Patent Application
20230303858
This invention relates to paints and coatings containing chitosan that provide useful benefits over conventional coatings in the form of improved resistance to leaching, improved elongation and lesser susceptibility to fungal or mildew defacement than conventional coatings, articles coated in the same, and methods for making said coatings or coated articles.
Paints and coatings typically contain three essential ingredients: carrier liquid, binder, and additives. Pigment is also commonly added in many paints and coatings. Each of such ingredients may comprise a single component or several different items mixed into the paint or coating.
The carrier liquid is a fluid component of the paint which serves to carry all of the other paint components. The carrier liquid is part of the wet paint and usually evaporates as the paint forms a film and dries on a surface. In latex paints, the carrier liquid is usually water. In oil-based paints, the carrier liquid is usually an organic solvent. The amount and type of liquid is usually determined by features of the other paint components.
The binder component of a paint or coating is what causes the paint or coating to form a film on and adhere to a surface. In a latex paint, the binder comprises a latex resin, usually selected from acrylics, vinyl acrylics, styrene acrylics, or polyurethane dispersions (“PUDs”). In a latex paint or coating, the latex resin particles usually are in a dispersion with water as the carrier liquid.
Pigments provide the paint or coating with both decorative and protective features. Pigments are solid particles used to provide the paint or coating with various qualities, including but not limited to color, opacity, and durability. The paint or coating may also contain other solid particles such as polyurethane beads or other solids. Pigments and other solids add bulk to the paint or coating and their levels are related to the gloss or flatness of the paint or coating. Pigments may also impart color to a paint or coating.
A multitude of additives may be included in paints and coatings. The additives are typically used at relatively low levels in the paint/coating formulation, but contribute to various properties of paints and coatings, including rheology, stability, paint performance, in-can preservation, dry film preservation or protection, and application quality.
Biocides are additives that have antimildew, bacteriostatic and bactericidal properties. A variety of biocidal agents are well known and are used for various purposes including but not limited to preservation of wet paint or coatings (“in-can” preservation) and preservation or protection of dry films on coated articles. Such biocides include inorganic biocidal agents, for example, those containing metal ions, such as silver, zinc, and copper. Other inorganic biocides include phosphates, metal ion, metal or other biocide containing zeolites or hydroxyapatites. There are also organic biocides including organic acids, phenols, alcohols, and quaternary ammonium compounds.
Some biocides act specifically, such as mildewcidal or fungicidal agents, which are additives that have mildewcidal or fungicidal properties. Mildewcidal and fungicidal agents work to prevent, reduce, or forestall the formation of mildew in cured paint or coating films. Zinc compounds, including zinc oxide, are common fungicides and mildewcides, the use of which is effective at mildew, mold, and fungus prevention and/or reduction in cured films. Zinc oxide can have drawbacks and create issues in dispersibility of paints and coatings. Other known fungicides include iodopropynyl butylcarbamate (IPBC), 2-octyl-3 (2H)-isothiazolone (OIT), chlorothalonil, and the like.
Chitosan is a bio-based material that may be obtained in a renewable fashion from chitin coming from crustaceans, among other sources, and, if dispersible, would be a useful additive or filler in paint formulations. In conventional practice, despite its relatively low cost and relative renewability, chitosan is not used in paints and coatings due to its water insolubility, a negative effect on the quality of the paint and coatings, and the difficulty in adequately dispersing chitosan in latex and other waterborne, dispersion systems for paints and coatings. Providing a consistently dispersed paint or coating is important for ease of manufacturability but also for providing a high-quality paint without grit or other defects in consistency, application, appearance, or feel.
The relevant art has pursued alternative approaches in attempts at solubilizing or dispersing chitosan in water. One such approach involves providing chitosan in acidic solution. Acidic solutions are highly impractical for direct addition to waterborne paints and coatings, which are overwhelmingly basic in pH. Adding a significantly acidic solution to maintain acidity and thus maintain the chitosan in solution would greatly disturb the stability of a coating formulation and would require drastic reformulation. Other approaches require cost-prohibitive chemical modification to the chitosan polymer backbone with hydrophilic groups prior to addition to waterborne paints or coatings to provide water solubility.
The present invention comprises, in one embodiment, a paint or coating composition comprising water, latex binder resin, and additives, wherein such additives include, but are not limited to, a chitosan compound. In some embodiments, the chitosan compound additive has a particle size of less than 30 microns in the paint or coating, determined using ASTM D1210-05 “Standard Test Method for Fineness of Dispersion of Pigment-Vehicle Systems by Hegman-Type Gage”. In another embodiment, the invention comprises a coated article formed from a paint or coating composition comprising water, latex binder resin, and additives, wherein such additives include but are not limited to, a chitosan compound and wherein the paint or coating composition dries to form a film on the coated article. The chitosan compound is distributed throughout the film on the coated article. In some embodiments, the chitosan compound additive has as particle size less than 30 microns when dispersed in a paint or coating, determined using ASTM D1210-05. Hegman gauge values below 30 microns are also indicative of adequate dispersibility of the chitosan. The dried paint or coating film displays improved elongation as measured according to ASTM D2370-16 “Standard Test Method for Tensile Properties”, improved thermocycling characteristics using the rating scales according to ASTM D714-02 “Standard Test Method for Evaluating Degree of Blistering of Paints” and ASTM D661-93 “Standard Test Method for Evaluating Degree of Cracking of Exterior Paints”, improved resistance to surfactant or other additive leaching as measured according to methods described herein. A modified version of the ASTM D5589-19 method “Standard Test Method for Determining the Resistance of Paint Films and Related Coatings to Algal Defacement” can be used to show reduced leaching of paint components in the exemplary compositions. The dried film may also be less susceptible to mildew or fungal growth and defacement than identical paints or coatings that do not include the chitosan compound. In some embodiments, coatings containing the chitosan compound may require reduced amounts of traditional fungicides like zinc oxide.
In embodiments of the present invention, chitosan is incorporated into said paints and coatings, wherein the chitosan ranges in particle size in said paints and coatings from 2 to 30 µm, 2 to 25 µm, 2 to 16 µm, or 4 to 16 µm, or less than 30 µm, less than 25 µm, less than 20 µm, or less than 16 µm.
In further useful embodiments of the present invention, chitosan is incorporated into said coatings from 0.02 to 1.0, 0.02 to 0.75, 0.05 to 0.40, or 0.02 to 0.30 percent by weight of dry coating solids.
In another embodiment, the paint or coating composition of the present invention may also include a pigment and extenders or fillers. The paint or coating composition of this embodiment has one or more of the following characteristics: pigment volume concentration (PVC) of less than 60, about 25% to about 65% by weight solids, at least 17% by weight binder polymer solids up to about 55% by weight binder polymer solids, and at least 10% by weight of a hiding pigment, for example, titanium dioxide. Further, the paint or coating composition may have one or more of the following qualities: improved dispersion of chitosan with chitosan particles in the paint or coating having particle size from 2 to 30 µm, 2 to 25 µm, 2 to 16 µm, or 4 to 16 µm, or less than 30 µm, less than 25 µm, less than 20 µm, or less than 16 µm and being evenly distributed, improved elongation in dried film form, improved thermocycling characteristics, improved resistance to surfactant or other additive leaching, and less susceptibility to fungal defacement in dried film form.
In further embodiments, said coating includes biocide additives. Such biocide additives may be selected by one having skill in the art to provide adequate additional mildew or fungal protection or other biocidal function, including but not limited to in-can preservation or dry film preservation.
In another embodiment of the invention, a method of manufacture is provided whereby a coating is made, the coating comprising water, latex binder resin, and additives, wherein such additives include, but are not limited to, a chitosan compound. The added chitosan is of relatively small particle size, in some embodiments less than 200 µm and others 100 µm. In certain other embodiments, a small particle size chitosan is obtained from traditional sources of chitosan by applying high rates of shear (e.g., as applied to pigment in the pigment grind stage of paint making) to an aqueous acetic acid solution containing chitosan and adding base (e.g. ammonium hydroxide) to neutralize the solution and precipitate out the chitosan from solution. In certain embodiments of the method of manufacture, the coating further comprises a pigment, and the chitosan is incorporated into the coating during the pigment grind stage. In certain embodiments of the method, the coating is further coated on an article and allowed to dry. The wet coating has a pH above 7, while the dry coating has a pH below 7, in certain embodiments from 5 to 6. The deacetylated, primary amine of the chitosan is present in the film in its protonated state.
The present invention comprises, in one embodiment, a paint or coating composition comprising water, latex binder resin, and additives, wherein such additives include, but are not limited to, a chitosan compound. In some embodiments, the chitosan compound additive has a particle size of less than 30 microns in the paint or coating, determined using ASTM D1210-05 “Standard Test Method for Fineness of Dispersion of Pigment-Vehicle Systems by Hegman-Type Gage”. In another embodiment, the invention comprises a coated article formed from a paint or coating composition comprising water, latex binder resin, and additives, wherein such additives include but are not limited to, a chitosan compound and wherein the paint or coating composition dries to form a film on the coated article. The chitosan compound is distributed throughout the film on the coated article. In some embodiments, the chitosan compound additive has as particle size less than 30 microns when dispersed in a paint or coating, determined using ASTM D1210-05. Hegman gauge values below 30 microns are also indicative of adequate dispersibility of the chitosan. The dried paint or coating film displays improved elongation as measured according to ASTM D2370-16 “Standard Test Method for Tensile Properties”, improved thermocycling characteristics using the rating scales according to ASTM D714-02 “Standard Test Method for Evaluating Degree of Blistering of Paints” and ASTM D661-93 “Standard Test Method for Evaluating Degree of Cracking of Exterior Paints”, improved resistance to surfactant or other additive leaching as measured according to methods described herein. A modified version of the ASTM D5589-19 method “Standard Test Method for Determining the Resistance of Paint Films and Related Coatings to Algal Defacement” can be used to show reduced leaching of paint components in the exemplary compositions. The dried film may also be less susceptible to mildew or fungal growth and defacement than identical paints or coatings that do not include the chitosan compound In some embodiments, coatings containing the chitosan compound may require reduced amounts of traditional fungicides like zinc oxide.
In embodiments of the present invention, chitosan is incorporated into said paints and coatings, wherein the chitosan ranges in particle size in said paints and coatings from 2 to 30 µm, 2 to 25 µm, 2 to 16 µm, or 4 to 16 µm, or less than 30 µm, less than 25 µm, less than 20 µm, or less than 16 µm.
In further useful embodiments of the present invention, chitosan is incorporated into said coatings from 0.02 to 1.0, 0.02 to 0.75, 0.05 to 0.40, or 0.02 to 0.30 percent by weight of dry coating solids.
In another embodiment, the paint or coating composition of the present invention may also include a pigment and extenders or fillers. The paint or coating composition of this embodiment has one or more of the following characteristics: pigment volume concentration (PVC) of less than 60, about 25% to about 65% by weight solids, at least 17% by weight binder polymer solids up to about 55% by weight binder polymer solids, and at least 10% by weight of a hiding pigment, for example, titanium dioxide. Further, the paint or coating composition may have one or more of the following qualities: improved dispersion of chitosan with chitosan particles in the paint or coating having particle size from 2 to 30 µm, 2 to 25 µm, 2 to 16 µm, or 4 to 16 µm, or less than 30 µm, less than 25 µm, less than 20 µm, or less than 16 µm and being evenly distributed, improved elongation in dried film form, improved thermocycling characteristics, improved resistance to surfactant or other additive leaching, and less susceptibility to fungal defacement in dried film form.
In further embodiments, said coating includes biocides additives. Such biocide additives may be selected by one having skill in the art to provide adequate additional mildew or fungal protection or other biocidal function, including but not limited to in-can preservation or dry film preservation.
In another embodiment of the invention, a method of manufacture is provided whereby a coating is made, the coating comprising water, latex binder resin, and additives, wherein such additives include, but are not limited to, a chitosan compound. The added chitosan is of relatively small particle size, in some embodiments less than 200 µm and others 100 µm. In certain other embodiments, a small particle size chitosan is obtained from traditional sources of chitosan by applying high rates of shear (e.g., as applied to pigment in the pigment grind stage of paint making) to an aqueous acetic acid solution containing chitosan and adding base (e.g. ammonium hydroxide) to neutralize the solution and precipitate out the chitosan from solution. In certain embodiments of the method of manufacture, the coating further comprises a pigment, and the chitosan is incorporated into the coating during the pigment grand stage. In certain embodiments of the method, the coating is further coated on an article and allowed to dry. The wet coating has a pH above 7, while the dry coating has a pH below 7, in certain embodiments from 5 to 6. The deacetylated, primary amine of the chitosan is present in the film in its protonated state.
The term “chitosan” as used herein refers to derivatives of naturally occurring chitin having the following general chemical structure:
wherein n indicates the number of repeating structural units in a polymeric or oligomeric structure. Minor chemical variations in this structure are possible and will be recognized by persons having skill in the art. Chitosan may also be obtainable from other sources recognized by those having skill in the art.
Chitosan is obtainable from a number of sources by deacetylation of naturally occurring chitin. Exemplary sources of chitosan are available in different molecular weights, and ordinarily provided in acidic solution from Tidal Vision Inc. located in Bellingham, WA, Millipore Sigma, a subsidiary of Merk KGaA headquartered in Burlington, VT, Qingdao Yunzhou Biochemistry Co. Ltd. Qingdao, China, KitoZyme LLC (providing vegan-sourced chitosan) located in Herstal, Belgium, and Kimica Corporation located in Chuo-ku. Chitosan can be obtained in a dry flake form, in acidic solution, or other form. Varying molecular weights of chitosan are useful for the present invention, including but not limited to commonly available molecular weights.
Particle size of conventionally available sources of chitosan and those used in the relevant art range are commonly above 60 microns when added to paint or coatings formulations as measured by Hegman gauge drawdown. These relatively large particle sizes result in gritty appearing, poorly applying paints or coatings that are unacceptable for commercial application. Additionally, larger particles have less available surface area per equivalent mass for interaction with other components of the paint.
In embodiments of the present invention, Chitosan compounds added to paints or coatings of the present invention are of particle size from 2 to 30 µm, 2 to 25 µm, 2 to 16 µm, or 4 to 16 µm, or less than 30 µm, less than 25 µm, less than 20 µm, or less than 16 µm as measured by Hegman gauge drawdown. Without being bound by theory, it is believed that the smaller particle size of the chitosan in the paints and coatings of the present invention and resulting greater surface area per equivalent mass allows for greater interaction with components like surfactants, potentially resulting in less leaching of coating materials. One specific theorized interaction could be hydrogen bonding occurring between the chitosan and any polar monomers in the binder polymer of a paint or coating, perhaps allowing for additional positive properties like improved elongation and thermocycling.
In embodiments of the present invention, chitosan is believed to act in one sense analogously to a filler or extender particle. Extenders or fillers may be used to reduce the quantity of the pigment required to achieve a desired hiding ability, sheen, etc., without significantly affecting the color of a paint or coating established by the pigment. Exemplary, conventional fillers include, for example, sodium-potassium alumina silicates such as MINEX® 4 and MINEX® 10 (sold by Unimin Corporation). When used, such fillers may be employed in any desired amount.
A paint or coating composition made in accordance with the present invention may comprise chitosan in amounts from about 0.02 to 1.0, 0.02 to 0.75, 0.05 to 0.40, or 0.02 to 0.30 percent by weight of dry coating solids. Persons having skill in the art, in light of this disclosure, will appreciate that the amount of chitosan that can be added to a paint or coating formulation will vary based on the amount of other pigments or fillers/extenders in the paint or coating, which is indicated by the coating’s base designation and/or sheen. In an ultradeep coating, for example, additional chitosan, which behaves like a filler when properly dispersed in a paint or coating formulation, could be added, perhaps in greater amounts than the ranges provided above. The maximum amount of chitosan that can be added to a paint or coatings formulation, like with other extenders or fillers, is bounded by an increasing viscosity when a threshold amount of chitosan is added.
Paint or coating compositions in accordance with the present invention generally comprise at least about 17%, for example, at least about 17.5% by weight, to about 55% by weight of binder polymer solids. Binders useful in latex paint compositions are known in the art and include polymeric binders, such as acrylics, vinyl acrylics, or styrene acrylics binders. Other binder suitable for waterborne paint and coatings formulations may also be used and include but are not limited to polyurethane dispersions, waterborne alkyds, and mixtures or modifications thereof. In one embodiment of the present invention, the paint or coating composition is formulated to have a binder that does not result in precipitation of components or the formation of grit. The paint and coatings compositions of the present invention may further comprise at least about 5% by weight pigments. Such pigments may comprise inorganic pigments, such as titanium dioxide. Exemplary paint and coatings compositions comprise at least about 11% by weight, further for example, at least about 12% by weight, further for example, at least about 13% by weight, further for example, at least about 14% by weight, further for example at least about 15% by weight, further for example, at least about 16%, further for example at least about 17%, further for example, at least about 18%, further for example at least about 19%, and even further for example at least about 20% up to about 30% by weight titanium dioxide. In another useful embodiment, the paint or coating composition comprises more than 10% titanium dioxide. Other colored pigments or dyes may also be added to the paint, alone or in combination, to produce a wide range of colored paint. Suitable additional pigments may include calcium carbonate, talc, clay, silicates, aluminum silicates, calcium metasilicates, aluminum potassium silicates, magnesium silicates, barium sulfates, nepheline syenite, feldspar, zinc oxides or sulfides, or others known to those skilled in the art. Such additional colored pigments may be included in amounts up to about 30% by weight, for example, about 10% to about 20%. In some cases, “pigments” may also refer to functional fillers which are non-water-soluble solids. Such functional fillers may include solids which provide additional functional characteristics to the paint, for example, intumescent ingredients, such as ammonium polyphosphates, melamines, pentaerythritol and similar compounds. In one useful embodiment, the coating composition of the present invention is substantially free or totally free of intumescent ingredients such as ammonium polyphosphates, melamines, and pentaerythritol and similar compounds. In further embodiments, paints and coatings comprise no or substantially no pigment and are considered “clear coats” for application to various substrates.
The pigment volume concentration, or PVC, of a coating is the ratio of the volume of pigments (including functional fillers and fillers or extenders) to the volume of total nonvolatile material (i.e. pigment and binder) present in the coating. The coating of the present invention preferably has a PVC of about 5 to about 60. In addition, the coating composition of the present invention has a maximum solids content of less than 65% by weight, for example, about 25% by weight to about 60% by weight, further for example about 30% by weight to about 58% by weight. In certain embodiments, the PVC of the present invention can be zero.
The paints and coatings disclosed herein may also include various other additives, including but not limited to thickeners, such as urethane thickeners, and acrylic thickeners in amounts up to about 10% by weight, for example about 1% to about 2%. Synthetic organic materials might also be incorporated; these include plastic beads, hollow spheres or other similar materials. Other optional components include glycols such as ethylene and/or propylene glycol in amounts up to about 7% and other solvents such as diethylene glycol dibenzoate and dipropylene glycol dibenzoate in amounts up to about 3%. The coating composition may also contain pigment dispersing agents which can be solvents or surfactants; wet paint preservatives; dry film preservatives; foam control agents such as oils, fatty acids and silicones; slip and mar additives; adhesion promoters, and/or other known paint additives.
The paint or coating composition of the present invention may also comprise biocides including but not limited to metal ion containing compounds, polymeric biocides, heterocyclic compounds, phenols, organometallics, aldehydes, proteins, peroxygens, alcohols, enzymes, polypeptides, cationic surfactants (including quaternary ammonium compounds), and halogen releasing compounds.
Paints and coatings made in accordance with the present invention are generally formulated to have a pH between 7 and 11 in the wet state (“in-can” prior to application and curing on a substrate). In exemplary embodiments, the wet state pH is from 8 - 10, or in other embodiments, 9 - 10. Various pH modifiers can be used to regulate wet-state pH. The pH of a paint or coating is very important to provide for dispersibility and compatibility of all of the other components conventionally used in paint and coatings making. Conventional methods of incorporating chitosan into a coating involve providing the coating as an acidic solution, having a significantly lower pH in the wet state that is friendly to the dissolving of chitosan in the wet-state coating. The present invention involves the dispersion of chitosan in a traditional, higher pH wet-state coating, which allows formulation with otherwise conventional materials; a formulation toolbox that is convenient and cost-effective for a paint and coating formulator.
It should be noted that in order to make a waterborne paint or coating formulation, an appropriate dispersant/surfactant system is needed in order to disperse the polymer and pigments in the paint or coatings formulation. The process for selecting dispersants/surfactants for paint and coatings formulations is well known to those of ordinary skill in the paint formulation art. One of ordinary skill in the art would be able to select a dispersant/surfactant combination in order to make a desired paint or coating composition having good stability characteristics.
The invention encompasses in some embodiments a method for preparing a coating composition. Generally, a method of making a coating composition can comprise conventional manufacturing methods for forming a paint or coating and then the addition of the chitosan compound. Conventional manufacturing processes often involve four or more stages, these including pre-thin stage, a grind stage, a wash stage, and a thindown or letdown stage. In the pre-thin stage, one or more binder resins may be blended together with a carrier liquid within a thindown tank. Low-shear mixing may be applied in the thindown tank to form a pre-thin mixture. In the grind stage, pigments and other additives that will not homogenize under low-shear mixing may be dispersed into a carrier liquid under high shear conditions. The grind stage may be carried out in a high-shear mixing device, such as mill. The high shear applied in the grind stage breaks up agglomerates of particles and wet particles with a liquid. The composition of the liquid added when thinning the grind may be the same as or different from the composition of the carrier liquid used when preparing the grind. Next, in a wash stage, a wash liquid, which may have a composition that is the same as or different from the composition of the carrier liquid, may be pumped into the high-shear mixing device to move the grind paste into the thindown tank. Finally, in a thindown stage, the grind paste, the carrier liquid, the wash liquid, and the pre-thin mixture including any other additional additives may be blended together in the thindown tank under low shear conditions. In this stage, the coating composition concentrate may be further let down through further addition of liquid, which may have the same composition as or a different composition from the carrier liquid. The method may employ these conventional stages, or the coating composition may be prepared by other suitable methods. For example, the method may employ continuous manufacturing using component slurries.
One or more additives may be added at any suitable point during the manufacturing process, such as during the pre-thin stage, a grind stage, a wash stage, and a thindown or letdown stage.
The chitosan compound can be added in acidic-aqueous or other solution to the paint or coating and then neutralized by the addition of a base to precipitate the chitosan into dispersion in the paint or coating. The chitosan must be added such that it is present and dispersed in the paint or coating at a particle size from 2 to 30 µm, 2 to 25 µm, 2 to 16 µm, or 4 to 16 µm, or less than 30 µm, less than 25 µm, less than 20 µm, or less than 16 µm. In preferred embodiments, application of shear such as that used in a pigment grind phase of paint-making adequately maintains a stable dispersion of the precipitated chitosan to and allows for chitosan in the paint with particle sizes of from 2 to 30 µm, 2 to 25 µm, 2 to 16 µm, or 4 to 16 µm, or less than 30 µm, less than 25 µm, less than 20 µm, or less than 16 µm. In certain embodiments, chitosan is added to the pigment grind fluid during the pigment grind stage. In preferred embodiments, the chitosan compound, prior to being added to the grind fluid is dissolved in an acetic or other acid solution. A chitosan-in-acidic solution may also be provided directly (e.g. High Molecular Weight Chitosan Acetate Aqueous Solution with 3% chitosan and 6% acetic acid by weight available from Tidal Vision Inc.). Once the chitosan acidic solution is incorporated into the grind water by pouring or any suitable addition method, the chitosan is precipitated into the grind water by the addition of base (for example, ammonia) forming a dispersion of the chitosan with the other grind fluid components. In certain embodiments, the chitosan acidic solution may be added to the grind water before any other grind fluid components are added. In certain embodiments, the chitosan acidic solution is added alongside or after the other grind components are added. In certain embodiments, the base is added slowly, under the shear of the pigment grind stage to allow for adequate mixing and to avoid rapid or localized precipitation of the chitosan. The dispersion is maintained throughout the paint or coating-making process and the chitosan remains in stable dispersion.
Once prepared, the coating composition may be dispensed into a storage container, such as a paint can. The coating composition then may be transported and stored, such as in a warehouse or on a store shelf.
In certain embodiments, an article is coated with the above-described paints and coatings containing the chitosan compound such that the coating forms a dried film on the article. The dried coating film displays superior properties over an identical dried film that does not contain the chitosan compound. One such improved set of properties is in elongation. Films of the present invention may show elongation improvements from 10% additional elongation to 50% additional elongation, 10% to 40%, 20% to 50%, or 15% to 35% as compared to identical films that do not contain chitosan and as measured according to ASTM D2370-16. Without being bound to theory, it is believed that hydrogen bonding may occur between the chitosan compound and any polar monomers in the binder polymer of a paint or coating to enable improved elongation. Binder polymers with increasingly polar monomers or an increased amount of polar monomers may exhibit increased elongation.
Dried films also show improved resistance to leaching of materials. Resistance to leaching is indicated by testing conducted using ASTM D5589-19, which traditionally is used to show resistance to algal defacement, but in the present case can be used to show reduced leaching by the absence of a ring of inhibition on exemplary samples. Dried films further appear to be less susceptible to fungal (including mildew) defacement than identical films not containing a chitosan compound. Susceptibility to mildew or fungal defacement can be determined using the method described in the Examples below or by any method acceptable to a person having ordinary skill in the art.
The coating composition may be employed for any suitable purpose. In some embodiments, the coating composition may be applied to interior or exterior architectural surfaces such as wood, drywall, masonry, metal, and plaster, or over a primer coating. In certain embodiments, the coating composition may be applied to metals, composites, and other materials as a protective coating. In other embodiments, the coating composition may be applied to a surface to impart dry-erase characteristics. For example, the surface may be a wall, which may have paint or a primer already applied to the surface of the wall, over which the coating can be applied to form a dry-erase surface. The coating composition may be applied with brush, roller, sponge, or spray gun, or other conventional painting or coating tool. The cured coating may have any suitable thickness, such as a thickness ranging from 0.05 - 2 mm with preferred thickness around 0.1 mm.
Certain embodiments of the present invention include:
Embodiment 1: A coating composition comprising: (a) a carrier liquid; (c) a binder polymer; and (d) a chitosan compound having a particle size in the coating composition of less than 30 µm.
Embodiment 2: The coating composition of embodiment 1, wherein the carrier liquid comprises water.
Embodiment 3: The coating composition of any of embodiments 1-2, wherein the coating composition further comprises pigment.
Embodiment 4: The coating composition of any of embodiments 1-3, wherein the coating composition comprises 13% to 30% by weight pigment and the pigment is titanium dioxide.
Embodiment 5: The coating composition of any of embodiments 1-4, wherein the coating composition has a PVC below 60.
Embodiment 6: The coating composition of any of embodiments 1-5, wherein the coating composition has about 25% to about 65% by weight solids.
Embodiment 7: The coating composition of any of embodiments 1-6, wherein the coating composition has about 30% to about 60% by weight solids.
Embodiment 8: The coating composition of any of embodiments 1-7, wherein the coating composition comprises about 0.02% to about 1.0% by weight chitosan compound.
Embodiment 9: The coating composition of any of embodiments 1-8, wherein the chitosan compound has a particle size of less than 16 microns in the coating composition.
Embodiment 10: The coating composition of any of embodiments 1-9, wherein the dried paint film has a Hegman gauge rating of 5 or higher.
Embodiment 11: The coating composition of any of embodiments 1-10, wherein the paint has a viscosity under 120 KU.
Embodiment 12: A coated article, coated in the coating composition of any of embodiments 1-11.
Embodiment 13: The coated article of embodiment 12, wherein the coating composition forms a dried film on the article, and the dried film exhibits improved elongation as measured by ASTM D2370-16 and compared to an identical dried film having no chitosan compound.
Embodiment 14: The coated article of embodiments 12 or 13, wherein the coating composition forms a dried film on the article, and the dried film exhibits improved thermocycling properties as measured by ASTM D714-02 and ASTM D661-93 and compared to an identical dried film having no chitosan compound.
Embodiment 15: The coated article of any of embodiments 12-14, wherein the coating composition forms a dried film on the article, and the dried film exhibits resistance to leaching compared to an identical dried film having no chitosan compound.
Embodiment 16: The coated article of any of embodiments 12-15, wherein the coating composition forms a dried film on the article, and the dried film exhibits reduced susceptibility to mildew or fungal defacement as compared to an identical dried film having no chitosan compound.
Embodiment 17: A method of making a coating composition, the method comprising providing the coating composition of any of embodiments 1-11.
Embodiment 18: A method of making a coating composition, the method comprising: (a) providing a coating composition comprising a carrier liquid, binder polymer, and a pigment, wherein said coating composition is formed by conventional manufacturing methods comprising a grind process and a thindown process; and (b) adding a chitosan compound to the coating composition during the pigment grind process and applying shear to the chitosan compound along with the grind fluid in the course of the grind process.
Embodiment 19: The method of embodiment 18, wherein the chitosan compound is provided in step (b) in an acetic acid and water solution, and the grind process further comprises the addition of a base to neutralize and precipitate the chitosan compound from the acetic acid and water solution while shear is applied in the grind process.
Comparative (or “Control”) and Example paint compositions were prepared according to the weight percent amounts shown in TABLE 1, below.
1 BYK® 021 from Byk Chemie
2 Dry Chitosan Powder, Low Molecular Weight available from Millipore Sigma
3 Chitosan Acetate in Aqueous Solution (3% chitosan by weight, high molecular weight, 6% acetic acid by weight) available from Tidal Vision Inc.
4 Aqueous Ammonium Hydroxide Solution (19.7% by weight)
5 ATTAGEL® Clay 40 available from BASF
6 Zinc Oxide (dry) available from Umicore Marketing
7 POLYPHASE® 663 available from Troy Corporation
8 Isothiazolinone and Zinc Pyrithione Mixture
9 ICEBERG™ Calcined Kaolin Clay available from Burgess Pigments
10 MINEX™ 4 from Unimin Specialty Minerals
11 BYK® 021 from Byk Chemie
As indicated in Table 1, varying levels of biocide and extender were added to the different paints to show the impact of chitosan addition while maintaining PVC across the various paint compositions. Minor variations in the amount of dispersant and thickeners used were also made across paints to maintain proper grind fluid viscosity, as will be appreciated by one having skill in the art. The Example and Control Paints were formed by mixing conventional paint components according to methods known in the art. Chitosan was incorporated into Example Paints 1, 2, and 3 by taking the Chitosan Acetate Aqueous Solution (3% by weight chitosan, 6% by weight acetic acid, high molecular weight solution available from Tidal Vision Inc.) and incorporating it into the grind water prior to other grind components being added by pouring. Following the Chitosan Acetate Aqueous Solution incorporation, Aqueous Ammonium Hydroxide Solution (19.7% by weight) was added slowly, over the course of 10 minutes, to neutralize and then bring the pH of the grind fluid up to about 9 to precipitate the chitosan into a dispersion in the grind water, all while high shear (typical of that applied in conducting a grind phase) was applied by a Cowles blade. This step results in the use of about 77% by weight of the Aqueous Ammonium Hydroxide Solution indicated in Table 1. The remaining grind fluid components, including about 23% of the Aqueous Ammonium Hydroxide Solution indicated in Table 1, were then added and each paint formed by conventional mixing techniques using the materials in Table 1. Thus, the example paints were formed.
A final control paint, Positive Control Paint 2, was also formed using Dry Chitosan Powder (low molecular weight chitosan powder available from Millipore Sigma) added to the grind water prior to the addition of the other grind components by dropping the Dry Chitosan Powder into the grind water. Following the Dry Chitosan Powder addition, Aqueous Ammonium Hydroxide Solution (19.7% by weight) was added slowly, over the course of 10 minutes, to neutralize and then bring the pH of the grind fluid up to about 9, all while high shear (typical of that applied in forming a grind phase) was applied by a Cowles blade. This step results in the use of about 77% by weight of the Aqueous Ammonium Hydroxide Solution indicated in Table 1. The remaining grind fluid components, including about 23% of the Aqueous Ammonium Hydroxide Solution indicated in Table 1 were then added and each paint formed by conventional mixing techniques using the materials in Table 1.
Hegman drawdowns of both Positive Control Paint 2 and Example Paint 1 were conducted according to ASTM 1210-5 and particle size observed from the Hegman gauge drawdowns.
Thermocycling testing was conducted on Positive Control Paint 1 and Example Paint 1 as shown below in Table 2. Cracking was evaluated and rated according to ASTM D661-93 and blistering was evaluated and rated according to ASTM D714-02. Films were applied using 1-inch wide paint brushes (polyester/nylon blend or china bristle) to three types of substrates for each paint. Two coats were applied for each sample with 24 hours dry time at 40° F. and 75% relative humidity for each coat, before heat or cold was applied for testing. Samples were then subjected to freezing or heating in accordance with the test method. The abbreviations in Table 2 correspond to the following substrates: GRA = Glossy red alkyd (alkyd paint applied over redwood 6×18 in. section); CLTX = Chalky latex (latex paint applied over redwood; 6×18 in. section); SYP = Southern yellow pine (uncoated; 6×18 in. section). Samples were made in triplicate and measurements averaged, yielding the below values.
Elongation testing was conducted on Positive Control Paint 1 and Example Paint 1 as shown below in Table 3. Percent elongation was evaluated according to ASTM D2370-16. Films were made using a 10-mil 8-path bar to draw wet paint over standard release paper. This first coat was allowed to dry 1 day at 23° C. and 50% humidity. A second coat was drawn down using the same 8-path bar perpendicular to the first coat and allowed to dry for 7 days at 23° C. and 50% humidity. Films were peeled off of release paper and then cut to half-inch by 3-inch samples. Tensile and elongation testing was conducted on sample films using an Instron Tensiometer. Ten specimens were generated from each paint, with the five highest tensile strength samples selected for each paint and corresponding measurements averaged, yielding the below values (± indicating standard deviation).
To characterize leaching of materials from paint films formed of the comparative and exemplary paints, Algal defacement testing was conducted on Positive Control Paint 1, Negative Control Paint, and Example Paint 1 generally following the method of ASTM D5589-19. Films were made by making drawdowns of each paint on #41 Whatman filter paper using a 4-mil Bird bar. Films were allowed to dry for 24 hours before being cut into 1-inch by 1-inch squares. Samples were immersed in standard deionized water for 48 hours to remove any mobile ions or water-soluble components that might affect the test. Samples were then placed on solidified B-11 agar plates. Samples were inoculated with 350 µL of an algae mixture including Chlorella vulgaris var viridis, Oscillatoria lutea, Scenedesmus quadricauda, and Ulothrix gigas. Samples were then placed in a Percival incubation chamber at constant temperature (25° C.) with a fluorescent light source to initiate growth. Samples were observed at 3 weeks following inoculation.
To illustrate reduced susceptibility to fungal/mildew defacement of the exemplary dried paint films, Positive Control Paint 1 and Experimental Paint 1 were applied to aluminum panels (available from Q-Lab, Westlake, OH) as well as Hardie board substrate. A 10 mil 8-path bar was used to apply each paint to the aluminum panels to give a final coating thickness of approx. 5 mil wet. The paints were applied to Hardie board by brush (2 coats) to give a similar final finish of 5 mil wet. Both sample sets were prepared in triplicate and allowed to cure fully under ambient conditions for 1 week prior to placement in a mildew cabinet with environmental control. Throughout the experiment, the mildew cabinet was kept at 90° F. (± 2° F.) at 95-98% humidity. Vermiculite pieces were inoculated with Aspergillus niger, Penicillium Sp., and Aureobasidium pullans species fungal spores and placed on the mildew cabinet floor. The painted aluminum panels and Hardie board were hung randomly on racks in the mildew cabinet with no panel or board touching another or directly touching the inoculated vermiculite. Measurements are made by rating each panel or board according to the scale provided below in Table 4 and then averaging the triplicate results for each paint after 19 weeks of exposure.
Rating results are provided below in Table 5. Reported ratings are the average of triplicate sample runs for each paint on each substrate.
This application claims priority to and is a continuation of International Patent Application No. PCT/US2021/051013 filed on Sep. 20, 2021, which claims priority to U.S. Provisional Pat. application No. 62/706,973, filed on Sep. 22, 2020.
| Number | Date | Country | |
|---|---|---|---|
| 62706973 | Sep 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/US2021/051013 | Sep 2021 | WO |
| Child | 18187806 | US |