Patent Grant
10843438
The present invention relates to a chemical barrier fabric comprising a plurality of layers. Such a chemical barrier fabric may be used, for example, in the manufacture of protective apparel which protect the wearer against a wide range of chemicals or for use as military or civil defence chemical protective cover applications. Such applications include, for example, covers for the chemical protection of equipment or for the manufacture of tent components or temporary shelters or for military or civil defence medical products such as evacuation or casualty bags. By civil defence is meant any of the emergency services, police, fire brigade, hospitals and other defensive measures which might be taken by local authorities or private organisations for the protection of their members.
The use of Personal Protective Equipment (PPE) is mandated in industry to protect operators against various hazards such as excessive heat, mechanical abrasion or laceration, ionising radiation or exposure to toxic or corrosive chemicals which may be present in the work environment. PPE comprises, for example, protective apparel such as hooded suits, gauntlets, gloves and the like, which provide protection against a range of potentially hazardous chemicals. The materials from which such protective apparel are made may consist of a single layer of film (or multiple layers of films) either used alone or in combination with other layers such as woven or non-woven fabrics. The film layers used in the manufacture of protective apparel materials provide protection to the wearer against toxic or hazardous chemicals by ensuring a low rate of molecular permeation across the two opposing faces of the materials forming the outer surface and inner surface of the protective apparel.
The permeation of a particular chemical or mixture of chemicals across the opposing faces of such barrier materials can be measured using standard test methods to determine the effectiveness of the barrier properties of the material under test. One such standard test method is EN ISO 6529:2001 “Protective clothing—Protection against chemicals—Determination of resistance of protective clothing materials to permeation by liquids and gases” which supersedes and incorporates the principles of EN 369:1993 “Protective clothing—Protection against liquid chemicals—Test method: Resistance of materials to permeation by liquids”. The former test method can be used for any chemical identified as a potential hazard which may be anticipated in a particular environment or, alternatively, it may be used for a standard range of chemicals such as that identified in Annex A (parts A2 and A3) of EN ISO 6529:2001 “Protective clothing—Protection against chemicals—Determination of resistance of protective clothing materials to permeation by liquids and gases”, or ASTM F1001-99a “Standard guide for selection of chemicals to evaluate protective clothing materials.”
Materials currently available for use as chemical barrier sheets or films for protective apparel manufacture include polyethylene, polyvinyl chloride, natural or synthetic rubbers and polyurethane. The limitations of such materials as chemical barriers for protective apparel have long been recognised. They are either prone to chemical degradation (e.g. polyurethane), or have poor resistance to chemical permeation through the film layer (e.g. polyethylene). Accordingly more complex materials have been developed comprising multiple layers of films bonded together by co-extrusion or by the use of an adhesive “tie” layer between the different film layers.
A known non-woven fibrous material is described in U.S. Pat. No. 3,169,899 (Du Pont). This material has found wide commercial application under the name Tyvek®. This patent lists a wide range of applications for Tyvek® including its use as a barrier material for protective clothing. In particular, it is described how Tyvek® may be coated, laminated or impregnated to provide additional barrier properties for use as a protective clothing material. Examples of such coating, lamination and impregnation are given in which the resultant sheet product consists of a Tyvek® substrate with further sheet materials attached to the whole surface of the Tyvek® substrate by any of the methods listed in the patent.
A multi-layer chemical barrier composite is disclosed in U.S. Pat. No. 4,833,010 (Kappler Safety Group). The composite is formed from a first multi-layer film sheet comprising ethylene vinyl alcohol (EVOH) film sandwiched between films of nylon. One of the nylon films is coated with a film of linear low-density polyethylene, and the second nylon film is adhesively bonded with ethylene vinyl acetate film acting as a tie layer to a non-woven polypropylene base fabric. A second multi-layer film sheet comprising a central polyvinylidine chloride film disposed between a linear low density polyethylene film outer surface and an ethylene vinyl acetate adhesive film inner surface acting as a tie layer is optionally bonded to the other surface of the non-woven polypropylene fabric. Thus, the resultant composite has either two multi-layer film components separated by a central non-woven polypropylene fabric, or a single multi-layer film bonded to the non-woven fabric Where two multi-layer film components are used, separated by a central nonwoven fabric layer, a synergistic effect on the chemical barrier properties is claimed due to the separation of the multi-layer film components by the layer of non-woven fabric. The chemical barrier material may be coloured by the addition of pigment in at least one of the adhesive layers.
Another multi-layer chemical barrier material is described in U.S. Pat. No. 4,992,335 (Sanders Associates, Inc.) This multi-layer chemical barrier material comprises a layer of polyvinylidine chloride or copolymer of vinylidine chloride bonded to at least one layer of polyolefin film by means of chemical treatment of one or more film layers, and laminating the oxidised and/or de-halogenated film layers together under heat and pressure. Additional layers may include fabric for comfort, textile scrims for strength, electrically conductive layers to dissipate static charge, or chemical indicators to warn of penetration by specified chemicals or chemical classes.
A further multi-layer chemical fabric is disclosed in U.S. Pat. No. 5,162,148 (Soplaril SA and Manufacture de Vetements Paul Boyé SA). This multi-layer chemical barrier fabric comprises a non-woven polyolefin substrate bonded by means of an adhesive tie layer to a multi-layer barrier film having an outer surface layer of polyolefin film. The multi-layer barrier film has a protective material component comprising either ethylene-hydrolysed vinyl acetate/ethylene copolymer (EVOH) at least 6 microns thick, or polyethylene terephthalate at least 12 microns thick coated with a layer of polyvinylidene chloride at least 3 microns thick. The outer film layer and non-woven substrate may both be polyethylene or may both be polypropylene to aid welding of the surfaces together. The film layers may be either co-extruded or bonded using adhesive tie layers.
The prior art chemical barrier composites all comprise film layers bonded together over the whole planar interface between any two adjacent film layers whether by coextrusion when the materials have an affinity for each other or are compatible, or by means of an adhesive tie layer when the materials have no affinity or are incompatible. The different film layers in any of the prior art multi-layer film constructions are thus in intimate contact with each other or with an adhesive tie layer over the whole of their planar interfacial surfaces. The disadvantage of this is that the fabrics/protective apparel made from such composites are generally stiff and uncomfortable to wear.
For extreme environments laminated materials have been developed consisting of many bonded layers. The company Saint-Gobain Performance Plastics markets such a material under the name Challenge®. Challenge® contains perfluoropolymer films as the main chemical barrier component, and may comprise as many as twelve polymeric layers which are bonded together over their whole surface, so that each layer is in intimate contact with the adjacent layer(s). Such materials find their main application in military protective suits and shelters.
A disadvantage of providing a chemical barrier material comprising multiple layers is that as the number of film layers is increased, the flexibility and perceived softness of the material decreases. This is exacerbated by bonding the multiple layers over their whole planar interfaces such that when flexed, the individual film layers are unable to move relative to each other. This increases the stiffness of the material.
An example of such a commercially available composite is “Tyvek® F”, a chemical barrier composite marketed by E.I. du Pont de Nemours. Tyvek® F comprises a high density polyethylene flash-spun non-woven substrate carrying a chemical barrier layer with a thermoplastic surface layer of polyethylene. The polyethylene film aids welding of the film surface and the non-woven substrate when manufacturing the required protective apparel. The chemical barrier properties of Tyvek® F are excellent against a wide range of different chemicals and chemical classes. The comfort factor is particularly important for industrial chemical protection applications where the use of such protection may be frequent. However, garments made from Tyvek® F are harsh to the touch, noisy and uncomfortable to wear.
The main object of the present invention is thus to provide a multi-layer chemical barrier fabric which overcomes or substantially alleviates the aforementioned problems.
The Applicant has discovered a principle which is that all the layers of a chemical barrier fabric can be in less than all-over contact with one another to provide a significantly improved chemical barrier effect over the sum barrier properties of the component layers.
In order to carry this principle into effect and from a first aspect, the present invention resides in a laminated chemical barrier fabric including at least first and second chemical barrier layers which have an interfacial region therebetween and which are intermittently point bonded providing a point-bonded area which is in the minority and an un-bonded area which is in the majority in the interfacial region.
By means of the intermittent point bonding of this aspect of the invention, the layers of the laminated chemical barrier fabric are not in continuous intimate contact over their whole planar interfaces, but are in intimate contact only in discrete bonded areas provided by the intermittent point bonding. The majority un-bonded area leaves a nominal air gap in the interfacial region between the chemical barrier layers. The reduced area of intimate contact between the chemical barrier layers of the laminated chemical barrier fabrics in accordance with the invention not only provides improved chemical barrier properties but also confer advantages in the required physical properties for use in protective apparel applications such as softness and comfort in use.
Advantageously, the majority unbonded area is at least about 60% and the minority point-bonded area no more than about 40% of a planar face of a chemical barrier layer in the interfacial region.
The minority point-bonded area may be from approximately 1% to approximately 40%, or from approximately 2% to approximately 19%, of a planar face of a chemical barrier layer in the interfacial region between the chemical barrier layers. However, point-bonded areas from approximately 19% to approximately 40% ensure that the chemical barrier fabric is very well bonded if, for example, it is to be used in a mechanically demanding application, whilst still conferring improved chemical barrier properties over the sum barrier properties of the individual components and avoiding compromising the synergistic effect on chemical barrier properties and increasing stiffness with higher bond areas.
The chemical barrier fabric of the present invention is distinguished from the chemical barrier fabric described in U.S. Pat. No. 4,833,010 to Kappler Safety Group as, in the fabric of the present invention, it is not essential to provide an additional component layer, such as a non-woven fabric, to separate the fabric layers to provide enhanced chemical barrier properties. The fabric of the present invention is therefore more flexible and less noisy in use than the multi-layer composite materials described in the prior art. A further advantage of the fabric of the present invention is that its structure provides a synergistic effect on chemical barrier properties, over and above the additive barrier properties of the component layers, due to the lack of intimate contact over the major area of adjacent interfaces of the component layers.
Intermittent (also known as discontinuous) point bonding providing discrete bonded areas (point-lamination pattern in a lamination process) may be provided by any means known to the skilled person. Such means can be adhesive bonding such as hot melt point adhesive bonding or powder point adhesive bonding which form the point-bonded areas or thermal bonding using heat and pressure with a single lamination pattern calender roll of which the lamination pattern has a plurality of lamination points which form the point-bonded areas. The calender roll may be a thermo-bonding calender cooperating with a smooth counter roll or a calender that cooperates with an ultrasonic applicator. Such calender rolls generally have a 19% point lamination pattern which is the industry standard and which falls within the preferred minority point-bonded area of a planar face of a chemical barrier layer in the interfacial region between the chemical barrier layers referred to above. Thus, a preferred embodiment of the present invention also includes a minority point-bonded area of 19% of a planar face of a chemical barrier layer in the interfacial region between the chemical barrier layers.
The first and second chemical barrier layers may each comprise a single layer polymer film. Alternatively, the first and second chemical barrier layers may each comprise a co-extruded (multilayer) film. In another alternative, the first chemical barrier layer may comprise a single layer polymer film, and the second chemical barrier layer may comprise a co-extruded (multilayer) film.
In order to provide for ease of lamination, the polymer preferably has a broad softening range well below the melt point of the polymer. The polymer is preferably a polyolefin, in particular polypropylene or a copolymer of polypropylene.
The co-extruded film preferably includes a chemical barrier middle (or core) layer co-extruded with first and second polyolefinic outer layers.
In a preferred embodiment, the co-extruded film includes a middle layer of hydrolysed vinyl acetate ethylene polymer (usually referred to as ethylene vinyl alcohol or EVOH) preferably of minimum 4 microns thickness, co-extruded with first and second outer layers of polypropylene copolymer. Alternatively, the middle layer of the co-extruded film may incorporate an alternative chemical barrier such as polyamide resin or polyvinylidine chloride resin.
The middle layer of the co-extruded film is preferably bonded to the first and second outer layers by use of a thin adhesive tie layer, typically about 1 micron to 4 microns thick. The outer layers of polypropylene copolymer are conveniently from about 8 microns to about 20 microns thick.
The chemical barrier fabric may further include an optional non-woven layer point-bonded to either of the opposing outer faces of the multi-layer films. The non-woven layer acts to provide both strength to the fabric and comfort as it may form the inside layer of a finished item of protective apparel.
Preferably the non-woven layer comprises a polymer such as a polyolefin or spunbonded polypropylene. Any fabric of thereto-fusible polymer or comprising a mixture of fibres including sufficient thermo-fusible fibres to form a permanent bond to the adjacent film surface may be suitable to provide the strength and comfort requirements of the product. By way of example and without limitation carded or hydro-entangled nonwoven fabrics, which may be composed either of 100% polypropylene fibres or a mixture of fibres such as 85% rayon or viscose fibres and 15% polypropylene fibres, may be considered suitable.
Conveniently, the composition of the polymer film is substantially identical to the composition of the outer layers of the co-extruded film. The composition of the non-woven layer may also be substantially identical to either the first and second chemical barrier layers or, if a co-extruded film is used, to the outer layers of the co-extruded film. Alternatively, the non-woven fabric may comprise mixed fibres or filaments at least one of which is formed of a substantially identical polymer to the polymer films or to the outer surfaces of the co-extruded films.
Thus, to form the chemical barrier fabric of the present invention, the co-extruded film may be intermittently point-bonded to a second or third component layer composed entirely or sufficiently of a substantially identical polymer to that used in the outer surfaces of the co-extruded film to form a permanent bond. By “substantially identical” it is meant that there is sufficient chemical and physical similarity between the polymers, particularly polyolefins, to form permanent thermal bonds when subjected to the appropriate temperature and pressure conditions during the laminating (point bonding) process. Such conditions are well known in the art.
The invention also comprehends a method of manufacturing any of the laminated chemical barrier fabrics defined hereinabove.
Therefore, according to a second aspect of the present invention there is provided a method of manufacturing a laminated chemical barrier fabric by a lamination process including intermittently point-bonding at least first and second chemical barrier layers which have an interfacial region therebetween to provide a point-bonded area which is in the minority and an un-bonded area which is in the majority in the interfacial region.
Advantageously, the intermittent point-bonding provides a majority un-bonded area which is at least about 60% and a minority point-bonded area of no more than about 40% of a planar face of a chemical barrier layer in the interfacial region.
As mentioned previously, intermittent point bonding may provide a minority point-bonded area from approximately 1% to approximately 40%, from approximately 2% to approximately 19%, or from approximately 19% to approximately 40% of a planar face of a chemical barrier layer in the interfacial region between the chemical barrier layers.
Advantageously, the majority unbonded area is at least about 60% and the minority point-bonded area no more than about 40% of a planar face of a chemical barrier layer in the interfacial region.
Intermittent point-bonding may be carried out by applying heat and pressure to discrete areas of the surface of the fabric, such as thermo-calender bonding or ultrasonic bonding. Alternatively, any other suitable method such as intermittent adhesive point bonding may be used.
A non-woven layer may be intermittently point-bonded simultaneously to the first or the second chemical barrier layer with any of the percentage point-bonded areas referred to above. Further layers may also be simultaneously point-bonded to the two or three-layer fabric, still providing the aforementioned point-bonded area.
According to another aspect of the present invention, there is provided a protective garment produced from any of the chemical barrier fabrics and/or by any of the methods defined hereinabove. Such garments may include, for example, suits, gloves, drapes etc. According to another aspect of the present invention there is provided non-apparel cover articles from the aforedescribed chemical barrier fabric. Such articles may include, for example, chemical barrier tarpaulins, bags, tents, shelters, evacuation bags or casualty bags.
In order that the invention may be more readily understood, some embodiments thereof will now be described, by way of example only, with reference to the accompanying drawings, in which:
Referring to
In order to effect intermittent point bonding of the material of the chemical barrier layers 18, 20 and 22, the upper calender roll 14a has a plurality of raised bosses 24, each boss providing a bond point 26. The bosses 24 are generally arranged in a pattern, known as a point-lamination pattern, on the surface of the upper calender roll 14a whilst the lower calender roll 14b has a smooth surface. The individual chemical barrier materials are generally supplied in a wound state, and are unwound and simultaneously passed between the rotating upper 14a and lower 14b calender rolls. The chemical barrier layers 18, 20 and 22 are intermittently point-bonded together at the nip 16 where the raised bosses 24 of the upper calender roll 14a compress the materials against the smooth surface of the lower calender roll 14b. The heat of the calender rolls 14a and 14b softens the material of the individual chemical barrier layers 18, 20, 22 and together with the pressure applied at the bond points 26 of the point-bonding pattern causing the materials of the chemical barrier layers to be melted locally, acts to create a point-bonded laminate of the layers 18, 20 and 22, providing a point-bonded area which is in the minority and an un-bonded area which is in the majority in an interfacial region between each two adjacent chemical barrier layers 18, 20 and 20, 22.
In use, the two calender rolls 14a and 14b are held apart by the materials being point-bonded, to an extent dependant primarily on the thickness of the materials and the set pressure. Heating of both the upper 14a and lower 14b calender rolls is achieved by thermostatically regulating the temperature of oil passing through each calender roll. The calender rolls 14a and 14b are heated to temperatures which are dependent upon the melting point of the materials being laminated. For example, if the materials comprise polypropylene, which has a melting point of 165° C., the oil of the upper calender roll 14a is typically maintained at a temperature of approximately 160° C., and the oil of the lower calender roll 14b is maintained at a temperature of approximately 155° C. These oil temperatures provide temperatures at the calender roll surfaces within the softening range of polypropylene and sufficient for bonding to be achieved between the components under pressure.
It will be appreciated by the skilled person that the pressure applied by the calender rolls 14a and 14b to the materials can be varied, along with the speed of rotation of the calender rolls. These factors have to be taken into account together with other factors such as the softening and melting points of the materials used, and the temperature of the bonding process. The calender roll speed determines the amount of time the materials are subject to the pressure and heat at the nip 16. Accordingly, the speed of the calender rolls 14a and 14b has to be set to ensure enough exposure time is given for the heat and pressure point-bonding to occur.
Referring now to
It will be appreciated that the arrangements shown in
To manufacture the chemical barrier fabric 12 in the alternative laminating apparatus incorporating, the ultrasonic applicator 28, the separate chemical barrier layers 18, 20 and 22 are generally provided in a wound state, and are unwound and simultaneously introduced into the gap between the ultra-sonic horn 32 and the anvil roll 30. The anvil roll 30 is rotated, and the chemical barrier layers 18, 20 and 22 are then point-bonded where the raised bosses 24 of the anvil roll 30 meet the ultra-sonic horn 32. The materials of the layers 18, 20 and 22 are bonded by the action of heat and pressure with the materials of the layers being melted locally, as for the calendar unit 10a, but the heat is generated by localised friction caused by the application of the ultra-sonic horn 32 acting upon the unheated anvil roll 30. Again, local melting acts to create a point-bonded laminate of the layers 18, 20 and 22, and provides a point-bonded area which is in the minority and an un-bonded area which is in the majority in the interfacial region between each two adjacent chemical barrier layers 18, 20 and 20, 22. The ultra-sonic horn 32 and the anvil roll 30 may advantageously be cooled to minimise thermal expansion of the components so that the gap setting between the horn 32 and the surface of the raised bosses 24 is kept as near constant as possible during extended production. This is typically achieved by air cooling the ultra-sonic horn 32 and water cooling the anvil roll 30.
The structure of the chemical barrier fabric 12 produced by the laminating processes described with reference to
Referring firstly to
In
Referring now to
The proportion of the chemical barrier fabric 12 which is bonded is dependent upon the point-bonding pattern formed on the upper calender rolls 14a (
In the present invention, the un-bonded areas are in the majority and the point bonded areas are in the minority in the respective interfacial region between the two adjacent chemical barrier layers 18, 20 and 20, 22. Put another way, the point-bonding pattern is selected such that the point-bond area forms a minority only of the total surface area of the fabric 12. That is, such that the point-bonded area is less than about 40% of the surface 38 and 40 (see
Examples of suitable point-bond patterns for manufacturing the chemical barrier fabric 12 of the present invention are given in
Firstly,
Secondly,
Lastly, a point-bond pattern comprising a plurality of diamonds is shown in
The present invention will be further understood by referring to the following Examples 1 to 6, and to
Referring to
A known co-extruded polymer film 46a of total thickness 40 microns is shown in
The 30 microns polypropylene co-polymer film 48 of Example 1 and the co-extruded polymer 46a film of Example 2 were bonded together with a 40 g/m2 basis weight polypropylene spunbonded non-woven fabric 58 using thermal point-bonding in a single calender bonding lamination step. The resultant chemical barrier fabric 12 thus comprised a 30 microns polypropylene co-polymer film forming the upper layer 18 (and upper surface 38) of the fabric, a non-woven layer 58 forming the lower layer 22 (and lower surface 40) of the fabric, and a co-extruded film layer disposed therebetween forming the middle layer 20 of the fabric. This fabric structure is shown in
The diamond point-bond pattern of
This chemical barrier fabric 12 was submitted to permeation testing of a 35% ammonia solution under the same conditions as Examples 1 and 2. The breakthrough time for this chemical barrier fabric was 91 minutes. It should be noted that this is appreciably in excess of the sum of the breakthrough times for the individual component films 48 and 46a tested in Examples 1 and 2. It should be noted that although neither Example 1 and Example 2 were bonded to a nonwoven fabric, the comparison with Example 3 is still valid since the test solution is in contact with the film surface of Example 3 while the collection medium, in this case deionised water is pumped within a closed loop system on the opposing side of the sample. The nonwoven fabric therefore can have no influence over the permeation of ammonia through the film layers. Furthermore, the comparison of the permeation rate for Example 3 with those of Example 1 and Example 2 indicates that the point bonding process has not significantly damaged either of the film layers when compared to the intact components of Example 1 and Example 2.
The explanation of the synergistic effect is not easy to elucidate, but in addition to the diffusion rate of the chemical under consideration through the thickness of any of the film component layers 18 and 20 of the chemical barrier laminate 12 there will undoubtedly be a contribution from sorption and desorption at the film-air interfaces. This is illustrated for any one single layer of film 18 or 20 in
A known co-extruded polymer film 46b of total thickness 40 microns is shown in
This polymer film 46b was tested in its unprocessed state for permeation of 35% ammonia solution, and the breakthrough time was 52 minutes.
Referring now to
The resultant chemical barrier fabric 12 thus comprised a 30 microns polypropylene co-polymer film forming the upper layer 18 (and thus upper surface 38) of the fabric 12, the non-woven fabric forming the lower layer 22 (and thus lower surface 40) of the fabric, and two co-extruded polymer films provided in respective first 20a and second 20b middle layers. The diamond point-bond pattern of
This chemical barrier fabric 12 was submitted to permeation testing of a 35% ammonia solution under the same conditions as the previous examples. The breakthrough time for this particular chemical barrier fabric 12 by the same test method as used when testing Examples 1 to 4, was 180 minutes. This is appreciably in excess of the sum of the breakthrough times for the individual component films tested in Examples 1, 2 and 4 which is 81 minutes. The same comments on the validity of the comparison of Example 3 with Examples 1 and 2 apply to this Example also so that the synergistic effect of combining and bonding films to give a chemical barrier fabric of this invention is clearly evident.
Two layers of the polypropylene co-polymer film 48 of Example 1, the co-extruded film 46a of Example 2, and the co-extruded film 46b of Example 4 were bonded together with a 40 g/m2 basis weight polypropylene spunbonded non-woven fabric 58 using thermal point-bonding in a single calender bonding lamination step. The resultant fabric is shown in
The diamond bond pattern of
The chemical barrier fabric 12 was submitted to permeation testing of a 35% ammonia solution under the same conditions as previous Examples 1 to 5 and the breakthrough time exceeded 326 minutes. This is appreciably in excess of the sum of the breakthrough times for the individual component films tested in Examples 1, 2 and 4 which is only 89 minutes and further demonstrates the synergistic effect of combining and bonding films to give a chemical barrier fabric of this invention.
Having described particular preferred embodiments of the present invention, it is to be appreciated that the embodiments in question are exemplary only, and that variations and modifications such as will occur to those possessed of the appropriate knowledge and skill may be made without departure from the scope of the invention as set forth in the appended claims. For example, the chemical barrier fabric is not limited to the number (or composition) of the layers described herein: more chemical barrier layers and/or support layers may be added as required.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0521630.4 | Oct 2005 | GB | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 689990 | Schroeder | Nov 1901 | A |
| 3169899 | Steuber | Feb 1965 | A |
| 4400227 | Riemersma | Aug 1983 | A |
| 4572753 | Bach | Feb 1986 | A |
| 4725473 | Van Gompel et al. | Feb 1988 | A |
| 4833010 | Langley | May 1989 | A |
| 4992335 | Guerra et al. | Feb 1991 | A |
| 5102711 | Keller et al. | Apr 1992 | A |
| 5162148 | Boyé et al. | Nov 1992 | A |
| 5449428 | Desmarais et al. | Sep 1995 | A |
| 5509142 | Connell | Apr 1996 | A |
| 5523146 | Bodford et al. | Jun 1996 | A |
| 5560974 | Langley | Oct 1996 | A |
| 5589249 | Bodford et al. | Dec 1996 | A |
| 5968643 | Topolkaraev et al. | Oct 1999 | A |
| 6235658 | Panzer et al. | May 2001 | B1 |
| 6286145 | Welchel et al. | Sep 2001 | B1 |
| 20010051481 | Carroll | Dec 2001 | A1 |
| 20020016122 | Curro et al. | Feb 2002 | A1 |
| 20040091677 | Topolkaraev | May 2004 | A1 |
| 20040102125 | Morman et al. | May 2004 | A1 |
| 20050037683 | Konishi et al. | Feb 2005 | A1 |
| 20050076418 | von Blucher | Apr 2005 | A1 |
| 20050191918 | Langley | Sep 2005 | A1 |
| Number | Date | Country |
|---|---|---|
| 0097206 | Jan 1984 | EP |
| 0391661 | Apr 1990 | EP |
| 0505027 | Feb 1992 | EP |
| 0604736 | Nov 1993 | EP |
| 0933198 | Aug 1999 | EP |
| 1205296 | May 2002 | EP |
| 1304216 | Apr 2003 | EP |
| 1506721 | Feb 2005 | EP |
| 2332644 | Jun 1999 | GB |
| 58074316 | May 1983 | JP |
| 62282914 | Dec 1987 | JP |
| 63037923 | Feb 1988 | JP |
| 1077518 | Mar 1989 | JP |
| 6079784 | Mar 1994 | JP |
| 7186266 | Jul 1995 | JP |
| 11269315 | Oct 1999 | JP |
| 2001301093 | Oct 2001 | JP |
| 9517302 | Jun 1995 | WO |
| 0009333 | Feb 2000 | WO |
| 0013889 | Mar 2000 | WO |
| 0102163 | Jan 2001 | WO |
| 0191992 | Dec 2001 | WO |
| 2004035305 | Apr 2004 | WO |
| 2004099009 | Nov 2004 | WO |
| Entry |
|---|
| Lue, C.T. et al.; “Economical Breathable Films for Medical and Consumer Soft Goods”; Polymers, Laminations & Coatings Conference; 1999; pp. 845-849. |
| Hale, W. R. et al.; “Linear Low Density Polyethylene Resins for Breathable Microporous Films”; INJ Fall 2002; pp. 34-40. |
| Rodie, “Assistant Editor; Quality Fabric of the Month”; Textile World; Jan. 2005; p. 1. |
| Dictionary.com definition of “barrier.” |
| European Office Action dated Jun. 6, 2016 for Application No. 06794845.5. |
| Number | Date | Country | |
|---|---|---|---|
| 20140141210 A1 | May 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12091361 | US | |
| Child | 13865347 | US |