Patent Grant
11155498
The present teaching relates generally to a cementitious composition, and more precisely to provide a permanent repair product which bonds to both asphalt and cement based roadway and walkway surfaces.
It is generally believed that fly ash, calcium aluminate, calcium sulfoaluminate, and Portland based hydraulic cements do not bond adequately to asphalt to be used as repair products. Most repair products are designed to be applied to either asphalt or cementitious substrates, but are not capable of bonding adequately to both.
Portland cement is hydraulic cement produced by pulverizing clinkers which consist essentially of hydraulic calcium silicates, usually containing one or more of the forms of calcium sulfate as an inter ground addition. It consists of at least two-thirds by mass of calcium silicates (3 CaO. SiO2 and 2 CaO.SiO2), the remainder consisting of aluminum- and iron-containing clinker phases and other compounds. The ratio of CaO to SiO2 shall not be less than 2.0. The magnesium oxide content shall not exceed 5.0% by mass.
Non-Portland cement is a high resistance, sustainable cement with the addition of raw materials such as: calcium sulfoaluminate, alkali aluminosilicates, and certain hydrocarbons.
Previous cementitious compositions comprise either multiple types of cement or only a single type of cement. However, each previous composition, whether made of a multiple or single types of cement, come with their own set of challenges.
Two component polymer based materials require on-site mixing of the resin and hardener in precise ratios in order to achieve the targeted performance. Epoxy, polyurea, and polyester resins are the most common in use and are typically supplied in pre-measured packaging to reduce the potential of the end user mixing the proportions incorrectly. The directions often state that to ensure proper performance, mix the entire contents of the packaging. This often results in wasted excess material and associated higher costs. Another negative aspect is that frequently the aggregate is packaged separately and must be mixed in a secondary step, which adds to the labor time on-site. Still another negative aspect is that the polymers used are not water based and thus the tool and on-site clean up requires flammable solvents or aggressive detergents whose run-off may contaminate adjacent soil and waterways.
Single component polymer compositions are moisture cured and designed to simplify the process for the end user by simply adding water once the material is placed. They have the disadvantage of short shelf life due to moisture contamination during manufacturing and packaging, particularly when produced on high humidity days. Once the packaging is opened, any unused material will be exposed to atmospheric moisture, resulting in the curing and hardening in the packaging, even after resealing. The end result is that the product is susceptible to hardening in the packaging either from the factory over time or once opened, rendering it useless, instilling cost losses, and yielding waste material.
Prior to the present teaching, the high strength cement, mortar, and concrete disclosed in U.S. Pat. No. 8,016,937 by Schumacher, Patel, Sampson, and Riley, explicitly has less than 20% Portland content in the hydratable cement portion of the compositions. None of the composition examples described therein contain Portland cement or calcium sulfoaluminate cement. Further, this composition does not provide adequate bonding to asphalt.
Prior to the present teaching, it is known to use fly ash in Portland cement compositions as a filler material. Brook, et. al. in U.S. Pat. No. 5,556,458 discloses that at least 20% Portland cement is needed to overcome the low early strength of their alkali earth metal salt activated fly ash cement compositions with calcium aluminate used for compensating autogenous shrinkage. Just like the other prior art, this composition does not provide adequate bonding to asphalt.
Prior to the present teaching, it is generally believed that fly ash, calcium aluminate, calcium sulfoaluminate, and Portland based hydraulic cements do not bond adequately to asphalt to be used as repair products.
Therefore, it would be beneficial to have a cementitious composition utilizing the synergistic effects of combining a particular blend of multiple types of cement, which provides a permanent repair product for both asphalt and cement based roadways and walkways without the negative attributes of previous cementitious compositions made up of cement blends.
The needs set forth herein as well as further and other needs and advantages are addressed by the present embodiments, which illustrate solutions and advantages described below.
The blended hydraulic cement composition of the present teaching may be formulated in the following manner. Each of the individual components may be added individually to the packaging and dry mixed in the packaging or on site prior to the addition of water. Each of the individual components may be pre-blended prior to packaging and the water added on site. The hydraulic cement may also have the aggregates incorporated into the packaging. Packaging may include plastic buckets, polyethylene lined Kraft paper bags, plastic bags, supersacks, and bulk totes, although not limited thereto.
The cementitious composition of the present teaching may be combined with fine and/or course aggregates as defined and recommended by the American Concrete Institute to produce a mortar, grout, or shotcrete.
The cementitious composition of the present teaching will permit the user to avoid being exposed to hazardous organic vapors, chemical burns, and thermal burns.
The cementitious composition of the present teaching will permit the user to avoid use of flammable solvents or corrosive detergents to clean tools and supplies, thus eliminating potential environmental damage caused by spills and washout runoff.
The cementitious composition of the present teaching forms a hardened cement when a sufficient amount of water is added to achieve the desired consistency and can be mixed until homogenous using either hand tools, drill mixer, rotary drum mixer, mortar mixer, grout pump, auger, sprayer, or shotcrete mixer, although not limited thereto.
The cementitious composition of the present teaching may be placed onto a cement, concrete, macadam, brick, compacted aggregate, compacted soil, asphalt substrate(s), although not limited thereto, prior to hardening, consolidating the composition, surface finishing the composition, and allowing the composition to cure.
The cured composition of the present teaching can be used to form a road surface, walkway, vertical barrier, wall, flooring, decking, cast articles, or repairs thereof, although not limited thereto.
The composition of the present teaching forms a bond to the substrate that is stronger than the substrate.
The cementitious composition of one embodiment, according to the present teaching, includes a Portland cement, a calcium sulfoaluminate cement, a non-Portland hydratable cement powder, which includes a pozzolanic powder and has a calcium content expressed as oxides of at least 15 weight percent based on the total weight of the non-Portland hydratable cement powder, and an alkali salt. The Portland cement has a content of at least 20 percent based on the total weight of the non-Portland hydratable cement powder.
In a further embodiment, the composition is free of latex bonding agents and calcium aluminate cement.
In a further embodiment, the calcium sulfoaluminate cement content is between 0.5 and 70 percent of the composition.
In a further embodiment, the alkali salt content is between 0.1 and 10 percent of the composition.
In a further embodiment, an alkali ion of the alkali salt is selected from a group comprising lithium, sodium, potassium, magnesium, and calcium.
In a further embodiment, the alkali ion is in stoichiometric proportion with a hydrocarboxylic acid to form a pH neutral salt.
In a further embodiment, the hydrocarboxylic acid is selected from a group comprising citric, lactic, and propionic.
In a further embodiment, the pozzolanic powder is selected from a group comprising Class C Fly Ash, Class F Fly Ash, volcanic ash, diatomaceous earth, rich hull ash, opal, and a high free lime content powder.
In a further embodiment, the high free lime content powder is selected from a group comprising lime kiln dust, cement kiln dust, slag, granulated blast furnace slag cement, and calcium oxide.
The cementitious composition of another embodiment, according to the present teaching, includes a Portland cement, calcium aluminosilicate, a non-Portland hydratable cement powder, which includes a pozzolanic powder and has a calcium content expressed as oxides of at least 15 weight percent based on the total weight of the non-Portland hydratable cement powder, and an alkali salt. The Portland cement has a content of at least 20 percent based on the total weight of the non-Portland hydratable cement powder.
In a further embodiment, the composition is free of latex bonding agents and calcium aluminate cement.
In a further embodiment, the calcium aluminosilicate content is between 0.5 and 70 percent of the composition.
In a further embodiment, the alkali salt content is between 0.1 and 10 percent of the composition.
In a further embodiment, an alkali ion of the alkali salt is selected from a group comprising lithium, sodium, potassium, magnesium, and calcium.
In a further embodiment, the alkali ion is in stoichiometric proportion with a hydrocarboxylic acid to form a pH neutral salt.
In a further embodiment, the hydrocarboxylic acid is selected from a group comprising citric, lactic, and propionic.
In a further embodiment, the pozzolanic powder is selected from a group comprising Class C Fly Ash, Class F Fly Ash, volcanic ash, diatomaceous earth, rich hull ash, opal, and a high free lime content powder.
In a further embodiment, the high free lime content powder is selected from a group comprising lime kiln dust, cement kiln dust, slag, granulated blast furnace slag cement, and calcium oxide.
In a further embodiment, the composition further includes an additive selected from a group comprising retarders, shrinkage reducing agents, air entraining agents, aggregates, fillers, extenders, pigments, water reducers, fiber reinforcements, rheology modifiers, and set accelerators.
Other embodiments of the composition are described in detail below and are also part of the present teachings.
For a better understanding of the present embodiments, together with other and further aspects thereof, reference is made to the detailed description.
This application discloses several numerical ranges in the text. The numerical ranges disclosed inherently support any range or value within the disclosed numerical ranges even though a precise range limitation is not stated verbatim in the specification because this present teaching can be practiced throughout the disclosed numerical ranges.
For the purpose of this teaching, the phrase “substantially free” shall mean present in an amount of less than 1 weight percent based on the total weight of the referenced composition.
In compliance with the statute, the present teachings have been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the present teachings are not limited to the specific features shown and described, since the systems and methods herein disclosed comprise preferred forms of putting the present teachings into effect.
Generally, all terms used in the claims are to be interpreted according to their ordinary meaning in the technical field, unless explicitly defined otherwise herein. All references to a/an/the element, composition, apparatus, component, means, step, etc., are to be interpreted openly as referring to at least one instance of the element, composition, apparatus, component, means, step, etc., unless explicitly stated otherwise. The steps of any method disclosed herein do not have to be performed in the exact order disclosed, unless explicitly stated. The use of “first,” “second,” etc. for different features/components of the present disclosure are only intended to distinguish the features/components from other similar features/components and not to impart any order or hierarchy to the features/components.
To aid the Patent Office and any readers of any patent issued on this application in interpreting the claims appended hereto, Applicant does not intend any of the appended claims or claim elements to invoke 35 U.S.C. 112(f) unless the words “means for” or “step for” are explicitly used in the particular claim.
The composition of one embodiment, according to the present teaching, includes, but is not limited to, a Portland cement, a calcium sulfoaluminate cement, calcium aluminosilicate, and a non-Portland hydratable cement powder, a metal alkali salt, or alkali earth metal salt, and wherein the non-Portland hydratable cement is a pozzolanic powder that has a calcium content expressed as oxides of 15 weight percent or more based on the total weight of the non-Portland hydrolysable cement, and wherein the Portland cement content is greater than twenty percent based on the total weight of the non-Portland hydratable cement, and wherein the cementitious composition is essentially free of latex bonding agents, and wherein the cementitious portion of the composition is essentially free from calcium aluminate cement, and wherein the calcium sulfoaluminate cement, or calcium aluminosilicate content is between 0.5 and 70 percent of the compositions, and wherein the metal alkali salt comprises between 0.1 and 10 percent of the composition, and wherein the metal alkali ion of said salt may be lithium, sodium, or potassium and the alkali earth metal ion may be magnesium or calcium, or in combinations thereof, in stoichiometric proportion with a hydrocarboxilic acid to form a pH neutral salt.
The composition of one embodiment, according to the present teaching, includes, but is not limited to, a Portland cement, which has a content greater than 20% based on the total weight of non-Portland hydratable cement, a calcium sulfoaluminate cement, a non-Portland cement, which includes a pozzolanic powder and has a calcium content expressed as oxides of 15 weight percent or more based on the total weight of the non-Portland hydratable cement, and an alkali salt.
According to one embodiment the cementitious composition is substantially free of latex bonding agents and calcium aluminate cement.
According to one embodiment the calcium sulfoaluminate cement, or calcium aluminosilicate content is between 0.5 and 70 percent of the cementitious composition.
According to one embodiment the pozzolanic powder is selected from a group consisting of Class C Fly Ash which was produced from the combustion of sub-bituminous or lignite coal, Class C Fly Ash which was produced by co-combustion of coal with clay and slag, Class F Fly Ash which was produced via co-combustion of coal with clay and slag, volcanic ash, diatomaceous earth, rice hull ash, opal, combinations thereof, or a blend of a high free lime content powder, and wherein the pozzolanic powder contains less than 15 percent calcium oxide and the overall calcium content of the calcium oxides is greater than 15 percent.
According to one embodiment the high free lime content powder is selected from a group consisting of lime kiln dust, cement kiln dust, slag, granulated blast furnace slag cement, calcium oxide, or combinations thereof.
According to one embodiment the alkali salt comprises either an alkali metal ion or an alkaline earth metal ion and comprises between 0.1 and 10 percent of said cementitious composition.
According to one embodiment the alkali metal ion is selected from a group consisting of lithium, sodium, or potassium and said alkaline earth metal ion is selected from a group consisting of magnesium or calcium, or in combinations thereof, in stoichiometric proportion with a hydrocarboxilic acid to form a pH neutral salt.
According to one embodiment the hydrocarboxilic acid is selected from a group consisting of citric, lactic, propioinic based, or combinations thereof.
According to one embodiment the cementitious composition further comprises an additive selected from a group consisting of retarders, shrinkage reducing agents (SRA), air entraining agents (AEA), aggregates, fillers or extenders, pigments, water reducers, fiber reinforcements, rheology modifiers, set accelerators, or combinations thereof.
According to one embodiment the retarder is selected from a group consisting of boric acid, sodium tetraborate, potassium tetraborate, boric oxide, sodium borate, potassium borate, borax pentahydrate, borax decahydrate, sulfate salts, sugars, sugar acids, lignins, or combinations thereof in total consisting of between 0.1 and 2.5 percent of said cementitious composition.
According to one embodiment the shrinkage reducing agents functions by expanding to offset the autogenous shrinkage of the Portland and pozzolanic materials, including certain compounds which can form ettringite in-situ, and/or metal oxides whose hydrates have a lower specific gravity than their oxides.
According to one embodiment the ettringite formation during hydration is the product of various combinations of calcium sulfate cement (CS), calcium sulfoaluminate cement (CSA), calcium sulfate hemihydrate, calcium sulfate, and/or aluminum sulfate.
According to one embodiment the shrinkage reducing agent functions as an inhibitor to moisture egress during hydration and is selected from a group consisting of silica fume, liquid glycol, neopentyl glycol, a liquid glycol adsorbed on a surface of a solid carrier, calcium stearate, magnesium stearate, or a combination thereof.
According to one embodiment the shrinkage reducing agent further comprises a fine particulate metal powder selected from a group of alkali metals, alkali earth metals, aluminum, titanium, zinc, iron, magnesium, manganese, nickel, zirconium, vanadium, or combinations thereof which will react with water to generate hydrogen or oxygen gas.
According to one embodiment the aggregate is selected from a group consisting of pea gravel, river rock, sand, crushed rock, or combinations thereof.
According to one embodiment the filler or extender is selected from a group consisting of ground glass, cenospheres, aluminum oxide, ground nutshells, ground rubber, fine ground hardened Portland cement, fine ground Portland concrete, find ground ceramic, fine ground clay brick, calcium carbonate, nephylene syenite, aluminum trihydrate, pumice, wollastonite, Class F fly ash, kaolin, meta-kaolin, silicon dioxide, dolomite, perlite, slate, other fine ground types of stone, or combinations thereof.
According to one embodiment the pigment is selected from a group consisting of metal oxides including iron oxides, titanium dioxide, or combinations thereof.
According to one embodiment the water reducer is selected from a group consisting of lignin, melamine, naphthalene, polycarboxylate, acrylic latex, or combinations thereof.
According to one embodiment the fiber reinforcement is selected from a group of fibers consisting of nylon, polypropylene, Kevlar, steel, polyester, polyamide, acrylamide, basalt, e-glass, s-glass, or combinations thereof, in various lengths between 0.125 and 2 inches in length.
According to one embodiment the rheology modifier is selected from a group consisting of lignin, melamine, naphthalene, polycarboxylate, acrylic latex, silica fume, fumed silica, precipitated silica, polyethylene oxide, or combinations thereof.
According to one embodiment the set accelerator is selected from a group consisting of lithium carbonate, lithium hydroxide monohydrate, lithium nitrate, lithium fluoride, lithium chloride, lithium borate, lithium acetate, lithium citrate, lithium lactate, lithium gluconate, or combinations thereof.
According to one embodiment the Portland cement, non-Portland cement, and calcium sulfoaluminate cement elements of the cementitious composition are free of the following materials: citric acid; lactic acid; alkali metal; metal carbonate; amine based activators; caustic compounds, such as sodium hydroxide, lithium hydroxide, and potassium hydroxide; geopolymers; non-aqueous thermoset organic polymers, such as polyurethane, epoxy, polyurea, and polyacrylates; bitumen; asphalt; asphalt polymer blends; chloride, iodide, bromide, and fluoride ions and salts; and combinations thereof.
According to one embodiment the cementitious composition can be used to repair roadways, sidewalks, foot paths, driveways, foundations, masonry work, joints for drains and pipes, water tightness of a structure, floors, roofs, beans, stairs, pillar, fencing posts, bridges, culverts, dams, tunnels, wells, water tanks, lighthouses, tennis courts, lamp posts, although not limited thereto.
Referring now to
Referring now to
Referring now to
Referring now to
Referring now to
Upon varying the ratios of the three different cement types, it was found that a strong bond to both Portland concrete and asphalt was obtained when the Portland cement comprised between 20% and 90% of the cementitious portion of the mortar and when the calcium sulfoaluminate cement comprised between 0.5% and 70% of the cementitious portion of the binder.
Upon varying the ratios of the three different cement types, it was found that a strong bond to both Portland concrete and asphalt was obtained when the Portland cement comprised between 20% and 50% of the cementitious portion of the mortar and when the calcium sulfoaluminate cement comprised between 0.5% and 5% of the cementitious portion of the binder.
Upon varying the ratios of the three different cement types, it was found that a strong bond to both Portland concrete and asphalt was obtained when the Portland cement comprised between 50% and 70% of the cementitious portion of the mortar and when the calcium sulfoaluminate cement comprised between 5% and 35% of the cementitious portion of the binder.
Upon varying the ratios of the three different cement types, it was found that a strong bond to both Portland concrete and asphalt was obtained when the Portland cement comprised between 70% and 90% of the cementitious portion of the mortar and when the calcium sulfoaluminate cement comprised between 35% and 70% of the cementitious portion of the binder.
The above description is presented to enable a person skilled in the art to make and use the present teaching, and is provided in the context of a particular application and its requirements. Various modifications to the preferred embodiments will be readily apparent to those skilled in the art, and the generic principles defined herein may be applied to other embodiments and applications without departing from the spirit and scope of the present teaching. Thus, this present teaching is not intended to be limited to the embodiments shown, but is to be accorded the widest scope consistent with the principles and features disclosed herein.
This application is a continuation of U.S. patent application Ser. No. 16/583,819 filed on Sep. 26, 2019, and now abandoned, which claims the benefit of U.S. Provisional Application Ser. No. 62/738,257 filed on Sep. 28, 2018.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4313763 | Turpin, Jr. | Feb 1982 | A |
| 7914685 | Constantz | Mar 2011 | B2 |
| 8519016 | Perez-Pena | Aug 2013 | B2 |
| 8551241 | Perez-Pena | Oct 2013 | B2 |
| 8562736 | Gill | Oct 2013 | B2 |
| 8580030 | Kanduth | Nov 2013 | B2 |
| 8765845 | Biasotti | Jul 2014 | B2 |
| 8864901 | Lloyd | Oct 2014 | B2 |
| 9090506 | Perez-Pena | Jul 2015 | B2 |
| 10221097 | Al-Kutti | Mar 2019 | B1 |
| 20040187740 | Timmons | Sep 2004 | A1 |
| 20040211342 | Sprouts | Oct 2004 | A1 |
| 20180162777 | White | Jun 2018 | A1 |
| Number | Date | Country |
|---|---|---|
| 105819798 | Aug 2016 | CN |
| 2067753 | Jun 2009 | EP |
| 2067753 | Jun 2009 | EP |
| 2714746 | Apr 2014 | EP |
| 2714746 | Apr 2014 | EP |
| 10-20180060672 | Jun 2018 | KR |
| 2012127067 | Sep 2012 | WO |
| WO-2012127067 | Sep 2012 | WO |
| Entry |
|---|
| Socrates, Ioannou, et al.: “Performance characteristics of concrete based on a ternary calcium sulfoaluminate-anhydrite-fly ash cement”. Cement and Concrete Composites vol. 55, published Jan. 2015, pp. 196-204. https://doi.org/10.1016/j.cemconcomp.2014.08.009 9 Pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20200407276 A1 | Dec 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62738257 | Sep 2018 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16583819 | Sep 2019 | US |
| Child | 16594822 | US |