This invention relates to cementitious compositions and to accelerators for use therein, particularly for sprayed concrete.
The application of a cementitious material such as concrete to a substrate by spraying from a nozzle is a well-established technology, and it is widely used in such applications as the lining of tunnels. It is important that the sprayed concrete set very rapidly on the substrate, and this is achieved by the addition to the concrete at the nozzle of an accelerator. These accelerators are quite different from those used with conventional concrete and have traditionally included such materials as alkali metal hydroxides, aluminates and silicates.
The highly alkaline nature of these materials has given handing problems. It also means that their use in confined spaces such as tunnels has led to very unpleasant working atmospheres. Recent attempts to avoid such materials have involved the use of aluminium compounds and typical examples may be found in European Patents 0 076 927, 0 775 097 and 0 742 179, Australian Patent 706917 and European Applications 0 812 812 and 0 946 451.
It has now been found that it is possible to prepare an accelerator for sprayed concrete by a simple process, which accelerator performs especially well. The invention therefore provides a method of preparing an accelerator for sprayed cementitious material consisting essentially of the steps of
(ii) optionally adding at least one defoaming agent;
the proportions of ingredients present being such that the final product contains from 3%-12% by weight of aluminium sulphate (measured as Al2O3), up to 30% by weight of amorphous aluminium hydroxide, up to 15% by weight amine, up to 3% by weight defoaming agent and up to 1.5 mol/kg. stabiliser, the stabiliser being glycolic acid.
The invention additionally provides an accelerator for use with sprayed cementitious material preparable by such a method.
The invention additionally provides an accelerator for cementitious material consisting essentially of a solution of aluminium sulphate, amorphous aluminium hydroxide and glycolic acid, optionally containing amine and defoaming agent, the accelerator containing from 3%-12% by weight of aluminium sulphate (measured as Al2O3), up to 30% by weight of amorphous aluminium hydroxide, up to 15% by weight amine, up to 3% by weight defoaming agent and up to 1.5 mol/kg. glycolic acid.
The aluminium sulphate used may be any commercially-available material. Aluminium sulphates differ in their purity and constitution, the most common being so-called “17%” because it contains 17% of Al2O3. In practical terms, the weight percentage of 17% aluminium sulphate, Al2(SO4)3. 14.3H2O, which should be used in the process according to the invention lies in the range of from 30% to 60%, preferably from 40%-54%.
The aluminium hydroxide may be any commercially-available amorphous aluminium hydroxide. Although all such aluminium hydroxides will give satisfactory results, it is generally true that the more recent the date of manufacture, the better the result. In addition, aluminium hydroxides which, as a result of their particular manner of manufacture, contain a small proportion of aluminium carbonate (up to 5%) are easier to dissolve and are preferred materials. This behaviour is not obtained by simply adding aluminium carbonate to pure aluminium hydroxide. Although very small quantities of aluminium hydroxide may be used (less than 0.1% is possible), a significant improvement is observed at 5% or more. The preferred range of weight proportions is from 4-25%, preferably from 6-18%.
There must also be present a stabiliser, which may be added at the end of the process. This is a material which prevents the aluminium hydroxide/aluminium sulphate solution either from precipitating or from forming a gel. Without stabiliser, the solution will function well as an accelerator, but it will lack stability and therefore shelf life, necessitating its use very shortly after manufacture, something usually not practical.
The stabiliser for use in this invention is glycolic acid (hydroxyacetic acid). It has been previously proposed to use hydroxycarboxylic acids as stabilisers in International Application PCT/EP00/12216, but there was no specific mention of glycolic acid and the preferred acid in that application was citric acid. It has been found surprisingly that glycolic acid gives outstanding stability, far better than other hydroxycarboxylic acids. Preferably the stabiliser is present to the extent of from 0.1-1 mol./kg. As a general rule, the more glycolic acid present, the better the stability. However, there comes a point when addition of further glycolic acid brings no improvement. Thus, although the stated maximum of 1.5 mol./kg. can be exceeded, this brings no benefit. The best results are obtained by using quantities in the region of 1 mol./kg.
The properties of the accelerators provided by this invention can be considerably enhanced by the use of one or both of two optional, but preferred, components.
The first of these is amine. This must be water-soluble, otherwise there is no restriction on the choice of amine. Preferred amines are alkanolamines, such as diglycolamine, diethanolamine and triethanolamine, diethanolamine being particularly preferred. Up to 12% by weight amine may be used, but the preferred quantity is from 1-4%.
The second preferred additional component, defoaming agent, may be any such material known to the art. Most of these are proprietary commercial materials whose precise composition is never revealed, but any such material known to the art is suitable. Typical examples include silicone types such as AGITAN (trade mark) and fatty acid polyether types such as LUMITEN (trade mark) EL.
The defoaming agent may be used at a rate out up to 5% (solids by weight of the whole composition), preferably from 0.5%-3%. The use of defoaming agent makes the use of less fresh aluminium hydroxides easier. It is believed, without restricting the scope of the invention in any way, that its presence helps in the removal of carbon dioxide which accumulates on the surface of the aluminium hydroxide over time. Surprisingly, provided that the defoamer contains no silicone and that it is not present to the extent of more than 3%, it gives an appreciable improvement in setting time over that of an identical composition without defoaming agent or with silicone types.
The process of the invention is readily carried out with standard equipment, and the skilled person will have no difficulty in doing so. It will be appreciated that in order to achieve solutions at the various stages, some heating may be necessary, typically to about 50-60° C.
In the process, the clear solution can be produced by any convenient method. It is possible to add the aluminium sulphate and aluminium hydroxide sequentially in any order to water. It is also possible to add them together to water, or to dissolve or disperse them individually in two different quantities of water and then combine these quantities.
Preferably, the aluminium sulphate and the aluminium hydroxide are added sequentially to water. Preferably the aluminium sulphate is first dissolved in water; aluminium sulphate will dissolve with heating. To this solution the aluminium hydroxide is then added. A clear solution is obtained.
It is possible, although less preferable, first to add the aluminium hydroxide to the water. Aluminium hydroxide does not dissolve readily in water, but gives a fine suspension. To this suspension the aluminium sulphate is added. A clear solution is obtained. The stabiliser is added to this solution and stirred in.
The precise nature of the product of the process is not known. It is certainly not a mere mixture of the original components (the fact that the product is a clear or slightly turbid solution and not an opaque suspension typical of aluminium hydroxide is evidence of this), and without restricting the invention in any way, it is believed to be oligomeric or polymeric in nature.
The accelerator thus prepared gives excellent results when used as an accelerator for sprayed cementitious material, especially concrete. Sprayed concrete treated with this accelerator hardens rapidly and has good final strength. The accelerator has a long shelf-life, is resistant to changes in temperature and is completely non-alkaline, thus leading to better working environments.
The invention therefore also provides a method of applying a cementitious composition to a substrate by spraying, comprising the conveying of the composition to a spray nozzle, there being added at the nozzle an accelerating composition of the kind hereinabove described.
The invention is further illustrated by the following non-limiting examples.
An accelerator is made from the following ingredients:
The water is heated to 55°-60° C., and the aluminium sulphate is added with stirring. When it has dissolved, the aluminium hydroxide is added, followed by the glycolic acids and the amine. The mixture is then allowed to cool. The final solution is a pale yellow, slightly turbid solution.
This accelerator composition is called Accelerator A.
Another accelerator (Accelerator B) is prepared in the same manner, but substituting formic acid, a well-known stabiliser, for glycolic acid. The quantity of water is reduced, so that more formic acid can be added—the quantity of formic acid in Accelerator B is twice that of glycolic acid in Accelerator A.
Both accelerators are subjected to long-term stability testing at 5° C., 20° C. and 40° C. The particular test period is 70 days. The assessment criteria and the results are as follows:
a) Change in turbidity Both accelerators show no change over the entire period at 5° and 20°. However, at 40°, Accelerator A shows a turbidity change (indicating the onset of instability) at 31 days, whereas Accelerator B showed this change at 13 days.
(b) Gelling A gelled accelerator cannot be used. Both accelerators show no gelling over the whole period at 5° and 20°, but Accelerator A gelled at 59 days and Accelerator B at 27 days.
(c) Separation The separation of the accelerator solution into discrete liquid layers indicates that it can no longer be used. Both accelerators show no separation over the period.
(d) Sedimentation Excessive sedimentation (in excess of 1 mm) means that an accelerator can no longer be used. Neither accelerator has excessive sedimentation over the period of the test.
The performance of Accelerator B is typical of a high-performance commercial accelerator. It can readily be seen that Accelerator A according to the invention has a significant edge in stability performance, even though it has only half of the quantity of stabiliser. 40° C. is typical of the temperatures commonly encountered in tunnels, and it is often required that accelerators ready for use be stored in such conditions. The improvement in performance shown by Accelerator B is therefore of major commercial significance, as it saves the need for less stable accelerators to be stored in cooler conditions and then brought in on demand.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0128438.9 | Nov 2001 | GB | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP02/12483 | 11/7/2002 | WO | 1/18/2005 |