Patent Application
20050118409
The present invention relates to inorganic oxide particles useful as packing materials for chromatography. More particularly, the invention is directed to inorganic oxide particles that have been modified with a chelator.
Many inorganic oxide particles are known in the art that are useful in sorbent applications, particularly as packing materials for High Performance Liquid Chromatography (HPLC).
The majority of separations employing high performance liquid chromatography are performed in the reversed-phase mode, wherein the column packing material surface is modified with a hydrophobic layer. In reversed-phase mode the column packing, or stationary phase, has is generally hydrophobic, while the mobile phase contains some fraction percent of water and therefore has more polarity. The most common presently used stationary phases employ a non-polar ligand (e.g., octane or octadecane) covalently bound to a porous silica (SiO2) particle through a siloxane bond to render the silica surface hydrophobic. Although these silica-based supports are very useful for a wide range of applications in reversed-phase HPLC, their use is typically limited to a pH range of between 2 and 8, due to the hydrolytic instability of both the silica support particle and the siloxane bond used to “anchor” the non-polar active group.
The strictly limited pH range for silica particles led, in part, to the use of other materials such as zirconia (ZrO2) as a substrate material for HPLC column packings. Particles made of zirconia have proven useful but have had other limitations. Some solutes, such as those that can act as a Lewis base, interact strongly with zirconia based particles and are not eluted with good peak shape or good efficiency. In extreme cases this interaction can result in irreversible adsorption of a solute on the chromatographic media. One approach to solving this problem has been the use of additives to the mobile phase capable of acting as a Lewis base, such as ammonium phosphate, sodium fluoride, sodium acetate or the like. However, this approach does not work with all applications (such as LC/MS which often requires volatile buffers) and still does not result in optimal chromatographic performance.
Therefore, a need exists for methods of modifying inorganic oxide particles so that Lewis base containing solutes can be eluted without the use of mobile phase additives and with enhanced chromatographic performance.
The present invention is directed to inorganic oxide particles that have been modified with a chelator group. In an embodiment, the chelator group is covalently bonded to a polymer. In an embodiment, the chelator group is covalently bonded to a chiral selector ligand. The present invention is also directed to methods of modifying inorganic oxide particles with a chelator group. The present invention is also directed to methods of eluting Lewis base containing solutes using a column with inorganic oxide particles that have been modified with a chelator group.
The invention may be more completely understood in connection with the following drawings, in which:
While the invention is susceptible to various modifications and alternative forms, specifics thereof have been shown by way of example and drawings, and will be described in detail. It should be understood, however, that the invention is not limited to the particular embodiments described. On the contrary, the intention is to cover modifications, equivalents, and alternatives falling within the spirit and scope of the invention.
It has been surprisingly discovered that, in an embodiment, a chelator can be used to prevent or reduce the effects of Lewis acid sites on zirconia oxide particles with respect to solutes containing Lewis bases and to improve overall chromatographic performance. In an embodiment, the present invention is directed to attaching an appropriate chelator group to an inorganic oxide substrate through a Lewis acid-base reaction and then covalently bonding the desired polymer to the chelator group. In an embodiment, where zirconia is used as the inorganic oxide, covalently chelator-modified polybutadiene (CCM-PBD) coated zirconia can be produced.
In an embodiment, the present invention is directed to attaching an appropriate chelator group to an inorganic oxide substrate through a Lewis acid-base reaction and then covalently bonding a chiral selector ligand to the chelator group through an organic reaction. In an embodiment, the invention includes inorganic oxide particles that are bound to a polyphosphate chelator group that is covalently bound to a chiral selector ligand.
While full examples of the modification process are provided below in examples 1, 7, and 11, an overview of the process in accordance with an embodiment of the invention will now be provided.
Modification Process Overview
In an embodiment for producing inorganic oxide particles that are bound to chelators, which in turn are covalently bound to polymers, starting with a bare inorganic oxide particle, a solution of a chelator is added such that it reacts with the surface of the inorganic oxide particle. After this step the particles are washed and then dried. Then a solution is added that will later allow the chelator to covalently bind to the polymer. One example of such a solution is allyl iodide solution to which 1,2,2,6,6-pentamethylpiperidine (as a sterically hindered base) is then added. This solution is allowed to react with the particles and then the particles are washed and dried again. Next, a solution of a polymer is added to the particles. After that, a cross-linking initiator is added and after drying and heating the chelator becomes covalently bound to a coating of polymer on the particles.
In an embodiment for producing inorganic oxide particles that are bound to polyphosphate chelators, which in turn are covalently bound to chiral selector ligands, starting with a bare inorganic oxide particle, a solution of a polyphosphate chelator is added such that it reacts with the inorganic oxide particle. After this step, the particles are washed and then dried. Next, a solution is added that will later allow the chelator to covalently bind to the stationary phase ligand. One example of such a solution is allyl iodide solution to which 1,2,2,6,6-pentamethylpiperidine is then added. This solution is allowed to react with the particles and then the particles are washed and dried again. Next, a solution of a suitable stationary phase, such as a chiral selector or hydrophobic polymer is added to the particles to tether the chelator and the stationary phase together. The stationary phase can be any number of molecules, peptide, polymers, protein, etc. that imparts a desired functionality to the surface of the particle for different modes of chromatographic use such as reverse-phase, ion-exchange, affinity, chiral, etc.
Modes of Use
Embodiments of the present invention are useful under a wide variety of conditions and protocols. By way of example, the present invention is useful in reversed-phase HPLC. The present invention is also useful in other modes of chromatography, including ion-exchange chromatography, reverse phase liquid chromatography, normal phase liquid chromatography, and hydrophilic interaction chromatography, etc. wherein the chromatography is conducted with inorganic oxides. In an embodiment, the present invention can be used with any sort of chromatography or chemical separation where Lewis base analytes may problematically interact with Lewis acid sites on the substrate.
Substrates
In an embodiment, the substrate of the present invention is porous or nonporous zirconia particles, porous or nonporous Titania particles, and porous or nonporous silica particles. In another embodiment, the substrate of the present invention may be any of zirconia, titania, hafnia, alumina, niobia, yttria, or magnesia, or mixed oxides thereof. In an embodiment, the substrate of the present invention is zirconia. In some embodiments, the particles are within the size range of 1-100 microns. In other embodiments, the particles may be within the size range of 0.5-200 microns. In still other embodiments, the particles may be from 0.1 micron to about 10 microns. In embodiments where the particles are porous, the pores may be from 50-2000 angstroms. In other embodiments where the particles are porous, the pores may be from 50-1500 angstroms. The particles may also be monolithic. The particles may be in the shape of microspheres or spherules, as well as non-spherical.
In some embodiments, the substrate of the present invention may be carbon coated or carbon-clad inorganic oxide particles. For example, the particles of the present invention can be clad or coated with a layer of pyrolytic carbon using a chemical vapor deposition (“CVD”) process. The terms “pyrolytic carbon” and “CVD carbon” are generic terms relating to the carbon material that is deposited on the substrate by the thermal pyrolysis of a carbon-bearing vapor. The term “CVD carbon” describes the processing used, whereas the term “pyrolytic carbon” refers more to the type of carbon material that is deposited. While many methods of applying pyrolytic carbon to a substrate can be used in the preparation of carbon-clad particles, the carbon cladding is generally applied in a manner that results in substantial carbon coverage of the surface of the microspheres. Funkenbusch et al. (U.S. Pat. No. 5,346,619) describes one method for producing carbon clad inorganic oxide particles, the disclosure of which is herein incorporated by reference.
Any carbon source that can be vaporized and which will carbonize on the surface of the particles can be employed to deposit a carbon cladding via CVD. Useful carbon sources include hydrocarbons such as aromatic hydrocarbons, e.g., benzene, toluene, xylene, and the like; aliphatic hydrocarbons, e.g., heptane, cyclohexane, substituted cyclohexane butane, propane, methane, and the like; unsaturated hydrocarbons; branched hydrocarbons (both saturated and unsaturated), e.g., isooctane; ethers; ketones; aldehydes; alcohols such as heptanol, butanol, propanol, and the like; chlorinated hydrocarbons, e.g., methylene chloride, chloroform, trichloroethylene, and the like; and mixtures thereof. The carbon source may be either a liquid or a vapor at room temperature and atmospheric pressure although it is employed in a CVD process in vapor form. If the carbon source is a liquid with low volatility at room temperature, it may be heated to produce sufficient vapor for the deposition. In general, the choice of the deposition temperature, pressure, and time conditions are dependent on the carbon source employed and the nature of the metal oxide. The thickness of the carbon cladding over the surface of the metal oxide particle ranges from the diameter of a single carbon atom (a monatomic layer), to about 20 Angstroms.
Chelator
In an embodiment, the chelator of the present invention is a compound having two functions: (1) at least one Lewis base metal site chelator group such as OH, COOH, COOR, PO3H, PO2H, POH, SiH, or SiCl, and (2) another reactive group such as OH, NH, NH2, COOH, and/or a double bond. Examples of suitable chelators include EDTPA (N,N,N′,N′-ethylenediaminetetra(methylenephosphonic acid)) and PEI (poly(ethyleneimine)). In some embodiments, mixtures of different chelators can be used.
In an embodiment, the chelator of the present invention is a polyphosphate chelator. Polyphosphate chelators include EDTPA (N,N,N′,N′-ethylenediaminetetra(methylenephosphonic acid)), phytic acid, methylene phosphonic acid, methylene diphosphonic acid, phospholipids, 2-[hydroxy(methyl)phosphoryl]ethyl(methyl)phosphinic acid, pyrrolidine-2,2-diylbis(phosphonic acid), 1-Hyfroxyethylidenedi(phosphonic acid), 1,3-diyl[bis]4,1-phenylene(difluoromethylene)bis(phosphonic acid), ENTMP (N,N,N-,N-ethylene diaminotetra methylene phosphonic acid), TENTMP (N,N,N-,N-triethylene diamine tetra (methylene phosphonic acid)), NTMP (Nitrilotris(Methylene Phosphonic acid)), and HDTMP (Hexamethylenediaminetetra(methylene phosphonic acid).
Chelators of the invention may also include naproxen, N-(phosphonomethyl)glycine, 2-aminoadipic acid, and (18-crown-6)-2,3,11,12-tetracarboxylic acid.
Polymers and Polymerization
The polymer of the present invention is a compound having at least a functional group such as, NH, NH2, COOH, and/or a double bond. In some embodiments, the polymer of the invention may be a hydrophobic polymer. For example, polybutadiene (PBD) may be used. In another embodiment, polystyrene may be used. Other hydrophobic polymers that may be used include: polyhexamethylenevinylene, poly(4-vinylbiphenyl), poly(2-vinylnaphthalene), poly(4-methylstyrene), and polylimonene. In some embodiments, the polymer of the invention may be a hydrophilic polymer. Suitable hydrophilic polymers include polyvinylalcohol, poly(ethyleneglycol), polyvinylpyrollidone, polyethyleneimine, poly(butadiene maleic acid), polysiloxane, poly-l-histidine, or a polysaccharide (including cellulose and dextran).
Other polymers that may be used include, poly (ethyl methacrylate) and other methacrylates, polyaniline, polyethylene, polypropylene, poly(styrene-co-divynlbenzene), poly (vinyl acetate), and the like. In some embodiments, such as where ion-exchange chromatography is contemplated, suitable polymers may include aminocellulosics such as chitosan (polyglucoseamine), copoylmers of acrylamide and cationic derivatives (esters) of acrylic/methacrylic acid such as acrylamide/dimethylaminoethylmethacrylate copolymer, copolymers of diethylenetriamine, triethylenetetramine, ethylenediamine, which have been chain extended with epichlorohydrin, polyamidoamines (e.g. adipic acid/diethylenetriamine condensation polymers, other monomers such as caprolactam, dimethyladipate, triethylenetetramine), poly(diallyldimethulammonium chloride), cationic starch (yellow corn, tapioca, potato, waxymaize corn starch derivatized with diethylamine ethyl chloride hydrochloride or epoxy propyl trimethylammonium chloride or other quaternary derivatizing reagent), epoxydized polyamide resin (contain azetidiunium functionality, e.g. adipic acid/diethylenetriamine/epichlorohydrin), acrylamide/diallyldimethylammonium chloride copolymers (e.g. cationic polyacrylamide), glycoxalated version of cationic polyacrylamide, cationic (grafted) cellulose derivatives, all polymers of diethyletriamine and ethylenediamine (such as for example PEI, KYMEME and RETEN) (KYMEME and RETEN are made by Hercules (Delaware, USA), comonomers of amines (for example glysine and lysine), any copolymer of polyamino acids that have lysine, hystidine or arganine and any other amino acid, and polyallylamines. Cross-linkers for polyamine compounds that can be used include: any dihaloalkane: for example 1,3 dibromopropane, 1,3 dichloropropane, 1,3 diiodopropane, and all the way up to 12 carbons, 1,4-dibromobenzene (and other halogenated versions), 1,4-dibromo-1,4 butanediol (hydrophillic), 1,4-dibromo-2,3-butanedione (hydrophillic), 2,6-bis(chloromethyl)pyridine (may be particularly useful on poly-L-lysine for a chiral stationary phase), 1,8-bis(bromomethyl)naphthalene (hydrophobic) (may be useful on poly-L-lysine for a chiral stationary phase), 2,2′-bis(bromomethyl-1,1′-biphenyl) (hydrophobic) (may be useful on poly-L-lysine for a chiral stationary phase), glutaraldehyde, 4,4′-diisothiocyantobiphenyl-2,2′-disulfonic acid and other diisothicyanates and diisothionates, bis-diazobenzene-2,2′-disulfonic acid, thiophosgene, succinic anhydride (other dianhydrides), any diacid chloride, and 1-cyclohexyl-3-(2-morpholinoethyl)-carbodiimide metho-p-toluene.
In those embodiments where cation-exchange is contemplated, any polymer with a carboxylic acid, phosphonic acid, or sulfonic acid group that has a benzene ring or is an alkene could be used.
In some embodiments, the polymer may be a homopolymer, while in other embodiments the polymer may be a heteropolymer. In other embodiments, the polymer coating may be mixtures of different hetero or homo polymers. One of skill in the art will appreciate that many different polymers may be used.
The initiator of the present invention is a compound used to produce free radicals to initiate the polymerization by crosslinking. Examples of suitable initiators include DCP (dicumyl peroxide) and AIBN (2,2′-Azobisisobutyronitrile). Other common initiators such as benzoyl peroxide may also be used. One of skill in the art will appreciate that many different initiators, including many different organic peroxides and diazo compounds, may be used.
Chiral Selector Ligands
Chiral selector ligands of the present include those that can be covalently bound to the chelator group. In an embodiment, the chiral selector ligand includes compounds having at least a functional group such as, NH, NH2, COOH, a double bond, and the like and at least one chiral center. By way of example, chiral selector ligands of the invention may include DNP-PG (3,5-dinitrobenzoyl-phenylglycine), DNB-LEU (3,5-dinitrobenzoyl-leucine), DNB-PRO (3,5-dinitrobenzoyl-proline), NAP-VAL (naphthoyl-valine), 1 or 2-NAP-LEU (naphthoyl-leucine),and NAP (naproxen). The chiral selector ligand may also include those referred to as “Whelk-O 1” ((3R,4R)-4-(3,5-dinitrobenzamido)-1,2,3,4-tetrahydro-phenanthrene or ((3S,4S)-4-(3,5-dinitrobenzamido)-1,2,3,4-tetrahydro-phenanthrene) (structure I) and “α-Burke 2” (derived from dimethyl N-3,5-dinitro-benzoyl-a-amino-2,2-dimethyl-4-pentenyl phosphonate) (structure II), and derivatives of these.
The present invention may be better understood with reference to the following examples. These examples are intended to be representative of specific embodiments of the invention, and are not intended as limiting the scope of the invention.
Step 1. A fresh solution was prepared by adding 3.0 g of EDTPA to 500 ml of HPLC grade water into 1000 ml flask. It was refluxed for 2 hours to dissolve the EDTPA and then cooled down to room temperature. The solution was filtered to remove the undissolved material and residuals. 150 g of bare zirconia (5 μm or 3 μm can be used) was placed in a 1000 ml, 2-necked round bottom flask, and the 500 ml of the EDTPA solution was added. The particles were thoroughly suspended by swirling the flask, then the mixture was sonicated under vacuum for 30 minutes. The flask was attached to a water-cooled condenser and set up to a heating mantle set to level 4.5. Nitrogen was bubbled through the mixture at 25 mL/min by running a nitrogen-line through a stopper and into the flask through one of the necks. The solution was stirred with a stir bar (Medium size). The mixture was monitored closely until it came to a gentle boil. The mixture was heated at reflux for 4 hours. The mixture was transferred to a membrane filter and filtered. The particles were washed with 3×300 ml of HPLC grade water followed by 3×300 ml of 100% HPLC grade ethanol. The particles were dried at room temperature under vacuum and then at 120° C. for 3 hours.
The dried particles were added into a 1000 ml round bottom flask. A solution of allyl iodide (238325-25G, lot 09128Ka) in isopropyl alcohol (IPA) was made by dissolving 15 g of allyl iodide in 450 ml of IPA in a 250-ml beaker. 1.500 ml of 1,2,2,6,6-pentamethylpiperidine (Aldrich, 27463-1, lot #08531JR PU) was added to the allyl iodide solution with swirling and heated with hot water. This solution was added into the particle flask. The suspension was sonicated under vacuum for 10 minutes. The flask was placed on a rota-vap (rotary evaporator) with the temperature set to 65° C. and rotated for rotated for 20 hours at 20 rpm (cover bath with foil to help with evaporation of H2O). After rotating overnight, the flask was removed from the rota-vap and the particles were collected by vacuum filtration and washed with 3×300 ml ethanol followed by 3×300 ml HPLC grade H2O, and 3×300 ml HPLC grade Ethanol. Air was pulled through the cake of the washes until the particles were dry. The particles were dried in a vacuum oven (23 torr) at 110° C. for 4 hrs to remove excess moisture.
Step 2. 10.0 g PBD (polybutadiene) (batch #09913 BA) was added to a 500 ml round bottom flask. 75 ml of HPLC grade Hexane was added and it was swirled until the PBD was fully dissolved. 50 g of the zirconia particles from Step 1 were added to the 500 ml round bottom flask and the slurry was sonicated for a few minutes under vacuum, breaking the vaccum periodically. 8.04 g of 20 mg/ml AIBN (azobisisobutyronitrile, Aldrich, catalog no. 441090-100G, batch no. 12603CB) hexane solution was added (DCP (dicumyl peroxide, Aldrich) hexane solution can also be used). The slurry was sonicated under vacuum for 5 minutes, breaking vacuum every minute to allow infiltration of particle pores. The flask was rotated on a rotary station for 2 hours. The solvent was evaporated at 50° C. with a vacuum of 14 in. Hg over a period of 15 minutes using a rotary evaporator. The material was allowed to continue to dry for 15 minutes 50° C. with a vacuum of 25 in. Hg.
The particles were transferred to a clean quartz tube. The quartz tube was placed in a rotating furnace. The tube was connected to an ultra pure nitrogen source and flushed for 30 min. The particles were dried at 80° C. (use 120° C. if DCP is used as the initiator) for 5 hours, the temperature was raised to 100° C. (use 160° C. if DCP is used as the initiator) and cross-linking took place for 1 hour while running ultra pure nitrogen through the tube.
After cross-linking, the particles were transferred from the tube to the Soxhlet extractor. 500 ml of toluene was used for 8 hours. Particles were collected on a membrane filter and rinsed with 2×200 ml of ethanol. Air was pulled through the cake for 3 hours until the particles were dry. The particles were resuspended in 300 ml 50/50 0.05 M HNO3/THF. The solution was sonicated under vacuum for 5 minutes, breaking vacuum once every minute. The wash was repeated once, and 300 ml 50/50 THF/water was used to wash the particles. The particles were then rinsed while on filter with 2×200 ml HPLC ethanol, and the particles were dried by pulling air through the cake for 3 hours.
The covalently chelator-modified PBD (CCM-PBD) coated zirconia was compared with unmodified PBD zirconia using some Lewis base probe solutes. Alkoxybenzoic acids, which interact strongly with unmodified PBD coated zirconia if an appropriate Lewis base mobile phase additive (such as phosphate) is not employed, were used as the Lewis base solutes.
Under the same chromatographic conditions, an unmodified PBD coated zirconia phase showed no elution of these compounds (not shown).
The peak shapes using the covalently chelator-modified PBD coated zirconia, as shown in
The effect of surface activation of PBD coated zirconia was demonstrated by separating a mixture of small organic compounds including (1) acetone, (2) phenol, (3) 4-chlorophenol, (4) anisole, and (5) toluene. The conditions where as follows: 35/65 ACN/water, Flow rate: 1 mL/min, 254 nm UV, 5 μl injection.
Retention comparison was conducted between (7A) CCM-PBD coated zirconia and (7B) unmodified PBD coated zirconia. The solutes tested were from left to right as follows: (1) acetone (2) phenol, (3) 4-hydroxyphenol, (4) anisol, and (5) toluene. The conditions were as follows: mobile phase—35/65 ACN/water, flow rate: 1 mL/min, 254 m UV, 5 ul injection.
Gradient reproducibility of the CCM-PBD coated zirconia was tested. Solutes eluted in order from left to right on
The same coating process described above can be applied to a carbon-clad zirconia substrate particle, which is described below:
Step 1. A fresh solution was prepared by adding 3.0 g of EDTPA to 500 ml of HPLC grade water into 1000 ml flask. It was refluxed for 2 hours to dissolve the EDTPA and then cooled down to room temperature. The solution was filtered to remove the undissolved material and residuals. 100 ml of ethanol and 50 g of carbon-clad zirconia (5 μm or 3 μm can be used) was added to a 1000 ml, 2-necked round bottom flask. The particles were suspended and sonicated for 10 minutes under vacuum. 400 ml of the EDTPA solution was added. The particles were suspended by swirling the flask and then sonicated under vacuum for 5 minutes. The flask was attached to a water-cooled condenser and set up to a heating mantle set to level 4.5. Nitrogen was bubbled through the mixture at 25 mL/min by running a nitrogen-line through a stopper and into the flask through one of the necks. The solution was stirred with a stir bar (Medium size). The mixture was monitored closely until it came to a gentle boil. The mixture was heated at reflux for 4 hours. The mixture was transferred to a membrane filter and filtered. The particles were washed with 3×200 ml of HPLC grade water followed by 3×200 ml of 100% HPLC grade ethanol. The particles were dried at room temperature under vacuum and then at 120° C. for 3 hours.
The dried particles were added into a 1000 ml round bottom flask. A solution of allyl iodide (238325-25G, lot 09128Ka) in IPA was made by dissolving 2.5 g of allyl iodide in 150 ml of IPA in a 250-ml beaker. 0.21 g of 1,2,2,6,6-pentamethylpiperidine (Aldrich, 27463-1, lot #08531JR PU) was added to the allyl iodide solution with swirling and heated with hot water. This solution was added into the particle flask. The suspension was sonicated under vacuum for 10 minutes. The flask was placed on a rota-vap (rotary evaporator) with the temperature set to 65° C. and rotated for 20 hours at 20 rpm (cover bath with foil to help with evaporation of H2O). After rotating overnight, the flask was removed from the rota-vap and the particles were collected by vacuum filtration and washed with 3×200 ml ethanol followed by 3×200 ml HPLC grade H2O, and 3×200 ml HPLC grade Ethanol. Air was pulled through the cake of the washes until the particles were dry. The particles were dried in a vacuum oven (23 torr) at 110° C. for 4 hrs to remove excess moisture.
Step 2. 1.2 g PBD (polybutadiene) (batch #09913 BA) was added to a 500 ml round bottom flask. 75 ml of HPLC grade Hexane was added and it was swirled until the PBD was fully dissolved. 10 g of the zirconia particles from Step 1 were added to the 500 ml round bottom flask and the slurry was sonicated for a few minutes under vacuum, breaking the vaccum periodically. 1.0 g of 20 mg/ml AIBN (azobisisobutyronitrile, Aldrich, catalog no. 441090-100G, batch no. 12603CB) hexane solution was added (DCP (dicumyl peroxide, Aldrich) hexane solution can also be used). The slurry was sonicated under vacuum for 5 minutes, breaking vacuum every minute to allow infiltration of particle pores. The flask was rotated on a rotary station for 2 hours. The solvent was evaporated at 50° C. with a vacuum of 14 in. Hg over a period of 15 minutes using a rotary evaporator. The material was allowed to continue to dry for 15 minutes 50° C. with a vacuum of 25 in. Hg.
The particles were transferred to a clean quartz tube. The quartz tube was placed in a rotating furnace. The tube was connected to an ultra pure nitrogen source and flushed for 30 min. The particles were dried at 80° C. (use 120° C. if DCP is used as the initiator) for 5 hours, the temperature was raised to 100° C. (use 160° C. if DCP is used as the initiator) and cross-linking took place for 1 hour while running ultra pure nitrogen through the tube.
After cross-linking, the particles were transferred from the tube to the Soxhlet extractor. 500 ml of toluene was used for 8 hours. Particles were collected on a membrane filter and rinsed with 2×100 ml of ethanol. Air was pulled through the cake for 3 hours until the particles were dry. The particles were resuspended in 200 ml 50/50 0.05 M HNO3/THF. The solution was sonicated under vacuum for 5 minutes, breaking vacuum once every minute. The wash was repeated once, and 200 ml 50/50 THF/water was used to wash the particles. The particles were then rinsed while on filter with 2×100 ml HPLC ethanol, and the particles were dried by pulling air through the cake for 3 hours.
The separation is easily achieved on the SUPERCARB (CCM-PBD coated carbon clad zirconia) column, however both solutes co-elute on the PBD coated zirconia phase. It is known in the art that carbon-based HPLC supports have good chromatographic selectivity for structurally closely related compounds such as diastereomers, cis/trans compounds and the like. Thus the SUPERCARB material retains some of its selectivity for these closely related compounds, while having much greater column efficiencies than pure carbon-based HPLC columns. Since the 3 micron particle (PBD coated zirconia) is more chromatographically efficient, it is clear that the separation is not due to better efficiency, but better selectivity for these two structurally closely related compounds.
Step 1. A fresh EDTPA solution was prepared by adding 3.0 g of EDTPA to 500 ml of HPLC grade water into 1000 ml flask. It was refluxed for 2 hours to dissolve the EDTPA and then cooled down to room temperature. The solution was filtered to remove the undissolved material and residuals. 150 g of bare zirconia (5 μm or 3 μm can be used) was placed in a 1000 ml, 2-necked round bottom flask, and the 500 ml of the EDTPA solution was added. The particles were thoroughly suspended by swirling the flask, then the mixture was sonicated under vacuum for 30 minutes. The flask was attached to a water-cooled condenser and set up to a heating mantle set to level 4.5. Nitrogen was bubbled through the mixture at 25 mL/min by running a nitrogen-line through a stopper and into the flask through one of the necks. The solution was stirred with a stir bar (medium size). The mixture was monitored closely until it came to a gentle boil. The mixture was heated at reflux for 4 hours. The mixture was transferred to a membrane filter and filtered. The particles were washed with 3×300 ml of HPLC grade water followed by 3×300 ml of 100% HPLC grade ethanol. The particles were dried at room temperature under vacuum and then at 120° C. for 3 hours.
The dried particles were added into a 1000 ml round bottom flask. A solution of allyl iodide (238325-25G, lot 09128Ka) in isopropyl alcohol (IPA) was made by dissolving 15 g of allyl iodide in 450 ml of IPA in a 250-ml beaker. 1.500 ml of 1,2,2,6,6-pentamethylpiperidine (Aldrich, 27463-1, lot #08531JR PU) was added to the allyl iodide solution with swirling and heated with hot water. This solution was added into the particle flask. The suspension was sonicated under vacuum for 10 minutes. The flask was placed on a rota-vap (rotary evaporator) with the temperature set to 65° C. and rotated for rotated for 20 hours at 20 rpm (cover bath with foil to help with evaporation of H2O). After rotating overnight, the flask was removed from the rota-vap and the particles were collected by vacuum filtration and washed with 3×300 ml ethanol followed by 3×300 ml HPLC grade H2O, and 3×300 ml HPLC grade Ethanol. Air was pulled through the cake of the washes until the particles were dry. The particles were dried in a vacuum oven (23 torr) at 110° C. for 4 hrs to remove excess moisture.
Step 2. A fresh solution of DNB-L-Leu (R-N-(3,5-dinitrobenzoyl)-L-leucine was prepared by adding 471 mg of DNB-L-Leu to 10 ml of HPLC grade THF in a 100 ml round bottom flask. The particles were added to the 100 ml round bottom flask and suspended by swirling the flask and sonicating the mixture for 2 minutes. 0.35 g of EEDQ were added with swirling. The mixture was swirled for another 8 hours at room temperature. The particles were filtered using a 0.45 μm membrane filter and washed with 3×5 ml aliquots of acetone and 3×5 ml aliquots of IPA. The particles were allowed to air-dry at room temperature.
The invention has been described with reference to various specific and preferred embodiments and techniques. However, it should be understood that many variations and modifications may be made while remaining within the spirit and scope of the invention.