Patent Application
20160367722
Guided tissue regeneration (GTR) membranes are used to direct the healing and formation of tissues by helping to prevent the overgrowth of fast healing epithelial tissues into areas of more slowly healing tissues. When the membranes are used to regenerate and restore dental, craniofacial, orthopedic bone volume, and shape and function loss due to disease or injury, the surgical technique is referred to as guided bone regeneration. In guided bone regeneration, the membranes are used to stabilize bone graft material in the defect site, to provide a barrier to prevent soft tissue infiltration and to preserve the space for bone regeneration. Guided bone regeneration (GBR) membranes are widely used with bone graft applications. They are used in approximately 50% of all dental implants, to regenerate bone defects due to chronic periodontitis and edentulism. The membranes are also widely used in craniofacial traumatic injuries especially when bone grafting is required and are beginning to be used for regenerating bone in large traumatic orthopedic injuries.
Current clinically-used membranes made from expanded polytetrafluoroethylene (ePTFE), a non-degradable woven material, require a second surgery for removal and are reported to have exposure/infection rates as high as 20-44%. The removal surgery may disrupt healing in the graft area and is a burden to both patient and physician. Commercially available biodegradable collagen membranes do not require removal, but their degradation is rapid and unpredictable and may not maintain barrier function for the full healing and regeneration period of 4-6 months. Collagen membranes, crosslinked with glutaraldehyde, have slower degradation rates, but they also have poor tissue response, become exposed more often and elicit less bone formation than uncrosslinked collagen membranes. Additional problems with collagen and ePTFE membranes include infection, wound dehiscence and membrane exposure, and premature membrane degradation, especially when exposed to the oral cavity.
Electrospun nanofibers that mimic the structure and function of the natural extracellular matrix (ECM) are of great interest in tissue engineering as scaffolding materials to restore, maintain or improve the function of human tissue. Recently, there has been a growing interest in nanofibers made of chitosan, a cationic polysaccharide derived from the exoskeletons of crustaceans.
Current methods for producing chitosan nanofibers by electrospinning result in poor structure, in which beads are extensively present and or are highly susceptible to swelling/dissolution. It is difficult to obtain chitosan nanofibers that are homogenous, free of beads, and that do not dissolve or swell significantly in water. All of these are important requirements of nanofibers suitable for biomedical applications.
Implanting biomedical devices/biomaterials to replace/restore tissue function results in surgical wound or injury. The wound healing process is important to the clinical success and functional outcome of the biomedical device. An important and normal step in wound healing is inflammation. Macrophage cells play a central role in directing the inflammatory and wound healing responses. In response to the implanted device or material, the macrophages become activated and will release a variety of chemokines and cytokines to direct the cleaning up of damaged cells/tissues, removal of infectious material/agents and recruitment of fibroblasts and other cells to close the wound and replace missing tissue matrix. This is the acute inflammatory process and it typically lasts for minutes to days depending on the extent of injury.
Chronic inflammation occurs as a result of persistent inflammatory stimuli to the macrophages due to a variety of causes such as the type of implant material, micromotion, infection of the implant, implant site and or implant material degradation/leachable components. Chronic inflammation results in tissue damage, failure of the wound to close and heal properly, poor integration/adaption of implant materials/devices into host tissues and leads to compromised/failed implant function/performance.
For closure of the wound and healing to occur, the acute inflammation stage needs to subside in favor of proliferation and function of cells responsible for elaboration of tissue extracellular matrix. During the transition from acute inflammation to wound closure/healing, macrophage cells transition from an initial inflammatory state involved in removing damaged/diseased tissues and bacteria from the site (referred to as M1 macrophages) to a healing state supporting and directing the healing response for new tissue and new blood vessel formation for the newly forming tissues (referred to as M2 macrophages). The ability of implant materials to help support the transition/formation to the M2 macrophage phenotype would be a great benefit to encouraging healing and normal tissue formation around implant devices and or materials used to for repairing/regenerating tissues by helping to promote healing as opposed to an extended/chronic inflammatory response.
Current anti-inflammatory treatments that are used with implant devices/materials are pharmacologically based and are generally administered systemically. These agents are typically directed towards reducing the inflammatory response associated with M1 type macrophages but are not necessarily directed at promoting the pro-healing activity of M2 macrophages.
Therefore, a biomaterial that promotes healing/tissue formation over inflammatory processes will be of significant benefit to the success of a broad spectrum of biomedical implant materials and devices.
As described below, the present invention features methods for producing chitosan nanofibers having enhanced structural integrity and/or morphology (e.g., maintainenance of nanofiber morphology/structure), membranes comprising such chitosan nanofibers, and methods of using the chitosan membranes to promote healing of a tissue in a subject. The invention includes chitosan nanofibers having enhanced structural integrity, compositions comprising such nanofibers, and related methods of use.
The present invention also features methods for producing a modified chitosan material having anti-inflammatory and pro-healing characteristics and methods of using the modified chitosan materials in a film, a gel, a sponge, a membrane, microfibers, nanofibers, and/or nano- or micro-particles/spheres.
Compositions and materials defined by the invention were prepared or otherwise manufactured in connection with the examples provided below. Other features and advantages of the invention will be apparent from the detailed description, and from the claims herein.
One aspect of the invention includes a method of preparing chitosan nanofibers comprising electrospinning an acidic solution comprising chitosan into chitosan nanofibers, acylating one or more of the electrospun chitosan nanofibers with an acylating agent, and washing the acylated chitosan nanofibers with a hydrophilic solvent.
Another aspect of the invention includes a method of protecting structural integrity of electrospun chitosan nanofibers from dissolution comprising reversibly acylating the chitosan nanofibers.
Yet another aspect of the invention includes a membrane comprising the electrospun chitosan nanofibers made by any of the methods included herein.
In another aspect, the invention includes a membrane comprising electrospun chitosan nanofibers that are reversibly acylated to retain nanofiber structure and integrity when the membrane is exposed to a hydrophilic solvent.
In yet another aspect, the invention includes a membrane comprising electrospun chitosan nanofibers that are reversibly acylated with at least one acyl group.
In still yet another aspect, the invention includes a composition comprising electrospun chitosan nanofibers that are reversibly acylated with at least one acyl group. In various embodiments of the above aspects or any other aspect of the invention delineated herein, the acidic solution comprises trifluoroacetic acid. In another embodiment, the chitosan nanofibers are electrospun in a solution comprising trifluoroacetic acid. In another embodiment, the acidic solution further comprises at least one selected from the group consisting of a natural material, a synthetic material, and an agent. In yet another embodiment, the electrospinning of the acidic solution yields immobilized salt residues on the chitosan nanofibers.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the step of acylating comprises exposing the electrospun chitosan nanofibers to an acylating catalyst and acylating agent. In one embodiment, the acylating catalyst is selected from the group consisting of pyridine, 4-dimethylamino-pyridine (DMAP), triethylamine, diisopropylethylamine (DIPEA), lutidine, aluminum chloride, aluminum trifluoride, triphenylphosphine, tributylphosphine, and combinations thereof. In another embodiment, acylating agent comprises a butyric anhydride, acyl chloride, symmetric or mixed acid anhydride, vinyl ester, cyanomethyl ester, S-phenyl thioester, piperidino ester, pyrid-3-yl ester, 4-nitrophenyl ester, 2,4,6-trichlorophenyl ester, 2,3,4,5,6-pentachlorophenyl ester, 2,3,4,5,6-pentafluorophenyl ester, phtalimido ester, succinimido ester, 4-oxo-3,4-dihydrobenzotriazin-3-yl ester, benzotriazolyl ester, and combinations thereof.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the chitosan nanofibers comprise an acyl group selected from the group consisting of formyl, acetyl, propionyl, butyryl, isobutyryl, pivaloyl, pentanoyl, hexanoyl, and benzoyl group. In one embodiment, the acylated chitosan nanofibers comprise an acyl group selected from the group consisting of formyl, acetyl, propionyl, butyryl, isobutyryl, pivaloyl, pentanoyl, hexanoyl, and benzoyl group. In another embodiment, the chitosan nanofibers are more hydrophobic than unacylated chitosan nanofibers. In yet another embodiment, the acylated chitosan nanofibers are more hydrophobic than unacylated chitosan nanofibers.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the step of washing comprises hydrolizing the immobilized salt residues from the chitosan nanofibers. In one embodiment, the nanofibers comprise immobilized trifluoroacetate salt residues on the surface of the nanofibers. In another embodiment, the method includes contacting the acylated chitosan nanofibers with a hydrophilic solvent. In yet another embodiment, the immobilized trifluoroacetate salt residues are hydrolyzed when exposed to a hydrophilic solvent. In still yet another embodiment, the exposure to the hydrophilic solvent hydrolyzes trifluoroacetate salt residues immobilized on the nanofibers.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, nanofibers have a mean diameter in the range of about 100 to about 200 nm. In one embodiment, the nanofibers exhibit minimal swelling when exposed to the hydrophilic solvent. In another embodiment, the nanofibers exhibit minimal dissolution when exposed to the hydrophilic solvent. In yet another embodiment, the nanofibers exhibit minimal loss of nanofiber structure when exposed to the hydrophilic solvent.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the method further comprises deacylating the acylated chitosan nanofibers. In one embodiment, the step of deacylating comprises exposing the acylated chitosan nanofibers to a deacylating agent. In another embodiment, the deacylating agent is selected from the group consisting of potassium hydroxide, lithium hydroxide, sodium hydroxide, rubidium hydroxide, cesium hydroxide, calcium hydroxide, strontium hydroxide, barium hydroxide, other basic solution, and combinations thereof.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the reversible acylation prevents or minimizes swelling of the nanofibers when exposed to the hydrophilic solvent. In one embodiment, the reversible acylation protects the nanofibers from dissolution when exposed to the hydrophilic solvent. In yet another embodiment, the reversible acylation protects the nanofibers from loss of nanofiber structure when exposed to the hydrophilic solvent.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the membrane and composition further comprise at least one selected from the group consisting of a natural material, a synthetic material, and an agent. In one embodiment, the method includes incorporating an agent around and/or in the nanofibers. In another embodiment, the agent is around and/or in the nanofibers.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the membrane and composition is a barrier membrane.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the method further comprises drying the acylated chitosan nanofibers. In another aspect, the invention includes an electrospun chitosan nanofiber with a water contact angle of at least 90 degrees. In various embodiments of the above aspects or any other aspect of the invention delineated herein, the water contact angle ranges from about 93.7 to about 100.3 degrees
In another aspect, the invention includes an electrospun chitosan nanofiber comprising a x-ray diffraction spectrum of
In yet another aspect, the invention includes an electrospun chitosan nanofiber comprising a Fourier transform infrared spectroscopy of
Yet another aspect of the invention includes a method for promoting or directing healing of a tissue in a subject at a target site comprising contacting the site with a barrier membrane comprising electrospun chitosan nanofibers produced according to any of the methods included herein.
In still yet another aspect, the invention includes a method of promoting or directing formation of tissues in a subject at a target site comprising contacting the site with a membrane comprising electrospun chitosan nanofibers produced according to any of the methods included herein.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the tissue is selected from the group consisting of epithelial, abdominal, gynecological, dental, craniofacial, connective and bone tissue. In one embodiment, the subject is suffering from chronic periodontitis, edentulism, and bone regeneration. In another embodiment, the step of contacting the site comprises implanting the membrane for guided bone regeneration.
Another aspect of the invention includes a kit comprising chitosan nanofibers, acylating catalyst, acylating agent, hydrophilic solvent. In various embodiments of the above aspects or any other aspect of the invention delineated herein, the kit further comprises a deacylating agent. In one embodiment, the kit further comprises at least one selected from the group consisting of a natural material, a synthetic material, and an agent.
One aspect of the invention includes a method of preparing chitosan nanofibers comprising electrospinning an acidic solution comprising chitosan to produce chitosan nanofibers with immobilized salts; removing one or more immobilized salts on the electrospun chitosan nanofibers with an organic solvent, thus generating one or more free amino groups on the nanofibers; and contacting one or more free amino groups on the nanofibers.
Another aspect of the invention includes a method of protecting structural integrity of electrospun chitosan nanofibers from dissolution comprising reacting at least a portion of the chitosan nanofibers with an amino protecting reagent.
Yet another aspect of the invention includes a membrane comprising the electrospun chitosan nanofibers made by any of the methods included herein.
In another aspect, the invention includes a membrane comprising electrospun chitosan nanofibers with at least a portion of the chitosan nanofibers amino protected with N-tert-butoxycarbonyl (t-Boc) groups to retain structure and integrity when the bather membrane is exposed to a hydrophilic solvent.
In yet another aspect, the invention includes a membrane comprising electrospun chitosan nanofibers comprising N-tert-butoxycarbonyl groups.
In still yet another aspect, the invention includes a composition comprising electrospun chitosan nanofibers comprising N-tert-butoxycarbonyl groups.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the acidic solution comprises trifluoroacetic acid, acetic acid, formic acid, nitric acid, or hydrochloric acid. In another embodiment, the chitosan nanofibers are electrospun in a solution comprising trifluoroacetic acid or hydrochloric acid. In yet another embodiment, the electrospinning of the acidic solution yields immobilized salt residues on the chitosan nanofibers. In yet another embodiment, the immobilized salt residues comprise salts of the amino groups on the chitosan nanofibers.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the organic solvent comprises a neat organic base or a solution of an organic base in at least one organic solvent. In other embodiments, the organic solvent comprises triethylamine, trimethylamine, diisopropylethylamine or pyridine. In yet other embodiments, the organic solvent comprises acetone, tetrahydrofuran, ethyl acetate, diethylether or dichloromethane. In one embodiment, the amino protecting reagent comprises a carbonate ester reagent. In another embodiment, the carbonate ester reagent is di-tert-butyl dicarbonate. In yet another embodiment, the reaction with di-tert-butyl dicarbonate yields N-tert-butoxycarbonyl on the chitosan nanofibers.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the amino protection comprises contacting the chitosan nanofibers with a carbonate ester reagent, such as di-tert-butyl dicarbonate. In another embodiment, the reaction with the amino protecting reagent yields amino protected chitosan nanofibers. In yet another embodiment, the acylated chitosan nanofibers are more hydrophobic than unacylated chitosan nanofibers. In still yet another embodiment, the amino protected chitosan nanofibers are more hydrophobic than unreacted chitosan nanofibers.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the invention comprises contacting the amino protected chitosan nanofibers with a hydrophilic solvent. In another embodiment, the reaction prevents or minimizes swelling of the chitosan nanofibers when exposed to the hydrophilic solvent. In yet another embodiment, the reaction protects the chitosan nanofibers from dissolution when exposed to the hydrophilic solvent.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the amino protected chitosan nanofibers are on an exterior surface of the barrier membrane. In one embodiment, the amino protected chitosan nanofibers create a hydrophobic barrier for the barrier membrane against hydrophilic solvents.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, at least a portion of the amino groups on the chitosan nanofibers are protected with N-tert-butoxycarbonyl groups. In still yet another embodiment, the chitosan nanofibers with N-tert-butoxycarbonyl groups are on an exterior surface of the composition.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the nanofibers have a mean diameter in the range of about 40 to about 130 nm.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the composition exhibits minimal swelling when exposed to a hydrophilic solvent. In another embodiment, the composition exhibits minimal chitosan nanofiber dissolution when exposed to a hydrophilic solvent. In yet another embodiment, the composition exhibits minimal loss of chitosan nanofiber structure when exposed to a hydrophilic solvent.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the amino protection prevents or minimizes swelling of the barrier membrane when exposed to a hydrophilic solvent. In one embodiment, the amino protection protects the barrier membrane from chitosan nanofiber dissolution when exposed to a hydrophilic solvent. In yet another embodiment, the amino protection protects the barrier membrane from loss of chitosan nanofiber structure when exposed to a hydrophilic solvent.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the method includes incorporating an agent around and/or in the nanofibers. In another embodiment, the membrane and composition further comprise an agent around and/or in the nanofibers.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the membrane and composition is a barrier membrane.
Yet another aspect of the invention includes a method for promoting or directing healing of a tissue in a subject at a target site comprising contacting the site with a barrier membrane comprising electrospun chitosan nanofibers produced according to any of the methods included herein.
In still yet another aspect, the invention includes a method of promoting or directing formation of tissues in a subject at a target site comprising contacting the site with a membrane comprising electrospun chitosan nanofibers produced according to any of the methods included herein.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the tissue is selected from the group consisting of epithelial, abdominal, gynecological, dental, craniofacial, connective and bone tissue. In one embodiment, the subject is suffering from chronic periodontitis, edentulism, and bone regeneration. In another embodiment, the step of contacting the site comprises implanting the membrane for guided bone regeneration.
Another aspect of the invention includes a kit comprising chitosan nanofibers and an amino protecting reagent. In various embodiments of the above aspects or any other aspect of the invention delineated herein, the amino protecting reagent comprises a carbonate ester reagent. In one embodiment, the carbonate ester reagent is di-tert-butyl dicarbonate.
The invention includes a chitosan material with anti-inflammatory and pro-healing characteristics. In one embodiment, the process of modifying the chitosan with raspberry ketone involves reacting the ketone group of raspberry ketone with a free amine of chitosan, which results in the production of an imine bond.
One aspect of the invention includes a method of modifying chitosan comprising obtaining an oxygen depleted acidic solution comprising chitosan and mixing the oxygen depleted chitosan solution with a phenyl-containing carbonyl derivative; wherein the phenyl-containing carbonyl derivative reacts with at least one free amino group on the chitosan to create an imine bond, thus modifying the chitosan. In one embodiment, this reaction may be facilitated by pyridine or pyridine derivatives 4-dimethylaminopyridine (DMAP) and 4-(1-pyrrolidinyl) pyridine.
In another aspect, the invention includes a modified chitosan comprising an iminyl group.
In one aspect, the invention includes a method of producing a chitosan composition (e.g., microspheres, nanoparticles, films, gels, sponges, fibers, and the like) comprising modifying at least one free amino group on the chitosan with an iminyl group, and crosslinking the modified chitosan to form chitosan microspheres.
In yet another aspect, the invention includes a method of producing microspheres of chitosan comprising modifying at least one free amino group on the chitosan with an iminyl group, and crosslinking the modified chitosan to form chitosan microspheres.
In still another aspect, the invention includes a chitosan microsphere comprising the modified chitosan made by any method described herein.
In still yet another aspect, the invention includes a chitosan microsphere comprising chitosan modified with an iminyl group.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the acidic solution comprises acetic acid. In another embodiment, obtaining the oxygen depleted chitosan solution comprises removing O2 gas and replacing the O2 gas with N2 gas. In yet another embodiment, mixing the oxygen depleted chitosan solution with the phenyl-containing carbonyl derivative comprises heating the mixture.
In another embodiment, the iminyl group has a structure as shown in Structure II:
wherein R can be selected from the group consisting of H, C1-C6alkyl, C1-C6 alkoxy, phenyl, and any combination thereof. In yet another embodiment, the iminyl group is derived from a phenyl-containing carbonyl derivative, such as a raspberry ketone. In still another embodiment, the phenyl-containing carbonyl derivative has a structure as shown in Structure I:
wherein R1 and R2 are each independently selected from the group consisting of H, C1-C6 alkyl, and C1-C6 alkoxy; and n is an integer selected from 1, 2, 3, 4, 5, and 6
In still another embodiment, the modification increases anti-inflammatory properties as compared to unmodified chitosan. In another embodiment, the modification increases pro-healing properties of the modified chitosan as compared to unmodified chitosan. In yet another embodiment, the modification decreases macrophage production of nitric oxide.
In another embodiment, modifying the chitosan comprises obtaining an oxygen depleted acidic solution comprising chitosan and mixing the oxygen depleted chitosan solution with a phenyl-containing carbonyl derivative; wherein the phenyl-containing carbonyl derivative reacts with at least one free amino group on the chitosan to create an imine bond, thus modifying the chitosan. In one embodiment, the modified chitosan is crosslinked by exposure to a crosslinking agent.
In yet another embodiment, the microsphere has a diameter in the range of about 50 nm to about 500 μm.
In another embodiment, the microsphere further comprises an agent. In one embodiment, the microsphere forms a biodegradable shell around the agent or the agent is incorporated into the microsphere.
In another aspect, the invention includes a method for preventing inflammation or promoting healing of tissue at a target site in a subject comprising contacting the site with modified chitosan, wherein the modified chitosan is produced according to any method described herein.
In yet another aspect, the invention includes a method of decreasing nitric oxide levels at a target site in a subject comprising contacting the site with modified chitosan, wherein the modified chitosan is produced according to any method described herein.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the modified chitosan is in the form of microspheres.
In another aspect, the invention includes a kit comprising chitosan and a phenyl-containing carbonyl derivative.
In various embodiments of the above aspects or any other aspect of the invention delineated herein, the kit further comprises a crosslinking agent.
Unless defined otherwise, all technical and scientific terms used herein have the meaning commonly understood by a person skilled in the art to which this invention belongs. The following references provide one of skill with a general definition of many of the terms used in this invention: Singleton et al., Dictionary of Microbiology and Molecular Biology (2nd ed. 1994); The Cambridge Dictionary of Science and Technology (Walker ed., 1988); The Glossary of Genetics, 5th Ed., R. Rieger et al. (eds.), Springer Verlag (1991); and Hale & Marham, The Harper Collins Dictionary of Biology (1991). As used herein, the following terms have the meanings ascribed to them below, unless specified otherwise.
By “acylation” is meant the process of derivatizing chitosan with one or more acyl groups. An acylating agent reacts with chitosan, providing the acyl group that is transferred to chitosan. An acylating catalyst is used to increase the rate of transfer of the acyl group from the acylating agent to chitosan. In certain embodiments, the reaction between chitosan and the acylating catalysts does not require the presence of an acylating agent. In other embodiments, the reaction between chitosan and the acylating agents does not require the presence of an acylating catalyst.
By “acylated chitosan” is meant a chitosan fiber derivatized with one or more acyl groups.
By “acylating agent” is meant a compound that provides an acyl group that can be transferred onto the chitosan nanofibers in an acylation reaction. Examples of acylating agents include, but are not limited to, acyl chloride, symmetric or mixed acid anhydride, vinyl ester, cyanomethyl ester, S-phenyl thioester, piperidino ester, pyrid-3-yl ester, 4-nitrophenyl ester, 2,4,6-trichlorophenyl ester, 2,3,4,5,6-pentachlorophenyl ester, 2,3,4,5,6-pentafluorophenyl ester, phtalimido ester, succinimido ester, 4-oxo-3,4-dihydrobenzotriazin-3-yl ester, and benzotriazolyl ester. In certain embodiments, the symmetric or mixed acid anhydride comprises a fatty acid anhydride. In other embodiments, the acyl group is derived from a fatty acid. In yet other embodiments, the acyl group is derived from an aliphatic carboxylic acid. In yet other embodiments, the acyl group is derived from a C2-C30 aliphatic carboxylic acid, for example, a C2-C4, C4-C6, C6-C8, C8-C12, C13-C21 or C21-C30 aliphatic carboxylic acid.
By “acylating catalyst” is meant a catalyst that increases the rate of the chemical reaction to transfer an acyl group from the acylating agent onto chitosan. In one embodiment, an acylating catalyst is a nucleophilic catalyst. Examples of acylating catalysts include, but are not limited to, pyridine, 4-dimethylamino-pyridine (DMAP), triethylamine, diisopropylethylamine (DIPEA), lutidine, aluminum chloride, aluminum trifluoride, triphenylphosphine and tributylphosphine.
By “acyl group” is meant a functional group represented by R—(C═O)—, wherein R is H, alkyl, cycloalkyl, alkenyl, cycloalkenyl, alkynyl, cycloalkynyl, aryl, heteroaryl or heterocyclyl, each of each groups may be optionally substituted. Examples of acyl groups include, but are not limited to, formyl, acetyl, propionyl, butyryl, isobutyryl, pivaloyl, pentanoyl, hexanoyl, and benzoyl groups.
By “amino protecting reagent” is meant a reagent that is capable of reacting with one or more of the free amino groups on a chitosan nanofiber to yield stably protected=amino groups and prevents hydrolysis or any other unwanted reaction of the chitosan nanofibers.
By “amino protected chitosan nanofibers” is meant chitosan nanofibers reacted with an amino protecting reagent, whereby one or more free amino groups on the chitosan nanofibers are protected. In an exemplary embodiment, di-tert-butyl dicarbonate is reacted with the amines on the chitosan nanofibers to yield N-tert-butoxycarbonyl (also known as t-Boc) derivatives on the chitosan nanofiber.
By “barrier membrane” is meant any material used to protect or promote healing or prevent tissue invasion or adhesions at a site. The barrier membrane includes an implantable device that is used in craniofacial, periodontal, or orthopedic surgery to prevent cell migration into a site of tissue regeneration. For example, barrier membranes are commonly used in periodontal surgery to separate the epithelium from slower growing tissue and preventing the epithelium from migrating to a site where bone regeneration is desired. The barrier membrane also includes an implantable device for preventing tissue adhesion in abdominal and gynecological cavities. For example, abdominal adhesions can result from inflammation, infection, treatments, or unknown reasons and barrier membranes are implanted to reduce adhesion formation.
By “carbonate ester” is meant an amino protecting reagent comprising the functionality —O—C(═O)—O— that reacts with the free amino group. In one embodiment, a chitosan nanofiber has a diameter in the range of about 40 nm to about 400 nm (e.g., 130 nm). An exemplary example of a carbonate ester includes, but is not limited to, di-tert-butyl dicarbonate. In certain embodiments, di-tert-butyl dicarbonate reacts with free amino groups on the chitosan nanofiber to yield N-tert-butoxycarbonyl or t-Boc derivatives.
By “chitosan” is meant a chitin-derived polymer. Chitin is a linear polysaccharide consisting of (1-4)-linked 2-acetamido-2-deoxy-b-D-glucopyranose. Preferably, chitosan is at least about 50% deacylated.
By “chitosan nanofiber” is meant a chitosan fiber with a diameter in the range of about 5 nm to about 1000 nm. In particular embodiments, a chitosan nanofiber has a diameter in the range of about 40 nm to about 400 nm (e.g., 130 nm). In certain embodiments, a chitosan nanofiber has a diameter in the range of about 50 nm to about 500 nm. In an exemplary embodiment, the chitosan nanofiber is produced from a chitosan solution through electrospinning. The resulting chitosan nanofiber has a substantially uniform diameter.
By “chitosan microsphere” is meant spherical shell or bead comprising chitosan with a small diameter usually in the micron or nanometer range. Microspheres can be hollow and filled with an agent (as a drug or antibody) that is released once the chitosan microsphere is degraded. Microspheres may incorporate the agent into the microsphere and the agent is released as the chitosan degrades.
By “chitosan nanoparticle” is meant a chitosan particle with a diameter in the range of about 5 nm to about 1000 nm. In one embodiment, a chitosan nanoparticle has a diameter in the range of about 40 nm to about 130 nm. In an exemplary embodiment, the chitosan nanoparticle is produced from a water-in-oil emulsion process. The resulting chitosan nanoparticle has a substantially uniform diameter.
By “chitosan film” is meant a sheet of chitosan with thickness in the range of about 0.01 mm to about 5 mm. In one embodiment, a chitosan film has a thickness in the range of about 0.1 mm to about 1 mm. In an exemplary embodiment, the chitosan film is produced from a chitosan solution through solution casting. The resulting chitosan film has a substantially uniform thickness.
By “deacylation” is meant the process of removing one or more acyl groups from an acylated chitosan.
By “deacylating agent” is meant a compound that removes an acyl group from the chitosan nanofibers in a deacylation reaction. Examples of deacylating agent include, but are not limited to, a basic solution such as ammonium hydroxide, potassium hydroxide, lithium hydroxide, sodium hydroxide, rubidium hydroxide, cesium hydroxide, calcium hydroxide, strontium hydroxide, barium hydroxide, other basic solutions (such as potassium carbonate or sodium carbonate), and combinations thereof.
By “deacylated chitosan” is meant a chitosan fiber wherein one or more acyl groups have been removed. In particular embodiment, a deacylated chitosan fiber is at least about 70%, 80%, 90%, 95% or more deacylated.
By “degrades” is meant physically or chemically breaks down in whole or in part. Preferably, the degradation represents a physical reduction in the mass or structural integrity of a nanofiber by at least about 10%, 25%, 50%, 75%, 80%, 85%, 90%, 95% or 100%.
By “dissolution” is meant the loss of nanofibrous structure after exposure to a hydrophilic solvent, such as water. Resistance to dissolution is imparted when the nanofibers, films, spheres, and particles do not increase in size or do not have an electrophilic group that is susceptible to nucleophile attack by a water molecule or hydroxyl ion which results in loss of structure.
By “electrospin” or “electrospinning” is meant a process of producing chitosan nanofibers from a solution of chitosan by applying an electric charge to the chitosan solution.
By “exterior surface” is meant a thickness of the barrier membrane or composition of chitosan nanofibers exposed to the amino protecting reagent and capable of reacting with the amino protecting reagent. In certain embodiments, the amino protecting reagent is in an organic solvent which may not penetrate the entire thickness of the barrier membrane or composition, such that only the chitosan nanofibers exposed to the reagent are present on the exterior surface.
By “hydrophilic solvent” is meant a solution that is capable of dissolving hydrophilic compounds. Typically hydrophilic solvents are charge-polarized and capable of hydrogen bonding. An exemplary example of a hydrophilic solvent includes, but is not limited to, water.
By “hydrophobic barrier” is meant chitosan nanofibers on an exterior surface of the barrier membrane or composition that are amino protected such that they are not or less susceptible to hydrolysis, swelling or loss of nanofibrous structure when exposed to a hydrophilic solvent.
By “iminyl group” is meant a nitrogen-carbon double bond having the general formula shown in Structure II:
wherein R can be selected from the group consisting of H, C1-C6 alkyl, C1-C6alkoxy, phenyl, and any combination thereof.
By “organic solvent” is meant a solvent capable of dissolving the amino protecting reagent. Examples of organic solvents include, but are not limited to, triethylamine, triethylamine in acetone, tetrahydrofuran, and toluene.
By “phenyl-containing carbonyl derivative” is meant to include a molecule having a general formula of Structure I:
wherein R1 and R2 are each independently selected from the group consisting of H, C1-C6 alkyl, and C1-C6 alkoxy, and n is selected from an integer 1, 2, 3, 4, 5, and 6.
By “biodegradable” is meant susceptible to breakdown by biological activity. For example, biodegradable chitosan compositions are susceptible to breakdown by enzymes present in vivo (e.g., lysozyme, N-acetyl-o-glucosaminidase and lipases). Degradation of a chitosan composition of the invention need not be complete. A chitosan composition of the invention may be degraded, for example, by the cleavage of one or more chemical bonds (e.g., glycosidic bonds).
By “pro-healing” is meant aiding in the processes that promote healing of a tissue. Examples would be to prevent or decrease inflammatory reactions within a tissue by preventing or decreasing leukocyte infiltration, nitric oxide production and release by macrophages, edema, redness, pain, and/or edema, redness, pain, and/or fibrosis (scar tissue formation).
By “reversible acylation” is meant the process of adding one or more acyl groups to chitosan, where the attachment of the acyl group to chitosan is not permanent and the attached acyl group may be removed as necessary.
By “structural integrity” or “nanofibrous structure” is meant the physical properties associated with the chitosan nanofibers. In an exemplary embodiment, the chitosan nanofibers demonstrate no or minimal change in physical properties, such as fiber or particle diameter, film thickness, tensile strength, and/or elasticity, etc., when exposed to different solvents, such as hydrophilic solvents. In a preferred embodiment, the chitosan nanofibers exhibit no or minimal swelling or dissolution when exposed to a hydrophilic solvent.
By “unmodified chitosan” is meant chitosan not reacted with a modifying agent, such as a phenyl-containing carbonyl derivative.
By “unreacted chitosan nanofibers” is meant either the chitosan nanofibers not reacted with the amino protecting reagent or the as-spun chitosan nanofibers.
By “acidic solution” is meant a solution that has an acidic pH and is used to solubilize chitosan. Examples of acidic solutions include, but are not limited to, trifluoroacetic acid.
By “agent” is meant any small molecule chemical compound, antibody, nucleic acid molecule, or polypeptide, or fragments thereof.
By “ameliorate” is meant decrease, suppress, attenuate, diminish, arrest, or stabilize the development or progression of a disease.
By “analog” is meant a molecule that is not identical, but has analogous functional or structural features. For example, a polypeptide analog retains the biological activity of a corresponding naturally-occurring polypeptide, while having certain biochemical modifications that enhance the analog's function relative to a naturally occurring polypeptide. Such biochemical modifications could increase the analog's protease resistance, membrane permeability, or half-life, without altering, for example, ligand binding. An analog may include an unnatural amino acid.
By “antimicrobial” is meant an agent that inhibits or stabilizes the proliferation or survival of a microbe. In one embodiment, a bacteriostatic agent is an antimicrobial. In other embodiments, any agent that kills a microbe (e.g., bacterium, fungus, virus) is an antimicrobial.
By “anti-inflammatory” is meant the reduction in severity or symptoms of an inflammatory reaction in a tissue. An inflammatory reaction within tissue is generally characterized by leukocyte infiltration, nitric oxide production and release by macrophages, edema, redness, pain, and/or neovascularization. Inflammation can also be measured by analyzing levels of nitric oxide, inflammatory cytokines, or any other inflammatory marker.
By “anti-inflammatory agent” is meant an agent that reduces the severity or symptoms of an inflammatory reaction in a tissue. An inflammatory reaction within tissue is generally characterized by leukocyte infiltration, edema, redness, pain, and/or fibrosis. Inflammation can also be measured by analyzing levels of inflammatory cytokines or any other pro-inflammatory markers.
By “biodegradable” is meant susceptible to breakdown by biological activity. For example, biodegradable chitosan compositions are susceptible to breakdown by enzymes present in vivo (e.g., lysozyme, N-acetyl-o-glucosaminidase and lipases). Degradation of a chitosan composition of the invention need not be complete. A chitosan composition of the invention may be degraded, for example, by the cleavage of one or more chemical bonds (e.g., glycosidic bonds).
By “clinician” is meant any healthcare provider. Exemplary clinicians include, but are not limited to, doctors, veterinarians, osteopaths, physician's assistants, emergency medical technicians, medics, nurse practitioners, and nurses.
In this disclosure, “comprises,” “comprising,” “containing” and “having” and the like can have the meaning ascribed to them in U.S. Patent law and can mean “includes,” “including,” and the like; “consisting essentially of” or “consists essentially” likewise has the meaning ascribed in U.S. Patent law and the term is open-ended, allowing for the presence of more than that which is recited so long as basic or novel characteristics of that which is recited is not changed by the presence of more than that which is recited, but excludes prior art embodiments.
By “degradation rate” is meant the time required to substantially degrade the composition. A composition is substantially degraded where at least about 75%, 85%, 90%, 95% or more has been degraded. Methods for measuring degradation of chitosan are known in the art and include measuring the amount of a nanofiber membrane, fibrous material, sponge, film, composite or other composition of the invention that remains following implantation in a subject or following in vitro exposure to an enzyme having chitosan-degrading activity.
By “disease” is meant any condition or disorder that damages or interferes with the normal function of a cell, tissue, or organ. Examples of diseases include, but are not limited to, bone defects, chronic periodontitis, edentulism, traumatic injury, ulcers, arthritis, and orthopedic injuries.
By “effective amount” is meant the amount of a required to ameliorate the symptoms of a disease relative to an untreated patient. The effective amount of active compound(s) used to practice the present invention for therapeutic treatment of a disease varies depending upon the manner of administration, the age, body weight, and general health of the subject. Ultimately, the attending physician or veterinarian will decide the appropriate amount and dosage regimen. Such amount is referred to as an “effective” amount.
By “fragment” is meant a portion of a polysaccharide, protein, polypeptide, nucleic acid, or other molecule. This portion contains, preferably, at least 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, or 90% of the entire length of the reference polysaccharide, protein, polypeptide, nucleic acid, or other molecule. A fragment may contain 10, 20, 30, 40, 50, 60, 70, 80, 90, or 100, 200, 300, 400, 500, 600, 700, 800, 900, or 1000 units of the polysaccharide, protein, polypeptide, nucleic acid, or other molecule.
The terms “isolated,” “purified,” or “biologically pure” refer to material that is free to varying degrees from components which normally accompany it as found in its native state. “Isolate” denotes a degree of separation from original source or surroundings. “Purify” denotes a degree of separation that is higher than isolation. A “purified” or “biologically pure” polysaccharide, protein, polypeptide, nucleic acid, or other molecule is sufficiently free of other materials such that any impurities do not materially affect the biological properties of the polysaccharide, protein, polypeptide, nucleic acid, or other molecule or cause other adverse consequences. That is, a polysaccharide, protein, polypeptide, nucleic acid, or other molecule is purified if it is substantially free of cellular material, viral material, or culture medium when produced by recombinant techniques, or chemical precursors or other chemicals when chemically synthesized. Purity and homogeneity are typically determined using analytical chemistry techniques, for example, polyacrylamide gel electrophoresis or high performance liquid chromatography. The term “purified” can denote that a polysaccharide, protein, polypeptide, nucleic acid, or other molecule gives rise to essentially one band in an electrophoretic gel. For a polysaccharide, protein, polypeptide, nucleic acid, or other molecule that can be subjected to modifications, for example, phosphorylation or glycosylation, different modifications may give rise to different isolated polysaccharides, proteins, polypeptides, nucleic acids, or other molecules, which can be separately purified.
As used herein, “obtaining” as in “obtaining an agent” includes synthesizing, purchasing, or otherwise acquiring the agent.
By “polymer” is meant a natural or synthetic organic molecule formed by combining smaller molecules in a regular pattern.
As used herein, the terms “prevent,” “preventing,” “prevention,” “prophylactic treatment” and the like refer to reducing the probability of developing a disorder or condition in a subject, who does not have, but is at risk of or susceptible to developing a disorder or condition.
By “prosthetic device” is meant an implanted medical device that substitutes for or supplements a missing or defective part of the body.
By “reduces” is meant a negative alteration of at least 10%, 25%, 50%, 75%, or 100%.
By “reference” is meant a standard or control condition.
By “small molecule” is meant any chemical compound.
By “subject” is meant a mammal, including, but not limited to, a human or non-human mammal, such as a bovine, equine, canine, ovine, or feline.
By “trauma” is meant any injury that damages a tissue or organ of a subject. The injury need not be severe. Therefore, a trauma includes any injury that breaks the skin. As used herein, the terms “treat,” treating,” “treatment,” and the like refer to reducing or ameliorating a disorder and/or symptoms associated therewith. It will be appreciated that, although not precluded, treating a disorder or condition does not require that the disorder, condition or symptoms associated therewith be completely eliminated.
Ranges provided herein are understood to be shorthand for all of the values within the range. For example, a range of 1 to 50 is understood to include any number, combination of numbers, or sub-range from the group consisting 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, or 50.
Unless specifically stated or obvious from context, as used herein, the term “or” is understood to be inclusive. Unless specifically stated or obvious from context, as used herein, the terms “a”, “an”, and “the” are understood to be singular or plural.
Unless specifically stated or obvious from context, as used herein, the term “about” is understood as within a range of normal tolerance in the art, for example within 2 standard deviations of the mean. About can be understood as within 10%, 9%, 8%, 7%, 6%, 5%, 4%, 3%, 2%, 1%, 0.5%, 0.1%, 0.05%, or 0.01% of the stated value. Unless otherwise clear from context, all numerical values provided herein are modified by the term about.
The recitation of a listing of chemical groups in any definition of a variable herein includes definitions of that variable as any single group or combination of listed groups. The recitation of an embodiment for a variable or aspect herein includes that embodiment as any single embodiment or in combination with any other embodiments or portions thereof.
Any compositions or methods provided herein can be combined with one or more of any of the other compositions and methods provided herein.
As described below, the present invention features chitosan compositions (e.g., barrier membranes) that maintain structural integrity when exposed to hydrophilic solvents and methods of making such compositions without dissolution of the chitosan caused by hydrolysis.
The invention is based, at least in part, on the discovery that acylation of electrospun chitosan nanofibers can prevent or minimize swelling and dissolution of the nanofibers when exposed to hydrophilic solvents used to neutralize and remove immobilized salts left by the acidic electrospinning solution.
The invention is also based, at least in part, on the discovery that protection of the amino groups on electrospun chitosan nanofibers can prevent or minimize swelling and dissolution of the nanofibers when exposed to hydrophilic solvents.
Chitosan is a naturally occurring linear polysaccharide composed of N-acetyl-glucosamine-co-N-glucosamine copolymers. Chitosan is derived from chitin, a naturally occurring polymer. Chitin is a white, hard, inelastic, nitrogenous polysaccharide isolated from fungi, mollusks, or from the exoskeletons of arthropods (e.g., crustaceans, insects).
Chitosan materials have shown great potential in guided tissue regeneration (GTR), particularly guided bone regeneration (GBR), applications because of their biocompatibility, controllable degradation, non-toxic degradation properties and are osteoconductive. Chitosan supports wound healing and osteogenesis because of its similarity to extracellular matrix polysaccharides such as hyaluronan and chondroitin sulfate. Chitosan may also be easily formed into nanofibrous membranes which have the advantage of mimicking the scale and topography of extracellular matrix fibers, providing high surface area for cell attachments and pore sizes for fluid/nutrient exchange between tissue compartments but not cell/tissue infiltration.
Conventional methods of producing chitosan nanofibers are inadequate. The selection of a suitable solvent system is a prerequisite for successful electrospinning. The ideal solvents should have two properties. One is to dissolve the polymer with high polymer concentration and low solution viscosity. The other is to carry the solvated polymer molecules towards the collector, then to leave the polymer fibers by rapid vaporization of the solvent molecules. So far, suitable electrospinning solvents for chitosan are rather limited. Concentrated acetic acid and trifluoroacetic acid (TFA) are commonly used to successfully electrospin chitosan. Other solvents, such as 1,1,1,3,3,3-hexafluoro-2-propanol, have been used in the past. However, such solvents are prohibitively expensive to utilize routinely or in large scale production. The methods using concentrated acetic acid produce nanofibers with poor structure, in which beads are extensively present. The solvent system of TFA/dichloromethane (DCM) is more successful producing continuous, homogenous, bead-free nanofibers. However, the vaporization of the TFA leaves an extensive presence of salt residues immobilized on and in the body of the nanofibers.
Currently, alkaline immersion with or without chemical crosslinking of the chitosan are used to remove immobilized salt residues from chitosan nanofibers. Both approaches suffer significant drawbacks. There are many crosslinking agents for chitosan including glutaraldehyde and genipin. The principle is to crosslink the amino groups of chitosan to prevent the dissolution of chitosan caused by hydrolysis when removing the immobilized salts. However, because the amino groups are extensively occupied by TFA salts, the crosslinking is inefficient because the number of free amino groups in chitosan molecules is too few. Alkaline immersion (e.g. concentrated NaOH or saturated Na2CO3) may be used to remove the immobilized TFA salts from electrospun chitosan nanofibers since chitosan is insoluble in base, but because water preferentially hydrolyzes the chitosan molecules, swelling and loss of nanofibrous structure of the membranes remains a problem. Despite significant progress made to electrospin chitosan and to stabilize the as-spun fibers against dissolution, the methods using concentrated acetic acid produce nanofibers with poor structure, in which beads were extensively present. The present invention addresses these problems by providing chitosan nanofibers that maintain structural integrity when exposed to hydrophilic solvents and methods of making such compositions without dissolution of the chitosan caused by hydrolysis.
Chitosan is a cationic weak base that is substantially insoluble in water and organic solvents. Typically, chitosan is fairly soluble in acidic solutions, such as acetic, citric, oxalic, proprionic, ascorbic, hydrochloric, formic, and lactic acids, as well as other organic and inorganic acids.
Chitosan nanofibrous membranes may be prepared by electrospinning chitosan dissolved in an acid solution. Electrospinning protocols can be modified to produce chitosan nanofiber membranes (Schiffman and Schauer, Bio macro molecules, 2007. 8(9): p. 2665-7).
Electrospun chitosan nanofibers typically have a mean diameter of about 100-150 nm or in the range of about 40 nm to about 400 nm (e.g., 40 nm, 100 nm, 130 nm, 200 nm or 400 nm), but can vary widely depending upon a number of factors, such as rotation speed of the spinning mandrel, concentration of the chitosan, electrostatic charge of the solution, etc. Some nanofibers can be as large as 1000 nm in diameter and as small as 5 nm. Some nanofibers have a mean diameter between about 10 nm to about 500 nm. Typically, nanofibers have a mean diameter between about 30 nm to about 500 nm.
In one aspect, the chitosan nanofibers are acylated with an acylating agent, and the acylated chitosan nanofibers are washed with a hydrophilic solvent. These nanofibers typically have a mean diameter of about 150 nm or in the range of about 100 nm to about 200 nm. Typically, nanofibers have a mean diameter between about 50 nm to about 500 nm. In one embodiment, the chitosan nanofibers have a substantially uniform diameter. In another embodiment, the nanofibers have a mean diameter in the range of about 100 to about 200 nm.
In another aspect, the chitosan nanofibers are treated with N-tert-butoxycarbonyl (t-BoC), these nanofibers typically have a mean diameter of about 100 nm or in the range of about 40 nm to about 130 nm. Some nanofibers have a mean diameter between about 10 nm to about 500 nm. Typically, nanofibers have a mean diameter between about 30 nm to about 200 nm. In one embodiment, the chitosan nanofibers have a substantially uniform diameter. In another embodiment, the nanofibers have a mean diameter in the range of about 40 to about 130 nm.
The degree of deacylation of the chitosan used for producing the nanofibers can vary from about 50% to about 99%, with about 70% deacylation preferable. The molecular weight of the chitosan can also vary from less than about 100 kDa to about 900 kDa, with about 300 kDa to about 325 kDa preferable. The chitosan weight volume in solution is from about 0.25 to about 10.0% weight/volume (e.g., 0.1, 0.2, 0.25, 0.3, 0.4, 0.5, 1, 1.25, 1.5, 1.75, 2.0, 2.5, 3.0, 3.5, 4, 4.5, 5, 5.5, 6, 6.5, 7, 7.5, 8, 8.5, 9, 9.5, and 10%). In one embodiment, 5.50% weight volume of chitosan in solution is used for the electrospinning process, where a 5.50% weight volume of chitosan contains 5.50 grams of chitosan per 100 ml solution.
In one aspect, the invention includes a method of preparing chitosan nanofibers that comprises electrospinning an acidic solution comprising chitosan into chitosan nanofibers, acylating one or more of the electrospun chitosan nanofibers with an acylating agent, washing the acylated chitosan nanofibers with a hydrophilic solvent, and deacylating the acylated chitosan nanofibers.
In another embodiment, the invention includes a method of preparing chitosan nanofibers comprises electrospinning an acidic solution comprising chitosan into chitosan nanofibers, removing one or more immobilized salts on the electrospun chitosan nanofibers with an organic solvent, and exposing at least one amino group with an amino protecting reagent to stabilize the chitosan membranes.
For the electrospinning process, the chitosan is dissolved in an acidic solution. The acidic solution includes, but is not limited to, trifluoroacetic acid (TFA), acetic, citric, oxalic, proprionic, ascorbic, hydrochloric, formic, salicylic and/or lactic acids, and any combination of those. In some embodiments, the acidic solutions include other organic compounds or solvents, such as methylene chloride. In one embodiment, the acid solution comprising other organic compounds includes a 90%/10%, 80%/20% 75%/25%, 70%/30%, 60%/40%, or 50%/50% of acidic solution to other organic solvent ratio. In an exemplary embodiment, the chitosan is dissolved in a solution of 70% trifluoroacetic acid and 30% methylene chloride.
In some embodiments, the chitosan solution is loaded into a 10-mL syringe with a blunt 20 G, 3.81 cm stainless steel needle tip. The syringe is loaded into the electrospinning apparatus and the flow rate set to a speed appropriate to the desired diameter size, e.g. 20 L/min. The solution is electrospun at about 25 kV and the fibers are collected on a target (such as about 38.1 cm diameter circular disc of non-stick aluminum foil). The target is positioned about 15 cm from the needle tip and rotated at about 8.4 RPM by an AC motor to ensure even and random distribution of fibers. The electrospinning apparatus is housed inside a ventilated box, which is vented, preferably to the fume hood. After electrospinning, the nanofibrous membrane is vacuum treated for several hours, e.g. overnight, to remove residual solvent.
The acidic solution, including solvents such as trifluoroacetic acid (TFA), yields immobilized salt residues on and in the chitosan nanofibers (chitosan trifluoroacetate, which may be represented as R1—NH3+CF3COO−). Chitosan/TFA salt is made of the acid, TFA, and base, chitosan, and it readily hydrolyzes in water. The hydrolysis of chitosan/TFA produces free TFA in water and creates an acidic environment which leads to the rapid swelling and dissolution of the electrospun chitosan nanofibers. As a result, chitosan nanofibrous membranes prepared by electrospinning acidic solutions of chitosan are prone to dissolution and swelling in hydrophilic solvents, such as water.
In one embodiment, chitosan nanofiber membranes are fabricated by electrospinning. The fiber orientation may be random or directed in uniform alignment. The fiber orientation may be altered or directed through manipulation of the orientation of the collection target mandrell and/or the speed of rotation.
In another embodiment, the chitosan nanofibers have a water contact angle that is greater than about 90 degrees, 91 degrees, 92 degrees, 93 degrees, 94 degrees, 95 degrees, 96 degrees, 97 degrees, 98 degrees, 99 degrees, 100 degrees, 101 degrees, or greater, or any number in between. In another embodiment, the chitosan nanofibers have a water contact angle in the range of about 93 degrees to about 101 degrees. In yet another embodiment, the chitosan nanofibers have a water contact angle that is greater than about 93 degrees.
Structural integrity of the chitosan can be modified to accommodate the site of injury or tissue being regenerated. Variations in physical properties of polymers, such as chitosan, depend on its molecular weight, number of repeating units in the polymer-chain, and regularity of polymer-chain, side group chemistry, the degree of matrix packing or density, and crosslinking. The physical properties of chitosan can be controlled or altered during manufacture through its molecular weight, degree of deacylation, and crosslinking to affect thermal properties, such as melting point, and physical-mechanical properties, such as tensile strength, Young's modulus, swelling and degradation.
Crosslinking is the process which links polymer chains together. In chitosan, crosslinking induces a three-dimensional matrix of interconnected, linear, polymeric chains. The degree or extent of crosslinking depends on the crosslinking agent. Exemplary crosslinking agents include sodium tripolyphosphate, ethylene glycol diglycidyl ether, ethylene oxide, glutaraldehyde, epichlorohydrin, diisocyanate, and genipin. Crosslinking can also be accomplished using microwave or ultraviolet exposure.
Acylation
In some embodiments, electrospinning acidic solutions of chitosan yields immobilized salt residues on the chitosan nanofibers. However, hydrolysis of the immobilized salts left by the acidic solution and exposure of the chitosan nanofibers to neutralization solutions, e.g., hydrophilic solvents, often results in the nanofibers being prone to dissolution. The chitosan nanofibers swell and lose nanofiber structure and integrity.
The present invention includes methods for preparing chitosan nanofibers by acylating one or more of the electrospun chitosan nanofibers (e.g., a surface of the nanofiber) with an acylating agent. In one embodiment, the electrospun chitosan nanofibers are exposed to an acylating catalyst and acylating agent. The acylating catalyst includes, but is not limited to, pyridine, 4-dimethylamino-pyridine (DMAP), triethylamine, diisopropylethylamine (DIPEA), lutidine, aluminum chloride, aluminum trifluoride, triphenylphosphine, tributylphosphine, and combinations thereof. The acylating agent includes, but is not limited to, acyl chloride, symmetric or mixed acid anhydride, vinyl ester, cyanomethyl ester, S-phenyl thioester, piperidino ester, pyrid-3-yl ester, 4-nitrophenyl ester, 2,4,6-trichlorophenyl ester, 2,3,4,5,6-pentachlorophenyl ester, 2,3,4,5,6-pentafluorophenyl ester, phtalimido ester, succinimido ester, 4-oxo-3,4-dihydrobenzotriazin-3-yl ester, benzotriazolyl ester, and combinations thereof. In certain embodiments, the symmetric or mixed acid anhydride comprises a fatty acid anhydride. In other embodiments, the symmetric or mixed acid anhydride comprises butyric anhydride.
In an exemplary embodiment, one gram of the chitosan nanofibrous membrane is placed in a flask before adding 50 ml of the acylating catalyst, e.g. pyridine, and 50 ml of the acylating agent, e.g. a fatty acid anhydride such as butyric anhydride. The ratio of chitosan material to the pyridine:fatty acid anhydride solution may be adjusted as needed. The mixture is stirred by a magnetic stirrer at 20° C. The degree of acylation on the surface of the nanofibers is controlled by changing the length of the reaction time, wherein longer reaction times increase the level of acylation.
After acylation, the acylated chitosan nanofibers comprise at least one acyl group. Examples of the acyl group include, but are not limited to, formyl, acetyl, propionyl, butyryl, isobutyryl, pivaloyl, pentanoyl, hexanoyl, and benzoyl group. In one embodiment, the acylated chitosan nanofibers are more hydrophobic than unacylated chitosan nanofibers. In another embodiment, the chitosan nanofibers comprise immobilized trifluoroacetate salt residues on the surface of the nanofibers. In yet another embodiment, the immobilized trifluoroacetate salt residues are hydrolyzed when exposed to a hydrophilic solvent.
In another aspect, the invention includes a method of protecting structural integrity of electrospun chitosan nanofibers from dissolution comprising reversibly acylating the chitosan nanofibers. In one embodiment, the reversible acylation prevents or minimizes swelling of the nanofibers when exposed to the hydrophilic solvent. In another embodiment, the reversible acylation protects the nanofibers from dissolution when exposed to the hydrophilic solvent.
The free amino groups on the chitosan nanofibers are susceptible to hydrolysis or any other unwanted reaction. Protecting the free amino groups, after removing the immobilized salt left from the electrospinning solution, stabilizes the amino group and prevents hydrolysis of the chitosan nanofibers Amino protection reagents, such as di-tert-butyl dicarbonate, a widely used carbonate ester reagent, can selectively protect free amino groups. Di-tert-butyl dicarbonate reacts with amines to yield N-tert-butoxycarbonyl or N-tert-butoxycarbonyl (t-BoC) derivatives of those amines. These derivatives do not behave as amines, and this prevents certain transformations that could otherwise affect the amine functional group, such as hydrolysis. t-Boc protected groups are stable in neutral or basic conditions, but are deprotected using strong acids. The t-Boc group can later be removed from the amine using strong acids, such as trifluoroacetic acid, H2SO4 or HCl. Thus, the t-Boc group serves as an amino protective group, since it is unreactive to most bases and nucleophiles.
The methods of the invention also include removing immobilized salts left from the electrospinning solution on the chitosan nanofibers by exposing the chitosan nanofibers to an organic base in an organic solvent. Chitosan nanofibers are susceptible to loss of structural integrity when exposed to hydrophilic solutions that hydrolyze the immobilized salt residues and/or neutralize the chitosan nanofibers. In one embodiment, removing immobilized salts on the chitosan nanofibers comprises neutralizing protonated amino groups on the nanofibers. In another embodiment, removing immobilized salts on the chitosan nanofibers comprises exposing the chitosan nanofibers to an organic solvent.
In one embodiment, the electrospun chitosan nanofibers are immersed in an organic solvent, which may be itself a base or optionally comprises a base, such as triethylamine (TEA) in an acetone solution (
After removal of the TFA salts, the chitosan fibers are highly susceptible to hydrolysis due to the many —OH and, —NH2 or —NH3+ groups on the chitosan polymer chain. To prevent excessive swelling and dissolution of the chitosan fibers, the amino groups are capped with a protection group by reacting the amino group with a carbonate ester in an organic solvent, such as tetrahydrofuran (THF,
In certain embodiments, the carbonate ester reagent, such as di-tert-butyl dicarbonate, reacts selectively with one or more of the amino groups that are near surface of the chitosan nanofibers since some carbonate ester reagents may not penetrate deep into the nanofibers. As a result, the amino protected chitosan nanofibers form a seal around the chitosan nanofibers, which retains at least a fraction of unprotected amino groups. The t-BOC modified chitosan polymers are more hydrophobic and less susceptible to hydrolysis in aqueous/physiological solutions, and hence, able to retain nanofibrous structure. In one embodiment, the amino protected chitosan nanofibers are more hydrophobic than unreacted chitosan nanofibers.
The amino protected chitosan nanofibers are also less susceptible to hydrolysis when exposed to the hydrophilic solvent. Thereby, contacting the amino protected chitosan nanofibers with a hydrophilic solvent prevents or minimizes swelling of the chitosan nanofibers. The amine protection reaction can also protect the chitosan nanofibers from dissolution when exposed to a hydrophilic solvent.
The methods of the invention also include washing the acylated chitosan nanofibers with a hydrophilic solvent. Acylated chitosan nanofibers that have undergone protection with acylation are not susceptible to loss of structural integrity when exposed to solutions that hydrolyze immobilized salt residues or neutralize the chitosan nanofibers. In one embodiment, washing the acylated chitosan nanofibers comprises hydrolyzing the immobilized salt residues from the chitosan nanofibers.
In an exemplary embodiment, the acylated chitosan nanofibers are isolated from the acylation reaction mixture and dialyzed in distilled water to remove the immobilized salt residues. Other washing methods, such as Soxhlet extraction or Kumagawa extraction in methanol, may also be used to remove immobilized acid salts and/or other contaminants. After hydrolysis of the immobilized salts, the chitosan nanofibers may be dried, such as through lyophilization, air drying or other convenient methods. In one embodiment, the acylated chitosan nanofibers are dried.
The methods included in the invention also include deacylating the acylated chitosan nanofibers. In one embodiment, the acylated chitosan nanofibers are exposed to a deacylating agent. Examples of the deacylating agent include, but are not limited to, a basic solution such as potassium hydroxide, lithium hydroxide, sodium hydroxide, rubidium hydroxide, cesium hydroxide, calcium hydroxide, strontium hydroxide, barium hydroxide, other basic solutions (such as sodium or potassium carbonate), and combinations thereof.
In an exemplary embodiment, one gram of acylated chitosan nanofibers are exposed to 100 ml of a basic solution, such as 5% potassium hydroxide, lithium hydroxide, sodium hydroxide, rubidium hydroxide, cesium hydroxide, calcium hydroxide, strontium hydroxide, barium hydroxide or other basic solutions (such as sodium or potassium carbonate). The ratio of acylated chitosan to base may be adjusted as needed (mol(base):mol(glycosamine unit of chitosan)>10). The mixture is stirred by a magnetic stirrer at 60° C. The degree of deacylation to remove the acyl groups, such as fatty acyl groups, attached to the nanofiber may be controlled by changing the length of the reaction time, wherein longer reaction times increase the level of deacylation. The deacylated chitosan nanofibrous membrane is dialyzed in distilled water to remove excess basic solution. The chitosan nanofibers may be dried, such as through lyophilization, air drying or other convenient methods.
The present invention includes membranes or compositions that comprise electrospun chitosan nanofibers. The membranes or compositions of the invention are useful as dressings, barrier membranes, adhesion, three-dimensional scaffolds, etc. Barrier membranes are used to direct the growth of new tissue (
In one aspect, the barrier membrane comprises electrospun chitosan nanofibers that are reversibly acylated to retain nanofiber structure and integrity when the barrier membrane is exposed to a hydrophilic solvent. When the chitosan nanofibers are electrospun in a solution, such as an acidic solution comprising trifluoroacetic acid, the acidic solution can form salts that become immobilized to the surface of and within the chitosan nanofibers. Exposure to the hydrophilic solvent hydrolyzes the immobilized salt residues, such as trifluoroacetate from the chitosan polymer. The reversible acylation is beneficial by preventing or minimizing swelling of the nanofibers, protecting the nanofibers from dissolution, and protects the nanofibers from loss of nanofiber structure when exposed to the hydrophilic solvent.
Another aspect of the invention includes a membrane comprising electrospun chitosan nanofibers that are reversibly acylated with at least one acyl group. The acyl groups may include formyl, acetyl, propionyl, butyryl, isobutyryl, pivaloyl, pentanoyl, hexanoyl, and benzoyl groups.
In yet another aspect, the barrier membrane comprises electrospun chitosan nanofibers comprising amino protecting groups, such as tert-butoxycarbonyl groups, that retain nanofiber structure and integrity when the bather membrane is exposed to a hydrophilic solvent. When the chitosan nanofibers are electrospun in a solution, such as an acidic solution comprising trifluoroacetic acid, the acidic solution can form salts that become immobilized to the surface of and within the chitosan nanofibers. Exposure to the hydrophilic solvent hydrolyzes the immobilized salt residues, such as trifluoroacetate from the chitosan polymer. The protection of at least a portion of the amino groups on the chitosan nanofibers is beneficial by preventing or minimizing swelling of the nanofibers, protecting the nanofibers from dissolution, and protects the nanofibers from loss of nanofiber structure when exposed to the hydrophilic solvent. In one embodiment, the amino protected chitosan nanofibers are on an exterior surface of the barrier membrane. When the amino protected chitosan nanofibers are on the exterior surface, the protected nanofibers create a hydrophobic barrier for the barrier membrane against hydrophilic solvents.
The membranes or compositions comprising chitosan nanofibers can be delivered by any method known to the skilled artisan. In one aspect, the chitosan nanofiber membrane or composition is delivered to a target site to promote or direct healing of a tissue at the target site. In another aspect, the chitosan nanofiber membrane or composition is delivered to a target site to promote or direct the formation of tissues at the target site. In one embodiment, the membrane or composition comprises electrospun chitosan nanofibers. In another embodiment, the membrane is a barrier membrane. The tissue at the target site includes epithelial, dental, craniofacial, connective (such as cartilage) and bone tissue. In another embodiment, the subject is suffering from a disease or disorder selected from chronic periodontitis, edentulism, and bone regeneration. In an exemplary embodiment, the bather membrane of the present invention is implanted for guided bone regeneration.
In some embodiment, the membrane includes electrospun chitosan nanofibers and one or more natural or synthetic materials that include, but are not limited to, collagen, fibrin, elastin, laminin, fibronectin, hyaluronic acid, chondroitin 4-sulfate, chondroitin 6-sulfate, dermatan sulfate, heparin sulfate, heparin, and keratan sulfate, proteoglycans, poly(lactic acid) polymers, poly(glycolic acid) polymers, poly(lactide-co-glycolides) (PLGA), poly(urethanes), poly(siloxanes) or silicones, poly(ethylene), poly(vinyl pyrrolidone), poly(2-hydroxy ethyl methacrylate), poly(N-vinyl pyrrolidone), poly(methyl methacrylate), poly(vinyl alcohol) (PVA), poly(acrylic acid), polyvinyl acetate), polyacrylamide, poly(ethylene-co-vinyl acetate), poly(ethylene glycol), poly(methacrylic acid), polylactic acid (PLA), polyglycolic acids (PGA), nylons, polyamides, polyanhydrides, poly(ethylene-co-vinyl alcohol) (EVOH), polycaprolactone, polyvinyl acetate), polyvinylhydroxide, poly(ethylene oxide) (PEO), and polyorthoesters or a co-polymer formed from at least two members of the group, and any combination thereof.
In some embodiments, the membrane includes at least one agent, such as a therapeutic agent or biological agent. The agent includes, but is not limited to, nucleic acids, antibiotic, anti-inflammatory agent, growth factor, cytokine, enzyme, protein, peptides, amino acids, carbohydrate, lipid, hormone, the like, and any combination thereof. The agent can be incorporated into the membrane during the electrospinning process. For example, the agent can be included in the electrospinning solution. This would allow the agent to be incorporated around and/or in the nanofibers. The agent can also be added to the nanofiber after the electrospinning process. The agent can be absorbed to the nanofibers, such as by exposing the nanofibers to a solution of the agent. The agent can also be immobilized to the nanofibers. The immobilized agent can be bound directly or indirectly to the nanofiber, such as through a covalent bond, a linker, and/or ionic bond. In one embodiment, the nanofibers comprise at least one of a natural material, a synthetic material, and an agent.
As described below, the present invention also features modified chitosan materials with anti-inflammatory and pro-healing properties and methods of making such modified chitosan materials. The invention is based, at least in part, on the discovery that modification of the amino group on chitosan to create an imine bond imparts anti-inflammatory and pro-healing properties to the chitosan material.
Chitosan is a biopolymer composed of N-glucosamine and N-acetyl-glucosamine units. Chitosan is derived from chitin, a naturally occurring polymer. Chitin is a white, hard, inelastic, nitrogenous polysaccharide isolated from fungi, mollusks, or from the exoskeletons of arthropods (e.g., crustaceans, insects). Chitosan is a biodegradable and biocompatible polymer that has much potential and been widely investigated for applications in wound healing, tissue engineering/regenerative medicine, drug delivery and implant applications.
Conventional methods to produce chitosan materials that effectively provide anti-inflammatory and pro-healing properties are inadequate. Chitosan is a cationic weak base that is substantially insoluble in water and organic solvents. Typically, chitosan is fairly soluble in acidic solutions, such as acetic, citric, oxalic, proprionic, ascorbic, hydrochloric, formic, and lactic acids, as well as other organic and inorganic acids. Solubility of chitosan in acidic solutions makes production of chitosan products rather limited. Chitosan is more readily solubilized in low pH solutions, such as concentrated acetic acid and trifluoroacetic acid (TFA). Other solvents, such as 1,1,1,3,3,3-hexafluoro-2-propanol, have also been used in the past. However, such solvents are prohibitively expensive to utilize routinely or in large scale production.
Because chitosan has free amino groups, they may be reacted with other functional groups to produce modified chitosan materials with different properties. Phenyl-containing carbonyl derivatives, such as raspberry ketones, can react with the free amino groups on chitosan to convert the amino group into an imine bond. Raspberry ketone, in particular, is an exemplary embodiment. a natural phenolic compound found in a variety of fruits including raspberries, cranberries and blackberries and is currently used as an additive in foods and cosmetics. Phenyl-containing carbonyl derivatives, such as raspberry ketone, have been shown to modulate the activation of macrophages in cell culture and to reduce effects of stimuli that may lead to chronic inflammation.
The formation of an imine bond on the chitosan molecule maintains many of the advantages of the native chitosan, but includes the ability of the modified chitosan to support/promote the M2 macrophage phenotype for promoting tissue healing/regeneration. For example, promoting healing would have a significant benefit to regenerating bone, cartilage, and nerve tissues for which chitosan materials are broadly investigated. Reducing inflammation around micro- and nano-particles would be important to local drug delivery strategies (e.g. antibiotics, anticancer drugs, etc) by avoiding confounding factors often associated with chronic inflammation that may impede local release rates.
In one aspect, the invention includes a modified chitosan comprising an iminyl group. The iminyl group can have a general structure as shown in Structure I:
wherein R can be selected from the group consisting of H, C1-C6 alkyl, C1-C6 alkoxy, phenyl, and any combination thereof. The iminyl group can also be derived from a phenyl-containing carbonyl derivative. The phenyl-containing carbonyl derivative can include a molecule having a general formula of Structure I:
wherein R1 and R2 are each independently selected from H, C1-C6 alkyl, and C1-C6 alkoxy, and n is an integer selected from 1, 2, 3, 4, 5, and 6. In one embodiment, the phenyl-containing carbonyl derivative is a raspberry ketone. The raspberry ketone or 4-(4-hydroxyphenyl)butan-2-one has the general formula of Structure III:
In another embodiment, the modified chitosan increases anti-inflammatory properties as compared to unmodified chitosan. Examples of increasing anti-inflammatory properties includes, but is not limited to, decreasing or preventing or inhibiting leukocyte infiltration, nitric oxide production and release by macrophages, edema, redness, pain, and/or neovascularization. The modified chitosan can increase pro-healing properties of the modified chitosan as compared to unmodified chitosan. In another embodiment, the modified chitosan decreases levels of nitric oxide and/or decreases or inhibits macrophage production of nitric oxide.
The invention includes methods for modifying chitosan. In one embodiment, a solution of 2% chitosan by weight (˜87% degree of deacetylation) in 2% acetic solution, creating approximately a 0.8:2 ratio, is stirred overnight at 56° C. Oxygen gas is purged from the acidic chitosan solution using nitrogen gas. A phenyl-containing carbonyl derivative, such as a raspberry ketone, is added to the solution and the mixture continues to be oxygen purged. Heat is applied, in the range of about 45° C. to about 90° C., to accelerate the reaction between the chitosan and the phenyl-containing carbonyl derivative. The reaction time may be controlled to control both the degree of modification of the chitosan by the raspberry ketone compound and the water contact angle (hydrophobicity) of the modified chitosan.
In one aspect, a method for modifying chitosan comprises obtaining an oxygen depleted acidic solution comprising chitosan, mixing the oxygen depleted chitosan solution with a phenyl-containing carbonyl derivative, and reacting the phenyl-containing carbonyl derivative with at least one free amino group on the chitosan to create an imine bond that modifies the chitosan. In one embodiment, the acidic solution comprises acetic acid. In another embodiment, obtaining the oxygen depleted chitosan solution comprises removing O2 gas and replacing the O2 gas with N2 gas. In another embodiment, mixing the oxygen depleted chitosan solution with the phenyl-containing carbonyl derivative comprises heating the mixture. In yet another embodiment, the phenyl-containing carbonyl derivative is a raspberry ketone.
The invention also includes chitosan microspheres and the method of making chitosan microspheres. One aspect of the invention includes a chitosan microsphere comprising chitosan modified with an iminyl group. Another aspect includes a chitosan microsphere comprising the modified chitosan made by any method described herein.
The chitosan microspheres are generally spherical shells or beads comprising chitosan having a small diameter, in the range of about 50 nm to about 500 μm. One embodiment includes the microsphere having a diameter in the range of about 1 μm to about 500 μm. The diameter includes at least about 50 nm, 100 nm, 150 nm, 200 nm, 250 nm, 300 nm, 350 nm, 400 nm, 500 nm, 600 nm, 700 nm, 800 nm, 900 nm, 1 μm, 5 μm, 10 μm, 15 μm, 16 μm, 17 μm, 18 μm, 19 μm, 20 μm, 21 μm, 22 μm, 23 μm, 24 μm, 25 μm, 26 μm, 27 μm, 28 μm, 29 μm, 30 μm, 31 μm, 32 μm, 33 μm, 34 μm, 35 μm, 36 μm, 37 μm, 38 μm, 39 μm, 40 μm, 41 μm, 42 μm, 43 μm, 44 μm, 45 μm, 46 μm, 47 μm, 48 μm, 49 μm, 50 μm, 51 μm, 52 μm, 53 μm, 54 μm, 55 μm, 56 μm, 57 μm, 58 μm, 59 μm, 60 μm, 61 μm, 62 μm, 63 μm, 64 μm, 65 μm, 66 μm, 67 μm, 68 μm, 69 μm, 70 μm, 71 μm, 72 μm, 73 μm, 74 μm, 75 μm, 76 μm, 77 μm, 78 μm, 79 μm, 80 μm, 81 μm, 82 μm, 83 μm, 84 μm, 85 μm, 86 μm, 87 μm, 88 μm, 89 μm, 90 μm, 91 μm, 92 μm, 93 μm, 94 μm, 95 μm, 96 μm, 97 μm, 98 μm, 99 μm, 100 μm, 150 μm, 200 μm, 250 μm, 300 μm, 350 μm, 400 μm, 450 μm, 500 μm, and any diameter in between.
Another embodiment, the modification increases anti-inflammatory properties of the modified chitosan as compared to unmodified chitosan. In yet another embodiment, the modification increases pro-healing properties of the modified chitosan as compared to unmodified chitosan. In still another embodiment, the modification decreases macrophage production of nitric oxide.
Microspheres are particularly useful for delayed or time release delivery of one or more agents to a target site. In one embodiment, the microsphere further comprises an agent. The microsphere can be hollow and filled with an agent (such as a drug or antibody) that is released upon degradation of the chitosan shell or the microsphere can incorporate the agent into the microsphere with the chitosan molecules and the agent is released as the chitosan degrades. In one embodiment, the microsphere forms a biodegradable shell around the agent or the agent is incorporated into the microsphere.
Another aspect of the invention includes method of producing microspheres of chitosan. The method includes modifying at least one free amino group on the chitosan with an iminyl group and crosslinking the modified chitosan to form chitosan microspheres. In one embodiment, the modified chitosan is crosslinked by exposure to a crosslinking agent, such as glutaraldehyde or genipin.
The method can also include modifying the chitosan by obtaining an oxygen depleted acidic solution comprising chitosan, mixing the oxygen depleted chitosan solution with a phenyl-containing carbonyl derivative, and reacting the phenyl-containing carbonyl derivative with at least one free amino group on the chitosan to create an imine bond that modifies the chitosan.
The modified chitosan can also be electrospin by methods known in the art to produce chitosan nanofibers (Schiffman and Schauer, Bio macro molecules, 2007. 8(9): p. 2665-7). These nanofibers typically have a mean diameter of about 100 nm or in the range of about 40 nm to about 130 nm, but the diameter of the chitosan nanofibers can vary widely depending upon a number of factors, such as rotation speed of the spinning mandrel, concentration of the chitosan, electrostatic charge of the solution, etc. Some nanofibers can be as large as 1000 nm in diameter and as small as 5 nm. Some nanofibers have a mean diameter between about 10 nm to about 500 nm. Typically, nanofibers have a mean diameter between about 30 nm to about 200 nm. In one embodiment, the chitosan nanofibers have a substantially uniform diameter. In another embodiment, the nanofibers have a mean diameter in the range of about 40 to about 130 nm.
The degree of deacylation of the chitosan used for producing the nanofibers can vary from about 50% to about 99%, with about 70% deacylation preferable. The molecular weight of the chitosan can also vary from less than about 100 kDa to about 900 kDa, with about 300 kDa to about 325 kDa preferable. The chitosan weight volume in solution is from about 0.25 to about 10.0% weight/volume (e.g., 0.1, 0.2, 0.25, 0.3, 0.4, 0.5, 1, 1.25, 1.5, 1.75, 2.0, 2.5, 3.0, 3.5, 4, 4.5, 5, 5.5, 6, 6.5, 7, 7.5, 8, 8.5, 9, 9.5, and 10%). In one embodiment, 5.50% weight volume of chitosan in solution is used for the electrospinning process, where a 5.50% weight volume of chitosan contains 5.50 grams of chitosan per 100 ml solution.
In one aspect, the invention includes a method of preparing modified chitosan nanofibers comprises electrospinning an acidic solution comprising modified chitosan into chitosan nanofibers. After the modification of the chitosan, the modified chitosan is dissolved in an acidic solution. The acidic solution includes, but is not limited to, trifluoroacetic acid (TFA), acetic, citric, oxalic, proprionic, ascorbic, hydrochloric, formic, salicylic and/or lactic acids, and any combination of those. In some embodiments, the acidic solutions include other organic compounds or solvents, such as methylene chloride. In one embodiment, the acid solution comprising other organic compounds includes a 90%/10%, 80%/20% 75%/25%, 70%/30%, 60%/40%, or 50%/50% of acidic solution to other organic solvent ratio. In an exemplary embodiment, the chitosan is dissolved in a solution of 70% trifluoroacetic acid and 30% methylene chloride.
In some embodiments, the modified chitosan is loaded into a 10-mL syringe with a blunt 20 G, 3.81 cm stainless steel needle tip. The syringe is loaded into the electrospinning apparatus and the flow rate set to a speed appropriate to the desired diameter size, e.g. 20 L/min. The solution is electrospun at about 25 kV and the fibers are collected on a target (such as about 38.1 cm diameter circular disc of non-stick aluminum foil). The target is positioned about 15 cm from the needle tip and rotated at about 8.4 RPM by an AC motor to ensure even and random distribution of fibers. The electrospinning apparatus is housed inside a ventilated box, which is vented, preferably to the fume hood. After electrospinning, the nanofibrous membrane is vacuum treated for several hours, e.g. overnight, to remove residual solvent.
In one embodiment, modified chitosan nanofiber membranes are fabricated by electrospinning. The fiber orientation may be random or directed in uniform alignment. The fiber orientation may be altered or directed through manipulation of the orientation of the collection target mandrell and/or the speed of rotation.
In another embodiment, the modified chitosan nanofibers have a water contact angle that is greater than about 90 degrees, 91 degrees, 92 degrees, 93 degrees, 94 degrees, 95 degrees, 96 degrees, 97 degrees, 98 degrees, 99 degrees, 100 degrees, 101 degrees, or greater, or any number in between. In another embodiment, the modified chitosan nanofibers have a water contact angle in the range of about 93 degrees to about 101 degrees. In yet another embodiment, the modified chitosan nanofibers have a water contact angle that is greater than about 93 degrees.
Structural integrity of the modified chitosan can be altered to accommodate the proposed use of the chitosan. Variations in physical properties of polymers, such as modified chitosan, depend on its molecular weight, number of repeating units in the polymer-chain, and regularity of polymer-chain, side group chemistry, the degree of matrix packing or density, and crosslinking. The physical properties of modified chitosan can be controlled or altered during manufacture through its molecular weight, degree of deacylation, and crosslinking to affect thermal properties, such as melting point, and physical-mechanical properties, such as tensile strength, Young's modulus, swelling and degradation.
Crosslinking is the process which links polymer chains together. Crosslinking induces a three-dimensional matrix of interconnected, linear, polymeric chains. The degree or extent of crosslinking depends on the crosslinking agent. Exemplary crosslinking agents include sodium tripolyphosphate, ethylene glycol diglycidyl ether, ethylene oxide, glutaraldehyde, epichlorohydrin, diisocyanate, and genipin. Crosslinking can also be accomplished using microwave or ultraviolet exposure.
The microspheres or membranes comprising the modified chitosan nanofibers can be delivered by any method known to the skilled artisan. In one aspect, the microspheres comprising modified chitosan are delivered to a target site to prevent inflammation or promote healing of tissue at the target site. In another aspect, the chitosan nanofiber membrane or composition is delivered to a target site to decrease nitric oxide levels at the target site. The methods comprise contacting the site with modified chitosan, wherein the modified chitosan is produced according to any of the methods described herein. In one embodiment, modified chitosan is in the form of microspheres.
In some embodiment, the membrane includes microspheres comprise modified chitosan and one or more natural or synthetic materials that include, but are not limited to, collagen, fibrin, elastin, laminin, fibronectin, hyaluronic acid, chondroitin 4-sulfate, chondroitin 6-sulfate, dermatan sulfate, heparin sulfate, heparin, and keratan sulfate, proteoglycans, poly(lactic acid) polymers, poly(glycolic acid) polymers, poly(lactide-co-glycolides) (PLGA), poly(urethanes), poly(siloxanes) or silicones, poly(ethylene), poly(vinyl pyrrolidone), poly(2-hydroxy ethyl methacrylate), poly(N-vinyl pyrrolidone), poly(methyl methacrylate), poly(vinyl alcohol) (PVA), poly(acrylic acid), polyvinyl acetate), polyacrylamide, poly(ethylene-co-vinyl acetate), poly(ethylene glycol), poly(methacrylic acid), polylactic acid (PLA), polyglycolic acids (PGA), nylons, polyamides, polyanhydrides, poly(ethylene-co-vinyl alcohol) (EVOH), polycaprolactone, polyvinyl acetate), polyvinylhydroxide, poly(ethylene oxide) (PEO), and polyorthoesters or a co-polymer formed from at least two members of the group, and any combination thereof.
In some embodiments, the microspheres include at least one agent, such as a therapeutic agent or biological agent. The agent includes, but is not limited to, nucleic acids, antibiotic, anti-inflammatory agent, growth factor, cytokine, enzyme, protein, peptides, amino acids, carbohydrate, lipid, hormone, the like, and any combination thereof. The agent can be encapsulated by the microsphere or incorporated into the microsphere. For example, the agent can be included in the chitosan solution during the production of the microsphere. This would allow the agent to be incorporated around and/or in the microsphere. The agent can be absorbed to the chitosan fibers, such as by exposing the modified chitosan to a solution of the agent. The agent can also be immobilized to the modified chitosan before the production of the microsphere. The immobilized agent can be bound directly or indirectly to the modified chitosan molecule, such as through a covalent bond, a linker, and/or ionic bond. In one embodiment, the microsphere further comprises at least one of a natural material, a synthetic material, and an agent.
The invention includes kits with reagents for preparing chitosan nanofibers or other modified chitosan materials. In one aspect, the kit includes chitosan nanofibers, acylating catalyst, acylating agent, and hydrophilic solvent. In another aspect, the kit includes a membrane comprising chitosan nanofibers, acylating catalyst, acylating agent, and hydrophilic solvent. In yet another aspect, the kit includes a membrane comprising electrospun chitosan nanofibers comprising acyl groups, and hydrophilic solvent. In one embodiment, the kit further includes a deacylating agent. In another embodiment, the kit further includes at least one of a natural material, a synthetic material, and an agent.
In another aspect, the kit includes chitosan nanofibers, carbonate ester reagent, and organic solvent. In one example, the kit includes a membrane comprising chitosan nanofibers, carbonate ester reagent, such as di-tert-butyl dicarbonate, and organic solvent. In another example, the kit includes a membrane comprising electrospun chitosan nanofibers comprising N-tert-butoxycarbonyl groups. In one embodiment, the kit further includes a hydrophilic solvent.
If desired the chitosan nanofibers and barrier membranes of the invention are provided with instructions for use in a prophylactic or therapeutic method described herein. The instructions will generally include information about the use of the composition in guided tissue regeneration in a subject in need thereof. The instructions may be printed directly on the container (when present), or as a label applied to the container, or as a separate sheet, pamphlet, card, or folder supplied in or with the container.
In another aspect, the kit includes chitosan and a phenyl-containing carbonyl derivative. In one embodiment, the phenyl-containing carbonyl derivative is a raspberry ketone. In another embodiment, the kit further comprises a crosslinking agent. In another aspect, the kit includes reagents for preparing chitosan products with modified chitosan materials. In one embodiment, the kit includes chitosan comprising an iminyl group modification and an acidic solution.
If desired the kit of the invention provides instructions for incorporating the modified chitosan materials in a film, a gel, a membrane, microfibers, nanofibers, and/or nano- or micro-particles/spheres as described herein. The instructions will generally include information about the use of the modified chitosan in therapeutic procedures, such as guided tissue regeneration or agent delivery, in a subject in need thereof. The instructions may be printed directly on the container (when present), or as a label applied to the container, or as a separate sheet, pamphlet, card, or folder supplied in or with the container.
The practice of the present invention employs, unless otherwise indicated, conventional techniques of molecular biology (including recombinant techniques), microbiology, cell biology, biochemistry and immunology, which are well within the purview of the skilled artisan. Such techniques are explained fully in the literature, such as, “Molecular Cloning: A Laboratory Manual”, second edition (Sambrook, 1989); “Oligonucleotide Synthesis” (Gait, 1984); “Animal Cell Culture” (Freshney, 1987); “Methods in Enzymology” “Handbook of Experimental Immunology” (Weir, 1996); “Gene Transfer Vectors for Mammalian Cells” (Miller and Calos, 1987); “Current Protocols in Molecular Biology” (Ausubel, 1987); “PCR: The Polymerase Chain Reaction”, (Mullis, 1994); “Current Protocols in Immunology” (Coligan, 1991). These techniques are applicable to the production of the polynucleotides and polypeptides of the invention, and, as such, may be considered in making and practicing the invention. Particularly useful techniques for particular embodiments will be discussed in the sections that follow.
The following examples are put forth so as to provide those of ordinary skill in the art with a complete disclosure and description of how to make and use the assay, screening, and therapeutic methods of the invention, and are not intended to limit the scope of what the inventors regard as their invention.
The first section shows the interior structure of the electrospun chitosan nanofibers immediately after electrospinning A large amount of dots, which represent the extensive presence of highly hydrophilic trifluoroacetate salt residues in the body of the electrospun chitosan nanofibers, were present inside the circular disk.
The second section shows the protection of electrospun chitosan nanofibers through acylation. The exterior of the circular disk is protected after the acylation reaction, which represents the exterior region of electrospun chitosan nanofibers become hydrophobic. The hydrophobicity is attributed from the grafted acyl groups.
The third section shows the depuration process or hydrolysis of the trifluoroacetate salt residues. The dots are released from the circular disk while the integrity of the disk circle is maintained. Through the protection of the acyl group, the immobilized trifluoroacetate salt residues are able to be released while the fiber structure is not damaged.
The last cartoon shows the deprotection process or deacylation of the electrospun chitosan nanofibers. The exterior of the circular disk has recovered back to its original state, which indicates the acyl groups have been removed from the chitosan nanofibers.
The Fourier transform infrared spectroscopy (FTIR) spectra of pristine chitosan powder, as-spun electrospun chitosan nanofibers, acylated electrospun chitosan nanofibers, and deacylated electrospun chitosan nanofibers were shown in
During the deacylation reaction, the DS value dropped rapidly in the first ten minutes and slowed until deacylation was completed at approximately 180 minutes. The reaction kinetics in the described chitosan system were similar to reaction kinetics of other nanomaterials with a high surface to volume ratio. These results indicated that a small gain in mass occurred due to the acyl modification and that the reaction was reversible.
The surface chemistry of the membranes was characterized by x-ray photoelectron spectroscopy (XPS).
In contrast, the N 1s spectrum of as-spun electrospun chitosan nanofibers (
Three peaks were present in the C 1s spectrum of chitosan: hydrocarbon at 284.6 eV, a peak at 286.2 eV assigned to both C—OH and C—O—R, and the peak at 287.9 eV assigned to both C═O of the amide and O—C—O of the anomeric carbon of chitosan's sugar residues. Compared with chitosan, two new peaks appeared in the C 1s spectrum of fluorocarbon (291.9 eV) and C═O of TFA (288.5 eV) and a new peak appeared in the C 1s spectrum of C═O of acyl groups (288.3 eV).
The structural integrity of electrospun chitosan nanofibers in water was characterized by electron microscopy.
Although pristine chitosan powder is insoluble in pure water, the as-spun electrospun chitosan nanofibers dissolve quickly in water. When a membrane of as-spun electrospun chitosan nanofibers was placed in a water-containing petri dish, it swelled rapidly and subsequently dissolved. The color of the membrane also changed from pale white to semi-transparent in the process. As suggested by the FTIR and XPS data and findings by other groups, electrospun chitosan nanofibers become water-soluble due to the change in the structure of the chitosan molecules after the electrospinning step. Ionic bonds (CF3COO− NH3+) were formed between the amino groups of the chitosan nanofibers and carboxyl groups of trifluoroacetic acid (TFA).
The TFA salt residues on the chitosan nanofibers cannot be eliminated by a simple physical process, like heating or washing in organic solvents, due to the stable nature of the ionic bonds. Alkaline neutralization is an indispensable treatment step in breaking the ionic bonds between the chitosan and the trifluoroacetate thereby releasing the TFA salt residues. However, the chitosan nanofiber salts undergo a hydrolysis process that partially releases the acid. As a weak-base, the chitosan is less competitive and the hydrolyzed acid is neutralized by the strong base. This process repeats until the acid residue is completely removed. While the alkaline treatment is effective in chemical restoration of chitosan from its salt form, it considerably damages the structure integrity of the treated chitosan materials, especially nanostructured materials.
Currently, no explanation is available to account for the deterioration of the nanofibrous structure during the alkaline neutralization process. One hypothesis is that there is a lag between the neutralization step and the hydrolysis step. When the as-spun electrospun chitosan nanofibers are in contact with water in the alkaline solution, the hydrolysis of the chitosan/TFA salt proceeded more rapidly than neutralization because TFA is a strong acid. The hydrolyzed TFA then created an acidic environment around the nanofibers. Since the neutralization reaction takes time for base to completely neutralize the acidic environment, a large amount of chitosan molecules were hydrolyzed and released in the acidic environment before being neutralized. This lag results in the enlargement of the fiber thickness due to the release of chitosan molecules into the adjacent spaces of the nanofibers.
When the water insoluble acylated electrospun chitosan nanofibers were washed in water, the TFA residues were released from the fibers and chitosan molecules were kept intact due to the hydrophobic character of the acylated electrospun chitosan nanofibers. The clearance of the TFA salt residues was evident in the FTIR, EDS and XPS evidences.
To further explore the potential of the electrospun chitosan nanofibers in tissue engineering applications, osteoblast proliferation on the membrane of electrospun chitosan nanofibers was examined by Celltiter Glo Assay Kit. As shown in
The cell morphology on the materials was visualized with fluorescence microscope after osteoblast cells were cultured on the top of the materials for 5 days. The cells grown on the electrospun chitosan nanofibers showed characteristic shapes associated with osteoblast cells, such as elongated/stretched shape, suggesting the material did not interfere with the growth of the osteoblasts.
These surprising results suggested that the problems with dissolution and swelling observed with electrospun chitosan fiber membranes can be solved by the reversible acylation method. The mechanisms behind the process were elucidated based on the data obtained from the FTIR, XPS and SEM analyses. The acylation method could potentially be used to synthesize other modified chitoan nanofibrous material containg acyl moieties as well.
There has been a growing interest in the fabrication of nanofibers derived from natural polymers due to their ability to mimic the structure and function of extracellular matrix. Electrospinning is a simple technique to obtain nano-micro fibers with customized fiber topology and composition. The chitosan electrospun nanofibers (CSEF) have recently been extensively studied due to the favorable properties of chitosan such as controllable biodegradation, good biocompatibility, high mechanical strength, lack of toxicity, promotion of cell proliferation; porosity (e.g., nanoscale); and large surface area. Currently, chitosan can be electrospun from a solution of chitosan dissolved in either trifluoroacetic acid (TFA) or acetic acid (HAc). However, processes to remove residual acid and acid salts from the electrospun material generally result in a swelling of fibers and deterioration of the nano-fibrous structure. Crosslinking in combination with neutralization methods also have not been effective at preventing loss of nano-fibrous structure. Surface acylation of cellulose nanowhiskers has been reported to increase hydrophobicity but has not been attempted in chitosan nanofibers. Surface acylation renders CSEF insoluble in water and enables the removal of residual acid from the electrospinning process while maintaining nano-fibrous structure and without causing cytotoxicity. This study aimed to evaluate acylation of CSEF and to characterize the aqueous stability and cytocompatibility of the acylated CSEF.
Untreated CSEF swelled and dissolved in PBS. When CSEF membranes were acetylated without pyridine catalyst, only membranes at the 90° C. were stable in PBS, whereas in reactions with pyridine catalyst, even membranes acetylated at room temperature (20° C.) were stable in PBS. SEM evaluation (
Osteoblast cells on acylated CSEF were viable and had low proportion of non-viable cells, as shown by live/dead staining (
Chitosan is an extensively studied natural polymer that has been used in tissue engineering and drug delivery applications. Electrospinning provides a new platform to fabricate fibrous biomaterials in a bottom-up approach. CSEF suffers from aqueous instability. Crosslinking by glutaraldehyde has been reported, but its toxicity raises a serious concern. Na2CO3 and NH3OH neutralization have been reported, but the fibers deform greatly after neutralization. This study presents a novel method without introducing harmful chemicals into the material to remove bound salts and retain desirable nanofibrous structure of CSEF. As the acyl moiety is chemically inactive and not likely to cause toxicity, extensive cellular proliferation was present in SAOS-2 cells cultured on acylated chitosan nanofibers.
This study identified surface acylation as an effective strategy to stabilize CSEF. The acylated CSEF were cytocompatible suggesting further investigation for tissue engineering.
An animal study was conducted to evaluate the biocompatibility, biodegradation and soft tissue excluding properties of a butyric anhydride modified electrospun chitosan nanofibrous membrane. The study used a critical size (8-mm) rat calvarial bone defect model. In the rat cranium, the established critical size defect was a circular defect of 8 mm in diameter. Repeated and current studies continued to show that defects of this size in rats failed to heal and fill primarily with fibrous tissue and only minimal bone growth at the edges over a 3-month period. The advantages of this model are; a) the calvarial bone is a plate which is large enough to allow creation of a circular defect that enables convenient radiographic and histological analysis, b) the calvarial bone has a large enough size for easy surgical procedures and specimen handling, c) no fixation is required, and dl the model is well studied and reproducible which enables comparison of variety of implant materials.
The animals were x-rayed at 2, 3, 9 and 12 weeks post implantation. One animal was euthanized by CO2 inhalation at 3-weeks post-implantation and the other animal at 12-weeks post-implantation. The craniotomy sites with implants were excised and fixed in formalin for histological evaluation.
X-rays were taken in the lateral view since this enabled easy viewing of the defect in the thin rat calvarial bone. The membrane was transparent in the x-ray. At two weeks, the calvarial defect was still seen as evidenced by the radiolucent area, indicating little to no bone formation (
Gross Histology of the implant retrieved from animal at the 12 week time point showed no gross inflammation and a normal tissue appearance (
Na2CO3 treated chitosan. The butyryl-chitosan and the regenerated electrospun chitosan nanofibers show good cytocompatibility, structural stability, suggesting future exploration in tissue engineering applications.
Guided tissue regeneration (GTR) membranes are employed in dental/maxillofacial treatments combined with bone graft for regeneration of periodontal tissues lost to disease or injury. The membranes act as barriers to soft tissues and prevent their migration into the bone graft site. Chitosan membranes have shown promise in GTR applications due to their biocompatibility and degradability. Electrospinning chitosan into nanofibrous membranes further adds biomimic extracellular matrix structure, and porosity to promote fluid/nutrient exchange between soft and hard tissue compartments while being cell occlusive. Using trifluoroacetic acid (TFA), electrospun chitosan membranes exhibited in vitro and in vivo compatibility and degradability. However, the nanofibrous structure was not optimal due to swelling of the fibers during removal of residual TFA solvent salts post spinning.
The Fourier transform infrared spectroscopy (FTIR) spectra shown in
There has been a growing interest in the fabrication of nanofibers derived from natural polymers due to their ability to mimic the structure and function of extracellular matrix. Electrospinning is a simple technique to obtain nano-micro fibers with customized fiber topology and composition (
The current study aimed to improve and maintain nano-fibrous and porous structure of the electrospun membranes by introducing a new post electrospinning chemical treatment. Membrane thickness was tripled in this research in order to increase the general tearing strength. Scanning electron micrograph (SEM) examination (
Chitosan membranes treated by TEA/tboc showed better nano-fiber morphology characteristics than membranes neutralized by saturated Na2CO3 solution before and after being soaked in PBS. Retention of the nanofibrous structure for guided tissue regeneration applications may be of benefit for enabling nutrient exchange between soft gingival tissue and bone compartments and for mimicking the natural nanofibrillar components of the extracellular matrix during regeneration.
To further explore the potential of the electrospun chitosan nanofibers in tissue engineering applications, osteoblast proliferation on the membrane of electrospun chitosan nanofibers was examined using a luminescence based high-throughput method for measuring cell growth based on ATP via the Celltiter Glo Assay Kit. The cell morphology on electrospun chitosan nanofibers membranes treated with triethanolamine/N-tert-butoxycarbonyl (TEA/t-BoC) or Na2CO3 was visualized with fluorescence microscope after osteoblast cells (SAOS-2 cells) were cultured on the top of the membranes for 5 days. The cells grown on both electrospun chitosan nanofiber membranes showed characteristic shapes associated with osteoblast cells, such as elongated/stretched shape, indicating the material did not interfere with the growth of the osteoblasts.
As shown in
Clinically, surgical tacks are one common method to secure the membrane on the bone during treatment (
A new post-electrospinning treatment of the chitosan membrane was explored in this research. The results indicate that this new post-electrospinning TEA/tBoc treatment of the chitosan membrane successfully preserved the porous structure in the water environment with good cell compatibility and degradation rate. In addition, tearing strength of the chitosan membrane was significantly improved compared with the previous study.
An animal study was conducted to evaluate the biocompatibility, biodegradation and soft tissue excluding properties of a butyric anhydride modified electrospun chitosan nanofibrous membrane. The study used a critical size (8-mm) rat calvarial bone defect model. In the rat cranium, the established critical size defect was a circular defect of 8 mm in diameter. Repeated and current studies continued to show that defects of this size in rats failed to heal and fill primarily with fibrous tissue and only minimal bone growth at the edges over a 3-month period. The advantages of this model are; a) the calvarial bone is a plate which is large enough to allow creation of a circular defect that enables convenient radiographic and histological analysis, b) the calvarial bone has a large enough size for easy surgical procedures and specimen handling, c) no fixation is required, and d] the model is well studied and reproducible which enables comparison of variety of implant materials.
The animals were x-rayed at 2, 3, 9 and 12 weeks post implantation. One group of animals was euthanized by CO2 inhalation at 3-weeks post-implantation and the other group of animals at 12-weeks post-implantation. The craniotomy sites with implants were excised and fixed in formalin for histological evaluation.
X-rays were taken in the lateral view since this enabled easy viewing of the defect in the thin rat calvarial bone. The membrane was transparent in the x-ray. At two weeks, the calvarial defect was still seen as evidenced by the radiolucent area, indicating little to no bone formation (
Evaluation of chitosan nanofiber membranes in rat calvarial model showing preliminary x-ray results was done comparing butyric anhydride- and triethanolamine/N-tert-butoxycarbonyl (TEA/t-BoC)-modified nanofibrous chitosans to a commercial collagen membrane. Electrospun chitosan nanofiber guided bone regeneration (GBR) membranes were modified by butyric anhydride or TEA/TBoC mechanisms to stabilize nanofibers in aqueous solutions. 15 mm diameter chitosan nanofiber membranes were implanted to cover 8 mm diameter critical sized rat calvarial defects; a commercial collagen membrane (Biomend Extend, Zimmer Dental) was used as a control. 15 animals (5 animals per membrane type) were x-rayed at implantation (0 week) and at 3 weeks after euthanasia (
Gross histology of the implants retrieved from animal at the 12 week time point showed no gross inflammation and a normal tissue appearance (
Raspberry ketone (Sigma) was added to de-aerated 2% chitosan by weight (87% degree of deacetylation) in 2% acetic solution in 1.6:2 ratio. The mixture was stirred overnight at 85° C. then lyophilized. The lyophilized modified chitosan was combined with unmodified chitosan in a 0:1, 25:75 and 50:50 ratio to make a 4% weight volume polymer in 5% acetic acid solution.
Using a water in oil emulsion crosslinking technique (Indian J Pharm Sci. 2007; 69:498-504), the modified chitosan solution was added to liquid paraffin while stirring and then crosslinked by 5 mM genipin (Wako) in acetone for about 12 hours. The microspheres were recovered by centrifugation and size characterization was performed using imaging software (ImageJ, NIH) on images taken under light microscopy.
Fourier transform infrared spectroscopy (FTIR) was performed to determine if raspberry ketone had attached to the chitosan via an imine bond.
X-ray diffraction of unmodified chitosan and raspberry ketone modified chitosan was performed.
In vitro analysis of the modified chitosan microspheres was performed by exposing macrophages (RAW 264.7) to the microspheres for 48 hours and measuring the nitric oxide response. Five groups (n=4) were analyzed. Macrophages were exposed to the microspheres of the different weight ratios including unmodified chitosan microspheres. Cells exposed to 2.5 μg/ml lipopolysaccharide (LPS) were used as positive controls, and cells with no LPS or microspheres were used as negative controls. Samples were taken at 24 and 48 hour intervals and nitric oxide concentration was measured using a Griess Reagent System (Promega). Macrophage cells exposed to all microsphere compositions showed low level nitric oxide production similar to the negative controls. Only the positive control cells exposed to lipopolysaccharide exhibited high levels of nitric oxide production (
Inducible nitric oxide syntase (iNos) gene expression in raw264.7 mouse monocytes on chitosan and raspberry ketone modified chitosan were significantly decreased from the control tissue culture plastic group, with raspberry ketone chitosan further reducing iNos expression in the group exposed to LPS (
A protocol is disclosed herein that allows the preparation of microspheres from raspberry ketone-modified chitosan via water in oil emulsion technique. While the size range is relatively large, the majority of microspheres fell between 30 and 90 μm diameter. The FTIR spectra demonstrated the imine bond peak appeared after modifying the chitosan with raspberry ketone indicating that raspberry ketone was bonded to the chitosan and not just absorbed to the chitosan polymer. The in vitro data demonstrates that the modified microspheres did not activate nitric oxide production at a higher level than the negative controls or unmodified chitosan groups. Further research is needed to explore whether the raspberry ketone modified chitosan microspheres can inhibit an nitric oxide response from macrophages that are exposed to LPS, as well as degradation profiles.
The results described herein relating to acylated chitosan nanofibers were obtained using the following methods and materials.
Electrospinning Procedure: electrospun chitosan nanofiber membrane with random fiber orientation was fabricated by electrospinning Briefly, a 5.50 (wt/vol) % chitosan (70% deacetylated, MW ¼ 311.5 KDa, Primex Inc.) solution in 70 (v/v) % TFA and 30 (vol/vol) % DCM was gently mixed overnight. The solution was electrospun at 25 kV and the fibers were collected on a non-stick aluminum foil target (Reynolds Wrap VR, 38.1 cm diameter circular disc), positioned 15 cm from needle tip and rotated at 8.4 RPM by an AC motor to ensure even and random distribution of fibers.
Surface acylation: 10 mg of electrospun chitosan nanofibers mats were placed in Petri dish containing 1 ml of butyric anhydride and 1 ml of pyridine. The mixtures were stirred for 1 h at 20° C. After acylation, the electrospun chitosan nanofibers mats were washed by Soxhlet extraction with methanol overnight and dried by lyophilization.
De-acylation: 10 mg of acylated electrospun chitosan nanofibers membrane was placed in a Petri dish containing about 5 ml of 5% KOH solution. The mixtures were stirred for 1 h at 60° C. In another experiment, one gram of acylated chitosan nanofiber membrane was placed in a flask before adding about 100 ml of 5% KOH solution or other base. The ratio of acylated chitosan to base may be adjusted as needed. The mixture was stirred by a magnetic stirrer at 60° C. The degree of deacylation to remove the acyl groups, such as fatty acid anhydrides, attached to the nanofiber surface were controlled by modifying the reaction times. The deacylated chitosan nanofiber membrane was removed from the solution, placed in a dialysis tubing, and dialyzed in distilled water for about 24 hours at room temperature. The membranes were dried by lyophilization. or drying or other convenient method.
Fourier Transform Infrared Spectroscopy (FTIR): electrospun chitosan nanofibers membranes were dried at 80° C. for at least 1 h and grinded with KBr to make pellets. Spectra were recorded on a Spectrum One spectrometer (Perkin-Elmer, Eden Prairie, Minn.) from about 4000 to about 500 cm−1 with a resolution of about 4 cm−1 in wave number at room temperature.
Scanning Electron Microscopy (SEM): electrospun chitosan nanofiber membranes were coated with an approximately 20 nm layer of gold by an ion sputter coater and were observed with a SEM (Philips XL-30 ESEM).
Transmission Electron Microscopy (TEM): electrospun chitosan nanofiber membranes were sonicated and loaded on carbon supported copper grids. The grids were freeze-dried and viewed at 120 kV in a electron microscope.
X-ray diffraction: Wide-angle X-ray scattering (WAXS) was recorded on a Bruker D8 diffractometer. Electrospun chitosan nanofibers membranes were ground into a fine powder with a mortar and pestle, after submersion in liquid nitrogen. Powders were scanned in grazing angle reflection mode and data were collected with 2 from 4 to 30.
Electrospinning: CSEF were prepared by electrospinning 5.5% wt/vol chitosan (71% DDA) in 70% TFA-30% methylene chloride solution at 25 kV onto a non-stick aluminum foil target rotating at 8.4 rpm.
Surface acylation: CSEF were acylated in acetic anhydride with or without pyridine for 1 hr at 20, 50 or 90° C. Pyridine derivatives 4-dimethylaminopyridine (DMAP) and 4-(1-pyrrolidinyl) pyridine may also be used. After reaction, the membranes were washed in sodium carbonate and water to remove by-products and acid contaminants.
Characterization: The acylated CSEF were characterized by immersion in PBS for stability, Fourier transform infrared spectroscopy (FTIR) for chemical structure, and electron microscope (TEM and SEM) for fiber diameter and morphology. Proliferation of osteoblast cells (SaOS-2) on membranes (n=5/membrane) was measured by the CellTitre Glow® (Promega) at 1, 3, and 5 days and compared to cast chitosan film controls. Cell morphology was observed by Live/Dead® staining (Molecular Probes).
Animal study: In the animal study, 10 Sprague Dawley rats weighting 250-280 g (approx. 2 months old) were used. Male animals of this size were selected to be skeletally mature and to avoid confounding factors associated with female estrous cycles. The test membranes were ethylene oxide gas sterilized prior to implantation. Each rat received one implant.
Rats were anesthetized with 4% isoflurane in oxygen for approximately 2 minutes. Maintenance of anesthesia was achieved with 2% isoflurane delivered via nosecone/non-rebreather. The dorsal part of the cranium was shaved and aseptically prepared with a solution of povidone iodine (BETADINE®). A U-shaped incision was made in the posterior part of the cranium, allowed the division of the subcutaneous fascia and the bilateral reflection of the periosteal flaps following blunt dissection, to expose the calvarial bone. Careful drilling with an 8-mm diameter trephine bur, mounted on a low-speed dental hand piece, around the sagittal suture, was used to create a standardized, round, defect. During drilling, the area was continuously irrigated with sterile saline solution. The calvarial disk was carefully removed to avoid tearing of the subjacent cranial structures.
A butyric anhydride modified membrane was placed to cover the circular defect overlapping the defect margin by at least 3-4 mm. There was one implant per animal. The periosteum and skin were carefully closed and secured with nylon sutures (e.g. Ethilon 4-0, Ethicon Endo-Surgery, Bridgewater, N.J.) after membrane implantation. After surgery, animals will be housed individually and given subcutaneous injections of buprenorphine (0.15 mg/kg) for postoperative analgesia after surgery. Animals were given free access to rodent chow and water. Sites healed without complication. The study was conducted as part of the animal protocol (#0732) that was reviewed and approved by the Institutional Animal Care and Use Committee at The University of Memphis in compliance with the NIH Guide for the Care and Use of Laboratory Animals.
The results described herein related to chitosan nanofibers treated with tboc were obtained using the following methods and materials.
Manufacture of chitosan nonwoven nanofiber membranes: nanofibrous chitosan membranes with random fiber orientation are fabricated by electrospinning Briefly, a 5.50 weight per volume percentage (w/v) chitosan (70% deacetylated, MW=311.5 KDa, Primex Inc.) solution in 70 (v/v) % trifluoroacetic acid and 30 (v/v) % methylene chloride was gently mixed overnight. Chitosans with other degrees of deacetylation (DDA)'s and MW may be used, though the exact weight percent of chitosan in the solvent spinning solution may need to be adjusted. The solution was loaded into a 10-mL syringe with a blunt 20 G, 3.81 cm stainless steel needle tip. The syringe was loaded into a syringe pump and the flow rate set to 20 L/min. The solution was electrospun at 25 kV and the fibers were collected on a non-stick aluminum foil target (REYNOLDS WRAP®, 38.1 cm diameter circular disc), positioned 15 cm from needle tip and rotated at 8.4 RPM by an AC motor to ensure even and random distribution of fibers. The electrospinning apparatus was housed inside a ventilated box, which was vented to the fume hood. After electrospinning, the nanofibrous mat was put under vacuum overnight to remove residual solvent and carefully removed from the foil. Note that aligned or other fiber orientations may also be made through simple manipulation of the orientation of the collection target mandrell and speed of rotation.
Electrospinning chitosan: chitosan solution was prepared by dissolving 5.5% (w/v) weight per volume Chitosan (71% DDA) in 70% (v/v) trifluoroacetic acid (TFA) and 30% (v/v) dichloromethane (DCM). Solution was loaded with 25 kV voltage and electrospun with a pumping rate of 15 L/min. Membranes were collected by non-stick aluminum foil in the distance of 15 cm.
Removal of TFA using TEA/acetone: in the post-electrospinning treatment, the membrane is treated in the circumstance of pure organic solvent to avoid swelling in aqueous solutions. The membrane is immersed in 10% (v/v) triethylamine (TEA)/Acetone solution for 8 hours under mild magnetic stirring to completely remove all trifluoroacetate ions and rinsed in pure acetone for 2 hours. The rinsing procedure is repeated two times in order to remove excess TEA. The purified chitosan membrane is placed in between two pieces of nylon net and quickly pressed to remove most of acetone. The membrane is immediately forwarded to the next protection step.
t-BOC protection of chitosan amino group in tetrahydrofuran (THF): the salt free chitosan membrane is then soaked in tetrahydrofuran solution containing di-t-butyl dicarbonate (Boc2O) (25 g/10 mL) in round bottom flask equipped with reflux condenser. The reaction is kept under mild magnetic stirring at the temperature of 65 degree Celsius. After 8 hours, the membrane is rinsed by pure tetrahydrofuran for 2 hours and repeated 2 times to fully remove unreacted di-t-butyl dicarbonate. The membrane is placed in between two pieces of nylon net and gently pressed to remove the solvent and then air-dried and stored in desiccator. The amount of t-BOC capping on the chitosan amino groups can be controlled by changing the di-t-butyl dicarbonate concentration and reaction conditions such as time and temperature. Additionally, 4-Dimethylaminopyridine (DMAP) or other cyclic amine catalyst may be used to increase reaction rate and or shorten reaction times for the t-BOC reaction.
Fourier Transform Infrared Spectroscopy (FTIR): electrospun chitosan nanofibers membranes were dried at 80° C. for at least 1 hour and grinded with KBr to make pellets. Spectra were recorded on a Spectrum One spectrometer (Perkin-Elmer, Eden Prairie, Minn.) from about 4000 to about 500 cm−1 with a resolution of about 4 cm−1 in wave number at room temperature.
Scanning Electron Microscopy (SEM): electrospun chitosan nanofiber membranes were coated with an approximately 20 nm layer of gold by an ion sputter coater and were observed with a SEM (Philips XL-30 ESEM).
Transmission Electron Microscopy (TEM): electrospun chitosan nanofiber membranes were sonicated and loaded on carbon supported copper grids. The grids were freeze-dried and viewed at 120 kV in a electron microscope.
X-ray diffraction (XRD): Wide-angle X-ray scattering (WAXS) was recorded on a Bruker D8 diffractometer. Electrospun chitosan nanofibers membranes were ground into a fine powder with a mortar and pestle, after submersion in liquid nitrogen. Powders were scanned in grazing angle reflection mode and data were collected with 2 from 4 to 30.
Post-operation: Electrospun membranes (n=4/treatment) were treated by 1] using saturated Na2CO3 solution (control) or 2] our novel method based on using triethylamine (TEA) and tert-butyl dicarbonate (tboc). The TEA is used to extract the TFA salts while the tboc is used to protect the —NH2 groups on the chitosan to reduce fiber swelling and maintain nanofibrous structure.
Characterization: Morphology and diameter of fibers in membranes was examined by scanning electron microscope (SEM) and transmission electron microscope (TEM). Fourier transform infrared spectroscopy (FTIR) spectra used to evaluate the removal of the TFA salts and changes in chitosan chemistry pre- and post-treatments. SAOS-2 (ATCC catalogue# HTB-85™) osteoblast cells were seeded on both types of treated membranes (n=4/treatment group) and cell proliferation and viability evaluated over three days using the CellTitre Glow® (Promega) and LIVW/DEAD® stain (Molecular Probes), which are proliferation and viability assays, respectively.
Animal study: In the animal study, 10 Sprague Dawley rats weighting 250-280 g (approx. 2 months old) were used. Male animals of this size were selected to be skeletally mature and to avoid confounding factors associated with female estrous cycles. The test membranes were ethylene oxide gas sterilized prior to implantation. Each rat received one implant.
Rats were anesthetized with 4% isoflurane in oxygen for approximately 2 minutes. Maintenance of anesthesia was achieved with 2% isoflurane delivered via nosecone/non-rebreather. The dorsal part of the cranium was shaved and aseptically prepared with a solution of povidone iodine (BETADINE®). A U-shaped incision was made in the posterior part of the cranium, allowed the division of the subcutaneous fascia and the bilateral reflection of the periosteal flaps following blunt dissection, to expose the calvarial bone. Careful drilling with an 8-mm diameter trephine bur, mounted on a low-speed dental hand piece, around the sagittal suture, was used to create a standardized, round, defect. During drilling, the area was continuously irrigated with sterile saline solution. The calvarial disk was carefully removed to avoid tearing of the subjacent cranial structures.
A TEA/t-boc modified membrane was placed to cover the circular defect overlapping the defect margin by at least 3-4 mm. There was one implant per animal. The periosteum and skin were carefully closed and secured with nylon sutures (e.g. ETHILON® 4-0, ETHICON® Endo-Surgery, Bridgewater, N.J.) after membrane implantation. After surgery, animals were housed individually and given subcutaneous injections of buprenorphine (0.15 mg/kg) for postoperative analgesia after surgery. Animals were given free access to rodent chow and water. Sites healed without complication. The study was conducted as part of the animal protocol (#0732) that was reviewed and approved by the Institutional Animal Care and Use Committee at The University of Memphis in compliance with the NIH Guide for the Care and Use of Laboratory Animals.
The results described herein relating to chitosan compositions treated with a phenyl-containing carbonyl derivative (e.g., raspberry ketone) were obtained using the following methods and materials.
Modification of chitosan material: 2% weight volume of chitosan (87.4% deacetylated, MW=470 kDa, Vanson Halosource) solution in 2% weight volume of acetic acid solution was mixed overnight to allow for homogeneous solution. 300 ml of the chitosan solution was stirred with magnetic stirrer/hot plate at 300 rpm while O2 was purged from the solution using N2 for two hours. 2.4 g of a phenyl-containing carbonyl derivative, such as raspberry ketone, was added to the solution and the mixture was purged using N2 for an additional 30 minutes. The mixture was covered with parafilm to keep O2 from being reintroduced to the system, and the hot plate was set to 85° C. and allowed to stir for 24 hours. Other chitosans with other degrees of deacetylation and molecular weights may be used and the weight percentage of chitosan and or acetic acid may be adjusted. Pyridine, pyridine derivatives 4-dimethylaminopyridine (DMAP) and 4-(1-pyrrolidinyl) pyridine and other catalysts may also be used. The reaction time may be controlled to control both the degree of modification of the chitosan by the raspberry ketone compound and the water contact angle (hydrophobicity) of the modified chitosan.
After 24 hours, the solution was aliquoted and frozen at −80° C., then lyophilized for 2-3 days, or enough all water content to be removed. The lyophilized raspberry ketone modified chitosan was washed with 100% ethanol to remove excess raspberry ketone, then dried in vacuum oven at 60° C. to remove the ethanol. Other drying methods such as air or vacuum drying may also be used to collect the modified material from reaction solution.
The final product can then be redissolved into acetic acid or other solvents for various uses such as films, gels, fibers, and or nano- micro-particles/spheres.
Fourier Transform Infrared Spectroscopy (FTIR): modified chitosan microspheres were dried at 80° C. for at least 1 hour and grinded with KBr to make pellets. Spectra were recorded on a Spectrum One spectrometer (Perkin-Elmer, Eden Prairie, Minn.) from about 4000 to about 500 cm−1 with a resolution of about 4 cm−1 in wave number at room temperature.
Scanning Electron Microscopy (SEM): modified chitosan microspheres were coated with an approximately 20 nm layer of gold by an ion sputter coater and were observed with a SEM (PHILIPS XL-30 ESEM).
X-ray diffraction: Wide-angle X-ray scattering (WAXS) was recorded on a Bruker D8 diffractometer. Modified chitosan was ground into a fine powder with a mortar and pestle, after submersion in liquid nitrogen. Powders were scanned in grazing angle reflection mode and data were collected with 2 from 4 to 30.
Characterization: Morphology and diameter of modified chitosan was examined by scanning electron microscope (SEM). Fourier transform infrared spectroscopy (FTIR) spectra used to evaluate the addition of the phenyl group and changes in chitosan chemistry pre- and post-treatments. Proliferation of NIH3T3 cells on modified chitosan films (n=5/membrane) was measured by the CELLTITRE GLOW® (Promega) at 1, 2, and 3 days and compared to cast chitosan film controls. Cell morphology was observed by Live/Dead® staining (Molecular Probes). Inducible nitric oxide syntase (iNos) gene expression of raw264.7 cells on raspberry ketone chitosan films was performed by seeding raw264.7 mouse monocytes on chitosan and raspberry ketone chitosan films as well as tissue culture plastic as a control onto multiwell plate. After seeding, half of the cells were exposed to 5 μg/ml lipopolysaccharide (LPS) and the other half were left as a negative control for LPS conditions. The LPS treatment activated the production of inducible nitric oxide syntase (iNos). After a 24 hours incubation, the cells were lysed and RNA extracted for use to synthesize cDNA, then Real Time PCR to measure iNos gene expression.
From the foregoing description, it will be apparent that variations and modifications may be made to the invention described herein to adopt it to various usages and conditions. Such embodiments are also within the scope of the following claims.
The recitation of a listing of elements in any definition of a variable herein includes definitions of that variable as any single element or combination (or subcombination) of listed elements. The recitation of an embodiment herein includes that embodiment as any single embodiment or in combination with any other embodiments or portions thereof.
All patents and publications mentioned in this specification are herein incorporated by reference to the same extent as if each independent patent and publication was specifically and individually indicated to be incorporated by reference.
This application claims the benefit of and priority to U.S. Provisional Applications Ser. Nos. 61/946,704, 61/975,881, and 61/980,278, the contents of each of which are incorporated herein by reference in their entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US15/18170 | 2/27/2015 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 61946704 | Feb 2014 | US | |
| 61975881 | Apr 2014 | US | |
| 61980278 | Apr 2014 | US |