having described embodiments of an anode that is an electroplated homogeneous solid metallic alloy (which are intended to be illustrative and not limiting), it is noted that modifications and variations may be made by persons skilled in the art in light of the above teachings. It is therefore to be understood that changes may be made in the particular embodiments disclosed which are within the scope of the present invention as outlined by the appended claims.
Embodiments of the present invention recognize that, in a thin-film microbattery, an electroplated anode has many advantages over an anode composed of a mixture of particles that may be in the form of a paste, for example. The smallest dimension of a structure composed of a mixture of particles is limited to the size of the largest particle in the mixture. For example, if the diameter of the largest particle is about 25 microns, a typical size of a particle in a metallic powder, a minimum anode thickness of about 25 microns is potentially possible with a material that incorporates the particle, if constraints imposed by a fabrication process are not taken into account.
Embodiments of the present invention can achieve a thickness of 1 micron for anode material 1601, an electroplated homogeneous solid metallic alloy. Therefore the minimum patternable line width of the electroplated homogeneous solid metallic alloy is 1 micron or less, which facilitates its use in microbatteries and micro-miniaturized devices. Embodiments of the present invention recognize that common fabrication techniques (e.g., screening, stenciling, and printing) employed to form a structure using particle-based material incorporating particles 25 microns in size, limit a minimum dimension of the material to something greater than 100 microns.
In addition to being patternable down to a 1 micron dimension, the electroplated homogeneous solid metallic alloy has essentially no porosity, increasing its density and efficiency as it contains no wasted space. In one embodiment, the percentage of voids by volume in the electroplated homogeneous solid metallic alloy is less than 0.01%, preferably 0%. It is denser than a particle-based material that often contains voids, conductivity-enhancing additives, and binder additives that envelope the particles to hold them in place in a battery. Because of its density, the electroplated homogeneous solid metallic alloy can be plated to an essentially mirror smooth surface, whereas the smoothness of a particle-based material is defined by the sizes of the particles that it contains. In one embodiment, the proportions of the constituent components in anode material 1601 are homogeneous to the degree that the proportion of any constituent component (In, Bi, Zn) within a volume defined within the anode material, such as film height of anode material (in mm) cubed, deviates by less than 10% from the bulk proportion of that constituent component in the total volume of the anode material.
Embodiments of the present invention recognize that anode material 1601 is more volume-efficient than a particle-based material as the entirety of its mass participates in its function whereas only a portion of the total mass of the material composed of a mixture of particles participates in its function. Therefore a material with low or no porosity is advantageous in a microbattery. The size of a microbattery is a significant factor in determining whether a use of the battery is practical in an application or in a given physical environment.
In an embodiment, anode material 1601 is a homogeneous solid metallic alloy composed of 100 ppm to 1000 ppm Bi, 100 ppm to 1000 ppm In, and the remainder is Zn and because it is a continuous film, its resistivity is close to that of bulk zinc which is about 5×10−8 to 6×10−8 ohm-m. The resistivity of a zinc paste composed of particles is about 10000×10−8 ohm-m, which is about a 2000 fold increase in resistivity over that of anode material 1601. Embodiments of the present invention recognize that an anode material with a low resistivity is advantageous in a microbattery because the resistivity of the anode material contributes to the internal resistance of the microbattery. The greater a battery's internal resistance is, the slower the battery is in providing pulses of current to a load, i.e., the rise time of a current pulse increases as the internal resistance increases. Therefore for a microbattery that is required to provide significant pulses of current, a continuous film anode material is better than a porous paste approach that uses a particle-based material. In an embodiment, the surface the exposed surface of seed metal 1302 is textured so that electroplated anode material 1601 is textured to increase its surface area to enhance its ability to provide large current draws.
In addition, the homogeneous solid metallic alloy of anode material 1601 is mechanically stronger than that of a particle-based paste. The strength of anode material 1601 is about 100 MPa while that of a particle-based paste is at least 1000 times lower. The strength of an anode material contributes to the physical robustness of a microbattery. Because anode material 1601 is electroplated to seed metal 1302, the interface between seed metal 1302 and anode material is exceptionally strong, while the anode/current collector interface of a particle-based paste anode material is relatively weak and contact between the anode and the current collector is predominately maintained only by forces external to the interface. In a flexible microbattery, the interface between anode material 1601 and seed metal 1302 is unlikely to crack or delaminate under flexing while that of a particle-based anode material is much more apt to crack or delaminate under flexing.
The homogeneous solid metallic alloy of anode material 1601 may interface with a variety of electrolytes (e.g., alkaline (KOH), zinc acetate, zinc chloride, and ammonium chloride) without a need to reformulate a mixture of the components of anode material 1601. Because a particle-base paste requires a binder to hold its constituent particles together, the characteristics of a chemical reaction at the binder/electrolyte contact interface must be carefully considered when selecting appropriate materials, as only specific binders can work with a specific electrolyte and vise versa, making the design and development of such a structure relatively involved compared to that of homogeneous solid metallic alloy of anode material 1601.
Another consideration in a development of a particle-based paste anode is that of an optimization of the relative quantities of the binder, conductivity enhancers, and the constituent particles is the paste, and optimizing the solvent that is used during screening, stenciling, or printing of the paste. Tradeoffs must be made between resistivity and mechanical properties of the paste, and flow enhancers that fabrication techniques may require during construction of particle-based paste anode. Anode material 1601 is optimized in situ so no optimization or tradeoffs are required during its development, and since it is not a paste, no solvent is necessary to enhance its handling characteristics during fabrication.
In an embodiment, a thickness of microbattery 2102 is no greater than about 150 μm. In an embodiment, microbattery 2102 has a volume less than 1 cubic mm. In an embodiment, microbattery 2102 has a flexibility defined by a radius of curvature of between about 4 mm and 20 mm. In an embodiment, microbattery 2102 has metal or dielectric coating applied to an exterior plane and/or an end surface of one or more of a surface or substrate and/or adhesive join on microbattery 2102 to create a sealing layer to prevent electrolyte egress. In an embodiment, microbattery 2102 produces an open circuit voltage of between 1.4V and 1.8V and has a discharge capacity of between 10 uA-hours and 200 uA-hours. In an embodiment, microbattery 2102 has a total cavity volume of less than 1 cubic millimeters. In an embodiment, microbattery 2102 is less than 200 μm thick. In an embodiment, microbattery 2102 powers silicon die 206 and/or silicon die 306. In an embodiment, microbattery 2102 powers one or more silicon dies that are substantially similar to silicon die 206 or silicon die 306.
The first step in this exemplary process flow is to etch cavity 203 into top polymer flex substrate 201 (step 2202) to accommodate a construction of a cathode of microbattery 2102 (e.g., by laser processing). The process of etching cavity 203 uses a first mask in the process. Subsequent to etching cavity 203, adhesive metal layer 801 (e.g., titanium tungsten) is deposited into cavity 203 (step 2203) and transparent conducting oxide 802 (e.g., indium tin oxide) is deposited on adhesive metal layer 801 in cavity 203 (step 2204). Subsequent to depositing transparent conducting oxide 802, photoresist 901 is deposited over transparent conducting oxide 802 and is photopatterned using a second mask in the process (step 2208). Areas of unmasked transparent conducting oxide 802 and adhesive metal layer 801 are subtractively etched to create interconnect wiring trace 210 and 214 (step 2210). In a subtractive etching process, unmasked areas of a material are removed.
Subsequent to creating cavity 1002, the photoresist pattern created in step 2208 is stripped (step 2212) and, using a third mask in the process, polymer bondable seal material 1001 (polymer bondable seal material 202 and 213) is applied and photopatterned (step 2214) creating cavity 1002. Cathode material 1101 is inserted into cavity 1002 (step 2216) to complete the construction of the cathode side of microbattery 2102 (step 2216).
The first step in this exemplary process flow is to etch cavity 303, using a first mask in the process, into bottom polymer flex substrate 301 (step 2302) to accommodate a construction of an anode of microbattery 2102 (e.g., by laser processing). Adhesion metal layer 1301 (e.g., titanium tungsten) is deposited in cavity 303 (step 2304) and seed metal 1302 (e.g., copper) is deposited on adhesion metal layer 1301 in cavity 303 to create cavity 1303 (step 2306). Subsequent to depositing seed metal 1302 in cavity 303, deposit photoresist 1401 over seed metal 1302 to completely fill cavity 1303 and form photoresist 1401 over bottom polymer flex substrate 301. Using a second mask in the process, photopattern photoresist 1401 to create cavity 1502 to expose surface of seed metal 1302, the anode current collector (step 2308). The surface of seed metal 1302 is electroplated with a homogeneous solid to form anode material 1601 (step 2310). In an embodiment anode material 1601 is zinc. In another embodiment anode material 1601 is a homogeneous solid metallic alloy comprising 100 ppm to 1000 ppm Bi and 100 ppm to 1000 ppm In, and a remainder is Zn. The remainder of photoresist 1401 is stripped (step 2312).
Photoresist 1701 is deposited over seed metal 1302 and anode material 1601 to form a layer of photoresist 1701 over anode material 1601 and seed metal 1302. A patterning of photoresist 1701 defines wiring trace 310 and wiring trace 314 and a pattern of seed metal 1302 and adhesion metal layer 1301 (step 2314). In a subtractive etching process, unmasked areas of seed metal 1302 and adhesion metal layer 1301 are removed (step 2316). In other embodiments, a plurality of wiring traces are defined to meet a requirement of microsystem 600. The remainder of photoresist 1701 is stripped (step 2318). Using a forth mask in the process, polymer bondable seal material 1801 (polymer bondable seal material 302 and 313) is applied and photopatterned to create cavity 1802 (step 2320). Electrolyte separator material 1901 is deposited into cavity 1802 forming anode side 1902 of the microbattery, completing the construction of anode side 1902 of microbattery 2102 (step 2320).
The first step in this exemplary process flow is to mask and etch cavity 203 and cavity 303 into top polymer flex substrate 201 and bottom polymer flex substrate 301 respectively, to accommodate a construction of a cathode in cavity 203 and an anode in cavity 303 (step 2402). In an embodiment, cavity 212 and cavity 312 accommodate protuberances from the anode side and the anode side of microsystem 600 and are also etched in step 2402. In other embodiments, one or more other cavities are created on the cathode and/or anode sides of microsystem 600 to accommodate necessary system components. In an embodiment, the mask used in step 2402 is the first mask used in the exemplary process to form microsystem 600.
On the cathode side, an adhesion metal layer 801 and a layer of transparent conducting oxide 802 are deposited in cavity 203 (step 2404). On the anode side, adhesion metal layer 1301 and a layer of seed metal 1302 are deposited in cavity 303 (step 2404).
The anode side is masked and photopatterned to create cavity 1502 and expose a surface of seed metal 1302 in preparation for electroplating the surface (step 2406). In an embodiment, the mask used in step 2406 is the second mask used in the exemplary process to form microsystem 600. The exposed surface of seed metal 1302 is electroplated with a homogeneous solid composed of indium, bismuth, and zinc (In/Bi/Zn) to form anode material 1601 (step 2408).
A seed etch mask is applied to the anode side (photoresist 1701) and the cathode side (photoresist 901) and a subtractive etch is performed to create interconnect wiring traces 310 and 314 on the anode side and interconnect wiring traces 210 and 214 on the cathode side (step 2410). In other embodiments, one or more other appropriate wiring traces are created to distribute signals and power on microsystem 600. In an embodiment, the mask used in step 2410 is the third mask used in the exemplary process to form microsystem 600.
In an embodiment, the seed etch mask applied in step 2410 is stripped from the anode side and the cathode side, exposing the electroplated anode (anode material 1601) on the anode side and transparent conducting oxide 802 on a floor of 1002 on the cathode side (step 2412). In an embodiment, transparent conducting oxide 802 is indium tin oxide (ITO).
Polymer bondable seal material is applied and photopatterned, creating polymer bondable seal material 202 and 213 on the cathode side and creating polymer bondable seal material 302 and 313 on the anode side (step 2414). In an embodiment, the mask used in step 2414 is the fourth mask used in the exemplary process to form microsystem 600. Cathode material 1101 is applied to and fills cavity 1002 on the cathode side and electrolyte separator material 1901 is deposited into cavity 1802 on the anode side (step 2416). In an embodiment, cathode material 1101 is manganese dioxide (MnO2), however, those skilled in the art understand that other suitable materials can be used.
The anode side and the cathode side are conjoined (step 2418). A first handler is removed (temporary support wafer 103), and the outlines of microsystem 600 is laser cut, and then a second handler (temporary support wafer 104) is removed (step 2420), creating “C” shaped microsystem 500. Those skilled in the art know that the order in which temporary support wafer 103 and temporary support wafer 104 are removed is immaterial to the present invention. An opening in “C” shaped microsystem 500 is closed by a bonding of rabbet joint adhesive 308 on microsystem bottom component 105 with rabbet joint adhesive 208 on microsystem top component 106 (step 2422). In an embodiment, a fabrication process of microsystem 600 completes in step 2422.
The embodiments of the invention described herein employ photolithographic fabrication techniques, but those skilled in the art know that other fabrication techniques can be used to fabricate microsystem 600, such as electron beam lithography, scanning probe lithography, and particle lithography among other techniques.
| Number | Date | Country | |
|---|---|---|---|
| 61976595 | Apr 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14340304 | Jul 2014 | US |
| Child | 15789584 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15789584 | Oct 2017 | US |
| Child | 16028085 | US |