CATHODE MATERIAL AND PROCESS

Information

  • Patent Application
  • 20220380227
  • Publication Number
    20220380227
  • Date Filed
    November 05, 2020
    3 years ago
  • Date Published
    December 01, 2022
    a year ago
Abstract
The present invention belongs to the field of battery materials, and relates to a process for preparing a particulate lithium manganese nickel spinel compound, and materials produced by the process. The process of the invention uses Mn-containing precursors, Ni-containing precursors, Li-containing precursors and optionally M-containing precursor which form substantially no NOx ases during calcination. The particulate lithium manganese nickel spinel compound product of the process may find use in a lithium ion battery.
Description
FIELD OF THE INVENTION

The present invention relates to processes for preparing lithium manganese nickel oxide spinel materials, the lithium manganese nickel oxide spinel materials which result from those processes, and electrodes and cells comprising the materials.


BACKGROUND OF THE INVENTION

Lithium manganese oxides have been identified as useful cathode materials in lithium ion batteries. Of the lithium manganese oxides, compounds with the spinel structure, such as LiMn2O4 (stoichiometric spinel), Li2Mn4O9 (oxygen-rich spinel) and LiaMn5O12 (lithium-rich spinel) have shown particular promise as cathode materials.


Such spinel compounds are made by combining metal salt precursor compounds, commonly metal nitrates such as manganese nitrate. Not only are nitrate precursors expensive, they necessitate treatment of the process exhaust gases to remove toxic NOx gases. However, so far no alternative way to prepare spinels of suitably high capacity has been suggested in the art.


There is therefore a need for improved processes for preparing spinel compounds for use in lithium battery applications, e.g. lithium ion battery applications, which can provide products which intercalate lithium at a high potential vs Li/Li+, provide a high capacity and have good cyclability (capacity retention).


SUMMARY OF THE INVENTION

The inventors have found that a particular process for the preparation of lithium manganese nickel oxide (LM NO) spinel compounds not only provides compounds with high capacity and improved cyclability, but eliminates the generation of toxic NOx exhaust gases, thereby removing the need for costly, difficult and potentially dangerous exhaust gas treatment.


Accordingly, a first aspect of the invention is a process for the preparation of a particulate lithium manganese nickel spinel compound, the process comprising:


(a) preparing a composition comprising an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and optionally an M-containing precursor, wherein a single compound may optionally contain two or more of Mn, Ni and M;


(b) milling the composition; and


(c) calcining the product of step (b); wherein M is one or more elements selected from Al, Mg, Ti, Co, Cu and Cr; and wherein the Mn-containing precursor, Ni-containing precursor, Li-containing precursor and optional M-containing precursor are selected such that substantially no NOx gases are formed during the calcination in step (c).


Some embodiments provide a process for the preparation of a particulate lithium manganese nickel spinel compound of Formula I:





LixMnyNizMaOb   Formula I


the process comprising:


(a) preparing a composition comprising an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and optionally an M-containing precursor, wherein a single compound may optionally contain two or more of Mn, Ni and M;


(b) milling the composition; and


(c) calcining the product of step (b);


wherein M is one or more elements selected from Al, Mg, Ti, Co, Cu and Cr


0.8≤x≤1.2;


y=2-z-a;


0.2<z<1.2;


0≤a≤0.06; and


3.5≤b≤5;


and the Mn-containing precursor, Ni-containing precursor, Li-containing precursor and optional M-containing precursor are selected such that substantially no NOx gases are formed during the calcination in step (c).


The manufacturing method of the invention selects starting materials which do not generate NOx gas products when calcined, thereby removing the need for costly, difficult and potentially dangerous exhaust gas treatment to remove NOx gases (i.e. NOx NO2 or a mixture thereof). Furthermore, the product spinel has very good properties. A high capacity of at least 120 mAh/g may be achieved, in some cases as high as 134 mAh/g. The product may retain at least 93% of initial capacity after 200 cycles at a discharge rate of C/2, and 23° C. at an electrode loading of 6 mg/cm2, in some cases as high as 96% retention.


A second aspect of the invention is a lithium manganese nickel spinel compound obtained or obtainable by a process according to the first aspect.


A third aspect of the invention provides a positive active electrode material comprising the compound according to the second aspect.


A fourth aspect of the invention provides an electrode comprising the material according to the third aspect.


A fifth aspect of the invention provides a lithium secondary cell or battery comprising the electrode according to the fourth aspect.


A sixth aspect of the invention is the use of a compound according to the second aspect in a lithium secondary cell or battery.


A seventh aspect of the invention is a method of reducing or eliminating the emission of NOx gas product from a calcination process carried out during the manufacture of a particulate lithium manganese nickel spinel compound, comprising selecting an Mn-containing precursor, Ni-containing precursor, Li-containing precursor and optionally an M-containing precursor such that substantially no NOx gases are formed during the calcination, wherein M is one or more elements selected from Al, Mg, Co, Cu, Cr and Ti.


An eighth aspect of the invention is a method of improving the initial capacity and/or cyclability of a particulate lithium manganese nickel spinel compound, comprising the use of a Mn-containing precursor having a D90 particle size less than 4 μm, for example less than 3 μm, during the manufacture of the lithium manganese spinel compound.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a plot of the specific capacity of three comparative materials (Samples C, D and E) at various discharge rates (“C-rates”).



FIG. 2 shows the specific capacity of three comparative materials (Samples C, D and E) plotted against the number of discharge cycles.



FIG. 3 is a plot of the discharge potential curves for three comparative materials (Samples C, D and E).



FIG. 4 is a plot of the discharge potential curves for a material made according to the inventive process (Sample A) and a comparative material (Sample C).



FIG. 5 is a plot of the specific capacity of a material made according to the inventive process (Sample A) and a comparative material (Sample C) at various discharge rates (“C-rates”).



FIG. 6 shows the specific capacity of a material made according to the inventive process (Sample A) and a comparative material (Sample C) plotted against the number of discharge cycles.



FIG. 7 is a plot of the discharge potential curves for two different materials made according to the inventive process (Samples A and B).



FIG. 8 shows (a) a particle size distribution for a first MnCO3 powder used as a precursor, and (b) a particle size distribution for a second MnCO3 powder used as a precursor.



FIG. 9 shows (a) a particle size distribution for a lithium manganese nickel spinel material (Sample A) prepared by a process of the invention, and (b) an SEM image of the lithium manganese nickel spinel material (Sample A) prepared by a process of the invention.



FIG. 10 shows an XRD scan for a lithium manganese nickel spinel material (Sample A) prepared by a process of the invention.



FIG. 11 shows discharge curves for a lithium manganese nickel spinel material (Sample F) at various discharge rates.



FIG. 12 shows a particle size distribution for a MnCO3 powder used as a precursor in Comparative Example 4.





DETAILED DESCRIPTION

Preferred and/or optional features of the invention will now be set out. Any aspect of the invention may be combined with any other aspect of the invention unless the context demands otherwise. Any of the preferred and/or optional features of any aspect may be combined, either singly or in combination, with any aspect of the invention unless the context demands otherwise.


The exact composition of the final product lithium manganese nickel spinel in the process of the invention is not particularly limited. The invention concerns an improved process which is applicable to the preparation of a range of lithium manganese nickel spinel materials and the skilled person is able to tailor the identities and quantities of starting materials accordingly depending upon the desired end product.


In some embodiments, the particulate lithium manganese nickel spinel compound has a composition according to Formula I:





LixMnyNizMaOb Formula I


wherein M is one or more elements selected from Al, Mg, Ti, Co, Cu and Cr;


0.8≤x≤1.2;


y=2-z-a;


0.2<z<1.2;


0≤a≤0.06; and


3.5≤b≤4.5.


In Formula I, 0.8≤x≤1.2. In some embodiments x is greater than or equal to 0.9, or 0.95. In some embodiments, xis less than or equal to 1.1, or less than or equal to 1.05. In some embodiments, 0.90≤x≤1.10, for example 0.95≤x≤1.05. In some embodiments, x is about 1.0, for example equal to 1.0.


In Formula I, 0.2<z<1.2. In some embodiments, 0.2<z<1.15, for example 0.2<z<1.1, 0.2<z<1.05, 0.2<z<1.0, 0.2<z<0.95, 0.2<z<0.9, 0.2<z<0.85, 0.2<z<0.8, 0.25<z<0.8, 0.3<z<0.8, 0.3<z<0.75, 0.3<z<0.7, 0.3<z<0.65 or 0.3<z<0.6. In some embodiments, 0.3<z<0.5. In some embodiments, z is about 0.4, for example equal to 0.4.


In Formula I, 0≤a≤0.06. In some embodiments, 0≤a≤0.06, for example 0≤a≤0.059, 0≤a≤0.058, 0≤a≤0.057, 0≤0.056, 0≤0.055, 0≤a≤0.054, 0≤a≤0.053, 0≤a≤0.052, 0≤a≤0.051, 0≤a≤0.05, 0≤a≤0.01 0.06, 0≤a≤0.02 0.06, 0≤a≤0.03 0.06, 0≤a≤0.03 0.055, 0.03≤a≤0.05, 0.035≤a≤0.06 or 0.04≤a≤0.06. In some embodiments, a=0. In some embodiments, a is about 0.05, for example equal to 0.05.


In Formula I, 3.5≤b≤4.5. In some embodiments, 3.55≤b≤4.45, for example 3.6≤b≤4.4, 3.65≤b≤4.35, 3.7≤b≤4.3, 3.75≤b≤4.25, 3.8≤b≤4.2, 3.85≤b≤4.15, 3.9≤b≤4.1 or 3.95≤b≤4.05. In some embodiments, b is about 4, for example equal to 4.


In Formula I, M is one or more elements selected from AI, Mg, Co, Cu and Cr. In some embodiments M is Al. In some embodiments M is Al and 0<a≤0.06, for example 0<a≤0.059, 0<a≤0.058, 0<a≤0.057, 0<a≤0.056, 0<a≤0.055, 0.01<a≤0.06, 0.02<a≤0.06, 0.03<a≤0.06, or a is about 0.05, for example equal to 0.05.


In Formula I, y is (2-z-a). In some embodiments, 0.74<y<1.8, for example 0.75<y<1.8, 0.8<y<1.8, 0.85<y<1.8, 0.9<y<1.8, 0.95<y<1.8, 1.0<y<1.8, 1.05<y<1.8, 1.1<y<1.8, 1.15<y<1.8, 1.2<y<1.8, 1.25<y<1.8, 1.3<y<1.8, 1.3<y<1.75, 1.3<y<1.7, 1.4<y<1.7 or 1.5<y<1.7. In some embodiments, y is about 1.55, for example equal to 1.55.


In some embodiments:


0.8≤x≤1.2;


0.2<z<1.2;


0≤a≤0.06; and


3.5≤b≤4.5;


wherein M is Al.


In some embodiments:


0.8≤x≤1.2;


0.2<z<0.6;


0≤a≤0.06; and


3.5≤b≤4.5.


In some embodiments:


0.9≤x≤1.1;


0.2<z<0.6;


0≤a≤0.06; and


3.5≤b ≤1.5.


In some embodiments:


0.9≤x≤1.1;


0.2<z<0.6;


0≤a≤0.06; and


3.9≤b≤4.1.


In some embodiments:


0.9≤x≤1.1;


0.3<z<0.5;


0≤a≤0.06; and


3.9≤b≤4.1.


In some embodiments:


0.9≤x≤1.1;


0.3<z<0.5;


a=0; and


3.9≤b≤4.1.


In some embodiments:


0.9≤x≤1.1;


0.3<z<0.5;


0.04≤a≤0.06; and


3.9≤b≤4.1;


wherein M is Al.


In some embodiments, the lithium manganese nickel spinel compound of Formula I is selected from:





LiMn1.6Ni0.4O4   Formula IA





LiMn1.55Ni0.4Al0.05Ob   Formula IB





LiMn1.55Ni0.4Ti0.05Ob   Formula IC





LiMn1.55Ni0.40O0.05Ob   Formula ID





LiMn1.50Ni0.45Al0.05Ob   Formula IE





LiMn1.45Ni0.5Al0.05Ob   Formula IF


Wherein 3.5≤b≤4.5. In some embodiments the lithium manganese nickel spinel compound of Formula I is selected from one of Formula IA to Formula IF and b=4. In some embodiments, the lithium manganese nickel spinel compound is a compound according to Formula IB and b=4.


In some embodiments, the particulate lithium manganese nickel spinel compound is a crystalline (or substantially crystalline) material. In some embodiments, the compound crystallises in the space group Fd-3m. In some embodiments, the lattice parameter is 8.170-8.180 Å, for example 8.170-8.175 Å, for example 8.170-8.174 Å, for example 8.171-8.174 Å.


The particles of lithium manganese nickel spinel typically have a D50 particle size of at least 4.0 μm, for example at least 4.1 μm, at least 4.2 μm, at least 4.3 μm, at least 4.4 μm, at least 4.5 μm, at least 4.6 μm or at least 4.7 μm. In some embodiments, the particles of lithium manganese nickel spinel have a D50 particle size of at least 7.0 μm, for example at least 7.1 μm, at least 7.2 μm, at least 7.3 μm or at least 7.4 μm. The particles of lithium manganese nickel spinel typically have a D50 particle size of 10.0 μm or less, for example 10.0 μm or less, 9.5 μm or less, 9.0 μm or less, 8.5 μm or less, 8.0 μm or less, 7.9 μm or less, 7.8 μm or less, 7.7 μm or less, 7.6 μm or less or 7.5 μm or less. In some embodiments, the D50 particle size is from about 4.0 μm to about 10.0 μm, for example from about 5.0 μm to about 9.0 μm. Unless otherwise specified herein, the D50 particle size refers to Dv50 (volume median diameter) and may be determined by a dynamic light scattering method (e.g. using a Malvern Mastersizer 2000), for example according to ASTM B822 of 2017 under the Mie scattering theory.


The particles of lithium manganese nickel spinel typically have a D10 particle size of at least 1.5 μm, for example at least 1.6 μm, at least 1.7 μm, at least 1.8 μm, at least 1.9 μm, at least 2.0 μm, at least 2.2 μm or at least 2.5 μm. The particles of lithium manganese nickel spinel typically have a D10 particle size of 4.0 μm or less, for example 3.9 μm or less, 3.8 μm or less, 3.7 μm or less, 3.6 μm or less or 3.5 μm or less. In some embodiments, the D10 particle size is from about 1.5 μm to about 4.0 μm, for example from about 1.6 μm to about 3.9 μm, about 1.7 μm to about 3.8 μm, about 1.8 μm to about 3.7 μm, about 1.9 μm to about 3.6 μm or about 2.5 μm to about 3.6 μm. In some embodiments, the D10 particle size is from about 1.0 μm to about 2.7 μm, for example from about 1.05 μm to about 3.7 μm, about 1.1 μm to about 3.7 μm. Unless otherwise specified herein, the D10 particle size refers to Dv10 (10% intercept in the cumulative volume distribution) and may be determined by a dynamic light scattering method (e.g. using a Malvern Mastersizer 2000), for example according to ASTM B822 of 2017 under the Mie scattering theory.


The particles of lithium manganese spinel typically have a D90 particle size of at least 12.0 μm, for example at least 12.5 μm, at least 13.0 μm, at least 13.5 μm, at least 14.0 μm, at least 14.5 μm or at least 15.0 μm. The particles of lithium manganese nickel spinel typically have a D90 particle size of 18.0 μm or less, for example 17.9 μm or less, 17.8 μm or less, 17.5 μm or less, 17.0 μm or less or 16.5 μm or less. In some embodiments, the D90 particle size is from about 12.0 μm to about 18.0 μm, for example from about 12.5 μm to about 18.0 μm, about 13.0 μm to about 18.0 μm, about 13.0 μm to about 17.0 μm, about 13.5 μm to about 17.0 μm, about 14.0 μm to about 18.0 μm, about 15.0 μm to about 17.0 μm, about 15.5 μm to about 17.0 μm, about 16.0 μm to about 16.5 μm, about 14.0 μm to about 16.0 μm, about 14.0 μm to about 15.5 μm, about 14.0 μm to about 15.0 μm, about 14.0 μm to about 14.5 μm or about 14.5 μm to about 15 μm. Unless otherwise specified herein, the D90 particle size refers to Dv90 (90% intercept in the cumulative volume distribution) and may be determined by a dynamic light scattering method (e.g. using a Malvern Mastersizer 2000), for example according to ASTM B822 of 2017 under the Mie scattering theory.


In some embodiments, the particulate lithium manganese nickel spinel crystallites are substantially octahedral in shape, as determined from the analysis of an SEM image.


In some embodiments, the particulate lithium manganese nickel spinel compound has a bimodal particle size distribution. In some embodiments, a first peak of the bimodal particle size distribution occurs at around 4.0 to 7.0 μm and a second peak occurs at around 10.0 to 13.0 μm.


In some embodiments, the tapped density of the lithium manganese nickel spinel is from about 1.9 g/cm3 to about 2.4 g/cm3.


The tapped density of the material can suitably be measured according to ASTM B527. In some embodiments, the BET surface area of the lithium manganese nickel spinel is from about 0.5 cm2/g to about 2.5 cm2/g, for example from about 0.6 cm2/g to about 2.0 cm2/g, from about 0.6 cm2/g to about 1.5 cm2/g, from about 0.7 cm2/g to about 1.4 cm2/g, or about 1.0 cm2/g.


The BET surface area of the material can suitably be measured by gas adsorption: Method of Brunauer, Emmett and Teller (BET) according DIN 66131 (Multi-point determination), for example using GEMINI 2360 (Micromeritics) apparatus.


In the process according to the invention, the first step (a) is to prepare a composition comprising an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and optionally an M-containing precursor.


In some embodiments, step (a) comprises preparing a slurry comprising a solvent, an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and optionally an M-containing precursor. Thus some embodiments of the invention provide a process for the preparation of a particulate lithium manganese nickel spinel compound, the process comprising:


(a) preparing a slurry comprising a solvent, an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and optionally an M-containing precursor, wherein a single compound may optionally contain two or more of Mn, Ni and M;


(b) milling the slurry; and


(c) calcining the product of step (b);


wherein M is one or more elements selected from Al, Mg, Ti, Co, Cu and Cr; and wherein the Mn-containing precursor, Ni-containing precursor, Li-containing precursor and optional M-containing precursor are selected such that substantially no NOx gases are formed during the calcination in step (c).


The milling of a slurry rather than a dry precursor composition may assist in providing a more homogeneous mixture of the precursor components.


In some embodiments the process further comprises drying the slurry after the milling step (b) and before the calcining step (c). The drying may comprise spray-drying.


In some embodiments, the solvent is water. In some embodiments the solvent may be an alcohol.


In some embodiments, the first step (a) comprises preparing a composition comprising an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and an M-containing precursor. In some embodiments, the first step (a) comprises preparing a slurry comprising a solvent, an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and an M-containing precursor.


In some embodiments, one or more of the Mn-containing precursor, Ni-containing precursor, Li-containing precursor and (when present) M-containing precursor is soluble in the solvent. In some embodiments, one or more of the Mn-containing precursor, Ni-containing precursor, Li-containing precursor and (when present) M-containing precursor is insoluble in the solvent.


Herein, “soluble” indicates a solubility of at least 5 g/100 mL, for example at least 10 g/100 mL at 25° C. Herein, “insoluble” indicates a solubility of less than 0.10 g/100 mL, for example less than 0.05 g/100 mL, for example less than 0.02 g/100 mL at 25° C.


In some embodiments, one of the Mn-containing precursor, Ni-containing precursor, Li-containing precursor and (when present) M-containing precursor is soluble in the solvent. In some embodiments, the Li-containing precursor is soluble in the solvent and each of the Mn-containing precursor, Ni-containing precursor, and (when present) M-containing precursor are insoluble in the solvent.


In some embodiments, the first step (a) comprises providing a solution of Li-containing precursor, and adding an Mn-containing precursor, a Ni-containing precursor and optionally an M-containing precursor to the solution to prepare a slurry. In some embodiments, the solution is an aqueous solution. In some embodiments, each of the Mn-containing precursor, Ni-containing precursor, and (when present) M-containing precursor are insoluble in the solvent.


In some embodiments, the first step (a) comprises dissolving a Li-containing precursor in the solvent, and adding an Mn-containing precursor, a Ni-containing precursor and optionally an M-containing precursor to the solution to prepare a slurry. In some embodiments, each of the Mn-containing precursor, Ni-containing precursor, and (when present) M-containing precursor are insoluble in the solvent.


In some embodiments, the first step (a) further comprises stirring or agitating the solution/slurry during and/or after the addition of the precursors.


In some embodiments, the stirring or agitating of the slurry or solution may be carried out, for example, for a period of at least 10 minutes, at least 20 minutes, or at least 30 minutes. The period may be less than 5 hours, e.g. less than 2 hours.


In some embodiments, the first step (a) comprises dissolving a Li-containing precursor in the solvent, adding the Ni-containing precursor and (when present) the M-containing precursor to the solution, stirring or agitating the slurry, then adding the Mn-containing precursor and stirring or agitating the slurry again.


In some embodiments, the composition prepared in step (a) further comprises H3BO3. Without wishing to be bound by theory, H3BO3 is believed to support crystallisation during the synthesis and as a result a lower temperature may be used.


The Mn-containing precursor may be any compound of Mn which generates substantially no NOx products when calcined. In some embodiments, the Mn-containing precursor is insoluble in water at 25° C. In some embodiments, the Mn-containing precursor comprises or consists of one or more of MnCO3,MnO and Mn3O4. In some embodiments, the Mn-containing precursor comprises or consists of MnCO3.


The Ni-containing precursor may be any compound of Ni which generates substantially no NOx products when calcined. In some embodiments, the Ni-containing precursor is insoluble in water at 25° C. In some embodiments, the Ni-containing precursor comprises or consists of one or more compounds selected from Ni(OH)2, NiO, NiO(OH), nickel sulfate, nickel acetate and hydrated forms thereof. In some embodiments, the Ni-containing precursor comprises or consists of Ni(OH)2 or a hydrated form thereof.


The Li-containing precursor may be any compound of Li which generates substantially no NOx products when calcined. In some embodiments, the Li-containing precursor is soluble in water at 25° C. In some embodiments, the Li-containing precursor comprises or consists of one or more compounds selected from LiOH, Li2CO3 and hydrated forms thereof. In some embodiments, the Li-containing precursor comprises or consists of LiOH or a hydrated form thereof.


The M-containing precursor may be any compound(s) of the element(s) M which generates substantially no NOx products when calcined. In some embodiments, the M-containing precursor is insoluble in water at 25° C. In some embodiments, the M-containing precursor comprises one or more compounds selected from M hydroxide, M oxide, M sulfate, M carbonate, M acetate and hydrated forms thereof. In some embodiments, the M-containing precursor comprises an Al-containing precursor. In some embodiments, the Al-containing precursor comprises or consists of one or more of Al(OH)3 and Al2(SO4)3. In some embodiments, the Al-containing precursor comprises or consists of Al(OH)3.


In some embodiments, two or more of the Mn-containing precursor, Ni-containing precursor, and (when present) M-containing precursor may be provided as a single compound, for example a mixed metal hydroxide such as a mixed nickel manganese hydroxide.


NOx refers to one or both of the two gases nitrogen dioxide (NO2) and nitric oxide (NO). The term “generates substantially no NOx gases” means that the calcination produces either no NOx gas product, or an amount of NOx gas product negligible enough that treatment of the exhaust gas to remove the NOx would not be required. For example, in some embodiments the amount of NOx produced during the calcination is such that the concentration of NOx in the exhaust gas from calcination is less than 50 ppm, for example less than 45 ppm, less than 40 ppm, less than 35 ppm, less than 30 ppm, less than 25 ppm, less than 20 ppm, less than 15 ppm, less than 10 ppm, less than 5 ppm or less than 1 ppm. In some embodiments the amount of NOx produced during the calcination is such that the concentration of NOx in the exhaust gas from calcination is less than 0.9 ppm, for example less than 0.8 ppm, less than 0.7 ppm, less than 0.6 ppm, less than 0.5 ppm, less than 0.2 ppm or less than 0.1 ppm, and in some embodiments about 0 ppm.


Suitable methods for detecting NOx and monitoring levels of NOx in exhaust gases from chemical processes are known to the skilled person and include gas-phase FTIR techniques and mass spectrometry. For example, the Antaris (RTM) IGS FTIR Analyzer from Thermo Scientific (RTM) may be used to monitor the levels of NO and NO2 in the exhaust bases.


The skilled person is able to select suitable precursor compounds which generate substantially no NOx products when calcined. For example, the precursor compounds used in the process contain substantially no N-containing anions, since the presence of nitrate would generate NOx exhaust gas.


In particular, the precursor compounds used in the process contain substantially no nitrate, since the presence of nitrate would generate NOx exhaust gas. The term “substantially no nitrate” is intended to refer to a lack of nitrate while allowing for e.g. unavoidable nitrate present as impurities or trace amounts which would not generate substantial amounts of NOx and therefore would not necessitate exhaust gas treatment. In some embodiments, each precursor contains less than 10 wt % nitrate with respect to the weight of metal element in the precursor. For example, in some embodiments the Mn-containing precursor contains less than 10 wt % nitrate (NO3) with respect to the amount of Mn in the precursor. For comparison, the compound Mn(NO3)2 would contain 225.7 wt % nitrate with respect to the amount of Mn in the compound.


In some embodiments, each precursor contains less than 5 wt % nitrate with respect to the weight of metal element in the precursor, for example less than 4 wt %, less than 3 wt %, less than 2 wt %, less than 1 wt %, less than 0.9 wt %, less than 0.5 wt % or less than 0.1 wt %.


In some embodiments, each precursor contains less than 5 wt % nitrogen atoms with respect to the weight of metal element in the precursor, for example less than 4 wt %, less than 3 wt %, less than 2 wt %, less than 1 wt %, less than 0.9 wt %, less than 0.5 wt % or less than 0.1 wt %. This includes nitrogen present in compounds such as nitrates, nitrites, nitrides and any organic nitrogen-containing species.


In some embodiments, the D90 particle size of the Mn-containing precursor is at least 2.0 μm, for example at least 2.1 μm, at least 2.2 μm, at least 2.3 μm, at least 2.4 μm or at least 2.5 μm. In some embodiments, the D90 particle size of the Mn-containing precursor is 120 μm or less, for example 119 μm or less, 118 μm or less, 117 μm or less, 116 μm or less, 115 μm or less or 114 μm or less.


In some embodiments, the D90 particle size of the Mn-containing precursor is less than 4 μm. The inventors have found that the use of a Mn-containing precursor in the initial slurry which has a D90 particle size of less than 4 μm provides a superior product with improved capacity and improved cyclability. The inventors have surprisingly found that this also provides a product with particularly high phase-purity, which is evident from analysis of XRD patterns for the material. In some embodiments, the D90 particle size of the Mn-containing precursor is less than 3 μm, which provides particularly good results. In some embodiments, the D90 particle size of the Mn-containing precursor is less than 2.9 μm, for example less than 2.8 μm, less than 2.7 μm, less than 2.6 μm, less than 2.5 μm, less than 2.4 μm, less than 2.3 μm, less than 2.2 μm, less than 2.1 μm or less than 2.2 μm.


In some embodiments, the D90 particle size of the Mn-containing precursor is from about 2.0 pm to about 120 μm, for example from about 2.0 μm to about 115 μm, about 2.0 μm to about 100 μm, about 2.0 μm to about 50 μm, about 2.0 μm to about 20 μm, about 2.0 μm to about 15 μm or about 2.0 μm to about 10 μm. In some embodiments, the D90 particle size of the Mn-containing precursor is from about 2.0 μm to about 4.0 μm, for example from about 2.0 μm to about 3.0 μm, 2.1 μm to about 3.0 μm, about 2.2 μm to about 3.0 μm, about 2.3 μm to about 3.0 μm, about 2.3 μm to about 2.9 μm, about 2.3 μm to about 2.8 μm, about 2.3 μm to about 2.7 μm, about 2.4 μm to about 2.6 μm, or about 2.5 μm.


In some embodiments, the D50 particle size of the Mn-containing precursor is less than 2 μm, for example less than 1.9 μm, less than 1.8 μm, less than 1.7 μm, less than 1.6 μm or less than 1.5 μm. In some embodiments, the D50 particle size of the Mn-containing precursor is at least 1.0 μm, for example at least 1.05 μm, at least 1.1 μm, at least 1.15 μm or at least 1.2 μm. In some embodiments, the D50 particle size of the Mn-containing precursor is from about 1.0 μm to about 80 μm, for example from about 1.2 μm to about 75 μm, about 1.2 μm to about 70 μm, about 1.2 μm to about 65 μm, about 1.0 μm to about 50 μm, about 1.0 μm to about 20 μm or about 1.0 μm to about 5 μm. In some embodiments, the D50 particle size of the Mn-containing precursor is from about 1.0 μm to about 2.0 μm, for example from about 1.0 μm to about 1.5 μm.


In some embodiments, the D10 particle size of the Mn-containing precursor is less than 15 μm, for example less than 12 μm, less than 10 μm, less than 9 μm or less than 8 μm. In some embodiments, the D10 particle size of the Mn-containing precursor is less than 2 μm, for example less than 1.5 μm, less than 1.4 μm, less than 1.3 μm, less than 1.2 μm, less than 1.1 μm or less than 1 μm. In some embodiments, the D10 particle size of the Mn-containing precursor is at least 0.4 μm, for example at least 0.45 μm, at least 0.5 μm, at least 0.55 μm or at least 0.6 μm. In some embodiments, the D10 particle size of the Mn-containing precursor is from about 0.4 μm to about 15 μm, for example from about 0.4 μm to about 12 μm, about 0.4 μm to about 10 μm, about 0.4 μm to about 9 μm, about 0.4 μm to about 8 μm, about 0.45 μm to about 8 μm, about 0.5 μm to about 8 μm, about 0.55 μm to about 8 μm or about 0.6 μm to about 8 μm. In some embodiments, the D10 particle size of the Mn-containing precursor is from about 0.4 μm to about 2.0 μm, for example from about 0.5 μm to about 2.0 μm or from about 0.5 μm to about 1.0 μm.


In some embodiments, the Mn-containing precursor has a D90 particle size of from about 2.0 μm to about 4.0 μm, a D50 particle size of from about 1.0 μm to about 1.5 μm and a D10 particle size of from about 0.5 μm to about 1.0 μm. In some embodiments, the Mn-containing precursor has a D90 particle size of from about 2.0 μm to about 3.0 μm, a D50 particle size of from about 1.0 μm to about 1.5 μm and a D10 particle size of from about 0.5 pm to about 1.0 μm.


Mn-containing precursors having the preferred particle size distributions are commercially available, for example from Tropaq. Alternatively, the desired D90 for the Mn-containing precursor may be obtained by milling a precursor of larger particle size until the correct particle size is reached, for example using milling equipment. The nature of the milling equipment is not particularly limited. For example, it may be a ball mill, a planetary ball mill, a rolling bed mill or a Pearl mill.


In some embodiments, the D90 particle size of the Ni-containing precursor is less than 25 μm, for example less than 20 μm or less than 15 μm. In some embodiments, the D90 particle size of the Ni-containing precursor is from 10 μm to 25 μm, for example from 10 μm to 20 μm, from 10 μm to 15 μm or from 12 μm to 14 μm. In some embodiments, the D50 particle size of the Ni-containing precursor is less than 15 μm, for example less than 10 μm or less than 8 μm. In some embodiments, the D50 particle size of the Ni-containing precursor is from 5 μm to 15 μm, for example from 5 μm to 12 μm, from 5 μm to 10 μm or from 5 μm to 8 μm. In some embodiments, the D10 particle size of the Ni-containing precursor is less than 5 μm, for example less than 3 μm, less than 2 μm, less than 1 μm or less than 0.8 μm. In some embodiments, the D10 particle size of the Ni-containing precursor is from 0.1 μm to 5 μm, for example from 0.2 μm to 5 μm, from 0.5 μm to 2 μm or from 0.5 μm to 1 μm.


In some embodiments, the D90 particle size of the M-containing precursor (e.g. Al-containing precursor) is less than 200 μm, for example less than 190 μm, less than 180 μm, less than 170 μm or less than 160 μm. In some embodiments, the D90 particle size of the M-containing precursor is from 120 μm to 200 μm, for example from 130 μm to 170 μm, from 140 μm to 160 μm or from 145 μm to 155 μm. In some embodiments, the D50 particle size of the M-containing precursor is less than 120 μm, for example less than 115 μm, less than 110 μm, less than 105 μm, less than 100 μm, less than 95 μm or less than 90 μm. In some embodiments, the D50 particle size of the M-containing precursor is from 50 μm to 120 μm, for example from 60 μm to 100 μm, from 60 μm to 90 μm or from 80 μm to 90 μm. In some embodiments, the D10 particle size of the M-containing precursor is less than 60 μm, for example less than 55 μm, less than 50 μm or less than 45 μm. In some embodiments, the D10 particle size of the M-containing precursor is from 30 μm to 55 μm, for example from 35 μm to 55 μm, from 35 μm to 50 μm or from 40 μm to 45 μm.


In step (b) of the process the composition which is prepared in step (a) is subjected to milling. Any suitable milling equipment known to the skilled person may be used. The nature of the milling equipment is not particularly limited. For example, it may be a ball mill, a planetary ball mill, a rolling bed mill or a Pearl mill. The milling may be carried out until the particles reach the desired size. For example, the composition is typically milled until the particles have a D50 particle size of less than 50 μm, e.g. less than 40 μm, less than 30 μm or less than 20 μm.


The use of such a milling step means that precursors of larger particle size may be used in the process with little or no negative impact on the structure or properties of the product. This makes the process more economical and more easily scalable, since larger particle size precursors are less expensive.


Thus in some embodiments, the process comprises

    • (a) preparing a composition comprising an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and optionally an M-containing precursor, wherein a single compound may optionally contain two or more of Mn, Ni and M;
    • (b) milling the composition; and
    • (c) calcining the product of step (b);
    • wherein M is one or more elements selected from Al, Mg, Ti, Co, Cu and Cr;
    • wherein the Mn-containing precursor, Ni-containing precursor, Li-containing precursor and optional M-containing precursor are selected such that substantially no NOx gases are formed during the calcination in step (c);
    • and wherein the Mn-containing precursor has a D90 particle size of at least 10 μm, for example at least 20 μm, at least 30 μm, at least 40 μm, at least 50 μm, at least 60 μm, at least 70 μm, at least 80 μm, at least 90 μm, at least 100 μm or at least 110 μm. In some embodiments, the Mn-containing precursor has a D10 particle size of at least 2 μm (for example at least 5 μm), a D50 particle size of at least 10 μm (for example at least 50 μm) and D90 particle size of at least 10 μm (for example at least 80 μm). In this way, a more economical process of preparing a high-quality product is provided.


In some embodiments the composition is a slurry and the slurry is subjected to milling in step (b).


In some embodiments, the composition is milled in a Pearl mill. This provides the advantage that the composition is in a circular flow and so is milled several times.


In some embodiments, the milling comprises milling in the presence of inert grinding media, for example grinding beads.


In some embodiments, grinding beads used in the mill comprise zirconium oxide (ZrO2).


In some embodiments, the grinding beads have a diameter of less than 1 mm, for example less than 0.9 mm, less than 0.8 mm or less than 0.7 mm. In some embodiments, 0.6 mm ZrO2 grinding beads are used.


In some embodiments, the milling is carried out for at least 30 mins, for example at least 45 mins, at least 60 mins, at least 75 mins, at least 90 mins or at least 105 mins. In some embodiments, the milling is carried out for up to 5 hrs, for example up to 4.5 hrs, up to 4 hrs, up to 3.5 hrs, up to 3 hrs, or up to 2.5 hrs.


In some embodiments, the milling is carried out for at least 2 hours. Such increased milling time allows a precursor of larger particle size to be used without jeopardising the product structure or properties, which as explained above provides a more economical process.


In some embodiments the slurry when added to the mill has a solids content of at least 10 wt %, for example at least 15 wt %, at least 20 wt %, at least 25 wt %, at least 30 wt %, at least 35 wt % or at least 40 wt %. In some embodiments the slurry when added to the mill has a solids content of up to 80 wt %, for example up to 75 wt %, up to 70 wt %, up to 65 wt %, up to 60 wt %, up to 55 wt % or up to 50 wt %. In some embodiments the slurry when added to the mill has a solids content of 10-80 wt %, for example 10-70 wt %, 20-70 wt %, 30-70 wt %, 30-60 wt %, 40-60 wt % or 40-50 wt %.


In some embodiments, the milling speed during step (b) is at least 1000 rpm, for example at least 1500 rpm, at least 2000 rpm or at least 2500 rpm. In some embodiments, the milling speed is about 3000 rpm.


When the composition which is subjected to milling comprises a solvent (i.e. when the composition is a slurry), after the milling in step (b), the milled slurry is dried.


Any suitable drying method known to the skilled person may be used, but preferably the slurry is spray-dried. This makes the drying step easier to scale up.


Other possible drying methods include drying the slurry in a heated vacuum oven.


In some embodiments, the slurry is spray-dried at a temperature of at least 150° C., for example at least 160° C., at least 170° C., at least 180° C., at least 190° C., at least 200° C. or at least 210° C. In some embodiments, the slurry is spray-dried at a temperature of up to 280° C., for example up to 270° C., up to 260° C., up to 250° C., up to 240° C. or up to 230° C. In some embodiments, the slurry is spray-dried at a temperature of 150-280° C., for example 160-270° C., 170-270° C., 180-270° C., 180-260° C., 180-250° C., 190-250° C., 190-240° C., 200-240° C., 200-230° C. or 210-230° C.


The skilled person will understand that the temperature selection will depend upon the scale of the spray drying process, with higher temperatures being possible for larger-scale processes (e.g. up to about 400° C.).


In some embodiments, the outlet temperature of the nozzle during the spray drying method is maintained at a temperature of from 80-130° C., for example 80-120° C., 90-120° C. or 100-120° C. As will be understood by the skilled person, the outlet temperature can be adjusted by adjustment of the pump speed.


The product of the drying step is a dry material which is then calcined in step (c).


Calcination of the composition is carried out in step (c).


In some embodiments, during calcination the material is exposed to a temperature of at least 350° C., for example at least 360° C., at least 370° C., at least 380° C., at least 390° C., at least 400° C., at least 410° C., at least 420° C., at least 430° C. or at least 440° C. for at least part of the calcination. In some embodiments, at least part of the calcination is carried out at a temperature of at least 750° C., for example at least 760° C., at least 770° C., at least 780° C., at least 790° C., at least 800° C., at least 810° C., at least 820° C., at least 830° C. or at least 840° C.


In some embodiments, for at least part of the calcination the material is exposed to a temperature of 350-950° C., for example 400-900° C., 440-860° C., 750-950° C., 760-940° C., 770-930° C., 780-920° C., 790-910° C., 800-900° C., 810-890° C., 820-880° C., 830-870° C. or 840-860° C. In some embodiments, for at least part of the calcination the material is exposed to a temperature of about 850° C. In some embodiments, for at least part of the calcination the material is exposed to a temperature of about 450° C.


In some embodiments, calcination is performed by heating the material up from ambient temperature T0 to a temperature T1 (over a period of ramping time t0-1) and holding the material at T1 for a period of time t1. In some embodiments, T1 is a temperature of 350-950° C., for example 400-900° C., 440-860° C., 750-950° C., 760-940° C., 770-930° C., 780-920° C., 790-910° C., 800-900° C., 810-890° C., 820-880° C., 830-870° C. or 840-860° C. In some embodiments, T1 is a temperature of about 850° C. T0 may be around room temperature.


In some embodiments, t1 is at least 10 mins, for example at least 20 mins, at least 30 mins, at least 40 mins or at least 50 mins. In some embodiments, t1 is up to 15 hrs, for example up to 14.5 hrs, up to 14 hrs, up to 13.5 hrs, up to 13 hrs, up to 12.5 hrs or up to 12 hrs. In some embodiments, t1 is from 20 mins to 15 hrs, for example 1 hr to 15 hrs, 5 hrs to 15 hrs or 8 mins to 13 hrs. In some embodiments, t1 is about 12 hrs.


In some embodiments, to_i is from about 1 to 10 hrs, for example from about 2 to 8 hrs, about 2 to 6 hrs, about 3 to 6 hrs or about 5 hrs.


Calcination may be performed in any suitable calciner, and non-limiting examples include a furnace, such as a batch furnace.


After calcination the material may be left to cool at ambient temperature.


The calcination step may be carried out in air. In other embodiments the calcination step may be carried out under a C2-free atmosphere. For example, CO2-free air may be flowed over the materials to be calcined during calcination and optionally during cooling. The C2-free air may, for example, be a mix of oxygen and nitrogen. The C2-free atmosphere may be oxygen (e.g. pure oxygen). Preferably, the atmosphere is an oxidising atmosphere. As used herein, the term “C2-free” is intended to include atmospheres including less than 100 ppm CO2,e.g. less than 50 ppm CO2,less than 20 ppm CO2 or less than 10 ppm CO2. These CO2 levels may be achieved by using a CO2 scrubber to remove CO2.


In some embodiments, the method further comprises a step (d) after calcination of deagglomerating the calcined material. In some embodiments, this comprises low-energy milling.


In some embodiments, the method further comprises a step of sieving the material. In some embodiments, the method further comprises deagglomeration followed by sieving. In some embodiments, the a sieve with an aperture size less than 60 μm is used, for example less than 55 μm or less than 50 μm.


The process of the present invention may further comprise the step of forming an electrode (typically a cathode) comprising the lithium manganese nickel spinel compound. Typically, this is carried out by forming a slurry of the particulate lithium manganese spinel compound, applying the slurry to the surface of a current collector (e.g. an aluminium current collector), and optionally processing (e.g. calendaring) to increase the density of the electrode. The slurry may comprise one or more of a solvent, a binder, carbon material and further additives.


Typically, the electrode of the present invention will have an electrode density of at least 2.5 g/cm3, at least 2.8 g/cm3 or at least 3 g/cm3. It may have an electrode density of 4.5 g/cm3 or less, or 4 g/cm3 or less. The electrode density is the electrode density (mass/volume) of the electrode, not including the current collector the electrode is formed on. It therefore includes contributions from the active material, any additives, any additional carbon material, and any remaining binder.


The process of the present invention may further comprise constructing a battery or electrochemical cell including the electrode comprising the lithium nickel oxide. The battery or cell typically further comprises an anode and an electrolyte. The battery or cell may typically be a secondary (rechargeable) lithium (e.g. lithium ion) battery.


A second aspect of the invention is a lithium manganese nickel spinel compound obtained or obtainable by a process according to the first aspect.


The lithium manganese spinel compound is characterised by high initial capacity and high capacity retention. In some embodiments, the compound retains at least 92% capacity after 200 cycles at 23° C., a discharge rate of C/2 and an electrode loading of 6 mg/cm2, for example at least 92.5%, at least 93%, at least 93.5%, at least 94%, at least 94.5%, at least 95% or at least 95.5%.


In some embodiments, the compound provides an initial capacity of at least 125 mAh/g, for example at least 126 mAh/g, at least 127 mAh/g, at least 128 mAh/g, at least 129 mAh/g, at least 130 mAh/g, at least 131 mAh/g, at least 132 mAh/g, at least 133 mAh/g, at least 134 mAh/g or at least 135 mAh/g.


A third aspect of the invention provides a positive active electrode material comprising the compound according to the second aspect.


A fourth aspect of the invention provides an electrode comprising the material according to the third aspect.


A fifth aspect of the invention provides a lithium secondary battery comprising the electrode according to the fourth aspect.


Another aspect of the invention is the use of a compound according to the second aspect in a lithium secondary cell or battery.


The present invention will now be described with reference to the following examples, which are provided to assist with understanding the present invention, and are not intended to limit its scope.


EXAMPLES
Example 1—Preparation of LiMn1.55Ni0.4Al0.05O4 from Hydroxide and Carbonate Precursors

58.4 g of LiOH.H2O (SQM) was dissolved in 250 mL of H2O.Ni(OH)2 (Todini GmbH, D50=5.9 μm) and Al(OH)3 (Clariant; D90=152.77 μm, D50=87.63 μm, D10=43.29 μm) were added along with an additional 50 mL of H2O, and the slurry was mixed at 3000 rpm using an Ultra Turrax disperser for 30 mins.


MnCO3 with a D90 particle size of 2.5 μm, a D50 particle size of 1.23 μm and a D10 particle size of 0.62 μm (Tropaq UF, Clariant) was added and the slurry was mixed for a further 20 mins at 6000 rpm. A particle size distribution of the MnCO3 powder is shown in FIG. 8(a).


1.14 g of H3BO3 and 2.3 g of LiOH were then thoroughly mixed in a pestle and mortar and added to the slurry with an additional 300 mL of H2O.


The slurry was then milled in a pearl mill for 2 hours. The chamber was 80% filled with 0.6 mm ZrO2 balls, and the slurry had a solids content of 42 wt %. The mill speed was 3000 rpm and the pump speed was 2500 rpm.


After milling the slurry was spray-dried using a Buchi lab spray dryer at 220° C. whilst the pump speed was adjusted to maintain the outlet temperature at 110° C. Subsequently the collected powder was calcined in air by heating up to 850° C. over 5 hours, then holding at 850° C. for 12 hours, using a batch furnace from Nabertherm. After calcination the powder was removed from the furnace and allowed to cool at ambient temperature. The powder was then gently milled in a Fritsch mill to de-agglomerate and passed through a 45 μm sieve.


The product, denoted “Sample A” herein, was found to have a D50 particle size of 5.68 μm. A typical particle size distribution is shown in FIG. 9(a).



FIG. 9(b) shows an SEM image of the lithium manganese nickel spinel material prepared in Example 1. FIG. 10 shows an XRD plot of the material.


Example 2—Preparation of LiMn1.55Ni0.4Al0.05O4 from Hydroxide and Carbonate Precursors

The method of Example 1 was carried out except that the MnCO3 precursor used had a D90 particle size of 113.6 μm, a D50 particle size of 60.61 μm and a D10 particle size of 7.84 μm (Tropaq HP, Clariant). A particle size distribution of the MnCO3 powder is shown in FIG. 8(b). The product is denoted “Sample B” herein.


Comparative Example 1—Preparation of LiMn1.55Ni0.4Al0.05O4 from Nitrate and Carbonate Precursors

Mn(NO3)2.4H2O, Ni(NO3)2.6H2O and Al(NO3)3.9H2O were dissolved in deionised water using an Ultra Turrax mixer for 30 minutes. Separately, LiOH.H2O was dissolved in deionised water with H3BO3. Subsequently the LiOH/H3BO3 solution was added dropwise to the mixed metal nitrate solution. The suspensions were mixed with the Ultra Turrax mixer for 10 minutes and then 60 minutes in a Pendraulik mixer.


MnCO3 with a D90 particle size of 2.5 μm, a D50 particle size of 1.23 μm and a D10 particle size of 0.62 μm (Tropaq UF) was added and the suspension which was then mixed for a further hour. The suspension was then milled in a bead mill for 1 hour. The grinding chamber was filled 75% with 1.3 mm ZrO2 balls and the solids content of the suspension was 50%. The milling was conducted over 3×20 minute periods with 20 minutes' rest between each milling period.


The milled suspension was spray-dried at 220° C., the pump rate was maintained to keep the outlet temperature around 110° C. Subsequently the collected powder was calcined in air at 450° C. for 1 hour and then 12 hours at 850° C. After calcination the powder was gently milled to de-agglomerate and passed through a 45 μm sieve.


The product, denoted “Sample C” herein, was found to have a D90 particle size of 11.01 μm, a D50 particle size of 4.79 μm and a D10 particle size of 1.68 μm.


Comparative Example 2—Preparation of LiMn1.55Ni0.4Al0.05O4 from Nitrate and Carbonate Precursors

The method of Comparative Example 1 was carried out except that the MnCO3 precursor used had a D90 particle size of 113.6 μm, a D50 particle size of 60.61 μm and a D10 particle size of 7.84 μm (Tropaq HP).


The product, denoted “Sample D” herein, was found to have a D90 particle size of 13.50 μm, a D50 particle size of 5.65 μm and a D10 particle size of 2.13 μm.


Comparative Example 3—Preparation of LiMn1.55Ni0.4Al0.05O4 from Nitrate and Carbonate Precursors

The method of Comparative Example 1 was carried out except that the MnCO3 precursor used had a D90 particle size of 113.6 μm, a D50 particle size of 60.61 μm and a D10 particle size of 7.84 μm (Tropaq HP). Furthermore, after the addition of the MnCO3,the milling in the bead mill was carried out for 4 hours instead of 1 hour.


The product, denoted “Sample E” herein, was found to have a D90 particle size of 12.73 μm, a D50 particle size of 5.98 μm and a D10 particle size of 2.47 μm.


Comparative Example 4—Preparation of LiMn1.55Ni0.4Al0.05O4 from Nitrate and Carbonate Precursors

Mn(NO3)2.4H2O, Ni(NO3)2.6H2O and Al(NO3)3.9H2O were dissolved in deionised water using an Ultra Turrax mixer for 30 minutes. Separately, LiOH.H2O was dissolved in deionised water with H3BO3. Subsequently the LiOH/H3BO3 solution was added dropwise to the mixed metal nitrate solution. The suspensions were mixed with the Ultra Turrax mixer for 10 minutes and then 60 minutes in a Pendraulik mixer.


MnCO3 with a D90 particle size of 54.17 μm, a D50 particle size of 31.74 μm and a D10 particle size of 18.07 μm (Tropaq Type N) was added and the suspension which was then mixed for a further hour. The suspension was not subjected to any milling or grinding. A PSD for the Tropaq Type N MnCO3 is provided in FIG. 12.


The suspension was spray-dried at 220° C., the pump rate was maintained to keep the outlet temperature around 110° C. Subsequently the collected powder was calcined in air at 450° C. for 1 hour and then 12 hours at 850° C. After calcination the powder was gently milled to de-agglomerate and passed through a 45 μm sieve. The product is denoted “Sample F” herein.


Electrochemical Testing

Electrodes were made in a 90:5:5 active:carbon:binder formulation with an ink at 40% solids. A 10 wt % solution of polyvinylidene fluoride (PVdF; Solvay Solexis Solef 5130) in N-methyl pyrollidone (NMP; ex Aldrich) was prepared. A 2 g extract of this solution was taken and 3.5 g of NMP was added. 0.2 g carbon black (Timcal, Super P Li) was added and the composition was mixed for 1 hour at 4000 rpm with a tube drive. 3.6 g of active material as prepared in the above examples and comparative examples was added and further mixed for 1 hour at 4000 rpm with a tube drive.


The resulting ink was cast onto aluminium foils using a fixed blade coater to provide a foil coated on both sides with a wet thickness of 170 μm. The foil was pre-dried at 50° C. on a heating plate and then dried for 120 minutes at 120° C. under vacuum. Once dry, the electrode sheet was cut into electrodes of 13 mm diameter (1.33 cm2 area) and further dried in vacuum overnight at 160° C. The electrodes were then compacted at a static pressure of 10 t/cm2 for two 1-minute periods. The thickness of the dried and pressed electrodes was 45 μm, with a typical loading of active material from 5-10mg/cm2.


Testing was performed in half-cells with a 15 mm lithium foil disk as a counter electrode, PSI glass fibre separator and 0.4 mL electrolyte made up of fluorinated ethylene carbonate (FEC): DMC in a 1:4 volume ratio. Galvanostatic cycling tests were performed by cycling the cell at C/2 between 3.0 V and 5.1 V vs. Li/Li+.


The specific capacity of three different materials is plotted against discharge rate in FIG. 1. The plot shows the specific capacities of the materials prepared in Comparative Examples 1, 2 and 3 (Samples C, D and E respectively). The plot shows that to match the capacity and rate performance of the material of Comparative Example 1 (prepared from an Mn precursor of smaller particle size), it is necessary to increase the milling time from 1 hour to 4 hours when a larger Mn precursor particle size is used. In other words, 4 hours of milling was required to achieve the same degree of homogeneity in the material prepared from an Mn precursor of larger particle size.



FIG. 2 is a plot of the cycle life for the materials of Comparative Examples 1, 2 and 3 (Samples C, D and E respectively). The results show that to match the cycle life of the material of Comparative Example 1 (prepared from an Mn precursor of smaller particle size), it is necessary to increase the milling time from 1 hour to 4 hours when a larger Mn precursor particle size is used.



FIG. 3 shows discharge curves for the materials of Comparative Examples 1, 2 and 3 (Samples C, D and E respectively). The results show that the materials of Comparative Examples 1 and 3 have comparable specific energy, while the specific energy of the material of Comparative Example 2 is lower, which corresponds with the results shown in FIGS. 1 and 2. FIG. 3 also shows that the Mn(III) plateau at 4.0 V is longer for Comparative Examples 2 and 3 than for Comparative Example 1, indicating that the Mn precursor in Comparative Examples 2 and 3 was partially oxidised during the manufacturing process.



FIG. 4 plots the specific capacities of the materials of Example 1 and Comparative Example 1 (Samples A and C respectively). The results show that the capacity of the Example 1 material is higher than the Comparative Example 1 material.



FIG. 5 shows that the rate capabilities of the Example 1 and Comparative Example 1 materials (Samples A and C respectively) were comparable. No difference in life cycle performance is evident from the results shown in FIG. 6 over the duration of the test (25 cycles).


It is therefore possible to obtain a phase pure material, with a similar particle size, higher capacity and comparable rate capability and cycle life with the processes of the invention relative to existing processes which use nitrate precursors. In addition to this, no NOx gases are produced and therefore no exhaust gas treatment is necessary.



FIG. 7 shows the specific capacities of the materials of Example 1 and Example 2 (Samples A and B respectively).


XRD indicated that a single phase was formed in both Examples 1 and 2, with a comparable lattice parameter. This suggests that the same amount of Ni and Al was incorporated into the lattice despite the change in precursor. However the results in FIG. 7 show that the material of Example 2, made using the larger MnCO3 precursor, has a lower capacity (128 mAh/g) than that of Example 1 (134 mAh/g). This may be due to some oxidation of Mn(II) to Mn(III) during the manufacture of the Example 2 product.



FIG. 11 shows discharge curves for the material of Comparative Example 4 at five different discharge rates: D/5 (5 hours), 1D (1 hour), 3D (20 mins), 5D (12 mins) and 10D (6 mins). Relative to the inventive materials, the discharge curves in FIG. 11 show relatively low specific capacity even at low discharge rates and a short high-volt plateau indicating a lower specific energy.

Claims
  • 1-20. (canceled)
  • 21. A process for the preparation of a particulate lithium manganese nickel spinel compound, the process comprising: (a) preparing a composition comprising an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and optionally an M-containing precursor, wherein a single compound may optionally contain two or more of Mn, Ni and M;(b) milling the composition; and(c) calcining the product of step (b);wherein M is one or more elements selected from Al, Mg, Ti, Co, Cu and Cr;and wherein the Mn-containing precursor, Ni-containing precursor, Li-containing precursor and optional M-containing precursor are selected such that substantially no NOx gases are formed during the calcination in step (c).
  • 22. The process according to claim 21, wherein the amount of NOx produced during the calcination is such that the concentration of NOx in the exhaust gas from calcination is less than 50 ppm.
  • 23. The process according to claim 21, wherein each of the Mn-containing precursor, Ni-containing precursor, Li-containing precursor and optional M-containing precursor contain substantially no nitrate, for example less than 5 wt % nitrate with respect to the weight of metal element in the precursor.
  • 24. The process according to claim 1, wherein the D90 particle size of the Mn-containing precursor is less than 4 μm, for example less than 3 μm or less than 2.5 μm; and/or wherein the D50 particle size of the Mn-containing precursor is less than 2 μm; and/orwherein the D10 particle size of the Mn-containing precursor is less than 1 μm.
  • 25. The process according to claim 1, wherein the Mn-containing precursor has a D90 particle size of from about 2.0 μm to about 4.0 μm, a D50 particle size of from about 1.0 μm to about 1.5 μm and a D10 particle size of from about 0.5 μm to about 1.0 μm.
  • 26. The process according to claim 1, wherein the particulate lithium manganese nickel spinel compound has a Dio particle size of from about 1.0 μm to about 3.0 μm; and/or wherein the particulate lithium manganese nickel spinel compound has a D90 particle size of from about 8.0 μm to about 15.0 μm.
  • 27. The process according to claim 1, wherein the Mn-containing precursor comprises MnCO3 ; and/or wherein the Ni-containing precursor comprises Ni(OH)2 or a hydrated form thereof; and/orwherein the Li-containing precursor comprises LiOH or a hydrated form thereof.
  • 28. The process according to claim 1, wherein the composition is a slurry comprising a solvent, the Mn-containing precursor, the Ni-containing precursor, the Li-containing precursor and optionally the M-containing precursor.
  • 29. The process according to claim 28, further comprising a step of drying the slurry after the milling step (b) and before the calcining step (c), wherein the drying preferably comprises spray drying.
  • 30. The process according to claim 28, wherein step (a) comprises preparing a slurry comprising a solvent, an Mn-containing precursor, a Ni-containing precursor, a Li-containing precursor and an M-containing precursor.
  • 31. The process according to claim 21, wherein the M-containing precursor comprises an Al-containing precursor, preferably Al(OH)3.
  • 32. The process according to claim 21, wherein step (b) is carried out in a Pearl mill.
  • 33. The process according to claim 21, wherein the Mn-containing precursor has a D90 particle size of at least 10 μm, and the milling in step (b) is performed for a period of at least 2 hours.
  • 34. The process according to claim 21, wherein in step (c) calcination is performed at a temperature of 350-950° C.
  • 35. The process according to claim 21, wherein the particulate lithium manganese nickel spinel compound has a composition according to Formula I: LixMnyNizMaOb   Formula IWherein M is one or more elements selected from Al, Mg, Ti, Co, Cu and Cr;0.8≤x≤1.2;y=2-z-a;0.2<z<1.2;0≤a≤0.06; and3.5≤b≤5;
  • 36. A process according to claim 35, wherein 0.9≤x≤1.1;0.3<z<0.5;0.04≤a≤0.06; and3.9≤b≤4.1;and wherein M is Al.
  • 37. A particulate lithium manganese nickel spinel compound obtained or obtainable by a process according to claim 21.
  • 38. A positive active electrode material comprising the compound according to claim 37.
  • 39. An electrode comprising the material according to claim 38.
  • 40. A lithium secondary cell or battery comprising the electrode according to claim 39.
Priority Claims (1)
Number Date Country Kind
1916198.3 Nov 2019 GB national
PCT Information
Filing Document Filing Date Country Kind
PCT/GB2020/052800 11/5/2020 WO