Patent Application
20200148602
The present invention relates to a ceramic and plastic composite and a method for fabricating the same, particularly to a ceramic and plastic composite and a method for fabricating the same, which uses nanoholes to enhance the combined strength of the composite.
With the popularization of 3C electronic products, the aesthetic level of consumers endlessly increases. The products are asked to have high performance, low thickness, light weight, and elegant and aesthetic texture. Since structural components made of ceramic have natural beauty and soft touches, they have better durability and better air tightness and prevent an antenna from shielding compared with the conventional structural components made of metal and plastic. Thus, the structural components made of ceramics are being greeted with increasing approval and popularly applied to 3C electronic products.
However, ceramics are hard and brittle and unsuited for some structures. Thus, how to combine ceramics with plastic structures very well is a difficult problem that the existing technology faces. In general, a plastic member is fixed to the inner surface of the ceramic component through an adhesive. Nevertheless, the plastic member easily drops off from the ceramic component, which results in large difficulty for subsequent process. In addition, various engaging components, such as buckles or indents, are also used to stably combine the ceramic member with the plastic component, but this way will greatly increase the fabrication cost.
To overcome the abovementioned problems, the present invention provides a ceramic and plastic composite and a method for fabricating the same. The fabrication method is very simple. Besides, the present invention greatly improves the combined strength and the air tightness of the composite. The present invention differs from the conventional structure and the method for fabricating the same and solves the afore-mentioned problems of the prior art. The embodiments of the present invention are described as follows.
The primary objective of the present invention is to provide a ceramic and plastic composite and a method for fabricating the same, which etches the surface of a ceramic matrix to have nanoholes with an average diameter ranging between 150 nm and 450 nm. Plastics are injected onto the surface of the baked ceramic matrix to form a plastic layer. The plastic layer more deeply fills the nanoholes to have higher adhesion. Thus, the higher combined strength and air tightness exist between the ceramic matrix and the plastic layer to improve the reliability and the performance of the product.
Another objective of the present invention is to provide a ceramic and plastic composite and a method for fabricating the same, which has a simple fabrication process and a low fabrication cost, easily produces a lightweight product, and decreases the thickness of the product.
To achieve the abovementioned objectives, the present invention provides an method for fabricating a ceramic and plastic composite, which comprises: (a) performing a chemical cleaning treatment on a surface of a ceramic matrix; (b) performing an activation treatment on the surface of the ceramic matrix after the chemical cleaning treatment; (c) performing a microetching treatment on the surface of the ceramic matrix after the activation treatment, so as to form a plurality of microholes; (d) performing a hole reaming treatment on the surface of the ceramic matrix after the microetching treatment, so as to enlarge an average diameter of the plurality of microholes, thereby forming a plurality of nanoholes, and the average diameter of the plurality of nanoholes ranges between 150 nm and 450 nm; (e) performing a surface activating treatment on the surface of the ceramic matrix after the hole reaming treatment; (f) performing a baking process on the surface of the ceramic matrix after the surface activating treatment; and (g) injecting plastics onto the surface of the ceramic matrix after the baking process to form a plastic layer and combining the plastic layer with the surface of the ceramic matrix through the plurality of nanoholes, so as to form the ceramic and plastic composite.
Preferably, the average diameter of the plurality of nanoholes ranges between 200 nm and 400 nm.
Preferably, in operation (a), the chemical cleaning treatment comprises a wax losing treatment and a degreasing treatment.
Preferably, the ceramic matrix comprises Si3N4, WC, ZrO2, or Al2O3.
Preferably, the plastic layer comprises polyamide (PA), polyphenylene sulfide (PPS), poly-(Butylene Terephthalate) (PBT), or polyetherketoneketone (PEAK).
Preferably, in operation (b), the activation treatment is performed by an activator, and the activator further comprises a surfactant of 8-10 percentage weight (wt %), an organic base of 5-8 wt %, a complexing agent of 2-5 wt %, an additive of 2-5 wt %, and water of remaining wt %.
Preferably, in operation (c), the microetching treatment is performed by a microetching processing agent, and the microetching processing agent further comprises acid salt of 50 wt %, a corrosion inhibitor of 1-5 wt %, a surfactant of 1-3 wt %, an additive of 1-3 wt %, and water of remaining wt %.
Preferably, in operation (d), the hole reaming treatment is performed by a hole reaming processing agent, and the hole reaming processing agent further comprises a penetrant of 5-10 wt %, organic acid salt of 35 wt %, a surfactant of 1-3 wt %, an additive of 1-3 wt %, and water of remaining wt %.
Preferably, in operation (e), the surface activating treatment is performed by a surface activating agent, and the surface activating agent comprises an organic acid of 1-10 wt %, a corrosion inhibitor of 1-5 wt %, a surfactant of 1-3 wt %, an additive of 1-3 wt %, and water of remaining wt %.
The present invention also provides a ceramic and plastic composite, which comprises a ceramic matrix and a plastic layer formed by injecting plastics onto a surface of the ceramic matrix. A plurality of nanoholes are distributed on the surface of the ceramic matrix, an average diameter of the plurality of nanoholes ranges between 150 nm and 450 nm, the plastic layer is embedded into the plurality of nanoholes, and the force of combining the plastic layer with the ceramic matrix reaches 300 kg/cm2.
Preferably, the average diameter of the plurality of nanoholes ranges between 200 nm and 400 nm.
Preferably, the ceramic matrix comprises Si3N4, WC, ZrO2, or Al2O3.
Preferably, the plastic layer comprises polyamide (PA), polyphenylene sulfide (PPS), poly-(Butylene Terephthalate) (PBT), or polyetherketoneketone (PEAK).
Compared with the conventional technology, the present invention performs a chemical cleaning treatment, a microetching treatment, a hole reaming treatment, and a surface activating treatment on the surface of a ceramic matrix to form nanoholes with an average diameter ranging between 150 nm and 450 nm. Plastics are injected onto the surface of the baked ceramic matrix to form a plastic layer. The plastic layer more completely fills the nanoholes to have higher adhesion. Thus, the strength of combining the ceramic matrix with the plastic layer is greatly improved, and the air tightness between the ceramic matrix and the plastic layer can be guaranteed.
Below, the embodiments are described in detail in cooperation with the drawings to make easily understood the technical contents, characteristics and accomplishments of the present invention.
Refer to
Refer to
Refer to
Firstly, in Step S10, ceramic powders are pulped and cast into slices, the slices are pressed, molded, and sintered to form ceramics, and the ceramics are mechanically processed, shaped, and polished to form a ceramic matrix.
In Step S20, a chemical cleaning treatment is performed on the surface of the ceramic matrix, wherein a solvent is used to perform a wax losing treatment, and then a degreasing treatment is performed to remove impurities and grease on the surface of the ceramic matrix.
In Step S21, in order to further remove filth on the surface of the ceramic matrix, a cleaning process is performed on the surface of the ceramic matrix one time or several times.
In Step S30, an activation treatment is performed on the surface of the ceramic matrix to form a surface of the ceramic matrix with catalytic properties, which favors the subsequent chemical reactions. The activation treatment is performed by an activator, and the activator further comprises a surfactant of 8-10 percentage weight (wt %), an organic base of 5-8 wt %, a complexing agent of 2-5 wt %, an additive of 2-5 wt %, and water of remaining wt %. The activation treatment is performed at a temperature of 45-55° C. for 5-8 min.
In Step S31, a cleaning process is also performed on the surface of the ceramic matrix one time or several times after the activation treatment.
In Step S40, a microetching processing agent is used to perform a microetching treatment on the surface of the ceramic matrix after the activation treatment, so as to form a plurality of microholes with an average diameter of 20-40 nm. The microetching processing agent further comprises acid salt of 50 wt %, a corrosion inhibitor of 1-5 wt %, a surfactant of 1-3 wt %, an additive of 1-3 wt %, and water of remaining wt %. The microetching treatment is performed at a temperature of 65-85° C. for 30 min.
In Step S41, a cleaning process is also performed on the surface of the ceramic matrix having the microholes one time or several times.
In Step S50, a hole reaming processing agent is used to perform a hole reaming treatment on the surface of the ceramic matrix after the microetching treatment, so as to enlarge an average diameter of the plurality of microholes, thereby forming a plurality of nanoholes, and the average diameter of the plurality of nanoholes ranges between 150 nm and 450 nm, preferably 200-400 nm. In the embodiment, the hole reaming processing agent further comprises a penetrant of 5-10 wt %, organic acid salt of 35 wt %, a surfactant of 1-3 wt %, an additive of 1-3 wt %, and water of remaining wt %. The hole reaming treatment is performed at a temperature of 65-85° C. for 35 min.
In Step S60, a surface activating agent is used to perform a surface activating treatment on the surface of the ceramic matrix after the hole reaming treatment, such that the surface of the ceramic matrix having the nanoholes changes its microstate. The surface activating agent comprises an organic acid of 1-10 wt %, a corrosion inhibitor of 1-5 wt %, a surfactant of 1-3 wt %, an additive of 1-3 wt %, and water of remaining wt %. The surface activating treatment is performed at a temperature of 55-65° C. for 3-5 min.
In Step S61, a cleaning process is also performed on the surface of the ceramic matrix one time or several times after the surface activating treatment.
Afterwards, the process proceeds to Step S70. In Step S70, a baking process is performed on the surface of the ceramic matrix after the surface activating treatment.
Finally, the process proceeds to Step S80. As shown in
In Step S80, the molding temperature is about 140° C., the barrel temperature at the first stage, the second stage, the third stage, and the fourth stage are respectively 290° C., 295° C., 300° C., and 305° C., and the injection pressure is 1750 kgf/cm2.
It is observed that the combined strength of the ceramic and plastic composite of the present invention reaches 300 kg/cm2 under a tensile strength test. The tensile strength test is performed by an electronic universal material testing machine. The testing speed and the testing standard of the electronic universal material testing machine are respectively 10.00 mm/min and 120/0.5 kgf/cm2. A testing specimen is made of a ceramic and plastic composite whose ceramic matrix is ZrO2. The plastic layer of the ceramic and plastic composite is made of poly-(Butylene Terephthalate) (PBT). The area of combining the plastic layer with the ceramic matrix is 0.5 cm2. The specimen has a size of 45×18×1.5 mm.
In conclusion, the effect of combining the ceramic matrix and the plastic layer of the ceramic and plastic composite are quite stable. Besides, the ceramic and plastic composite has a high combined strength. As a result, compared with the conventional technology, the ceramic and plastic composite and the method for fabricating the same of the present invention perform the chemical cleaning treatment, the microetching treatment, the hole reaming treatment, and the surface activating treatment to form the nanoholes having an average diameter of 150-450 nm. Thus, the injection molded plastic layer more completely cover each of the nanoholes to have higher adhesion, thereby effectively improving the combined strength of the ceramic matrix and the plastic layer, guaranteeing the air tightness between the ceramic matrix and the plastic layer, and further stabilizing the quality and performance of the product. In addition, the present invention has a simple fabrication process and a low cost, easily produces lightweight products, decreases thickness, satisfies the market requirement for precise electronic products, and improves the industrial competitiveness of products.
The embodiments described above are only to exemplify the present invention but not to limit the scope of the present invention. Therefore, any equivalent modification or variation according to the shapes, structures, features, or spirit disclosed by the present invention is to be also included within the scope of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 106130046 | Sep 2017 | TW | national |
This application is a Divisional of co-pending application Ser. No. 15/978,749, filed on May 14, 2018, for which priority is claimed under 35 U.S.C. § 120; and this application claims priority of Taiwan Application No. 106130046 filed on Sep. 1, 2017 under 35 U.S.C. § 119, the entire contents of all of which are hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15978749 | May 2018 | US |
| Child | 16743359 | US |