Patent Application
20180146665
The present disclosure relates to antimicrobial molecules and the construction of antimicrobial polymers such as polyurethanes, polyesters, and polyacrylates.
Microbes are everywhere in the world and some of them are positive, but others may be fatal. According to the list of major concerns about health from the World Health Organization (WHO), many health concerns are caused by micro-organisms, which contaminate water and sanitation services and infect thousands of people. Therefore, some treatments such as cleaning, disinfection, and sterilization of wastewater and air are necessary. Some natural products or small molecules are used to prevent the spread and growth of microbes, but various unpleasant side effects (such as releasing biocides into the environment) are still significant concerns.
Compared to low molecular weight antibacterial agents, antimicrobial polymers are chemically stable macromolecules with reduced residual toxicity, prolonged lifetime, and improved antimicrobial efficiency. Antimicrobial polymers can be classified into three types: (a) polymeric biocides, (b) biocidal polymers, and (c) biocide-releasing polymers. Siedenbiedel, F.; Tiller, J. C. Polymers 2012, 4, 46. In essence, the active ingredients of the polymeric biocides and biocide-releasing polymers are small molecules possessing antimicrobial activity. On the other hand, biocidal polymers can be an effective tool to kill microbes and may be less likely to result in evolved drug resistance. Typical representatives of biocidal polymers are cationic polymers containing quaternary ammonium groups. In terms of evolutionary history, it is difficult for microbes to produce drug resistance to such species because polycations interact with the microbial cells carrying a negative charge.
To obtain permanent, non-leaching antimicrobial polymeric materials, specific antibacterial small molecules (e.g., 1,2-benzisothiazolin-3-one (BIT)) and small or macro cationic molecules (e.g., trimethylguanidine or tetramethylguanidine (TMG) or polyhexamethylene guanidine (PHMG)) can be immobilized to polymers.
For specific antibacterial small molecules, U.S. Pat. No. 9,371,479 discloses a technique for encapsulating a biocide such as BIT into carrier materials. After a predetermined time, biocides are released from the carrier materials and then kill the microbes. U.S. Pat. No. 9,392,786 discloses BIT serving as an ingredient to control pest. But this physically blended BIT material is not environment-friendly and increases the risk of drug resistance.
For small or macro cationic molecules, U.S. Patent Application Publication 2004/0115160 discloses that quaternary ammonium esters are dissolved in water or other solvent for disinfection and preservation of devices. Cationic molecules present antimicrobial properties as they universally interact with negatively charged microbial membranes via electrostatic interactions. A variety of methods were used to fabricate cationic polymers in the antimicrobial field because cationic polymers do not have to interact with specific targets in microbes and can effectively suppress bacterial drug resistance. For example, U.S. Patent Application Publication 2011/0150977 discloses biodegradable cationic block copolymers containing quaternary amine group prepared by ring-opening polymerization (ROP), which can form aqueous mixtures suitable for antimicrobial applications. Through the ROP method, U.S. Patent Application Publication 2012/0251607 and U.S. Patent Application Publication 2012/0251608 also disclose certain antimicrobial polycarbonates containing quaternary amine groups. U.S. Patent Application 2012/0195849 discloses certain novel polymers (SMAMPs) containing a guanidine group or quaternary amine group prepared by ring-opening metathesis polymerization (ROMP), which kill microbes through mimicking the structure of natural antimicrobial peptides (AMPs). U.S. Patent Application Publication 2010/0240799 discloses an application of PHMG in the antimicrobial film. The PHMG serves as film-forming composition via physical blending and also exhibits antimicrobial property. U.S. Pat. No. 7,282,538 and U.S. Pat. No. 7,531,225 disclose a functional polyolefin master batch containing guanidine salt oligomer by radical initiator. For these methods, physical blending results in quickly reduced bactericidal efficiency over service time due to the diffusion of the physically mixed antimicrobial agents. Polymerization of monomers containing guanidine group or quaternary amine may limit the use of available types and number of cationic monomer, which may also result in the loss of flexibility or range of polymer properties, such as mechanical properties.
Due to the above-mentioned limitations, there still exists an urgent need for an efficient and convenient approach to prepare coating materials with long-lasting antimicrobial properties and to enable fine-tuning of material properties such as mechanical properties.
In one aspect, the present disclosure relates to new click-functional antimicrobial molecules (including small molecules or, in some cases, macromolecules) and the construction of antimicrobial polymers such as polyurethanes, polyesters, and polyacrylates, including through the use of such molecules. In some cases, the antimicrobial click-functional molecules are based on 1,2-benzisothiazolin-3-one (BIT), trimethylguanidine or tetramethylguanidine (TMG), polyhexamethylene guanidine (PHMG), fluorine-containing molecules, or a combinations thereof. For example, 1,2-benzisothiazolin-3-one (BIT) functioned with an alkyne (BIT-Al), trimethylguanidine or tetramethylguanidine (TMG) functioned with an alkyne (TMG-Al) or dual alkynes (TMG-dAl) and polyhexamethylene guanidine (PHMG) functioned with an alkyne (PHMG-Al) are described herein.
As understood by one of ordinary skill in the art, a “clickable” moiety or a “click-functional” species is a moiety or species that can participate in a so-called “click chemistry” reaction, such as an azide-alkyne cycloaddition reaction or a thiol-ene reaction. For instance, a clickable moiety can include an azide or alkyne moiety. Similarly, a click-functional species can be a chemical species that includes, somewhere in the species, one or more clickable moieties. As described further hereinbelow, a click-functional species can and generally does include moieties other than the one or more clickable moieties of the species.
The present disclosure also provides a facile method to prepare antimicrobial polymers containing clickable functional groups. For instance, quaternary ammonium groups can be readily incorporated into the polymers and used as antimicrobial active moieties, and clickable quaternary ammonium functional groups can be incorporated and used to link different functional molecules to the polymers. Quaternary ammonium polymers described herein containing clickable functional group are effective antimicrobial agents. Moreover, in some cases, the antimicrobial activity of the polymers is effectively increased with the use of fluorine-containing molecule via click chemistry. Thus, in another aspect, the present disclosure relates to introducing fluorine-containing small molecules; 1,2-benzisothiazolin-3-one (BIT); trimethylguanidine or tetramethylguanidine (TMG); or polyhexamethylene guanidine (PHMG) into polymers to improve the antimicrobial properties of the polymers through a click reaction between the clickable polymer platforms and the clickable antimicrobial small molecule/macro cationic molecules. Further, in some embodiments, polymers having improved mechanical properties as well as improved antimicrobial properties are described herein. For example, in some cases, TMG-dAl is used to attach a TMG moiety to a “clickable” polymer, wherein TMG-dAl is trimethylguanidine or tetramethylguanidine functionalized with dual alkynes. The guanidinium cations and the alkyne moieties, respectively, introduce an antimicrobial property to the clickable polymer and also enhance the mechanical properties of the clickable polymer.
The present disclosure also provides a facile way to synthesize a diol monomer containing a quaternary ammonium group and a clickable functional group. For example, in some embodiments, new functional diols that contain an anti-microbial tertiary amine and clickable alkyne are disclosed herein. These diols can be used as a “diol” reactant in many polymer syntheses to confer antimicrobial properties to polymers such as polyurethanes, polyesters, and polyacrylates.
In still another aspect, the present disclosure further provides new small molecules containing a quaternary ammonium group, fluorine, and clickable azide group.
As described further hereinbelow, the objectives of this disclosure relating to polymers containing 1,2-benzisothiazolin-3-one (denoted as “PU-BIT”), polymers containing trimethylguanidine or tetramethylguanidine (PU-TMG), and polymers containing polyhexamethylene guanidine (PU-PHMG) are achieved, in some cases, through introducing small molecular clickable monomers into polymer side chains to produce antimicrobial polymers with specific antimicrobial small molecule or non-specific (broad spectrum) small/macro cationic molecules. The clickable small molecular monomers include, for example, BIT with alkyne, TMG with alkyne, and PHMG with alkyne, which can be introduced into polymer side chains by click chemistry, for example the copper (I)-catalyzed alkyne-azidecycloaddition (CuAAC).
Thus, objectives of the present disclosure include the following: provide compositions useful as antimicrobial material and coating; provide methods for using compositions useful as antimicrobial material and coating; provide compositions useful in contact antimicrobial surfaces; provide compositions useful in preserving a material's surface from contamination; provide a facile method to prepare clickable antimicrobial polymers and antimicrobial monomers containing quaternary ammonium group and clickable functional group; and provide a method to improve the antimicrobial activity by the use of fluorine-containing molecule via click chemistry.
In some embodiments, compounds consistent with the foregoing are described herein. In some such instances, a compound described herein has the structure of Formula (I):
wherein R1 comprises an antimicrobial moiety or a dehydrogenated antimicrobial moiety. For example, in some cases, R1 comprises trimethylguanidine or tetramethylguanidine (TMG) or dehydrogenated TMG. An “antimicrobial” moiety or composition, for reference purposes herein, is any moiety or composition that has antimicrobial activity, such as indicated by an antimicrobial rate described herein. More particularly, an antimicrobial moiety or composition described herein can have an antimicrobial rate of, or reduce microbial proliferation (such as bacterial proliferation) by, at least 20%, at least 30%, at least 40%, at least 50%, at least 60%, at least 70%, at least 80%, at least 90%, at least 95%, or at least 99%, relative to a negative control. In some cases, an antimicrobial moiety or composition described herein has an antimicrobial rate or reduces microbial proliferation such as bacterial proliferation by 20-100%, 20-80%, 20-60%, 40-100%, 40-99%, 40-90%, 50-99%, 50-90%, 50-80%, 60-99%, 60-95%, 60-85%, 60-75%, 70-100%, 70-95%, 70-90%, 80-99%, or 80-90%, relative to a negative control. Further, in some embodiments, an antimicrobial moiety or composition described herein can kill and/or reduce the proliferation of both Gram-positive bacteria and Gram-negative bacteria. Additionally, in some instances, an antimicrobial moiety or composition described herein can kill and/or reduce the proliferation of microbes over a sustained period of time, such as a period of up to 6 months, up to 3 months, up to 2 months, or up to 1 month. In some cases, the period of time is 1 week to 6 months, 1 week to 3 months, or 1 week to 1 month. Non-limiting examples of antimicrobial moieties, as described further herein, include moieties having a quaternary nitrogen/ammonium group. An antimicrobial moiety described herein can also include a fluorinated hydrocarbon.
Moreover, turning again to Formula (I), in some cases, R1 is joined to the HC≡C—(CH2)— moiety of the structure of Formula (I) through a nitrogen-carbon bond. For example, in some instances, the compound having the structure of Formula (I) comprises Compound (I-1) or Compound (I-2):
wherein X− is a monovalent anion. Any monovalent anion not consistent with the objectives of the present disclosure may be used. For example, as described further below, in some cases the monovalent anion is a halide anion, such as chloride, bromide, or iodide. In other instances, the monovalent anion is a complex or multi-atom monovalent anion, such as BF4−.
In other embodiments, a compound described herein has the structure of Formula (II):
N3—R2 (II),
wherein R2 comprises an antimicrobial moiety or an antimicrobial moiety in which a leaving group of the antimicrobial moiety has been replaced with the azido group of the structure of Formula (II). As understood by one of ordinary skill in the art, a “leaving group” of the antimicrobial moiety is any atom, ion, or other moiety that is displaced or replaced by an azido group during the course of a reaction for modifying the antimicrobial moiety to include an azido group. Some exemplary reactions and leaving groups are described further hereinbelow. Turning again to Formula (II), in some cases, R2 comprises a fluorinated hydrocarbon moiety and/or a quaternary ammonium moiety. In addition, in some embodiments, the fluorinated hydrocarbon moiety is joined to the N3— moiety of the structure of Formula (II) through the quaternary ammonium moiety. For instance, a compound described herein can have the structure of Formula (II-1):
wherein R1 and R2 are each independently a linear or branched C1-C20 alkyl, alkenyl, aryl, or heteroaryl group; wherein X− is a monovalent anion (such as described above); and wherein x, y, and z are each independently an integer from 1 to 20. As understood by one of ordinary skill in the art, a “C1-C20” group described herein has 1 to 20 carbon atoms.
In still other embodiments, a compound described herein has the structure of Formula (III):
wherein R4 is a linear or branched C1-C20 alkyl, alkenyl, aryl, or heteroaryl group; and x, y, and z are each independently an integer from 1 to 20.
In another aspect, compositions are described herein, wherein the composition comprises a polymer or oligomer formed from a reaction product of (i) a compound having any of the Formulas described hereinabove and (ii) one or more second monomers that react with the compound of (i) to form the polymer or oligomer. In some cases, the one or more second monomers comprise one or more diisocyanates. The use of a diisocyanate may be especially preferred when the compound of the foregoing Formulas is a diol that can react with the diisocyanate to form a polyurethane. Other second monomers may also be used. Additional monomers (e.g., third, fourth, and/or fifth monomers) may also be used to form a reaction product described herein. For instance, in some cases, a polymer or oligomer described herein is a reaction product of (i) and (ii) above as well as (iii) a chain extender and/or (iv) a crosslinker. A “chain extender,” as understood by one of ordinary skill in the art, can have two reactive groups operable to link or crosslink a polymer, such as a polyurethane. In some cases, a chain extender described herein is a diol, such as ethylene glycol, 1,4-butanediol (1,4-BDO or BDO), 1,6-hexanediol, cyclohexane dimethanol, or hydroquinone bis(2-hydroxyethyl) ether (HQEE). A “crosslinker” can include more than two reactive groups operable to crosslink the polymer. Further, in some embodiments, a polymer or oligomer described herein is a reaction product of (i), (ii), optionally (iii) and/or (iv), and also (v) a polymerizable antimicrobial moiety, such as a diol including a quaternary ammonium portion. It is further to be understood that (v) and (i) may be the same or different species. It is further to be understood that, in some cases, (i) is at least partially replaced with a diol not according to the Formulas described above. For instance, a polymeric or oligomeric diol such as a polyalkylene glycol may be used to initially form the polymer through reaction with the diisocyanate, and then a species according to one of the Formulas described above can be subsequently or simultaneously added as a separate component. Additionally, in some instances, the polymer or oligomer comprises a quaternary ammonium moiety within a backbone of the polymer or oligomer, and the polymer or oligomer is antimicrobial. Moreover, in some embodiments, the polymer or oligomer of a composition described herein forms an antimicrobial coating or film on a surface. Any surface not inconsistent with the objectives of the present disclosure may be coated with a polymer or oligomer or composition described herein. For example, in some cases, the surface is an exterior surface of a medical device or implant. In other instances, the surface is an exterior surface of a work space, piece of furniture, fixture, or textile. The surface can also be a leather, wood, plastic, or metal surface. Other surfaces may also be used, and the precise surface is not particularly limited. Moreover, as described above, in some embodiments, the surface is formed from an organic material such as an organic polymeric material. In other cases, the surface is formed from an inorganic material such as an elemental metal, metal alloy, or metal mixture (such as stainless steel), or a metal oxide (such as silicon dioxide).
In still another aspect, methods of reducing microbial proliferation on a surface are described herein. In some embodiments, such a method comprises disposing a composition described herein on the surface.
These and other embodiments are described in more detail in the detailed description which follows.
Embodiments described herein can be understood more readily by reference to the following detailed description, examples, and figures. Elements, apparatus, and methods described herein, however, are not limited to the specific embodiments presented in the detailed description, examples, and figures. It should be recognized that these embodiments are merely illustrative of the principles of the present invention. Numerous modifications and adaptations will be readily apparent to those of skill in the art without departing from the spirit and scope of the invention.
In addition, all ranges disclosed herein are to be understood to encompass any and all subranges subsumed therein. For example, a stated range of “1.0 to 10.0” should be considered to include any and all subranges beginning with a minimum value of 1.0 or more and ending with a maximum value of 10.0 or less, e.g., 1.0 to 5.3, or 4.7 to 10.0, or 3.6 to 7.9. Similarly, a stated range of “1 to 10” should be considered to include any and all subranges beginning with a minimum value of 1 or more and ending with a maximum value of 10 or less, e.g., 1 to 6, 3 to 9, or 4 to 7.
All ranges disclosed herein are also to be considered to include the end points of the range, unless expressly stated otherwise. For example, a range of “between 5 and 10” or “from 5 to 10” or “5-10” should generally be considered to include the end points 5 and 10.
Further, when the phrase “up to” is used in connection with an amount or quantity, it is to be understood that the amount is at least a detectable amount or quantity. For example, a material present in an amount “up to” a specified amount can be present from a detectable amount and up to and including the specified amount.
The present disclosure provides clickable antimicrobial polymers, clickable polymers, clickable antimicrobial monomers, and functionalized antimicrobial polymers. For example, in some embodiments, clickable antimicrobial polymers described herein have one or more side-chains including an alkyne (or other clickable moiety) and a quaternary ammonium group (or other antimicrobial moiety), and clickable polymers described herein have one or more side-chains with an azide group (or other clickable moiety). Click functionalized molecules described herein, in some cases, are alkyne- or azide-functionalized molecules that also have an antimicrobial function or antimicrobial functional group. Also provided are methods of making and using such polymers and molecules.
Click chemistry, especially the copper-catalyzed 1,3-dipolar cycloaddition of azides and alkynes (CuAAC), was used to make antimicrobial polymers according to some embodiments of the instant disclosure. This reaction is regioselective, forming only 1,4-substituted products, is insensitive to oxygen, water and solvents, and can be performed at room temperature. The reaction proceeds with high yields and the reaction rate is much faster than many other crosslinking reactions. Another important aspect of the CuAAC reaction is this: the starting materials, azides and alkynes, are exceptionally stable and can be introduced into a wide range of polymer structures.
As described further herein, alkyne or azide containing monomers were introduced into polymer syntheses to create novel polymers with side-chain alkyne or azide groups. Click-functionalized molecules, such as click-functionalized specific antimicrobial or non-specific cationic molecules, were synthesized and incorporated into clickable antimicrobial or clickable polymers, which can significantly improve the antimicrobial properties of the clickable antimicrobial polymers or introduce the antimicrobial properties to the clickable polymers. Additionally, using the click-functionalized monomers to react with corresponding clickable polymers can confer various functions to polymers such as specific antimicrobial or non-specific antimicrobial properties.
The synthesis of clickable waterborne polymers of the disclosure, in some embodiments, was achieved through introducing small molecular clickable monomers with alkyne or azide groups into polymer backbones by step-growth polymerization to produce clickable antimicrobial polymers with one or more side-chain alkyne groups or one or more side-chain azide groups. These “clickable” polymers can link or click with click-functionalized molecules using click chemistry.
In an aspect, the present disclosure provides monomers comprising an alkyne and quaternary ammonium group or monomers comprising azide groups. The monomers can be used to synthesize clickable polymers.
For example,
In one embodiment, monomers described herein are clickable diols having alkyne groups in accordance with the structure of Formula M1:
wherein n and m are each integers from 1 to 10. In some cases, the methyl substituent on the nitrogen is replaced with a more general “R” group, which may be H or a C1-C6 hydrocarbyl group, such as CH3 or CH2CH3. Such a species can be referred to as Formula M1-2.
In one aspect, the present disclosure provides clickable antimicrobial polymers. In some cases, the clickable antimicrobial polymers have at least one pendant group (i.e., a side-chain group) comprising an alkyne group. Moreover, in some embodiments, such a clickable antimicrobial polymer is made by a method disclosed herein.
In some instances, a “clickable antimicrobial polymer” is a polymer containing at least one side-chain alkyne group (or other clickable group) and at least one quaternary ammonium group (or other antimicrobial moiety). As described further herein, the antimicrobial polymers can be synthesized by step-growth polymerization. The disclosure, in some cases, provides antimicrobial polymers with side-chain alkyne groups, which are expressed by schematically in the structures of
In an embodiment, the clickable antimicrobial polymer is a polyurethane polymer having at least one pendant group comprising an alkyne group. In some such instances, the amount of clickable diols (having alkyne groups) used to form the antimicrobial polyurethane was 1% to 25% by weight, based on the total weight of the polyurethane. An exemplary clickable, water dispersible polymer with side-chain alkyne groups is the clickable antimicrobial polyurethane with alkyne groups illustrated in
In an aspect, the present disclosure provides methods of making clickable antimicrobial polymers. For example, the methods use the click functionalized monomers described herein (e.g., a click functional monomer containing a quaternary ammonium group) in step-growth polymerization. For example, in one embodiment, clickable antimicrobial polyurethanes with alkyne groups are synthesized by step-growth polymerization comprising (a) reacting (i) diisocyanate with (ii) polymeric polyol, at for example 70-90° C., and then (b) adding solvent (e.g., DMF), (iii) optionally a chain extender (e.g., 1,4-butanediol (BDO)), (iv) optionally a crosslinker such as trimethylolpropane (TMP)) and (v) clickable diol (e.g., having an alkyne group or other clickable moiety, and optionally also having a quaternary ammonium group or other antimicrobial moiety) to the product from (a). In this manner, clickable reactive groups and optionally quaternary ammonium groups or other antimicrobial groups can be introduced into a polymer.
For instance, a clickable polyurethane with alkyne groups (or other clickable groups) can be synthesized by step-growth polymerization according to the scheme illustrated in
Examples of suitable diisocyanates that can be used to form a polymer or oligomer described herein include but are not limited to 1,6-hexamethylene diisocyanate (HDI), isophoronediisocyanate (IPDI), mixtures of 2,4- and 2,6-toluene diisocyanate (TDI), 4,4′-diphenylmethane diisocyanate (MDI), dicyclohexylmethanediisocyanate (H12MDI), 4,4′-dibenzyl-diisocyanate, and 1,4-cyclohexylene diisocyanate. Some preferred diisocyanates are 1,6-hexamethylene diisocyanate (HDI) and isophoronediisocyanate (IPDI).
Any amount of diisocyanate not inconsistent with the objectives of the present disclosure may be used. In some cases, the amount of diisocyanate used is 15% to 65% by weight, based on the total weight of the polyurethane solid. Preferably, the amount of diisocyanate used is 25% to 55% by weight, based on the total weight of the resulting polyurethane solid.
Examples of polymeric polyols include polyethylene glycol, polypropylene glycol, polytetramethylene ether glycol, poly(butanediol-co-adipate) glycol, and polycaprolactone glycol. It is preferred to use difunctional compounds, although small amounts of trifunctional compounds may be used. Moreover, in some cases, the weight average molecular weight of the polymeric polyol is 600 to 3000. Preferably, the molecular weight of the polymeric polyol used to form a composition described herein is 1000 to 2000.
Any amount of polymeric polyol not inconsistent with the objectives of the present disclosure may be used. In some cases, the amount of polymeric polyol used is 15% to 55% by weight, based on the total weight of the polyurethane solid. Preferably, the amount of polymeric polyol used is 15% to 45% by weight, based on the total weight of the resulting polyurethane solid.
With regard to the preparation of antimicrobial polyurethane with alkyne groups (e.g., (
In another aspect, the present disclosure provides clickable polymers. In some cases, the clickable polymers have has at least one pendant group (i.e., a side-chain group) comprising an azide group. In some embodiments, a clickable polymer is made by a method disclosed herein.
A “clickable polymer,” in some cases, refers to a polymer containing at least one side-chain azide group (or other clickable group) and at least one quaternary ammonium group (or other antimicrobial group). The antimicrobial polymers can be synthesized by step-growth polymerization. The disclosure provides polymers with side-chain azide groups, which are illustrated schematically in
In one embodiment, the clickable polymer is a polyurethane polymer having at least one pendant group comprising an azide group. Any amount of clickable diol not inconsistent with the objectives of the present disclosure may be used to form such a polyurethane. In some cases, the amount of clickable diol (with azide groups) is 5% to 25% by weight, based on the total weight of the polyurethane.
Methods of making clickable polymers are also described herein. In some embodiments, clickable polyurethanes with azide groups are synthesized by step-growth polymerization, the method more particularly comprising (a) reacting (i) one or more diisocyanates with (ii) one or more polymeric polyols (at 70-90° C., for example), and then (b) adding solvent (e.g., DMF), (iii) optionally a chain extender (e.g., BDO)), (iv) optionally a crosslinker such as trimethylolpropane (TMP), and (v) one or more clickable diols having an azide group (or other clickable moiety) to the product from (a). In this manner, clickable reactive groups can be introduced into the polymer.
For example, clickable polyurethane with azide groups can be synthesized by step-growth polymerization according to the scheme illustrated in
Examples of suitable diisocyanates for use in such a scheme include those include those mentioned above, such as HDI and IPDI. Any amount of diisocyanate not inconsistent with the objectives of the present disclosure may be used. In some cases, the amount of diisocyanate is 25% to 65% by weight, based on the total weight of the polyurethane solid. Preferably, the amount of diisocyanate is 25% to 55% by weight, based on the total weight of the polyurethane solid.
Examples of polymeric polyol for use in a scheme such as that of
With regard to the preparation of polyurethane with azide groups (e.g., (
In still another aspect, the present disclosure provides click-functional or—functionalized molecules or monomers comprising one or two alkynes or azides. Such click-functionalized molecules may also exhibit antimicrobial behavior. In some cases, such click-functionalized molecules can be synthesized via the clickable modification of functional molecules with, for example, an antimicrobial functional group. A “functional” molecule refers to a molecule having a function or functional group (e.g., an antimicrobial group) other than the clickable function or functional group(s). The structures of exemplary species are illustrated schematically in
In some embodiments, the functional molecules are molecules containing fluorine and quaternary ammonium with antimicrobial function, which can improve the antimicrobial properties of coatings and films via antimicrobial molecules containing fluorine presented onto the material surfaces. A scheme for synthesizing an exemplary click-functionalized molecule including an azide group and fluorine functional groups is illustrated in
With reference to one exemplary embodiment consistent with
For example, the functional molecules are 1,2-Benzisothiazolin-3-one (BIT) with antimicrobial function, trimethylguanidine (TMG) with antimicrobial function, and polyhexamethylene guanidine (PHMG) with antimicrobial function. Reaction schemes for preparing click-functionalized molecules including alkyne modified benzisothiazolinone (BIT-Al), alkyne modified trimethylguanidine (TMG-Al), and alkyne modified polyhexamethylene guanidine hydrochloride (PHMG-Al) are illustrated in
BIT-Al is prepared by reacting (i) BIT, (ii) 3-halo-propynyl, such as 3-chloro-propynyl and 3-bromo-propynyl at a molar ratio of BIT to 3-halo-propynyl as 1:1.1-2.0, in (iii) suitable solvent, such as such as methanol, ethanol, isopropanol, diethyl ether, tetrahydrofuran and DMF, with the catalyst of (iv) alkali, such as sodium hydride, sodium methoxide and sodium ethoxide at a temperature of 30-50° C. for 16-24 hours.
TMG-Al is prepared by reacting (i) TMG, (ii) 3-halo-propynyl, such as 3-chloro-propynyl and 3-bromo-propynyl at a molar ratio of TMG to 3-halo-propynyl as 1:1.1-2.0, in (iii) suitable solvent, such as such as methanol, ethanol, isopropanol, diethyl ether, tetrahydrofuran and DMF, with the catalyst of (iv) alkali, such as sodium hydride, sodium methoxide and sodium ethoxide at a temperature of 30-50° C. for 16-24 hours.
TMG-dAl is prepared by reacting (i) TMG, (ii) 3-halo-propynyl, such as 3-chloro-propynyl and 3-bromo-propynyl, at a molar ratio of TMG to 3-halo-propynyl as 1:2.0-3.0, in (iii) suitable solvent, such as such as methanol, ethanol, isopropanol, diethyl ether, tetrahydrofuran and DMF, with the catalyst of (iv) alkali, such as sodium hydride, sodium methoxide and sodium ethoxide at a temperature of 30-50° C. for 16-24 hours.
PHMG-alkyne is prepared by reacting (i) PHMG, (ii) 3-halo-propynyl, such as 3-chloro-propynyl and 3-bromo-propynyl at the molar ratio of PHMG to 3-halo-propynyl as 1:1.1-2.0, in (iii) suitable solvent, such as such as methanol, ethanol, isopropanol, diethyl ether, tetrahydrofuran and DMF, with the catalyst of (iv) alkali, such as sodium hydride, sodium methoxide and sodium ethoxide at a temperature of 30-50° C. for 16-24 hours.
In still another aspect, the present disclosure provides antimicrobial polymers comprising one or more pendant functional molecules covalently bound to the polymer backbone by a linking group comprising a 1,2,3-triazole (i.e., functionalized antimicrobial polymers). Such antimicrobial polymers can be synthesized using a process of click reaction between a clickable polymer and a click-functionalized molecule, wherein a clickable polymer with side-chain alkyne (P1) or side-chain azide groups (P2) is clicked with a click-functionalized molecule with azide groups (FG-N3) or alkyne groups (FG-Al) catalyzed by, for example, copper(I) bromide/copper(I)chloride and N,N,N′,N″,N″-Pentamethyldiethylenetriamine (PMDETA) or CuSO4.5H2O and sodium ascorbate. In one embodiment, the antimicrobial polymer is a polyurethane having at least one linking group, wherein the linking group comprises a 1,2,3-trazole (e.g., a 1,4-substituted 1,2,3-triazole). A click reaction via clickable polymers to functionalized molecule reaction is illustrated in the scheme of
In another aspect, the present disclosure provides methods of making crosslinked antimicrobial polymers, including crosslinked antimicrobial polymers described above. For example, in some cases, the clickable antimicrobial polymers or clickable polymers are polyurethane polymers having at least one pendant group as azide group or at least one pendant group as alkyne group.
In one exemplary embodiment, a clickable antimicrobial polymer with side-chain alkyne groups (P1) is click-crosslinked with a corresponding clickable polymer with side-chain azide groups (P2) in the presence/absence of functional molecules with alkyne and/or azide group under catalysis, for example, copper(I) bromide/copper(I) chloride and N,N,N′,N″,N″Pentamethyldiethylenetriamine (PMDETA) or CuSO4.5H2O and sodium ascorbate catalysis. The click crosslinking via polymer to polymer and/or azide/alkyne functionalized small molecules reaction is illustrated schematically in
In some cases, a method of crosslinking a clickable antimicrobial polymer/clickable polymer (e.g., a clickable antimicrobial polyurethane/clickable polyurethane) comprises crosslinking a clickable polymer having at least one pendant group including an azide group or at least one pendant group including an alkyne group and further comprising a quaternary ammonium salt group. Such crosslinking can be carried out in the presence/absence of alkyne or/and azide functionalized molecules with a copper(I)/copper (II) catalysts, for example, copper(I) bromide/copper(I) chloride and N,N,N′,N″,N″ Pentamethyldiethylenetriamine (PMDETA) or CuSO4.5H2O and sodium ascorbate, under conditions such that a crosslinking group comprising a 1,2,3-triazole is formed. The 1,2,3-triazole(s) of the crosslinking group(s) of cross-linked polymer (e.g., a cross-linked polyurethane) is/are formed by the reaction of a pendant azide group and a pendant alkyne group. The pendant azide group and pendant alkyne group can be on the same polymer chain or different polymer chains.
In still another aspect, the present disclosure provides uses of small molecules, monomers, polymers or oligomers, and/or compositions described herein. For example, in some cases, a polymer or composition described herein is used in a coating or film, or as a coating or film of a surface. Examples of such coatings and adhesives include, but are not limited to, exterior and interior coatings, coil coatings, marine coatings, leather coatings, wood coatings, textile coatings, plastic coatings, metal anticorrosive coatings and shoe coatings and films.
Some embodiments described herein are further illustrated in the following non-limiting Examples.
Example of Synthesis of Clickable Diols with Alkyne Groups (M1, n=1, m=1) and Clickable Diols with Azide Groups (M2).
Briefly, 100 mL round bottom flask charged with N-methyldiethanolamine (10 g, 84 mmol) and 30 mL DMF. Slowly dropwise was added propargyl bromide (9.98 g, 84 mmol) under magnetic stirring at room temperature. After 24 h, the reaction was quickly transferred from the round bottom flask to a vial. M1 (n=1, m=1) precipitated from the DMF solution as a sticky material. The supernatant was removed and washed with acetone (since it was only soluble in protic solvents it was not used further). The final product was then put under vacuum for at least 3 days and used without further purification.
2,2-Bis(azidomethyl)propane-1,3-diol (M2) was synthesized as described in Xu et al., Macromolecules 2011, 44, 2660-2667. Briefly, 2,2-bis(bromomethyl)propane-1,3-diol (98%, 10.4 g, 40 mmol) was dissolved in DMSO (40 mL) in a 100 mL 3-neck flask equipped with a reflux condenser. Next, sodium azide (6.5 g, 100 mmol) was added under nitrogen. The suspension was heated to 110° C. and stirred for 20 h. After being cooled to room temperature, 30 mL of water was added and the mixture was transferred to a 500 mL separatory funnel and extracted with 90 mL of ethyl acetate 3 times. The combined organic phase was washed with 50 mL of saturated brine 3 times and dried with sodium sulfate. The final product (yellow liquid) was then put under vacuum for at least 3 days before use.
Example of Synthesis of Non-Clickable Polyurethane (PU 1), Antimicrobial Polyurethane with Side-Chain Alkyne Groups (PU-Al 1) and Polyurethane with Side-Chain Azide Groups (PU-N3).
Non-clickable polyurethane (PU 1), antimicrobial polyurethane with side-chain alkyne groups (PU-Al 1) and polyurethane with side-chain azide groups (PU-N3 1) were prepared from the following materials of Table 1:
The polyurethane samples were prepared according to the above amounts and the following procedure. Firstly, isophoronediisocyanate and polypropylene glycol were charged into a 250 mL dried four-necked flask with a mechanical stirrer, thermometer, condenser, and nitrogen in/outlet. The mixture was uniform after being stirred for 10 min. The temperature of the mixture was increased to 85° C., and the reaction was maintained for 2 h. Then, DMF, 1,4-Butanediol and Trimethylolpropane (for PU1) or 1,4-Butanediol, N,N-bis(2-hydroxyethyl)-N-methylprop-2-yn-1-aminium (M1, n=1, m=1) and Trimethylolpropane (for PU-Al 1) or 1,4-Butanediol, 2,2-Bis(azidomethyl) propane-1,3-diol and Trimethylolpropane (for PU-N3 1) were added into the flask. The reaction was then maintained for 6-7 h. PU1, PU-Al 1 or PU-N3 1 were prepared.
Example of Synthesis of Non-Clickable Waterborne Polyurethane (WPU 2), Waterborne Polyurethane with Side-Chain Alkyne Groups (WPU-Alkyne 2) and Waterborne Polyurethane with Side-Chain Azide Groups (WPU-Azide 2).
Non-clickable waterborne polyurethane (WPU 2), waterborne polyurethane with side-chain alkyne groups (WPU-alkyne 2), and waterborne polyurethane with side-chain azide groups (WPU-azide 2) were prepared from the following materials of Table 2:
The polyurethane samples were prepared according to the above amounts and the following procedure. Firstly, 1,6-hexamethylene diisocyanate and polytetramethylene ether glycol were charged into a 500 mL dried four-necked flask with a mechanical stirrer, thermometer, condenser, and nitrogen in/outlet. The mixture was uniform after being stirred for 10 min, and increased the temperature to 85° C., maintained reaction for 2 h. Then, DMF, 1,4-Butanedioland Trimethylolpropane (for PU2) or 1,4-Butanediol, N,N-bis(2-hydroxyethyl)-N-methylprop-2-yn-1-aminium (M1, n=1, m=1) and Trimethylolpropane (for PU-Al 2) or 1,4-Butanediol, 2,2-Bis(azidomethyl) propane-1,3-diol and Trimethylolpropane (for PU-N3 2) were added into the flask and kept reaction for 6-7 h. PU1, PU-Al 1 or PU-N3 1 were prepared.
Example of Synthesis of Clickable Fluorine Containing Molecules with Azide Groups (FG-1)
Clickable fluorine containing molecules with azide groups (FG-1) were synthesized according to Huang et. al., Journal of Applied Polymer Science, 2011, 122, 1251-1257. Briefly, A solution of dimethylaminoethyl chloride hydrochloride (20.0 g, 139 mmol) in DMF/water (v/v: 7:3, 150 mL) was added sodium azide (10.0 g, 154 mmol) and a catalytic amount of NaI, followed by heating the mixture at 80° C. for 36 hours. After cooling to room temperature, the mixture was neutralized with solid Na2CO3. Then NaOH was added to the above solution until pH at around 11. The mixture solution was extracted with ethyl acetate (100 mL) and diethylether (3×60 mL). The combined organic phase was dried with MgSO4, filtered, and the solvent was partially evaporated, slowly and carefully, under vacuum at room temperature. The residual ethylacetate solution was added 1-Iodo-1H,1H,2H,2H-perfluorodecane (100.0 g, 174 mmol) directly. The reaction was heated overnight at 75° C. The obtained yellow solid was collected, washed with EtOAc and diethyl ether yield. The final product (yellow liquid) was then put under vacuum for at least 2 days before use.
Example of the Synthesis of Click-Functionalized Molecules: BIT-Al.
To a solution of 1,2-benzisothiazol-3-one BIT (755 mg, 5 mmol) in 10 mL of DMF at 25 degrees C. was added K2CO3 (1.75 g, 12.5 mmol), and then propargyl bromide (10 mmol) was added. The reaction mixture was stirred at room temperature for 24 h. Upon dilution with water, a light yellow crystalline product was separated and filtered. In another procedure, the mixture was extracted with several portions of chloroform and the volatile material was removed under vacuum. The residue was dissolved in CH2Cl2 and washed with water. In the two procedures, the combined extracts were dried over anhydrous sodium sulfate. The residue obtained upon evaporation of the solvent was recrystallized from ethanol.
Example of the Synthesis of Click-Functionalized Molecules: TMG-Al.
Alkyne-functionalized trimethylguanidine (TMG-Al) was prepared according to the following procedure. 100 mL flask charged with 50 g TMG, and then slowly dropwise added 6.5 g propargyl bromide. The mixture was kept stirred for 16-24 h reaction at room temperature. After completion of the reaction, the solid was filtered and the excess TMG in mother liquor was removed under a pressure-reducing condition. The final product was obtained without further purification.
Example of the Synthesis of Click-Functionalized Molecules: TMG-dAl.
Alkyne-functionalized trimethylguanidine (TMG-dAl) was prepared according to the following procedure. A 250-mL flask was charged with 20 g TMG, 50 mL ethanol and then 41 g propargyl bromide was slowly added dropwise. The mixture was kept stirred for 16-24 h reaction at room temperature. After completion of the reaction, the solid was filtered and washed with ethanol. The final product was obtained without further purification.
Example of the Synthesis of Click-Functionalized Molecules: PHMG-Al.
Alkyne-functionalized polyhexamethylene guanidine hydrochloride (PHMG-Al) was prepared according to the following procedure. In a 500 mL flask, 25 g PHMG was dissolved in 100 mL DMSO, and heated to 50° C., and then added 0.8 g of sodium ethoxide and 10 g propargyl bromide. The mixture was kept stirred for 16-24 h reaction. After completion of the reaction, water (250 mL) was added and mixed, the aqueous layer was then separated and excess 3-bromo-propynyl extracted with dichloromethane. Removed the solvent and obtained the final product PHMG-Al.
Example of the Synthesis of Antimicrobial Polymers Such as Polyurethane with Side-Chain Fluorine and Quaternary Ammonium Containing Molecules (PU-F).
PU-F was prepared according to the following procedure. The click reaction was performed between PU-Al 1 (prepared in Example 2) and FG-1 (prepared in Example 4) as follows: 15 mL water/DMF mixture (VDMF:VH2O=9:1), 0.8 g FG-1 were added to 15 g solution of PU-Al 1 in DMF at room temperature under stirring followed by the addition of 0.01 g CuSO4.5H2O in 1 mL water-DMF mixed solvent and 0.03 g sodium ascorbate in 1 mL water-DMF mixed solvent, respectively, and then the click reaction was initiated. The mixture was stirred for additional 2 min, then 10 g of mixture was poured into a 6 cm diameter Teflon disk to be dried at 75° C. for 24 h.
Example of the Synthesis of Antimicrobial Polymers Such as Polyurethane with Side-Chain BIT (PU-BIT).
PU-BIT was prepared according to the following procedure. The click reaction was performed between PU-N3 1 (prepared in Example 2) and BIT-Al (prepared in Example 5) as follows: 15 mL water/DMF mixture (VDMF:VH2O=9:1), 0.45 g BIT-Al were added to 15 g solution of PU-N3 1 in DMF at room temperature under stirring followed by the addition of 0.01 g CuSO4.5H2O in 1 mL water-DMF mixed solvent and 0.03 g sodium ascorbate in 1 mL water-DMF mixed solvent, respectively, and then the click reaction was initiated. The mixture was stirred for additional 2 min, then 10 g of mixture was poured into a 6 cm diameter Teflon disk to be dried at 75° C. for 24 h.
Example of the Synthesis of Antimicrobial Polymers Such as Polyurethane with Side-Chain Trimethylguanidine (PU-TMG).
PU-TMG was prepared according to the following procedure. The click reaction was performed between PU-N3 2 (prepared in Example 3) and TMG-Al (prepared in Example 6) as follows: 15 mL water/DMF mixture (VDMF:VH2O=9:1), 0.31 g TMG-Al were added to 15 g solution of PU-N3 1 in DMF at room temperature under stirring followed by the addition of 0.01 g CuSO4.5H2O in 1 mL water-DMF mixed solvent and 0.03 g sodium ascorbate in 1 mL water-DMF mixed solvent, respectively, and then the click reaction was initiated. The mixture was stirred for additional 2 min, then 10 g of mixture was poured into a 6 cm diameter Teflon disk to be dried at 75° C. for 24 h.
Example of the Synthesis of Antimicrobial Polymers Such as PU-dTMG.
PU-dTMG was prepared according to the following procedure. The click reaction was performed between PU-N3 2 (prepared in Example 3) and TMG-dAl (prepared in Example 7) as follows: 15 mL water/DMF mixture (VDMF:VH2O=9:1), 0.25 g TMG-dAl were added to 15 g solution of PU-N3 1 in DMF at room temperature under stirring followed by the addition of 0.01 g CuSO4.5H2O in 1 mL water-DMF mixed solvent and 0.03 g sodium ascorbate in 1 mL water-DMF mixed solvent, respectively, and then the click reaction was initiated. The mixture was stirred for additional 2 min, then 10 g of mixture was poured into a 6 cm diameter Teflon disk to be dried at 75° C. for 24 h.
Example of the Synthesis of Antimicrobial Polymers Such as Polyurethane with Side-Chain Polyhexamethylene Guanidine (PU-PHMG).
PU-PHMG was prepared according to the following procedure. The click reaction was performed between PU-N3 2 (prepared in Example 3) and PHMG-Al (prepared in Example 8) as follows: 15 mL water/DMF mixture (VDMF:VH2O=9:1), 1 g PHMG-Al were added to 15 g solution of PU-N3 1 in DMF at room temperature under stirring followed by the addition of 0.01 g CuSO4.5H2O in 1 mL water-DMF mixed solvent and 0.03 g sodium ascorbate in 1 mL water-DMF mixed solvent, respectively, and then the click reaction was initiated. The mixture was stirred for additional 2 min, then 10 g of mixture was poured into a 6 cm diameter Teflon disk to be dried at 75° C. for 24 h.
This application claims priority pursuant to 35 U.S.C. § 119(e) to U.S. Provisional Patent Application Ser. No. 62/426,668, filed on Nov. 28, 2016, which is hereby incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62426668 | Nov 2016 | US |