Patent Grant
10913863
The present disclosure relates to the field of coating materials, and in particular to a cesium tungsten bronze-based self-cleaning nano heat-insulation coating material and method of preparing the same.
It is reported that building energy consumption accounts for 40% of the global energy consumption, and more than 50% of the building energy consumption comes from the energy consumption of air conditioners. Particularly in China, heating, air conditioners, fans and household appliances account for 95% of the building energy consumption. Therefore, heat insulation is of great significance in reducing building energy consumption. In order to ensure adequate indoor lighting and aesthetic appearance of the buildings, large-area windows or glass curtain walls are increasingly common in modern buildings to replace the previous concrete structures. As such, cooling in summer and heating in winter will inevitably cause extra energy consumption. Without reducing the area of building glass, the goal of energy saving can be achieved by improving the heat insulation performance of glass. A lot of attempts and researches have been made on glass insulation in China and abroad. At present, mainstream energy-saving and heat-insulation products include heat reflective coated glass, vacuum glass, hollow glass and so on. Heat reflective coated glass has a notable heat insulation performance, but causes problem of light pollution due to its high reflectivity of visible light. Though the hollow glass achieves a certain heat insulation effect, the heat insulation performance is unsatisfactory. On the basis of hollow glass, vacuum glass achieves thermal insulation by removing the air in the gap between the glasses. This kind of glass requires good airtightness and is expensive. Filmed glass is glass with a film made from an infrared shielding material attached onto its surface. This technology provides a good solution to the problem associated with the heat insulation of glass; however, the cost is extremely high, and thus this technology cannot be widely used.
Cesium tungsten bronze has good visible light transmittance and infrared absorption characteristics, and thus receives extensive attentions. Novel transparent heat-insulation coating material, which may be prepared with cesium tungsten bronze, is currently not available in the market. Its poor dispersibility is a main factor limiting its application. Moreover, most of the heat-insulation coating materials currently available in the market are oil-based heat-insulation coating materials having a high content of volatile organic compounds (VOCs), which causes hazards to the health of construction workers and users. Therefore, there is a need for developing a water-based transparent heat-insulation coating material having excellent visible light transmittance and good dispersibility.
In view of the above technical problems, the present disclosure provides a cesium tungsten bronze-based self-cleaning nano heat-insulation coating material and method of preparing the same.
The present disclosure provides a method for preparing a cesium tungsten bronze-based self-cleaning nano heat-insulation coating material, which comprises:
preparing cesium tungsten bronze nanoparticles by hydrothermal method using WCl6 and CsOH.5H2O as raw materials, PVP as a surfactant and acetic acid as an acid catalyst;
preparing TiO2 nanoparticles from TiCl4 solvothermally; and
ball milling and dispersing the cesium tungsten bronze nanoparticles, the TiO2 nanoparticles, a silane coupling agent and water to obtain an aqueous slurry containing cesium tungsten bronze/TiO2 composite particles; and adjusting the concentration of the aqueous slurry containing cesium tungsten bronze/TiO2 composite particles, to obtain a self-cleaning nano heat-insulation coating material.
In the preparation method according to the present disclosure, preparing cesium tungsten bronze nanoparticles comprises:
stirring 10-15 parts by weight of WCl6, 2-4 parts by weight of CsOH.5H2O, 30-40 parts by weight of acetic acid, and 15-20 parts by weight of PVP together, to obtain a first mixture; and
heating the first mixture to 70° C.-80° C., and maintaining this temperature for 1 h-2 h; and then heating the first mixture further to 220° C.-240° C., and reacting for 20 h-30 h at this temperature, followed by centrifugation and oven drying to obtain the cesium tungsten bronze nanoparticles.
In the preparation method according to the present disclosure, preparing TiO2 nanoparticles comprises:
mixing 10-15 parts by weight of TiCl4 and 30-40 parts by weight of anhydrous ethanol solvothermally, to obtain a second mixture; and
then reacting the second mixture at 180° C. for 8 h, followed by centrifuging and oven drying, to obtain TiO2 nanoparticles.
In the preparation method according to the present disclosure, ball milling and dispersing may comprises:
ball milling 40-50 parts by weight of cesium tungsten bronze nanoparticles, 5-10 parts by weight of TiO2 nanoparticles, 1-2 parts by weight of sodium polyacrylate coupling agent (SN5040) and 40-50 parts by weight of deionized water, to obtain an aqueous slurry containing cesium tungsten bronze/TiO2 composite particles.
In the preparation method according to the present disclosure, the rotation speed of the ball mill machine for ball milling is 500 r/min-5000 r/min, and the ball milling time is 4 h-12 h.
The present disclosure further provides a self-cleaning nano heat-insulation coating material prepared from the method described above.
In the present disclosure, cesium tungsten bronze nanoparticles are prepared through hydrothermal method.
The cesium tungsten bronze nanoparticles have a large specific surface area, thus having a positive effect on the improvement of infrared absorptivity. The TiO2 nanoparticles have good dispersibility in water, and virtually do not block visible light.
Further, in the present disclosure, an aqueous slurry containing cesium tungsten bronze/TiO2 composite particles may be prepared by ball milling and dispersing, in which the well-dispersed cesium tungsten bronze nanoparticles and TiO2 nanoparticles are beneficial to the improvement of the visible light transmittance and the infrared blocking performance of the coating.
A coating obtained by applying the self-cleaning nano heat-insulation coating material of the present disclosure has a good hydrophilicity, which effectively prevents contamination of the nano-coating by organic oils and inorganic dusts, thereby greatly enhancing the anti-fouling performance and extending the service life of the coating.
The self-cleaning nano heat-insulation coating material of the present disclosure is a water-based heat-insulation coating material, which has low content of volatile organic compounds (VOCs) and causes no hazards to the environment and the health of construction workers and users.
The present disclosure will be further described in connection with embodiments with reference to the accompanying drawings, in which
Novel transparent heat-insulation coating material prepared with cesium tungsten bronze is currently not available in the market due its poor dispersibility which limits its application. However, the present disclosure provides a cesium tungsten bronze-based self-cleaning nano heat-insulation coating material and method of preparing the same. The heat-insulation coating material is a water-based coating material having excellent light transmittance and good dispersibility.
The method for preparing the self-cleaning nano heat-insulation coating material provided comprises preparing cesium tungsten bronze nanoparticles by hydrothermal method using WCl6 and CsOH.5H2O as raw materials, polyvinyl pyrrolidone (PVP) as a surfactant and acetic acid as an acid catalyst; then preparing TiO2 nanoparticles by solvothermally hydrolyzing TiCl4 which acts as a major raw material; and finally, ball milling and dispersing the cesium tungsten bronze nanoparticles, the TiO2 nanoparticles, a silane coupling agent, and water to obtain an aqueous slurry containing cesium tungsten bronze/TiO2 composite particles, and adjusting the concentration of the aqueous slurry containing cesium tungsten bronze/TiO2 composite particles, to obtain a self-cleaning nano heat-insulation coating material. Herein, the aqueous slurry containing cesium tungsten bronze/TiO2 composite particles is dispersed by high-speed shearing and ultrasonically.
In a further embodiment, the preparation process for cesium tungsten bronze nanoparticles comprises:
stirring 10-15 parts by weight of WCl6, 2-4 parts by weight of CsOH.5H2O, 30-40 parts by weight of acetic acid, and 15-20 parts by weight of PVP together, to obtain a first mixture; and heating the first mixture to 70° C.-80° C., and maintaining this temperature for 1 h-2 h; and then heating the first mixture further to 220° C.-240° C., and reacting for 20 h-30 h at this temperature, followed by centrifugation and oven drying, to obtain the cesium tungsten bronze nanoparticles.
Herein, suitable amount of water may be added to the first mixture. The first mixture is heated in a reactor having an internal lining made with a material that does not react with the first mixture. Preferably, the internal lining of the reactor is made from p-polyphenol (PPL). It should be understood that polytetrafluoroethylene (PTFE) may also be used as the internal lining of the reactor.
In a further embodiment, the preparation process of TiO2 particles comprises:
mixing 10-15 parts by weight of TiCl4 and 30-40 parts by weight of anhydrous ethanol solvothermally, to obtain a second mixture; and
then reacting the second mixture at 180° C. for 8 h, followed by centrifuging and oven drying, to obtain TiO2 nanoparticles.
Herein, the second mixture is also heated in a reactor having an internal lining made with a material that does not react with the second mixture. Preferably, the internal lining of the reactor is made with p-polyphenol (PPL). It should be understood that polytetrafluoroethylene (PTFE) may also be used as the internal lining of the reactor.
Further, the preparation process for the aqueous slurry containing cesium tungsten bronze/TiO2 composite particles comprises
ball milling 40-50 parts by weight of cesium tungsten bronze nanoparticles, 5-10 parts by weight of TiO2 nanoparticles, 1-2 parts by weight of sodium polyacrylate coupling agent (SN5040) and 40-50 parts by weight of deionized water, to obtain an aqueous slurry containing cesium tungsten bronze/TiO2 composite particles.
During the preparation of the aqueous slurry containing the cesium tungsten bronze/TiO2 composite particles, the rotation speed of the ball mill machine for ball milling is 500 r/min-5000 r/min, and the ball milling time is 4 h-12 h.
The concentration of the aqueous slurry containing cesium tungsten bronze/TiO2 composite particles can be adjusted through evaporation using a rotary evaporator, or by adjusting the amount of water used in the preparation of the aqueous slurry containing cesium tungsten bronze/TiO2 composite particles, or through other methods.
In order to make the technical objectives, technical solutions and technical effects of the present disclosure clearer so that those skilled in the art can understand and implement the present disclosure, the present disclosure will be further described in detail below with reference to the accompanying drawings and specific embodiments.
10 parts by weight of WCl6, 2 parts by weight of CsOH.5H2O, 35 parts by weight of acetic acid and 15 parts by weight of PVP were stirred together to obtain a first mixture. The first mixture was heated to 80° C. and maintained at this temperature for 2 h. Then, the first mixture was further heated to 220° C., reacted for 20 h at this temperature, then centrifuged and oven dried, to obtain cesium tungsten bronze nanoparticles. The cesium tungsten bronze nanoparticles were analyzed by XRD, as shown in
10 parts by weight of TiCl4 and 30 parts by weight of anhydrous ethanol were mixed, to obtain a second mixture. Then, the second mixture was reacted at 180° C. for 8 h, and then centrifuged and oven dried, to obtain TiO2 nanoparticles. The TiO2 particles were analyzed by XRD, as shown in
40 parts by weight of the cesium tungsten bronze nanoparticles, 5 parts by weight of the TiO2 nanoparticles, 1 parts by weight of sodium polyacrylate coupling agent (SN5040) and 40 parts by weight of deionized water were ball milled, to obtain an aqueous slurry containing cesium tungsten bronze/TiO2 composite particles, which is used as a self-cleaning nano heat-insulation coating material.
The self-cleaning nano heat-insulation coating material is uniform and stable.
A self-cleaning nano heat-insulation coating was formed with the self-cleaning nano heat-insulation coating material using a spin coater. Then, light transmittance curve of the self-cleaning nano heat-insulation coating was measured, as shown in
A drop of water was dripped on the self-cleaning nano heat-insulation coating, and a photo of the contact angle was taken. As shown in
13 parts by weight of WCl6, 2 parts by weight of CsOH.5H2O, 40 parts by weight of acetic acid and 20 parts by weight of PVP were stirred together to obtain a first mixture. The first mixture was heated to 70° C. and maintained at this temperature for 1.5 h. Then, the first mixture was further heated to 220° C., reacted for 20 h at this temperature, then centrifuged and oven dried, to obtain cesium tungsten bronze nanoparticles.
15 parts by weight of TiCl4 and 40 parts by weight of anhydrous ethanol were mixed, to obtain a second mixture. Then, the second mixture was reacted at 180° C. for 8 h, and then centrifuged and oven dried, to obtain TiO2 nanoparticles.
50 parts by weight of cesium tungsten bronze nanoparticles, 10 parts by weight of TiO2 nanoparticles, 2 parts by weight of sodium polyacrylate coupling agent (SN5040) and 40 parts by weight of deionized water were ball milled, to obtain an aqueous slurry containing cesium tungsten bronze/TiO2 composite particles, which can be used as a self-cleaning nano heat-insulation coating material. The self-cleaning nano heat-insulation coating material is uniform and stable.
15 parts by weight of WCl6, 4 parts by weight of CsOH.5H2O, 30 parts by weight of acetic acid and 15 parts by weight of PVP were stirred together to obtain a first mixture. The first mixture was heated to 70° C. and maintained at this temperature for 1 h. Then, the first mixture was further heated to 240° C., reacted for 30 h at this temperature, then centrifuged and oven dried, to obtain cesium tungsten bronze nanoparticles.
12 parts by weight of TiCl4 and 30 parts by weight of anhydrous ethanol were mixed, to obtain a second mixture. Then, the second mixture was reacted at 180° C. for 8 h, and then centrifuged and oven dried, to obtain TiO2 nanoparticles.
45 parts by weight of cesium tungsten bronze nanoparticles, 8 parts by weight of TiO2 nanoparticles, 2 parts by weight of sodium polyacrylate coupling agent (SN5040) and 50 parts by weight of deionized water were ball milled, to obtain an aqueous slurry containing cesium tungsten bronze/TiO2 composite particles, which can be used as a self-cleaning nano heat-insulation coating material. The self-cleaning nano heat-insulation coating material is uniform and stable.
In the present disclosure, cesium tungsten bronze nanoparticles are prepared through hydrothermal method. The cesium tungsten bronze nanoparticles have a large specific surface area, thus is beneficial to improving infrared absorptivity. TiO2 nanoparticles have a good dispersibility in water, and virtually does not block visible light.
Further, in the present disclosure, an aqueous slurry containing cesium tungsten bronze/TiO2 composite particles is prepared by ball milling and dispersing, in which the well-dispersed cesium tungsten bronze nanoparticles and TiO2 nanoparticles are beneficial to improving visible light transmittance and infrared blocking performance of the coating.
A coating obtained by applying the self-cleaning nano heat-insulation coating material of the present disclosure has a good hydrophilicity which prevents contamination of the nano-coating by organic oils and inorganic dusts, thereby greatly enhancing the anti-fouling performance and extending the service life of the coating.
The self-cleaning nano heat-insulation coating material of the present disclosure is a water-based heat-insulation coating material, which has low content of volatile organic compounds (VOCs) and causes no hazards to the environment and the health of construction workers and users.
It should be understood that improvements or replacements can be made by those skilled in the art based on the above description, and all such improvements and replacements shall fall within the protection scope of the appended claims of the present disclosure
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017 1 0395687 | May 2017 | CN | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6328947 | Monden | Dec 2001 | B1 |
| 20100219654 | Fujita | Sep 2010 | A1 |
| 20170183240 | Lin | Jun 2017 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20180340082 A1 | Nov 2018 | US |