Patent Grant
10962696
Light consists of electromagnetic fields that oscillate in a direction perpendicular to the direction of propagation. Unpolarized light is the most general case of light polarization, and linear, elliptical, and circular polarizations are specific cases. Linearly polarized light is the case where electromagnetic fields oscillate in a plane, and this plane defines the polarization plane. One can convert polarization from linear polarization to circular or elliptical polarization. Polarized light may be used in a variety of optical devices in general and display in devices in particular.
A polarizer is an optical filter that passes light of a specific polarization and blocks waves of other polarizations. It can convert a beam of light of undefined or mixed polarization into a beam with well-defined polarization, polarized light. The common types of polarizers are linear polarizers and circular polarizers. Polarizers are used in many optical techniques and instruments, and polarizing filters find applications in photography and liquid crystal display technology.
Current polarizer technology utilizes a polarizing film formed of a polyvinyl alcohol type resin layer having a dichroic material impregnated therein. Such known technologies include a method wherein a polyvinyl alcohol type resin layer is formed by coating and drying a solution of polyvinyl alcohol type resin on a resin substrate and then subjecting this resin layer to a stretching process, and then subjecting the stretched resin substrate to a dyeing process to form a polarizing film having a dichroic material impregnated therein in a molecularly oriented state. Alternatively, a method includes forming a polyvinyl alcohol type resin layer and applying a dichroic material therein, and then stretching the dyed resin layer to form a polarizing film having the dichroic material impregnated therein in a molecularly oriented state.
A liquid-crystal display element can have a polarizing film (described above) laminated on each of a front and back surface of a liquid-crystal cell. The polarizing film typically has a thickness of at least 20 micrometers. These polarizing films typically include additional barrier layers to maintain the dimensional stability of the polarizing film but add thickness to the polarizing film element.
In recent years, OLED (organic light-emitting diode) technology has come into wide use in Smartphones and TVs. Each pixel in an OLED display has a cathode and an anode. Since the cathode is metallic, ambient light that enters the OLED display and is incident on a cathode gets reflected. Light that gets past the cathode may be reflected from a reflection film underneath the TFT (thin-film transistor) substrate. A circular polarizer is inserted in the OLED display in order to address the problem of contrast degradation due to ambient light reflection. The circular polarizer consists of a linear polarizer and a quarter-wave plate (QWP). Unpolarized ambient light is polarized by the linear polarizer; the linearly polarized light is converted to circularly polarized light upon passing through the QWP. The handedness of the circularly polarized light is switched upon reflection from the metallic layer, so most of the reflected light does not pass through the linear polarizer.
For both LCDs and OLEDs, there is an interest in realizing foldable displays for mobile applications. In order to make this possible, it is important to provide polarizers that are thinner or polarizers that can be directly coated on the display substrate. Therefore, improvements in polarizer technology are desired.
The present disclosure relates to a coatable grey polarizer. The coatable grey polarizer may be formed with a composition that includes two or more dichroic dye compounds that exhibit a dichroic ratio that is greater than the dichroic ratio of either individual dichroic dye compound forming the composition. The coatable grey polarizer may form an achromatic polarizer.
In one aspect, a linear polarizer may be formed a blue dichroic dye compound, having a maximum dichroic ratio Kd≤12 in an entire visible wavelength range, and a red dichroic dye compound, having a maximum dichroic ratio Kd≤16 in the entire visible wavelength range. The linear polarizer has a dichroic ratio Kd≥18 and a thickness of less than or equal to 2 micrometers. The linear polarizer may form an achromatic polarizer.
The blue dichroic dye compound may have its maximum visible light absorption in a wavelength range 600 nm-700 nm and a maximum dichroic ratio Kd≤12 in an entire visible wavelength range (such as at 550 nm). The red dichroic dye compound may have its maximum visible light absorption in a wavelength range 430 nm-520 nm and a maximum dichroic ratio Kd≤16 in the entire visible wavelength range (such as at 550 nm). The linear polarizer has a dichroic ratio at 550 nm, and a thickness of the linear polarizer is less than or equal to 2 micrometers.
In another aspect, a linear polarizer film includes a substrate and a linear polarizer, described herein, overlying the substrate.
In another aspect, a circular polarizer includes a retarder, configured as an achromatic quarter-wave plate, and a linear polarizer, described herein, overlying the retarder such that the retarder and a first major surface of the linear polarizer are facing toward each other.
In another aspect, a light emissive display module includes a substrate, an array of light emissive elements overlying the substrate, and a circular polarizer, described herein, overlying the array of light emissive elements.
In a further aspect, a lyotropic liquid crystal formulation includes a blue lyotropic liquid crystal, a red lyotropic liquid crystal, and a violet lyotropic liquid crystal. The blue lyotropic liquid crystal includes a blue compound of structure B:
wherein: X is a SO3H (sulfonic) group or a salt thereof, and 1≤m≤4; Z is a Cl (chloro) group, and 0≤p≤2; and m+p≤4. The red lyotropic liquid crystal includes a red compound of structure R:
or a trans-isomer of structure R, wherein, X is a SO3H (sulfonic) group or a salt thereof. The violet lyotropic liquid crystal includes a violet compound having a structure Va:
or a cis-isomer of structure Va, wherein: X is a SO3H (sulfonic) group or a salt thereof, and 1≤m≤4; Y is a S(═O)2 (sulfone) group, and 0≤n≤2; Z is a OH (hydroxy) group, and 0≤p≤4; R is an O (oxo) group, and 0≤q≤4; and m+p+q≤6. This lyotropic liquid crystal formulation may have the blue:violet:red compounds present in a solids weight ratio of 100:35-45:40-50.
In a further aspect, a lyotropic liquid crystal formulation includes a blue lyotropic liquid crystal, a red lyotropic liquid crystal, and a yellow lyotropic liquid crystal. The blue lyotropic liquid crystal includes a blue compound of structure B:
wherein: X is a SO3H (sulfonic) group or a salt thereof, and 1≤m≤4; Z is a Cl (chloro) group, and 0≤p≤2; and m+p≤4. The red lyotropic liquid crystal includes a red compound of structure R:
or a trans-isomer of structure R, wherein, X is a SO3H (sulfonic) group or a salt thereof. The yellow lyotropic liquid crystal includes a yellow compound having a structure Y:
wherein: X is a SO3H (sulfonic) group or a salt thereof, and 1≤m≤4; Z is a Cl (chloro) group, and 0≤p≤2; and m+p≤6.
These and various other features and advantages will be apparent from a reading of the following detailed description.
The disclosure may be more completely understood in consideration of the following detailed description of various embodiments of the disclosure in connection with the accompanying drawings; in which:
In the following detailed description, reference is made to the accompanying drawings that form a part hereof, and in which are shown by way of illustration several specific embodiments. It is to be understood that other embodiments are contemplated and may be made without departing from the scope or spirit of the present disclosure. The following detailed description, therefore, is not to be taken in a limiting sense.
All scientific and technical terms used herein have meanings commonly used in the art unless otherwise specified. The definitions provided herein are to facilitate understanding of certain terms used frequently herein and are not meant to limit the scope of the present disclosure.
Unless otherwise indicated, all numbers expressing feature sizes, amounts, and physical properties used in the specification and claims are to be understood as being modified in all instances by the term “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the foregoing specification and attached claims are approximations that can vary depending upon the properties sought to be obtained by those skilled in the art utilizing the teachings disclosed herein.
The recitation of numerical ranges by endpoints includes all numbers subsumed within that range (e.g. 1 to 5 includes 1, 1.5, 2, 2.75, 3, 3.80, 4, and 5) and any range within that range.
As used in this specification and the appended claims, the singular forms “a”, “an”, and “the” encompass embodiments having plural referents, unless the content clearly dictates otherwise.
As used in this specification and the appended claims, the term “or” is generally employed in its sense including “and/or” unless the content clearly dictates otherwise.
As used herein, “have”, “having”, “include”, “including”, “comprise”, “comprising” or the like are used in their open ended sense, and generally mean “including, but not limited to”. It will be understood that “consisting essentially of”, “consisting of”, and the like are subsumed in “comprising,” and the like.
In this disclosure:
“visible light” refers to light wavelengths generally from about 400 nm to about 800 nm;
“achromatic” refers to color-less
“dichroic ratio” or “Kd” refers to a ratio αmax/αmin, of an absorption coefficient αmax along a first direction within the plane of the polarizer showing the maximum absorption to an absorption coefficient αmin along a second direction within the plane of the polarizer showing the minimum absorption.
The present disclosure relates to a coatable polarizer or a lyotropic liquid crystal coatable composition or formulation that may be coated onto a substrate to form a polarizer and preferably an achromatic linear polarizer. The coatable polarizer may be referred to as a grey polarizer. The coatable grey polarizer may be formed with a composition that includes two or more dichroic dye compounds that exhibit a dichroic ratio that is greater than the dichroic ratio of either individual dichroic dye compound forming the composition. The coatable grey polarizer may form an achromatic polarizer. The linear polarizer may be formed a blue dichroic dye compound, having a dichroic ratio Kd≤12 in a visible wavelength range, and a red dichroic dye compound, having a dichroic ratio Kd≤16 in the visible wavelength range. The linear polarizer has a dichroic ratio Kd≥18 and a thickness of less than or equal to 2 micrometers. The linear polarizer may form an achromatic polarizer. The blue dichroic dye compound may have its maximum visible light absorption in a wavelength range 600 nm-700 nm and a dichroic ratio Kd≤12 in a visible wavelength range (such as at 550 nm). The red dichroic dye compound may have its maximum visible light absorption in a wavelength range 430 nm-520 nm and a dichroic ratio Kd≤16 in the visible wavelength range (such as at 550 nm). The linear polarizer has a dichroic ratio Kd≥18 at 550 nm, and a thickness of the linear polarizer is less than or equal to 2 micrometers. The coatable grey polarizer may be formed from a lyotropic liquid crystal material solution coated onto a substrate to create a layer of aligned material transmitting most visible light of a first polarization and absorbing most visible light having a second polarization (generally orthogonal to the first polarization). This coatable grey polarizer may be achromatic and appear clear, black or grey. This coatable grey polarizer may have a thickness of less than five micrometers or less than one micrometer, or less than one micrometer. The aligned material may be formed by shear coating the lyotropic liquid crystal material onto a substrate. The lyotropic liquid crystal material can be coated directly onto an optical element such as a glass substrate of a LCD panel. The optical element may be a planar surface or a curved surface. This coatable grey polarizer be utilized to form a circular polarizer, eyewear, or displays. While the present disclosure is not so limited, an appreciation of various aspects of the disclosure will be gained through a discussion of the examples provided below.
The linear polarizer or linear grey polarizer is formed from aligned coatings that are prepared from lyotropic liquid crystal solutions of dichroic dye compounds, described below. An aligned coating layer is obtained by shear coating these lyotropic liquid crystal solutions of dichroic dye compounds. The dichroic dye compounds may be combined with other chromonic mesogens or molecules, polymers or small molecules to form the optical coating layer.
Shear coating methods include slot coating, slit coating, doctor blade coating, die coating, slot-die coating, gravure coating, micro-gravure coating, curtain coating and the like. After the shear coating step, the coated solution is dried to remove the solvent (such as water) and form a polarizer or linear polarizer (optical coating layer). The optical coating layer may be stabilized by converting it to a water-insoluble layer. This conversion can be accomplished by ion exchange of mono-valent ions with di-valent or tri-valent ions.
The polarizer or linear polarizer may be coated directly onto a substrate or an optical element. The substrate or an optical element may be primed and/or corona treated to improve adhesion of the optical coating to the surface of the substrate or an optical element. The final optical coating layer or polarizer or linear polarizer has any useful thickness (dry thickness). The final optical coating or polarizer or linear polarizer may have a thickness of less than 10 micrometers, or less than 5 micrometers, or less than 3 micrometers, or less than 2 micrometers, or less than 1 micrometer, or less than 750 nm. The optical coating or polarizer or linear polarizer may have a thickness in a range from 250 nanometers to 5 micrometers, or from 500 nanometers to 2 micrometers, or from 500 nanometers to 1 micrometer, or from 500 nanometers to 1000 nanometers.
The optical coating (lyotropic liquid crystal solution of dichroic dye compounds) may be utilized to alter or modify spectral or polarization properties of light incident on the optical coating. In many embodiments, this optical coating transmits visible light. This optical coating may be achromatic. This optical coating may be formed of a mixture of dichroic dye compounds, such as two or more dichroic dye compounds, or three or more dichroic dye compounds, where each dichroic dye compound has a different structure, or color. Each dichroic dye compounds may have a different visible light absorption or transmission spectrum. A variety of different dichroic dye compounds may form a mixture that results in an achromatic optical coating (for example, an achromatic polarizer layer).
The substrate may be glass or a polymeric layer such as a polyolefin (PET or PEN), polycarbonate, or polyimide and the like. Glass substrates may form an element of a liquid crystal display panel. The glass substrate may have a reduced thickness such as about 1000 micrometers or less or 500 micrometers or less. In embodiments where the substrate is a polymer layer, the polymeric layer may be a flexible film layer that may be processed in a roll-to-roll manufacturing process.
The linear polarizer described herein may be described as an achromatic or grey polarizer. This linear polarizer may uniformly absorb light at all wavelengths of the visible light spectrum, or at all wavelengths from 500 nm to 700 nm, or at all wavelengths from 400 nm to 800 nm. Uniform absorption provides the polarizer with a grey appearance. Uniform absorption may be defined as a constant absorption ±20%, or ±15%, or ±10%, or ±5%.
Dichroic ratio (Kd) a ratio α1/α2, of an absorption coefficient α1 along a first direction within the plane of the polarizer showing the maximum absorption (minimum transmittance) to an absorption coefficient α2 along a second direction within the plane of the polarizer showing the minimum absorption (maximum transmittance). The dichroic ratio Kd can also be expressed as ln(T1)/ln(T2). T1 is the polarizer transmittance for polarization along a first direction showing minimum polarizer transmittance. T2 is the polarizer transmittance for polarization along a second direction showing a maximum polarizer transmittance. In the examples described herein, the first and second directions are perpendicular or approximately perpendicular to each other. Furthermore, the second direction (maximum polarizer transmittance) is approximately parallel to the shear-coating direction and the first direction (minimum polarizer transmittance) is approximately perpendicular to the shear-coating direction. This occurs because the dichroic dye molecules described herein tend to stack along the shear-coating direction.
The linear polarizers, described herein, are formed of a mixture of two different dichroic dye compounds, three different dichroic dye compounds, or four different dichroic dye compounds. The dichroic ratio (Kd) of the linear polarizer is surprisingly larger than the individual dichroic ratio (Kd) of a shear coated layer formed from each dichroic dye compound. The dichroic ratio (Kd) of the linear polarizer may be at least 5% or greater, or 10% greater, or 15% greater, or 20% greater than the individual dichroic ratio (Kd) of the shear coated layers formed from dichroic dye compounds used to form the linear polarizer.
In some embodiments, the dichroic ratio (Kd) of the linear polarizer may be at least 18 and the individual dichroic ratio (Kd) of each dichroic dye compounds used to form the linear polarizer may be no greater than 17, or no greater than 16, or no greater than 15, or no greater than 14, or no greater than 13 or no greater than 12.
In one embodiments, the dichroic ratio (Kd) of the linear polarizer is 18 or greater and the individual dichroic ratio (Kd) of each dichroic dye compounds forming the linear polarizer is 12 or less for a blue dichroic dye compound, and 16 or less for a red dichroic dye compound.
Useful dichroic dye compounds include blue dichroic dye compounds, red dichroic dye compounds, violet dichroic dye compounds, and/or yellow dichroic dye compounds.
Blue dichroic dye compounds include compounds having a structure B:
wherein:
X is a SO3H (sulfonic) group or a salt thereof, and 1≤m≤4;
Z is a Cl (chloro) group, and 0≤p≤2; and
m+p≤4. In the case that X is a salt, the cation can be: Na+, K+, Cs+, or NH4+.
Red dichroic dye compounds include compounds having a structure R:
or a trans-isomer of structure R, wherein, X is a SO3H (sulfonic) group or a salt thereof. In the case that X is a salt, the cation can be: Na+, K+, Cs+, or NH4+.
A violet dichroic dye compound has a structure Vc:
wherein:
X is a SO3H (sulfonic) group or a salt thereof, and 1≤m≤4;
Y is a S(═O)2 (sulfone) group, and 0≤n≤2;
Z is a OH (hydroxy) group, and 0≤p≤4;
R is an O (oxo) group, and 0≤q≤4; and
m+p+q≤6. In the case that X is a salt, the cation can be: Na+, K+, Cs+, or NH4+.
Another violet dichroic dye compound has a structure Va:
or a cis-isomer of structure Va, wherein:
X is a SO3H (sulfonic) group or a salt thereof, and 1≤m≤4;
Y is a S(═O)2 (sulfone) group, and 0≤n≤2;
Z is a OH (hydroxy) group, and 0≤p≤4;
R is an O (oxo) group, and 0≤q≤4; and
m+p+q≤6. In the case that X is a salt, the cation can be: Na+, K+, Cs+, or NH4+.
A yellow dichroic dye compound has a structure Y:
wherein:
X is a SO3H (sulfonic) group or a salt thereof, and 1≤m≤4;
Z is a Cl (chloro) group, and 0≤p≤2; and
m+p≤6. In the case that X is a salt, the cation can be: Na+, K+, Cs+, or NH4+.
Useful lyotropic liquid crystal formulations include two or more dichroic dye compounds such as the blue dichroic dye compounds, red dichroic dye compounds, violet dichroic dye compounds, and/or yellow dichroic dye compounds, as described herein.
Useful lyotropic liquid crystal formulations include the red dichroic dye compounds of structure R, the blue dichroic dye compounds of structure B, and violet dichroic dye compounds of structure Vc or Va. This lyotropic liquid crystal formulation may have the blue:violet:red compounds present in a solids weight ratio of 100:35-45:40-50.
Other useful lyotropic liquid crystal formulations include the red dichroic dye compounds of structure R, the blue dichroic dye compounds of structure B, and the yellow dichroic dye compounds of structure Y.
The dichroic dye compounds, described herein, form a lyotropic liquid crystal phase can be dissolved in a useful solvent, such as water (or aqueous solvent). The dichroic dye compounds may be present in the solution in a concentration range in which a lyotropic liquid crystal is formed. The dichroic dye compounds may be present in the solution in an amount from about 1% wt to about 40% wt or from about 2% wt to about 25% wt or from about 5% wt to about 18% wt. or about 12% wt.
The dichroic dye compounds may form a lyotropic liquid crystal solution that may be shear-coated onto a substrate and dried to form the grey linear polarizer described herein. After the shear coating step, the coated solution is dried to remove the solvent (such as water) and form a polarizer or linear polarizer (optical coating layer). The optical coating layer may be stabilized by converting it to a water-insoluble layer. This conversion can be accomplished by ion exchange of mono-valent ions with di-valent or tri-valent ions. After the ion exchange, at least some of the dichroic dyes would contain cations selected from the following: Sr2+, Mg2+, Ba2+, Al3+, La3+, Ce3+, Fe3+, Cr3+, Mn2+, Cu2+, Zn2+, Pb2+, Ca2+, Ni2+, Co2+, or Sn2+.
The substrate 14 may be glass or a polymer layer such as a polyolefin (polyethylene terephthalate (PET) or polyethylene naphthalate (PEN)), polycarbonate (PC), polyimide (PI), triacetylcellulose (TAC), cyclic olefin polymer (COP), optically clear adhesive (OCA) film, antireflection (AR) film, and the like. Glass substrates may form an element of a liquid crystal display panel or an OLED display panel. The glass substrate may have a reduced thickness such as a 1000 micrometers or less or 500 micrometers or less. In embodiments where the substrate 14 is a polymer layer, the polymer layer may be a flexible film layer that may be processed in a roll-to-roll manufacturing process.
In some embodiments, the coatable polymer polarizer layer 12 may be coated on an adhesive layer such as an OCA film.
In some embodiments, the polarizing article 20 is a circular polarizer. As shown in
All chemical materials listed herein (and not specifically mentioned by source) are commercially available from Sigma-Aldrich (USA).
Examples of synthesis of four different dichroic dye compounds are shown below.
Blue Dichroic Dye Compound (Structure B)
20 g of Indanthrone was added to a mixture of 40 ml Fuming Sulfuric Acid 20% SO3 and 60 ml Chlorosulfonic Acid, well agitated, heated to 40-55 degrees Celsius and kept at temperature for 3 days. Then the resulted reaction mass was quenched with water and ice, neutralized with 28-30% Ammonium hydroxide and ultrafiltered to remove ammonium sulfate. The retentate was microfiltered and concentrated. Yield 25 g on solid basis. Resulting product was:
wherein:
X is an ammonium sulfonate, and 1≤m≤4;
Z is a Cl (chloro) group, and 0≤p≤2; and
m+p≤4.
A lyotropic liquid crystal solution in water of the Blue dichroic dye compound (Structure B) was prepared and shear-coated and dried on a glass substrate. Transmittance spectra were taken for two orientations of the sample (shear-coating direction perpendicular (Tper) and parallel (Tpar) to the direction of the polarized light incident on the sample). The Dichroic ratio (Kd) was calculated as ln(Tper)/ln(Tpar).
Red Dichroic Dye Compound (Structure R)
150 g of pure starting material was prepared by crystallization of commercially available Vat Red 15 from concentrated Sulfuric acid. This material was mixed with 450 ml of Fuming Sulfuric Acid 20% SO3, heated to 36-46 degrees Celsius and kept at temperature for 3 hrs. The reaction mass was quenched with water and Ammonium Hydroxide, the resulted precipitate was isolated, dissolved in water and ultrafiltered. The retentate was microfiltered and concentrated. Yield 180 g on solid basis. Resulting product was:
and a trans-isomer of structure R, wherein, X is an ammonium sulfonate.
A lyotropic liquid crystal solution in water of the Red dichroic dye compound (Structure R and its trans-isomer) was prepared and shear-coated and dried on a glass substrate. Transmittance spectra were taken for two orientations of the sample (shear-coating direction perpendicular (Tper) and parallel (Tpar) to the direction of the polarized light incident on the sample). The Dichroic ratio (Kd) was calculated as ln(Tper)/ln(Tpar).
Yellow Dichroic Dye Compound (Structure Y)
2 g of Vat Orange 9 was added to a mixture of 2 ml of Fuming Sulfuric Acid 20% SO3 and 4 ml of Chlorosulfonic Acid, well agitated, heated to 70-90 degrees Celsius and kept at temperature for 30 hours. The reaction mass was quenched with 95% Sulfuric acid and water, neutralized with Ammonium Hydroxide and ultrafiltered to remove inorganic salts. The retentate was microfiltered and concentrated. Yield 2.2 g on solid basis. Resulting product was:
wherein:
X is an ammonium sulfonate, and 1≤m≤4;
Z is a Cl (chloro) group, and 0≤p≤2;
and m+p≤6.
A lyotropic liquid crystal solution in water of the Yellow dichroic dye compound (Structure Y) was prepared and shear-coated and dried on a glass substrate. Transmittance spectra were taken for two orientations of the sample (shear-coating direction perpendicular (Tper) and parallel (Tpar) to the direction of the polarized light incident on the sample). The Dichroic ratio (Kd) was calculated as ln(Tper)/ln(Tpar).
Violet Dichroic Dye Compound (Structure Vc)
3.25 g of Isoviolanthrone (TCI America) was mixed with 36 ml Fuming Sulfuric Acid 30% SO3 and agitated overnight. Then the reaction mass was fortified by addition of 47 ml Fuming Sulfuric Acid 65% SO3 and heated to 75-80 degrees Celsius. The reaction time at temperature was 7 hrs. Then the reaction mass was quenched with water, neutralized with Ammonium Hydroxide and ultrafiltered to remove inorganic salts. The retentate was microfiltered and concentrated. Yield 1.7 g on solid basis. Resulting product was:
wherein:
X is an ammonium sulfonate, and 1≤m≤4;
Y is a S(═O)2 (sulfone) group, and 0≤n≤2;
Z is a OH (hydroxy) group, and 0≤p≤4;
R is an O (oxo) group, and 0≤q≤4; and
m+p+q≤6.
Violet Dichroic Dye Compound (Structure Va)
2 g of Pigment Black (BASF) was mixed with 8 ml Fuming Sulfuric Acid 30% SO3 and agitated overnight. Then the acid was fortified by addition of 6 ml Fuming Sulfuric Acid 65% SO3 and heated to 61-65 degrees Celsius. The reaction time at temperature was 8 hrs. Then the reaction mass was quenched with water, neutralized with Ammonium Hydroxide and ultrafiltered to remove inorganic salts. The retentate was microfiltered and concentrated. Yield 2.2 g on solid basis. Resulting product was:
or a cis-isomer of Structure Va, wherein:
X is an ammonium sulfonate, and 1≤m≤4;
Y is a S(═O)2 (sulfone) group, and 0≤n≤2;
Z is a OH (hydroxy) group, and 0≤p≤4;
R is an O (oxo) group, and 0≤p≤4; and
m+p+q≤6.
A lyotropic liquid crystal solution in water of the Violet dichroic dye compound (Structure Va and cis-isomer of Structure Va) was prepared and shear-coated and dried on a glass substrate. Transmittance spectra were taken for two orientations of the sample (shear-coating direction perpendicular (Tper) and parallel (Tpar) to the direction of the polarized light incident on the sample). The Dichroic ratio (Kd) was calculated as ln(Tper)/ln(Tpar).
Formulation
Dichroic dye compounds Blue (Structure B), Red (Structure R and trans-isomer of Structure R), Yellow (Structure Y) and Violet (Structure Va and its cis-isomer) are mixed in a certain ratio that defines the spectral performance of the coating. In order to ensure mixing of the components on molecular level the total concentration of the initial mixture is less than 2% solids so that all components are in an isotropic state. For example, in order to prepare 100 mL of the formulation comprising B, Va (including its cis-isomer) and R (including its trans-isomer) components in the solid to solid ratio of 18:7:8 correspondingly targeting 12% solid content one takes 131 mL of the 5% Structure B, 51 mL of the 5% Structure Va (including its cis-isomer), 58 mL of the 5% Structure R (including its trans-isomer) and adds 400 mL of water. Resulting solids concentration is approximately 1.9% by weight.
Then the mixture is filtered through a 0.45 micrometer nylon filter and concentrated to 12% solids by weight using any available method including but not limited to rotary evaporating machines or an ultrafiltration setup.
The final mixture is filtered once again through a 0.45 micrometer nylon filter.
Coating
The Grey Polarizer (GP) coating liquid can be applied to a variety of substrates.
Glass—LCD grade clean glass substrates do not require additional treatment and GP coating liquid can be applied directly to it. One cleaning procedure is as follows. Glass is sonicated in cleaning solution e.g., Alconox cleaner (Alconox Inc.) or similar at 30 degrees Celsius for 30 min. Then soaked in tap water for 15 min followed by the rinsing with deionized water. After that the glass sonicated in water solution of NaOH (10% wt) at 30 degrees Celsius for 30 min. Rinsed again with deionized water and finally dried with compressed air.
TAC—TAC surface is activated via a saponification process in order to ensure uniform wetting and adhesion. TAC film piece is soaked in water for 10 min, then rinsed under water stream. Then the film is placed into water solution of NaOH (6% wt.) at 55 degrees Celsius for 2 min. Thoroughly rinsed with deionized water. Placed on a flat, clean soft cloth and dried with a flow of compressed air. Treated TAC film can be used immediately after this process or later up to 3 days.
COP, PC, PET—Due to low surface energy these plastic substrates require pre-treatment such as a corona or plasma treatment. Adhesion of the coating to the substrates is provided by a primer (MICA A-131-X waterborne primer). The substrate sheet was placed onto a solid flat surface and corona treated a few times at a rate of about 1 cm/s (for a hand-held corona treater BD-20AC, Electro-Technic Products). Immediately after corona treatment the substrate was primed by coating the primer solution at 1% solids using Mayer rod #1.5. Sufficient drying of the primer coated with Mayer rod #1.5 takes place in about 5 seconds under ambient conditions.
TAC and glass substrates can also be primed to make adhesion stronger.
GP Coating
Substrate was pre-treated according to the above examples. Then the substrate was secured onto a solid flat surface. GP formulation of 12% solid content was shear-coated using Mayer rod #4. It takes about 0.5-1 mL to cover an A5 size sheet. The best results are achieved when the GP coating is dried undisturbed under ambient conditions. These coating steps gave approximately 800 nm physical thickness of polarizing plate. For thinner or thicker coatings, a different Mayer rod size can be used.
Testing
Thus, embodiments of COATABLE GREY POLARIZER are disclosed.
All references and publications cited herein are expressly incorporated herein by reference in their entirety into this disclosure, except to the extent they may directly contradict this disclosure. Although specific embodiments have been illustrated and described herein, it will be appreciated by those of ordinary skill in the art that a variety of alternate and/or equivalent implementations can be substituted for the specific embodiments shown and described without departing from the scope of the present disclosure. This application is intended to cover any adaptations or variations of the specific embodiments discussed herein. Therefore, it is intended that this disclosure be limited only by the claims and the equivalents thereof. The disclosed embodiments are presented for purposes of illustration and not limitation.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3208814 | Sievenpiper et al. | Sep 1965 | A |
| 4179395 | Cole, Jr. | Dec 1979 | A |
| 4278578 | Carpenter | Jul 1981 | A |
| 4605698 | Briden | Aug 1986 | A |
| 5067797 | Yokokura et al. | Nov 1991 | A |
| 5739296 | Gvon et al. | Apr 1998 | A |
| 5863113 | Oe et al. | Jan 1999 | A |
| 6002829 | Winston et al. | Dec 1999 | A |
| 6045894 | Jonza et al. | Apr 2000 | A |
| 6049428 | Khan et al. | Apr 2000 | A |
| 6144424 | Okuda et al. | Nov 2000 | A |
| 6174394 | Gvon et al. | Jan 2001 | B1 |
| 6322236 | Campbell et al. | Nov 2001 | B1 |
| 6399166 | Khan et al. | Jun 2002 | B1 |
| 6481864 | Hosseini et al. | Nov 2002 | B2 |
| 6563640 | Ignatov et al. | May 2003 | B1 |
| 6583284 | Sidorenko et al. | Jun 2003 | B1 |
| 6619553 | Bobrov et al. | Sep 2003 | B1 |
| 6734936 | Schadt et al. | May 2004 | B1 |
| 6841320 | Lazarev et al. | Jan 2005 | B2 |
| 6846522 | Bobrov et al. | Jan 2005 | B1 |
| 6847420 | Lazarev et al. | Jan 2005 | B2 |
| 6848897 | Lazarev et al. | Feb 2005 | B2 |
| 6876806 | Lazarev et al. | Apr 2005 | B2 |
| 6913783 | Lazarev et al. | Jul 2005 | B2 |
| 6942925 | Lazarev et al. | Sep 2005 | B1 |
| 6962734 | Nazarov et al. | Nov 2005 | B2 |
| 7015990 | Yeh et al. | Mar 2006 | B2 |
| 7025900 | Sidorenko et al. | Apr 2006 | B2 |
| 7026019 | Dutova et al. | Apr 2006 | B2 |
| 7031053 | Bobrov et al. | Apr 2006 | B2 |
| 7042612 | Lazarev et al. | May 2006 | B2 |
| 7045177 | Dutova et al. | May 2006 | B2 |
| 7053970 | Lazarev | May 2006 | B2 |
| 7084939 | Paukshto et al. | Aug 2006 | B2 |
| 7092163 | Bastawros et al. | Aug 2006 | B2 |
| 7106398 | Bobrov | Sep 2006 | B2 |
| 7108749 | Bobrov | Sep 2006 | B2 |
| 7110177 | Sugino et al. | Sep 2006 | B2 |
| 7113337 | Lazarev et al. | Sep 2006 | B2 |
| 7132138 | Lazarev | Nov 2006 | B2 |
| 7144608 | Paukshto | Dec 2006 | B2 |
| 7160485 | Nazarov et al. | Jan 2007 | B2 |
| 7166161 | Lazarev et al. | Jan 2007 | B2 |
| 7190416 | Paukshto et al. | Mar 2007 | B2 |
| 7204938 | Lazarev | Apr 2007 | B2 |
| 7211824 | Lazarev | May 2007 | B2 |
| 7267849 | Lazarev et al. | Sep 2007 | B2 |
| 7271863 | Paukshto et al. | Sep 2007 | B2 |
| 7291223 | Lazarev | Nov 2007 | B2 |
| 7297209 | Lazarev et al. | Nov 2007 | B2 |
| 7315338 | Yeh et al. | Jan 2008 | B2 |
| 7317499 | Paukshto et al. | Jan 2008 | B2 |
| 7324181 | Lazarev et al. | Jan 2008 | B2 |
| 7405787 | Paukshto et al. | Jul 2008 | B2 |
| 7450194 | Lazarev | Nov 2008 | B2 |
| 7456915 | Lazarev et al. | Nov 2008 | B2 |
| 7479311 | Bobrov | Jan 2009 | B2 |
| 7480021 | Rao et al. | Jan 2009 | B2 |
| 7554636 | Nakatsugawa | Jun 2009 | B2 |
| 7557876 | Lazarev et al. | Jul 2009 | B2 |
| 7651738 | Grodsky et al. | Jan 2010 | B2 |
| 7660047 | Travis et al. | Feb 2010 | B1 |
| 7733443 | Lazarev et al. | Jun 2010 | B2 |
| 7850868 | Matsuda et al. | Dec 2010 | B2 |
| 7888505 | Doutova et al. | Feb 2011 | B2 |
| 7889297 | Palto | Feb 2011 | B2 |
| 7911557 | Lazarev et al. | Mar 2011 | B2 |
| 7969531 | Li et al. | Jun 2011 | B1 |
| 8081270 | Lazarev | Dec 2011 | B2 |
| 8142863 | Palto | Mar 2012 | B2 |
| 8168082 | Matsuda et al. | May 2012 | B2 |
| 8189165 | Umemoto et al. | May 2012 | B2 |
| 8257802 | Inoue et al. | Sep 2012 | B2 |
| 8268937 | Bos et al. | Sep 2012 | B2 |
| 8305350 | Chang | Nov 2012 | B2 |
| 8404066 | Goto et al. | Mar 2013 | B2 |
| 8416376 | Palto | Apr 2013 | B2 |
| 8512824 | Kasianova et al. | Aug 2013 | B2 |
| 8551357 | Miyazaki et al. | Oct 2013 | B2 |
| 10023123 | Takada | Jul 2018 | B2 |
| 20030179363 | Wang | Sep 2003 | A1 |
| 20040146663 | Paukshto | Jul 2004 | A1 |
| 20070064417 | Hatanaka et al. | Mar 2007 | A1 |
| 20070110378 | Zarian | May 2007 | A1 |
| 20070159580 | Yoshioka | Jul 2007 | A1 |
| 20070279934 | Kim et al. | Dec 2007 | A1 |
| 20070285599 | Oxude | Dec 2007 | A1 |
| 20080042154 | Wano | Feb 2008 | A1 |
| 20080074595 | Nakatsugawa | Mar 2008 | A1 |
| 20080252974 | Futamura | Oct 2008 | A1 |
| 20080278673 | Yoshioka | Nov 2008 | A1 |
| 20080298067 | Chu | Dec 2008 | A1 |
| 20080304283 | Parker et al. | Dec 2008 | A1 |
| 20090269591 | Kasianova et al. | Oct 2009 | A1 |
| 20100039705 | Doutova et al. | Feb 2010 | A1 |
| 20100085521 | Kasianova et al. | Apr 2010 | A1 |
| 20100149471 | Palto | Jun 2010 | A1 |
| 20100190015 | Kasianova | Jul 2010 | A1 |
| 20100215954 | Kuzmin et al. | Aug 2010 | A1 |
| 20110149206 | Lazarev | Jun 2011 | A1 |
| 20110149393 | Nokel et al. | Jun 2011 | A1 |
| 20110182084 | Tomlinson et al. | Jul 2011 | A1 |
| 20110255305 | Chen et al. | Oct 2011 | A1 |
| 20120013982 | Kharatiyan | Jan 2012 | A1 |
| 20120081784 | Lazarev | Apr 2012 | A1 |
| 20120099052 | Lazarev | Apr 2012 | A1 |
| 20120113380 | Geivandov et al. | May 2012 | A1 |
| 20120113678 | Cornelissen et al. | May 2012 | A1 |
| 20120113680 | Nakai et al. | May 2012 | A1 |
| 20120244330 | Sun | Sep 2012 | A1 |
| 20130003178 | Lazarev | Jan 2013 | A1 |
| 20130011642 | Sun | Jan 2013 | A1 |
| 20130070480 | Griffin et al. | Mar 2013 | A1 |
| 20130251947 | Lazarev | Sep 2013 | A1 |
| 20140133177 | Miller et al. | May 2014 | A1 |
| 20140140091 | Vasylyev | May 2014 | A1 |
| 20140186637 | Kasianova et al. | Jul 2014 | A1 |
| 20140320961 | Lazarev | Oct 2014 | A1 |
| 20140322452 | Kasyanova et al. | Oct 2014 | A1 |
| 20140350214 | Kharatiyan | Nov 2014 | A1 |
| 20150086799 | Kasyanova et al. | Mar 2015 | A1 |
| 20150123911 | Poliakov et al. | May 2015 | A1 |
| 20150266999 | Kuzmin et al. | Sep 2015 | A1 |
| 20160200255 | Takada | Jul 2016 | A1 |
| 20170184769 | Kim | Jun 2017 | A1 |
| 20190391433 | Hashimoto | Dec 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 0489951 | Jun 1992 | EP |
| 06235917 | Aug 1994 | JP |
| 2010-091984 | Apr 2010 | JP |
| WO 2010-064194 | Jun 2010 | WO |
| WO 2012-007923 | Jan 2012 | WO |
| WO 2013-119922 | Aug 2013 | WO |
| WO 2014174381 | Oct 2014 | WO |
| Entry |
|---|
| Gribkova “Chemical synthesis of polyaniline in the presence of poly(amidosulfonic acids) with different rigidity of the polymer chain,” Apr. 2011, Polymer 52(12):2474-2484. |
| Kasianova, “New Transparent Birefringent Material for Interference Polarizer Fabrication” 2006 XV International Symposium Advanced Display Technologies (ADT '06), Moscow, Russia, 1-6. |
| Konoshchuk, “Physicochemical Properties of Chemically and Mechanochemically Prepared Interpolymer Complexes of Poly(3,4-Ethylenedioxythiophene) with Polyamidosulfonate Dopants,” Jan. 2014, Theoretical and Experimental Chemistry 50(1): 21-28 (Russian Original, Jan. 2014). |
| Koo et al., “Preparation and humidity-sensitive properties of novel photocurable sulfonated polyimides,” Macromolecular Research, Dec. 1, 2012, 20(12):1226-1233. |
| Li, “Design Optimization of Reflective Polarizers for LCD Backlight Recycling” Aug. 2009 J Display Tech., 56(8): 335-340. |
| Number | Date | Country | |
|---|---|---|---|
| 20190235144 A1 | Aug 2019 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62624407 | Jan 2018 | US | |
| 62652591 | Apr 2018 | US |