Cationic Comb Copolymers, Preparation Thereof And Use Thereof In Cosmetic, Pharmaceutical And Dermatological Formulations

Abstract
Copolymers are described, containing a) 20.0-99.9% by weight of one or more structural units resulting from polymerizable substances of the following structural formula (I) in which R2 is a linear or branched saturated alkyl radical having 6 to 200 carbon atoms or a linear or branched, mono- or polyunsaturated alkenyl radical having 6 to 200 carbon atoms, and R1, Y, n and m are each as defined in claims 1, b) 0.1-20.0% by weight of one or more structural units resulting from polymerizable quaternary ammonium compounds, and c) 0-60.0% by weight of one or more nonionic structural units resulting from one or more further polymerizable substances. The copolymers are advantageously suitable, for example, for the production of cosmetic, dermatological or pharmaceutical formulations.
Description

The invention which follows relates to cationic comb copolymers, to a process for preparing such cationic comb copolymers, and to the use of these copolymers in cosmetic, pharmaceutical, and dermatological formulations.


Consumer desires and rheology of cosmetic products are closely interlinked. Thus, for example, the visual appearance of a shampoo or of a cream wash and the handling qualities of an oil are influenced by the viscosity. The sensorial properties, such as consistency or spreadability, determine the individual profile of a cosmetic product. Not only the effectiveness of active substances (e.g., sun protection filters) but also the storage stability of the formulation are closely correlated with the rheological properties of the products.


In the cosmetics segment, cationic polymers are accorded a key role as conditioners. State of the art are, in particular, conditioners based on polydiallyldimethylammonium chloride and the water-soluble copolymers thereof. The diversity of possible structures and the diverse possibilities for application that are associated with these structures are manifested not least in a multiplicity of patents filed worldwide since the mid-1970s.


A substantial drawback of the conditioners based on polydiallyldimethylammonium chloride is that, in oil-based formulations, they exhibit an inadequate thickening capacity. In order to improve the consistency of the formulations, fats and waxes are often added, which in turn bring with them the drawback of a dull and sticky skin feel.


The object was to provide substances for cosmetic, pharmaceutical, and dermatological formulations that exhibit conditioning properties for the skin and for the hair and that also have good consistency-imparting properties even in oil-based formulations or in formulations with a high oil fraction.


It has surprisingly been found that this object is achieved by certain cationic comb copolymers comprising structural units which derive, formally, from polymerizable quaternary ammonium compounds and from polymerizable nonionic compounds which comprise hydrocarbon groups having at least six carbon atoms.


The invention provides copolymers comprising


a) 20.0%-99.9% by weight of one or more structural units originating from polymerizable substances of the following structural formula (I)




embedded image


in which

  • R1 is hydrogen or methyl,
  • Y is a chemical bond, O, NR3, S, PR3, CH2, CH2O, CH2NR3, CH2S, C(O), C(NR3), C(O)O, C(O)NR3, C(NR4)NR3, C(O)S, R6OC(O)O, R6OC(O)NR3, R6R3NC(O)NR4, R6NR3C(NR5)NR4, R6OC(O)S, R6P(O)O, R6OP(O)O, R6S(O), R6S(O)(O), R6S(O)O, R6S(O)(O)O, R6OS(O)O or R6OS(O)(O)O,
  • R2 is a linear or branched saturated alkyl radical, having 6 to 200 carbon atoms, or a linear or branched mono- or polyunsaturated alkenyl radical having 6 to 200 carbon atoms,
  • R3, R4 and R5 each independently of one another are hydrogen or a linear or branched saturated alkyl radical having 1 to 200 carbon atoms, or a linear or branched mono- or polyunsaturated alkenyl radical having 2 to 200 carbon atoms,
  • R6 is a chemical bond or CH2, and
  • n and m each independently of one another are an integer from 0 to 200,


    b) 0.1%-20.0% by weight of one or more structural units, originating from polymerizable quaternary ammonium compounds, and


    c) 0%-60.0% by weight of one or more nonionic structural units originating from one or more further polymerizable substances.


The term “originating from one or more further polymerizable substances” set out above in component c) means, for the purposes of the present invention, that component c) does not comprise any compound which takes on a definition of the above-stated formula (I).


The copolymers of the invention are colorless to opaque and transparent, produce a good skin feel, and give the hair shine and good combability. They are suitable for preparing a very wide variety of cosmetic, pharmaceutical, and dermatological formulations, and are highly compatible in particular with water/oil-based or oil-based formulations. They display an outstanding oil-binding capacity and are able to thicken oils effectively. Furthermore, they display a good dispersing capacity and are suitable for imparting consistency stably to emulsions and creams. They are further suitable for the formulation of water-resistant sun protection products.


WO 2004/041220 and WO 2004/041150 describe cosmetic preparations, more particularly lipsticks and makeup preparations, which in addition to a liquid fatty phase comprise a semicrystalline polymer of a C14-C24-α-olefin and of a further monomer selected from carboxylic esters, preferably C14-C24 alkyl- or C11-C15 perfluoroalkyl (meth)acrylates, and N-alkyl(meth)acrylamides.


EP 1 681 046 describes cosmetic, pharmaceutical, and dermatological preparations which comprise copolymer waxes. The copolymer waxes comprise structural units derived formally from α-olefins having 26 to 60 carbon atoms, derivatives of (meth)acrylic acid such as esters, amides or salts, and optionally further monomers.


EP 1 693 047 describes cosmetic, pharmaceutical, and dermatological preparations which comprise copolymer waxes. The copolymer waxes comprise structural units derived from α-olefins having 26 to 60 carbon atoms, from maleic anhydride, maleic acid or salts thereof, and optionally from further monomers.


Preferred copolymers of the invention comprise 20.0% to 99.9% by weight of one or more structural units of component a) originating from polymerizable substances of the following structural formula (I)




embedded image


in which

  • R1 is hydrogen or methyl,
  • Y is a chemical bond, O, NR3, S, CH2O, CH2NR3, CH2S, C(O), C(NR3), C(O)O or C(O)NR3, preferably a chemical bond, O, NR3, CH2O, CH2NR3, C(O)O or C(O)NR3, and more preferably a chemical bond C(O)O or C(O)NR3,
  • R2 is a linear or branched saturated alkyl radical having 6 to 200, preferably having 8 to 58, more preferably having 12 to 40, and with particular preference having 12 to 30 carbon atoms, or a linear or branched mono- or polyunsaturated alkenyl radical having 6 to 200, preferably having 8 to 58, more preferably having 12 to 40, and with particular preference having 12 to 30 carbon atoms,
  • R3 is hydrogen or methyl, and
  • n and m each independently of one another are an integer from 0 to 200, preferably from 0 to 100, more preferably from 0 to 50, and with particular preference from 0 to 30.


In the compounds of the formula (I), Y with particular preference is a chemical bond or C(O)O.


Particularly preferred copolymers of the invention comprise 20.0% to 99.9% by weight of one or more structural units of component a) originating from one or more polymerizable compounds selected from the structural formulae (Ia), (Ib), and (Ic)




embedded image


in which

  • R1 is hydrogen or methyl, and
  • R2 is a linear or branched saturated alkyl radical having 6 to 200, preferably having 8 to 58, more preferably having 12 to 40, and with particular preference having 12 to 30 carbon atoms, or a linear or branched mono- or polyunsaturated alkenyl radical having 6 to 200, preferably having 8 to 58, more preferably having 12 to 40, and with particular preference having 12 to 30 carbon atoms, and
  • n and m each independently of one another are an integer from 0 to 200, preferably from 0 to 100, more preferably from 0 to 50, and with particular preference from 0 to 30, and the sum n+m is a number from 1 to 200, preferably from 2 to 100, more preferably from 3 to 50, and with particular preference from 3 to 30.


In one preferred embodiment of the invention, preference among the compounds of the formula (Ia) is given to the (meth)acrylic esters of the alkyl alcohols, i.e., R2 in these preferred compounds of the formula (Ia) is an alkyl radical. In one particularly preferred embodiment of the invention, R2 in these compounds is a linear alkyl radical.


The prefix “(meth)acryl” for the purposes of the present invention is an abbreviational designation for the two prefixes, “acryl” and “methacryl”.


In a further preferred embodiment of the invention, among the compounds of the formula (Ia), the (meth)acrylic esters of lauryl, myristyl, cetyl, stearyl, isostearyl, oleyl, octyldodecyl, behenyl, and myricyl alcohols are preferred.


In a further preferred embodiment of the invention, among the compounds of the formula (Ia), the (meth)acrylic esters of alcohols having 12 to 22 carbon atoms are preferred. In this preferred embodiment of the invention, among the compounds of the formula (Ia), the (meth)acrylic esters of lauryl, myristyl, cetyl, stearyl, isostearyl, oleyl, octyldodecyl, and behenyl alcohols are particularly preferred, and the (meth)acrylic esters of lauryl, cetyl, stearyl, isostearyl, octyldodecyl, and behenyl alcohols are especially preferred. Of the (meth)acrylic esters just stated, preference is given in turn to those of the linear alkyl alcohols.


In another preferred embodiment of the invention, among the compounds of the formula (Ib), the substances selected from (meth)acrylic esters of alkyl-polyethylene glycols, of alkyl-polypropylene glycols and of alkyl-polyethylene-polypropylene glycols are preferred, i.e., R2 in these preferred compounds of the formula (Ib) is an alkyl radical. In one particularly preferred embodiment of the invention, R2 in these compounds is a linear alkyl radical.


In a further preferred embodiment of the invention, “m” in the compounds of the formula (Ib) is 0, i.e., these compounds are purely ethoxylated compounds. Where m in the compounds of the formula (Ib) is 0, n is an integer from 1 to 200, preferably from 2 to 100, more preferably from 3 to 50 and with particular preference from 3 to 30.


In another preferred embodiment of the invention, among the compounds of the formula (Ib), the acrylic and/or methacrylic esters of alcohol polyglycol ethers are selected from


a) lauryl ethoxylates, more particularly

  • Genapol® LA 020 lauryl ethoxylate with 2 EO C12/14 alcohol, linear
  • Genapol® LA 030 lauryl ethoxylate with 3 EO C12/14 alcohol, linear
  • Genapol® LA 040 lauryl ethoxylate with 4 EO C12/14 alcohol, linear
  • Genapol® LA 050 lauryl ethoxylate with 5 EO C12/14 alcohol, linear
  • Genapol® LA 070 lauryl ethoxylate with 7 EO C12/14 alcohol, linear
  • Genapol® LA 080 lauryl ethoxylate with 8 EO C12/14 alcohol, linear
  • Genapol® LA 090 lauryl ethoxylate with 9 EO C12/14 alcohol, linear
  • Genapol® LA 110 lauryl ethoxylate with 11 EO C12/14 alcohol, linear
  • Genapol® LA 200 lauryl ethoxylate with 20 EO C12/14 alcohol, linear
  • Genapol® LA 2310 lauryl ethoxylate with 23 EO C12/14 alcohol, linear
  • Genapol® LA 250 lauryl ethoxylate with 25 EO C12/14 alcohol, linear


    b) cocoalkyl ethoxylates, more particularly
  • Genapol® C 050 C12/14/16 alkyl ethoxylate with 5 EO C12/14/16 alcohol, linear
  • Genapol® C 100 C12/14/16 alkyl ethoxylate with 10 EO C12/14/16 alcohol, linear
  • Genapol® C 200 C12/14/16 alkyl ethoxylate with 20 EO C12/14/16 alcohol, linear
  • Genapol® C 250 C12/14/16 alkyl ethoxylate with 25 EO C12/14/16 alcohol, linear
  • Genapol® U 100 C14/16/18 alkyl ethoxylate with 10 EO C14/16/18 alcohol, unsaturated
  • Genapol® U 200 C14/16/18 alkyl ethoxylate with 20 EO C14/16/18 alcohol, unsaturated
  • Genapol® GS 080 C12-20 alkyl ethoxylate with 8 EO C12-20 alcohol, linear


    c) oleyl ethoxylates, more particularly
  • Genapol® O 020 oleyl ethoxylate with 2 EO C16/18 alcohol, linear, unsaturated
  • Genapol® O 050 oleyl ethoxylate with 5 EO C16/18 alcohol, linear, unsaturated
  • Genapol® O 080 oleyl ethoxylate with 8 EO C16/18 alcohol, linear, unsaturated
  • Genapol® O 100 oleyl ethoxylate with 10 EO C16/18 alcohol, linear, unsaturated
  • Genapol® O 120 oleyl ethoxylate with 12 EO C16/18 alcohol, linear, unsaturated
  • Genapol® O 150 oleyl ethoxylate with 15 EO C16/18 alcohol, linear, unsaturated
  • Genapol® O 200 oleyl ethoxylate with 20 EO C16/18 alcohol, linear, unsaturated
  • Genapol® O 230 oleyl ethoxylate with 23 EO C16/18 alcohol, linear, unsaturated
  • Genapol® O 250 oleyl ethoxylate with 25 EO C16/18 alcohol, linear, unsaturated
  • Genapol® O 300 oleyl ethoxylate with 30 EO C16/18 alcohol, linear, unsaturated


    d) tallowalkyl ethoxylates, more particularly
  • Genapol® T 080 tallowalkyl ethoxylate with 8 EO C16/18 alcohol, linear, unsaturated
  • Genapol® T 110 tallowalkyl ethoxylate with 11 EO C16/18 alcohol, linear, unsaturated
  • Genapol® T 150 tallowalkyl ethoxylate with 15 EO C16/18 alcohol, linear, unsaturated
  • Genapol® T 200 tallowalkyl ethoxylate with 20 EO C16/18 alcohol, linear, unsaturated
  • Genapol® T 250 tallowalkyl ethoxylate with 25 EO C16/18 alcohol, linear, unsaturated
  • Genapol® T 500 tallowalkyl ethoxylate with 50 EO C16/18 alcohol, linear, unsaturated
  • Genapol® T 800 tallowalkyl ethoxylate with 80 EO C16/18 alcohol, linear, unsaturated
  • e) stearyl alcohol ethoxylates, more particularly
  • Genapol® HS 020 stearyl alcohol with 2 EO C16/18 alcohol, linear, saturated
  • Genapol® HS 200 stearyl alcohol with 20 EO C16/18 alcohol, linear, saturated
  • f) C11 alkyl ethoxylates, more particularly
  • Emulsogen® EPN 118 C11 alkyl ethoxylate with 11 EO C11 alcohol, linear, little branching
  • Emulsogen® EPN 287 C11 alkyl ethoxylate with 28 EO C11 alcohol, linear, little branching
  • Emulsogen® EPN 407 C11 alkyl ethoxylate with 40 EO C11 alcohol, linear, little branching
  • Emulsogen® LCN 050 C11 alkyl ethoxylate with 5 EO C11 alcohol, branched
  • Emulsogen® LCN 070 C11 alkyl ethoxylate with 7 EO C11 alcohol, branched
  • Emulsogen® LCN 088 C11 alkyl ethoxylate with 8 EO C11 alcohol, branched
  • Emulsogen® LCN 118 C11 alkyl ethoxylate with 11 EO C11 alcohol, branched
  • Emulsogen® LCN 158 C11 alkyl ethoxylate with 15 EO C11 alcohol, branched
  • Emulsogen® LCN 217 C11 alkyl ethoxylate with 21 EO C11 alcohol, branched
  • Emulsogen® LCN 287 C11 alkyl ethoxylate with 28 EO C11 alcohol, branched
  • Emulsogen® LCN 407 C11 alkyl ethoxylate with 40 EO C11 alcohol, branched
  • Emulsogen® LCN 506 C11 alkyl ethoxylate with 50 EO C11 alcohol, branched
  • Genapol® UD 030 C11 alkyl ethoxylate with 3 EO C11 alcohol, linear, little branching
  • Genapol® UD 050 C11 alkyl ethoxylate with 5 EO C11 alcohol, linear, little branching
  • Genapol® UD 079 C11 alkyl ethoxylate with 7 EO C11 alcohol, linear, little branching
  • Genapol® UD 080 C11 alkyl ethoxylate with 8 EO C11 alcohol, linear, little branching
  • Genapol® UD 088 C11 alkyl ethoxylate with 8 EO C11 alcohol, linear, little branching
  • Genapol® UD 110 C11 alkyl ethoxylate with 11 EO C11 alcohol, linear, little branching
  • g) isotridecyl ethoxylates, more particularly
  • Genapol® X 020 isotridecyl ethoxylate with 2 EO C13 alcohol, branched
  • Genapol® X 050 isotridecyl ethoxylate with 5 EO C13 alcohol, branched
  • Genapol® X 060 isotridecyl ethoxylate with 6 EO C13 alcohol, branched
  • Genapol® X 065 isotridecyl ethoxylate with 6.5 EO C13 alcohol, branched
  • Genapol® X 080 isotridecyl ethoxylate with 8 EO C13 alcohol, branched
  • Genapol® X 089 isotridecyl ethoxylate with 8 EO C13 alcohol, branched
  • Genapol® X 090 isotridecyl ethoxylate with 9 EO C13 alcohol, branched
  • Genapol® X 100 isotridecyl ethoxylate with 10 EO C13 alcohol, branched
  • Genapol® X 150 isotridecyl ethoxylate with 15 EO C13 alcohol, branched
  • Genapol® X 158 isotridecyl ethoxylate with 15 EO C13 alcohol, branched
  • Genapol® X 307 isotridecyl ethoxylate with 30 EO C13 alcohol, branched
  • Genapol® X 407 isotridecyl ethoxylate with 40 EO C13 alcohol, branched
  • Genapol® X 1003 isotridecyl ethoxylate with 100 EO C13 alcohol, branched
  • Genapol® X 1005 isotridecyl ethoxylate with 100 EO C13 alcohol, branched
  • Genapol® 1879 isotridecyl ethoxylate with 15 EO C13 alcohol, branched
  • Genapol® 3214 isotridecyl ethoxylate with 25 EO C13 alcohol, branched


    h) isodecyl ethoxylates, more particularly
  • Genapol® ID 030 isodecyl ethoxylate with 3 EO C10 alcohol, branched
  • Genapol® ID 060 isodecyl ethoxylate with 6 EO C10 alcohol, branched
  • Genapol® ID 070 isodecyl ethoxylate with 7 EO C10 alcohol, branched
  • Genapol® EP 1022 isodecyl ethoxylate with 2 EO, 2PO C10 alcohol, branched


    i) oxo-process alcohol ethoxylates, more particularly
  • Genapol® OX 030 C12/15 alkyl ethoxylate with 3 EO C12/15 alcohol, little branching
  • Genapol® OX 050 C12/15 alkyl ethoxylate with 5 EO C12/15 alcohol, little branching
  • Genapol® OX 070 C12/15 alkyl ethoxylate with 7 EO C12/15 alcohol, little branching
  • Genapol® OX 080 C12/15 alkyl ethoxylate with 8 EO C12/15 alcohol, little branching
  • Genapol® OX 100 C12/15 alkyl ethoxylate with 10 EO C12/15 alcohol, little branching
  • Genapol® OX 109 C12/15 alkyl ethoxylate with 10 EO C12/15 alcohol, little branching
  • Genapol® OA 030 C14/15 oxo-process alcohol with 3 EO C14/15 oxo-process alcohol
  • Genapol® OA 3070 C14/15 oxo alcohol, 3EO, 7PO C14/15 oxo-process alcohol
  • Genapol® OA 040 C14/15 oxo-process alcohol with 4 EO C14/15 oxo-process alcohol
  • Genapol® OA 050 C14/15 oxo-process alcohol with 5 EO C14/15 oxo-process alcohol
  • Genapol® OA 070 C14/15 oxo-process alcohol with 7 EO C14/15 oxo-process alcohol
  • Genapol® OA 080 C14/15 oxo-process alcohol with 8 EO C14/15 oxo-process alcohol
  • Hostacerin® T3 cetyl alcohol with 3 EO C16 alcohol, linear, saturated
  • Hostacerin® CS 200 cetyl alcohol with 20 EO C16 alcohol, linear, saturated
  • Emulsogen® HCO 040 PEG-40 castor oil, hydrogenated C16/18 hydroxyalcohol, linear, saturated
  • Emulsogen® HCO 060 PEG-60 castor oil, hydrogenated C16/18 hydroxyalcohol, linear, saturated and


    j) alcohol alkoxylates, EO/PO, more particularly
  • Genapol® EO 0244 C10/12 alcohol with 4 EO and 4 PO C10/12 alcohol
  • Genapol® EP 1182 C11 oxo-process alcohol with 8 EO and 2 PO C11 oxo-process alcohol
  • Genapol® EP 2464 C12/14 alcohol having 6 EO and 4 PO C12/14 alcohol
  • Genapol® EP 2544 C12/15 oxo-process alcohol with 4 EO and 4 PO C12/15 oxo-process alcohol
  • Genapol® EP 2564 C12/15 oxo-process alcohol with 6 EO and 4 PO C12/15 oxo-process alcohol
  • Genapol® EP 2584 C12/15 oxo-process alcohol with 8 EO and 4 PO C12/15 oxo-process alcohol
  • Genapol® EP2525 C12/15 oxo-process alcohol with 2 EO and 5 PO C12/15 oxo-process alcohol
  • Genapol® EP 2552 C12/15 oxo-process alcohol with 5 EO and 2 PO C12/15 oxo-process alcohol


    and also


    (C10-C18) fatty alcohol polyglycol ethers having 8 EO units,


    iso-(C16-C18) fatty alcohol polyglycol ethers having 25 EO units,


    (C18-C22) fatty alcohol polyglycol ethers having 25 EO units,


    octyl alcohol ethers having 3 EO units,


    octyl alcohol ethers having 10 EO units and 3 PO units,


    behenyl alcohol ethers having 10 EO units,


    behenyl alcohol ether having 20 EO units, and


    behenyl alcohol ether having 25 EO units


    are preferred.


In the list above (subgroups a) to j)), relating to preferred acrylic and/or methacrylic esters of alcohol polyglycol ethers and of alkoxylated alcohols in accordance with formula (Ib), the trade names of the alkoxylated alcohols are given on the left, the chemical identification of the alkoxylated alcohols in the middle, and a definition of the alcohols on the right. The products represent commercial products from Clariant.


In the context of the present invention, the abbreviation “EO” denotes ethylene oxide C2H4O—, and “PO” propylene oxide C3H6O—.


In one particularly preferred embodiment of the invention, of the compounds of the formula (Ib), preference is given to those selected from lauryl methacrylate ethoxylated with 7 EO units; talyl methacrylate ethoxylated with 8 EO units; talyl methacrylate ethoxylated with 25 EO units; and behenyl methacrylate ethoxylated with 25 EO units.


For the purposes of the present invention, the designation “talyl” is used synonymously for the designation “tallowalkyl”.


In a further preferred embodiment of the invention, among the compounds of the formula (Ic), preference is given to those in which R2 in an alkyl radical. These compounds are α-olefins. In one particularly preferred embodiment of the invention, R2 in these compounds is a linear alkyl radical.


In a further particularly preferred embodiment of the invention, among the compounds of the formula (Ic), preference is given to those selected from 1-hexene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene, C20 α-olefin, C22 α-olefin, C24 α-olefin, C26 α-olefin, C28 α-olefin, C30 α-olefin, and also mixtures of α-olefines, including preferably C14-16 α-olefins, C20-24 α-olefins, C24-28 α-olefins, C26-28 α-olefins, and isomerized α-olefins, including preferably 4-methyl-1-pentene, isomerized C16 α-olefins, isomerized C18 α-olefins, and isomerized C16-18 α-olefins, such as, for example, isomerized C16-18 α-olefins in a C16:C18 weight ratio of 65:35.


In another particularly preferred embodiment of the invention, of the compounds of the formula (Ic), preference is given to those selected from α-olefins having 10 to 60 carbon atoms, i.e., R2 in these compounds of the formula (Ic) is a saturated alkyl radical having 8 to 58 carbon atoms, and the structural units originating from these compounds of the formula (Ic) are those of the formula —CH2CHR2—, in which R2 is a saturated alkyl radical having 8 to 58 carbon atoms.


In one especially preferred embodiment of the invention among the compounds of the formula (Ic), preference is given to those in which R2 is an alkyl radical having 12 to 40 carbon atoms. In an embodiment of the invention which is preferred among these in turn, from among the compounds of the formula (Ic), preference in turn is given to those in which R2 is an alkyl radical having 12 to 30 carbon atoms.


In an embodiment of the invention which is preferred in turn among these, from among the compounds of the formula (Ic), preference in turn is given to those in which R2 is an alkyl radical having 24 or 26 carbon atoms or stands for mixtures of alkyl radicals having 24 and 26 carbon atoms. In a further embodiment of the invention that is preferred in turn among these, from among the compounds of the formula (Ic), preference is given in turn to those in which R2 is an alkyl radical having 28 carbon atoms.


In an extraordinarily preferred embodiment of the invention, from among the compounds of the formula (Ic), preference is given to those selected from C26 α-olefin, C28 α-olefin, C26-C28 α-olefin, and C30 α-olefin.


Extraordinarily preferred are the compounds of the formula (Ia) selected from hexyl acrylate, hexyl methacrylate, decyl acrylate, decyl methacrylate, lauryl acrylate, lauryl methacrylate, hexadecyl acrylate, hexadecyl methacrylate, stearyl acrylate, stearyl methacrylate, isostearyl acrylate, isostearyl methacrylate, octyldodecyl acrylate, octyldodecyl methacrylate, behenyl acrylate and behenyl methacrylate,


the compounds of the formula (Ib) selected from acrylic ester of lauryl alcohol with 7 EO units, methacrylic ester of lauryl alcohol with 7 EO units, acrylic ester of talyl alcohol with 8 EO units, methacrylic ester of talyl alcohol with 8 EO units, acrylic ester of talyl alcohol with 25 EO units, methacrylic ester of talyl alcohol with 25 EO units, acrylic ester of behenyl alcohol with 25 EO units and methacrylic ester of behenyl alcohol with 25 EO units, and


the compounds of the formula (Ic) selected from C26 α-olefin, C28 α-olefin, C26-C28 α-olefin, and C30 α-olefin.


Preferred among these in turn are the compounds of the formula (Ia) selected from lauryl acrylate, lauryl methacrylate, hexadecyl acrylate, stearyl acrylate, isostearyl acrylate, octyldodecyl acrylate, and behenyl acrylate,


the compounds of the formula (Ib) selected from methacrylic ester of lauryl alcohol with 7 EO units, methacrylic ester of talyl alcohol with 8 EO units, methacrylic ester of talyl alcohol with 25 EO units, and methacrylic ester of behenyl alcohol with 25 EO units, and


the compounds of the formula (Ic) selected from C26 α-olefin, C28 α-olefin, C26-C28 α-olefin, and C30 α-olefin.


In a further preferred embodiment of the invention, R2 in the compounds of the formula (I) or in the formulae (Ia), (Ib), and (Ic) is a linear or branched saturated alkyl radical having 6 to 200, preferably having 8 to 58, more preferably having 12 to 40, and with particular preference having 12 to 30 carbon atoms. In a particularly preferred embodiment of the invention, R2 in the compounds of the formulae (I), (Ia), (Ib), and (Ic) is a linear saturated alkyl radical having 6 to 200, preferably having 8 to 58, more preferably having 12 to 40, and with particular preference having 12 to 30 carbon atoms.


The structural units of component b) preferably originate from substances selected from


b1) polymerizable quaternary ammonium compounds of the following structural formula (II)





X+NR7R8R9R10  (II)


in which


X is a negatively charged counterion,


R7 is vinyl radical, allyl radical or a radical of the following structural formula (III)




embedded image


in which

  • R11 is hydrogen or methyl,
  • Z is O, NH, NCH3 or S,
  • n is an integer from 1 to 50,
  • R8 is a linear or branched alkyl radical having 1 to 50 carbon atoms or is a radical R7,
  • R9 is a linear or branched alkyl radical having 1 to 50 carbon atoms or is a radical R7, and
  • R10 is a linear or branched alkyl radical having 1 to 50 carbon atoms,


    and


    b2) polymerizable cyclic quaternary ammonium compounds with the following structural formula (IV)




embedded image


in which


o and p each independently of one another are an integer from 0 to 5,


A is C, CH, N or P, and

X is a negatively charged counterion.


In the compounds of the formula (IV), where o is zero or even-numbered, A is C and p is odd-numbered.


In the compounds of the formula (IV), where o is odd-numbered, p may be zero, even-numbered or odd-numbered. If p is zero or even-numbered, A is C. If, however, p is odd-numbered, A may take on the definition CH, N or P.


In the compounds of the formula (IV), where p is zero or is even-numbered, A is C and o is odd-numbered.


In the compounds of the formula (IV), where p is odd-numbered, o may be zero, even-numbered or odd-numbered. If o is zero or even-numbered, A is C. If, however, o is odd-numbered, A may take on the definition CH, N or P.


Preferred negatively charged counterions Xin formula (II) and (IV) are chloride, bromide, iodide, ½ SO42−, and methosulfate.


In one particularly preferred embodiment of the invention, the structural units of component b) originate from polymerizable quaternary ammonium compounds selected from diallyldimethylammonium chloride (DADMAC), [2-(methacryloyloxy)ethyl]trimethylammonium chloride (MAOETAC), [2-(acryloyloxy)ethyl]trimethylammonium chloride (AOETAC), [2-methacrylamidoethyl]trimethylammonium chloride, [2-(acrylamido)ethyl]trimethylammonium chloride, [3-methacrylamidopropyl]trimethylammonium chloride (MAPTAC), [3-acrylamidopropyl]trimethylammonium chloride (APTAC), N-methyl-2-vinylpyridinium chloride, N-methyl-4-vinylpyridinium chloride, and N-methyl-3-vinylimidazolinium chloride.


In another particularly preferred embodiment of the invention, the structural units of component b) originate from polymerizable quaternary ammonium compounds of the above-stated structural formula (II). Preferred among these structural units of component b), in turn, are those originating from polymerizable quaternary ammonium compounds of the structural formula (II)





X+NR7R8R9R10  (II)


in which


Xis a negatively charged counterion,


R7 is vinyl radical, allyl radical or a radical of the following structural formula (III)




embedded image


in which

  • R11 is hydrogen or methyl,
  • Z is O, NH, NCH3 or S,
  • n is an integer from 1 to 50,
  • R8 is a linear or branched alkyl radical having 2 to 50, preferably 2 to 25, and more preferably 4 to 8 carbon atoms, or is a radical R7,
  • R9 is a linear or branched alkyl radical having 1 to 50, preferably 2 to 25, and more preferably 4 to 8 carbon atoms, or is a radical R7, and
  • R10 is a linear or branched alkyl radical having 1 to 50, preferably 2 to 25, and more preferably 4 to 8 carbon atoms.


In one especially preferred embodiment of the invention, the structural units of component b) originate from polymerizable quaternary ammonium compounds selected from diallyldimethylammonium chloride (DADMAC), [2-(methacryloyloxy)-ethyl]trimethylammonium chloride (MAOETAC), [2-(acryloyloxy)ethyl]-trimethylammonium chloride (AOETAC), [2-methacrylamidoethyl]trimethylammonium chloride, [2-(acrylamido)ethyl]trimethylammonium chloride, and [3-methacrylamidopropyl]trimethylammonium chloride (MAPTAC) and [3-acryl-amidopropyl]trimethylammonium chloride (APTAC).


In an extraordinarily preferred embodiment of the invention, the polymers of the invention comprise structural units of component b) that originate from [2-(acryloyl-oxy)ethyl]trimethylammonium chloride. These polymers are preferred in oil gels, in relation to clarity and transparency, over analogous polymers comprising structural units originating from [3-methacrylamidopropyl]trimethylammonium chloride.


In a further preferred embodiment of the invention, the amount used of substances selected from monomers having more than one polymerizable group, which may have a crosslinking action (crosslinkers), for preparing the copolymers of the invention, based on the total mass of the monomers to be polymerized in the polymerization, is 0% to 20.0%, preferably 0% to 10.0%, and more preferably 0% to 5.0% by weight.


A “polymerizable group” in this context means a polymerizable double bond.


In a further preferred embodiment of the invention, the copolymers of the invention comprise one or more structural units of component c) originating from substances selected from monomers having more than one polymerizable group, which may have a crosslinking action, in an amount of 0% to 20.0%, preferably 0% to 10.0%, and more preferably 0% to 5.0% by weight, based on the total mass of the copolymers of the invention.


In a particularly preferred embodiment of the invention, the copolymers of the invention comprise no structural units of component c) which originate from substances selected from monomers having more than one polymerizable group, which may have a crosslinking action.


In a further particularly preferred embodiment of the invention, the copolymers of the invention comprise one or more structural units of component c) that originate from substances selected from monomers having more than one polymerizable group, which may have a crosslinking action.


The crosslinking structural units of component c) originate preferably from substances selected from divinylbenzene, methylenebisacrylamide (MBA), triallylamine, triallyl cyanurate, ethanediol diacrylate, ethanediol dimethacrylate (EDDMA), butanediol diacrylate, butanediol dimethacrylate (BDDMA), hexanediol diacrylate, hexanediol dimethacrylate (HDDMA), dodecanediol diacrylate, dodecanediol dimethacrylate (DDDMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane trimethacrylate (TMPTMA), glycerol diacrylate, glycerol dimethacrylate, tetraethylene glycol diacrylate, tetraethylene glycol dimethacrylate, polyethylene glycol diacrylate with molar masses between 400 and 800 g/mol, polyethylene glycol dimethacrylate with molar masses between 400 and 800 g/mol, allyl acrylate, methacrylate or ethacrylate, preferably allyl acrylate or methacrylate, and more particularly allyl methacrylate (AMA), dipropylene glycol diallyl ether, polyglycol diallyl ether, hydroquinone diallyl ether, trimethylolpropane diallyl ether, trimethylolpropane triallyl ether, tetraallyloxyethane, triethylene glycol divinyl ether, and other allyl ethers or vinyl ethers of polyfunctional alcohols, and also from mixtures of the aforesaid substances, such as, for example, from mixtures of hexanediol dimethacrylate and trimethylolpropane trimethacrylate.


Preferred among these in turn are the crosslinking structural units of component c) that originate from substances selected from methylenebisacrylamide (MBA), triallylamine, triallyl cyanurate, ethanediol dimethacrylate (EDDMA), butanediol dimethacrylate (BDDMA), hexanediol dimethacrylate (HDDMA), dodecanediol dimethacrylate (DDDMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane trimethacrylate (TMPTMA), glycerol diacrylate, polyethylene glycol diacrylate having molar masses between 400 and 800 g/mol, allyl methacrylate (AMA), and also from mixtures of the aforesaid substances, such as, for example, from mixtures of hexanediol dimethacrylate and trimethylolpropane trimethacrylate.


With particular preference the crosslinking structural units of component c) originate from hexanediol dimethacrylate, trimethylolpropane triacrylate, and mixtures of these substances.


In one especially preferred embodiment of the invention, the amount used of the crosslinker for preparing the copolymers of the invention, based on the total mass of the monomers to be polymerized in the polymerization, is 0.1% to 20.0%, preferably 0.5% to 10.0%, and are preferably 1.0% to 5.0% by weight.


Where the copolymers of the invention comprise one or more structural units of component c) that originate from substances selected from monomers having more than one polymerizable group, which may have a crosslinking action, they comprise, in a further, especially preferred embodiment of the invention, 0.1% to 20.0%, preferably 0.5% to 10.0%, and more preferably 1.0% to 5.0% by weight of these structural units, based on the total mass of the copolymers of the invention.


In a further preferred embodiment of the invention, the copolymers comprise one or more structural units of component c) that originate from substances selected from acrylic or methacrylic esters of alkyl alcohols having 1 to 5 carbon atoms, which optionally may also have been alkoxylated with 1 to 25 alkylene oxide units, such as, for example, with ethylene oxide units, with propylene oxide units or with mixtures of ethylene oxide units and propylene oxide units, preference among these compounds being given to butyl acrylate, and hydroxyethyl methacrylate (HEMA), (meth)acrylic esters of polyethylene glycols, polypropylene glycols, and polyethylene-polypropylene glycols, N-vinylpyrrolidone, and also ethene, propene, 1-butene, and 1-pentene. Among the stated compounds, butyl acrylate is preferred. Where the copolymers of the invention comprise one or more of the structural units just stated, these units are present preferably in an amount of 0.1% to 10.0% by weight, based on the total mass of the copolymer, in the copolymers of the invention.


The copolymers of the invention may also, for example, be “grafted”, meaning that they have been applied to a support. The preparation of supported polymers is general knowledge. Where a support is used, the amount of the support, based on the mass of the supported copolymer, is preferably from 0.1% to 10.0% by weight and more preferably from 2.0% to 6.0% by weight. Where a support is used, it is preferably polyvinylpyrrolidone, polyethylene glycol, polypropylene glycol or polyethylene/polypropylene glycol, and more preferably polyvinylpyrrolidone.


In the copolymers of the invention, preferably, the amount of structural units of component a) is from 60.0% to 99.5% by weight, the amount of structural units of component b) is from 0.5% to 20.0% by weight, and the amount of structural units of component c) is from 0% to 20.0% by weight.


In the copolymers of the invention, more preferably, the amount of structural units of component a) is from 75.0% to 98.5% by weight, the amount of structural units of component b) is from 0.6% to 12.5% by weight, and the amount of structural units of component c) is from 0% to 12.5% by weight.


In the copolymers of the invention, especially preferably, the amount of structural units of component a) is from 80.0% to 98.0% by weight, the amount of structural units of component b) is from 0.7% to 11.0% by weight, and the amount of structural units of component c) is from 0% to 11.0% by weight.


The ratio of the structural units originating from the compounds of the formulae (Ia), (Ib) and (Ic) within component a) of the copolymers of the invention is preferably as follows: 50.0% to 100.0% by weight of structural units originating from the compounds of the formula (Ia), 0% to 40.0% by weight of structural units originating from the compounds of the formula (Ib), and 0% to 20.0% by weight of structural units originating from the compounds of the formula (Ic). The weight ratio of structural units originating from the compound of the formula (Ia): structural units originating from the compounds of the formula (Ib): structural units originating from the compounds of the formula (Ic) in the copolymers of the invention is preferably 1.0:0 to 0.8:0 to 0.4.


In a further preferred embodiment of the invention, the copolymers of the invention comprise no structural units originating from anionic polymerizable substances.


In a further preferred embodiment of the invention, the copolymers of the invention consist of the structural units stated under components a) and b).


In a further preferred embodiment of the invention, the copolymers of the invention consist of the structural units stated under components a), b), and c). Preference in turn among these copolymers is given to those in which the structural units of component c) are selected from crosslinking structural units.


In one particularly preferred embodiment of the invention, the copolymers of the invention comprise from 95.0% to 99.0% by weight of one or more structural units originating from the compounds of the formula (Ia) of component a), preferably selected from stearyl acrylate and lauryl methacrylate, and from 0.1% to 5.0% by weight of one or more structural units originating from the compounds of component b), preferably [2-(acryloyloxy)ethyl]trimethylammonium chloride (AOETAC) (copolymers A hereinbelow).


Among the copolymers A, the copolymer consisting of 97.0% by weight of structural units originating from stearyl acrylate and 3.0% by weight of structural units originating from [2-(acryloyloxy) ethyl]trimethylammonium chloride (AOETAC) is preferred (e.g., copolymers #1, 273 and 278).


Among the copolymers A, furthermore, the copolymer consisting of 82.0% by weight of structural units originating from stearyl acrylate, 15.0% by weight of structural units originating from lauryl methacrylate, and 3.0% by weight of structural units originating from [2-(acryloyloxy)ethyl]trimethylammonium chloride (AOETAC) is preferred (e.g., copolymer #277).


In another particularly preferred embodiment of the invention, the copolymers of the invention comprise from 90.0% to 98.0% by weight of one or more structural units originating from compounds of the formula (I) of component a), preferably selected from stearyl acrylate, isostearyl acrylate, behenyl methacrylate ethoxylated with 25 EO units (B250MA) and C26-C28 α-olefin, from 1.5% to 5.0% by weight of one or more structural units originating from compounds of component b), preferably selected from [2-(acryloyloxy)ethyl]trimethylammonium chloride (AOETAC) and [3-methacrylamidopropyl]trimethylammonium chloride (MAPTAC) and from 0.5% to 6.0% by weight of one or more structural units originating from compounds of component c), preferably selected from crosslinkers, more particularly selected from hexanediol dimethacrylate (HDDMA) and trimethylolpropane triacrylate (TMPTA) (copolymers B hereinbelow).


Among the copolymers B, preference is given to those comprising, as structural units originating from compounds of the formula (I) of component (a), structural units originating from compounds of the formulae (Ia) and (Ib), and preference in turn is given to these in which the weight ratio of structural units originating from the compound or compounds of the formula (Ia): structural units originating from the compound or compounds of the formula (Ib)=1.0:0.1 to 1.0 (copolymers B1 hereinbelow).


Among the copolymers B1, the copolymers consisting of 56.4% by weight of structural units originating from stearyl acrylate, 39.6% by weight of structural units originating from behenyl methacrylate ethoxylated with 25 EO units (B250MA), 3.0% by weight of structural units originating from [2-(acryloyloxy)-ethyl]trimethylammonium chloride (AOETAC), and 1.0% by weight of structural units originating from hexanediol dimethacrylate (HDDMA) are preferred (e.g., copolymer #30).


Among the copolymers B1, furthermore, those copolymers consisting of 74.6% by weight of structural units originating from stearyl acrylate, 9.5% by weight of structural units originating from isostearyl acrylate, 8.6% by weight of structural units originating from behenyl methacrylate ethoxylated with 25 EO units (B250MA), 2.5% by weight of structural units originating from [2-(acryloyloxy)-ethyl]trimethylammonium chloride (AOETAC), and 4.8% by weight of structural units originating from hexanediol dimethacrylate (HDDMA) are preferred (e.g., copolymer #40).


Among the copolymers B, furthermore, preference is given to those which comprise structural units originating from compounds of the formulae (Ia), (Ib), and (Ic), and preference in turn to these in which the weight ratio of structural units originating from the compound or compounds of the formula (Ia): structural units originating from the compound or compounds of the formula (Ib): structural units originating from the compound or compounds of the formula (Ic)=10.0 to 20.0:1.0 to 3.0:1.0 (copolymers B2 hereinbelow).


Among the copolymers B2, the copolymers consisting of 78.2% by weight of structural units originating from stearyl acrylate, 9.0% by weight of structural units originating from behenyl methacrylate ethoxylated with 25 EO units (B250MA), 4.7% by weight of structural units originating from C26-C28 α-olefin, 3.6% by weight of structural units originating from a mixture of [2-(acryloyloxy)-ethyl]trimethylammonium chloride (AOETAC) and [3-methacrylamidopropyl]trimethylammonium chloride (MAPTAC) and 4.7% by weight of structural units originating from a mixture of hexanediol dimethacrylate (HDDMA) and trimethylolpropane triacrylate (TMPTA) are preferred (e.g., copolymer #111).


Among the copolymers B2, furthermore, the copolymers consisting of 78.2% by weight of structural units originating from stearyl acrylate, 9.0% by weight of structural units originating from behenyl methacrylate ethoxylated with 25 EO units (B250MA), 4.7% by weight of structural units originating from C26-C28 α-olefin, 3.6% by weight of structural units originating from [2-(acryloyloxy)-ethyl]trimethylammonium chloride (AOETAC), and 4.7% by weight of structural units originating from a mixture of hexanediol dimethacrylate (HDDMA) and trimethylolpropane triacrylate (TMPTA) are preferred (e.g., copolymer #60).


Among the copolymers B, furthermore, preference is given to those which comprise structural units originating from compounds of the formulae (Ia), (Ib), and (Ic), and preference in turn to these in which the weight ratio of structural units originating from the compound or compounds of the formula (Ia): structural units originating from the compound or compounds of the formula (Ib): structural units originating from the compound or compounds of the formula (Ic)=50.0 to 60.0:5.0 to 7.0:1.0 (copolymers B3 hereinbelow).


Among the copolymers B3, the copolymers consisting of 84.1% by weight of structural units originating from stearyl acrylate, 9.4% by weight of structural units originating from behenyl methacrylate ethoxylated with 25 EO units (B250MA), 1.6% by weight of structural units originating from C26-C28 α-olefin, 1.6% by weight of structural units originating from [2-(acryloyloxy)ethyl]trimethylammonium chloride (AOETAC), and 3.3% by weight of structural units originating from trimethylolpropane triacrylate (TMPTA) are preferred (e.g., copolymer #52).


The distribution of the various structural units in the copolymers of the invention may be random, blocklike, alternating or gradientlike.


The copolymers of the invention preferably possess a molecular weight of 103 to 109 g/mol, more preferably from 104 to 107 g/mol, and with particular preference from 5*105 to 5*106 g/mol.


The copolymers of the invention are prepared by radical polymerization reaction of the polymerizable substances from which the repeating structural units of components a), b), and optionally c), and also any further structural units, originate.


The invention further provides a process for preparing a copolymer of the invention, which comprises polymerizing the monomers in a radical polymerization reaction.


Serving as the polymerization medium may be all solvents which behave very largely inertly in respect of radical polymerization reactions and which allow the formulation of high molecular weights. Finding use preferably are organic solvents, more particularly lower, tertiary alcohols or hydrocarbons having 3 to 30 carbon atoms. One particularly preferred embodiment uses tert-butanol or toluene as reactive medium. Mixtures of two or more representatives from the potential solvents described are of course likewise in accordance with the invention. This also includes emulsions of mutually immiscible solvents (e.g., water/hydrocarbons). In principle, all kinds of reaction regime are suitable that lead to the polymer structures of the invention (solution polymerization, emulsion processes, precipitation processes, high-pressure processes, suspension processes, bulk polymerization, gel polymerization, and so on).


The polymerization reaction takes place preferably in the temperature range between 0 and 150° C., more preferably between 10 and 110° C., either at atmospheric pressure or under increased or reduced pressure. The polymerization may optionally also be performed under an inert gas atmosphere, preferably under nitrogen or argon.


To initiate the polymerization it is possible to use high-energy electromagnetic rays, mechanical energy, or the customary chemical polymerization initiators, such as organic peroxides, examples being benzoyl peroxide, tert.-butyl hydroperoxide, methyl ethyl ketone peroxide, cumene hydroperoxide, dilauroyl peroxide, or azo initiators, such as azodiisobutyronitrile (AIBN), azomethylbutyronitrile (AMBN), or dimethyl 2,2″-azobis(2-methylpropionate), for example.


In the course of the preparation of the copolymers of the invention it is also possible to use substances which regulate the polymerization or the chain length of the copolymers of the invention, such as methallyl sulfonate, isopropanol or dodecyl mercaptan, for example. The use of such substances in polymerization reactions is general knowledge. Where an initiator for the polymerization reaction is used, corresponding comments apply.


In the preparation of the copolymers of the invention it is also possible to use substances which control the radical polymerization by reversibly deactivating the very reactive chain ends. Where controlled radical polymerization is employed, it is carried out preferably with organic halides/transition metal complex compounds, preferably secondary alkyl halides in conjunction with copper (I) complexes, as ATRP (Atom Transfer Radical Polymerization) or through the use of linear or cyclic nitroxides, preferably in the form of what is called the TEMPO method.


One preferred embodiment of the process of the invention is characterized in that the radical polymerization takes place in an organic solvent, preferably in tert-butanol or toluene, more preferably in tert-butanol.


A further preferred embodiment of the process of the invention is characterized in that the copolymers of the invention are isolated by distillative removal of the solvent and by subsequent vacuum drying.


A further preferred embodiment of the invention is characterized in that the copolymers of the invention are isolated by precipitation in a nonsolvent, i.e., a solvent in which the copolymer of the invention is insoluble, preferably in water, and by subsequent filtration and vacuum drying.


The above-described copolymers are odor-neutral, are white to beige, and have excellent processing properties; they are kind to the skin, highly compatible with all commonplace ingredients of cosmetic formulations, and therefore suitable for preparing cosmetic, dermatological, and pharmaceutical formulations.


The invention accordingly further provides a cosmetic, pharmaceutical or dermatological formulation, preferably a cosmetic formulation, characterized in that it comprises one or more copolymers of the invention.


In one preferred embodiment of the invention, the cosmetic formulations of the invention are skin cleansing products, skincare products or hair treatment products.


The copolymers of the invention are notable for excellent oil-binding capacity and are outstandingly suitable for thickening oil-based formulations.


The invention therefore further provides for the use of one or more of the copolymers of the invention for thickening oils. These oils are preferably cosmetic oils, i.e., oils which may find use in cosmetic formulations.


The oils may advantageously be selected from the groups of triglycerides, natural and synthetic fatty substances, preferably esters of fatty acids with alcohols of low C number, such as with methanol, isopropanol, propylene glycol or glycerol, for example, or esters of fatty alcohols with alkanoic acids of low C number, or with fatty acids, or from the group of the alkylbenzoates, and also natural or synthetic hydrocarbon oils.


Substances contemplated include triglycerides of linear or branched, saturated or unsaturated, optionally hydroxylated, C8-C30 fatty acids, especially vegetable oils, such as sunflower oil, corn oil, soybean oil, rice oil, jojoba oil, babassu oil, pumpkin oil, grapeseed oil, sesame oil, walnut oil, apricot oil, orange oil, wheatgerm oil, peach kernel oil, macadamia oil, avocado oil, sweet almond oil, lady's smock oil, castor oil, olive oil, peanut oil, rapeseed oil, and coconut oil, and also synthetic triglyceride oils, examples being the commercial product Myritol® 318 and also the commercial product Velsan® CCT (caprylic/capric triglyceride, Clariant). Hydrogenated triglycerides are inventively preferred as well. It is also possible to use oils of animal origin, examples being beef tallow, perhydrosqualene, and lanolin.


A further class of preferred oily substances are the benzoic esters of linear or branched C8-22 alkanols, examples being the commercial products Finsolv® SB (isostearyl benzoate), Finsolv® TN (C12-C15 alkylbenzoate), and Finsolv® EB (ethylhexyl benzoate).


A further class of preferred oily substances are the dialkyl ethers having a total of 12 to 36 carbon atoms, more particularly with 12 to 24 carbon atoms, such as, for example, di-n-octyl ether (Cetiol® OE), di-n-nonyl ether, di-n-decyl ether, di-n-undecyl ether, di-n-dodecyl ether, n-hexyl n-octyl ether, n-octyl n-decyl ether, n-decyl n-undecyl ether, n-undecyl n-dodecyl ether, and n-hexyl n-undecyl ether, di-3-ethyldecyl ether, tert-butyl n-octyl ether, isopentyl n-octyl ether, and 2-methylpentyl n-octyl ether, and also di-tert-butyl ether and diisopentyl ether.


Also contemplated are branched saturated or unsaturated fatty alcohols having 6-30 carbon atoms, isostearyl alcohol, for example, and also Guerbet alcohols.


A further class of preferred oily substances are alkyl esters of hydroxycarboxylic acids. Preferred alkyl esters of hydroxycarboxylic acids are full esters of glycolic acid, lactic acid, malic acid, tartaric acid or citric acid. Further hydroxycarboxylic esters suitable in principle are esters of β-hydroxypropionic acid, of tartronic acid, of D-gluconic acid, saccharic acid, mucic acid or glucuronic acid. Suitability as the alcohol component of these esters is possessed by primary, linear or branched aliphatic alcohols having 8 to 22 carbon atoms. Particular preference in this context is given to the esters of C12-C15 fatty alcohols. Esters of this type are available commercially, as for example under the trade name Cosmacol® from EniChem, Augusta Industriale.


A further class of preferred oily substances are dicarboxylic esters of linear or branched C2-C10 alkanols, such as di-n-butyl adipate (Cetiol® B), di(2-ethylhexyl) adipate, and di(2-ethylhexyl) succinate, and also diol esters such as ethylene glycol dioleate, ethylene glycol diisotridecanoate, propylene glycol di(2-ethylhexanoate), propylene glycol diisostearate, propylene glycol dipelargonate, butanediol diisostearate, and neopentyl glycol dicaprylate, and also diisotridecyl azelaate.


Preferred oily substances are also symmetrical, unsymmetrical or cyclic esters of carbonic acid with fatty alcohols, glycerol carbonate or dicaprylyl carbonate (Cetiol® CC).


A further class of preferred oily substances are the esters of dimers of unsaturated C12-C22 fatty acids (dimer fatty acids) with monohydric linear, branched or cyclic C2-C18 alkanols or with polyhydric linear or branched C2-C6 alkanols.


A further class of preferred oily substances are hydrocarbon oils, examples being those having linear or branched, saturated or unsaturated C7-C40 carbon chains, such as, for example, petrolatum, dodecane, isododecane, cholesterol, lanolin, synthetic hydrocarbons such as polyolefins, especially polyisobutene, hydrogenated polyisobutene, polydecane, and also hexadecane, isohexadecane, paraffin oils, isoparaffin oils, examples being the commercial products of the Permethyl® series, squalane, squalene, and alicyclic hydrocarbons, such as the commercial product 1,3-di(2-ethylhexyl)cyclohexane (Cetiol® S), for example, ozokerite, and ceresin.


Silicone oils and silicone waxes are likewise contemplated, preferably dimethylpolysiloxanes and cyclomethicones, polydialkylsiloxanes R3SiO(R2SiO)xSiR3, where R is methyl or ethyl, more preferably methyl, and x is a number from 2 to 500, examples being the dimethicones available under the trade names VICASIL (General Electric Company), DOW CORNING 200, DOW CORNING 225, DOW CORNING 200 (Dow Corning Corporation), and also the dimethicones available as SilCare® Silicone 41M65, SilCare® Silicone 41M70, SilCare® Silicone 41M80 (Clariant), stearyldimethylpolysiloxane, C20-C24-alkyl-dimethylpolysiloxane, C24-C28-alkyl-dimethylpolysiloxane, and also the methicones available as SilCare® Silicone 41M40 and SilCare® Silicone 41M50 (Clariant), and additionally trimethylsiloxysilicates [(CH2)3SiO)1/2]x[SiO2]y, where x is a number from 1 to 500 and y is a number from 1 to 500, dimethiconols R3SiO[R2SiO]xSiR2OH and HOR2SiO[R2SiO]xSiR2OH, where R is methyl or ethyl and x is a number up to 500, polyalkylarylsiloxanes, examples being the polymethylphenylsiloxanes available under the commercial designations SF 1075 METHYLPHENYL FLUID (General Electric Company) and 556 COSMETIC GRADE PHENYL TRIMETHICONE FLUID (Dow Corning Corporation), polydiarylsiloxanes, silicone resins, cyclic silicones, and amino-, fatty acid-, alcohol-, polyether-, epoxy-, fluorine- and/or alkyl-modified silicone compounds, and also polyethersiloxane copolymers.


The copolymers of the invention can also be used advantageously for preparing oil gels. In a further preferred embodiment of the invention, therefore, the cosmetic, pharmaceutical or dermatological formulations of the invention are oil gels such as thickened baby oils, for example.


The oil gels of the invention comprise preferably 90.0% to 99.99% by weight, more preferably 94.0% to 99.9% by weight and with particular preference 97.0% to 99.5% by weight of one or more oils or oily substances, and preferably 0.01% to 10.0% by weight, more preferably 0.1% to 6.0% by weight, and with particular preference 0.5% to 3.0% by weight of one or more of the copolymers of the invention, in each case based on the overall oil gel. The oils or oily substances preferably present in the oil gels of the invention correspond to the above-identified preferred oils or oily substances.


Further advantageous are the outstanding conditioning properties of the copolymers of the invention with respect to keratinic fibers. They produce an excellent skin feel and are superior to the wax-containing formulations, which frequently exhibit a sticky and dull behavior. They enhance the shine of the hair, and also its easy combability.


The present invention accordingly further provides for the use of one or more of the copolymers of the invention for conditioning fibers, preferably keratinic fibers, more preferably in cosmetic formulations.


One particularly preferred embodiment of the invention sees the cosmetic formulations of the invention as hair treatment compositions. Preference here is given to hair treatment compositions, more particularly hair conditioning products such as cream washes and hair rinses, which are used for improving the shine and combability of the hair and for protecting it from heat. In an especially preferred embodiment of the invention, the hair treatment compositions of the invention, more particularly the hair treatment compositions just identified, comprise one or more copolymers of the invention and one or more further cationic surfactants such as cetrimonium chloride, behentrimonium chloride, stearamidopropyldimethylamine, behenamidopropyldimethylamine or quaternary ammonium compounds with an ester basis, and/or one or more silicones.


On account of their substantivity and low water-solubility, the copolymers of the invention are suitable for application as water resistance improvers. The invention accordingly further provides for the use of one or more of the polymers of the invention as water resistance improvers.


The copolymers of the invention are suitable, furthermore, for the surface treatment of pigments such as FeO, TiO2, and ZnO, for example. The invention accordingly further provides for the use of one or more of the polymers of the invention for surface treatment of pigments.


The copolymers of the invention are advantageously suitable, moreover, for enhancing the water resistance of sun protection formulations.


The invention accordingly further provides for the use of one or more of the copolymers of the invention for enhancing the water resistance of sun protection formulations.


Furthermore, the copolymers of the invention are advantageously suitable for increasing the sun protection factor in sun protection formulations.


The invention accordingly further provides for the use of one or more of the copolymers of the invention for increasing the sun protection factor of sun protection formulations.


In a further preferred embodiment of the invention, the formulations of the invention are sun protection compositions and comprise one or more organic and/or inorganic sun protection filters.


On account of the pigment-dispersing properties of the copolymers of the invention, the cosmetic formulations or products of the invention, in a further preferred embodiment of the invention, are decorative cosmetics such as, for example, powders, foundations, mascaras or lipsticks.


The copolymers of the invention are additionally suitable advantageously as emulsifier, particularly in cosmetic formulations.


The invention therefore further provides for the use of one or more of the copolymers of the invention as emulsifier, preferably in cosmetic formulations.


In a further preferred embodiment of the invention, the formulations of the invention are in the form of emulsions of the water-in-oil or oil-in-water type, especially the skin care products of the invention. In a particularly preferred embodiment of the invention, besides the one or more copolymers of the invention, these emulsions comprise one or more nonionic emulsifiers. Among the emulsions, preference is given to the emulsions of the water-in-oil type.


A further preferred embodiment of the invention is the use of one or more of the copolymers in formulations which are free from wax components.


The copolymers of the invention are suitable not only as thickeners, consistency modifiers and sensorial additives but also as emulsifiers, solubilizers, dispersants, suspension media, lubricants, adherents, and stabilizers.


The invention accordingly further provides for the use of one or more of the copolymers of the invention as thickeners, consistency modifiers, sensorial additives, emulsifiers, solubilizers, dispersants, suspension media, lubricants, adherents or stabilizers.


Relative to the completed cosmetic, pharmaceutical or dermatological formulations, the formulations of the invention comprise preferably 0.01% to 10.0% by weight, more preferably 0.1% to 6.0% by weight, and with particular preference 0.5% to 3.0% by weight of the copolymers of the invention.


The formulations of the invention may comprise cationic, nonionic, ampholytic surfactants, betaine surfactants and/or, in small amounts, anionic surfactants.


The total amount of the surfactants used in the compositions of the invention (e.g., in the case of rinse-off products), based on the completed formulations of the invention, is preferably from 1.0% to 70.0% by weight, more preferably from 5.0% to 40.0% by weight, and with particular preference from 10.0% to 35.0% by weight.


Preferred anionic surfactants are (C10-C22)-alkyl carboxylates and alkylene carboxylates, alkyl ether carboxylates, fatty alcohol sulfates, fatty alcohol ether sulfates, alkylamide sulfates and alkylamide sulfonates, fatty acid alkylamide polyglycol ether sulfates, alkanesulfonates and hydroxyalkanesulfonates, olefinsulfonates, acyl esters of isethionates, α-sulfo fatty acid esters, alkylbenzenesulfonates, alkylphenol glycol ether sulfonates, sulfosuccinates, sulfosuccinic monoesters and diesters, fatty alcohol phosphates, fatty alcohol ether phosphates, protein-fatty acid condensates, alkylmonoglyceride sulfates and alkylmonoglyceride sulfonates, alkylglyceride ether sulfonates, fatty acid methyltaurides, fatty acid sarcosinates, sulforicinoleates, acylglutamates and acylglycinates. These compounds and their mixtures are used in the form of their water-soluble or water-dispersible salts, examples being the sodium, potassium, magnesium, ammonium salts and mono-, di- and triethanolammonium and analogous alkylammonium salts.


The amount of the anionic surfactants in the formulations of the invention is preferably from 0.1% to 10.0% by weight, more preferably from 0.2% to 5.0% by weight, and with particular preference from 0.5% to 2.0% by weight, based on the completed formulations.


Preferred cationic surfactants are quaternary ammonium salts, such as di-(C8-C22)-alkyl-dimethylammonium chloride or bromide, preferably di-(C8-C22)-alkyl-dimethylammonium chloride or bromide; (C8-C22)-alkyl-dimethylethylammonium chloride or bromide; (C8-C22)-alkyl-trimethylammonium chloride or bromide, preferably cetyltrimethylammonium chloride or bromide and (C8-C22)-alkyl-trimethylammonium chloride or bromide; (C10-C24)-alkyl-dimethylbenzylammonium chloride or bromide, preferably (C12-C18)-alkyl-dimethylbenzylammonium chloride, (C8-C22)-alkyl-dimethyl-hydroxyethylammonium chloride, phosphate, sulfate, and lactate, (C8-C22)-alkylamidopropyltrimethylammonium chloride and methosulfate, N,N-bis(2-C8-C22-alkanoyl-oxyethyl)-dimethylammonium chloride and methosulfate and N,N-bis(2-C8-C22-alkanoyl-oxyethyl)hydroxyethyl-methyl-ammonium chloride and methosulfate.


The amount of the cationic surfactants in the formulations of the invention is preferably from 0.1% to 10.0% by weight, more preferably from 0.5% to 7.0% by weight, and with particular preference from 1.0% to 5.0% by weight, based on the completed formulations.


Preferred nonionic surfactants are fatty alcohol ethoxylates (alkylpolyethylene glycols); alkylphenolpolyethylene glycols; fatty amine ethoxylates (alkylaminopolyethylene glycols); fatty acid ethoxylates (acylpolyethylene glycols); polypropylene glycol ethoxylates (Pluronics®); fatty acid alkanolamides (fatty acid amide polyethylene glycols); sucrose esters; sorbitol esters and sorbitan esters and their polyglycol ethers, and also C8-C22-alkylpolyglucosides.


The amount of the nonionic surfactants in the formulations of the invention (in the case of rinse-off products, for example) is preferably in the range from 1.0% to 20.0% by weight, more preferably from 2.0% to 10.0% by weight, and with particular preference from 3.0% to 7.0% by weight, based on the completed formulations.


The formulations of the invention may further comprise amphoteric surfactants. These surfactants may be described as derivatives of long-chain secondary or tertiary amines which possess an alkyl group having 8 to 18 carbon atoms and in which a further group is substituted by an anionic group which imparts solubility in water, as for example by a carboxyl, sulfate or sulfonate group. Preferred amphoteric surfactants are N—(C12-C18)-alkyl-β-aminopropionates and N—(C12-C18)-alkyl-β-iminodipropionates in the form of alkali metal salts and mono-, di-, and trialkylammonium salts. Suitable further surfactants are also amine oxides. These are oxides of tertiary amines with a long-chain group of 8 to 18 carbon atoms and two usually short-chain alkyl groups with 1 to 4 carbon atoms. Preference is given here, for example, to the C10 to C18 alkyl-dimethylamine oxides, fatty acid amidoalkyldimethylamine oxide.


A further preferred group of surfactants are betaine surfactants, also called zwitterionic surfactants. These surfactants contain in the same molecule a cationic group, more particularly an ammonium group, and an anionic group, which may be a carboxylate group, sulfate group or sulfonate group. Suitable betaines are preferably alkyl betaines such as coco-betaine or fatty acid alkylamidopropyl betaines, examples being cocoacylamidopropyldimethyl betaine, or the C12 to C18 dimethylaminohexanoates and/or the C10 to C18 acylamidopropanedimethyl betaines.


As further auxiliaries and additives, the formulations of the invention may comprise waxes, emulsifiers, co-emulsifiers, solubilizers, electrolytes, hydroxyl acids, stabilizers, further cationic polymers, film formers, further thickeners, gelling agents, superfatting agents, refatting agents, antimicrobial actives, biogenic actives, astringents, deodorants, non protection antioxidants, humectants, solvents, filters, colorants, fragrances, pearlescents, opacifiers and/or water-soluble silicones.


The amount of the amphoteric surfactants and/or betaine surfactants in the formulations of the invention is preferably from 0.5% to 20.0% by weight and more preferably from 1.0% to 10.0% by weight, based on the completed formulations.


Preferred surfactants are lauryl sulfate, laureth sulfate, cocoamidopropyl betaine, alkyl betaines such as, for example, coco-betaine, sodium cocoylglutamate, and lauroamphoacetate.


In a further preferred embodiment of the invention the formulations of the invention further comprise, as foam boosters, co-surfactants from the group of alkyl betaines, alkylamido betaines, aminopropionates, aminoglycinates, imidazolinium betaines, and sulfo betaines, amine oxides, fatty acid alkanolamides, and polyhydroxyam ides.


As further auxiliaries and additives, the formulations of the invention may comprise waxes, emulsifiers, co-emulsifiers, solubilizers, electrolytes, hydroxyl acids, stabilizers, further cationic polymers, film formers, further thickeners, gelling agents, superfatting agents, refatting agents, antimicrobial actives, biogeneic actives, astringents, deodorants, unprotection filters, antioxidants, humectants, solvents, colorants, fragrances, pearlescents, opacifiers and/or water-soluble silicones.


The formulations of the invention may comprise waxes, examples being paraffin waxes, microwaxes, and ozokerites, beeswax and its component fractions, and also beeswax derivatives, waxes from the group of homopolymeric polyethylenes or copolymers of α-olefins, and also natural waxes such as rice wax, candelilla wax, carnauba wax, Japan wax or shellac wax.


Emulsifiers, co-emulsifiers and solubilizers may be nonionic, anionic, cationic or amphoteric surface-active compounds.


Suitable nonionic surface-active compounds are preferably as follows:


Adducts of 0 to 30 mol of ethylene oxide and/or 0 to 5 mol of propylene oxide with linear fatty alcohols having 8 to 22 carbon atoms, with fatty acids having 12 to 22 carbon atoms, with alkylphenols having 8 to 15 carbon atoms in the alkyl group, and with sorbitan and/or sorbitol esters; (C12-C18) fatty acid monoesters and diesters of adducts of 0 to 30 mol of ethylene oxide with glycerol; glycerol mono esters and diesters and sorbitan monoesters and diesters of saturated and unsaturated fatty acids having 6 to 22 carbon atoms and, if desired, their ethylene oxide adducts; adducts of 15 to 60 mol of ethylene oxide with castor oil and/or hydrogenated castor oil; polyol esters and especially polyglycerol esters, such as polyglycerol polyricinoleate and polyglycerol poly-12-hydroxystearate, for example. Likewise suitable with preference are ethoxylated fatty amines, fatty acid amides, fatty acid alkanolamides, and mixtures of compounds from two or more of these classes of substance.


Examples of suitable ionogenic co-emulsifiers include anionic emulsifiers, such as mono-, di- or tri-phosphoric esters, soaps (e.g., sodium stearate), fatty alcohol sulfates, and also cationic emulsifiers such as mono-, di-, and tri-alkyl quats and their polymeric derivatives.


Amphoteric emulsifiers preferentially available are alkylaminoalkylcarboxylic acids, betaines, sulfo betaines, and imidazoline derivatives.


Used with particular preference are fatty alcohol ethoxylates selected from the group of ethoxylated stearyl alcohols, isostearyl alcohols, cetyl alcohols, isocetyl alcohols, oleyl alcohols, lauryl alcohols, isolauryl alcohols, and cetylstearyl alcohols, more particularly polyethylene glycol(13) stearyl ether, polyethylene glycol(14) stearyl ether, polyethylene glycol(15) stearyl ether, polyethylene glycol(16) stearyl ether, polyethylene glycol(17) stearyl ether, polyethylene glycol(18) stearyl ether, polyethylene glycol(19) stearyl ether, polyethylene glycol(20) stearyl ether, polyethylene glycol(12) isostearyl ether, polyethylene glycol(13) isostearyl ether, polyethylene glycol(14) isostearyl ether, polyethylene glycol(15) isostearyl ether, polyethylene glycol(16) isostearyl ether, polyethylene glycol(17) isostearyl ether, polyethylene glycol(18) isostearyl ether, polyethylene glycol(19) isostearyl ether, polyethylene glycol(20) isostearyl ether, polyethylene glycol(13) cetyl ether, polyethylene glycol(14) cetyl ether, polyethylene glycol(15) cetyl ether, polyethylene glycol(16) cetyl ether, polyethylene glycol(17) cetyl ether, polyethylene glycol(18) cetyl ether, polyethylene glycol(19) cetyl ether, polyethylene glycol(20) cetyl ether, polyethylene glycol(13) isocetyl ether, polyethylene glycol(14) isocetyl ether, polyethylene glycol(15) isocetyl ether, polyethylene glycol(16) isocetyl ether, polyethylene glycol(17) isocetyl ether, polyethylene glycol(18) isocetyl ether, polyethylene glycol(19) isocetyl ether, polyethylene glycol(20) isocetyl ether, polyethylene glycol(12) oleyl ether, polyethylene glycol(13) oleyl ether, polyethylene glycol(14) oleyl ether, polyethylene glycol(15) oleyl ether, polyethylene glycol(12) lauryl ether, polyethylene glycol(12) isolauryl ether, polyethylene glycol(13) cetylstearyl ether, polyethylene glycol(14) cetylstearyl ether, polyethylene glycol(15) cetylstearyl ether, polyethylene glycol(16) cetylstearyl ether, polyethylene glycol(17) cetylstearyl ether, polyethylene glycol(18) cetylstearyl ether, polyethylene glycol(19) cetylstearyl ether.


Fatty acid ethoxylates selected from the group of ethoxylated stearates, isostearates and oleates, in particular polyethylene glycol(20) stearate, polyethylene glycol(21) stearate, polyethylene glycol(22) stearate, polyethylene glycol(23) stearate, polyethylene glycol(24) stearate, polyethylene glycol(25) stearate, polyethylene glycol(12) isostearate, polyethylene glycol(13) isostearate, polyethylene glycol(14) isostearate, polyethylene glycol(15) isostearate, polyethylene glycol(16) isostearate, polyethylene glycol(17) isostearate, polyethylene glycol(18) isostearate, polyethylene glycol(19) isostearate, polyethylene glycol(20) isostearate, polyethylene glycol(21) isostearate, polyethylene glycol(22) isostearate, polyethylene glycol(23) isostearate, polyethylene glycol(24) isostearate, polyethylene glycol(25) isostearate, polyethylene glycol(12) oleate, polyethylene glycol(13) oleate, polyethylene glycol(14) oleate, polyethylene glycol(15) oleate, polyethylene glycol(16) oleate, polyethylene glycol(17) oleate, polyethylene glycol(18) oleate, polyethylene glycol(19) oleate, polyethylene glycol(20)oleate are likewise preferred.


Sodium laureth-11 carboxylate can advantageously be used as ethoxylated alkylether carboxylic acid or salts thereof.


Ethoxylated triglycerides which can be used are advantageously polyethylene glycol(60) evening primrose glycerides.


It is furthermore advantageous to select the polyethylene glycol glycerol fatty acid esters from the group polyethylene glycol(20) glyceryl laurate, polyethylene glycol(6) glyceryl caprate/caprinate, polyethylene glycol(20) glyceryl oleate, polyethylene glycol(20) glyceryl isostearate, and polyethylene glycol(18) glyceryl oleate/cocoate.


Among the sorbitan esters, polyethylene glycol(20) sorbitan monolaurate, polyethylene glycol(20) sorbitan monostearate, polyethylene glycol(20) sorbitan monoisostearate, polyethylene glycol(20) sorbitan monopalmitate, polyethylene glycol(20) sorbitan monooleate are particularly suitable.


Particularly advantageous co-emulsifiers are glyceryl monostearate, glyceryl monooleate, diglyceryl monostearate, glyceryl isostearate, polyglyceryl-3 oleate, polyglyceryl-3 diisostearate, polyglyceryl-4 isostearate, polyglyceryl-2 dipolyhydroxystearate, polyglyceryl-4 dipolyhydroxystearate, PEG-30 dipolyhydroxystearate, diisostearoyl polyglyceryl-3 diisostearate, glycol distearate and polyglyceryl-3 dipolyhydroxystearate, sorbitan monoisostearate, sorbitan stearate, sorbitan oleate, sucrose distearate, lecithin, PEG-7-hydrogenated castor oil, cetyl alcohol, stearyl alcohol, behenyl alcohol, isobehenyl alcohol and polyethylene glycol(2) stearyl ether (steareth-2), alkylmethicone copolyols, and alkyldimethicone copolyols, in particular cetyldimethicone copolyol, laurylmethiconecopolyol.


The formulations of the invention can comprise one or more of the emulsifiers, co-emulsifiers or solubilizers in amounts of from 0.1% to 20.0% by weight, preferably 1.0% to 15.0% by weight, and more preferably 3.0% to 10.0% by weight, based on the completed formulations.


As electrolyte use may be made of inorganic salts, preferably ammonium or metal salts, particularly preferably of halides, among them in turn preferably CaCl2, MgCl2, LiCl, KCl, NaCl, carbonates, hydrogencarbonates, phosphates, sulfates, nitrates, especially preferably sodium chloride, and/or organic salts, preferably ammonium or metal salts, particularly preferably of glycolic acid, lactic acid, citric acid, tartaric acid, mandelic acid, salicylic acid, ascorbic acid, pyruvic acid, fumaric acid, retinoic acid, sulfonic acids, benzoic acid, kojic acid, fruit acid, malic acid, gluconic acid or galacturonic acid.


Included among these salts are aluminum salts, preferably aluminum chlorohydrate or aluminum-zirconium complex salts.


As electrolyte, the formulations of the invention can also comprise mixtures of different salts. The content of the one or more electrolytes, based on the total formulation of the invention, is preferably from 0.1% to 20.0% by weight, more preferably from 0.2% to 10.0% by weight, and especially preferably from 0.5% to 5.0% by weight.


In terms of hydroxy acids, the formulations of the invention may comprise preferably lactic acid, glycolic acid, salicylic acid, citric acid or polyglycol diacids in free or partial neutralization. Furthermore, formulations of the invention comprising vitamin C or vitamin C derivatives, dihydroxyacetone or skin-whitening actives such as arbutin or glycyrrhetinic acid and salts thereof may be stabilized. The amount of one or more of these substances just stated, based on total formulation of the invention, is preferably from 0.1% to 20.0% by weight, more preferably from 0.2% to 10.0% by weight, and with particular preference from 0.5% to 5.0% by weight.


For the copolymers of the invention it is possible, as additional stabilizers to use metal salts of fatty acids, such as, for example, magnesium stearate, aluminum stearate and/or zinc stearate, preferably in amounts of from 0.1% to 10.0% by weight, preferably from 0.5% to 8.0% by weight, and more preferably from 1.0% to 5.0% by weight, based on the completed formulations.


Suitable cationic polymers are those known under the INCI name “Polyquaternium”, in particular Polyquaternium-31, Polyquaternium-16, Polyquaternium-24, Polyquaternium-7, Polyquaternium-22, Polyquaternium-39, Polyquaternium-28, Polyquaternium-2, Polyquaternium-10, Polyquaternium-11, and Polyquaternium 37&mineral oil&PPG trideceth (Salcare SC95), PVP-dimethylaminoethyl methacrylate copolymer, guar hydroxypropyltriammonium chloride, and calcium alginate and ammonium alginate. Furthermore, cationic cellulose derivatives; cationic starch; copolymers of diallylammonium salts and acrylamides; quaternized vinylpyrrolidone/vinylimidazole polymers; condensation products of polyglycols and amines; quaternized collagen polypeptides; quaternized wheat polypeptides; polyethyleneimines; cationic silicone polymers, such as, for example, amidomethicones; copolymers of adipic acid and dimethylaminohydroxypropyldiethylenetriamine; polyaminopolyamide and cationic chitin derivatives, such as, for example, chitosan, can be used.


The formulations of the invention can comprise one or more of the aforementioned cationic polymers in amounts of from 0.1% to 5.0% by weight, preferably from 0.2% to 3.0% by weight, more preferably from 0.5% to 2.0% by weight, based on the completed formulations.


Furthermore, the formulations of the invention can comprise film formers which, depending on the intended use, are selected from salts of phenylbenzimidazolesulfonic acid, water-soluble polyurethanes, for example C10-polycarbamyl polyglyceryl ester, polyvinyl alcohol, polyvinylpyrrolidone copolymers, for example vinylpyrrolidone/vinyl acetate copolymer, water-soluble acrylic acid polymers/copolymers and esters or salts thereof, for example partial ester copolymers of acrylic acid/methacrylic acid, water-soluble cellulose, for example hydroxymethylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, water-soluble quaterniums, polyquaterniums, carboxyvinyl polymers, such as carbomers and salts thereof, polysaccharides, for example polydextrose and glucan, vinyl acetate/crotonate, for example available under the trade name Aristoflex® A 60 (Clariant).


The formulations of the invention can comprise one or more film formers in amounts of from 0.1% to 10.0% by weight, preferably from 0.2% to 5.0% by weight, and more preferably from 0.5% to 3.0% by weight, based on the completed formulations.


The desired viscosity of the formulations can be established by adding further thickeners and gelling agents. Suitable are preferably cellulose ethers and other cellulose derivatives (e.g., carboxymethylcellulose, hydroxyethylcellulose), gelatin, starch and starch derivatives, sodium alginates, fatty acid polyethylene glycol esters, agar agar, tragacanth or dextrin derivatives, in particular dextrin esters. Furthermore, metal salts of fatty acids, preferably having 12 to 22 carbon atoms, for example sodium stearate, sodium palmitate, sodium laurate, sodium arachidates, sodium behenate, potassium stearate, potassium palmitate, sodium myristate, aluminum monostearate, hydroxyl fatty acids, for example 12-hydroxystearic acid, 16-hydroxyhexadecanoyl acid; fatty acid amides; fatty acid alkanolamides; dibenzalsorbitol and alcohol-soluble polyamides and polyacrylamides or mixtures of such are suitable. Furthermore, crosslinked and uncrosslinked polyacrylates such as carbomers, sodium polyacrylates or polymers containing sulfonic acid, such as ammonium acryloyldimethyltaurate/VP copolymer, can be used.


In one further preferred embodiment of the invention, the formulations of the invention contain 0.01% to 20.0% by weight, more preferably 0.1% to 10.0% by weight, with particular preference 0.2% to 3.0% by weight, and very preferably 0.4% to 2.0% by weight, of thickeners and/or gelling agents, based on the completed formulations of the invention.


Superfatting agents which can be used are preferably lanolin and lecithin, nonethoxylated and polyethoxylated or acylated lanolin derivatives and lecithin derivatives, polyol fatty acid esters, mono-, di- and triglycerides and/or fatty acid alkanolamides, where the latter simultaneously serve as foam stabilizers, and which are preferably used in amounts of from 0.01% to 10.0% by weight, more preferably from 0.1% to 5.0% by weight and especially preferably from 0.5% to 3.0% by weight, based on the completed formulations of the invention.


Active antimicrobial ingredients that can be used are cetyltrimethylammonium chloride, cetylpyridinium chloride, benzethonium chloride, diisobutylethoxyethyldimethylbenzylammonium chloride, sodium aluminum chlorohydroxylactate, triethyl citrate, tricetylmethylammonium chloride, 2,4,4′-trichloro-2′-hydroxydiphenyl ether (triclosan), phenoxyethanol, 1,5-pentanediol, 1,6-hexanediol, 3,4,4′-trichlorocarbanilide (triclocarban), diaminoalkylamide, for example L-lysine hexadecylamide, citrate heavy metal salts, salicylates, piroctoses, in particular zinc salts, pyrithiones and heavy metal salts thereof, in particular zinc pyrithione, zinc phenol sulfate, farnesol, ketoconazole, oxiconazole, bifonazole, butoconazole, cloconazole, clotrimazole, econazole, enilconazole, fenticonazole, isoconazole, miconazole, sulconazole, tioconazole, fluconazole, itraconazole, terconazole, naftifine and terbinafine, selenium disulfide and Octopirox®, iodopropynyl butylcarbamate, methylchloroisothiazolinone, methylisothiazolinone, methyldibromoglutaronitrile, AgCl, chloroxylenol, Na salt of diethylhexyl sulfosuccinate, sodium benzoate, and phenoxyethanol, benzyl alcohol, phenoxyisopropanol, parabens, preferably butyl, ethyl, methyl and propyl paraben, and Na salts thereof, pentanediol, 1,2-octanediol, 2-bromo-2-nitropropane-1,3-diol, ethylhexylglycerol, benzyl alcohol, sorbic acid, benzoic acid, lactic acid, imidazolidinylurea, diazolidinylurea, dimethyloldimethylhydantoin (DMDMH), Na salt of hydroxymethylglycine, and combinations of these active substances.


The formulations of the invention comprise the active antimicrobial ingredients preferably in amounts from 0.001% to 5.0% by weight, more preferably from 0.01% to 3.0% by weight, and with particular preference from 0.1% to 2.0% by weight, based on the completed formulations of the invention.


The formulations of the invention may further comprise active biogenic ingredients selected from plant extracts, such as, for example, aloe vera, and also local anesthetics, antibiotics, antiphlogistics, antiallergics, corticosteroids, sebostatics, Bisabolol®, allantoin, Phytantriol®, proteins, vitamins selected from niacin, biotin, vitamin B2, vitamin B3, vitamin B6, vitamin B3 derivatives (salts, acids, esters, amides, alcohols), vitamin C and vitamin C derivatives (salts, acids, esters, amides, alcohols), preferably as sodium salt of the monophosphoric acid ester of ascorbic acid or as magnesium salt of the phosphoric acid ester of ascorbic acid, tocopherol and tocopherol acetate, and also vitamin E and/or derivatives thereof.


The formulations of the invention may comprise active biogenic ingredients preferably in amounts from 0.001% to 5.0% by weight, more preferably from 0.01% to 3.0% by weight, and with particular preference from 0.1% to 2.0% by weight, based on the completed formulations.


The formulations of the invention can comprise astringents, preferably magnesium oxide, aluminum oxide, titanium dioxide, zirconium dioxide and zinc oxide, oxide hydrates, preferably aluminum oxide hydrate (boehmite) and hydroxides, preferably of calcium, magnesium, aluminum, titanium, zirconium or zinc, and also aluminum chlorohydrates, preferably in amounts of from 0% to 50.0% by weight, particularly preferably in amounts of from 0.01% to 10.0% by weight and especially preferably in amounts of from 0.1% to 10.0% by weight. Allantoin and bisabolol are preferred as deodorizing substances. They are preferably used in amounts of from 0.0001% to 10.0% by weight.


The formulations of the invention can comprise microfine titanium dioxide, mica-titanium oxide, iron oxides, mica-iron oxide, zinc oxide, silicon oxides, ultramarine blue, chromium oxides as pigments/micropigments and also as inorganic sun protection filters.


The formulations of the invention may comprise one or more organic sun protection filters, preferably selected from 4-aminobenzoic acid, 3-(4′-trimethylammonium)benzylideneboran-2-one methyl sulfate, camphor benzalkoniummethosulfate, 3,3,5-trimethylcyclohexyl salicylate, 2-hydroxy-4-methoxybenzophenone, 2-phenylbenzimidazole-5-sulfonic acid and its potassium, sodium and triethanolamine salts, 3,3′-(1,4-phenylenedimethine)bis(7,7-dimethyl-2-oxobicyclo[2.2.1]heptane-1-methanesulfonic acid) and its salts, 1-(4-tert-butylphenyl)-3-(4-methoxyphenyl)propane-1,3-dione, 3-(4′-sulfo)benzylidenebornan-2-one and its salts, 2-ethylhexyl 2-cyano-3,3-diphenylacrylate, polymers of N-[2(and 4)-(2-oxoborn-3-ylidenemethyl)benzyl]acrylamide, 2-ethylhexyl 4-methoxycinnamate, ethoxylated ethyl 4-aminobenzoate, isoamyl 4-methoxycinnamate, 2,4,6-tris[p-(2-ethyl hexyloxycarbonyl)anilino]-1,3,5-triazine, 2-(2H-benzotriazol-2-yl)-4-methyl-6-(2-methyl-3-(1,3,3,3-tetramethyl-1-(trimethylsilyloxy)disiloxanyl)propyl)phenol, bis(2-ethylhexyl) 4,4′-[(6-[4-((1,1-dimethylethyl)aminocarbonyl)phenylamino]-1,3,5-triazin-2,4-yl)diimino]bisbenzoate, benzophenone-3, benzophenone-4 (acid), 3-(4′-methylbenzylidene)-DL-camphor, 3-benzylidenecamphor, 2-ethylhexyl salicylate, 2-ethylhexyl 4-dimethylaminobenzoate, hydroxy-4-methoxybenzophenone-5-sulfon ic acid (sulfisobenzone) and the sodium salt, 4-isopropylbenzyl salicylate, N,N,N-trimethyl-4-(2-oxoborn-3-ylidenemethyl)anilium methyl sulfate, homosalate (INN), oxybenzone (INN), 2-phenylbenzimidazole-5-sulfonic acid and its sodium, potassium and triethanolamine salts, octylmethoxycinnamic acid, isopentyl-4-methoxycinnamic acid, isoamyl-p-methoxycinnamic acid, 2,4,6-trianilino(p-carbo-2′-ethylhexyl-1′-oxy)-1,3,5-triazine (octyltriazone) phenol, 2-2(2H-benzotriazol-2-yl)-4-methyl-6-(2-methyl-3-(1,3,3,3-tetramethyl-1-(trimethylsilyl)oxy)disiloxanyl)propyl (drometrizoletrisiloxane) benzoic acid, 4,4-((6-(((1,1-dimethylethyl)amino)carbonyl)phenyl)amino)-1,3,5-triazine-2,4-diyl)diimino)bis,bis(2-ethylhexyl) ester)benzoic acid, 4,4-((6-(((1,1-dimethylethyl)amino)carbonyl)phenyl)amino)-1,3,5-triazine-2,4-diyl)diimino)bis,bis(2-ethylhexyl)ester), 3-(4′-methylbenzylidene)-DL-camphor (4-methylbenzylidenecamphor), benzylidenecamphorsulfonic acid, octocrylene, polyacrylamidomethylbenzylidenecamphor, 2-ethylhexyl salicylate (octylsalicylate), ethyl-2-hexyl 4-dimethylaminobenzoate (octyldimethyl PABA), PEG-25 PABA, 2-hydroxy-4-methoxybenzophenone-5-sulfonic acid (benzophenone-5) and the Na salt, 2,2′-methylenebis-6-(2H-benzotriazol-2-yl)-4-(tetramethylbutyl)-1,1,3,3-phenol, sodium salt of 2-2′-bis(1,4-phenylene)-1H-benzimidazole-4,6-disulfonic acid, (1,3,5)-triazine-2,4-bis((4-(2-ethylhexyloxy)-2-hydroxy)phenyl)-6-(4-methoxyphenyl), 2-ethylhexyl 2-cyano-3,3-diphenyl-2-propenoate, glyceryl octanoate, di-p-methoxycinnamic acid, p-aminobenzoic acid and esters thereof, 4-tert-butyl-4′-methoxydibenzoylmethane, 4-(2-β-glucopyranoxy)propoxy-2-hydroxybenzophenone, octyl salicylate, methyl-2,5-diisopropylcinnamic acid, cinoxate, dihydroxydimethoxybenzophenone, disodium salt of 2,2′-dihydroxy-4,4′-dimethoxy-5,5′-d isulfobenzophenone, dihydroxybenzophenone, 1,3,4-dimethoxyphenyl-4,4-dimethyl-1,3-pentanedione, 2-ethylhexyl dimethoxybenzyl idened ioxoim idazol id inepropionate, methylenebisbenzotriazolyl tetramethylbutylphenol, phenyl dibenzimidazoletetrasulfonate, bis-ethylhexyloxyphenol methoxyphenol triazine, tetrahydroxybenzophenones, terephthalylidenedicamphorsulfonic acid, 2,4,6-tris[4,2-ethylhexyloxy carbonyl)anilino]-1,3,5-triazine, methylbis(trimethylsiloxy)silylisopentyltrimethoxycinnamic acid, amyl p-dimethylaminobenzoate, amyl p-dimethylaminobenzoate, 2-ethylhexyl p-dimethylaminobenzoate, isopropyl-p-methoxycinnamic acid/diisopropylcinnamic acid esters, 2-ethylhexyl-p-methoxycinnamic acid, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-methoxybenzophenone-5-sulfonic acid and the trihydrate, and also 2-hydroxy-4-methoxybenzophenone-5-sulfonate sodium salt and phenylbenzimidazolesulfonic acid.


The amount of the aforementioned sun protection filters (one or more compounds) in the formulations of the invention is preferably from 0.001% to 30.0% by weight, particularly preferably from 0.05% to 20.0% by weight and especially preferably from 1.0% to 10.0% by weight, based on the total weight of the completed formulation.


The formulations of the invention can comprise one or more antioxidants, preferably selected from amino acids (e.g., glycine, histidine, tyrosine, tryptophan) and derivatives thereof, imidazoles (e.g., urocanic acid) and derivatives thereof, peptides such as DL-carnosine, D-carnosine, L-carnosine and derivatives thereof (e.g., anserine), carotenoids, carotenes (e.g., α-carotene, β-carotene, lycopene) and derivatives thereof, chlorogenic acid and derivatives thereof, lipoic acid and derivatives thereof (e.g., dihydrolipoic acid), aurothioglucose, propylthiouracil and other thiols (e.g., thioredoxin, glutathione, cysteine, cystine, cystamine and the glycosyl, N-acetyl, methyl, ethyl, propyl, amyl, butyl and lauryl, palmitoyl, oleyl, γ-linoleyl, cholesteryl, and glyceryl esters thereof), and also salts thereof, dilauryl thiodipropionate, distearyl thiodipropionate, thiodipropionic acid, and derivatives thereof (e.g., esters, ethers, peptides, lipids, nucleotides, nucleosides, and salts), and also sulfoximine compounds (e.g., buthionine sulfoximines, homocysteine sulfoximine, buthionine sulfones, penta-, hexa-, heptathionine sulfoximine) in very low tolerated doses, also (metal) chelating agents (e.g., α-hydroxyfatty acids, palmitic acid, phytic acid, lactoferrin), α-hydroxy acids (e.g., citric acid, lactic acid, malic acid), humic acid, bile acid, bile extracts, bilirubin, biliverdin, EDTA, EGTA, and derivatives thereof, unsaturated fatty acids and derivatives thereof (e.g., γ-linolenic acid, linoleic acid, oleic acid), folic acid and derivatives thereof, ubiquinone and ubiquinol and derivatives thereof, vitamin C and derivatives (e.g., ascorbyl palmitate, Mg ascorbyl phosphate, ascorbyl acetate), tocopherols and derivatives (e.g., vitamin E acetate), vitamin A and derivatives (vitamin A palmitate), and coniferyl benzoate of benzoin resin, rutinic acid and derivatives thereof, α-glycosylrutin, ferulic acid, furfurylideneglucitol, carnosine, butylhydroxytoluene, butylhydroxyanisole, nordihydroguaiacic acid, nordihydroguaiaretic acid, trihydroxybutyrophenone, uric acid and derivatives thereof, mannose and derivatives thereof, zinc and derivatives thereof (e.g., ZnO, ZnSO4), selenium and derivatives thereof (e.g., selenomethionine), stilbenes and derivatives thereof (e.g., stilbene oxide, trans-stilbene oxide), superoxide dismutase, and the derivatives suitable according to the invention (salts, esters, ethers, sugars, nucleotides, nucleosides, peptides, and lipids) of these specified substances.


The antioxidants can protect the skin and the hair against oxidative stress. Preferred antioxidants here are vitamin E and derivatives thereof, and vitamin A and derivatives thereof.


The amount of the one or more antioxidants in the formulations of the invention is preferably from 0.001% to 30.0% by weight, particularly preferably from 0.05% to 20.0% by weight, and especially preferably from 1% to 10.0% by weight, based on the total weight of the formulation.


Furthermore, humectants selected from the sodium salt of 2-pyrrolidone-5-carboxylate (NaPCA), guanidine; glycolic acid and salts thereof, lactic acid and salts thereof, glucosamines and salts thereof, lactamide monoethanolamine, acetamide monoethanolamine, urea, hydroxy acids, panthenol and derivatives thereof, for example D-panthenol (R-2,4-dihydroxy-N-(3-hydroxypropyl)-3,3-dimethylbutamide), DL-panthenol, calcium pantothenate, panthetine, pantotheine, panthenyl ethyl ether, isopropyl palmitate, glycerol and/or sorbitol can be used, preferably in amounts of from 0.1 to 15% by weight and particularly preferably from 0.5% to 5.0% by weight, based on the completed formulations.


Additionally, the formulations of the invention can comprise organic solvents. In principle, suitable organic solvents are all mono- or polyhydric alcohols. Preference is given to using alcohols having 1 to 4 carbon atoms, such as ethanol, propanol, isopropanol, n-butanol, isobutanol, tert-butanol, glycerol, and mixtures of said alcohols. Further preferred alcohols are polyethylene glycols with a relative molecular mass below 2000. In particular, the use of polyethylene glycol with a relative molecular mass between 200 and 600 and in amounts up to 45.0% by weight and of polyethylene glycol with a relative molecular mass between 400 and 600 in amounts of from 5.0% to 25.0% by weight is preferred. Further suitable solvents are, for example, triacetin (glycerol triacetate) and 1-methoxy-2-propanol.


The formulations of the invention may comprise one or more substances selected from colorants, examples being dyes and/or pigments. The dyes and/or pigments present in the formulations of the invention, not only organic but also inorganic dyes and pigments, are selected from the corresponding positive list of the German cosmetics ordinance or from the EC list of cosmetic colorants.














Chemical or other name
CIN
Color

















Pigment Green
10006
green


Acid Green 1
10020
green


2,4-Dinitrohydroxynaphthalene-7-sulfonic acid
10316
yellow


Pigment Yellow 1
11680
yellow


Pigment Yellow 3
11710
yellow


Pigment Orange 1
11725
orange


2,4-Dihydroxyazobenzene
11920
orange


Solvent Red 3
12010
red


1-(2′-Chloro-4′-nitro-1′-phenylazo)-2-
12085
red


hydroxynaphthalene




Pigment Red 3
12120
red


Cerise Red; Sudan Red; Fat Red G
12150
red


Pigment Red 112
12370
red


Pigment Red 7
12420
red


Pigment Brown 1
12480
brown


4-(2′-Methoxy-5′-sulfonic acid diethylamide-1′-
12490
red


phenylazo)-3-hydroxy-5″-chloro-2″,4″-




dimethoxy-2-naphthoic acid anilide




Disperse Yellow 16
12700
yellow


1-(4-Sulfo-1-phenylazo)-4-aminobenzenesulfonic acid
13015
yellow


2,4-Dihydroxyazobenzene-4′-sulfonic acid
14270
orange


2-(2,4-Dimethylphenylazo-5-sulfonic acid)-1-
14700
red


hydroxy-naphthalene-4-sulfonic acid




2-(4-Sulfo-1-naphthylazo)-1-naphthol-4-sulfonic acid
14720
red


2-(6-Sulfo-2,4-xylylazo)-1-naphthol-5-sulfonic acid
14815
red


1-(4′-Sulfophenylazo)-2-hydroxynaphthalene
15510
orange


1-(2-Sulfonic acid-4-chloro-5-carboxylic acid-1-
15525
red


phenylazo)-2-hydroxynaphthalene




1-(3-Methylphenylazo-4-sulfonic acid)-2-
15580
red


hydroxynaphthalene




1-(4′,(8′)-Sulfonic acid naphthylazo)-2-
15620
red


hydroxynaphthalene




2-Hydroxy-1,2′-azonaphthalene-1′-sulfonic acid
15630
red


3-Hydroxy-4-phenylazo-2-naphthylcarboxylic acid
15800
red


1-(2-Sulfo-4-methyl-1-phenylazo)-2-
15850
red


naphthylcarboxylic acid




1-(2-Sulfo-4-methyl-5-chloro-1-phenylazo)-2-
15865
red


hydroxy-naphthalene-3-carboxylic acid




1-(2-Sulfo-1-naphthylazo)-2-hydroxynaphthalene-
15880
red


3-carboxylic acid




1-(3-Sulfo-1-phenylazo)-2-naphthol-6-sulfonic acid
15980
orange


1-(4-Sulfo-1-phenylazo)-2-naphthol-6-sulfonic acid
15985
yellow


Allura Red
16035
red


1-(4-Sulfo-1-naphthylazo)-2-naphthol-3,6-
16185
red


disulfonic acid




Acid Orange 10
16230
orange


1-(4-Sulfo-1-naphthylazo)-2-naphthol-6,8-
16255
red


disulfonic acid




1-(4-Sulfo-1-naphthylazo)-2-naphthol-3,6,8-
16290
red


trisulfonic acid




8-Amino-2-phenylazo-1-naphthol-3,6-disulfonic acid
17200
red


Acid Red 1
18050
red


Acid Red 155
18130
red


Acid Yellow 121
18690
yellow


Acid Red 180
18736
red


Acid Yellow 11
18820
yellow


Acid Yellow 17
18965
yellow


4-(4-Sulfo-1-phenylazo)-1-(4-sulfophenyl)-5-
19140
yellow


hydroxypyrazolone-3-carboxylic acid




Pigment Yellow 16
20040
yellow


2,6-(4′-Sulfo-2″,4″-dimethyl)bisphenylazo)-1,3-
20170
orange


dihydroxybenzene




Acid Black 1
20470
black


Pigment Yellow 13
21100
yellow


Pigment Yellow 83
21108
yellow


Solvent Yellow
21230
yellow


Acid Red 163
24790
red


Acid Red 73
27290
red


2-[4′-(4″-Sulfo-1″-phenylazo)-7′-sulfo-1′-
27755
black


naphthylazo]-1-hydroxy-7-aminonaphthalene-




3,6-disulfonic acid




4′-[(4″-Sulfo-1″-phenylazo)-7′-sulfo-1′-naphthylazo]-
28440
black


1-hydroxy-8-acetylaminonaphthalene-3,5-




disulfonic acid




Direct Orange 34, 39, 44, 46, 60
40215
orange


Food Yellow
40800
orange


trans-β-Apo-8′-Carotenealdehyde (C30)
40820
orange


trans-Apo-8′-Carotenic acid (C30)-ethyl ester
40825
orange


Canthaxanthin
40850
orange


Acid Blue 1
42045
blue


2,4-Disulfo-5-hydroxy-4′-4″-bis(diethylamino)
42051
blue


triphenyl-carbinol




4-[(4-N-Ethyl-p-sulfobenzylamino)phenyl-(4-
42053
green


hydroxy-2-sulfophenyl)(methylene)-1-(N-ethyl-N-




p-sulfobenzyl)-2,5-cyclohexadieneimine]




Acid Blue 7
42080
blue


(N-Ethyl-p-sulfobenzylaminophenyl-(2-
42090
blue


sulfophenyl)-methylene-(N-ethyl-N-p-




sulfobenzyl)cyclohexadieneimine




Acid Green 9
42100
green


Diethyldisulfobenzyldi-4-amino-2-chlorodi-2-
42170
green


methyl-fuchsonimmonium




Basic Violet 14
42510
violet


Basic Violet 2
42520
violet


2′-Methyl-4′-(N-ethyl-N-m-sulfobenzyl)amino-
42735
blue


4″-(N-diethyl)-amino-2-methyl-N-ethyl-N-m-




sulfobenzylfuchsonimmonium




4′-(N-Dimethyl)amino-4″-(N-phenyl)aminonaphtho-
44045
blue


N-dimethylfuchsonimmonium




2-Hydroxy-3,6-disulfo-4,4′-
44090
green


bisdimethylaminonaphtho-fuchsinimmonium




Acid Red
45100
red


3-(2′-Methylphenylamino)-6-(2′-methyl-4′-
45190
violet


sulfophenylamino)-9-(2″-carboxyphenyl)




xanthenium salt




Acid Red 50
45220
red


Phenyl-2-oxyfluorone-2-carboxylic acid
45350
yellow


4,5-Dibromofluorescein
45370
orange


2,4,5,7-Tetrabromofluorescein
45380
red


Solvent Dye
45396
orange


Acid Red 98
45405
red


3′,4′,5′,6′-Tetrachloro-2,4,5,7-tetrabromofluorescein
45410
red


4,5-Diiodofluorescein
45425
red


2,4,5,7-Tetraiodofluorescein
45430
red


Quinophthalone
47000
yellow


Quinophthalonedisulfonic acid
47005
yellow


Acid Violet 50
50325
violet


Acid Black 2
50420
black


Pigment Violet 23
51319
violet


1,2-Dioxyanthraquinone, calcium-aluminum complex
58000
red


3-Oxypyrene-5,8,10-sulfonic acid
59040
green


1-Hydroxy-4-N-phenylaminoanthraquinone
60724
violet


1-Hydroxy-4-(4′-methylphenylamino)anthraquinone
60725
violet


Acid Violet 23
60730
violet


1,4-Di(4′-methylphenylamino)anthraquinone
61565
green


1,4-Bis(o-sulfo-p-toluidine)anthraquinone
61570
green


Acid Blue 80
61585
blue


Acid Blue 62
62045
blue


N,N′-Dihydro-1,2,1′,2′-anthraquinoneazine
69800
blue


Vat Blue 6; Pigment Blue 64
69825
blue


Vat Orange 7
71105
orange


Indigo
73000
blue


Indigodisulfonic acid
73015
blue


4,4′-Dimethyl-6,6′-dichlorothioindigo
73360
red


5,5′-Dichloro-7,7′-dimethylthioindigo
73385
violet


Quinacridone Violet 19
73900
violet


Pigment Red 122
73915
red


Pigment Blue 16
74100
blue


Phthalocyanine
74160
blue


Direct Blue 86
74180
blue


Chlorinated phthalocyanines
74260
green


Natural Yellow 6, 19; Natural Red 1
75100
yellow


Bixin, Nor-Bixin
75120
orange


Lycopene
75125
yellow


trans-alpha, beta- or gamma-Carotene
75130
orange


Keto- and/or hydroxyl derivatives of carotene
75135
yellow


Guanine or pearlescent agents
75170
white


1,7-Bis(4-hydroxy-3-methoxyphenyl)-1,6-
75300
yellow


heptadiene-3,5-dione




Complex salt (Na, Al, Ca) of carminic acid
75470
red


Chlorophyll a and b; copper compounds of
75810
green


the chlorophylls and chlorophyllines




Aluminum
77000
white


Aluminum hydrate
77002
white


Water-containing aluminum silicates
77004
white


Ultramarine
77007
blue


Pigment Red 101 and 102
77015
red


Barium sulfate
77120
white


Bismuth oxychloride and its mixtures with mica
77163
white


Calcium carbonate
77220
white


Calcium sulfate
77231
white


Carbon
77266
black


Pigment Black 9
77267
black


Carbo medicinalis vegetabilis
77268:1
black


Chromium oxide
77288
green


Chromium oxide, hydrated
77289
green


Pigment Blue 28, Pigment Green 14
77346
green


Pigment Metal 2
77400
brown


Gold
77480
brown


Iron oxides and hydroxides
77489
orange


Iron oxides and hydroxides
77491
red


Hydrated iron oxide
77492
yellow


Iron oxide
77499
black


Mixtures of iron(II) and iron(III) hexacyanoferrate
77510
blue


Pigment White 18
77713
white


Manganese ammonium diphosphate
77742
violet


Manganese phosphate; Mn3(PO4)2*•7H2O
77745
red


Silver
77820
white


Titanium dioxide and its mixtures with mica
77891
white


Zinc oxide
77947
white


6,7-Dimethyl-9-(1′-D-ribityl)isoalloxazine,

yellow


lactoflavin




Caramel

brown


Capsanthin, Capsorubin

orange


Betanine

red


Benzopyrilium salts, anthocyanines

red


Aluminum, zinc, magnesium and calcium stearate

white


Bromothymol Blue

blue


Bromocresol Green

green


Acid Red 195

red









Also advantageous are oil-soluble natural dyes, such as, for example, paprika extracts, β-carotene, and cochineal.


Pearlescent pigments are also advantageously used, e.g., pearl essence (guanine/hypoxanthine mixed crystals from fish scales) and mother-of-pearl (ground mussel shells), monocrystalline pearlescent pigments, such as, for example, bismuth oxychloride (BiOCl), layer-substrate pigments, e.g., mica/metal oxide, silver-white pearlescent pigments of TiO2, interference pigments (TiO2, varying layer thickness), color luster pigments (Fe2O3) and combination pigments (TiO2/Fe2O3, TiO2/Cr2O3, TiO2/Prussian blue, TiO2/carmine).


Within the context of the present invention, effect pigments are to be understood as meaning pigments which bring about particular optical effects as a result of their refractive properties. Effect pigments impart luster or glitter effects to the treated surface (skin, hair, mucosa) or are able to optically conceal skin unevennesses and skin wrinkles through diffuse light scattering. As a particular embodiment of the effect pigments, interference pigments are preferred. Particularly suitable effect pigments are, for example, mica particles which are coated with at least one metal oxide. Besides mica, a sheet silicate, silica gel and other SiO2 modifications are also suitable as carriers. A metal oxide which is often used for the coating is, for example, titanium oxide, to which, if desired, iron oxide can be admixed. The reflection properties can be influenced via the size and the shape (e.g., spherical, ellipsoidal, flattened, planar, nonplanar) of the pigment particles and also via the thickness of the oxide coating. Other metal oxides too, e.g., bismuth oxychloride (BiOCl), and the oxides of, for example, titanium, in particular the TiO2 modifications anatase and rutile, and of aluminum, tantalum, niobium, zirconium, and hafnium. With magnesium fluoride (MgF2) and calcium fluoride (fluorspar, CaF2), too, it is possible to produce effect pigments.


The effects can be controlled not only via the particle size but also via the particle size distribution of the pigment assembly. Suitable particle size distributions range, for example, from 2-50 μm, 5-25 μm, 5-40 μm, 5-60 μm, 5-95 μm, 5-100 μm, 10-60 μm, 10-100 μm, 10-125 μm, 20-100 μm, 20-150 μm, and <15 μm. A broader particle size distribution, for example of 20-150 μm, brings about glittering effects, whereas a narrower particle size distribution of <15 μm provides a uniform satin appearance.


The formulations of the invention comprise effect pigments preferably in amounts of from 0.1% to 20.0% by weight, more preferably from 0.5% to 10.0% by weight and especially preferably from 1% to 5.0% by weight, in each case based on the total weight of the formulation.


Preferably suitable as pearlizing component are fatty acid monoalkanolamides, fatty acid dialkanolamides, monoesters or diesters of alkylene glycols, in particular ethylene glycol and/or propylene glycol or oligomers thereof, with higher fatty acids, such as, for example, palmitic acid, stearic acid and behenic acid, monoesters or polyesters of glycerol with carboxylic acids, fatty acids and metal salts thereof, ketosulfones or mixtures of the specified compounds. Particular preference is given to ethylene glycol distearates and/or polyethylene glycol distearates having on average 3 glycol units.


If the formulations of the invention comprise pearlizing compounds, these are preferably present in the formulations of the invention in an amount of from 0.1% to 15.0% by weight and more preferably in an amount of from 1.0% to 10.0% by weight.


Fragrance and/or perfume oils which may be used are individual odorant compounds, examples being the synthetic products of the ester, ether, aldehyde, ketone, alcohol, and hydrocarbon types. Odorant compounds of the ester type are, for example, benzyl acetate, phenoxyethyl isobutyrate, p-tert-butylcyclohexyl acetate, linalyl acetate, dimethylbenzylcarbinyl acetate, phenylethyl acetate, linalyl benzoate, benzyl formate, ethylmethylphenyl glycinate, allyl cyclohexyl propionate, styrallyl propionate, and benzyl salicylate. The ethers include, for example, benzyl ethyl ethers; the aldehydes include, for example, the linear alkanals having 8 to 18 carbon atoms, citral, citronellal, citronellyloxyacetaldehyde, cyclamenaldehyde, hydroxycitronellal, lilial, and bourgeonal; the ketones include, for example, the ionones, alpha-isomethylionone, and methyl cedryl ketone; the alcohols include anethol, citronellol, eugenol, geraniol, linalool, phenylethyl alcohol, and terpineol; and the hydrocarbons include primarily the terpenes and balsams. Preference is given to using mixtures of different odorants which together produce a pleasing scent note.


Perfume oils can also comprise natural odorant mixtures, as are accessible from vegetable or animal sources, e.g., pine oil, citrus oil, jasmine oil, lily oil, rose oil or ylang-ylang oil. Essential oils of relatively low volatility, which in most cases are used as aromatic components, are also suitable as perfume oils, e.g., sage oil, chamomile oil, clove oil, melissa oil, mint oil, cinnamon leaf oil, linden blossom oil, juniperberry oil, vetiver oil, olibanum oil, galbanum oil, and ladanum oil.


Acids or alkalis used for adjusting the pH are preferably mineral acids, in particular HCl, inorganic bases, in particular NaOH or KOH, and organic acids, in particular citric acid.


The formulations have pH values of preferably 2 to 10, more preferably from 3 to 9, with particular preference from 4.5 to 8, and exceptionally preferably from 5.5 to 7.5.


The examples and applications below are intended to illustrate the invention, but without restricting it to them. All percentage figures are in percent by weight (% by weight), unless explicitly indicated otherwise.







EXAMPLES

The listing below shows 285 copolymers of the invention that are suitable with particular advantage for formulating the compositions of the invention. The various copolymers #1 to #285 are obtainable in accordance with preparation processes a), b1), and b2) below.


Process a):

These polymers are preparable by means of radical polymerization in tert-butanol. For this procedure, the monomers were introduced into tert-butanol, the reaction mixture was rendered inert, and then the reaction was started, after initial heating to 60° C., by addition of the corresponding tert-butanol-soluble initiator (preferably dilauroyl peroxide). After the end of reaction (two hours), the polymers are isolated by distillative removal of the solvent, followed by vacuum drying.












Copolymer # 1

















350
g
tert-butanol with 2.5% water


58.2
g
stearyl acrylate


1.8
g
[2-(acryloyloxy)-ethyl]trimethylammonium chloride (AOETAC)


2.0
g
dilauroyl peroxide (DLP)









Procedure:

350 g of tert-butanol and 58.2 g of stearyl acrylate are charged to a 1 l flask with stirrer, temperature sensor, reflux condenser, and N2 introduction facility, and the flask is closed. It is then rendered inert with N2, after which 1.8 g of [2-(acryloyloxy)-ethyl]trimethylammonium chloride (AOETAC) are added. At an internal temperature of 60° C., the reaction is initiated with 2.0 g of dilauroyl peroxide (DLP). The resultant polymer remains in solution. The solution is subsequently stirred, after which the internal temperature is increased to reflux temperature, and subsequent stirring takes place to a sufficient degree. The product is dried in a vacuum drying oven at 35° C.


Process b):

These polymers are preparable by the solution process in organic solvents (preferably toluene, also tertiary alcohols, for example). Here, the monomers are introduced into the solvent, the reaction mixture is rendered inert, and then the reaction is started, after heating to 60° C., by addition of suitable initiators or initiator systems (preferably dilauroyl peroxide). After the end of reaction, the polymers are precipitated by evaporation or cooling of the solvent or else isolated by precipitation from a solvent in which the polymer is insoluble, and are subsequently vacuum-dried.


Process b1): One-Pot Process












Copolymer # 276
















 350 g
tert-butanol with 2.5% water


58.2 g
stearyl acrylate


 1.8 g
[2-(acryloyloxy)-ethyl]trimethylammonium



chloride (AOETAC), and


 6.0 g
lauryl methacrylate


 2.0 g
dilauroyl peroxide (DLP)









Procedure:

350 g of tert-butanol and 58.2 g of stearyl acrylate are charged to a 1 l flask with stirrer, temperature sensor, reflux condenser, and N2 introduction facility, and the flask is closed. It is then rendered inert with N2, after which 1.8 g of [2-(acryloyloxy)-ethyl]trimethylammonium chloride (AOETAC) and 6.0 g of lauryl methacrylate are added. At an internal temperature of 60° C., the reaction is initiated with 2.0 g of dilauroyl peroxide (DLP). The polymer formed remains in solution. The solution is subsequently stirred and then the internal temperature is raised to reflux temperature. After a sufficient subsequent stirring period, the heating is switched off and the system is cooled to room temperature (RT). The polymer precipitates. The precipitate is isolated by suction filtration on a suction filter, and the product is washed and dried in a vacuum drying oven at 35° C.


Process b2): Precipitation from Cold Water












Copolymer # 1
















 350 g
tert-butanol with 2.5% water


58.2 g
stearyl acrylate


 1.8 g
[2-(acryloyloxy)-ethyl]trimethylammonium chloride (AOETAC)


 2.0 g
dilauroyl peroxide (DLP)









Procedure:

350 g of tert-butanol and 58.2 g of stearyl acrylate are charged to a 1 l flask with stirrer, temperature sensor, reflux condenser, and N2 introduction facility, and the flask is closed. It is then rendered inert with N2, after which 1.8 g of [2-(acryloyloxy)-ethyl]trimethylammonium chloride (AOETAC) are added. At an internal temperature of 60° C., the reaction is initiated with 2.0 g of dilauroyl peroxide (DLP). The polymer formed remains in solution. The solution is subsequently stirred, after which the internal temperature is increased to reflux temperature, followed by subsequent stirring to a sufficient degree. The hot batch is then pumped, by means of a pump, into 700 g of ice-cold water. A white precipitate is formed. This precipitate is filtered off with suction, cold, on a white-ribbon circular filter, and dried in a vacuum drying oven at 35° C.


Table A below lists examples of polymers of the invention. In the first column of the table, monomers of the following structural formula (Ia1)




embedded image


of component a) are shown.









TABLE A







Examples of polymers of the invention













Polymer





Preparation


#
Component a)
Component b)
Component c)
Component a)
Component a) or c)
route






Below:








R2 of the formula








(la1) with R1 = H





 1
97% C18H37
3% AOETAC



a


 2
97% C18H37
2% AOETAC
1% EDDMA


a


 3
98% C18H37
1% AOETAC
1% HDDMA


a


 4
97% C18H37
2% AOETAC
1% HDDMA


a


 5
96% C18H37
3% AOETAC
1% HDDMA


a


 6
94% C18H37
5% AOETAC
1% HDDMA


a


 7
89% C18H37
10% AOETAC
1% HDDMA


a


 8
96.5% C18H37
2% AOETAC
1.5% HDDMA


a


 9
96% C18H37
2% AOETAC
2% HDDMA


a


 10
95% C18H37
2% AOETAC
3% HDDMA


a


 11
93% C18H37
2% AOETAC
5% HDDMA


a


 12
97% C18H37
2% AOETAC
1% BDDMA


a


 13
97% C18H37
2% AOETAC
1% DDDMA


a


 14
97% C18H37
2% AOETAC
1% TMPTA


a


 15
97% C18H37
2% AOETAC
1% TMPTMA


a


 16
97% C18H37
2% AOETAC
1% MBA


a


 17
97% C18H37
2% AOETAC
1% HDDMA/TMPTA


a


 18
97% C18H37
2% AOETAC
1% AMA


a


 19
97% C18H37
2% AOETAC
1% Glycerol


a





diacrylate





 20
97% C18H37
2% AOETAC
1% Triallylamine


a


 21
97% C18H37
2% AOETAC
1% Triallylcyanurate


a


 22
97% C18H37
2% AOETAC
1% PEG diacrylate


a


 23
93% C18H37
3% AOETAC

4% B250MA

a


 24
89% C18H37
3% AOETAC

8% B250MA

a


 25
87% C18H37
3% AOETAC

10% B250MA

a


 26
85% C18H37
3% AOETAC

12% B250MA

a


 27
91% C18H37
3% AOETAC
1% HDDMA
5% B250MA

a


 28
86% C18H37
3% AOETAC
1% HDDMA
10% B250MA

a


 29
76.2% C18H37
3% AOETAC
1% HDDMA
19.8% B250MA

a


 30
56.4% C18H37
3% AOETAC
1% HDDMA
39.6% B250MA

a


 31
82.9% C18H37
2.9% AOETAC
4.7% HDDMA
9.5% B250MA

a


 32
79.1% C18H37
2.7% AOETAC
9.1% HDDMA
9.1% B250MA

a


 33
78.7% C18H37
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% Hexadecyl acrylate
a


 34
74.6% C18H37
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% Hexadecyl acrylate
a


 35
66.3% C18H37
2.3% AOETAC
4.8% HDDMA
7.6% B250MA
19% Hexadecyl acrylate
a


 36
78.7% C18H37
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% Octyldodecyl
a







acrylate



 37
74.6% C18H37
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% Octyldodecyl acrylate
a


 38
66.3% C18H37
2.3% AOETAC
4.8% HDDMA
7.6% B250MA
19% Octyldodecyl acrylate
a


 39
78.7% C18H37
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% Isostearyl acrylate
a


 40
74.6% C18H37
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% Isostearyl acrylate
a


 41
66.3% C18H37
2.3% AOETAC
4.8% HDDMA
7.6% B250MA
19% Isostearyl acrylate
a


 42
78.7% C18H37
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


 43
74.6% C18H37
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% C26-C28 α-olefin
a


 44
66.3% C18H37
2.3% AOETAC
4.8% HDDMA
7.6% B250MA
19% C26-C28 α-olefin
a


 45
84.2% C18H37
1.6% AOETAC
3.3% DDDMA
9.3% B250MA
1.6% C26-C28 α-olefin
a


 46
82.8% C18H37
4.2% AOETAC
3.3% DDDMA
4.7% B250MA
5% C26-C28 α-olefin
a


 47
78.4% C18H37
5.2% AOETAC
5% DDDMA
4.7% B250MA
6.7% C26-C28 α-olefin
a


 48
78.7% C18H37
2.7% AOETAC
4.8% DDDMA
9% B250MA
4.8% C30 α-olefin
a


 49
81.3% C18H37
2.8% AOETAC
1.6% TMPTA
9.3% B250MA
5% C26-C28 α-olefin
a


 50
80% C18H37
2.8% AOETAC
3.2% TMPTA
9.2% B250MA
4.8% C26-C28 α-olefin
a


 51
81.9% C18H37
1.6% AOETAC
3.3% TMPTA
9.9% B250MA
3.3% C26-C28 α-olefin
a


 52
84.1% C18H37
1.6% AOETAC
3.3% TMPTA
9.4% B250MA
1.6% C26-C28 α-olefin
a


 53
88.5% C18H37
1.7% AOETAC
3.4% TMPTA
4.7% B250MA
1.7% C26-C28 α-olefin
a


 54
81.3% C18H37
1.7% AOETAC
3.3% TMPTA
12% B250MA
1.7% C26-C28 α-olefin
a


 55
80.7% C18H37
0.8% AOETAC
3.3% TMPTA
10.2% B250MA
5% C26-C28 α-olefin
a


 56
83.2% C18H37
1.7% AOETAC
3.3% TMPTA
8.4% B250MA
3.4% C26-C28 α-olefin
a


 57
78.7% C18H37
2.7% AOETAC
4.8% TMPTA
9% B250MA
4.8% C26-C28 α-olefin
a


 58
82.5% C18H37
0.8% AOETAC
5% TMPTA
8.4% B250MA
3.3% C26-C28 α-olefin
a


 59
82.9% C18H37
2.9% AOETAC
4.7% HDDMA/TMPTA
9.5% B250MA

a


 60
78.2% C18H37
3.6% AOETAC
4.7% HDDMA/TMPTA
9% B250MA
4.7% C26-C28 α-olefin
a


 61
91% C18H37
3% AOETAC
1% HDDMA
5% T250MA

a


 62
86.1% C18H37
3% AOETAC
1% HDDMA
9.9% T250MA

a


 63
91% C18H37
3% AOETAC
1% HDDMA
5% T080MA

a


 64
86.1% C18H37
3% AOETAC
1% HDDMA
9.9% T080MA




 65
91% C18H37
3% AOETAC
1% HDDMA
5% LA070MA

a


 66
86.1% C18H37
3% AOETAC
1% HDDMA
9.9% LA070MA




 67
91% C18H37
3% AOETAC
1% HDDMA

5% Butyl acrylate
a


 68
86.1% C18H37
3% AOETAC
1% HDDMA

9.9% Butyl acrylate
a


 69
86.1% C18H37
3% AOETAC
1% HDDMA

9.9% Hexadecyl acrylate
a


 70
86.1% C18H37
3% AOETAC
1% HDDMA

9.9% Octyldodecyl
a







acrylate



 71
86.1% C18H37
3% AOETAC
1% HDDMA

9.9% Isostearyl acrylate
a


 72
86.1% C18H37
3% AOETAC
1% HDDMA

9.9% C26-C28 α-olefin
a


 73
86.1% C18H37
3% AOETAC
1% HDDMA

9.9% C30 α-olefin
a


 74
97% C18H37
3% MAPTAC



a


 75
97% C18H37
2% MAPTAC
1% EDDMA


a


 76
97% C18H37
2% MAPTAC
1% HDDMA


a


 77
97% C18H37
2% MAPTAC
1% BDDMA


a


 78
97%C18H37
2% MAPTAC
1% DDDMA


a


 79
97% C18H37
2% MAPTAC
1% TMPTA


a


 80
97% C18H37
2% MAPTAC
1% TMPTMA


a


 81
97% C18H37
2% MAPTAC
1% MBA

-—
a


 82
97% C18H37
2% MAPTAC
1% HDDMA/TMPTA


a


 83
97% C18H37
2% MAPTAC
1% AMA


a


 84
97% C18H37
2% MAPTAC
1% Glycerol


a





diacrylate





 85
97% C18H37
2% MAPTAC
1% Triallylamine


a


 86
97% C18H37
2% MAPTAC
1% Triallylcyanurate


a


 87
97% C18H37
2% MAPTAC
1% PEG diacrylate


a


 88
87% C18H37
3% MAPTAC

10% B250MA

a


 89
86% C18H37
3% MAPTAC
1% HDDMA
10% B250MA

a


 90
78.7% C18H37
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Butyl acrylate
a


 91
78.7% C18H37
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Hexadecyl acrylate
a


 92
78.7% C18H37
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Octyldodecyl
a







acrylate



 93
78.7% C18H37
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Isostearyl acrylate
a


 94
78.7% C18H37
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


 95
78.7% C18H37
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% C30 α-olefin
a


 96
78.7% C18H37
2.7% MAPTAC
4.8% DDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


 97
78.7% C18H37
2.7% MAPTAC
4.8% DDDMA
9% B250MA
4.8% C30 α-olefin
a


 98
78.7% C18H37
2.7% MAPTAC
4.8% TMPTA
9% B250MA
4.8% C26-C28 α-olefin
a


 99
78.7% C18H37
2.7% MAPTAC
4.8% TMPTA
9% B250MA
4.8% C30 α-olefin
a


100
78.7% C18H37
3% MAPTAC
1% HDDMA/TMPTA
10% B250MA

a


101
78.7% C18H37
2.7% MAPTAC
4.8% HDDMA/TMPTA
9% B250MA
4.8% C26-C28 α-olefin
a


102
86% C18H37
3% MAPTAC
1% HDDMA
10% T250MA

a


103
86% C18H37
3% MAPTAC
1% HDDMA
10% T080MA

a


104
86% C18H37
3% MAPTAC
1% HDDMA
10% LA070MA

a


105
86.1% C18H37
3% MAPTAC
1% HDDMA

9.9% Butyl acrylate
a


106
86.1% C18H37
3% MAPTAC
1% HDDMA

9.9% Hexadecyl acrylate
a


107
86.1% C18H37
3% MAPTAC
1% HDDMA

9.9% Octyldodecy
a







acrylate



108
86.1% C18H37
3% MAPTAC
1% HDDMA

9.9% Isostearyl acrylate
a


109
86.1% C18H37
3% MAPTAC
1% HDDMA

9.9% C26-C28 α-olefin
a


110
86.1% C18H37
3% MAPTAC
1% HDDMA

9.9% C30 α-olefin
a


111
78.2% C18H37
3.6% AOETAC/
4.7% HDDMA/TMPTA
9% B250MA
4.7% C26-C28 α-olefin
a




MAPTAC






112
97% C18H37
3% DADMAC



a


113
97% C18H37
2% DADMAC
1% EDDMA


a


114
97% C18H37
2% DADMAC
1% HDDMA


a


115
97% C18H37
2% DADMAC
1% BDDMA


a


116
97% C18H37
2% DADMAC
1% DDDMA


a


117
97% C18H37
2% DADMAC
1% TMPTA


a


118
86% C18H37
3% DADMAC
1% HDDMA
10% B250MA

a


119
78.7% C18H37
2.7% DADMAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


120
78.7% C18H37
2.7% DADMAC
4.8% HDDMA
9% B250MA
4.8% C30 α-olefin
a






Below:








R2 of the formula








(la1) with R1 =








Methyl





121
97% C12H25
3% AOETAC



a


122
98% C12H25
1% AOETAC
1% HDDMA


a


123
97% C12H25
2% AOETAC
1% HDDMA


a


124
96% C12H25
3% AOETAC
1% HDDMA


a


125
94% C12H25
5% AOETAC
1% HDDMA


a


126
89% C12H25
10% AOETAC
1% HDDMA


a


127
97% C12H25
2% AOETAC
1% DDDMA


a


128
97% C12H25
2% AOETAC
1% TMPTA


a


129
97% C12H25
2% AOETAC
1% HDDMA/TMPTA


a


130
93% C12H25
3% AOETAC

4% B250MA

a


131
89% C12H25
3% AOETAC

8% B250MA

a


132
87% C12H25
3% AOETAC

10% B250MA

a


133
91% C12H25
3% AOETAC
1% HDDMA
5% B250MA

a


134
86% C12H25
3% AOETAC
1% HDDMA
10% B250MA

a


135
82.9% C12H25
2.9% AOETAC
4.7% HDDMA
9.5% B250MA

a


136
78.7% C12H25
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% Hexadecyl acrylate
a


137
74.6% C12H25
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% Hexadecyl acrylate
a


138
78.7% C12H25
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% Octyldodecyl
a







acrylate



139
74.6% C12H25
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% Octyldodecy
a







acrylate



140
78.7% C12H25
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% Isostearyl acrylate
a


141
74.6% C12H25
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% Isostearyl acrylate
a


142
78.7% C12H25
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


143
74.6% C12H25
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% C26-C28 α-olefin
a


144
78.7% C12H25
2.7% AOETAC
4.8% DDDMA
9% B250MA
4.8% C30 α-olefin
a


145
80% C12H25
2.8% AOETAC
3.2% TMPTA
9% B250MA
4.8% C26-C28 α-olefin
a


146
82.9% C12H25
2.9% AOETAC
4.7% HDDMA/TMPTA
9.5% B250MA

a


147
78.2% C12H25
3.6% AOETAC
4.7% HDDMA/TMPTA
9% B250MA
4.7% C26-C28 α-olefin
a


148
91% C12H25
3% AOETAC
1% HDDMA
5% T250MA

a


149
86.1% C12H25
3% AOETAC
1% HDDMA
9.9% T250MA

A


150
91% C12H25
3% AOETAC
1% HDDMA
5% T080MA

A


151
86.1% C12H25
3% AOETAC
1% HDDMA
9.9% T080MA




152
91% C12H25
3% AOETAC
1% HDDMA
5% LA070MA

A


153
86.1% C12H25
3% AOETAC
1% HDDMA
9.9% LA070MA




154
91% C12H25
3% AOETAC
1% HDDMA

5% Butyl acrylate
a


155
86.1% C12H25
3% AOETAC
1% HDDMA

9.9% Butyl acrylate
a


156
86.1% C12H25
3% AOETAC
1% HDDMA

9.9% Hexadecyl acrylate
a


157
86.1% C12H25
3% AOETAC
1% HDDMA

9.9% Octyldodecy
a







acrylate



158
86.1% C12H25
3% AOETAC
1% HDDMA

9.9% Isostearyl acrylate
a


159
86.1% C12H25
3% AOETAC
1% HDDMA

9.9% C26-C28 α-olefin
a


160
86.1% C12H25
3% AOETAC
1% HDDMA

9.9% C30 α-olefin
a


161
97% C12H25
3% MAPTAC



a


162
97% C12H25
2% MAPTAC
1% HDDMA


a


163
97% C12H25
2% MAPTAC
1% DDDMA


a


164
97% C12H25
2% MAPTAC
1% TMPTA


a


165
97% C12H25
2% MAPTAC
1% HDDMA/TMPTA


a


166
87% C12H25
3% MAPTAC

10% B250MA

a


167
86% C12H25
3% MAPTAC
1% HDDMA
10% B250MA

a


168
78.7% C12H25
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Butyl acrylate
a


169
78.7% C12H25
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Hexadecyl acrylate
a


170
78.7% C12H25
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Octyldodecy
a







acrylate



171
78.7% C12H25
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Isostearyl acrylate
a


172
78.7% C12H25
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


173
78.7% C12H25
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% C30 α-olefin
a


174
78.7% C12H25
2.7% MAPTAC
4.8% DDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


175
78.7% C12H25
2.7% MAPTAC
4.8% DDDMA
9% B250MA
4.8% C30 α-olefin
a


176
78.7% C12H25
2.7% MAPTAC
4.8% TMPTA
9% B250MA
4.8% C26-C28 α-olefin
a


177
78.7% C12H25
2.7% MAPTAC
4.8% TMPTA
9% B250MA
4.8% C30 α-olefin
a


178
78.7% C12H25
3% MAPTAC
1% HDDMA/TMPTA
10% B250MA

a


179
78.7% C12H25
2.7% MAPTAC
4.8% HDDMA/TMPTA
9% B250MA
4.8% C26-C28 α-olefin
a


180
86% C12H25
3% MAPTAC
1% HDDMA
10% T250MA

a


181
86% C12H25
3% MAPTAC
1% HDDMA
10% T080MA

a


182
86% C12H25
3% MAPTAC
1% HDDMA
10% LA070MA

a


183
86.1% C12H25
3% MAPTAC
1% HDDMA

9.9% Butyl acrylate
a


184
86.1% C12H25
3% MAPTAC
1% HDDMA

9.9% Hexadecyl acrylate
a


185
86.1% C12H25
3% MAPTAC
1% HDDMA

9.9% Octyldodecy
a







acrylate



186
86.1% C12H25
3% MAPTAC
1% HDDMA

9.9% Isostearyl acrylate
a


187
86.1% C12H25
3% MAPTAC
1% HDDMA

9.9% C26-C28 α-olefin
a


188
86.1% C12H25
3% MAPTAC
1% HDDMA

9.9% C30 α-olefin
a


189
78.2% C12H25
3.6% AOETAC/
4.7% HDDMA/TMPTA
9% B250MA
4.7% C26-C28 α-olefin
a




MAPTAC






190
97% C12H25
3% DADMAC



a


191
97% C12H25
2% DADMAC
1% HDDMA


a


192
97% C12H25
2% DADMAC
1% DDDMA


a


193
97% C12H25
2% DADMAC
1% TMPTA


a


194
86% C12H25
3% DADMAC
1% HDDMA
10% B250MA

a


195
78.7% C12H25
2.7% DADMAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


196
78.7% C12H25
2.7% DADMAC
4.8% HDDMA
9% B250MA
4.8% C30 α-olefin
a






Below:








R2 of the formula








(la1)








with R1 = H





197
97% C22H45
3% AOETAC



a


198
98% C22H45
1% AOETAC
1% HDDMA


a


199
97% C22H45
2% AOETAC
1% HDDMA


a


200
96% C22H45
3% AOETAC
1% HDDMA


a


201
94% C22H45
5% AOETAC
1% HDDMA


a


202
89% C22H45
10 % AOETAC
1% HDDMA


a


203
97% C22H45
2% AOETAC
1% DDDMA


a


204
97% C22H45
2% AOETAC
1% TMPTA


a


205
97% C22H45
2% AOETAC
1% HDDMA/TMPTA


a


206
93% C22H45
3% AOETAC

4% B250MA

a


207
89% C22H45
3% AOETAC

8% B250MA

a


208
87% C22H45
3% AOETAC

10% B250MA

a


209
91% C22H45
3% AOETAC
1% HDDMA
5% B250MA

a


210
86% C22H45
3% AOETAC
1% HDDMA
10% B250MA

a


211
82.9% C22H45
2.9% AOETAC
4.7% HDDMA
9.5% B250MA

a


212
78.7% C22H45
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% Hexadecyl acrylate
a


213
74.6% C22H45
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% Hexadecyl acrylate
a


214
78.7% C22H45
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% Octyldodecyl
a







acrylate



215
74.6% C22H45
2.5% AOETAC
4.8% HDDMA
8.6 % B250MA
9.5% Octyldodecyl
a







acrylate



216
78.7% C22H45
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% Isostearyl acrylate
a


217
74.6% C22H45
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% Isostearyl acrylate
a


218
78.7% C22H45
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


219
74.6% C22H45
2.5% AOETAC
4.8% HDDMA
8.6% B250MA
9.5% C26-C28 α-olefin
a


220
78.7% C22H45
2.7% AOETAC
4.8% DDDMA
9% B250MA
4.8% C30 α-olefin
a


221
80% C22H45
2.8% AOETAC
3.2% TMPTA
9.2% B250MA
4.8% C26-C28 α-olefin
a


222
82.9% C22H45
2.9% AOETAC
4.7% HDDMA/TMPTA
9.5% B250MA

a


223
78.2% C22H45
3.6% AOETAC
4.7% HDDMA/TMPTA
9% B250MA
4.7% C26-C28 α-olefin
a


224
91% C22H45
3% AOETAC
1% HDDMA
5% T250MA

a


225
86.1% C22H45
3% AOETAC
1% HDDMA
9.9% T250MA

a


226
91% C22H45
3% AOETAC
1% HDDMA
5% T080MA

a


227
86.1% C22H45
3% AOETAC
1% HDDMA
9.9% T080MA




228
91% C22H45
3% AOETAC
1% HDDMA
5% LA070MA

a


229
86.1% C22H45
3% AOETAC
1% HDDMA
9.9% LA070MA




230
91% C22H45
3% AOETAC
1% HDDMA

5% Butyl acrylate
a


231
86.1% C22H45
3% AOETAC
1% HDDMA

9.9% Butyl acrylate
a


232
86.1% C22H45
3% AOETAC
1% HDDMA

9.9% Hexadecyl acrylate
a


233
86.1% C22H45
3% AOETAC
1% HDDMA

9.9% Octyldodecyl
a







acrylate



234
86.1% C22H45
3% AOETAC
1% HDDMA

9.9% Isostearyl acrylate
a


235
86.1% C22H45
3% AOETAC
1% HDDMA

9.9% C26-C28 α-olefin
a


236
86.1% C22H45
3% AOETAC
1% HDDMA

9.9% C30 α-olefin
a


237
97% C22H45
3% MAPTAC



a


238
97% C22H45
2% MAPTAC
1% HDDMA


a


239
97% C22H45
2% MAPTAC
1% DDDMA


a


240
97% C22H45
2% MAPTAC
1% TMPTA


a


241
97% C22H45
2% MAPTAC
1% HDDMA/TMPTA


a


242
87% C22H45
3% MAPTAC

10% B250MA

a


243
86% C22H45
3% MAPTAC
1% HDDMA
10% B250MA

a


244
78.7% C22H45
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Butyl acrylate
a


245
78.7% C22H45
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Hexadecyl acrylate
a


246
78.7% C22H45
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Octyldodecyl
a







acrylate



247
78.7% C22H45
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% Isostearyl acrylate
a


248
78.7% C22H45
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


249
78.7% C22H45
2.7% MAPTAC
4.8% HDDMA
9% B250MA
4.8% C30 α-olefin
a


250
78.7% C22H45
2.7% MAPTAC
4.8% DDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


251
78.7% C22H45
2.7% MAPTAC
4.8% DDDMA
9% B250MA
4.8% C30 α-olefin
a


252
78.7% C22H45
2.7% MAPTAC
4.8% TMPTA
9% B250MA
4.8% C26-C28 α-olefin
a


253
78.7% C22H45
2.7% MAPTAC
4.8% TMPTA
9% B250MA
4.8% C30 α-olefin
a


254
78.7% C22H45
3% MAPTAC
1% HDDMA/TMPTA
10% B250MA

a


255
78.7% C22H45
2.7% MAPTAC
4.8% HDDMA/TMPTA
9% B250MA
4.8% C26-C28 α-olefin
a


256
78.7% C22H45
3% MAPTAC
1% HDDMA
10% T250MA

a


257
78.7% C22H45
3% MAPTAC
1% HDDMA
10% T080MA

a


258
78.7% C22H45
3% MAPTAC
1% HDDMA
10% LA070MA

a


259
86.1% C22H45
3% MAPTAC
1% HDDMA

9.9% Butyl acrylate
a


260
86.1% C22H45
3% MAPTAC
1% HDDMA

9.9% Hexadecyl acrylate
a


261
86.1% C22H45
3% MAPTAC
1% HDDMA

9.9% Octyldodecyl
a







acrylate



262
86.1% C22H45
3% MAPTAC
1% HDDMA

9.9% Isostearyl acrylate
a


263
86.1% C22H45
3% MAPTAC
1% HDDMA

9.9% C26-C28 α-olefin
a


264
86.1% C22H45
3% MAPTAC
1% HDDMA

9.9% C30 α-olefin
a


265
78.2% C22H45
3.6% AOETAC/
4.7% HDDMA/TMPTA
9% B250MA
4.7% C26-C28 α-olefin
a




MAPTAC






266
97% C22H45
3% DADMAC



a


267
97% C22H45
2% DADMAC
1% HDDMA


a


268
97% C22H45
2% DADMAC
1% DDDMA


a


269
97% C22H45
2% DADMAC
1% TMPTA


a


270
86% C22H45
3% DADMAC
1% HDDMA
10% B250MA

a


271
78.7% C22H45
2.7% DADMAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
a


272
78.7% C22H45
2.7% DADMAC
4.8% HDDMA
9% B250MA
4.8% C30 α-olefin
a


273
97% C18H37
3% AOETAC



b1


274
92.4% C18H37
2.8% AOETAC
4.8% HDDMA


b1


275
92% C18H37
3% AOETAC


5% Lauryl methacrylate
b1


276
87% C18H37
3% AOETAC


10% Lauryl methacrylate
b1


277
82% C18H37
3% AOETAC


15% Lauryl methacrylate
b1


278
97% C18H37
3% AOETAC



b2


279
92.4% C18H37
2.8% AOETAC
4.8% HDDMA


b2


280
86% C18H37
3% AOETAC
1% HDDMA
10% B250MA

b2


281
92% C18H37
3% AOETAC

5% B250MA

b2


282
87% C18H37
3% AOETAC

10% B250MA

b2


283
82% C18H37
3% AOETAC

15% B250MA

b2


284
77% C18H37
3% AOETAC

20% B250MA

b2


285
78.7% C18H37
2.7% AOETAC
4.8% HDDMA
9% B250MA
4.8% C26-C28 α-olefin
b2









Cosmetic formulations below were prepared with copolymers of the invention:


Example 1
W/O Cream

















A
Liquid paraffin
12.50%




Isopropyl palmitate
7.50%




Soybean oil
5.00%




Magnesium stearate
1.00%




Copolymer #1
2.00%



B
Water
ad 100%



C
Preservative
q.s.










Preparation



  • I Melt components A at 80° C.

  • II Heat B to 80° C.

  • III Stir II into I

  • IV Add C at 35° C.



Example 2
W/O Cream

















A
Decyl oleate
7.50%




Squalane
7.50%




Velsan ® CCT
7.50%




Caprylic-Capric triglyceride





Isopropyl palmitate
7.50%




Magnesium stearate
0.67%




Aluminum stearate
0.33%




Copolymer #1
2.50%



B
Water
ad 100%




1,2-propylene glycol
2.00%




Magnesium sulfate
1.00%



C
Preservative
q.s.




Tocopherol acetate
0.10%










Preparation



  • I Melt components A at 80° C.

  • II Mix components B and heat to 80° C.

  • III Stir II into I

  • IV Add C at 35° C.



Example 3
W/O Cream

















A
Polyglyceryl-2 sesquiisostearate
2.00%




Liquid paraffin
12.50%




Isopropyl palmitate
7.50%




Soybean oil
5.00%




Magnesium stearate
1.00%




Copolymer #1
2.00%



B
Water
ad 100%



C
Preservative
q.s.










Preparation



  • I Melt components A at 80° C.

  • II Heat component B to 80° C.

  • III Stir II into I

  • IV Add C at 35° C.



Example 4
W/O Cream

















A
Polyglyceryl-2 sesquiisostearate
2.00%




Beeswax
1.00%




Microcrystalline wax
1.00%




Liquid paraffin
12.50%




Isopropyl palmitate
7.50%




Soybean oil
5.00%




Magnesium stearate
1.00%




Copolymer #1
1.00%



B
Water
ad 100



C
Preservative
q.s.










Preparation



  • I Melt components A at 80° C.

  • II Heat component B to 80° C.

  • III Stir II into I

  • IV Add C at 35° C.



Example 5
W/O Cream

















A
Beeswax
2.00%




Microcrystalline wax
3.00%




Liquid paraffin
12.50%




Isopropyl palmitate
7.50%




Soybean oil
5.00%




Magnesium stearate
1.00%




Copolymer #1
1.00%



B
Water
ad 100



C
Preservative
q.s.










Preparation



  • I Melt components A at 80° C.

  • II Heat component B to 80° C.

  • III Stir II into I

  • IV Add C at 35° C.



Example 6
Cream Rinse

















A
Hostacerin ® T3
1.50%




Ceteareth-3





Cetyl alcohol
3.00%




Copolymer #30
1.00%




Genamin ® CTAC
2.30%




Cetrimonium Chloride




B
Water
ad 100%



C
Citric acid
q.s.










Preparation



  • I Melt components A at 80° C.

  • II Add C to B to a pH of 3.7, and heat to 80° C.

  • III Stir II into I, continue stirring until cooling to 35° C.



Example 7
Cream Rinse

















A
Hostacerin ® T3
1.50%




Ceteareth-3





Cetyl alcohol
3.00%




Copolymer #30
0.50%




Genamin ® CTAC
1.65%




Cetrimonium chloride




B
Water
ad 100%



C
Citric acid
q.s.










Preparation



  • I Melt components A at 80° C.

  • II Add C to B to a pH of 3.7

  • III Heat II to 80° C.

  • IV Stir III into I, continue stirring until cooling to 35° C.



Example 8
Sun Protection Cream Gel

















A
Tegosoft ® TN
8.00%




C12-15 alkyl benzoate





Velsan ® CCT
5.00%




Capryl-capric triglyceride





Eusolex ® OCR
9.00%




Octocrylene





Eusolex ® 2292
7.00%




Ethylhexyl methoxycinnamate





Eusolex ® 9020
2.50%




Butyl methoxydibenzoylmethane





Cetearyl alcohol
1.00%




Emulsogen ® HCO 040
1.00%




PEG-40 hydrogenated castor oil





Copolymer # 1
2.00%




Phenonip ®
q.s.




Phenoxyethanol, methylparaben,





ethylparaben, butylparaben,





propylparaben, isobutylparaben




B
Water
ad 100.00%










Preparation



  • I Melt components A at 70° C.

  • II Heat component B to 70° C.

  • III Stir II into I



Example 9
Cream Rinse

















A
Dow Corning ® 5200
1.00%




Laurylmethicone copolyol





Cetyl ester
1.00%




Cetearyl alcohol
3.00%



B
Genamin ® KDMP
0.50%




Behentrimonium chloride





Copolymer # 30
1.00%



C
Water
ad 100.00%




Preservative
q.s.




Hydrotriticum WQ
1.00%



D
Fragrance
0.30%




Dye
q.s.




Dow Corning ® 949
2.00%




Amodimethicone cetrimonium





chloride trideceth-12











Preparation



  • I Melt components A at 75° C.

  • II Stir B into C and heat to 75° C.

  • III Stir II into I, continue stirring until cooling to 30° C.

  • IV Add D at a temperature of 30° C. to III

  • V Adjust IV to pH 4.0



Example 10
Cream Rinse

















A
Hostacerin ® DGI
1.50%




Polyglyceryl-2 sesquiisostearate





Cetyl alcohol
4.00%



B
Genamin ® BTLF
2.30%




Behentrimonium chloride





Copolymer #30
1.00%




Water
ad 100%



C
Fragrance
0.30%




Preservative
q.s.




Dye
q.s.




SilCare ® Silicone SEA
1.00%




Trideceth-9 PG-Amodimethicone





Trideceth-12











Preparation



  • I Melt components A at 70° C.

  • II Heat components B to 70° C.

  • III Stir II into I, continue stirring until cooling to 30° C.

  • IV Add C at 30° C. to III

  • V Adjust IV to pH 4.0



Example 11
Child Sun Protection

















A
Abil ® EM 90
2.00%




Cetyl PEG/PPG-10/1 dimethicone





Dow Corning ® 246
11.00%




Cyclopentasiloxane/





Cyclohexasiloxane





Titanium dioxide UV Titan M 262
10.00%




Titanium dioxide/Aluminum oxide/





Stearic acid





Crodamol AB
12.00%




C12-15 alkylbenzoate





Zinc oxide HP1
4.00%




Zinc oxide





1,3-butanediol
3.00%




Butylene glycol





Abil ® WE09
6.00%




Hexyl laurate/





Polyglyceryl-4 isostearate/





cetyldimethicone





Copolymer #1
0.50%




Aluminum/Magnesium hydroxide
0.50%




stearate





Aluminum stearate
0.50%




Cutina ® HR
0.50%




hydrogenated castor oil




B
Water
ad 100%




Glycerol
5.00%




Ginkgo Biloba extract (liquid)
0.70%




Sodium carboxymethyl betaglutan
0.20%




Polyglucose





Aquamollin BC powder Hoko
0.20%




Disodium EDTA




C
Phenonip ® ME
0.80%




Methyl-/propylparaben/





phenoxyethanol





Sodium chloride
1.00%




Aluminum hydroxide
0.30%










Preparation



  • I Melt components A at 80° C.

  • II Heat components B to 80° C.

  • III Stir II into I

  • IV Add C to III after cooling to 35° C.



Example 12
Liquid Paraffin Gel


















Copolymer #277
 5.00%



Liquid paraffin
95.00%










Preparation



  • I Mix and heat the components until a homogeneous solution is obtained



The gel was assessed after cooling to room temperature. The resulting oil gel was colorless and transparent to slightly opaque.


Example 13
Thickening of Velsan® CCT (Capric/Caprylic Triglyceride, Clariant)


















Copolymer #60
 5.00%



Velsan ® CCT
95.00%



Caprylic/capric triglyceride










Preparation



  • I Mix and heat the components until a homogeneous solution is obtained



The gel was assessed after cooling to room temperature. The resulting oil gel was amber and transparent to slightly opaque.


Example 14
Thickening of Rapeseed Oil Methyl Ester


















Copolymer #40
 5.00%



Rapeseed oil methyl ester
95.00%










Preparation



  • I Mix and heat the components until a homogeneous solution is obtained



The gel was assessed after cooling to room temperature. The resulting oil gel was deep yellow and transparent to slightly opaque.


Example 15
Thickening of a Sunflower Oil/Soya Oil (23:77% by Weight) Mixture


















Copolymer #52
 5.00%



Sunflower oil/Soya oil
95.00%










Preparation



  • I Mix and heat the components until a homogeneous solution is obtained



The gel was assessed after cooling to room temperature. The resulting oil gel was yellow and transparent to slightly opaque.


Example A

Formulation examples 1-5, 8, and 11 were repeated, but replacing polymer #1 in each case by polymers #4, 25, 30, 31, 33, 39, 40, 44, 52, 60, 111, 273, 275, 276, 277, 278, and 282 from Table A in equal quantity. These formulations were stored at 40° C. and held at this temperature for six weeks. Stable formulations were obtained.


Example B

Formulation examples 6, 7, 9, and 10 were repeated, replacing polymer #30 by polymers #1, 4, 25, 31, 33, 39, 40, 44, 52, 60, 111, 273, 275, 276, 277, 278, and 282 from Table A in equal quantity. Homogeneous cream rinses were obtained.


Example C

In formulation examples 12-15, alternatively, 2% by weight of the corresponding polymers and 98% by weight of oil were used. Even with the reduced polymer fraction, good to very good thickening properties were achieved.


Example D

Formulation examples 12-15 were repeated, using in formulation example 12, instead of polymer #277, the polymers #1, 4, 25, 30, 31, 33, 39, 40, 44, 52, 60, 111, 273, 275, 276, 278, and 282; in formulation example 13, instead of polymer #60, polymers #1, 4, 25, 30, 31, 33, 39, 40, 44, 52, 111, 273, 275, 276, 277, 278, and 282, in formulation example 14, instead of polymer #40, polymers #1, 4, 25, 30, 31, 33, 39, 44, 52, 60, 111, 273, 275, 276, 277, 278, and 282, in formulation example 15, instead of polymer #52, polymers #1, 4, 25, 30, 31, 33, 39, 40, 44, 60, 111, 273, 275, 276, 277, 278, and 282, from Table A, in equal quantity. The oil gels were assessed visually at 20° C. as being clear and transparent to slightly opaque.


Example E

The formulation examples from example D were repeated, but using, instead of 5% by weight of the corresponding polymer, in each case 2% by weight of polymer and 98% by weight of oil. Even with the reduced polymer fraction, good to very good thickening properties were achieved.


Example F

The formulation examples from example A-E were repeated, using, instead of the polymers used in examples A-E, the polymers #121, 123, 132, 135, 136, 140, 141, 145, 147, 189, 197, 199, 208, 211, 212, 216, 217, 221, 223, and 265 from Table A, in equal quantity.


Chemical or INCI designation of the trade names or abbreviations used

  • AMA Allyl methacrylate
  • AOETAC 2-(Acryloyloxy)ethyl]trimethylammonium chloride
  • APTAC [3-Acrylamidopropyl]trimethylammonium chloride
  • B250MA Behenyl methacrylate, ethoxylated with 25 EO units
  • BDDMA Buanediol dimethacrylate
  • DADMAC Diallyldimethylammonium chloride
  • DDDMA Dodecanediol dimethacrylate
  • EDDMA Ethanediol dimethacrylate
  • HDDMA Hexanediol dimethacrylate
  • HEMA 2-Hydroxyethyl methacrylate
  • LA070MA Lauryl methacrylate, ethoxylated with 7 EO units
  • MAOETAC [2-(Methacryloyloxy)ethyl]trimethylammonium chloride
  • MAPTAC [3-Methacrylamidopropyl]trimethylammonium chloride
  • MBA Methylene-bis-acrylamide
  • PEG diacrylate Polyethylene glycol diacrylate having an average
  • molecular weight Mn=575
  • Poly-NVP Poly-N-vinylpyrrolidone
  • T080MA Talyl methacrylate, ethoxylated with 8 EO units
  • T250MA Talyl methacrylate, ethoxylated with 25 EO units
  • TEMPO 2,2,6,6-Tetramethylpiperidinyloxyl
  • TMPTA Trimethylolpropane triacrylate
  • TMPTMA Trimethylolpropane trimethacrylate

Claims
  • 1. A cosmetic, pharmaceutical or dermatological formulation comprising a copolymer comprising a) 60.0%-99.9% by weight of at least one structural unit originating from at least one polymerizable compound selected from group consisting of the structural formulae (Ia) and (Ib)
  • 2. (canceled)
  • 3. (canceled)
  • 4. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1, wherein the at least one compound of the formula (Ia) is selected from the group consisting of lauryl acrylate, lauryl methacrylate, hexadecyl acrylate, hexadecyl methacrylate, stearyl acrylate, stearyl methacrylate, isostearyl acrylate, isostearyl methacrylate, octyldodecyl acrylate, octyldodecyl methacrylate, behenyl acrylate and behenyl methacrylate, and the at least one compound of the formula (Ib) is selected from the group consisting of acrylic ester of lauryl alcohol with 7 EO units, methacrylic ester of lauryl alcohol with 7 EO units, acrylic ester of talyl alcohol with 8 EO units, methacrylic ester of talyl alcohol with 8 EO units, acrylic ester of talyl alcohol with 25 EO units, methacrylic ester of talyl alcohol with 25 EO units, acrylic ester of behenyl alcohol with 25 EO units, and methacrylic ester of behenyl alcohol with 25 EO units.
  • 5. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1, wherein R2 in the at least one compound of the formulae (Ia) and (Ib) is a linear or branched, saturated alkyl radical having 12 to 200 carbon atoms.
  • 6. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1, wherein the at least one structural unit of component b) originates from at least one substance selected from the group consisting of b1) at least one polymerizable quaternary ammonium compound of the following structural formula (II) X−+NR7R8R9R10  (II)whereinX− is a negatively charged counterion,R7 is vinyl radical, allyl radical or a radical of the following structural formula (III)
  • 7. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 6, wherein the negatively charged counterion X− in formula (II) and (IV) is selected from the group consisting of chloride, bromide, iodide, ½ SO42− and methosulfate.
  • 8. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1, wherein the at least one structural unit of component b) originates from at least one polymerizable quaternary ammonium compound selected from the group consisting of diallyldimethylammonium chloride (DADMAC), [2-(methacryloyloxy)ethyl]trimethylammonium chloride (MAOETAC), [2-(acryloyloxy)ethyl]trimethylammonium chloride (AOETAC), [2-methacrylamidoethyl]trimethylammonium chloride, [2-(acrylamido)ethyl]trimethylammonium chloride, [3-methacrylamidopropyl]trimethylammonium chloride (MAPTAC), [3-acrylamidopropyl]trimethylammonium chloride (APTAC), N-methyl-2-vinylpyridinium chloride, N-methyl-4-vinylpyridinium chloride, and N-methyl-3-vinylimidazolinium chloride.
  • 9. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 6, wherein the at least one structural unit of component b) originates from at least one polymerizable quaternary ammonium compound of formula (II).
  • 10. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1, comprising at least one structural unit of component c) that originates from substances selected from the group consisting of monomers having more than one polymerizable group, which may have a crosslinking effect.
  • 11. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1, wherein the at least one structural unit of component c) originates from substances selected from the group consisting of divinylbenzene, methylenebisacrylamide (MBA), triallylamine, triallyl cyanurate, ethanediol diacrylate, ethanediol dimethacrylate (EDDMA), buanediol diacrylate, buanediol dimethacrylate (BDDMA), hexanediol diacrylate, hexanediol dimethacrylate (HDDMA), dodecanediol diacrylate, dodecanediol dimethacrylate (DDDMA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane trimethacrylate (TMPTMA), glycerol diacrylate, glycerol dimethacrylate, tetraethylene glycol diacrylate, tetraethylene glycol dimethacrylate, polyethylene glycol diacrylate with molar masses between 400 and 800 g/mol, polyethylene glycol dimethacrylate with molar masses between 400 and 800 g/mol, allyl acrylate, methacrylate or ethacrylate, preferably allyl acrylate or methacrylate, and more particularly allyl methacrylate (AMA), dipropylene glycol diallyl ether, polyglycol diallyl ether, hydroquinone diallyl ether, trimethylolpropane diallyl ether, trimethylolpropane triallyl ether, tetraallyloxyethane, triethylene glycol divinyl ether, other allyl ethers or vinyl ethers of polyfunctional alcohols, and mixtures thereof.
  • 12. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1, wherein, the amount of structural units of component a) is from 60.0% to 99.5% by weight, the amount of structural units of component b) is from 0.5% to 20.0% by weight, and the amount of structural units of component c) is from 0% to 20.0% by weight.
  • 13. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1, wherein the amount of structural units of component a) is from 80.0% to 98.0% by weight, the amount of structural units of component b) is from 0.7% to 11.0% by weight, and the amount of structural units of component c) is from 0% to 11.0% by weight.
  • 14. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 3, wherein the weight ratio of structural units originating from the compounds of the formula (Ia) to structural units originating from the compounds of the formula (Ib) in the copolymer is 1.0:0 to 0.8.
  • 15. (canceled)
  • 16. The cosmetic, pharmaceutical or dermatological formulation wherein the copolymer as claimed in claim 1, consists of components a) and b).
  • 17. The cosmetic, pharmaceutical or dermatological formulation wherein the copolymer as claimed in claim 1, consists of components a), b), and c).
  • 18. The cosmetic, pharmaceutical or dermatological formulation as claimed in claim 17, wherein the structural units of component c) are selected from crosslinking structural units.
  • 19. A process for preparing the copolymer as claimed in claim 1, comprising the step of radically polymerizing the monomers.
  • 20. (canceled)
  • 21. A process for thickening oil comprising the step of adding at least one copolymer comprising a) 60.0%-99.9% by weight of at least one structural unit originating from at least one polymerizable compound selected from group consisting of the structural formulae (Ia) and (Ib)
  • 22. A process for conditioning fibers comprising the step of contacting the fibers with at least one cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1.
  • 23. A process for increasing the water resistance of sun protection formulations comprising the step of adding at least one cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1 to the sun protection formulation.
  • 24. A process for increasing the sun protection factor of sun protection formulations comprising the step of adding at least one cosmetic, pharmaceutical or dermatological formulation as claimed in claim 1 to the sun protection formulation.
  • 25. (canceled)
Priority Claims (1)
Number Date Country Kind
10 2009 015 868.5 Apr 2009 DE national
Divisions (1)
Number Date Country
Parent 13262382 Jan 2012 US
Child 14820317 US