Patent Grant
8268234
1. Field of the Invention
The present invention relates to processing of cermet materials, and more specifically, it relates to the fabrication of cermet materials by molten metal infiltration of metals into ceramic bodies.
2. Description of Related Art
Ceramic materials have been used in advanced body armor systems to reduce weight and still defeat armor penetrating projectles. Such projectiles can be defeated if the point of the projectiles can be blunted by the armor when a harder material (like ceramics and/or cermets) is used at the impact point. Body armor has required one of the lightest weight ceramic, boron carbide, with a fiber polymer composite backing to meet past requirements for the best body armor. New threats and the need for lighter loads for solders to carry into battle have driven new requirements for improved materials in body armor and vehicle armor. Current ceramic and cermet armors can not achieve this new requirement.
It is an object of the present invention to provide cermet materials that are processed by molten metal infiltration of ceramics.
It is another object of the present invention to provide cermet materials that have properties that are useful in armor applications.
Still another object is to provide a process that is cost effective to form molten metal infiltrated cermets with properties useful in applications like armor, cutting tools, wear parts, etc.
These and other objects will be apparent based on the disclosure herein.
Prior to the parent application, lightweight cermets fabricated by the molten metal infiltration process were limited to boron carbide (B4C) infiltrated with aluminum alloy. See U.S. Pat. No. 4,718,941. The present invention utilizes developments in the areas of lightweight ceramics, lightweight alloys, and finer starting ceramic powders to provide new cermets with improved properties and applications. These new cermets have lower density and/or higher hardness than the B4C cermet. By incorporating other new ceramics into the B4C powders or as a substitute for the B4C, lower densities and/or higher hardness are achieved in these new cermets. The ceramic powders have much finer particle size (nano-powders, 40 μm to 900 μm) than those previously used (B4C powders) which significantly reduces grain size of the cermet microstructure and improves the cermet properties over that of prior cermets (B4C—Al). These improved cermets also use lower density alloys to improve these properties and to reduce the overall cermet density.
The B4C—Al cermet was developed for opaque armor applications, both military and civilian. The present cermets can replace the B4C—Al cermets in these applications and, due to the improved properties, could find new applications in industry and in the military complex. The new applications include electrical switches, medicial instruments, wear parts and cutting tools.
The accompanying drawings, which are incorporated into and form a part of the disclosure, illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.
Recent development of a wide variety of nano-powders has resulted in the improvement of many products and development of other products for new applications. Similar improvements are gained by applying this nano-powder technology to cermets. This is especially beneficial in the molten metal processing of cermets since lower temperatures and shorter times at temperature allow consolidation of the present cermets. These processing advantages prevent coarsing of the microstructure during processing and provide a finer grain structure in the cermets, which increases performance over previous cermets. This finer microstructure is enhanced further by the additions of lighter weight and/or harder ceramic powders in the nano-powder state.
The partial or complete substitution of boron carbide powder with these ceramic nano-powders before molten metal infiltration gives lighter weight and/or harder cermets, which results in a direct improvement in ballistic performance for armor applications. These new ceramic additions include borides, nitrides, and/or carbides of the lighter elements, e.g., Al, B, C, Mg, Be, Ca, Si, Li, Ti and V. These new ceramic substitutions also allow the additional options of using lighter weight alloys that wet the compacted ceramic bodies used in the molten metal infiltration process. A wider variety of alloys can now be used for molten metal infiltration due to improved wetting between these blended ceramics and the molten alloys. These alloys include, but are not limited to, combinations of the light elements of Al, Mg, Be, Li, Ti, V, etc. The general properties of desired alloys usable in the present invention are low density alloys (less than 2.8 gm/cc) that wet the ceramics at a reasonable temperature (<1150 C) during a relatively short infiltration period (<3 hours).
The new ceramic powders can be formed from the elements or from the pre-reacted compounds of borides, nitrides and/or carbides. Blending of the compounds is preferred in most cases due the reactive nature and/or toxicity of some elements. Blends of these nano-powder ceramics can be prepared by several methods (flame spray, milling, and/or sol-gel processes). Nano-powders of B4C can be mixed with various amounts of other nano-powders to make up the final powder blend needed to form the powder compact for molten metal infiltration. The powders should be pressed to greater than 55% of theoretical density for armor applications. Other applications may require less ceramic and more metal content for higher tensile strength and toughness but less hardness.
The metal alloys used in the molten metal infiltration process are selected for their wetability with the specific ceramic composite at a low infiltration temperature (<1150 C). The better the wetting of the molten alloy to the cermaic, the shorter the time at temperature for nearly complete infiltration (>98%). Similarly, the lower the infiltration temperature required, the shorter the time needed to complete the infiltration. Less time at the infiltration temperature results in a finer microstructure and better performance of the cermet. A typical example of forming these new cermets is the selection of the nano-powder blend of boron carbide aluminum boride and magnesium boride. This powder blend would be cold pressed to greater than 55% density and heat treated in a protective environment (vacuum, argon, etc.) to form a porous component that would have a density lower than B4C if pressed alone. A metal alloy (with good wetting characteristics for this component) would be melted in contact with the ceramic component at a low temperature in a protective atmosphere (vacuum, argon, etc.) to achieve nearly complete infiltration in a short time (<1 hour). Subsequent heat treatments of the infiltrated component could be made to adjust the properties of the cermet for a specific application. Use of the toxic element, Be, is possible if the compositions selected for the ceramic compound and/or metal alloy does not exceed toxicity limits set for this element for the specific application.
The foregoing description of the invention has been presented for purposes of illustration and description and is not intended to be exhaustive or to limit the invention to the precise form disclosed. Many modifications and variations are possible in light of the above teaching. The embodiments disclosed were meant only to explain the principles of the invention and its practical application to thereby enable others skilled in the art to best use the invention in various embodiments and with various modifications suited to the particular use contemplated. The scope of the invention is to be defined by the following claims.
This application is a continuation-in-part of and claims priority to U.S. patent application Ser. No. 08/829,034 titled “Novel Cermets and Molten Metal Infiltration Method and Process for their Fabrication,” filed Mar. 31, 1997, now abandoned, incorporated herein by reference. This application is a Continuation-in-part of and claims priority to U.S. patent application Ser. No. 10/260,121 titled “Process for Fabrication of Cermets,” filed Sep. 27, 2002, now U.S. Pat. No. 7,879,285, incorporated herein by reference.
The United States Government has rights in this invention pursuant to Contract No. DE-AC52-07NA27344 between the United States Department of Energy and Lawrence Livermore National Security, LLC.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3026210 | Cobble | Mar 1962 | A |
| 3734997 | Mandorf, Jr. et al. | May 1973 | A |
| 4150317 | Laska et al. | Apr 1979 | A |
| 4605440 | Halverson et al. | Aug 1986 | A |
| 4718941 | Halverson et al. | Jan 1988 | A |
| 4906295 | Miyamoto et al. | Mar 1990 | A |
| 5041248 | Renlund et al. | Aug 1991 | A |
| 5249621 | Aghajanian et al. | Oct 1993 | A |
| 5296419 | White et al. | Mar 1994 | A |
| 5308422 | Askay et al. | May 1994 | A |
| 5458705 | Mazur et al. | Oct 1995 | A |
| 5511603 | Brown et al. | Apr 1996 | A |
| 5518974 | Krahn et al. | May 1996 | A |
| 5595622 | Pyzik et al. | Jan 1997 | A |
| 5624505 | Mazur et al. | Apr 1997 | A |
| 5628938 | Sangeeta et al. | May 1997 | A |
| 5676907 | Ritland et al. | Oct 1997 | A |
| 5702542 | Brown et al. | Dec 1997 | A |
| 5735332 | Ritland et al. | Apr 1998 | A |
| 6025065 | Claussen et al. | Feb 2000 | A |
| Number | Date | Country |
|---|---|---|
| 2148270 | May 1985 | GB |
| Number | Date | Country | |
|---|---|---|---|
| 20120153548 A1 | Jun 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10260121 | Sep 2002 | US |
| Child | 13016459 | US | |
| Parent | 08829034 | Mar 1997 | US |
| Child | 10260121 | US |