Cladding materials for optical fibers

FIELD OF THE INVENTION
This invention relates to a cladding material for optical fibers which has outstanding light transmission characteristics and high heat resistance.
BACKGROUND OF THE INVENTION
Optical fibers are well known which comprise a transparent glass or plastic core and a cladding covering the core concentrically therewith and having a lower refractive index than the core material, such that when light incidents on one end of the fiber, light travels through the fiber while being totally reflected in its interior.
Many of the polymers, such as fluoroalkyl methacrylate polymers, have been heretofore proposed for use as plastic cladding materials. However, these methacrylate polymers still remain to be improved in softening temperature, decomposition temperature, refractive index and other properties which are required of cladding materials for optical fibers.
SUMMARY OF THE INVENTION
An object of the present invention is to provide a plastic cladding material for optical fibers which is outstanding in the above-mentioned properties and satisfactory in processability, transparency and flexibility.
Other objects and features of the invention will become apparent from the following description.
The present invention provides an improvement in an optical fiber comprising a cladding and a core wherein said cladding comprises a polymer comprising:
(1) 10 to 100 mole % of a structural unit represented by the formula ##STR4## wherein Rf is a chlorofluorobutyl group, fluoro-lower alkyl group, fluoromethylbenzyl group, fluoromethylcyclohexyl group, ##STR5## (wherein R.sup.1 is a fluoroheptyl group) or ##STR6## (wherein R.sup.2 is fluoropropyl group), and
(2) up to 90 mole % of at least one structural unit selected from the group consisting of;
(i) ##STR7## wherein R.sup.3 is hydrogen, fluorine or methyl group and R.sup.4 is methyl group, phenyl group, cyclohexyl group, trimethylcyclohexyl group or ##STR8## (wherein R.sup.1 is as defined above) and (ii) ##STR9## wherein R.sup.5 is hydrogen or methyl group and Rf is as defined above.
DETAILED DESCRIPTION OF THE INVENTION
The fluorine-containing polymer used in the invention may be a homopolymer which comprises a structural unit of the formula (a), or a copolymer which comprises a structural unit of the formula (a) and at least one of structural units represented by the formula (b) and (c).
In the invention, said homopolymer may be those wherein the substituents Rf are the same or different and said copolymer may be those wherein the substituent or substituents in each structural unit are respectively the same or different.
The fluorine-containing polymer used in the invention comprising structual units (a) or (a) and (b) and/or (c) can be prepared by homopolymerization of a monomer represented by the formula ##STR10## wherein Rf is as defined above, or by copolymerizing the monomer of the formula (d) with a monomer represented by the formula ##STR11## wherein R.sup.3 and R.sup.4 are as defined above and/or a monomer represented by the formula ##STR12## wherein R.sup.5 and Rf are as defined above.
When a copolymer is to be prepared, the monomer (d) and at least one of the monomers (e) and (f) are used in such a ratio that the copolymer obtained comprises at least 10 mole % of the former and up to 90 mole % of the latter.
These monomers can be copolymerized with other monomers, such as an alicyclic ester of methacrylic acid, styrene and vinyl chloride, insofar as such monomers do not impair the characteristics of the fluorine-containing polymer for use as a cladding material for optical fibers.
The monomer (c) for preparing the polymer used in the invention can be prepared, for example, by the following process. ##STR13##
The fluorine-containing polymer used in the invention can be prepared by a usual method or polymerization, e.g. by block, solution, suspension or emulsion polymerization.
Polymerizsation initiators useful for preparing the polymer of the invention are azo compounds and organic peroxides in the case of solution or suspension polymerization, such as azobisisobutyronitrile, isobutyryl peroxide, octanoyl peroxide, di-iso-propylperoxy dicarbonate and fluorine-containing organic peroxides represented by the formulae [Cl(CF.sub.2 CFCl).sub.2 CF.sub.2 COO].sub.2, [H(CF.sub.2 CF.sub.2).sub.3 COO].sub.2 and (ClCF.sub.2 CF.sub.2 COO).sub.2. Initiators useful for emulsion polymerization are redox initiators including oxidizing agents such as ammonium persulfate, potassium persulfate and like persulfates, reducing agents such as sodium sulfite, and salts of transition metals such as ferrous sulfate.
For block, solution or suspension polymerization, it is desirable to use a mercaptan or like chain transfer agent in order to give a higher thermal decomposition temperature to the polymer of the invention or to adjust the molecular weight thereof. The chain transfer agent is used usually in an amount of about 0.01 to about 1 part by weight per 100 parts by weight of the combined amount of the monomers (d), (e) and/or (f).
Typical of media useful for preparing the fluorine-containing polymer used in the invention by solution or suspension polymerization are dichlorodifluoromethane, trichlorotrifluoroethane, dichlorotetrafluoroethane, trichlorohexafluorobutane and like fluorine-containing solvents, and butyl acetate, methyl isobutyl ketone and like hydrocarbon solvents.
The polymerization temperature, which is usually in the range of from 0.degree. to 100.degree. C., is determined in connnection with the decomposition temperature of the polymerization initiator used. Preferably the temperature is about 10.degree. to about 80.degree. C.
The pressure to be used for polymerization is 0 to about 50 kg/cm.sup.2 gauge.
The polymers obtained by the foregoing methods of polymerization and useful as cladding materials usually range from about 200,000 to about 5,000,000 in molecular weight as determined by gel permeation method and have a refractive index of about 1.36 to about 1.44 and a softening temperature of about 80.degree. to about 140.degree. C.
The fluorine-containing polymers of the invention are higher in softening temperature than the fluoroalkyl methacrylate polymers which are usually used as plastic cladding materials and are therefore usable at relatively high temperatures, for example, in the engine rooms of vehicles in which the conventional plastic cladding materials are not usable. The polymer of the invention, which has a high decomposition temperature, can be heated to a wider range of temperatures for the melt-spinning of optical fibers. This facilitates the adjustment of the polymer melting temperature.
When the fluorine-containing polymer of the invention is used as a cladding material for optical fibers, the core material to be used in combination therewith is transparent and is usually at least about 3% higher in refractive index than the cladding material. Examples of such core materials are inorganic materials such as quartz and glass, and organic materials such as methacrylate or acrylates polymers, polycarbonates, polybutyl phthalate, polystyrene and heavy hydrogen-substituted compounds of these polymers.
The fluorine-containing polymer of the invention has a low refractive index, high transparency and good flexibility and is useful as an excellent optical material.
The present polymer, which is useful as a plastic cladding material for optical fibers, is also usable for example as organic glass and an additive for weather-resistant coating compositions because the polymer has high impact resistance.

EXAMPLES 1-7
Fluoroalkyl-.alpha.-fluoroacrylate (100 parts by weight), which is listed in Table 1 as monomer (d), 0.01 part by weight of azobisisobutyronitrile and 0.05 parts by weight of n-dodecylmercaptan were subjected to block polymerization at 60.degree.-70.degree. C. for 3 hours to obtain a polymer.
The molecular weight of the polymer was measured by gel permeation chromatography at room temperature using a column assembly of "Showdex A-803, A-805 and A-806" (products of Japan Waters, Ltd.), acetonitrile as solvent and polystyrene as standard sample. All the fractions were within the range of 200,000 to 5,000,000 in molecular weight.
The fluorine-containing polymer of the invention was then checked for the following properties. Table 1 shows the results.
(1) Softening temperature (Tg)
Using a differential scanning calorimeter (Model DSC II, product of Perkin Elemer Co.), the temperature at which the polymer started to absorb heat was measured while elevating the temperature at a rate of 20.degree. C./min.
(2) Decomposition temperature (T.sub.D)
Using a differential thermobalance (Model DTG-30, product of Shimadzu Seisakusho, Ltd.), the temperature at which the polymer started to decrease in weight was measured while heating the polymer in air at a temperature elevating rate of 10.degree. C./min.
(3) Refractive index (n.sub.D)
Measured at 25.degree. C. with Abbe refractometer (product of Atago Kagakukiki Mfg. Co., Ltd.).
(4) Melt index (MI)
A Koka flow tester, manufactured by Shimadzu Seisakusho, Ltd., was used. The polymer was placed into a cylinder having an inside diameter of 9.5 mm, maintained at 250.degree. C. for 5 minutes and thereafter extruded through a nozzle having a length of 8 mm and an orifice diameter of 2.1 mm under a piston load of 7 kg. The amount in gram of the polymer extruded for a period of 10 minutes was measured as MI.
(5) Transmission (Tm)
An optical fiber, 300 .mu.m in diameter and 15 .mu.m in the wall thickness of cladding, was conjugate spun at 250.degree. C. with use of the polymer of the invention as the cladding material and polymethylmethacrylate as the cladding material. The transmission per 500-mm length of the fiber was measured with light 650 to 680 nm in wavelength.
(6) Flexibility (Fb)
The polymer of the invention was extruded by the same method as used for measuring MI, and the extrudate was drawn at 180.degree. C. into a fiber having a diameter of 1 mm. The fiber was wound around round steel rods of varying radii to determine the radius of the rod on which cracks developed in the fiber.
TABLE 1__________________________________________________________________________Example Monomer (c)* Tg (.degree.C.) T.sub.D (.degree.C.) n.sub.D MI Tm (%) Fb (mm)__________________________________________________________________________1 --CH.sub.2 CF.sub.2 CF.sub.3 105 350 1.37 131 84 Up to 52 --CH.sub.2 CF.sub.2 CF.sub.2 H 103 336 1.40 72 78 Up to 53 --C(CH.sub.3).sub.2 CF.sub.2 CF.sub.2 H 125 322 1.40 86 82 Up to 54 --CH.sub.2 CF.sub.2 CFHCF.sub.3 86 313 1.38 105 86 Up to 55 --CH.sub.2 CH(CF.sub.3).sub.2 111 330 1.37 63 83 Up to 56 --CH.sub.2 CF(CF.sub.3).sub.2 118 341 1.36 60 85 Up to 57 --CH.sub.2 CF.sub.3 104 339 1.39 75 81 Up to 5__________________________________________________________________________ *The Table shows only the Rf group in each monomer (d). The optical fibers used for the test for (Tm) showed oven at -20.degree. C. good flexibility comparable with that at room temperature.
EXAMPLES 8-10
Fluorine-containing polymers of the invention were prepared in the same manner as in Examples 1-7 from 2,2,3,3,3-pentafluoropropyl-.alpha.-fluoroacrylate (PFPFA) as monomer (d), and methyl methacrylate (MMA) as monomer (e) which were used in the proportions listed in Table 2. The polymers were checked for the above-mentioned properties. Table 2 shows the results.
EXAMPLES 11-14
Fluorine-containing polymers of the invention were prepared in the same manner as in Examples 8-10 from PFPFA as monomer (d) and methyl-.alpha.-fluoroacrylate (MFA) as monomer (e) which were used in the proportions listed in Table 3. The polymers were checked for the properties with the results listed in Table 3.
TABLE 2__________________________________________________________________________ PFPFA MMAExample (wt. parts) (wt. parts) Tg (.degree.C.) T.sub.D (.degree.C.) n.sub.D MI Tm (%) Fb (mm)__________________________________________________________________________8 80 20 105 330 1.39 74 78 Up to 59 60 40 105 306 1.42 55 75 Up to 510 40 60 107 295 1.44 86 73 Up to 5__________________________________________________________________________
TABLE 3__________________________________________________________________________ PFPFA MFAExample (wt. parts) (wt. parts) Tg (.degree.C.) T.sub.D (.degree.C.) n.sub.D MI Tm (%) Fb (mm)__________________________________________________________________________11 80 20 110 352 1.39 103 84 Up to 512 60 40 115 331 1.41 121 81 Up to 513 40 60 120 326 1.42 98 78 Up to 514 30 70 123 315 1.43 86 71 Up to 5__________________________________________________________________________
EXAMPLE 15
Fluorine-containing polymer (copolymer) was prepared in the same manner as in Examples 8-14 from 50 parts of ##STR14## as monomer (d) and 50 parts of methyl-.alpha.-fluoroacrylate as monomer (e). The polymer showed Transmission (Tm) as good as 74%.
EXAMPLE 16
An optical fiber, as described in the above item (5) Transmission, was spun with use of the polymer prepared in Example 14 as the cladding material and methyl-.alpha.-fluoroacrylate, which was prepared in the same manner as in Examples 1-7, as the core material.
The optical fiber thus prepared was checked for properties. The results revealed that: transmission (Tm) was as good as 86%, no crack developed and no change of transmission was observed in the fiber when checked for flexibility by 500-times repetition of a cycle of winding the fiber around a steel rod of 10 mm in diameter and rewinding therefrom, and no reduction in the length of fiber was occured after the fiber was allowed to stand in an atmosphere at 120.degree. C. for 10 hours.
COMPARISON EXAMPLE
A polymer was prepared in the same manner as in Example 1-7 except that 2,2,3,3,-tetrafluoropropylmethacrylate was used in place of fluoroalkyl-.alpha.-fluoroacrylate as monomer (d).
The polymer was found to have softening temperature of 72.degree. C., decomposition temperature of as low as 265.degree. C. and refractive index of 1.42.
An optical fiber was spun at 250.degree. C. with use of the polymer obtained above as the cladding material and polymethylmethacrylate as the core material to find formation of voids in the cladding. At 210.degree. C., spinning could not be continued due to clogging of nozzle. At 230.degree. C., was obtained an optical fiber having transmission of 76%. However, the transmission of the fiber reduced to 52% when allowed to stand in an atmosphere at 85.degree. C. for 100 hours. Further, there occurred cracks in the fiber when wound on a steel rod of 10 mm in diameter at -20.degree. C.
EXAMPLES 17-21
Fluorine-containing polymers of the invention were prepared in the same manner as in Examples 8-10 from two kinds of .alpha.-fluoroacrylate listed in Table 4.
The polymers obtained were respectively dissolved in a solvent as listed in Table 4 to prepare a solution of 10 wt. % concentration. Through the resulting solution was passed a polymethylmethacrylate fiber at a speed of 30 cm/min to produce coated fiber. After drying, the fibers were tested for transmission. The results are shown in Table 4 below.
TABLE 4__________________________________________________________________________ SolventExample .alpha.-fluoroacrylate (parts by weight) (parts by weight) Tm (%)__________________________________________________________________________17 CH.sub.2 CF.sub.2 CFClCF.sub.2 Cl (10) CH.sub.2 CF.sub.2 CF.sub.3 (90) Ethylacetate (100) 7118 ##STR15## (1) CH.sub.2 CF.sub.3 (99) Ethylacetate (100) 8119 ##STR16## (20) CH.sub.2 CH.sub.2 F (80) Ethylacetate (50)/ R-113 730)20 ##STR17## (20) (CH.sub.2).sub.2 C.sub.8 F.sub.17 (80) Ethylacetate (50)/ R-113 720)21 ##STR18## (30) (CH.sub.2).sub.2 C.sub.8 F.sub.17 (70) Ethylacetate (50)/ R-113 700)__________________________________________________________________________ The table shows only the Rf group in each .alpha.-fluoroacrylate. R113 represents 1,1,2trichlorotrifluoroethane.
EXAMPLES 22-29
Fluorine-containing polymers were prepared in the same manner as in Examples 8-10 with use of .alpha.-fluoroacrylate and methacrylate listed in Table 5.
An optical fiber was spun from each of the polymers prepared above in the same manner as in Examples 17-21. The fibers were tested for transmission (Tm). The results are shown in Table 5.
TABLE 5__________________________________________________________________________ .alpha.-fluoroacrylate Methacrylate SolventExample (parts by weight) (parts by weight) (parts by weight) Tm (%)__________________________________________________________________________22 CH.sub.2 CH.sub.2 CF.sub.3 (10) ##STR19## (90) Ethylacetate (100) 7623 CH.sub.2 CF.sub.2 CF.sub.3 (90) ##STR20## (10) Ethylacetate (100) 7324 CH.sub.2 CF.sub.2 CF.sub.3 (90) CH.sub.2 CF.sub.2 CFClCFCl (10) Ethylacetate (100) 7125 CH.sub.2 CF.sub.2 CF.sub.3 (90) ##STR21## (10) Ethylacetate (100) 7826 CH.sub.2 CF.sub.3 (80) ##STR22## (20) Ethylacetate (100) 8327 CH.sub.2 CF.sub.3 (20) ##STR23## (80) Ethylacetate (100) 8228 CH.sub.2 CF.sub.3 (80) ##STR24## (20) Ethylacetate (50)/ R113 (50) 8129 CH.sub.2 CF.sub.3 (80) ##STR25## (20) Ethylacetate (100) 77__________________________________________________________________________ The table shows only the Rf and R groups in each ##STR26##
EXAMPLES 30-34
Polymers of the invention were prepared in the same manner as in Examples 8-10 by copolymerizing 70 parts by weight of pentafluoropropyl-.alpha.-fluoroacrylate and 30 parts by weight of 2,2,3,3-tetrafluoropropyl-.alpha.-fluoroacrylate (intrinsic viscosity (y)=0.72; solvent: methylethylketone; at 35.degree. C.).
Each of the polymer was dissolved in methylethylketone to prepare a solution of 10% by weight in concentration. Through the solution was passed the core material listed in Table 5 in the same manner as in Examples 17-21. The optical fibers thus obtained were tested for Tm. The results are shown in Table 6.
TABLE 6______________________________________Core material and properties thereofExample Core Material Tg (.degree.C.) n.sub.D Tm (%)______________________________________30 Quartz -- 1.46 9331 Polymethylmethacrylate 105 1.49 8432 Polystyrene 85 1.59 7233 Polycarbonate 135 1.59 7834 3,3,5-Trimethyl 140 1.51 81 cyclohexyl methacrylate______________________________________
EXAMPLES 35-36
The monomers listed in Table 7, 0.05 parts by weight of azobisisobutyronitrile and 0.1 part by weight of dodecylmercaptan were subjected to block polymerization at 60.degree. C. for 6 hours to obtain polymers.
The polymers were checked for the properties of Tg, n.sub.D, MI, Tm and Fb in the same manner as in Examples 1-7. Table 7 shows the results.
TABLE 7______________________________________Ex-am- monomersple (parts by weight) Tg n.sub.D MI Tm Fb______________________________________35 CH.sub.2 .dbd.CFCOOCH.sub.3 (10) 120 1.39 76 82 up to 5 CH.sub.2 .dbd.CFCOOCH.sub.2 CF.sub.3 (90) CH.sub.2 .dbd.CHCOOCH.sub.3 (1)36 CH.sub.2 .dbd.CFCOOCH.sub.2 CF.sub.3 108 1.39 110 81 up to 5 (85) CH.sub.2 .dbd.CHCOOCH.sub.2 CF3 (15)______________________________________

Number	Name	Date
4259407	Tada	Mar 1981
4566755	Ohmori	Jan 1986
4615584	Ohmori	Oct 1986

Cladding materials for optical fibers

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

CROSS REFERENCE TO RELATED APPLICATION

US Referenced Citations (3)

Continuations (1)

Continuation in Parts (1)