The present disclosure relates to polymeric materials that may be formed to produce a container, in particular polymeric materials that insulate. More particularly, the present disclosure relates to morphology and crystalline structure of cellular polymeric material that may be transformed into usable articles, such as insulated containers.
An insulated container in accordance with the present disclosure, which may be a drink cup or a food-storage cup (e.g.), is manufactured from a sheet extrudate or tubular extrudate produced in an extrusion process. In illustrative embodiments, the extrudate is a cellular polymeric material.
In illustrative embodiments, an insulative container in accordance with the present disclosure is manufactured from a tubular extrudate produced in an extrusion process. In illustrative embodiments, the extrudate is an insulative cellular polypropylene-based material configured to crease and/or wrinkle during cup convolution or shaping.
In illustrative embodiments, the cell morphology of an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure is a function of the extrusion angle, which has an effect on the quality of an article, such as an insulative container, formed therewith. In particular, cell morphology is affected by the angle at which a polypropylene-based material in accordance with the present disclosure exits an enclosed die volume through extruder die lips, and is related to deep creasing and/or wrinkling in the formed article.
In illustrative embodiments, the cell morphology of an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure is a function of formulation and process conditions, which conditions have an effect on the quality of an article, such as an insulative container, formed therewith. In particular, the effects of such conditions on cell density and cell dimensional attributes, and ultimately on creasing/wrinkling, results in a wrinkle prediction model based on power law regression.
In illustrative embodiments, the cell aspect ratio of insulative cellular polypropylene-based material in accordance with the present disclosure has an effect on the wrinkling of that material during mechanical convolution. Parameters such as cell density and aspect ratio ultimately determine control limits that result in a wrinkling model for a mechanically convoluted container.
In illustrative embodiments, the circumferential direction cell aspect ratio of an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure has a greater effect than the cell aspect ratio in the axial direction on the wrinkling of that material during mechanical convolution.
In illustrative embodiments, the orientation of an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure has an effect on the wrinkling of that material during mechanical convolution. In particular, when formed into a circular article, the sheet may be oriented such that the circumference of the circular article represents −45° to +45° perpendicular to the direction of flow for the material of the sheet. The effects of parameters such as sheet orientation in formed circular articles affect the cell morphology of articles, and the cell morphology of the articles ultimately influence their tendency to wrinkle.
Additional features of the present disclosure will become apparent to those skilled in the art upon consideration of illustrative embodiments exemplifying the best mode of carrying out the disclosure as presently perceived.
The detailed description particularly refers to the accompanying figures in which:
One feature of of an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure is the ability of the sheet to form a surface with noticeable creases and wrinkles when curved to form a round article, such as an insulative cup. The surface may be wrinkled inside the cup, where compression forces may cause material to crush and/or crease easily, especially for low density material with a large cell aspect ratio. In exemplary embodiments, the surface profile of a cup made from an extruded sheet of insulative cellular polypropylene-based material as detected by microscopy is such that there is at least one indentation (i.e., creases and/or wrinkles) that is about 5 microns or more naturally occurring in the outside and/or inside of the cup surface when it is subject to extension and compression forces during cup forming. In one exemplary embodiment, the surface profile may include indentations of about 50 microns or more. In another exemplary embodiment, the surface profile may include indentations of about 100 microns or more. At a depth of about 10 microns and less, micro-wrinkles and/or creases on a cup surface are ordinarily not visible to the naked eye.
In one exemplary embodiment, an insulative cup formed from a sheet comprising a skin and a strip of insulative cellular polypropylene-based material in accordance with the present disclosure had typical creases (i.e., deep wrinkles) about 200 microns deep extending from the top of the cup to the bottom of the cup. In another exemplary embodiment, an insulative cup formed from a sheet comprising a strip of insulative cellular polypropylene-based material only (without a skin) in accordance with the present disclosure had typical creases about 200 microns deep extending from the top of the cup to the bottom of the cup. Such creases with depths from about 100 microns to about 500 microns are typically formed inside of a cup undergoing compression. Creases may form in instances where sheets include a skin or exclude a skin.
It was unexpectedly found that the cell morphology of an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure has an effect on the quality of the formed article, such as an insulative cup. The effects of cell morphology on a tendency of insulative cellular polypropylene-based material to wrinkle during convolution may be illustrated through examining the effect of varying the angle of the extruder die lips. In exemplary embodiments, the angle at which insulative cellular polypropylene-based material in accordance with the present disclosure exits an enclosed volume may affect the material's tendency to wrinkle. It was found that for a specified formulation of insulative cellular polypropylene-based material and specified cup forming conditions, different die exit angles lead to noticeably different levels of creasing and/or wrinkling in article surfaces during extruded sheet convolution. The two geometric exit angles selected for examination in the present disclosure are those commonly used in polyethylene foam production, i.e., an exit angle of 90°, and in polystyrene foam production, i.e., an exit angle of 44° (see, Example 1).
In exemplary embodiments, insulative cellular polypropylene-based material in accordance with the present disclosure may be extruded as sheet. Microscopy images show that distinct cell morphology exists, i.e., cell structure distinctions, within insulative cups made from such extruded sheets when one sheet is produced with a higher curvature die exit angle and the other with a lower curvature die exit angle. Insulative cups may be made by cutting the sheets such that the resulting circumference of the insulative cup is aligned to be perpendicular or parallel to the direction the sheets are extruded. The difference in cell morphology between cups cut in the two directions may be detected by examining portions cut from the axial sides of the cups under a microscope.
Direct evidence of polymer cell structure is provided by microscopy studies. There is a close relationship between the regularity of molecular structure and malleability. Cell morphology describes polymer cell density, cell structure, cell wall thickness, cell shape, and cell size distribution of cells. Polymer cell structures may have the same general shape and appearance, being composed predominantly of ovular cells, and the same lognormal cell distribution, but possess a different cell aspect ratio and cell wall thickness. Illustratively, cell aspect ratio is the ratio between lengths of the ovular polymer cells to widths of the ovular polymer cells. Illustratively, cell wall thickness is the solid polymeric distance between individual polymer cells.
In one exemplary embodiment, an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure may exit from an enclosed die volume at an angle of 90°. In another exemplary embodiment, an extruded sheet of insulative cellular polypropylene-based material may exit from an enclosed die volume at an angle of 44°. Illustratively, an extruded sheet of insulative cellular polypropylene-based material may exit from an enclosed die volume at an angle between 44° and 90°. Two such sheets, one produced at an exit angle of 44° and the other at an exit angle of 90°, may be prepared as strips either in the machine direction or in the cross direction and analyzed with digital microscopy. Cell density, cell distribution, cell shape, cell aspect ratio, and cell wall thickness of an extruded sheet may be held constant when extrusion parameters such as recipe, temperature, and cooling rate are the same. In the present disclosure, formation of wrinkled material was found to occur when the exit angle of curvature increased from 44° to 90° (see, Example 1,
The disclosure herein provides methods of producing an insulative cellular material. In an embodiment, the insulative cellular material is polypropylene based. In an embodiment, the insulative cellular material produces wrinkles and/or creases during mechanical convolution. In an embodiment, a method of producing an insulative cellular material includes extruding a formulation as disclosed herein through an extruder die lips at an exit angle from about 0° to about 60°. In an embodiment, the formulation is extruded through die lips at an angle of about 0° to about 10°, about 10° to about 20°, about 20° to about 30°, about 30° to about 40°, about 40° to about 50°, about 50° to about 60°, about 40° to about 45°, 0° to about 20°, 0° to about 30°, 0° to about 40°, 0° to about 50°, about 10° to about 60°, about 10° to about 50°, about 10° to about 40°, about 10° to about 30°, about 20° to about 60°, about 20° to about 50°, about 20° to about 40°, about 30° to about 60°, about 30° to about 50°, or about 40° to about 60°. An embodiment includes the method wherein the die exit angle may be about 10°, 20°, 30°, 40°, 41°, 42°, 43°, 44°, 45°, 46°, 47°, 48°, 49°, 50°, or 60°.
In an embodiment of a method of producing an insulative cellular material, wherein the formulation comprises i) a first polymer material comprising at least one high melt strength polypropylene homopolymer, and ii) a second polymer material comprising at least one polymer selected from the group consisting of crystalline polypropylene homopolymer, impact polypropylene copolymer, and mixtures thereof. In an embodiment, the formulation further comprises at least one nucleating agent. In an embodiment, the formulation further comprises at least one slip agent. In an embodiment of a method of producing an insulative cellular material, cell dimensional attributes are according to y=AxK, wherein either x or y is cell density of the insulative cellular polypropylene-based material and the non-cell density variable is cell length, cell width, or cell wall thickness of the insulative cellular polypropylene-based material.
It was unexpectedly found that cell morphology, especially cell density, of an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure has an effect on the quality of the formed article, such as a cup, formed therewith. The effects of cell density and dimensional attributes on wrinkling in insulative cellular polypropylene-based material may be illustrated through examining cell morphology data from different formulations and process conditions, thus creating a wrinkling prediction model based on power law regression.
In exemplary embodiments, the cell density of insulative cellular polypropylene-based material in accordance with the present disclosure may affect the material's tendency to wrinkle during mechanical convolution. In other exemplary embodiments, the total number of cells of insulative cellular polypropylene-based material may affect the material's tendency to wrinkle during mechanical convolution. In other exemplary embodiments, the cell aspect ratio in the circumferential direction 10 of an insulative cup 12, may affect the material's tendency to wrinkle during mechanical convolution. In other exemplary embodiments, the cell aspect ratio in the axial direction 20 of an insulative cup 12, may affect the material's tendency to wrinkle during mechanical convolution.
As shown in
Insulative cup 12 includes a sheet of insulative cellular non-aromatic polymeric material made according to a material-forming process 100 as shown in
As shown in
In exemplary embodiments, a physical blowing agent may be introduced and mixed into molten resin 122 after molten resin 122 is established. In exemplary embodiments, as discussed further herein, the physical blowing agent may be a gas introduced as a pressurized liquid via a port 115A and mixed with molten resin 122 to form a molten extrusion resin mixture 123 as shown in
Extrusion resin mixture 123 is conveyed by screw 114 into a second extrusion zone included in second extruder 112 as shown in
A blank 200 used to form a portion of insulative cup 10 is shown in phantom in
In other exemplary embodiments, the cell length of insulative cellular polypropylene-based material may affect the material's tendency to wrinkle during mechanical convolution. When cells are measured in the circumferential direction 10, cell length is the circumferential distance in the circumferential direction 10. When cells are measured in the axial direction 20, cell length is the axial distance in the axial direction 20.
In other exemplary embodiments, the cell width of insulative cellular polypropylene-based material may affect the material's tendency to wrinkle during mechanical convolution. Cell width is the maximum radial distance measured in a radial direction. In other exemplary embodiments, the cell wall thickness of insulative cellular polypropylene-based material may affect the material's tendency to wrinkle during mechanical convolution. In other exemplary embodiments, cell dimensional attributes may follow a power law that is independent of formula and processing conditions (see, Example 2,
The insulative cellular polypropylene-based material of the present disclosure may be formed into an article, such as an insulative cup, that includes the features of a tendency to wrinkle and/or crease during mechanical convolution as described herein, and may include many, if not all, of the features of insulative performance, recyclability, puncture resistance, frangibility resistance, and microwavability, which features are described in U.S. patent application Ser. Nos. 13/491,007 and 13/491,327 both of which are incorporated herein by reference in their entirety.
Nucleating agent means a chemical or physical material that provides sites for cells to form in a molten formulation mixture. Nucleating agents may include chemical nucleating agents and physical nucleating agents. The nucleating agent may be blended with the formulation that is introduced into the hopper of the extruder. Alternatively, the nucleating agent may be added to the molten resin mixture in the extruder.
Suitable physical nucleating agents have desirable particle size, aspect ratio, and top-cut properties. Examples include, but are not limited to, talc, CaCO3, mica, and mixtures of at least two of the foregoing. One representative example is Heritage Plastics HT6000 Linear Low Density Polyethylene (LLDPE) Based Talc Concentrate.
Suitable chemical nucleating agents decompose to create cells in the molten formulation when a chemical reaction temperature is reached. These small cells act as nucleation sites for larger cell growth from a physical or other type of blowing agent. In one example, the chemical nucleating agent is citric acid or a citric acid-based material. One representative example is HYDROCEROL™ CF-40E (available from Clariant Corporation), which contains citric acid and a crystal nucleating agent.
A blowing agent refers to a physical or a chemical blowing agent (or combination of materials) that acts to expand nucleation sites. Blowing agents may include only chemical blowing agents, only physical blowing agents, combinations thereof, or several types of chemical and physical blowing agents. The blowing agent acts to reduce density by forming cells in the molten formulation at the nucleation sites. The blowing agent may be added to the molten resin mixture in the extruder.
Chemical blowing agents are materials that degrade or react to produce a gas. Chemical blowing agents may be endothermic or exothermic. Chemical blowing agents typically degrade at a certain temperature to decompose and release gas. One example of a chemical blowing agent is citric acid or citric-based material. One representative example is HYDROCEROL™ CF-40E (available from Clariant Corporation), which contains citric acid and a crystal nucleating agent. Here, the citric acid decomposes at the appropriate temperature in the molten formulation and forms a gas which migrates toward the nucleation sites and grows cells in the molten formulation. If sufficient chemical blowing agent is present, the chemical blowing agent may act as both the nucleating agent and the blowing agent.
In another example, chemical blowing agents may be selected from the group consisting of azodicarbonamide; azodiisobutyro-nitrile; benzenesulfonhydrazide; 4,4-oxybenzene sulfonylsemicarbazide; p-toluene sulfonyl semi-carbazide; barium azodicarboxylate; N,N′-dimethyl-N,N′-dinitrosoterephthalamide; trihydrazino triazine; methane; ethane; propane; n-butane; isobutane; n-pentane; isopentane; neopentane; methyl fluoride; perfluoromethane; ethyl fluoride; 1,1-difluoroethane; 1,1,1-trifluoroethane; 1,1,1,2-tetrafluoro-ethane; pentafluoroethane; perfluoroethane; 2,2-difluoropropane; 1,1,1-trifluoropropane; perfluoropropane; perfluorobutane; perfluorocyclobutane; methyl chloride; methylene chloride; ethyl chloride; 1,1,1-trichloroethane; 1,1-dichloro-1-fluoroethane; 1-chloro-1,1-difluoroethane; 1,1-dichloro-2,2,2-trifluoroethane; 1-chloro-1,2,2,2-tetrafluoroethane; trichloromonofluoromethane; dichlorodifluoromethane; trichlorotrifluoroethane; dichlorotetrafluoroethane; chloroheptafluoropropane; dichlorohexafluoropropane; methanol; ethanol; n-propanol; isopropanol; sodium bicarbonate; sodium carbonate; ammonium bicarbonate; ammonium carbonate; ammonium nitrite; N,N′-dimethyl-N,N′-dinitrosoterephthalamide; N,N′-dinitrosopentamethylene tetramine; azodicarbonamide; azobisisobutylonitrile; azocyclohexylnitrile; azodiaminobenzene; bariumazodicarboxylate; benzene sulfonyl hydrazide; toluene sulfonyl hydrazide; p,p′-oxybis(benzene sulfonyl hydrazide); diphenyl sulfone-3,3′-disulfonyl hydrazide; calcium azide; 4,4′-diphenyl disulfonyl azide; p-toluene sulfonyl azide; and combinations thereof.
In an illustrative embodiment, a nucleating agent may be about 0.1% to about 20% (w/w), about 0.25% to about 20%, about 0.5% to about 20%, about 0.75% to about 20%, about 1% to about 20%, about 1.5% to about 20%, about 2% to about 20%, about 2.5% to about 20%, about 3% to about 20%, about 3% to about 20%, about 4% to about 20%, about 4.5% to about 20%, about 5% to about 20%, about 0.1% to about 10%, about 0.25% to about 10%, about 0.5% to about 10%, about 0.75% to about 10%, about 1.0% to about 10%, about 1.5% to about 10%, about 1.0% to about 10%, about 2.0% to about 10%, about 2.5% to about 10%, about 3.0% to about 10%, about 3.5% to about 10%, about 4.0% to about 10%, about 4.5% to about 10%, about 5.0% to about 10%, about 0.1% to about 5%, about 0.25% to about 5%, about 0.5% to about 5%, about 0.75% to about 5%, about 1% to about 5%, about 1.5% to about 5%, about 1% to about 5%, about 2% to about 5%, about 2.5% to about 5%, about 3% to about 5%, about 3.5% to about 5%, or about 4% to about 5%, or about 4.5% to about 5%. In an embodiment, a nucleating agent may be about 0.5%, about 1%, about 1.5%, about 2%, about 2.5%, about 3%, about 4%, or about 5% (w/w). In an embodiment, the polymeric material lacks a nucleating agent. In an embodiment, the polymeric material lacks talc.
In an illustrative embodiment, a chemical blowing agent may be about 0 to about 5% (w/w), about 0.1% to about 5% (w/w), about 0.25% to about 5%, about 0.5% to about 5%, about 0.75% to about 5%, about 1% to about 5%, about 1.5% to about 5%, about 2% to about 5%, about 3% to about 5%, about 4% to about 5%, 0 to about 4% (w/w), about 0.1% to about 4% (w/w), about 0.25% to about 4%, about 0.5% to about 4%, about 0.75% to about 4%, about 1% to about 4%, about 1.5% to about 4%, about 2% to about 4%, about 3% to about 4%, 0 to about 3% (w/w), about 0.1% to about 3% (w/w), about 0.25% to about 3%, about 0.5% to about 3%, about 0.75% to about 3%, about 1% to about 3%, about 1.5% to about 3%, about 2% to about 3%, 0 to about 2%, about 0.1% to about 2% (w/w), about 0.25% to about 2%, about 0.5% to about 2%, about 0.75% to about 2%, about 1% to about 2%, about 1.5% to about 2%, 0 to about 1%, about 0.1% to about 1%, about 0.5% to about 1%, or about 0.75% to about 1%. In an illustrative embodiment, a chemical blowing agent may be about 0.1%, 0.5%, 0.75%, 1%, 1.5% or about 2%. In one aspect of the present disclosure, where a chemical blowing agent is used, the chemical blowing agent may be introduced into the material formulation that is added to the hopper.
One example of a physical blowing agent is nitrogen (N2). The N2 is pumped into the molten formulation via a port in the extruder as a supercritical fluid. The molten material with the N2 in suspension then exits the extruder via a die where a pressure drop occurs. As the pressure drop happens, N2 moves out of suspension toward the nucleation sites where cells grow. Excess gas blows off after extrusion with the remaining gas trapped in the cells formed in the extrudate. Other suitable examples of physical blowing agents include, but are not limited to, carbon dioxide (CO2), helium, argon, air, pentane, butane, other alkanes, mixtures of the foregoing, and the like.
In one aspect of the present disclosure, at least one slip agent may be incorporated into the formulation to aid in increasing production rates. Slip agent (also known as a process aid) is a term used to describe a general class of materials which are added to the formulation and provide surface lubrication to the polymer during and after conversion. Slip agents may also reduce or eliminate die drool. Representative examples of slip agent materials include amides of fats or fatty acids, such as, but not limited to, erucamide and oleamide. In one exemplary aspect, amides from oleyl (single unsaturated C-18) through erucyl (C-22 single unsaturated) may be used. Other representative examples of slip agent materials include low molecular weight amides and fluoroelastomers. Combinations of two or more slip agents may be used. Slip agents may be provided in a master batch pellet form and blended with the resin formulation. One example of a suitable slip agent is Ampacet 102823 Process Aid PE MB LLDPE.
In an embodiment, a slip agent may be about 0% to about 10% (w/w), about 0.5% to about 10% (w/w), about 1% to about 10% (w/w), about 2% to about 10% (w/w), about 3% to about 10% (w/w), about 4% to about 10% (w/w), about 5% to about 10% (w/w), about 6% to about 10% (w/w), about 7% to about 10% (w/w), about 8% to about 10% (w/w), about 9% to about 10% (w/w), about 0% to about 9% (w/w), about 0.5% to about 9% (w/w), about 1% to about 9% (w/w), about 2% to about 9% (w/w), about 3% to about 9% (w/w), about 4% to about 9% (w/w), about 5% to about 9% (w/w), about 6% to about 9% (w/w), about 7% to about 9% (w/w), about 8% to about 9% (w/w), about 0% to about 8% (w/w), about 0.5% to about 8% (w/w), about 1% to about 8% (w/w), about 2% to about 8% (w/w), about 3% to about 8% (w/w), about 4% to about 8% (w/w), about 5% to about 8% (w/w), about 6% to about 8% (w/w), about 7% to about 8% (w/w), about 0% to about 7% (w/w), about 0.5% to about 7% (w/w), about 1% to about 7% (w/w), about 2% to about 7% (w/w), about 3% to about 7% (w/w), about 4% to about 7% (w/w), about 5% to about 7% (w/w), about 6% to about 7% (w/w), about 0% to about 6% (w/w), about 0.5% to about 6% (w/w), about 1% to about 6% (w/w), about 2% to about 6% (w/w), about 3% to about 6% (w/w), about 4% to about 6% (w/w), about 5% to about 6% (w/w), about 0% to about 5% (w/w), about 0.5% to about 5% (w/w), about 1% to about 5% (w/w), about 2% to about 5% (w/w), about 3% to about 5% (w/w), about 4% to about 5% (w/w), about 0% to about 4% (w/w), about 0.5% to about 4% (w/w), about 1% to about 4% (w/w), about 2% to about 4% (w/w), about 3% to about 4% (w/w), about 0% to about 3% (w/w), about 0.5% to about 3% (w/w), about 1% to about 3% (w/w), about 2% to about 3% (w/w), about 0% to about 2% (w/w), about 0.5% to about 2% (w/w), about 1% to about 2% (w/w), about 0% to about 1% (w/w), or about 0.5% to about 1% (w/w). In an embodiment, a slip agent may be about 0.5%, about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, or about 10% (w/w). In an embodiment, the formulation lacks a slip agent.
In an embodiment, a colorant may be about 0% to about 20% (w/w), about 0% to about 15% (w/w), about 0% to about 10% (w/w), about 0% to about 5% (w/w), about 0% to about 4% (w/w), about 0.1% to about 4%, about 0.25% to about 4%, about 0.5% to about 4%, about 0.75% to about 4%, about 1.0% to about 4%, about 1.5% to about 4%, about 2.0% to about 4%, about 2.5% to about 4%, about 3% to about 4%, about 0% to about 3.0%, about 0% to about 2.5%, about 0% to about 2.25%, about 0% to about 2.0%, about 0% to about 1.5%, about 0% to about 1.0%, about 0% to about 0.5%, about 0.1% to about 3.5%, about 0.1% to about 3.0%, about 0.1% to about 2.5%, about 0.1% to about 2.0%, about 0.1% to about 1.5%, about 0.1% to about 1.0%, about 1% to about 5%, about 1% to about 10%, about 1% to about 15%, about 1% to about 20%, or about 0.1% to about 0.5%. In an embodiment, a formulation lacks a colorant.
In one exemplary embodiment, a formulation used to produce the cellular polymeric material includes at least one polymeric material. The polymeric material may include one or more base resins. In one example, the base resin is polypropylene. In an illustrative embodiment, a base resin may include Borealis WB140 HMS polypropylene homopolymer. In another illustrative embodiment, a base resin may include Braskem F020HC polypropylene homopolymer. In an embodiment, a base resin may include both Borealis WB140 HMS polypropylene homopolymer and Braskem F020HC polypropylene homopolymer.
In embodiments with more than one polypropylene copolymer base resin, different polypropylene copolymers may be used depending on the attributes desired in the formulation. Depending on the desired characteristics, the ratio of two polypropylene resins may be varied, e.g., 10%/90%, 20%/80%, 25%/75%, 30%/70%, 35%/65%, 40%/60%, 45%/55%, 50%/50%, etc. In an embodiment, a formulation includes three polypropylene resins in the base resin. Again, depending on the desired characteristics, the percentage of three polypropylene resins may be varied, 33%/33%/33%, 30%/30%/40%, 25%/25%/50%, etc.
In illustrative embodiments, a polymeric material includes a primary base resin. In illustrative embodiments, a base resin may include polypropylene. In illustrative embodiments, an insulative cellular non-aromatic polymeric material comprises a polypropylene base resin having a high melt strength and a polypropylene copolymer or homopolymer (or both). In one example, the polypropylene base resin has a drawdown force greater than about 15 cN. In another example, the polypropylene base resin has a drawdown force greater than about 20 cN. In another example, the polypropylene base resin has a drawdown force greater than about 25 cN. In another example, the polypropylene base resin has a drawdown force greater than about 35 cN.
In an embodiment, a formulation of the polymeric material comprises about 50 wt % to about 100 wt %, about 70 wt % to about 100 wt %, about 50 wt % to about 99 wt %, 50 wt % to about 95 wt %, about 50 wt % to about 85 wt %, about 55 wt % to about 85 wt %, about 80 wt % to about 85 wt %, about 80 wt % to about 90 wt %, about 80 wt % to about 91 wt %, about 80 wt % to about 92 wt %, about 80 wt % to about 93 wt %, about 80 wt % to about 94 wt %, about 80 wt % to about 95 wt %, about 80 wt % to about 96 wt %, about 80 wt % to about 97 wt %, about 80 wt % to about 98 wt %, about 80 wt % to about 99 wt %, about 85 wt % to about 90 wt %, or about 85 wt % to about 95 wt % of the primary base resin. In an embodiment, a colorant may be about 80%, 81%, 82%, 83%, 84%, 85%, 86%, 87%, 88%, 89%, 90%, 91%, 92%, 93%, 94%, 95%, 96%, 97%, 98%, 99%, or 100%.
As defined hereinbefore, any suitable primary base resin may be used. One illustrative example of a suitable polypropylene base resin is DAPLOY™ WB140 homopolymer (available from Borealis A/S) which is a high melt strength structural isomeric modified polypropylene homopolymer.
In illustrative embodiments, a polymeric material includes a secondary resin, wherein the secondary resin may be a polypropylene copolymer or homopolymer (or both). In another embodiment, a secondary resin may be about 0 wt % to about 50 wt %, about 0 wt % to about 30 wt %, about 0 wt % to about 25 wt %, about 0 wt % to about 20 wt %, about 0 wt % to about 15 wt %, about 10 wt % to about 50 wt %, about 10 wt % to about 40 wt %, about 10 wt % to about 30 wt %, about 10 wt % to about 25 wt %, about 10 wt % to about 20 wt %, or about 10 wt % to about 15 wt % of a secondary resin. In an embodiment, a polymeric material includes about 0 wt %, about 10 wt %, about 15 wt %, about 20 wt %, about 25 wt %, or about 30 wt %. In an embodiment, a polymeric material does not have a secondary resin. In an embodiment, a secondary resin may be a high crystalline polypropylene homopolymer, such as F020HC (available from Braskem) or PP 527K (available from Sabic). In an embodiment, a polymeric material lacks a secondary resin.
The term die exit angle means the angle subtended by the central axis of the torpedo mandrel and the outer surface of the torpedo mandrel adjacent the exit lip of an extrusion apparatus. Such an angle may be referred to as an inner lip angle, and is commonly understood to be angle X as shown in
1.) 1-60°
2.) 10-60°
3.) 20-60°
4.) 30-60°
5.) 30-58°
6.) 32-58°
7.) 35-58°
8.) 35-56°
9.) 37-54°
10.) 40-54°
11.) 40-52°
12.) 40-50°
13.) 40-48°
14.) 42-48°
15.) 42-46°
In particular embodiments of the disclosure, the die exit angle may be formed by an inner lip angle identified as X in
16.) X is 45-60° and Y is 35-55°
17.) X is 47-58° and Y is 37-50°
18.) X is 47-56° and Y is 37-48°
19.) X is 47-54° and Y is 39-46°
20.) X is 48-54° and Y is 40-45°
21.) X is 49° and Y is 41°
22.) X is 53° and Y is 41°
In an embodiment, the process comprises extruding a formulation at any of the angles disclosed in numbered lines 1-22 above, wherein the formulation comprises:
50-100 wt % of a primary base resin
0-50 wt % of a secondary resin
0-5 wt % of a chemical blowing agent
0.1-20 wt % of a nucleating agent
0-20 wt % of a colorant
0-10 wt % of a slip agent
In an embodiment, the process comprises extruding a formulation at any of the angles defined in numbered paragraphs 1-22 above, wherein the formulation comprises:
50-100 wt % of a primary base resin
0-50 wt % of a secondary resin
0-2 wt % of a chemical blowing agent
0-20 wt % of a physical nucleating agent
0-20 wt % of a colorant
0-10 wt % of a slip agent
In an embodiment, the process comprises extruding a formulation at any of the angles disclosed in the numbered lines 1-22 above, wherein the formulation comprises:
75-85 wt % of a primary base resin
10-20 wt % of a secondary resin
0-0.1 wt % of a chemical blowing agent
0.1-3 wt % of a nucleating agent
0-2 wt % of a colorant
0-4 wt % of a slip agent
In an embodiment, the process comprises extruding a formulation at any of the angles disclosed in the numbered lines 1-22 above, wherein the formulation comprises:
50-99.65 wt % of the primary base resin
0-50 wt % of the secondary resin
0-10 wt % of the slip agent
0-10 wt % of the colorant
0.35-1.5 wt % of nucleating agent
In an embodiment, the process comprises extruding a formulation at any of the angles disclosed in the numbered lines 1-22 above, wherein the formulation comprises:
50-95 wt % of the primary base resin
0-50 wt % of the secondary resin
0-10 wt % of the slip agent
0-10 wt % of the colorant
0.4-1.2 wt % of nucleating agent
In an embodiment, the process comprises extruding a formulation at any of the angles disclosed in the numbered lines 1-22 above, wherein the formulation comprises:
55-85 wt % of the primary base resin
0-50 wt % of the secondary resin
0-10 wt % of the slip agent
0-10 wt % of the colorant
0.45-1.25 wt % of nucleating agent
In an embodiment, the process comprises extruding a formulation at any of the angles disclosed in the numbered lines 1-22 above, wherein the formulation comprises:
50-99.69 wt % of the primary base resin
0-50 wt % of the secondary resin
0-10 wt % of the slip agent
0-10 wt % of the colorant
0.01-1.5 wt % of the primary nucleating agent
0.3-1.7 wt % of the secondary nucleating agent
In an embodiment, the process comprises extruding a formulation at any of the angles disclosed in the numbered lines 1-22 above, wherein the formulation comprises:
50-95 wt % of the primary base resin
0-50 wt % of the secondary resin
0-10 wt % of the slip agent
0-10 wt % of the colorant
0.02-1.0 wt % of the primary nucleating agent
0.4-1.5 wt % of the secondary nucleating agent
In an embodiment, the process comprises extruding a formulation at any of the angles disclosed in the numbered lines 1-22 above, wherein the formulation comprises:
55-85 wt % of the primary base resin
0-50 wt % of the secondary resin
0-10 wt % of the slip agent
0-10 wt % of the colorant
0.03-0.7 wt % of the primary nucleating agent
0.45-1.25 wt % of the secondary nucleating agent
In an embodiment, the process comprises extruding a formulation at any of the angles disclosed in the numbered lines 1-22 above, wherein the formulation comprises:
78-83 wt % of a primary base resin
14-16 wt % of a secondary resin
0-0.05 wt % of a chemical blowing agent
0.25-2 wt % of a nucleating agent
1-2 wt % of a colorant
1.5-3.5 wt % of a slip agent
In the preceding embodiments, the primary base resin may comprise polypropylene. In another illustrative embodiment, the primary base resin comprises at least one of Borealis WB140 HMS polypropylene homopolymer and Braskem F020HC polypropylene homopolymer. In another embodiment, the primary base resin is Borealis WB140 HMS polypropylene homopolymer.
In the preceding embodiments, the secondary resin may comprise at least one polypropylene copolymer or polypropylene homopolymer. In another embodiment, the secondary resin comprises at least one of Braskem F020HC polypropylene homopolymer and PP 527K (available from Sabic). In another embodiment, the secondary resin is Braskem F020HC polypropylene homopolymer.
In the preceding embodiments, the chemical blowing agent may comprise citric acid, or a citric acid-based material. In an illustrative embodiment the chemical blowing agent is Hydrocerol™ CF-40E (available from Clariant Corporation).
In the preceding embodiments, the nucleating agent may comprise talc, CaCO3, mica, or mixtures thereof. In an illustrative embodiment, the nucleating agent is one or more of HT4HP talc (available from Heritage Plastics), HT6000 Linear Low Density Polyethylene (LLDPE) (available from Heritage Plastics), and Techmer PM PPM 16466 Silica. In another embodiment, the nucleating agent is HT4HP talc (available from Heritage Plastics) or Techmer PM PPM 16466 Silica. A primary nucleating agent may be defined as a chemical blowing agent or chemical foaming agent, itself comprising a nucleating agent. In another embodiment, a primary nucleating agent is Hydrocerol™ CF-40E™ (available from Clariant Corporation). In an illustrative embodiment, a secondary nucleating agent is selected from HPR-803i fibers (available from Milliken) or talc
In the preceding embodiments, the colorant may comprise at least one of Colortech 11933-19 TiO2 PP or Cell Stabilizer. In another embodiment, the colorant is Colortech 11933-19 TiO2 PP.
In the preceding embodiments, the slip agent may comprise one or more amides of fats or fatty acids, such as erucamide and oleamide. The slip agent may also comprise one or more low molecular weight amides and fluoroelastomers. In an embodiment, the slip agent is Ampacet 102823 Process Aid PE MB LLDPE.
The method of any of the preceding embodiments may also comprise adding CO2 to the formulation prior to extrusion at a rate of 1-4 lbs/hr. In an embodiment, the CO2 is added at a rate of 2-3 lbs/hr. In another embodiment, the CO2 is added at a rate of 2.2-2.8 lbs/hr. Such practice may also be referred to as adding a physical blowing agent.
The following examples are set forth for purposes of illustration only. Parts and percentages appearing in such examples are by weight unless otherwise stipulated.
An Exemplary Formulation Used to Illustrate the Present Disclosure is presented below and is described in U.S. Provisional Application Ser. No. 61/719,096, the disclosure of which is hereby incorporated herein by reference in its entirety:
DAPLOY™ WB140 polypropylene homopolymer (available from Borealis A/S) was used as the polypropylene base resin. F020HC, available from Braskem, a polypropylene homopolymer resin, was used as the secondary resin. The two resins were blended with: Hydrocerol™ CF-40E™ as a chemical blowing agent, talc as a nucleation agent, CO2 as a blowing agent, a slip agent, and titanium dioxide as a colorant. Percentages were:
The formulation described above was added to an extruder hopper. The extruder heated the formulation to form a molten resin mixture. To this mixture was added 2.2 lbs/hr CO2, which was injected into the resin blend to expand the resin and reduce density. The mixture thus formed was extruded through a die head into a sheet as described in U.S. application Ser. No. 13/491,007, the disclosure of which is hereby incorporated herein by reference in its entirety.
High resolution microscopy may be used to determine the dimensional properties of insulative cellular non-aromatic polymeric material. The Keyence VHX-1000 Digital Microscope was used to determine the dimensional properties of insulative cellular polypropylene-based material cells of the present disclosure. In one exemplary embodiment, cell length may be the dimensional property denoting maximum distance from top to bottom of cells running parallel to the circumferential direction 10 of an insulative cup made from insulative cellular non-aromatic polymeric material. In another exemplary embodiment, cell length may also be the dimensional property denoting maximum distance from top to bottom of cells running parallel to the axial direction 20 of an insulative cup made from insulative cellular non-aromatic polymeric material. In yet another exemplary embodiment, cell width may be the dimensional property denoting maximum distance from top to bottom of cells running in the radial direction of an insulative cup made from insulative cellular non-aromatic polymeric material. In still another exemplary embodiment, cell wall thickness may be the dimensional property denoting maximum distance between separated cell voids across a line running perpendicular to the circumferential and axial direction.
In order to assess the effect of cell morphology of an extruded sheet of insulative cellular polypropylene-based material on the quality of an article formed therewith, such as an insulative cup, a minimum of 700 measurement points were chosen for each of the length and width dimensional properties in order to verify consistency throughout a strip of the material. A minimum of 200 measurement points were chosen for cell wall thickness as a dimensional property in order to verify consistency throughout the strip of insulative cellular polypropylene-based material. In one exemplary embodiment, a sheet of insulative cellular polypropylene-based material may be extruded from an enclosed die volume at an angle of 44°. In another exemplary embodiment, a sheet of insulative cellular polypropylene-based material may be extruded from an enclosed die volume at an angle of 90°. A sheet of insulative cellular polypropylene-based material extruded at an angle of 44° is referred to herein as Material C. A sheet of insulative cellular polypropylene-based material extruded at an angle of 90° is referred to herein as Material D. Strips of insulative cellular polypropylene-based material from 44° and 90° exit angles were quantitatively compared as shown in
The typical testing method used for cell morphology measurement was as follows:
A sheet of insulative cellular polypropylene-based material produced as described herein typically possessed a density of about 0.1615 g/cm3 and material thickness of about 0.066 inches (1.6764 mm).
The cell morphology of an extruded sheet of insulative cellular polypropylene-based material exiting the enclosed die volume at angles of 44° and 90° differed greatly in terms of cell height, cell width, cell aspect ratio, and cell wall thickness as shown in Table 1. In the circumferential direction, Material C had an average length of 19.54 mils (49.63 mm), an average width of 8.53 mils (21.67 mm), an average cell wall thickness of 1.02 mils (2.59 mm), and average aspect ratio of 2.29. In the circumferential direction, Material D had an average length of 17.01 mils (43.21 mm), an average width of 5.22 mils (13.26 mm), an average cell wall thickness of 0.77 mils (1.96 mm), and average aspect ratio of 3.26.
In the axial direction, Material C had an average length of 18.45 mils (46.86 mm), an average width of 8.28 mils (21.03 mm), an average cell wall thickness of 0.96 mils (2.44 mm), and average aspect ratio of 2.23. In the axial direction, Material D had an average length of 16.43 mils (41.73 mm), an average width of 5.30 mils (13.46 mm), an average cell wall thickness of 0.84 mils (2.13 mm), and average aspect ratio of 3.10.
Moreover, formation of wrinkled insulative cellular polypropylene-based material was found to occur when the exit angle of curvature increased from 44° to 90° as suggested by Example 1,
In exemplary embodiments, die exit angles within an inclusive range of 50°-60° may produce insulative cellular polypropylene-based material with a tendency to wrinkle during convolution. In other exemplary embodiments, die exit angles within an inclusive range of 40°-50° may produce insulative cellular polypropylene-based material with a tendency to wrinkle during convolution. In other exemplary embodiments, die exit angles within an inclusive range of 30°-40° may produce insulative cellular polypropylene-based material with a tendency to wrinkle during convolution. In other exemplary embodiments, die exit angles within an inclusive range of 20°-30° may produce insulative cellular polypropylene-based material with a tendency to wrinkle during convolution. In other exemplary embodiments, die exit angles within an inclusive range of 10°-20° may produce insulative cellular polypropylene-based material with a tendency to wrinkle during convolution. In other exemplary embodiments, die exit angles within an inclusive range of 0°-10° may produce insulative cellular polypropylene-based material with a tendency to wrinkle during convolution. The lower the angle of die exit, the further from 1 the cell aspect ratio becomes, especially in the direction parallel to the flow of insulative cellular polypropylene-based material. Without wishing to be bound by theory, higher cell aspect ratios may increase local stress concentrations that are experienced during convolution of insulative cellular polypropylene-based material, thus leading to material with a greater tendency to wrinkle during convolution.
High resolution microscopy may be used to determine the dimensional properties of insulative cellular non-aromatic polymeric materials. The Keyence VHX-1000 Digital Microscope and Keyence VHX-2000 Digital Microscope were used to determine the dimensional properties of insulative cellular polypropylene-based material cells from the present disclosure.
Nine specified formulations with dissimilar processing conditions as shown in Table 2 produced cell dimensional properties that were found to follow a power law model with high accuracy and produce material that may possess a tendency to wrinkle during convolution. The following variables were held constant throughout iterations 1-18: 1° extruder temperature, 2° temperature, extruder speed, sheet pull rate, cooling mandrel diameter, cooling mandrel temperature, and overall die temperature as shown in Table 3A. The following variables were altered throughout the aforementioned trial iterations: formula, exit die pressure, die lip angle, die air ring cooling [l/min], and orientation as shown in Table 3A. The following variables were held constant throughout iterations 19-45: 1° extruder temperature, extruder speed, sheet pull rate, cooling mandrel diameter, cooling mandrel temperature, and overall die temperature as shown in Table 3B. The following variables were altered throughout the aforementioned trial iterations: 2° temperature, exit die pressure, die air ring cooling [l/min], CO2%, and orientation as shown in Table 3B. Iterations 46-50 were conducted in a manner similar to iterations 1-45 in order to investigate the occurrence of creasing during convolution of insulative cellular polypropylene-based material into a circular article (see, Table 3C).
Axial direction and circumferential direction dimensional attributes of 50 different iterations with nine specified formulations were incorporated in the analysis in order to produce data sufficient for high accuracy and precision, as shown in
The typical testing method used for cell morphology measurement was as follows:
A sheet of insulative cellular polypropylene-based material produced as described herein typically possessed a density of about 0.1615 g/cm3 and material thickness of about 0.066 inches (1.6764 mm).
All cell measurements were performed on over 7500 unique cell units from 50 different samples produced in various ways as described above. Although the maximum window view range of the Keyence digital microscope was 100 mils by 100 mils, careful attention was paid to ensure that each cell was unique and that the overall height and width of the measured strip was an average of values. A total of six (6) different dimensional parameters were measured for iterations 1-18.
In one exemplary embodiment, dimensional parameters of overall strip length (L), overall strip thickness (T), and total numbers of cells in the measured strip area (n) may be classified as bulk properties because they describe an overall cell property. In another exemplary embodiment, dimensional parameters of cell length (l), cell width (w), and cell wall thickness (t) may be classified as cell properties because they describe each cell unit.
A total of five (5) different dimensional parameters were measured for iterations 19-50. In one exemplary embodiment, dimensional parameters of overall strip length (L), overall strip thickness (T), and total numbers of cells in the measured strip area (n) may be classified as bulk properties because they describe an overall cell property. In another exemplary embodiment, dimensional parameters of cell length (l) and cell width (w) may be classified as cell properties because they describe each cell unit.
Each set of dimensional values was separately analyzed to ascertain a correlation between bulk properties and cell properties. Cell density (p) was used to normalize each cell number value because each of the 50 iterations possessed a different number of cells per area (cells/m2) due to different strip geometries. Cell density is calculated as the total number of cells in a given strip (n) divided by the overall strip length (L) and overall strip thickness (T), raised to the 3/2 power, as shown in Equation 1. Cell aspect ratio (A) is calculated as the average cell length (l) divided by the average cell width (w) of given iterations, as shown in Equation 2.
p=(n/TL)3/2 Equation 1:
A=(l/w) Equation 2:
Equation 1 transforms the units from cells per unit area (cells/in2) into cells per unit volume (cells/in3). Through mathematical manipulation of the denominator, the area (m2) is raised to the 3/2 power to transform the dimensional property into volume with correct units (m3). The same correlative effect is applied to the number of cells for consistency. Therefore, cell density is independently measured and calculated from the average bulk properties, as shown in Table 4 and Table 5. Cell properties such as cell length, cell width, and cell wall thickness are also independently measured and the average is calculated, also as shown in Table 4 and Table 5. By comparing independent values, quantitative correlations may be established to predict the occurrence of wrinkling during mechanical convolution of a material based solely on comparison of independent variables.
By correlating cell density bulk property to cell length, cell width, and cell wall thickness cell properties, a strong correlation was found that may predict dimensional properties with respect to cell density, and subsequently cell area. The coefficient of determination (R2) values produced by Microsoft Excel 2010 power law regression fit demonstrates a high degree of accuracy with regard to the validity of the fitted power law-based model. The power law has an equation form of two dependent variables, x and y, and two independent variables or constants, A and K, as shown in Equation 3 and Equation 4:
y=AxK Equation 3:
x=(y/A)l/K Equation 4:
In exemplary embodiments, cell density may predict cell length, cell width, and cell wall thickness with R2 values of 0.945, 0.939, and 0.973 as shown in
In exemplary embodiments, the equation for predicting cell length with respect to cell density may be y=1,243,388,528.483x−2.626, wherein the power law constants for predicting cell length with respect to cell density are A=1,243,388,528.483 and K=−2.626. In other exemplary embodiments, the equation for predicting cell width with respect to cell density may be y=426,736,129.761x−3417 wherein the power law constants for predicting cell width with respect to cell density are A=426,736,129.761 and K=−3.417. In other exemplary embodiments, the equation for predicting cell wall thickness with respect to cell density may be y=448,002.648x−3653 wherein the power law constants for predicting cell wall thickness with respect to cell density are A=448,002.648 and K=−3.053.
The data also illustrate a satisfactory range where insulative cellular polypropylene-based material possesses wrinkles, as defined by Wrinkles and Minimal Wrinkles, where Wrinkles means the cup possesses wrinkles and/or creases and Minimal Wrinkles means wrinkles and/or creases are not present. As shown in
In exemplary embodiments as suggested by
The cell prediction model accurately describes cell growth in the cell width, cell length, and cell wall thickness category and possesses power law functionality, similarly to that seen in many natural phenomena. By taking on a log-log plot form, the correlation is unexpectedly a straight line that penetrates near or through all data points with accuracy. This development provides further evidence for power law correlation and subsequently the ability to model and predict cell growth, as shown in
As presaged by the cell morphology versus micro-creasing/macro-creasing results shown in
Micro-Creasing defines small creases inside the cup found in the middle, top, and especially bottom areas; they are generally ¼″ to ½″ in length and near invisible to the eye unless you look for them.
Macro-Creasing defines large creases inside the cup that run all the way from the bottom to top or tangent to the cup; they are generally cup-length and very visible to the eye.
This application claims priority under 35 U.S.C. §119(e) to U.S. Provisional Application Ser. No. 62/052,296, filed Sep. 18, 2014, which is expressly incorporated by reference herein.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1396282 | Penn | Nov 1921 | A |
| 1435120 | Holman | Nov 1922 | A |
| 1920529 | Sidebotham | Aug 1933 | A |
| 1969030 | Page | Aug 1934 | A |
| 2097899 | Smith | Dec 1935 | A |
| 2809776 | Barrington | Mar 1956 | A |
| 3221954 | Lux | Dec 1965 | A |
| 3227784 | Blades | Jan 1966 | A |
| 3252387 | Schur | May 1966 | A |
| 3290198 | Lux | Dec 1966 | A |
| 3312383 | Shapiro | Apr 1967 | A |
| 3327038 | Fox | Jun 1967 | A |
| 3327103 | Bonnet | Jun 1967 | A |
| 3344222 | Shapiro | Sep 1967 | A |
| 3381880 | Lewallen et al. | May 1968 | A |
| 3409204 | Carle | Nov 1968 | A |
| 3431163 | Gilbert | Mar 1969 | A |
| 3468467 | Amberg | Sep 1969 | A |
| 3547012 | Amberg | Dec 1970 | A |
| 3583624 | Peacock | Jun 1971 | A |
| 3658615 | Amberg | Apr 1972 | A |
| 3661282 | Buhayar | May 1972 | A |
| 3733381 | Willette | May 1973 | A |
| 3793283 | Frailey | Feb 1974 | A |
| 3846349 | Harada | Nov 1974 | A |
| 3907193 | Heller | Sep 1975 | A |
| 3919368 | Seto | Nov 1975 | A |
| RE28658 | Macdaniel | Dec 1975 | E |
| 3967991 | Shimano | Jul 1976 | A |
| 3969173 | Amberg | Jul 1976 | A |
| 3971696 | Manfredi | Jul 1976 | A |
| 3973721 | Nakane | Aug 1976 | A |
| 3981412 | Asmus | Sep 1976 | A |
| 4026458 | Morris | May 1977 | A |
| 4049122 | Maxwell | Sep 1977 | A |
| 4070513 | Rhoads | Jan 1978 | A |
| 4106397 | Amberg | Aug 1978 | A |
| 4171085 | Doty | Oct 1979 | A |
| 4197948 | Amberg | Apr 1980 | A |
| 4240568 | Pool | Dec 1980 | A |
| 4284226 | Herbst | Aug 1981 | A |
| 4288026 | Wilhelm | Sep 1981 | A |
| 4298331 | Mueller | Nov 1981 | A |
| 4299349 | Gilden | Nov 1981 | A |
| 4300891 | Bemiss | Nov 1981 | A |
| 4306849 | Cress | Dec 1981 | A |
| 4310369 | Miller | Jan 1982 | A |
| 4349400 | Gilden | Sep 1982 | A |
| 4365460 | Cress | Dec 1982 | A |
| 4391666 | Mueller | Jul 1983 | A |
| 4409045 | Busse | Oct 1983 | A |
| 4490130 | Konzal | Dec 1984 | A |
| 4550046 | Miller | Oct 1985 | A |
| 4579275 | Peelman | Apr 1986 | A |
| 4604324 | Nahmias | Aug 1986 | A |
| 4621763 | Brauner | Nov 1986 | A |
| 4706873 | Schulz | Nov 1987 | A |
| 4720023 | Jeff | Jan 1988 | A |
| 4856989 | Siebert | Aug 1989 | A |
| 4878970 | Schubert | Nov 1989 | A |
| 4918112 | Roox | Apr 1990 | A |
| 4940736 | Alteepping | Jul 1990 | A |
| 5078817 | Takagaki | Jan 1992 | A |
| 5116881 | Park | May 1992 | A |
| 5149579 | Park | Sep 1992 | A |
| 5158986 | Cha | Oct 1992 | A |
| 5160674 | Colton | Nov 1992 | A |
| 5180751 | Park | Jan 1993 | A |
| 5236963 | Jacoby | Aug 1993 | A |
| 5256462 | Callahan | Oct 1993 | A |
| 5286428 | Hayashi | Feb 1994 | A |
| 5308568 | Lipp | May 1994 | A |
| 5348795 | Park | Sep 1994 | A |
| 5366791 | Carr | Nov 1994 | A |
| 5385260 | Gatcomb | Jan 1995 | A |
| 5443769 | Karabedian | Aug 1995 | A |
| 5445315 | Shelby | Aug 1995 | A |
| 5490631 | Iioka | Feb 1996 | A |
| 5507640 | Gilmer | Apr 1996 | A |
| 5547124 | Mueller | Aug 1996 | A |
| 5549864 | Greene | Aug 1996 | A |
| 5605936 | DeNicola, Jr. | Feb 1997 | A |
| 5622308 | Ito | Apr 1997 | A |
| 5628453 | MacLaughlin | May 1997 | A |
| 5629076 | Fukasawa | May 1997 | A |
| 5713512 | Barrett | Feb 1998 | A |
| 5759624 | Neale | Jun 1998 | A |
| 5765710 | Bergerioux | Jun 1998 | A |
| 5766709 | Geddes | Jun 1998 | A |
| 5769311 | Morita | Jun 1998 | A |
| 5819507 | Kaneko | Oct 1998 | A |
| 5840139 | Geddes | Nov 1998 | A |
| 5866053 | Park | Feb 1999 | A |
| 5868309 | Sandstrom | Feb 1999 | A |
| 5895614 | Rivera | Apr 1999 | A |
| 5925450 | Karabedian | Jul 1999 | A |
| 5928741 | Andersen | Jul 1999 | A |
| 5944225 | Kawolics | Aug 1999 | A |
| 5948839 | Chatterjee | Sep 1999 | A |
| 6007437 | Schickert | Dec 1999 | A |
| 6010062 | Shimono | Jan 2000 | A |
| 6030476 | Geddes | Feb 2000 | A |
| 6034144 | Shioya | Mar 2000 | A |
| 6051174 | Park | Apr 2000 | A |
| 6071580 | Bland | Jun 2000 | A |
| 6083611 | Eichbauer | Jul 2000 | A |
| 6103153 | Park | Aug 2000 | A |
| 6109518 | Mueller | Aug 2000 | A |
| 6129653 | Fredricks | Oct 2000 | A |
| 6136396 | Gilmer | Oct 2000 | A |
| 6139665 | Schmelzer | Oct 2000 | A |
| 6142331 | Breining | Nov 2000 | A |
| 6169122 | Blizard | Jan 2001 | B1 |
| 6174930 | Agarwal | Jan 2001 | B1 |
| 6218023 | DeNicola | Apr 2001 | B1 |
| 6231942 | Blizard | May 2001 | B1 |
| 6235380 | Tupil | May 2001 | B1 |
| 6251319 | Tusim | Jun 2001 | B1 |
| 6257485 | Sadlier | Jul 2001 | B1 |
| 6258862 | Matz | Jul 2001 | B1 |
| 6267837 | Mitchell | Jul 2001 | B1 |
| 6284810 | Burnham | Sep 2001 | B1 |
| 6294115 | Blizard | Sep 2001 | B1 |
| 6306973 | Takaoka | Oct 2001 | B1 |
| 6308883 | Schmelzer | Oct 2001 | B1 |
| 6319590 | Geddes | Nov 2001 | B1 |
| 6328916 | Nishikawa | Dec 2001 | B1 |
| 6376059 | Anderson | Apr 2002 | B1 |
| 6378733 | Boonzaier | Apr 2002 | B1 |
| 6379802 | Ito | Apr 2002 | B2 |
| 6383425 | Wu | May 2002 | B1 |
| 6420024 | Perez | Jul 2002 | B1 |
| 6444073 | Reeves | Sep 2002 | B1 |
| 6455150 | Sheppard | Sep 2002 | B1 |
| 6468451 | Perez | Oct 2002 | B1 |
| 6472473 | Ansems | Oct 2002 | B1 |
| RE37932 | Baldwin | Dec 2002 | E |
| 6512019 | Agarwal | Jan 2003 | B1 |
| 6521675 | Wu | Feb 2003 | B1 |
| 6541105 | Park | Apr 2003 | B1 |
| 6562447 | Wu | May 2003 | B2 |
| 6565934 | Fredricks | May 2003 | B1 |
| 6586532 | Gauthy | Jul 2003 | B1 |
| 6593005 | Tau | Jul 2003 | B2 |
| 6593384 | Anderson | Jul 2003 | B2 |
| 6613811 | Pallaver | Sep 2003 | B1 |
| 6616434 | Burnham | Sep 2003 | B1 |
| 6646019 | Perez | Nov 2003 | B2 |
| 6649666 | Read | Nov 2003 | B1 |
| 6713139 | Usui | Mar 2004 | B2 |
| 6720362 | Park | Apr 2004 | B1 |
| 6749913 | Watanabe | Jun 2004 | B2 |
| 6779662 | Dorsey | Aug 2004 | B2 |
| 6811843 | DeBraal | Nov 2004 | B2 |
| 6814253 | Wong | Nov 2004 | B2 |
| 6875826 | Huovinen | Apr 2005 | B1 |
| 6883677 | Goeking | Apr 2005 | B2 |
| 6884377 | Burnham | Apr 2005 | B1 |
| 6884851 | Gauthy | Apr 2005 | B2 |
| 6908651 | Watanabe | Jun 2005 | B2 |
| 6926507 | Cardona | Aug 2005 | B2 |
| 6926512 | Wu | Aug 2005 | B2 |
| 6982107 | Hennen | Jan 2006 | B1 |
| 7056563 | Halabisky | Jun 2006 | B2 |
| 7070852 | Reiners | Jul 2006 | B1 |
| 7074466 | DeBraal | Jul 2006 | B2 |
| 7094463 | Haas | Aug 2006 | B2 |
| 7121991 | Mannlein | Oct 2006 | B2 |
| 7144532 | Kim | Dec 2006 | B2 |
| 7173069 | Swennen | Feb 2007 | B2 |
| 7234629 | Herbert | Jun 2007 | B2 |
| 7281650 | Milan | Oct 2007 | B1 |
| 7355089 | Chang | Apr 2008 | B2 |
| 7361720 | Pierini | Apr 2008 | B2 |
| 7365136 | Huovinen | Apr 2008 | B2 |
| 7423071 | Mogami | Sep 2008 | B2 |
| 7458504 | Robertson | Dec 2008 | B2 |
| 7504347 | Poon | Mar 2009 | B2 |
| 7510098 | Hartjes | Mar 2009 | B2 |
| 7513386 | Hartjes | Apr 2009 | B2 |
| 7514517 | Hoenig | Apr 2009 | B2 |
| 7524911 | Karjala | Apr 2009 | B2 |
| 7557147 | Martinez | Jul 2009 | B2 |
| 7579408 | Walton | Aug 2009 | B2 |
| 7582716 | Liang | Sep 2009 | B2 |
| 7585557 | Aylward | Sep 2009 | B2 |
| 7592397 | Markovich | Sep 2009 | B2 |
| 7608668 | Shan | Oct 2009 | B2 |
| 7622179 | Patel | Nov 2009 | B2 |
| 7622529 | Walton | Nov 2009 | B2 |
| 7629416 | Li | Dec 2009 | B2 |
| 7655296 | Haas | Feb 2010 | B2 |
| 7662881 | Walton | Feb 2010 | B2 |
| 7666918 | Prieto | Feb 2010 | B2 |
| 7671106 | Markovich | Mar 2010 | B2 |
| 7671131 | Hughes | Mar 2010 | B2 |
| 7673564 | Wolf | Mar 2010 | B2 |
| 7687442 | Walton | Mar 2010 | B2 |
| 7695812 | Peng | Apr 2010 | B2 |
| 7714071 | Hoenig | May 2010 | B2 |
| 7732052 | Chang | Jun 2010 | B2 |
| 7737061 | Chang | Jun 2010 | B2 |
| 7737215 | Chang | Jun 2010 | B2 |
| 7741397 | Liang | Jun 2010 | B2 |
| 7754814 | Barcus | Jul 2010 | B2 |
| 7759404 | Burgun | Jul 2010 | B2 |
| 7786216 | Soediono | Aug 2010 | B2 |
| 7787216 | Soediono | Aug 2010 | B2 |
| 7795321 | Cheung | Sep 2010 | B2 |
| 7803728 | Poon | Sep 2010 | B2 |
| 7811644 | DeBraal | Oct 2010 | B2 |
| 7818866 | Hollis | Oct 2010 | B2 |
| 7820282 | Haas | Oct 2010 | B2 |
| 7825166 | Sasaki | Nov 2010 | B2 |
| 7841974 | Hartjes | Nov 2010 | B2 |
| 7842770 | Liang | Nov 2010 | B2 |
| 7858706 | Arriola | Dec 2010 | B2 |
| 7863379 | Kapur | Jan 2011 | B2 |
| 7883769 | Seth | Feb 2011 | B2 |
| 7893166 | Shan | Feb 2011 | B2 |
| 7897689 | Harris | Mar 2011 | B2 |
| 7906587 | Poon | Mar 2011 | B2 |
| 7910658 | Chang | Mar 2011 | B2 |
| 7915192 | Arriola | Mar 2011 | B2 |
| 7918005 | Hollis | Apr 2011 | B2 |
| 7918016 | Hollis | Apr 2011 | B2 |
| 7922071 | Robertson | Apr 2011 | B2 |
| 7922971 | Robertson | Apr 2011 | B2 |
| 7928162 | Kiss | Apr 2011 | B2 |
| 7935740 | Dang | May 2011 | B2 |
| 7947367 | Poon | May 2011 | B2 |
| 7951882 | Arriola | May 2011 | B2 |
| 7977397 | Cheung | Jul 2011 | B2 |
| 7989543 | Karjala | Aug 2011 | B2 |
| 7993254 | Robertson | Aug 2011 | B2 |
| 7998579 | Lin | Aug 2011 | B2 |
| 7998728 | Rhoads | Aug 2011 | B2 |
| 8003176 | Ylitalo | Aug 2011 | B2 |
| 8003744 | Okamoto | Aug 2011 | B2 |
| 8012550 | Ylitalo | Sep 2011 | B2 |
| 8026291 | Handa | Sep 2011 | B2 |
| 8043695 | Ballard | Oct 2011 | B2 |
| 8067319 | Poon | Nov 2011 | B2 |
| 8076381 | Miyagawa | Dec 2011 | B2 |
| 8076416 | Ellul | Dec 2011 | B2 |
| 8084537 | Walton | Dec 2011 | B2 |
| 8087147 | Hollis | Jan 2012 | B2 |
| 8105459 | Alvarez | Jan 2012 | B2 |
| 8119237 | Peng | Feb 2012 | B2 |
| 8124234 | Weaver | Feb 2012 | B2 |
| 8173233 | Rogers | May 2012 | B2 |
| 8198374 | Arriola | Jun 2012 | B2 |
| 8211982 | Harris | Jul 2012 | B2 |
| 8227075 | Matsushita | Jul 2012 | B2 |
| 8273068 | Chang | Sep 2012 | B2 |
| 8273826 | Walton | Sep 2012 | B2 |
| 8273838 | Shan | Sep 2012 | B2 |
| 8288470 | Ansems | Oct 2012 | B2 |
| 8304496 | Weaver | Nov 2012 | B2 |
| 8404780 | Weaver | Mar 2013 | B2 |
| 8435615 | Tsuchida | May 2013 | B2 |
| 8679620 | Matsushita | Mar 2014 | B2 |
| 8715449 | Leser | May 2014 | B2 |
| 8721823 | Vaideeswaran | May 2014 | B2 |
| 8883280 | Leser | Nov 2014 | B2 |
| 9067705 | Leser | Jun 2015 | B2 |
| 9180995 | Iyori | Nov 2015 | B2 |
| 9358772 | Leser | Jun 2016 | B2 |
| 20010010848 | Usui | Aug 2001 | A1 |
| 20010010849 | Blizard | Aug 2001 | A1 |
| 20010038893 | Mohan | Nov 2001 | A1 |
| 20010041236 | Usui | Nov 2001 | A1 |
| 20020030296 | Geddes | Mar 2002 | A1 |
| 20020041046 | Hartjes | Apr 2002 | A1 |
| 20020058126 | Kannankeril | May 2002 | A1 |
| 20020135088 | Harfmann | Sep 2002 | A1 |
| 20020137851 | Kim | Sep 2002 | A1 |
| 20020144769 | Debraal | Oct 2002 | A1 |
| 20020172818 | DeBraal | Nov 2002 | A1 |
| 20030003251 | DeBraal | Jan 2003 | A1 |
| 20030017284 | Watanabe | Jan 2003 | A1 |
| 20030021921 | DeBraal | Jan 2003 | A1 |
| 20030029876 | Giraud | Feb 2003 | A1 |
| 20030108695 | Freek | Jun 2003 | A1 |
| 20030138515 | Harfmann | Jul 2003 | A1 |
| 20030211310 | Haas | Nov 2003 | A1 |
| 20030228336 | Gervasio | Dec 2003 | A1 |
| 20030232210 | Haas | Dec 2003 | A1 |
| 20040013830 | Nonomura | Jan 2004 | A1 |
| 20040031714 | Hanson | Feb 2004 | A1 |
| 20040038018 | Anderson | Feb 2004 | A1 |
| 20040062885 | Imanari | Apr 2004 | A1 |
| 20040115418 | Anderson | Jun 2004 | A1 |
| 20040170814 | VanHandel | Sep 2004 | A1 |
| 20050003122 | Debraal | Jan 2005 | A1 |
| 20050006449 | DAmato | Jan 2005 | A1 |
| 20050101926 | Ausen | May 2005 | A1 |
| 20050104365 | Haas | May 2005 | A1 |
| 20050115975 | Smith | Jun 2005 | A1 |
| 20050121457 | Wilson | Jun 2005 | A1 |
| 20050124709 | Krueger | Jun 2005 | A1 |
| 20050145317 | Yamamoto | Jul 2005 | A1 |
| 20050147807 | Haas | Jul 2005 | A1 |
| 20050159496 | Bambara | Jul 2005 | A1 |
| 20050165165 | Zwynenburg | Jul 2005 | A1 |
| 20050184136 | Baynum | Aug 2005 | A1 |
| 20050236294 | Herbert | Oct 2005 | A1 |
| 20050256215 | Burnham | Nov 2005 | A1 |
| 20050272858 | Pierini | Dec 2005 | A1 |
| 20050288383 | Haas | Dec 2005 | A1 |
| 20060000882 | Darzinskas | Jan 2006 | A1 |
| 20060094577 | Mannlein | May 2006 | A1 |
| 20060095151 | Mannlein | May 2006 | A1 |
| 20060108409 | Pyper | May 2006 | A1 |
| 20060135699 | Li | Jun 2006 | A1 |
| 20060148920 | Musgrave | Jul 2006 | A1 |
| 20060151584 | Wonnacott | Jul 2006 | A1 |
| 20060178478 | Ellul | Aug 2006 | A1 |
| 20060198983 | Patel | Sep 2006 | A1 |
| 20060199006 | Poon | Sep 2006 | A1 |
| 20060199030 | Liang | Sep 2006 | A1 |
| 20060199744 | Walton | Sep 2006 | A1 |
| 20060199872 | Prieto | Sep 2006 | A1 |
| 20060199884 | Hoenig | Sep 2006 | A1 |
| 20060199887 | Liang | Sep 2006 | A1 |
| 20060199896 | Walton | Sep 2006 | A1 |
| 20060199897 | Karjala | Sep 2006 | A1 |
| 20060199905 | Hughes | Sep 2006 | A1 |
| 20060199906 | Walton | Sep 2006 | A1 |
| 20060199907 | Chang | Sep 2006 | A1 |
| 20060199908 | Cheung | Sep 2006 | A1 |
| 20060199910 | Walton | Sep 2006 | A1 |
| 20060199911 | Markovich | Sep 2006 | A1 |
| 20060199912 | Fuchs | Sep 2006 | A1 |
| 20060199914 | Harris | Sep 2006 | A1 |
| 20060199930 | Shan | Sep 2006 | A1 |
| 20060199931 | Poon | Sep 2006 | A1 |
| 20060199933 | Okamoto | Sep 2006 | A1 |
| 20060205833 | Martinez | Sep 2006 | A1 |
| 20060211819 | Hoenig | Sep 2006 | A1 |
| 20060234033 | Nishikawa | Oct 2006 | A1 |
| 20060289609 | Fritz | Dec 2006 | A1 |
| 20060289610 | Kling | Dec 2006 | A1 |
| 20070000983 | Spurrell | Jan 2007 | A1 |
| 20070010616 | Kapur | Jan 2007 | A1 |
| 20070032600 | Mogami | Feb 2007 | A1 |
| 20070056964 | Holcomb | Mar 2007 | A1 |
| 20070065615 | Odle | Mar 2007 | A1 |
| 20070066756 | Poon | Mar 2007 | A1 |
| 20070078222 | Chang | Apr 2007 | A1 |
| 20070095837 | Meier | May 2007 | A1 |
| 20070112127 | Soediono | May 2007 | A1 |
| 20070141188 | Kim | Jun 2007 | A1 |
| 20070155900 | Chang | Jul 2007 | A1 |
| 20070167315 | Arriola | Jul 2007 | A1 |
| 20070167575 | Weaver | Jul 2007 | A1 |
| 20070167578 | Arriola | Jul 2007 | A1 |
| 20070202330 | Peng | Aug 2007 | A1 |
| 20070219334 | LiPiShan | Sep 2007 | A1 |
| 20080020162 | Fackler | Jan 2008 | A1 |
| 20080045638 | Chapman | Feb 2008 | A1 |
| 20080118738 | Boyer | May 2008 | A1 |
| 20080121681 | Wiedmeyer | May 2008 | A1 |
| 20080138593 | Martinez | Jun 2008 | A1 |
| 20080156857 | Johnston | Jul 2008 | A1 |
| 20080177242 | Chang | Jul 2008 | A1 |
| 20080227877 | Stadlbauer | Sep 2008 | A1 |
| 20080234435 | Chang | Sep 2008 | A1 |
| 20080260996 | Heilman | Oct 2008 | A1 |
| 20080269388 | Markovich | Oct 2008 | A1 |
| 20080280517 | Chang | Nov 2008 | A1 |
| 20080281037 | Karjala | Nov 2008 | A1 |
| 20080311812 | Arriola | Dec 2008 | A1 |
| 20090042472 | Poon | Feb 2009 | A1 |
| 20090068402 | Yoshida | Mar 2009 | A1 |
| 20090069523 | Itakura | Mar 2009 | A1 |
| 20090076216 | Kiss | Mar 2009 | A1 |
| 20090105417 | Walton | Apr 2009 | A1 |
| 20090110855 | McCarthy | Apr 2009 | A1 |
| 20090110944 | Aguirre | Apr 2009 | A1 |
| 20090170679 | Hartjes | Jul 2009 | A1 |
| 20090220711 | Chang | Sep 2009 | A1 |
| 20090247033 | Peng | Oct 2009 | A1 |
| 20090263645 | Barger | Oct 2009 | A1 |
| 20090275690 | Weaver | Nov 2009 | A1 |
| 20090324914 | Lieng | Dec 2009 | A1 |
| 20100025073 | Fagrell | Feb 2010 | A1 |
| 20100028568 | Weaver | Feb 2010 | A1 |
| 20100029827 | Ansems | Feb 2010 | A1 |
| 20100040818 | Farha | Feb 2010 | A1 |
| 20100055358 | Weaver | Mar 2010 | A1 |
| 20100069574 | Shan | Mar 2010 | A1 |
| 20100093942 | Silvis | Apr 2010 | A1 |
| 20100116422 | Vaideeswaran | May 2010 | A1 |
| 20100137118 | Chang | Jun 2010 | A1 |
| 20100168267 | Dang | Jul 2010 | A1 |
| 20100181328 | Cook | Jul 2010 | A1 |
| 20100181370 | Berbert | Jul 2010 | A1 |
| 20100196610 | Chang | Aug 2010 | A1 |
| 20100240818 | Walton | Sep 2010 | A1 |
| 20100279571 | Poon | Nov 2010 | A1 |
| 20100324202 | Bafna | Dec 2010 | A1 |
| 20110003929 | Soediono | Jan 2011 | A1 |
| 20110008570 | Seth | Jan 2011 | A1 |
| 20110009513 | Chaudhary | Jan 2011 | A1 |
| 20110014835 | Sieradzki | Jan 2011 | A1 |
| 20110091688 | Maurer | Apr 2011 | A1 |
| 20110104414 | Onodera | May 2011 | A1 |
| 20110111150 | Matsuzaki | May 2011 | A1 |
| 20110118370 | Jiang | May 2011 | A1 |
| 20110118416 | Arriola | May 2011 | A1 |
| 20110124818 | Arriola | May 2011 | A1 |
| 20110136959 | Brandstetter | Jun 2011 | A1 |
| 20110144240 | Harris | Jun 2011 | A1 |
| 20110217492 | Stamatiou | Sep 2011 | A1 |
| 20110229693 | Maurer | Sep 2011 | A1 |
| 20110230108 | Arriola | Sep 2011 | A1 |
| 20110318560 | Yun | Dec 2011 | A1 |
| 20120004087 | Tharayil | Jan 2012 | A1 |
| 20120024873 | Roseblade | Feb 2012 | A1 |
| 20120028065 | Bafna | Feb 2012 | A1 |
| 20120041148 | Bafna | Feb 2012 | A1 |
| 20120043374 | Lemon | Feb 2012 | A1 |
| 20120045603 | Zerafati | Feb 2012 | A1 |
| 20120108714 | Wittner | May 2012 | A1 |
| 20120108741 | Wu | May 2012 | A1 |
| 20120108743 | Krishnaswamy | May 2012 | A1 |
| 20120125926 | Iyori | May 2012 | A1 |
| 20120132699 | Mann | May 2012 | A1 |
| 20120178896 | Bastioli | Jul 2012 | A1 |
| 20120184657 | Lake | Jul 2012 | A1 |
| 20120193365 | Humphries | Aug 2012 | A1 |
| 20120199278 | Lee | Aug 2012 | A1 |
| 20120199279 | Lee | Aug 2012 | A1 |
| 20120199641 | Hsieh | Aug 2012 | A1 |
| 20120214890 | Senda | Aug 2012 | A1 |
| 20120220730 | Li | Aug 2012 | A1 |
| 20120225961 | VanHorn | Sep 2012 | A1 |
| 20120237734 | Maurer | Sep 2012 | A1 |
| 20120267368 | Wu | Oct 2012 | A1 |
| 20120270039 | Tynys | Oct 2012 | A1 |
| 20120295994 | Bernreitner | Nov 2012 | A1 |
| 20120318805 | Leser | Dec 2012 | A1 |
| 20120318807 | Leser | Dec 2012 | A1 |
| 20120318859 | Leser | Dec 2012 | A1 |
| 20130023598 | Song | Jan 2013 | A1 |
| 20130032963 | Tokiwa | Feb 2013 | A1 |
| 20130052385 | Leser | Feb 2013 | A1 |
| 20130140320 | Nadella | Jun 2013 | A1 |
| 20130216744 | Liao | Aug 2013 | A1 |
| 20130280517 | Buehring | Oct 2013 | A1 |
| 20130303645 | Dix | Nov 2013 | A1 |
| 20140131430 | Leser | May 2014 | A1 |
| 20140263367 | Robertson | Sep 2014 | A1 |
| 20150250342 | Euler | Sep 2015 | A1 |
| 20150258771 | Leser | Sep 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 2291607 | Jun 2000 | AQ |
| 2765489 | Dec 2010 | CA |
| 1288427 | Mar 2001 | CN |
| 1495100 | May 2004 | CN |
| 1942370 | Apr 2007 | CN |
| 101370873 | Feb 2009 | CN |
| 101429309 | May 2009 | CN |
| 101531260 | Sep 2009 | CN |
| 101538387 | Sep 2009 | CN |
| 102115561 | Jul 2011 | CN |
| 102245368 | Nov 2011 | CN |
| 102391570 | Mar 2012 | CN |
| 102762350 | Oct 2012 | CN |
| 102115561 | Feb 2013 | CN |
| 102089370 | Jun 2011 | CO |
| 2831240 | Jan 1980 | DE |
| 2831240 | Mar 1988 | DE |
| 102006025612 | Nov 2007 | DE |
| 102006025612 | Nov 2007 | DE |
| 0001791 | May 1979 | EP |
| 0086869 | Aug 1983 | EP |
| 0161597 | Nov 1985 | EP |
| 0318167 | May 1989 | EP |
| 0520028 | Dec 1992 | EP |
| 0570221 | Nov 1993 | EP |
| 0588321 | Mar 1994 | EP |
| 0659647 | Jun 1995 | EP |
| 0879844 | Nov 1998 | EP |
| 0972727 | Jan 2000 | EP |
| 0796199 | Feb 2001 | EP |
| 0940240 | Oct 2002 | EP |
| 1308263 | May 2003 | EP |
| 1323779 | Jul 2003 | EP |
| 1479716 | Nov 2004 | EP |
| 1666530 | Jun 2006 | EP |
| 1754744 | Feb 2007 | EP |
| 1921023 | May 2008 | EP |
| 1939099 | Jul 2008 | EP |
| 2266894 | Dec 2010 | EP |
| 2386584 | Nov 2011 | EP |
| 2386601 | Nov 2011 | EP |
| 2720954 | Apr 2014 | EP |
| 1078326 | Aug 1967 | GB |
| 2485077 | May 2012 | GB |
| 52123043 | Oct 1977 | JP |
| 52123043 | Oct 1977 | JP |
| 58029618 | Feb 1983 | JP |
| H02129040 | May 1990 | JP |
| H02269683 | Nov 1990 | JP |
| H0543967 | Jun 1993 | JP |
| 0615751 | Jan 1994 | JP |
| 3140847 | Jan 1994 | JP |
| 06192460 | Jul 1994 | JP |
| P310847 | Dec 2000 | JP |
| 2001310429 | Nov 2001 | JP |
| 2003292663 | Oct 2003 | JP |
| 2003321566 | Nov 2003 | JP |
| 2004018101 | Jan 2004 | JP |
| 2004168421 | Jun 2004 | JP |
| 2004168421 | Jun 2004 | JP |
| 2006096390 | Apr 2006 | JP |
| 2006130814 | May 2006 | JP |
| 2006142008 | Jun 2006 | JP |
| 2007154172 | Jun 2007 | JP |
| 2008162700 | Jul 2008 | JP |
| 2009504858 | Feb 2009 | JP |
| 2009066856 | Apr 2009 | JP |
| 2009126922 | Jun 2009 | JP |
| 2009138029 | Jun 2009 | JP |
| 2009190756 | Aug 2009 | JP |
| 2010173258 | Aug 2010 | JP |
| 100306320 | Oct 2001 | KR |
| 2003036558 | May 2003 | KR |
| 2004017234 | Feb 2004 | KR |
| 101196666 | Nov 2012 | KR |
| 9113933 | Sep 1991 | TK |
| 9413460 | Jun 1994 | TK |
| 2010076701 | Jul 2010 | TK |
| 2011036272 | Mar 2011 | TK |
| 2011141044 | Nov 2011 | TK |
| 2012173873 | Dec 2012 | TK |
| 2006124369 | Nov 2006 | TN |
| 9413460 | Jun 1994 | WO |
| 9729150 | Aug 1997 | WO |
| 1998016575 | Apr 1998 | WO |
| 0002800 | Jan 2000 | WO |
| 0119733 | Mar 2001 | WO |
| 0132758 | May 2001 | WO |
| 0153079 | Jul 2001 | WO |
| 0234824 | May 2002 | WO |
| 03076497 | Sep 2003 | WO |
| 03099913 | Dec 2003 | WO |
| 2004104075 | Dec 2004 | WO |
| 2006042908 | Apr 2006 | WO |
| 2007003523 | Jan 2007 | WO |
| 2007020074 | Feb 2007 | WO |
| 2007068766 | Jun 2007 | WO |
| 2007090845 | Aug 2007 | WO |
| 2008030953 | Mar 2008 | WO |
| 2008038750 | Apr 2008 | WO |
| 2008045944 | Apr 2008 | WO |
| 2008057878 | May 2008 | WO |
| 2008080111 | Jul 2008 | WO |
| 2008145267 | Dec 2008 | WO |
| 2009035580 | Mar 2009 | WO |
| 2010006272 | Jan 2010 | WO |
| 2010019146 | Feb 2010 | WO |
| 2010111869 | Oct 2010 | WO |
| 2011005856 | Jan 2011 | WO |
| 2011036272 | Mar 2011 | WO |
| 2011038081 | Mar 2011 | WO |
| 2011076637 | Jun 2011 | WO |
| 2012020106 | Feb 2012 | WO |
| 2012025584 | Mar 2012 | WO |
| 2012044730 | Apr 2012 | WO |
| 2012055797 | May 2012 | WO |
| 2012099682 | Jul 2012 | WO |
| 2012174422 | Dec 2012 | WO |
| 2012174567 | Dec 2012 | WO |
| 2012174568 | Dec 2012 | WO |
| 2013032552 | Mar 2013 | WO |
| 2013101301 | Jul 2013 | WO |
| Entry |
|---|
| Office Action dated Dec. 31, 2015 for U.S. Appl. No. 14/755,546. |
| Notice of Allowance dated Jan. 29, 2016 for U.S. Appl. No. 14/755,546. |
| English translation of First Office Action for Taiwanese Application No. 101121656, Nov. 13, 2015. |
| Singapore Notice of Eligibility for Grant, Search Report, and Examination Report transmitted Dec. 10, 2015 for Singapore Application No. 11201503336V. |
| Office Action dated Jan. 11, 2016 for U.S. Appl. No. 14/161,328. |
| English Summary of Russian Office Action for Application Serial No. 2014111340, dated Feb. 25, 2016, 8 pages. |
| United Kingdom Examination Report for Patent Application No. GB1400762.9 dated Feb. 11, 2016. |
| Office Action dated Feb. 16, 2016 for U.S. Appl. No. 14/108,142. |
| Extended European Search Report for European Application No. 13849152.7-1303 / 2912142 PCT/US2013/066811, dated Feb. 12, 2016. |
| English summary of Spanish Office Action for Application Serial No. P201490025, Feb. 9, 2016, 8 pages. |
| Supplemental European Search Report for European Application No. 12727994.1-1302, dated Feb. 17, 2016. |
| International Search Report and Written Opinion dated Oct. 18, 2013, relating to International Application No. PCT/US2013/053935. |
| International Preliminary Report on Patentability dated Feb. 16, 2016, relating to International Application No. PCT/US2014/051508. |
| English Summary of Chinese Office Action for Application Serial No. 201380041896.1, dated Mar. 21, 7 pages. |
| Extended European Search Report for European Application No. 13827981.5-1708 / 2888092 PCT/US2013/053935, dated Feb. 19, 2016. |
| Australian First Patent Examination Report for Application No. 2012271047, dated Feb. 29, 2016. |
| N.N. Najib, N.M. Manan, A.A. Bakar, and C.S. Sipaut, Effect of Blowing Agent Concentration on Cell Morphology and Impact Properties of Natural Rubber Foam, Journal of Physical Science, vol. 20(1), 13-25, 2009 (13 pages). |
| Nigel Mills, Polymer Foams Handbook, Fig. 2.2, 1st ed. 2007 (2 pages). |
| University of Massachusetts , Advanced Plastics Processing Lecture, Lecture 11: Foam Processes, Slide 4 (Nov. 11, 2012) (2 pages). |
| Australian Second Patent Examination Report for Application No. 2012302251, dated Feb. 26, 2016. |
| English summary of Chinese Office Action for Chinese Application Serial No. 201380065781.6, Apr. 19, 2016, 14 pages. |
| Affidavit of Christopher Butler of Internet Archive, Borealis webpage dated Jan. 20, 2010 (https://web.archive.org/web/20100120102738/http://www.borealisgroup.com/industry-solutions/advancedpackaging/rigid-packaging/polyolefin-foam/daploy-hmspp-extruded-foam/). |
| Reichelt et al., “PP-Blends with Tailored Foamability and Mechanical Properties”, Cellular Polymers, vol. 22, No. 5, 2003, 14 pages. |
| Ratzsch et al., “Radical reactions on polypropylene in the solid state”, Prog. Polym. Sci. 27 (2002) 1195-1282, 88 pages. |
| Excerpts from Encyclopedia of Polymer Science and Technology: Plastics, Resins, Rubbers, and Fibers, “Blowing Agents”, vol. 2, John Wiley & Sons, Inc. (1965), 37 pages. |
| Excerpts from Polymer Foams: Science and Technology, Lee et al., “Introduction to Polymeric Foams”, CRC Press (2007) 51 pages. |
| “Daploy(TM) HMS Polypropylene for Foam Extrusion”, obtained from Borealis webpage obtained from the Internet Archive\s “Wayback Machine” as of Nov. 16, 2008 https://web.archive.org/web/20081116085125/http://www.borealisgroup.com/pdf/literature/borealisborouge/brochure/K—IN0020—GB—FF—2007—10—BB.pdf). |
| Excerpts from Gibson and Ashby, Cellular solids: Structure and properties—Second edition, Cambridge University Press, 1997, 66 pages. |
| Excerpts from Maier and Calafut, Polypropylene: the Definitive User's Guild and Databook, Plastics Design Library, William Andrew Inc. (1998), 35 pages. |
| ASTM D3763-86, an American Society for Testing of Materials (ASTM), “Standard Method for High-Speed Puncture Properties of Plastics Using Load and Displacement Sensors” (1986 Edition), 5 pages. |
| ASTM D1922-93, an American Society for Testing of Materials (ASTM), “Standard Method for Propagation Tear Resistance of Plastic Film and Thin Sheeting by Pendulum Method” (1993 Edition), 5 pages. |
| Naguib et al., “Effect of Supercritical Gas on Crystallization of Linear and Branched Polypropylene Resins with Foaming Additives”, Ind. Eng. Chem. Res., 44 (2005), 6685-6691. |
| Tabatabaei et al., “Rheological and thermal properties of blends of a long-chain branched polypropylene and different linear polypropylenes”, Chemical Engineering Science, 64 (2009), 4719-4731. |
| Almanza et al., “Applicability of the Transient Plane Source Method to Measure the Thermal Conductivity of Low-Density Polyethylene Foams”, Journal of Polymer Science: Part B: Polymer Physics, vol. 42 (2004), 1226-1234. |
| The Burn Foundation, “Scald Burns”, available at https://web.archive.org/web/20080926114057/http:/wwwvii.burnfoundation.org/programs/resource.cfm?c=1&a=3, dated Sep. 26, 2008, accessed on Feb. 5, 2016. |
| AntiScald Inc. available at https://web.archive.org/web/20080517041952/http:/www.antiscald.com/prevention/general—info/table.php, dated May 17, 2008, accessed on Feb. 5, 2016. |
| “Fire Dynamics”, available at http://www.nist.gov/fire/fire—behavior.cfm, accessed on Feb. 5, 2016. |
| “Power of a Microwave Oven”, available at https://web.archive.org/web/20071010183358/http://hypertextbook.com/facts/2007/TatyanaNektalova.shtml, dated Oct. 10, 2007, accessed on Feb. 5, 2016. |
| Health Physics Society, “Microwave Oven Q & A”, available at https://web.archive.org/web/20090302090144/http://www.hps.org/publicinformation/ate/faqs/microwaveoveng&a.html, dated Mar. 2, 2009, accessed on Feb. 5,2016. |
| Cook's Info, “Microwave Ovens”, available at http://www.cooksinfo.com/microwave-ovens, accessed on Feb. 5, 2016. |
| Antunes et al., “Heat Transfer in Polypropylene-Based Foams ProducedUsing Different Foaming Processes”, Advanced Engineering Materials, 11, No. 10 (2009), 811-817. |
| Excerpts from Frank Kreith, Principles of Heat Transfer, 3rd ed., Intext Educational Publishers (1973). |
| Excerpts from James M. Gere, Mechanics of Materials, 5th ed., Brooks/Cole (2001). |
| Technical data sheet of HIFAX CA 60 A, obtained from https://www.lyondellbasell.com/en/polymers/p/Hifax-CA-60-A/d372c484-8f5a-4b2c-8674-8b7b781a1796, accessed on Feb. 4, 2016, 2 pages. |
| Michel Biron, “Chapter 4—Detailed Accounts of Thermoplastic Resins,” Thermoplastics and Thermoplastic Composites, Technical Information for Plastics Users, Elsevier Ltd. (2007), 217-714. |
| Excerpts from Cornelia Vasile, “Mechanical Properties and Parameters of Polyolefins”, Handbook of Polyolefins, 2nd ed., Marcel Dekker, Inc. (2000). |
| Williams et al., “Thermal Connectivity of Plastic Foams”, Polymer Engineering and Science, Apr. 1983, vol. 23, No. 6., 293-298. |
| Excerpts from M.C. McCrum et al., Principles of Polymer Engineering, 2nd ed., Oxford Science Publications (1997). |
| Excerpts from Robert H. Perry, Perry\s Chemical Engineers Handbook, 7th ed., The McGraw-Hill Companies, Inc. (1997). |
| Martinez-Diez et al., “The Thermal Conductivity of a Polyethylene Foam Block Produced by a Compression Molding Process”, Journal of Cellular Plastics, vol. 37 (2001), 21-42. |
| Borealis Product Brochure, Daploy HMS Polypropylene for Foam Extrusion (2010), 20 pages. |
| R. Coquard and D. Baillis, Journal of Heat Transfer, 2006, 128(6): 538-549. |
| A. R. Katritzky et al., “Correlation and Prediction of the Refractive Indices of Polymers by QSPR,” J. Chem. Inf. Comput. Sci., 38 (1998), 1171-1176. |
| M. Antunes et al., “Heat Transfer in Polyolefin Foams,” Heat Transfer in Multi-Phase Materials, A. Öchsner and G. E. Murch, Eds. Springer-Verlag Berlin Heidelberg, 2011, 131-161. |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (2101 pages) [Submitted in multiple parts—section 1]. |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (2101 pages) [Submitted in multiple parts—section 2]. |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (2101 pages) [Submitted in multiple parts—section 3]. |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (2101 pages) [Submitted in multiple parts—section 4]. |
| English summary of Mexican Office Action for Application Serial No. MX/a/2013/014993, Apr. 27, 2016, 5 pages. |
| Japanese Office Action for Japanese Patent Application No. 2014-528384, dated Mar. 1, 2016. |
| International Preliminary Report on Patentability dated Feb. 16, 2016, relating to International Application No. PCT/US2014/051508. E |
| English Summary of Chinese Office Action for Application Serial No. 201380041896.1, dated Mar. 18, 2016, 7 pages. |
| Doerpinghaus et al., “Separating the effects of sparse long-chain branching on rheology from those due to molecular weight in polyethylenes”, Journal of Rheology, 47, 717 (2003). |
| English Summary of Chinese Office Action for Application Serial No. 201280051426.9, Apr. 29, 2016, 5 pages. |
| English translation of Japanese Office Action for Japanese Application No. 2014-516089, dated May 10, 2016. |
| Third Party Submission Under 37 CFR 1.290 filed on May 12, 2016 in U.S. Appl. No. 14/739,510. |
| Daploy HMS Polypropylene for Foam Extrusion, 20 pages, BOREALIS Borouge Shaping the Future with Plastics, Published 2010, www.borealisgroup.com, www.borouge.com, Vienna, Austria. |
| Lugao, A.B. et al., HMSPP—New Developments, Chemical and Environmental Technology Center, IPEN—Progress Report, 2002-2004 (1 page). |
| Davesh Tripathi, Practical Guide to Polypropylene, 2002 (5 pages). |
| Jinghua Tian et al., The Preparation and Rheology Characterization of Long Chain Branching Polypropylene, Polymer, 2006 (9 pages). |
| Bc. Lukas Kovar, High Pressure Crystallization of Long Chain Branched Polypropylene, Master Thesis, Thomas Bata University in Zlin, 2010 (83 pages). |
| Office Action dated Jun. 30, 2016 for U.S. Appl. No. 14/106,276. |
| Australian First Patent Examination Report for Application No. 2012363114, dated Jun. 15, 2016, 4 pages. |
| Office Action for Chinese Patent Application No. 201380064860.5, dated Jun. 2, 2016 including English language summary, 13 pages. |
| Singapore Office Action and Written Opinion dated May 26, 2016 for Singapore Application No. 11201504333Y. |
| Singapore Office Action and Written Opinion dated May 27, 2016 for Singapore Application No. 11201504330U. |
| Singapore Office Action and Written Opinion dated May 27, 2016 for Singapore Application No. 11201504327V. |
| Office Action dated Jun. 10, 2016 for U.S. Appl. No. 14/188,504. |
| Office Action dated Mar. 10, 2016 for U.S. Appl. No. 14/620,073. |
| Notice of Acceptance dated Jun. 10, 2016 for Australian Application No. 2012302251. |
| Office Action for Chinese Patent Application No. 201380065116.7, dated Jun. 28, 2016, including English language summary, 12 pages. |
| Australian First Patent Examination Report for Application No. 2013334155, dated May 23, 2016, 4 pages. |
| Extended European Search Report for European Application No. 13862331.9-1708 / 2931627 PCT/US2013/074923, dated Jul. 7, 2016. |
| English translation of Russian Office Action for Application Serial No. 2014101298, dated Jul. 22, 2016, 7 pages. |
| Office Action dated Sep. 1, 2016 for U.S. Appl. No. 14/106,212. |
| Australian First Patent Examination Report for Application No. 2013359097 sent Aug. 26, 2016, 3 pages. |
| British Examamination Report for GB Application No. GB1400762.9, sent on Aug. 8, 2016, 2 pages. |
| Extended European Search Report for European Application No. 13863546.1 established Jul. 12, 2016, 7 pages. |
| Office Action dated Aug. 9, 2016 for U.S. Appl. No. 14/108,142. |
| Jacoby, Philip, “Recent Insights on the Use of Beta Nucleation to Improve the Thermoforming Characteristics of Polypropylene,” Society of Plastics Engineers, Annual Technical Conference Proceedings, ANTEC 2012, Apr. 2012, pp. 2292-2296. |
| Singapre Written Opinion for Singapore Patent Application No. 11201504756T established Jul. 19, 2016, 7 pages. |
| Office Action dated Sep. 27, 2016 for U.S. Appl. No. 14/725,319. |
| Taiwan Office Action for Taiwan Pat. App. No. 102146299 received on Oct. 21, 2016, 7 pages. |
| Third Party Observation filed in European Patent App. No. 12727994.1 received on Nov. 4, 2016, 11 pages. |
| International Standard ISO 16790:2005(E), 20 pages. |
| S. Muke et al., The Melt Extensibility of Polypropylene, Polym. Int. 2001,515-523, 9 pages. |
| P. Spitael and C.W. Macosko, Strain Hardening in Polypropylenes and its Role in Extrusion Foaming, Polym. Eng. Sci. 2004, 2090-2100. |
| Combined Search and Examination Report for Great Britain App. No. GB1616321.4 received Oct. 12, 2016, 4 pages. |
| British Examination Report for GB App. No. 1400762.9 received Oct. 12, 2016, 2 pages. |
| Chinese Office Action for Chinese Applicaiton 201380065781.6 received Oct. 18, 2016, 33 pages. |
| Research Progress of Polypropylene Foamed Material, Baiquan Chen et al., Plastics Manufacture, No. 12, pp. 55-58. |
| Modification and Formulation of Polypropylene, Mingshan Yang edits, Chemical Industry Press, p. 43, the second paragraph from the bottom, Jan. 31, 2009. |
| Extended European Search Report for European App. No. 13863649.3 received Sep. 27, 2016, 9 pages. |
| Office Action dated Nov. 4, 2016 for U.S. Appl. No. 13/961,411. |
| Chinese Office Action for Chinese Application No. 201280051426.9 received Nov. 1, 9 pages. |
| English Summary of Chinese Office Action for Application Serial No. 201380041896.1, dated Nov. 11, 2016, 11 pages. |
| Extended European Search Report for European App. No. 14775300.8 sent Oct. 24, 2016, 9 pages. |
| Office Action dated Nov. 18, 2016 for U.S. Appl. No. 14/718,836. |
| Borealis AG, Daploy(TM) HMS Polypropylene for Foam Extrusion, 2010, 20 pages. |
| International Search Report and Written Opinion dated Apr. 16, 2014, relating to International Application No. PCT/US2013/075013. |
| International Search Report and Written Opinion dated Apr. 21, 2014, relating to International Application No. PCT/US2013/074923. |
| International Search Report and Written Opinion dated Apr. 22, 2014, relating to PCT/US2013/074965. |
| International Search Report and Written Opinion dated Apr. 25, 2014, relating to PCT/US2013/075052. |
| International Search Report and Written Opinion dated Jul. 3, 2014, relating to International Application No. PCT/US2014/025697. |
| International Search Report and Written Opinion dated Sep. 17, 2013, relating to International Application No. PCT/US2012/041395. |
| International Search Report dated Feb. 26, 2013, relating to International Application No. PCT/US2012/043018. |
| International Search Report dated Jan. 29, 2013, relating to International Application No. PCT/US2012/043017. |
| International Search Report dated Jan. 30, 2013, relating to International Application No. PCT/US2012/042737. |
| International Search Report dated Jul. 29, 2013, relating to International Application No. PCT/US2012/043016, 25 pages. |
| International Search Report dated Jul. 30, 2012, relating to International Application No. PCT/US2012/041397. |
| International Search Report dated Mar. 11, 2014, relating to International Application No. PCT/US2013/66811. |
| International Search Report dated Nov. 19, 2012, relating to International Application No. PCT/US2012/041395. |
| Jaakko I. Raukola, A New Technology to Manufacture Polypropylene Foam Sheet and Biaxially Oriented Foam Film, VTT Publications 361, Technical Research Centre of Finland, Apr. 1998, 100 pages. |
| Machine English translation of JP 2006-130814. |
| Notice of Allowance dated Jun. 23, 2014 for U.S. Appl. No. 13/491,327. |
| Notice of Allowance dated Oct. 6, 2014 for U.S. Appl. No. 13/491,327. |
| Office action dated Apr. 11, 2014 for U.S. Appl. No. 13/526,417. |
| Office Action dated Aug. 19, 2014 for Chinese Application No. 201280035667.4. |
| Office Action dated Aug. 21, 2014 for U.S. Appl. No. 13/526,454. |
| Office Action dated Jul. 25, 2014 for U.S. Appl. No. 13/525,640. |
| Office Action dated Oct. 10, 2014 for U.S. Appl. No. 14/106,358. |
| Office Action dated Oct. 16, 2014 for U.S. Appl. No. 14/106,212. |
| Office Action dated Sep. 25, 2014 for U.S. Appl. No. 13/526,417. |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (712 pages) [Reference submitted in three parts]. |
| Borealis webpage dated Jan. 20, 2010 from Internet Archive (6 pages). |
| Gibson and Ashby, Cellular solids: structure and properties, 2nd ed., Cambridge University Press (1997) (7 pages). |
| C. Maier and T. Calafut, Polypropylene: the Definitive User\s Guide and Databook, Plastics Design Library, William Andrew Inc. (1998) (19 pages). |
| Reichelt et al., Cellular Polymers, vol. 22, No. 5 (2003) (14 pages). |
| Ratzsch et al., Prog. Polym. Sci., 27 (2002), 1195-1282 (88 pages). |
| Encyclopedia of Polymer Science and Technology: Plastics, Resins, Rubbers, and Fibers, vol. 2, John Wiley & Sons, Inc. (1965) (37 pages). |
| Shau-Tarng Lee, Chul B. Park, and N.S. Ramesh, Polymer Foams: Science and Technology, CRC Press (2007) (51 pages). |
| Grant & Hackh\s Chemical Dictionary, 5th ed., McGraw-Hill, Inc. (1987) (3 pages). |
| Merriam-Webster\s Collegiate Dictionary, 11th ed. (2003), p. 70 (3 pages). |
| Merriam-Webster\s Collegiate Dictionary, 11th ed. (2003), p. 1237 (3 pages). |
| Hawley\s Condensed Chemical Dictionary, 14th Ed. (2001) (5 pages). |
| Reichelt et al., Abstract of PP-Blends with Tailored Foamability and Mechanical Properties, Cellular Polymers, (2003) available from http://www.polymerjournals.com/journals.asp?Page=111&JournalType=cp&JournalIssue=cp22-5&JIP=, listing (4 pages). |
| Ratzsch et al., Abstract of Radical Reactions on Polypropylene in the Solid State, Progress in Polymer Science, vol. 27, Issue 7, (Sep. 2002), available from http://www.sciencedirect.com/science/article/pii/S0079670002000060 (3 pages). |
| “Borealis Dapoly HMS Polypropylene for Foam Extrusion” obtained from Borealis webpage obtained from the Internet Archive\s “Wayback Machine” as of Nov. 16, 2008 (https://web.archive.org/web/20081116085125/http://www.borealisgroup.com/pdf/literature/borealis-borouge/brochure/K—IN0020—GB—FF—2007—10—BB.pdf) (“Brochure \08” ) (20 pages). |
| Certified English translation of EP0086869. |
| English translation of Spanish Search Report of Application No. 201490025, dated Apr. 20, 2015. |
| European Search Report of Application No. 12861450.0, dated Nov. 21, 2014. |
| International Search Report and Written Opinion dated Jan. 19, 2015, relating to International Application No. PCT/US2014/059312. |
| International Search Report dated Jan. 19, 2015, relating to International Application No. PCT/US2014/059216. |
| International Search Report dated Nov. 7, 2014, relating to International Application No. PCT/US2014/51508. |
| Machine English translation of EP0086869. |
| Naguib et al., “Fundamental Foaming Mechanisms Governing the Volume Expansion of Extruded Polypropylene Foams,” Journal of Applied Polymer Science, vol. 91, pp. 2661-2668, 2004 (10 pages). |
| New Zealand First Examination Report for Application No. 619616 dated Oct. 10, 2014. |
| New Zealand First Examination Report for Application No. 621219 dated Nov. 17, 2014. |
| Notice of Allowance dated Apr. 6, 2015 for U.S. Appl. No. 13/526,417. |
| Office Action dated Apr. 10, 2015 for U.S. Appl. No. 14/106,358. |
| Office Action dated Apr. 14, 2015 for U.S. Appl. No. 14/106,212. |
| Office Action dated Apr. 30, 2015 for U.S. Appl. No. 14/462,073. |
| Office Action dated Feb. 2, 2015 for U.S. Appl. No. 14/106,114. |
| Office Action dated Jan. 6, 2015 for Chinese Application No. 201280034350.9 (11 pages). |
| Office Action dated Jan. 9, 2015 for Chinese Application No. 201280035667.4 (22 pages). |
| Office Action dated Jun. 23, 2015 for U.S. Appl. No. 13/525,640. |
| Singapore Office Action dated Dec. 18, 2014 for Singapore Application No. 2014002273. |
| Spanish Search Report for Application No. 201490025, dated Apr. 20, 2015. |
| Spanish Search Report of Application No. 201390099, dated Feb. 9, 2015. |
| Third-Party Submission Under 37 CFR 1.290 filed on Dec. 9, 2014 in U.S. Appl. No. 14/063,252. |
| Third-Party Submission Under 37 CFR 1.290 filed on Feb. 26, 2015 in U.S. Appl. No. 13/491,007. |
| Third Party Submission Under 37 CFR 1.290 in U.S. Appl. No. 14/188,504 submitted May 11, 2015 and May 27, 2015 (43 pages). |
| Wang et al., “Extending PP\s Foamability Through Tailored Melt Strength and Crystallization Kinetics,” paper 19 from the Conference Proceedings of the 8th International Conferences of Blowing Agents and Foaming Processes, May 16-17, 2006 in Munich, Germany Smithers Rapra Ltd, 2006 (14 pages). |
| Australian First Patent Examination Report for Application No. 2012302251 dated Jul. 9, 2015. |
| Certified English translation of JP2003292663. |
| Office Action Chinese Patent Application No. 201280051426.9 dated Jul. 23, 2015. |
| Office Action dated Aug. 18, 2015 for U.S. Appl. No. 14/106,212. |
| Office Action dated Aug. 27, 2015 for U.S. Appl. No. 14/106,358. |
| Office Action dated May 19, 2015 for Chinese Application No. 201280035667.4. |
| Office Action dated Oct. 27, 2015 for U.S. Appl. No. 14/462,073. |
| Office Action dated Oct. 8, 2015 for U.S. Appl. No. 14/188,504. |
| Second Chinese Office Action dated Sep. 6, 2015 for Chinese Application Serial No. 201280034350.9. |
| Third Party Observations filed with respect to European Patent Application No. 12727994.1, Aug. 17, 2015 (22 pages). |
| U.S. Appl. No. 61/498,455, filed Jun. 17, 2011, related to PCT Application No. PCT/US2012/041395, 46 pages. |
| “Slip Agents”, Polypropylene Handbook, 2nd edition, 2005, pp. 285-286. |
| English translation of Russian Office Action for Application Serial No. 2015127677, dated Sep. 16, 2015. |
| Japanese Office Action for Japanese App. No. 2014-528384 received Dec. 6, 2016, 15 pages. |
| Singapore Office Action and Written Opinion received Feb. 6, 2017 for Singapore Application No 11201504330U, 6 pages. |
| Office Action dated Feb. 7, 2017 for U.S. Appl. No. 13/491,007. |
| Office Action for Chinese Patent Application No. 201380064860.5, dated Jan. 25, 2017, 12 pages. |
| European Examination Report for European App. No. 13849152.7 sent Jan. 30, 2017, 3 pages. |
| Singapore Office Action and Written Opinion dated Feb. 14, 2017 for Singapore Application No. 11201504327V, 6 pages. |
| Spanish Search Report for Spanish App. No. 201490025 received Dec. 23, 2016, 5 pages. |
| Japanese Office Action for Japanese Patent App. 2014-516089 sent Dec. 20, 2016, 6 pages. |
| European Examination Report for European App. No. 12727994.1 received on Jan. 25, 2016, 4 pages. |
| Typical Engineering Properties of Polypropylene information sheet, Ineos Olefins and Polymers USA, archived at https://web.archive.org/web/20160501000000*/http://www.ineos.com/globalassets/ineos-group/businesses/ineos-olefins-and-polymers-usa/products/technical-information-patents/ineos-engineering-properties-of-pp.pdf, Mar. 2016, p. 1. |
| Gulf Cooperation Council Examination Report for GCC Patent App. No. GC2012-21529 received on Nov. 14, 2016, 6 pages. |
| Chinese Office Action for Chinese App. No. 201480052411.3 dated Feb. 28, 2017, 16 pages. |
| New Zealand First Examination Report for New Zealand Application 708546 dated Feb. 23, 2014, 2 pages. |
| Singapore Office Action and Written Opinion dated Dec. 13, 2016 and received on Feb. 28, 2017 for Singapore Application No. 11201504333Y, 6 pages. |
| Office Action for Chinese Patent Application No. 201380065116.7, dated Mar. 1, 2017, 9 pages. |
| Chinese Office Action dated Mar. 10, 2017 for Chinese Patent Application 201480007369.3, 11 pages. |
| New Zealand Examination Report for New Zealand Application No. 708463 dated Mar. 16, 2017, 3 pages. |
| Supplemental European Search Report for European App. No. 14836418 dated Feb. 23, 2017, 6 pages. |
| New Zealand Examination Report for New Zealand Application No. 708552 received on Mar. 29, 2017, 2 pages. |
| Australian Search Report for Australian App. No. 2013359028, dated Apr. 10, 2017, 5 pages. |
| Australian Search Report for Australian App. No. 20133358988 dated Apr. 11, 2017, 4 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20160083569 A1 | Mar 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62052296 | Sep 2014 | US |