Ceramic heater

Abstract

A ceramic heater has a heater element made of a mixture including MoSi.sub.2 and Si.sub.3 N.sub.4 powder as a main ingredient and silica (SiO.sub.2) powder as an additive, a heater support member made of an electrically insulating ceramic sintered body for supporting the heater element and an electric current supply means for supplying an electric current to the heater element. The composition of the mixture for the heater element is defined so as to satisfy the following formula: 0.035.ltoreq.B/A<0.35 where A is the amount of Si.sub.3 N.sub.4 expressed by mol percent of the total amount of the main ingredient of MoSi.sub.2 and Si.sub.3 N.sub.4 and B is the amount of SiO.sub.2 expressed by mol percent of the total amount of the main ingredient of MoSi.sub.2 and Si.sub.3 N.sub.4.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a ceramic heater, especially a ceramic heater suitably employed as a glow plug in a diesel engine.

2. Description of the Prior Art

In diesel engines, glow plugs are employed for starting engines in an atmosphere of low temperatures and these glow plugs are required to be provided with a heater having a rapidly heating property in order to improve the startability of engines.

The present inventors have developed a ceramic heater comprising a supporting member made of electrically insulating ceramic sintered body, a heater element formed by bonding a ceramic sintered body of MoSi.sub.2 and Si.sub.3 N.sub.4 to a top end of the supporting member, and lead wires embedded in the supporting member and connected to the heater element (U.S. application Ser. Nos. 717,875 and 739,474).

This ceramic heater has oxidization resistance at high temperatures due to the existence of MoSi.sub.2 and thermal shock resistance due to the existence of Si.sub.3 N.sub.4. Therefore, this ceramic heater can be employed in a combustion chamber of a diesel engine without being covered with any covering member and accordingly, exhibits an excellent rapidly heating property.

The temperature of glow plugs is controlled in accordance with the driving condition of engines. In cold districts where the ambient temperature is not more than -15.degree. C., it takes time until the diesel engines become the state of good startability. So, the diesel engines are earnestly desired to have good startability at low temperatures similar to gasoline engines, and accordingly, the heaters are desired to generate heat of about 1300.degree. C. to 1400.degree. C. for the above purpose.

However, the ceramic heater made of MoSi.sub.2 and Si.sub.3 N.sub.4 cannot maintain good durability at a heating temperature of the heater as high as 1300.degree. C. or more.

SUMMARY OF THE INVENTION

One object of the present invention is to provide a ceramic heater having excellent oxidization resistance, thermal shock resistance and a good rapidly heating property.

Another object of the present invention is to provide a ceramic heater having excellent durability at temperatures as high as 1300.degree. C. or more.

The ceramic heater of the present invention comprises a heater element made of a ceramic sintered body which generates heat upon receiving an electric current, a heater support member made of an electrically insulating ceramic sintered body for supporting the heater element and an electric current supply means for supplying an electric current to the heater element.

The heater element used in the ceramic heater of the present invention is formed of a sintered body of a mixture including MoSi.sub.2 and Si.sub.3 N.sub.4 powder as a main ingredient and silica (SiO.sub.2) powder as an additive.

The sintered body for the heater element is composed of MoSi.sub.2, Si.sub.3 N.sub.4 and Si.sub.2 N.sub.2 O converted from part of Si.sub.3 N.sub.4.

In the above described mixture, the composition thereof is defined so as to satisfy the following formula:

0.035.ltoreq.B/A&lt;0.35 where A is the amount of Si.sub.3 N.sub.4 expressed by mol percent of the total amount of the main ingredient of MoSi.sub.2 and Si.sub.3 N.sub.4 and B is the amount of SiO.sub.2 expressed by mol percent of the total amount of the main ingredient of MoSi.sub.2 and Si.sub.3 N.sub.4.

When the ratio B/A reaches 0.035, part of Si.sub.3 N.sub.4 is converted to siliconoxinitride (Si.sub.2 N.sub.2 O) in the sintered body. Si.sub.2 N.sub.2 O is excellent in heat resistance, and especially oxidization resistance at high temperatures and the existence of Si.sub.2 N.sub.2 O enables the long period usage of the heater element of which the heating temperature is not less than 1300.degree. C.

When the ratio B/A reaches 0.35, .alpha.-cristobalite is formed in the sintered body. This .alpha.-cristobalite is converted to .beta.-cristobalite at about 200.degree. C. to generate cracks in the heater element due to distortion occurring when .alpha.-cristobalite is converted to .beta.-cristobalite. From this reason, the existence of .alpha.-cristobalite is not preferable.

SiO.sub.2 itself, aluminum silicate, silica glass, high silicate glass or the like can be employed as the substance supplying SiO.sub.2.

Preferably, the above described mixture is composed of 30 to 65 mol% of MoSi.sub.2 and 70 to 35 mol% of Si.sub.3 N.sub.4. The composition ratio of Si.sub.3 N.sub.4 exceeds 70 mol%, the specific resistance of the heater element is undesirably increased though the thermal shock resistance thereof is improved.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a sectional view of a glow plug provided with a ceramic heater according to the present invention;

FIG. 2 is a view illustrating one producing step of the ceramic heater;

FIGS. 3, 4, 5, 6 and 7 are graphs showing the experimental results on the ceramic heater according to the present invention; and

FIG. 8 is a view showing one example of conditions of one experiment.

DETAILED DESCRIPTION OF THE EMBODIMENTS

FIG. 1 illustrates a glow plug provided with a ceramic heater according to the present invention.

The ceramic heater is composed of a rod-shaped supporting member 2 formed of a ceramic sintered body, a heater element 1 having a U-shaped cross section, formed of a ceramic sintered body and bonded to an end surface of the supporting member 2, and a pair of lead wires 3a and 3b embedded in the supporting member 2. A top end of each of the lead wires 3a and 3b is connected to the heater element 1.

A metallic sleeve 4 is secured to the outer periphery of the supporting member 2 and a metallic body 5 is secured to the outer periphery of the metallic sleeve 4.

A rear end of the lead wire 3a extends to a base end of the supporting member 2 and is in contact with a metallic cap 6 fit in the base end of the supporting member 2.

The metallic cap 6 is electrically connected to an electric power source (not shown) through a nickel line 7. The glow plug having the above described structure is secured to an engine so as to be exposed to the interior of a combustion chamber thereof by a screw 51 formed in the metallic body 5.

The supporting member 2 is formed of a sintered body of a mixture of Si.sub.3 N.sub.4 and Al.sub.2 O.sub.3 (alumina).

The heater element 1 is formed of a sintered body of a mixture of MoSi.sub.2, Si.sub.3 N.sub.4 and SiO.sub.2. The composition ratio of each material of the above mixture is adjusted so as to satisfy the following formula: 0.035.ltoreq.B/A&lt;0.35 where A is the amount of Si.sub.3 N.sub.4 expressed by mol percent of the total amount of the main ingredient of MoSi.sub.2 and Si.sub.3 N.sub.4 and B is the amount of SiO.sub.2 expressed by mol percent of the total amount of the main ingredient of MoSi.sub.2 and Si.sub.3 N.sub.4.

In the obtained heater element, part of Si.sub.3 N.sub.4 is converted to Si.sub.2 N.sub.2 O.

FIG. 2 is a view explaining one producing step of the ceramic heater according to the present invention.

At first, MoSi.sub.2 powder, Si.sub.3 N.sub.4 powder, SiO.sub.2 powder and organic solvent are mixed and a plurality of ceramic sheets 1' for the heater element are formed from the obtained mixture by a doctor blade method.

Next, Si.sub.3 N.sub.4 powder, Al.sub.2 O.sub.3 powder and organic solvent are mixed and a plurality of ceramic sheets 2' for the supporting member are formed from the obtained mixture by a doctor blade method.

The obtained ceramic sheets 1' and 2' are piled on one another, respectively as shown in FIG. 2 and the lead wires 3a ad 3b are also disposed as shown in FIG. 2.

Then, the piled ceramic sheets 1' and 2' with the lead wires 3a and 3b are hot-pressed at a temperature of 1600.degree. C. and under a pressure of 500 Kg/cm.sup.2 to obtain a ceramic heater shown in FIG. 1.

Hereinafter, the experimental results on the heater element of the ceramic heater according to the present invention will be explained.

A mixture powder composed of MoSi.sub.2 powder(average particle diameter: 0.9 .mu.m), Si.sub.3 N.sub.4 powder (average particel diameter: 35 .mu.m) is mixed with SiO.sub.2 powder(average particle diameter: 1 .mu.m) as an additive. Then, the obtained mixture is sintered to obtain a sintered body for a heater element.

The relation between the composition ratio of the materials and the specific resistance of the obtained sintered body is shown in FIG. 3.

In FIG. 3, the composition ratio of Si.sub.3 N.sub.4 is shown by mol percent of the main ingredient of MoSi.sub.2 and Si.sub.3 N.sub.4, and the composition ratio of SiO.sub.2 is shown by mol percent of the total amount of the main ingredient of MoSi.sub.2 and Si.sub.3 N.sub.4.

As shown in FIG. 3, the specific resistance is increased with the increase of the amount of SiO.sub.2.

Next, the structure of the sintered bodies having different amounts of Si.sub.3 N.sub.4 and SiO.sub.2 is examined by a X ray analysis. The obtained result is shown in the following table. In this table, marks .circle. mean existence of substance and marks -- mean nonexistence of substance.

______________________________________ ##STR1## 0 0.035 0.14 0.35______________________________________Si.sub.3 N.sub.4 O O O OMoSi.sub.2 O O OSi.sub.2 N.sub.2 O -- O O O.alpha.-cristobalite -- -- -- O______________________________________

As shown in the above table, when the ratio B/A reaches 0.035, part of Si.sub.3 N.sub.4 is converted to Si.sub.2 N.sub.2 O. Si.sub.2 N.sub.2 O is excellent in oxidization resistance at high temperatures and accordingly serves to improve the heat resistance of the sintered body.

When the amount of additive SiO.sub.2 is increased and the ratio B/A reaches 0.35, .alpha.-cristobalite begins to be formed.

As described above, the existence of .alpha.-cristobalite is not preferable since cracks are formed when the sintered bodies containing .alpha.-cristobalite are heated.

From the above result, the amount of SiO.sub.2 for the heater element must be defined so as to satisfy the formula 0.035.ltoreq.B/A&lt;0.35.

FIGS. 4 and 5 show the relation between the amount of SiO.sub.2 added to the main ingredient of MoSi.sub.2 -70 mol%Si.sub.3 N.sub.4 and MoSi.sub.2 -35 mol%Si.sub.3 N.sub.4 and the density of the obtained sintered bodies.

In the former case, when the amount of SiO.sub.2 is about 10 to 20 mol%, high density can be obtained and accordingly, heat resistance of the sintered body can be improved. When the amount of SiO.sub.2 is 25 mol%, the ratio B/A is larger than 0.35 and .alpha.-cristobalite is formed in the sintered body.

In the latter case, when the amount of SiO.sub.2 is about 5 to 10 mol%, high density can be obtained and when the amount of SiO.sub.2 is 13 mol%, .alpha.-cristobalite is formed in the obtained sintered body.

As is apparent from the experimental results shown in FIGS. 4 and 5, the addition of SiO.sub.2 in such an amount as satisfying the formula of 0.035.ltoreq.B/A&lt;0.35 serves to increase the density of the obtained sintered body.

FIG. 6 shows the relation between the amount of additive SiO.sub.2 and the thermal expansion coefficient of the obtained sintered bodies.

As is apparent from FIG. 6, in all of the sintered bodies of MoSi.sub.2 -70 mol%Si.sub.3 N.sub.4, MoSi.sub.2 -50 mol%Si.sub.3 N.sub.4 and MoSi.sub.2 -35 mol%Si.sub.3 N.sub.4, the thermal expansion coefficient thereof scarcely increases by the addition of SiO.sub.2 in the amount within the range defined in the present invention.

FIG. 7 shows the result of examination on the variation of the resistance of a glow plug(resistance at a normal temperature is 0.18.OMEGA.) formed by sintering a mixture powder of MoSi.sub.2 -70mol% Si.sub.3 N.sub.4 with an additive powder of 25mol% of SiO.sub.2 (B/A.apprxeq.0.035) and securing the obtained sintered body to a supporting member made of a sintered body of Si.sub.3 N.sub.4 -50mol%Al.sub.2 O.sub.3.

In this experiment, the glow plug is subjected to a number of cooling and heating cycles as shown in FIG. 8 by intermittently applying electric current to the glow plug, and the variation of the resistance of the heater elements of which the heating temperature is 1300.degree. C. and 1400.degree. C., respectively, is examined.

As is shown in FIG. 7, the resistance of the heater element is changed only within 10% when the amount of SiO.sub.2 is 2.5 mol%.

In contrast, when the glow plug having a heater element made of a sintered body of MoSi.sub.2 -70mol%Si.sub.3 N.sub.4 without SiO.sub.2 being added thereto is subjected to the same cooling and heating cycles, the resistance of the heating element is increased over 10% with the increase of the number of cycles.

When the amount of SiO.sub.2 is 25 mol%(B/A&gt;0.35), the heater element is damaged due to cracks formed therein at the moment of generating heat.

From the above experimental results, it has become clear that by adding not less than 2.5 mol% of SiO.sub.2 powder to a mixture powder of MoSi.sub.2 -70 mol%Si.sub.3 N.sub.4, Si.sub.2 N.sub.2 O having excellent oxidization resistance at high temperatures is formed in the obtained heater element. Furthermore, in this case, the density of the obtained heater element is increased as shown in FIGS. 4 and 5 to make the structure thereof compact. This results in the heat resistance of the heater element is largely improved.

However, when the amount of additive SiO.sub.2 exceeds 25 mol%, .alpha.-cristobalite is formed in the heater element. And when this .alpha.-cristobalite is phase-transferred to .alpha.-cristobalite, distortion is generated to damage high temperature heater element.

As described above, the ceramic heater of the present invention is excellent in its rapidly heating property and exhibits good durability at temperatures as high as 1300.degree. C.

Accordingly, the ceramic heater of the present invention is suitable to a heater for a glow plug of a diesel engine.

Claims

1. A ceramic heater comprising:

a heater element made of a ceramic sintered body which generates heat upon receiving an electric current;

a heater support member made of a electrically insulating ceramic sintered body, said heater element being affixed to one end of said heater support member; and

an electric current supply means for supplying an electric current to said heater element;

said heater element being a sintered body of a mixture including MoSi.sub.2 and Si.sub.3 N.sub.4 powder as a main ingredient and SiO.sub.2 powder as an additive; said sintered body being composed of MoSi.sub.2, Si.sub.3 N.sub.4 and siliconoxinitride converted from part of Si.sub.3 N.sub.4 ;

said mixture having a composition expressed by the formula: 0.035.ltoreq.B/A&lt;0.35 where A is the amount of Si.sub.3 N.sub.4 powder expressec by mol percent of the total amount of said main ingredient and B is the amount of SiO.sub.2 powder expressed by mol percent of the total amount of said main ingredient.

2. A ceramic heater according to claim 1, wherein said main ingredient is composed of 30 to 65 mol% of MoSi.sub.2 powder and 70 to 35 mol% of Si.sub.3 N.sub.4 powder.

3. A ceramic heater according to claim 1, wherein said SiO.sub.2 powder is supplied from a material selected from the group consisting of silica, aluminum silicate, silica glass and high silicate glass.

4. A ceramic heater according to claim 1, wherein said electric current supply means comprises a pair of lead wires for connecting said heater element to an electric power source, and said lead wires are embedded within said heater support member.

5. A ceramic heater according to claim 4, wherein said heater element is integrally sintered with said heater support member.