Patent Application
20140217864
The present invention relates to treatments for a surface of a metal article and an article with a treated surface. More particularly, the present invention relates to performing laser cladding treatments to coat all or part of one or more surfaces of a metal enclosure with cladding material, and farther relates to a metal enclosure with different coatings of cladding material on selective regions to provide different structural and/or cosmetic properties at these regions of the metal enclosure.
Many products in the commercial and consumer industries are metal articles, or include metal enclosures. The metal surfaces of these products may be treated by any number of processes to alter the surface to create a desired effect, either functional (such as corrosion resistance and wear resistance), cosmetic (such as color, shininess or surface texture), or both. Such characteristics are important to consumers because they want to purchase products that have surfaces that will stand up to normal wear and tear of everyday use and continue to look brand new. One example of such a surface treatment is anodization. Anodizing a metal surface converts a portion of the metal surface into a metal oxide, thereby creating a metal oxide layer. The porous nature of the metal oxide layer created by anodization can be used for absorbing dyes to impart a color to the anodized metal surface. While anodized metal surfaces can provide increased corrosion resistance and wear resistance, it can be difficult for a metal oxide layer to form at edges, such as at corners of the metal article. The metal oxide grows vertically into and outward from a surface, and these growing surfaces intersect at a corner such that the corner itself does not have metal oxide growth.
In broad terms, a metal enclosure can be surface treated using a laser cladding process to create a cladding layer on a surface region of the enclosure. The cladding layer can have one or more structural properties chosen from corrosion resistance, hardness, and fracture toughness that are greater than corresponding structural properties of the underlying metal substrate. The cladding layer can have a cosmetic property such as color, shininess and/or texture, that is different from a corresponding cosmetic property of the underlying metal substrate. The metal enclosure can form all or part of an electronic device housing.
The metal enclosure can include a second surface region having a cladding layer. The cladding layers on the first and second surface regions can have different properties. For example, the cladding layers can have different structural properties, such as different corrosion resistance, hardness, and/or fracture toughness. The cladding layers can have different thicknesses. The cladding layers can have different appearances, such as different colors, shininess and/or texture. The cladding layers on the first and second surface regions can have different compositions, which can achieve the difference in structural properties or appearance between the cladding layers. The metal enclosure can be surface treated to create an anodized layer on one surface region and a cladding layer on another surface region using respective anodization and laser cladding processes. The metal enclosure can have non-anodized corners adjacent the anodized layer, and the corners can be coated with the cladding layer.
The accompanying drawings, which are incorporated herein and form a part of the specification, illustrate the present invention by way of example, and not by way of limitation. The drawings together with the description, further serve to explain the principles of the invention and to enable a person skilled in the pertinent art to make and use the invention.
The present invention will be described with reference to the accompanying drawings, in which like reference numerals refer to similar elements. While specific configurations and arrangements are discussed, it should be understood that this is done for illustrative purposes only. A person skilled in the pertinent art will recognize that other configurations and arrangements can be used without departing from the spirit and scope of the present invention. It will be apparent to a person skilled in the pertinent art that this invention can also be employed in a variety of other applications.
In embodiments presented herein, a metal enclosure is surface treated using a laser cladding process to create a cladding layer on a surface region of the enclosure. The cladding layer can be more durable or cosmetically appealing than the underlying metal substrate and provide the enclosure with a more durable and/or attractive surface. For example, in some embodiments, the cladding layer can have a structural property chosen from corrosion resistance, hardness, and fracture toughness that is greater than a corresponding structural property of the underlying metal substrate. The cladding layer can have a cosmetic property such as color, shininess and/or texture, that is different from that of the underlying metal substrate.
As known to one of skill in the art, a laser cladding process is a hard coating technique in which a cladding material with the desired properties is fused onto a metal substrate by means of a laser beam, resulting in a metallurgical bond between the cladding material and the metal substrate. Laser cladding can yield a cladding layer formed of the cladding material that can have superior properties in terms of pureness, homogeneity, hardness, bonding and microstructure, as compared to other hard coating techniques. The laser beam can be controlled to provide focused heating and localized melting of the substrate and the cladding material. Compared to conventional welding, laser cladding can provide minimal dilution and a small heat affected zone where the substrate and the cladding material melt and minimally mix together to achieve the metallurgical bond. A high degree of mixing between the cladding material and the substrate, which can deteriorate the properties of the resulting cladding layer, can be avoided using a laser cladding process. In some embodiments presented herein, a laser cladding process is used to clad a surface region of a metal enclosure. In some embodiments, laser cladding can be used to form the metal enclosure itself, in which the enclosure is manufactured as a near-net-shape part using a laser cladding process.
A laser cladding process can be automated and can be controlled to precisely coat a selective surface region of the metal enclosure with a cladding layer. The thickness of the cladding layer can be selected depending on the target structural properties and/or cosmetic properties (e.g., color, shininess and/or texture). The laser cladding process can control the deposition of the cladding layer to achieve a desired thickness varying between several micrometers to several centimeters. For example, in some embodiments, a laser cladding process is used to apply a cladding layer having a thickness in a range of from about 50 mm to about 2 mm, or a thickness of from about 0.1 mm to about 0.5 mm in other embodiments. Exemplary deposition rates can involve several square-cm per minute for cladding layers with a thickness of around 1 mm.
A wide selection of homologous and non-homologous powder materials car be used as the cladding material, and the materials can be selected depending on the target structural properties and/or cosmetic properties. In some embodiments, the cladding material can include a ceramic and a metal. For example, the cladding material can include ceramic particles (e.g., titanium carbide, tungsten carbide) suspended in a metal matrix (e.g., stainless steel and other steel alloys, as well as aluminum, nickel, cobalt, magnesium, titanium and alloys thereof). In some embodiments, the matrix metal is selected to be the same metal which forms the metal substrate. The homogeneity of the cladding metal matrix and the metal substrate can improve the metallurgical bond. The ratio of ceramic to metal can be selected depending on the target structural properties and/or cosmetic properties. For example, increasing the loading of the ceramic particles in a metal matrix can achieve a harder, more brittle cladding layer. Decreasing the loading of the ceramic particles in the metal matrix can achieve a cladding layer that is less brittle (i.e., lower fracture toughness) and has a lower hardness. A harder cladding layer can be more resistant to abrasions, scratches and other wear, and a less brittle cladding layer can be more resistant to fracturing when subject to impact forces during use of the metal enclosure. In some embodiments, the material of cladding layer includes hard, brittle particles (e.g., carbides) in a ductile metal matrix that improves the cladding material's resistance to fracture. The ratio of ceramic particles to matrix material can be selected to achieve a desired balance of both hardness and fracture toughness properties.
In some embodiments, the volume percent of ceramic particles in the cladding material does not exceed about 60 vol %, does not exceed about 50 vol %, or is from about 40 vol % to about 50 vol %. In some embodiments, the powder materials of the cladding material can be mixed with a binder to form agglomerated powder or to form a paste, to facilitate application of the cladding material to the metal substrate during the laser cladding process.
The cladding materials can be selected depending on the target cosmetic properties. For example, the color of the cladding layer can also be modified by changing the composition of the metal matrix and/or the ratio of ceramic particles to metal matrix. For example, in some embodiments, the different colors achieved by varying the cladding material composition appear as different shades of grey. In some embodiments, a glass matrix is used in the cladding material, which can render the cladding layer translucent or transparent and the color of the underlying metal substrate can show through the cladding layer. The cosmetic properties of the cladding layer can also be varied by adjusting the size and/or shape of the particles in the matrix, which can affect the texture.
The metal substrate of the metal enclosure can be any suitable metal for forming metal enclosures (e.g., stainless steel and other steel alloys, as well as aluminum, nickel, cobalt, magnesium, titanium and alloys thereof). The metal enclosure can be formed using any metalworking process (e.g., extrusion, cast, forging, machining, metal injection molding (MIMS) processes).
As an example, a method to achieve a laser clad metal enclosure according to some embodiments presented herein, a metal enclosure can be forged, with any additional structural details thereafter machined (such as machining to provide grooves or holes or to refine the profile of the enclosure using, e.g., computer numerical controls (CNC)). Then, all or part of one or more surfaces of the metal enclosure can be laser clad with a cladding material. For example, in some embodiments, all or part of the exterior surface of the metal enclosure is laser clad. In some embodiments, the entire exterior surface of a metal enclosure is laser clad. Following the laser cladding process, any additional structural details can be machined into the laser clad surface. In some embodiments, the metal enclosure forms all or part of an electronic device housing. The laser clad surface can be provided on the exterior surface of the metal enclosure to constitute an outer, exposed surface of the device.
The metal enclosure can be provided with an initial base surface finish prior to performing the laser cladding process, and a finish can be provided on the cladding layer after performing the laser cladding process. For example, a finishing process such as blasting can be performed on the surface region of the metal substrate prior to being laser clad, and a finishing process such as polishing can be performed on the resulting cladding layer. Any mechanical or chemical finishing processes known to one of skill in the relevant arts can be performed on the metal substrate or the cladding layer. Non-limiting examples of mechanical finishing processes include polishing (e.g., lapping or buffing), blasting (e.g., grit or sand blasting), and mass finishing methods such as sanding, tumbling, brushing, and any combination thereof. Non-limiting examples of chemical finishing processes include electropolishing and chemical polishing, such as bright dipping. Moreover, finishing of a cladding layer on a surface region can include application of a top coating, such as a powder coating, clear coating, lacquer or other cosmetic finishing layer. In some embodiments, finishing of a cladding layer on a surface region can also include a removal process (e.g., machining) for leveling the cladding layer relative to adjacent surface layers (see, e.g., steps 30 and 50 of the embodiments illustrated in later-described
A laser cladding process can involve a 1-stage or a 2-stage process, as known to one of skill in the relevant arts. In a 1-stage process, the cladding material is applied during application of the laser beam (e.g., as a powder or wire fed alongside the laser beam). The powder can be injected onto the substrate by either coaxial or lateral nozzles relative to the laser's position as known in the art. In a 2-stage process, the cladding material is preplaced on the substrate surface (e.g., as preplaced powder, paste/binder mix, plate, wire, through plasma spraying or flame spraying). The cladding material is then melted onto the substrate using a laser beam. In some embodiments, preplacement of cladding material on multiple surfaces of a 3-D enclosure can achieved by using a mold within which the preform is adhered to the metal enclosure (see, e.g., laser cladding steps of later-described
As known in the art, the laser beam causes a melt pool to form in the beam's path. Removal of the beam from the melt pool allows the pool to solidify and produce a track of a solid clad layer following the beam's path. Thereafter, if desired, another clad layer can be deposited on top of the first clad layer to achieve a desired thickness or property of the final cladding layer. Either the laser beam or the substrate can be kept stationary while the other of the substrate or the laser beam is controlled to move in the x,y,z, directions so that the beam tracks along the surface of the substrate, locally melting the cladding material in the beam's path to bond the cladding material onto the substrate. In some embodiments, the metal substrate can be preheated before laser cladding, in order to reduce the cooling rates in the cladding layer and minimize or prevent cracking of the layer on cooling.
The resulting cladding layer on the metal enclosure can be one or more stacked clad layers. In some embodiments, the cladding layer is one clad layer, and in some embodiments, the clad layer is a plurality of clad layers. In cases where multiple clad layers form a cladding layer, the number of clad layers is optimized to a minimum amount, because the bond between adjacent clad layers can fail and adversely affect the mechanical properties of the cladding layer.
The flowcharts and illustrations of
In some embodiments, the laser cladding process is used to deposit inlays of the cladding material. For example, the surface region to be laser clad is a groove in a surface of the metal enclosure. Laser cladding the groove inlays the cladding material in the groove. The resulting cladding layer in the groove can be subjected to a finishing process that removes any excess cladding so that the cladding layer is substantially flush with the adjacent surface of the enclosure.
In some embodiments, metal enclosure can include one or more additional surface regions coated with one or more cladding layers that each have different properties. For example, in some embodiments, the metal enclosure can include a second surface region having a second cladding layer. The cladding layers on the first and second surface regions can have different properties (e.g., different structure and/or cosmetic properties). In some embodiments, the cladding layers on the first and second surface regions can have different compositions, which can achieve the difference in structural properties or appearance between the cladding layers. For example, the compositions of the cladding layers can include a ceramic and a metal, and the ratio of ceramic to metal can vary between cladding layers at different surface regions. In some embodiments, the cladding layers on the first and second surface regions can have different thicknesses. A surface region that may be exposed to a higher likelihood of receiving impact during user-handling of the metal enclosure may have a cladding layer with a greater fracture resistance as compared with a cladding layer on another surface region without the same likelihood of impact exposure. A surface region that may be exposed to a higher likelihood of receiving scratches or abrasions during use of the metal enclosure may have a cladding layer which provides a greater hardness as compared with a cladding layer on another surface region without the same likelihood of such exposure.
Cladding layers 25 and 35 may have different properties (e.g., structural and/or cosmetic properties such as earlier described). In some embodiments, cladding layers 25 and 35 are formed of the same cladding material (with the same composition) but with different thicknesses, which result in differences in properties between layers 25 and 35. In some embodiments, cladding layers 25 and 35 are formed of different cladding materials (with different compositions). The cladding layers 25 and 35 (with different compositions) can further differ in thickness. In some embodiments, the cladding material compositions of cladding layers 25 and 35 differ in type and/or amount of components. For cladding materials including particles (e.g., ceramic particles) suspended in a matrix material (e.g., a metal matrix), the type of matrix material or the type of particles may differ between compositions of cladding layers 25 and 35. The compositions of cladding layers 25 and 35 can further differ in the relative ratio (e.g., volume ratio) of particles to matrix material.
In some embodiments, the cladding materials of cladding layers 25 and 35 can each comprise the same ceramic and metal matrix, with the difference in compositions being a difference in a volume percent of ceramic particles in each cladding layer. As an example only and not by way of limitation, a volume percent of the ceramic particles in first cladding layer 25 can be greater than a volume percent of the ceramic particles in second cladding layer 35, or vice versa. In some embodiments, this difference in properties of cladding layers 25 and 35 can be achieved by varying the composition of the cladding materials forming cladding layers 25 and 35. For example, the composition of cladding layer 35 can have a lower volume percent of hard ceramic particles (relative to that of cladding layer 25) to improve fracture toughness, and the composition of cladding layer 25 can have a higher volume percent of hard ceramic particles to improve hardness. In the embodiment of
Use of a 1-stage or a 2-stage laser cladding process can be employed for coating metal enclosure 15 with cladding layers 25 and 35. In some embodiments, cladding layers 25 and 35 are sequentially coated on surface regions that are immediately adjacent to each other (e.g., regions 16 and 16b or regions 16b and 18a) and abut each other. In such embodiments, a suitable masking material can be used to mask one cladding layer (e.g., layer 25) on enclosure 15 while the other cladding layer (e.g., layer 35) is deposited via the laser cladding process. The masking can be used to provide additional precision to depositing cladding layers 25 and 35 at the boundary where they meet. In some embodiments, the cladding materials can be deposited with the desired precision by virtue of the focus of the laser beam, and masking is unnecessary.
In some embodiments employing a 2-stage process, a mold can be used to preplace the cladding materials (e.g., cladding materials of layers 2.5 and 35) on a 3-D substrate (erg., on surfaces 16 and 18 of metal enclosure 15) prior to application of the laser beam.
It should be understood that the foregoing reference to coating enclosure 15 with two cladding layers 25 and 35 of
In some embodiments, the metal enclosure can be surface treated to create an anodized layer on one surface region and a cladding layer on another surface region using respective anodization and laser cladding processes. The metal enclosure can have non-anodized corners adjacent the anodized layer, and the corners can be coated with the cladding layer. Thus, surfaces (such as corners) where it may be difficult for a metal oxide layer to form an anodized layer can instead be laser clad.
As earlier described, the laser cladding process can be any of one or more laser cladding surface treatments as known to one of skill in the art. The anodization process can be any of one or more anodization surface treatments as known to one of skill in the art. Such anodization surface treatments can include standard and hard anodization methods, for example. Standard anodizing and hard anodizing are terms of art. Standard anodizing refers to an anodization process using a sulfuric acid bath that is able to produce an oxide layer of up to about 25 microns (pm). Hard anodizing refers to an anodization process using a sulfuric acid bath maintained at about or slightly above the freezing point of water, for example in a range between about 0 and 5 degrees Celsius, to produce an oxide layer of up to about 100 microns. Standard anodized layers are generally a brighter color than hard anodized layers when dyed with the same solution, and when neither is dyed. Hard anodized layers, as the name connotes, are harder than standard anodized layers and therefore are more scratch and abrasion resistant. In some embodiments, a dual anodization treatment can be used to form anodized layer 25, whereby anodized layer 25 includes both standard and hard anodized layers and/or regions, such as described in detail in U.S. Pat. No. 8,398,841, which is incorporated herein in its entirety by reference thereto.
In some embodiments, cladding step 20 includes the substeps of
As another example, anodizing step 40 can be conducted prior to cladding step 20. The first surface region can be masked while the second surface region is anodized. The masking on the first surface region can be removed, and the anodized region can then be masked. The first surface region can then be laser clad, whereafter the masking on the anodized region can be removed. In some embodiments, the cladding materials can be deposited with the desired precision by virtue of the focus of the laser beam, and masking of the anodized region is unnecessary.
Applications of metal enclosures produced according to the methods described herein can include any product having an enclosure made of metal. In some embodiments, the product is an electronic device (e.g., a PC computer, tablet, cell phone, MP3 player, scanner), and metal enclosure 15 forms all or part of the housing of the electronic device.
In some embodiments, surface region 16a may have a higher likelihood of receiving scratches or abrasions during use of device 100 than surface regions 16b and 18a (e.g., surface region 16a may be scratched by audio and power jacks attaching to connector ports 112 and 114). Corner 19 may have a higher likelihood than surface region 16a of receiving greater impact forces if a user drops device 100. In such instances, it may be desirable for cladding layer 35 to have a greater fracture toughness than that of cladding layer 25, and for cladding layer 25 to have a greater hardness than that of cladding layer 35.
The foregoing description of the specific embodiments will so fully reveal the general nature of the invention that others can, by applying knowledge within the skill of the art, readily modify and/or adapt for various applications such specific embodiments, without undue experimentation, and without departing from the general concept of the present invention. Therefore, such adaptations and modifications are intended to be within the meaning and range of equivalents of the disclosed embodiments, based on the teaching and guidance presented herein.
It is to be understood that the phraseology or terminology herein is for the purpose of description and not of limitation, such that the terminology or phraseology of the present specification is to be interpreted by the skilled artisan in light of the teachings and guidance. In addition, the breadth and scope of the present invention should not be limited by any, of the above-described exemplary embodiments, but should be defined only in accordance with the following claims and their equivalents.
This is a divisional of U.S. application Ser. No. 13/430,221 filed Mar. 26, 2012 entitled LASER CLADDING SURFACE TREATMENTS, which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13430221 | Mar 2012 | US |
| Child | 14251298 | US |