Claims
- 1. A method of preparing a ceramic material with increased crystallinity, said method comprising heating a modified R.sub.3 SINH-containing silazane polymer in an inert atmosphere or in a vacuum to a temperature of at least 750.degree. C. until said modified R.sub.3 SiNH- containing silazane polymer is converted to a ceramic material with increased crystallinity relative to a non-modified R.sub.3 SiNH-containing silazane polymer heated under the same conditions, wherein said modified R.sub.3 SiNH-contianing silazane polymer is prepared by mixing the non-modified R.sub.3 SiNH-containing silazane polymer with an effective, crystallinity increasing, amount of an inorganic compound selected form the group consisting of iron III oxide, iron III octoate, iron II acetylacetonate, iron III chloride, cobalt II octoate, copper II octoate, nickel II octoate and noncarbonyldiiron.
- 2. A process as defined in claim 1 wherein said non-modified R.sub.3 SiNH-containing silazane polymer is prepared by contacting and reacting in an inert, essentially anhydrous atmosphere, a chlorine-containing disilane or a mixture of chlorine-containing disilanes of general formula
- (Cl.sub.b R.sub.c.sup.' Si).sub.2
- with a disilazane of general formula
- (R.sub.3 Si).sub.2 NH
- at a temperature in the range of 25.degree. C. to 300.degree. C. while distilling by-produced volatile products, wherein R' is a vinyl group, an alkyl group of 1-3 carbon atoms, or a phenyl group; R is a hydrogen atom, a vinyl group, an alkyl group of 1-3 carbon atoms, or a phenyl group; b has a value of 0.5-3; c has a value of 0-2.5; and the sum of (b+c) is equal to three.
- 3. A process as defined in claim 1 wherein said non-modified R.sub.3 SiNH-containing silazane polymer is prepared by contacting and reacting in an inert, essentially anhydrous atmosphere, an organochlorosilane or a mixture of organochlorosilanes of general formula
- R.sub.n.sup.' SiCl.sub.(4-n)
- with a disilazane of general formula
- (R.sub.3 Si).sub.2 NH
- at a temperature in the range of 25.degree. C. to 300.degree. C. while distilling by-produced volatile products, wherein R' is a vinyl group, an alkyl group of 1-3 carbon atoms, or a phenyl group; R is a hydrogen atom, a vinyl group, an alkyl group of 1-3 carbon atoms, or a phenyl group; and n has a value of 1 or 2.
- 4. A method as defined in claim 1 wherein said modified R.sub.3 SiNH-containing silazane polymer is heated to a temperature of at least 1000.degree. C.
- 5. A method as defined in claim 2 wherein said modified R.sub.3 SiNH-containing silazane polymer is heated to a temperature of at least 1000.degree. C.
- 6. A method as defined in claim 3 wherein said modified R.sub.3 SiNH-containing silazane polymer is heated to a temperature of at least 1000.degree. C.
- 7. A method as defined in claim 4 wherein said iron compound is selected from the group consisting of iron (III) octoate, iron (III) oxide, iron (II) acetylacetonate, iron (III) chloride, and nonocarbonyl diiron.
- 8. A method as defined in claim 5 wherein said iron compound is selected from the group consisting of iron (III) octoate, iron (III) oxide, iron (II) acetylacetonate, iron (III) chloride, and nonocarbonyl diiron.
- 9. A method as defined in claim 6 wherein said iron compound is selected from the group consisting of iron (III) octoate, iron (III) oxide, iron (II) acetylacetonate, iron (III) chloride, and nonocarbonyl diiron.
- 10. A method as defined in claim 4 wherein said cobalt compound is cobalt (II) octoate.
- 11. A method as defined in claim 5 wherein said cobalt compound is cobalt (II) octoate.
- 12. A method as defined in claim 6 wherein said cobalt compound is cobalt (II) octoate.
- 13. A method as defined in claim 4 wherein said nickel compound is nickel (II) octoate.
- 14. A method as defined in claim 5 wherein said nickel compound is nickel (II) octoate.
- 15. A method as defined in claim 6 wherein said nickel compound is nickel (II) octoate.
- 16. A method as defined in claim 4 wherein said copper compound is copper (II) octoate.
- 17. A method as defined in claim 5 wherein said copper compound is copper (II) octoate.
- 18. A method as defined in claim 6 wherein said copper compound is copper (II) octoate.
- 19. A ceramic material as prepared by the method of claim 1.
- 20. A ceramic material as prepared by the method of claim 2.
- 21. A ceramic material as prepared by the method of claim 3.
- 22. A ceramic material as prepared by the method of claim 4.
- 23. A ceramic material as prepared by the method of claim 5.
- 24. A ceramic material as prepared by the method of claim 6.
- 25. A method of preparing a ceramic material with increased crystallinity, said method comprising heating a modified R.sub.3 SiNH-containing silazane polymer in an inert atmosphere or in a vacuum to a temperature of at least 1000 degrees C. until said modified R.sub.3 SiNH-containing silazane polymer is converted to a ceramic material with increased crystallinity relative to a non-modified R.sub.3 SiNH-containing silazane polymer heated under the same conditions wherein said increased crystallinity is in the form of increased levels of alpha-SiC, beta-SiC, alpha-Si.sub.3 N.sub.4, or beta-Si.sub.3 N.sub.4, wherein said modified R.sub.3 SiNH-containing silazane polymer is prepared by mixing the non-modified R.sub.3 SiNH-containing silazane polymer with an effective, crystallinity increasing amount of an inorganic compound selected from the group consisting of iron III oxide, iron III octoate, iron II acetylacetonate, iron III chloride, cobalt II octoate, copper II octoate, nickel II octoate and noncarbonyldiiron.
- 26. A method as defined in claim 25 wherein said non-modified R.sub.3 SiNH-containing silazane polymer is prepared by contacting and reacting in an inert, essentially anhydrous atmosphere, a chlorine-containing disilane or a mixture of chlorine-containing disilanes of general formula
- (Cl.sub.b R.sub.c.sup.' Si).sub.2
- with a disilazane of general formula
- (R.sub.3 Si).sub.2 NH
- at a temperature in the range of 25.degree. C. to 300.degree. C. while distilling by-produced volatile products, wherein R' is a vinyl group, an alkyl group of 1-3 carbon atoms, or a phenyl group; R is a hydrogen atom, a vinyl group, an alkyl group of 1-3 carbon atoms, or a phenyl group; b has a value of 0.5-3; c has a value of 0-2.5; and the sum of (b+c) is equal to three.
- 27. A method as defined in claim 25 wherein said non-modified R.sub.3 SiNH-containing silazane polymer is prepared by contacting and reacting in an inert, essentially anhydrous atmosphere, an organochlorosilane or a mixture of organochlorosilanes of general formula
- R.sub.n.sup.' SiCl.sub.(4-n)
- with a disilazane of general formula
- (R.sub.3 Si).sub.2 NH
- at a temperature in the range of 25.degree. C. to 300.degree. C. while distilling by-produced volatile products, wherein R' is a vinyl group, an alkyl group of 1-3 carbon atoms, or a phenyl group; R is a hydrogen atom, a vinyl group, an alkyl group of 1-3 carbon atoms, or a phenyl group; and n has a value of 1 or 2.
Parent Case Info
This application is a continuation-in-part of application Ser. No. 652,939, filed Sept. 21, 1984, now abandoned.
US Referenced Citations (2)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
652939 |
Sep 1984 |
|