Chemical grafting onto a substrate and coating composition

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] This invention relates to coatings on a substrate, and, more specifically, to coatings that do not delaminate from the substrate and to coatings that are capable of receiving indicia.

[0003] 2. Description of the Related Art

[0004] It is generally known in the art that the surface properties of shaped articles such as polymeric films and fibers can be modified by graft polymerization processes wherein the article is treated with a free radical generating agent such as an organic peroxide or high energy radiation and then contacted with an ethylenically unsaturated monomeric material under conditions wherein the monomer or graft polymer chain is caused to be covalently bonded to the substrate.

[0005] One particular process involves the treatment of natural or synthetic polymer substrates containing active hydrogen with an aqueous solution containing a silver salt (silver nitrate), a free radical polymerization catalyst and a free radically polymerizable monomer. The silver salt acts upon the substrate to remove active hydrogen thereby creating active sites or free radicals along the molecular chain and initiating and propagating polymerization of the monomer in conjunction with the free radical polymerization catalyst. The resulting product is a graft copolymer comprising a substrate having a plurality of polymeric side chains covalently bonded thereto. Examples of such processes are disclosed in U.S. Pat. Nos. 3,401,049 and 3,698,931, which are incorporated herein by reference in their entireties. This process is similar to grafting processes disclosed in U.S. Pat. Nos. 5,342,659; 5,439,969; 5,552,472; and 5,741,548, which are incorporated herein by reference in their entireties.

[0006] Organic solvent-based coating compositions are known in the art based on compositions curable by condensation reactions and containing polymeric material such as hydroxy terminated polyesters, diesters, acrylics and alkyds and an amino or polyisocyanate crosslinking agent. These formulations are adapted to be applied to a substrate such as metal, heated to drive off the solvent and further heated at temperatures above 80 degrees C. to activate the crosslinking mechanism.

[0007] It is known in the prior art that it is difficult to bond ink to certain substrates such as wood-based products and plastics, and even more specifically to polyolefin. The prior art discloses that the substrates may be precoated with a material to which the ink bonds. However, the prior art also discloses that the coatings may delaminate or be otherwise removed from the substrate. This is especially true for plastic substrates that are flexible or heat shrinkable, such as polyolefin tubing.

[0008] It is known in the prior art that a substrate may be treated to grow a polymer coating using a process known as chemical grafting. The resulting coating is covalently bonded to the substrate that is resistant to delamination. Chemical grafting involves the activation of the substrate. Once the substrate has been activated, chains of monomers linked by carbon-carbon bonds grow on the substrate as whiskers. These whiskers impart new and desirable properties to the substrate without damaging any of the existing positive characteristics of the substrate.

[0009] The chemical grafting processes relics on the fact that many materials both naturally occurring and synthetic, possess hydrogens which are more active than the “bulk hydrogens.” Examples of relatively more active hydrogens include the tertiary hydrogen in polypropylene, the amide hydrogen in proteins, and the hydroxyl hydrogen in polysaccharide.

[0010] The chemical grafting process utilizes graft initiators (GI) that have the capacity of removing the active hydrogens and initiating the growth of polymer chains at the site of the removed hydrogen. In the case of polypropylene, the series of reactions is represented as follows:

[0011] A • represents a free radical, anion or cation, depending on whether the GI removes a hydrogen and one electron, no electrons, or two electrons. The below structure:

[0012] represents a unit of vinyl monomer where X governs the property or properties that are obtained with the resulting polymers attached and grown on the substrate. The graft polymer chains are formed from vinyl monomers or monomers contaning appropriate functionability, e.g. groups such as hydroxyl, carboxyl, epoxy, amide, amine anhydride. In many instances a mixture of monomers is employed and often more than one property can be altered in one processing step. The polymers, whose length can be controlled, are permanently attached to the substrate. The linkage is between the grafted polymer and the substrate is covalent and cannot be leached or otherwise removed from the substrate absent mechanical means such as abrasion.

SUMMARY OF THE INVENTION

[0013] In an aspect of the invention, a composition provides a chemically grafted coating onto a substrate, wherein the composition comprises an acrylate and a grafting initiator. In further aspects of the invention, the acrylate is a waterborne urethane acrylate.

[0014] In further aspects of the invention, the composition comprises resistance agent, an adhesion agent, a UV curing photoinitator, a defoaming agent, and/or a deglossing agent. The resistance agent increases the chemical or mechanical resistance of the coating. In still further aspects of the invention, the resistance agent is an acryl-alkyd emulsion, a polyether, or a polyethylene glycol diacrylate. In other aspects of the invention, the adhesion agent is a polyethylene glycol diacrylate or an ethoxylated trimethylol propane triacrylate monomer. In additional aspects of the invention, the UV curing photoinitiator is 2-hydroxy-2-methyl-1 phenyl-propane-1-one.

[0015] In an aspect of the invention, the composition comprises VIAKTIN VTE 6155W/50WA at 20-30 parts per weight; RESYDROL VAY 6278W/45WA at 4-5 parts per weight; RESYDROL AY 586 W/28 WA at 5-7 parts per weight; BYK 024 at 0.1-0.2 parts per weight; FUJI 370 at 1.5-3.0 parts per weight; SR 344 at 0. 12-0.20 parts per weight; de-ionized water at 4-50 parts per weight; ferrous ammonium sulfate (0.1% in de-ionized water) at 0.10-0.15 parts per weight; and DARACUR 1173 at 1.2-1.8 parts per weight.

[0016] In an aspect of the invention, the composition comprises VLAKTIN VTE 6155W/50WA at approximately 28.95 parts per weight; RESYDROL VAY 6278W/45WA at approximately 4.45 parts per weight; RESYDROL AY 586 W/28 WA at approximately 5.00 parts per weight; BYK 024 at approximately 0.10 parts per weight; FUJI 370 at approximately 1.8 parts per weight; SR 344 at approximately 0.16 parts per weight; de-ionized water at approximately 46.00 parts per weight; ferrous ammonium sulfate (0.1% in de-ionized water) at approximately 0.10 parts per weight; and DARACUR 1173 at approximately 1.55 parts per weight.

[0017] In an aspect of the invention, the composition comprises VIAKTIN VTE 6155W/50WA at approximately 28.95 parts per weight; RESYDROL VAY 6278W/45WA at approximately 4.45 parts per weight; RESYDROL AY 586 W/28 WA at approximately 5.00 parts per weight; BYK 024 at approximately 0.10 parts per weight; FUJI 370 at approximately 1.40 parts per weight; SR9035 at approximately 0.20 parts per weight; de-ionized water at approximately 46.00 parts per weight; ferrous ammonium sulfate (0.1% in de-ionized water) at approximately 0.10 parts per weight; and DARACUR 1173 at approximately 1.55 parts per weight.

[0018] In an aspect of the invention, the substrate is plastic or wood. In a still further aspect of the invention, the substrate is polyolefin.

[0019] In an aspect of the invention, a process for chemically grafting a coating onto a substrate comprising the step of providing a composition comprising an urethane acrylate and a grafting initiator along with the step of coating the substrate with the composition and curing the composition coated on the substrate. Further aspects of the invention include a product made by the process and that the substrate is plastic or wood, such as polyolefin for example.

[0020] In a further aspect of the invention, the curing step further comprises curing the composition coated on the substrate under a D bulb and an H bulb at a rate of 100-160 feet/minute. In a still further aspect of the invention, a product is made by the process having the step of curing the composition under the D bulb and the H bulb at the rate of 100-160 feet/minute. In an additional aspect of the invention, the substrate is polyolefin.

[0021] In still further aspects of the invention, processes use the compositions described above and products made with these processes, including having polyolefin as a substrate.

[0022] In still further aspects of the invention, the processes include the step of applying readable indicia onto the coating. In a still further aspect of the invention, the readable indicia is ink.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0023] In an embodiment of the invention, a co-polymer, a monomer/prepolymer and a graft initiator are mixed together and coated onto a substrate, such as plastic or wood. The resulting coating is then cured, resulting in a covalently bonded polymer coating on the substrate. In a more preferred embodiment of the invention, the substrate is flexible, such as heat shrinkable polyolefin tubing, and the copolymer comprises a functional group to add flexibility to the bonded polymer coating, with an example of such a functional group being urethane.

[0024] In embodiments of the invention, the functional groups of the monomers and prepolymers may consist of hydroxyl groups, carboxyl groups, secondary and/or tertiary amino groups, and epoxy groups. In a preferred embodiment of the invention, the molecular ratio of the reactive components of the mixture are adjusted so that no free groups are left after the reaction is complete. Examples of suitable monomers include ethoxylated trimethyl propane triacrylate, polyethylene gycol (400) diacrylate,, sodium vinyl sulfate, ethoxylated bisphenol A dimethacrylate, ethoxylated bisphenol A diacrylate, trifunctional methacrylate ester, trifunctional acrylate ester, alkoxyated diacrylate. The concentration of the monomers in the solution can vary within practically any limits. In a preferred embodiment of the invention, the concentration of monomers is between about 0.1% and about 50% of the formulation and, more preferably, between about 0.1% and about 20%.

[0025] In a step of the reaction, one of the terminal hydrogens of the co-polymer is covalently bonded to the substrate. This is accomplished by the graft initiator acting as a catalyst. The graft initiator in a preferred embodiment of the invention is ferrous ammonium sulfate which contributes the metal ion Fe++. Other embodiments of the invention may use graft initiators that contribute any other suitable metal ion, such as Fe+++, Ag+, Co++, Cu++, and ions of cerium for example. The choice of the metal ion depends of the nature of the substrate. In a preferred embodiment of the invention, only a single ion is used as a graft initiator and not a combination of ions. In a preferred embodiment of the invention the graft initiator ion salt concentration may vary in the rage of about 0.01% to 0.1% by weight of the monomers.

[0026] In an embodiment of the invention, the copolymer comprises ethylene vinyl 5 acetate copolymer (EVA) and/or ethylene ethyl acrylate copolymer (EEA), represented as structures (3) and (4), respectively, below.

[0027] The EVA and/or and the EEA is grafted to the substrate and is represented as “R—H” in the below structures and reactions. The mechanism of reaction between the EVA and/or the EEA and the monomer/prepolymer is carried out via a free radical mechanism as disclosed below.

[0028] In the first stage of the free radical mechanism, the substrate reacts with the graft initiator (GI) to create the radical:

[0029] The propagation of the polymer is then initiated by a monomer bonding to the radical:

[0030] and the polymer propagating therefrom and terminating chain propagation as shown in steps (7) and (8):

[0031] “X” represents side functional groups, which may react between themselves and with additional prepolymers or polymers included in the mixture. The reaction of the side functional groups may result in the polymer coating being crosslinked.

[0032] A radical combination reaction is used to terminate the polymer propagation step. In a preferred embodiment of the invention, the radical combination reaction is initiated by a UV curing step. Other embodiments of the invention may have the free radical produced by any other suitable means, such as by supplying a peroxide. The peroxide supplier may be any suitable catalyst, such as benzoyl peroxide, methyl ethyl ketone peroxide, tert butyl hydroperoxide, hydrogen peroxide, and ammonium ferrous sulfate. In an embodiment of the invention, the concentration of the catalyst may vary in the range of about 0.1% to about 5.0% of the polymerization solution and, in a preferred embodiment of the invention, between about 0.1% and about 10%.

[0033] In embodiments of the invention, the mixture coating may be applied to the substrate using any suitable method, such a brushing, spraying, and dipping. Embodiments of the invention have mixtures of appropriate properties for the specific application method. For example, a low viscosity mixture may be used for a spraying application.

[0034] In a preferred embodiment of the invention, ink or another indicia creating substance is applied to the coating, either before or after curing, to dispose readable indicia on the coating surface. The indicia creating substance may be visible or invisible. The invisible indicia creating substance may be, for example, machine readable, comprise electrically charged or magnetically charged particles, emit electromagnetic wavelengths outside of the visible light wavelength band, or any other suitable application.

EXAMPLE 1

[0035] The formula for the coating mixture according to an embodiment of the invention is:

1INGREDIENTSParts by WeightVIAKTIN VTE 6155W/50WA20-30RESYDROL VAY 6278W/45WA4-5RESYDROL AY 586 W/28 WA5-7BYK 0240.1-0.2FUJI 3701.5-3.0SR 3440.12-0.20De-ionized Water 4-50Ferrous Ammonium Sulfate 0.1-0.15(0.1% in De-ionized Water)DARACUR 11731.2-1.8

[0036] VIAKTIN VTE 6155 W/50 WA is the tradename of a prepolymer of urethane acrylate that acts as a binder to the substrate, which in an embodiment of the invention is polyolefin, through chemical grafting. It also forms the main polymer mix. The urethane part maintains flexibility of the polymer. RESYDROL VAY 6278W/45WA is the tradename of an acryl-alkyd hybrid emulsion that increases the chemical resistance of the polymer and improves its scrub resistance. RESYDROL AY 586 W/28 WA is the tradename of a polyether that functions as a coalescent for the VIAKTIN VTE 6155 W/50 WA and the RESYDROL VAY 6278W/45WA, which eliminates the use of solvents and improves chemical resistance of the coating. The three above-discussed ingredients are obtained from Vianova Resins, Inc., Charlotte, N.C. Other embodiments of the invention may use other suitable chemicals from other suppliers and other embodiments of the invention may only use the urethane acrylate.

[0037] BYK 024 is a tradename of a defoarner sold by BYK Chemie USA, Wallingford, CT that is mixture of hydrophobic solids and foam destroying polysiloxanes in polyglycol. Other embodiments of the invention may not have the defoamer or may have another suitable defoamer. FUJI 370 is a tradename of a deglossing or flattening agent sold by Fuji Silysia Chemical Ltd., Portland, Oreg. that is silica based. Other embodiments of the invention may not have a flattening agent or may have another suitable flattening agent. SR 344 is a tradename of a polyethylene glycol (400) diacrylate sold by Sartomer Company, Exton, PAS that promotes adhesion and increases the flexibility of the coating. Other embodiments of the invention may not have the polyethylene glycol (400) diacrylate, may have polyethylene glycol diacrylate of another weight, or may have another suitable chemical that promotes adhesion. The ferrous ammonium sulfate is the graft initiator. The Daracur 1173 is a tradename of a 2-hydroxy-2-methyl-1 phenyl-propane-1-one sold by Ciba Geigy Chemicals, Tarrytown, N.Y. It is a liquid UV curing photoinitiator for radical polymerization at a relatively high speed of curing. Other embodiments of the invention may use another UV curing photoinitator. In a preferred embodiment of the invention, the coating on the substrate cures under a D bulb and an H bulb at a speed of 100-160 feet/minute. urethane acrylate coatings in the prior art cure at a speed of 12-30 feet/minute under similar conditions.

[0038] In a preferred embodiment of the invention, the compounding procedure of the above formula is to disperse the FUJI 370 into roughly half of the VIAKTIN 6155W/50WA in a high speed mixer, then add the remainder of the VIAKTIN 6155W/SOWA and the other ingredients one at a time. After all of the ingredients are added to the batch, reduce the speed of the mixer and continue mixing for approximately twenty minutes. The resulting mixture is filtered and drawn off.

EXAMPLE 2

[0039] The formula for the coating mixture according to an embodiment of the invention is:

2INGREDIENTSParts by WeightVIAKTIN VTE 6155W/50WA28.95RESYDROL VAY 6278W/45WA4.45RESYDROL AY 586 W/28 WA5.00BYK 0240.10FUJI 3701.80SR 3440.16De-ionized Water46.00Ferrous Ammonium Sulfate0.1(0.1% in De-ionized Water)DARACUR 11731.55

EXAMPLE 3

[0040] The formula for the coating mixture according to an embodiment of the invention is:

3INGREDIENTSParts by WeightVIAKTIN VTE 6155W/50WA28.95RESYDROL VAY 6278W/45WA4.45RESYDROL AY 586 W/28 WA5.00BYK 0240.10FUJI 3701.40SR90350.20De-ionized Water8.00Ferrous Ammonium Sulfate0.10(0.1% in De-ionized Water)DARACUR 11731.55

[0041] SR9035 is a tradename of an ethoxylated trimethylol propane triacrylate monomer that is sold by Sartomer Company, Exton Pa. that introduces flexiblity, chemical resistance, and abrasion resistance besides being an adhesion promoter.

[0042] Although presently preferred embodiments of the present invention have been described in detail hereinabove, it should be clearly understood that many variations and/or modifications of the basic inventive concepts herein taught, which may appear to those skilled in the pertinent art, will still fall within the spirit and scope of the present invention, as defined in the appended claims.

Claims

1. A composition for providing a chemically grafted coating onto a substrate, wherein the composition comprises an acrylate and a grafting initiator.
2. The composition of claim 1, wherein the acrylate is a waterborne urethane acrylate.
3. The composition of claim 2, further comprising a resistance agent that increases the chemical or mechanical resistance of the coating.
4. The composition of claim 3, wherein the resistance agent is an acryl-alkyd emulsion, a polyether, or a polyethylene glycol diacrylate.
5. The composition of claim 2, further comprising an adhesion agent.
6. The composition of claim 5, wherein the adhesion agent is a polyethylene glycol diacrylate or an ethoxylated trimethylol propane triacrylate monomer.
7. The composition of claim 2, further comprising a UV curing photoinitiator.
8. The composition of claim 7, wherein the UV curing photoinitiator is 2-hydroxy-2-methyl-1 phenyl-propane-1-one.
9. The composition of claim 1, wherein the composition comprises a defoamer and a flattening agent
10. The composition of claim 1, comprising VIAKTIN VTE 6155W/50WA at 20-30 parts per weight; RESYDROL VAY 6278W/45WA at 4-5 parts per weight; RESYDROL AY 586 W/28 WA at 5-7 parts per weight; BYK 024 at 0.1-0.2 parts per weight; FUJI 370 at 1.5-3.0 parts per weight; SR 344 at 0.12-0.20 parts per weight; de-ionized water at 4-50 parts per weight; ferrous ammonium sulfate (0.1% in de-ionized water) at 0.10-0.15 parts per weight; and DARACUR 1173 at 1.2-1.8 parts per weight.
11. The composition of claim 1, comprising VIAKTIN VTE 6155W/50WA at approximately 28.95 parts per weight; RESYDROL VAY 6278W/45WA at approximately 4.45 parts per weight; RESYDROL AY 586 W/28 WA at approximately 5.00 parts per weight; BYK 024 at approximately 0.10 parts per weight; FUJI 370 at approximately 1.8 parts per weight; SR 344 at approximately 0.16 parts per weight; de-ionized water at approximately 46.00 parts per weight; ferrous ammonium sulfate (0.1% in de-ionized water) at approximately 0.10 parts per weight; and DARACUR 1173 at approximately 1.55 parts per weight.
12. The composition of claim 1, comprising VIAKTIN VTE 6155W/50WA at approximately 28.95 parts per weight; RESYDROL VAY 6278W/45WA at approximately 4.45 parts per weight; RESYDROL AY 586 W/28 WA at approximately 5.00 parts per weight; BYK 024 at approximately 0.10 parts per weight; FUJI 370 at approximately 1.40 parts per weight; SR9035 at approximately 0.20 parts per weight; de-ionized water at approximately 46.00 parts per weight; ferrous ammonium sulfate (0.1% in de-ionized water) at approximately 0.10 parts per weight; and DARACUR 1173 at approximately 1.55 parts per weight.
13. The composition of claim 1, wherein the substrate is plastic or wood.
14. The composition of claim 1, wherein the substrate is polyolefin.
13. A process for chemically grafting a coating onto a substrate comprising the steps of: a. providing a composition comprising an urethane acrylate and a grafting initiator; b. coating the substrate with the composition; and c. curing the composition coated on the substrate.
14. A product made by the process of claim 13.
15. The product of claim 14, wherein the substrate is plastic or wood.
16. The product of claim 14, wherein the substrate is polyolefin.
17. The process of claim 13, wherein the curing step further comprises curing the composition coated on the substrate under a D bulb and an H bulb at a rate of 100-160 feet/minute.
18. A product made by the process of claim 17.
19. The product of claim 18, wherein the substrate is polyolefin.
20. The process of claim 13, wherein the composition comprises VIAKTIN VIE 6155W/50WA at 20-30 parts per weight; RESYDROL VAY 6278W/45WA at 4-5 parts per weight; RESYDROL AY 586 W/28 WA at 5-7 parts per weight; BYK 024 at 0.1-0.2 parts per weight; FUJI 370 at 1.5-3.0 parts per weight; SR 344 at 0.12-0.20 parts per 5 weight; de-ionized water at 4-50 parts per weight; ferrous ammonium sulfate (0.1% in de-ionized water) at 0.10-0.15 parts per weight; and DARACUR 1173 at 1.2-1.8 parts per weight.
21. A product made by the process of claim 20.
22. The product of claim 21, wherein the substrate is polyolefin.
23. The process of claim 13, wherein the composition comprises VIAKTTN VTE 6155W/50WA at approximately 28.95 parts per weight; RESYDROL VAY 6278W/45WA at approximately 4.45 parts per weight; RESYDROL AY 586 W/28 WA at approximately 5.00 parts per weight; BYK 024 at approximately 0.10 parts per weight; FUJI 370 at approximately 1.8 parts per weight; SR 344 at approximately 0.16 parts per weight; de-ionized water at approximately 46.00 parts per weight; ferrous ammonium sulfate (0.1% in de-ionized water) at approximately 0.10 parts per weight; and DARACUR 1173 at approximately 1.55 parts per weight.
24. A product made by the process of claim 23.
25. The product of claim 24, wherein the substrate is polyolefin.
26. The process of claim 13, wherein the composition comprises VIAKTIN VTE 6155W/50WA at approximately 28.95 parts per weight; RESYDROL VAY 6278W/45WA at approximately 4.45 parts per weight; RESYDROL AY 586 W/28 WA at approximately 5.00 parts per weight; BYK 024 at approximately 0.10 parts per weight; FUJI 370 at approximately 1.40 parts per weight; SR9035 at approximately 0.20 parts per weight; de-ionized Water at approximately 46.00 parts per weight; ferrous ammonium sulfate (0.1% in de-ionized water) at approximately 0.10 parts per weight; and DARACUR 1173 at approximately 1.55 parts per weight.
27. A product made by the process of claim 26.
28. The product of claim 27, wherein the substrate is polyolefin.
29. The process of claim 13, further comprising the step of applying readable indicia onto the coating.
30. The process of claim 29, wherein the readable indicia is ink.

Divisions (1)

	Number	Date	Country
Parent	09456742	Dec 1999	US
Child	10173371	Jun 2002	US

Chemical grafting onto a substrate and coating composition

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

US Classifications

International Classifications

Abstract

Description

Claims

Divisions (1)