Claims
- 1. A composition which forms a drying type joint compound when mixed with water suitable for use in finishing joints between gypsum wallboards, said composition being free of asbestos and any clay substitute therefor, and containing no glass microbubbles, comprising at least about 50% by weight of a filler selected from the group consisting of calcium carbonate and calcium sulfate dihydrate, a binder, a cellulosic thickener and an acidic acrylate copolymer in-situ thickener.
- 2. The composition of claim 1 in which the filler is calcium carbonate.
- 3. The composition of claim 2 in which the in-situ thickener is an acrylic emulsion copolymer of methacrylic acid and ethyl acrylate.
- 4. The composition of claim 2 which contains at least about 5% by weight of an expanded perlite treated to render it water insensitive whereby the composition is a lightweight joint compound.
- 5. The composition of claim 1 which contains from about 0.1 to about 2% by weight of the in-situ thickener and from about 0.1 to about 2% by weight of the cellulosic thickener.
- 6. The wetted composition of claim 5 having a viscosity ranging between about 400 to about 700 Brabender units and a pH in the range of 8-10.
- 7. in a composition comprising at least about 50% by weight of a filler selected from calcium carbonate and calcium sulfate dihydrate, which forms a drying type joint compound when mixed with water suitable for use in finishing joints between gypsum wallboards, said composition being free of asbestos and any clay substitute for asbestos and containing no glass microbubbles, the improvement comprising incorporating a cellulosic thickener and an in-situ thickener in the composition to provide the composition with those properties normally provided by asbestos or the clay substitutes for asbestos.
- 8. The composition of claim 7 in which the filler is calcium carbonate and the in-situ thickener is an acidic acrylate copolymer.
- 9. The composition of claim 8 in which the in-situ thickener is an acrylic emulsion copolymer of methacrylic acid and ethyl acrylate.
- 10. The composition of claim 8 which contains at least about 5% by weight of an expanded perlite treated to render it water insensitive whereby the composition is a lightweight joint compound.
- 11. The composition of claim 8 which contains from about 0.1 to about 2% by weight of the in-situ thickener and from about 0.1 to about 2% by weight of the cellulosic thickener.
- 12. A drying type joint compound composition containing no asbestos or clay substitute therefor consisting essentially of at least 50% by weight of a filler selected from the group consisting of calcium carbonate and calcium sulfate dihydrate, latex emulsion binder, a cellulosic thickener, and an acidic acrylate copolymer in-situ thickener.
- 13. The composition of claim 12 wherein the in-situ thickener is an acrylic emulsion copolymer of methacrylic acid and ethyl acrylate which is present in the composition in an amount ranging from about 0.1 to about 2% .by weight.
- 14. The composition of claim 12 which contains at least about 5% by weight of an expanded perlite treated to render it water insensitive whereby the composition is a lightweight joint compound.
- 15. The wetted composition of claim 13 having a viscosity ranging between about 400 to about 700 Brabender units and a pH in the range of 8-10.
- 16. A ready-mixed, drying type joint compound composition containing no asbestos or clay substitute therefor consisting essentially of the following ingredients:
- water;
- at least about 50% by weight of a filler selected from the group consisting of calcium carbonate and calcium sulfate dihydrate;
- a cellulosic thickener; and
- an acidic acrylate copolymer in-situ thickener,
- said composition having a pH in the range of 8-10.
- 17. The composition of claim 16 in which the in-situ thickener is an acrylic emulsion copolymer of methacryllc acid and ethyl acrylate.
- 18. The composition of claim 16 which contains at least about 5% by weight of an expanded perlite treated to render it water insensitive whereby the composition is a lightweight joint compound.
- 19. The composition of claim 16 which has a viscosity ranging between about 400 to about 700 Brabender units.
- 20. The composition of claim 18 which also contains up to about 2% by weight of an alpha cellulose fiber.
Parent Case Info
This application Is a continuation-in-part of U.S. patent application Ser. No. 583,845, filed on Sept. 17, 1990 which was abandoned subsequent to the filing of this application.
US Referenced Citations (22)
Non-Patent Literature Citations (6)
Entry |
Alco Chemical Corp.-"ALCOGUM L-15"; May 19, 1987. |
Alco Chemical Corp.-"ALCOGUM L-35"; May 19, 1987. |
Alco Chemical Corp.-"ALCOGUM SL-65"; Jan. 20, 1988. |
Alco Chemical Corp.-"Alcogum SL-Series Thickeners in Ready Mix Joint Cement"; Mar. 28, 1989. |
Alco Chemical Corp.-"ALCOGUM L Thickeners"; Aug. 5, 1993. |
Alco Chemical Corp.-"ALCOGUM L-11"; May 19, 1987. |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
583845 |
Sep 1990 |
|