This application claims priority under 35 U.S.C. § 119 to Swedish Application No. 0300175-7 filed in Sweden on Jan. 24, 2003; the entire contents of which is hereby incorporated by reference.
The present invention relates to a coated cemented carbide cutting tool insert for the machining in general of steel in applications having high requirements on wear resistance and toughness behaviour of the cutting edge. The tool is particularly suitable for the turning of stainless steels.
When cemented carbide cutting tools are used in the machining of steels, the tool is worn by different mechanisms such as abrasive and chemical wear, chipping and fracturing of the cutting edge. The cutting of stainless steel is considered to be a particularly difficult machining operation since in addition to the above mentioned wear mechanisms, adhesive wear is also prominent. Adhesive wear is obtained when smearing materials like stainless steels continuously adhere to and tear off material from the cutting edge during the cutting operation. A short tool life is therefore very frequent when machining stainless steels. Furthermore, when cutting stainless steels at high cutting speeds, the thermal energy transferred to the cutting edge is considerable and the tool edge may partly or entirely deform plastically. This mode of deterioration of the cutting edge is known as plastic deformation wear. A large requirement of plastic deformation resistance is in clear contrast to a large requirement of edge toughness.
Multilayer coatings comprising first and second coating layers of different materials which are alternately laminated on the substrate, each of the first coating layers having a first thickness and each of the second coating layers having a second thickness are known. The two layers should preferably have a different crystal structure and/or at least different lattice spacings. One example of such a structure is when the Al2O3 growth periodically is interrupted by a short TiN deposition process resulting in a (Al2O3+TiN)x multilayer structure see e.g. Proceedings of the 12th European CVD Conference page pr.8–349. GB 2048960A discloses a multilayer coating with a multiplicity of alternating layers of 0.02 to 0.1 μm consisting of hard material of different compositions. U.S. Pat. No. 4,599,281 discloses a multilayer coating with alternating layers of an aluminium-boron mixed oxide and another oxide layer of e g Ti(C,N,O). Dreyer and Kolaska, Metals Society (Book 278), London, England (1982) 112–117 report an A—O—N multilayer. In U.S. Pat. No. 4,984,940 Bryant et al. disclose a cutting insert composed of a cemented carbide substrate with 6.1–6.5 wt % cobalt, a coating including a base layer of titaniumcarbonitride followed by a multilayered coating consisting of a plurality of alumina layers. A cemented carbide substrate with a coating comprising 6–8 alumina layers is also claimed in U.S. Pat. No. 5,700,569. WO 99/58738 describes a tool consisting of a hard wear resistant substrate and a CVD multilayer of about 50 layers. EP-A-1103635 claims a cutting tool consisting of a cemented carbide substrate with 9.0–10.9 wt % cobalt and a coating comprising a medium temperature CVD (MTCVD) deposited TiCN-layer and a multilayer composed of totally 7–41 layers of α-alumina and TiN or Ti(C,N). EP-A-1245698, EP-A-1245700, and EP-1209255 also relate to multilayer coatings.
Smoothing of coatings by mechanical post treatment in order to e g minimize the friction between the tool and the workpiece is disclosed in EP-A-127416, EP-A-298729, EP-A-693574 and EP-A-683244.
It is an object of the present invention to provide a cutting tool insert able to simultaneously withstand all the above mentioned wear modes.
It is a further object of the present invention to eliminate the deficiencies of prior art tool products and to provide a high performance cutting tool.
It is a still further object of the present invention to provide a tool with excellent cutting performance in demanding stainless steel turning operations.
In the aspect of the present invention, there is provided a coated cemented carbide cutting tool insert, said coating comprising a first, innermost layer system of at least two layers of TiCxNyOz with x+y+z≦1; and a second multilayer system comprising from about 5 to about 31 alternating layers of Al2O3 and TiCxNyOz (x+y+z≦1), the Al2O3-layers having an individual layer thickness of <0.5 μm and the TiCxNyOz-layers from about 0.01 to about 0.2 μm with a total thickness of the multilayer from about 1.0 to about 4.0 μm, and wherein the multilayer is exposed along the edge line and into the rake and flank face, such that the exposure on the rake face (a) is greater than about 0.03 and less than about 0.9 mm, the exposure on the flank face (b) is greater than about 0.02 and less than about 0.2 mm and a>b.
A.=TiN,
B.=columnar Ti(C,N),
C.=TiN,
D.=multilayer (Al2O3+TiN)6Al2O3 and
E.=TiN+TiC+TiN.
More specifically, the invention relates to a WC+Co-based cemented carbide substrate with additions of cubic carbides, a specific grain size range of the WC grains, a specific composition range of WC+Co and a coating on the cemented carbide substrate including an innermost thin layer of equiaxed TiCxNyOz followed by a layer of columnar TiCxNyOz, a thin layer of equiaxed TiCxNyOz, a multilayer with a periodic variation of TiCxNyOz and Al2O3 layers (x+y+z≦1) and an outermost layer of TiCxNy (x+y≦1). At least the non-oxide outermost layer in areas in direct contact with material from the work-piece around the cutting edge is missing.
The composition of the cemented carbide substrate should be from about 7 to about 10.5 wt % Co, preferably from about 8.0 to about 9.5 wt % Co, and from about 0.2 to about 1.6 wt % cubic carbides, preferably from about 0.4 to about 1.0 wt % cubic carbides of the metals Ta, Nb and Ti and possibly other carbides of the elements from group IVb, Vb or VIb of the periodic table and balance tungsten carbide (WC). The preferred average grain size of the WC is from about 1.5 to about 3.5 μm, preferably from about 1.9 to about 2.1 μm.
In an alternative embodiment, the cemented carbide substrate has a cubic carbide depleted and binder enriched volume near the surface. The measured distance from the surface should be from about 5 to about 50 μm until the end of the cubic carbide depletion. In this embodiment the composition comprises from about 7.0 to about 10.5 wt % Co and from about 4.0 to about 9.0 wt % cubic carbides and balance tungsten carbide (WC). Said cubic carbides may contain substantial amounts of N and O such that certain microstructural constituents should be referred to as e.g. carbonitride or oxycarbonitride. The cubic carbides are preferably Nb, Ta and Ti but may include carbides of elements from group IVb, Vb or VIb of the periodic table. The amount of N should be in the range of from about 0.01 to about 0.2 wt %.
The hard and wear resistant refractory coating (
The outermost part of the coating is missing around the edge such that this area corresponds to the chip contact on the rake side and the contact with the work piece on the flank side. Most preferably this uncoated area correspond to the primary land on the rake side when a primary land exists on the geometry at hand such that the coating is missing a distance from a point defined in
The removal of the outermost layer (E) at the edge-line will expose the Al2O3 layers in layers along the edge line. The edge-line is defined as the edge-honed portion of the cutting tool insert. The untreated edge-line is illustrated in
The cemented carbide body is mainly produced by mixing of powders, ball milling, spray-drying, some pressing method followed by sintering according to conventional methods and pre-treatment before coating.
In an alternative embodiment, the cemented carbide substrate is made in such a way that a cubic carbide depleted and binder phase enriched volume near the surface is obtained by sintering in vacuum after the addition of a small amount of nitrogen. The measured distance from the surface should be from about 5 to about 50 μm until the end of the cubic carbide depletion. In this embodiment, the composition comprises from about 7.0 to about 10.5 wt % Co and from about 4.0 to about 9.0 wt % cubic carbides and balance tungsten carbide (WC). Said cubic carbides may contain substantial amounts of N and O such that certain microstructural constituents should be referred to as, e.g., carbonitride or oxycarbonitride. The cubic carbides are preferably Nb, Ta and Ti but may include carbides of elements from group IVb, Vb or VIb of the periodic table. The amount of N in the substrate should be in the range of from about 0.01 to about 0.2 wt %.
The body is then coated with
G. the total thickness of layers A–E is from about 2.0 to about 8.0 μm.
The coating is mechanically post-treated to expose the multilayer along the edge line by a brushing, blasting, grinding operation or combinations thereof such that the areas on the rake and flank face with chip and work piece contact respectively have been treated.
In the preferred method, two nylon brushes containing SiC grains with settings and insert positioning such that one brush mainly brushes the rake side and the other mainly the flank side to achieve the desired properties on the flank and rake face of the insert.
The invention is additionally illustrated in connection with the following Examples, which are to be considered as illustrative of the present invention. It should be understood, however, that the invention is not limited to the specific details of the Examples.
The following inserts and examples are selected to exemplify the advantages with the invention. These examples are summarised in Table 1.
The presented inserts have been tested with identical conditions in each example.
Insert A. Cemented carbide turning inserts according to the invention with the composition 8.75 wt % Co, 1.17 wt % Ta, 0.29 wt % Nb and balance made up by WC and with an average WC grain size of 2.0 μm were coated with 0.5 μm TiN (innermost layer), 2.2 μm columnar Ti(C,N), and 0.5 μm equiaxed TiN, 2.2 μm (κ-Al2O3+TiN)6κ-Al2O3 multilayer with 250 nm thick κ-Al2O3-layers and 80 nm thick TiN-layers and an outermost layer of 0.5 μm TiN+TiC+TiN. The coating was post-treated along the edge line with nylon brushes containing SiC grains. The outermost coating was removed a=0.1 mm and b=0.05 mm into the rake and flank face.
Insert B. (Prior Art) Commercial cemented carbide turning inserts having 10.5 wt % Co, 1.16 wt % Ta, 0.28 wt % Nb and balance made up by WC and with an average grain size of 1.7 μm, was coated with an innermost 0.5 μm equiaxed TiN layer, 4.0 μm columnar Ti(C,N), 1.0 μm κ-Al2O3, and an outermost layer of 0.5 μm TiN+TiC+TiN. The coating was brushed along the edge line with nylon straw brushes containing SiC grains. The outermost coating was removed a=0.025 mm and b=0.05 mm along the edge line according to prior art.
Insert C. (Comparative) Cemented carbide turning inserts with the composition 9.15 wt % Co, 1.17 wt % Ta, 0.29 wt % Nb and balance made up by WC and with an average WC grain size of 1.7 μm, were coated with 0.5 μm TiN (innermost layer), 2.2 μm columnar TiCN, a 1.8 μm (κ-Al2O3+TiN)5κ-Al2O3 multilayer, and an outermost layer of 0.5 μm TiN. The coating was post-treated along the edge line with nylon brushes containing SiC grains. The outermost coating was removed a=0.025 mm and b=0.05 mm along the edge line, according to prior art.
Insert D. (Comparative) Identical substrates to C were coated with 0.5 μm TiN (innermost layer), 2.3 μm columnar Ti(C,N), a 1.9 μm (κ-Al2O3+TiN)3κ-Al2O3 multilayer, and an outermost layer of 0.5 μm TiN. The coating was post-treated along the edge line with nylon brushes containing SiC grains. The outermost coating was removed a=0.025 mm and b=0.05 mm along the edge line according to prior art.
Insert E. (Prior Art) Identical substrates to C were coated with an innermost 0.5 μm equiaxed TiN layer, 2.2 μm columnar Ti(C,N), 1.5 μm κ-Al2O3, and an outermost layer of 0.5 μm TiN+TiC+TiN. The outermost coating was removed a=0.025 mm and b=0.05 mm along the edge line according to prior art.
Insert F. Cemented carbide turning inserts having 7.5 wt % Co, 2.72 wt % Ta, 0.44 wt % Nb, 1.83 wt % Ti, 0.09 wt % N and balance made up by WC and with an average grain size of 2.0 μm and with a binder phase enriched and cubic carbide free zone 26 μm from the surface were coated with 0.5 μm TiN (innermost layer), 2.2 μm columnar Ti(C,N), and 0.5 μm equiaxed TiN, 2.2 μm (κ-Al2O3+TiN)6κ-Al2O3 multilayer and an outermost layer of 0.5 μm TiN+TiC+TiN.
The coating was post-treated along the edge line with nylon brushes containing SiC grains. The outermost coating was removed a=0.1 mm and b=0.05 mm into the rake and flank face.
Insert G. (Prior Art) Commercial cemented carbide turning inserts having 7.5 wt % Co, 2.72 wt % Ta, 0.44 wt % Nb, 1.83 wt % Ti, 0.09 wt % N and balance made up by WC and with an average grain size of 2.0 μm and with a binder phase enriched and cubic carbide free zone 26 μm from the surface were coated with an innermost 0.5 μm equiaxed TiN layer, 7.5 μm columnar Ti(C,N), 1.2 μm κ-Al2O3, and an outermost layer of 0.5 μm TiN+TiC+TiN.
The coating was brushed along the edge line with nylon straw brushes containing SiC grains. The outermost coating was removed a=0.025 mm and b=0.05 mm along the edge line as disclosed in EP-A-693574.
Inserts from A and B were tested in a turning operation.
Comment: Tool life criterion was maximum flank wear 0.3 mm of the cutting edge line. The wear develops irregularly due to local plastic deformation. This example shows the improvement in plastic deformation resistance.
Inserts from A and B were tested in a turning operation.
Comment: The wear in this test was flank wear, thermal cracks, chipping. The tool-life-determining criterion is chipping i.e. edge toughness. Consequently it shows improved edge toughness in combination with maintained properties in other wear modes.
Inserts from A and B were tested in a turning operation.
Comment: The criterion in this test is working through a full item taking total time in cut 6.2 min without showing excessive flank wear or edge damage. The critical wear criteria are flank wear and plastic deformation in combination.
The insert according to the invention shows improvements in these respects.
Inserts from A and B were tested in a turning operation.
Comment: This test shows a clear improvement compared to prior art. It is however difficult in this example to determine one single critical wear but it can be described as a combination of flank wear, flaking on rake and edge toughness.
Inserts from A and B were tested in a turning operation.
Comment: This test shows improvement in toughness since the main wear criterion is edge toughness in this demanding application.
Inserts from C and D were tested in a turning operation.
Comment: This example shows improved flaking resistance compared to the reference implying the importance of alumina layer thickness.
Inserts from C and E were tested in a turning operation.
Comment: Main wears are notch wear of the cutting depth and chipping outside the part of the edge in cut.
The example shows that the thin multilayer coating adds edge toughness compared to a coating according to prior art.
Inserts from C and E were tested in a turning operation.
Comment: Tool life criterion was maximum flank wear 0.3 mm of the cutting edge line. The wear develops irregularly due to local plastic deformation. This example shows that the thin multilayer coating add plastic deformation resistance compared to a coating according to prior art in this operation.
Considering example 7 this shows an improvement in these contradictory properties.
Inserts from F and G were tested in a turning operation.
Comment: The critical wear criteria are flank wear and plastic deformation in combination in this test. The insert according to the invention shows improvement in these respects.
In conclusion it can be stated that from the result of the examples given above it is evident that by combining a cemented carbide substrate with the given composition, the selection of the multilayered coating with specific thicknesses and the special edge treatment a tool insert has been created with excellent cutting performance in that it combines much of what was believed to be contradictory properties as described in the introduction.
The principles, preferred embodiments and modes of operation of the present invention have been described in the foregoing specification. The invention which is intended to be protected herein, however, is not to be construed as limited to the particular forms disclosed, since these are to be regarded as illustrative rather than restrictive. Variations and changes may be made by those skilled in the art without departing from the spirit of the invention.
Number | Date | Country | Kind |
---|---|---|---|
0300175 | Jan 2003 | SE | national |
Number | Name | Date | Kind |
---|---|---|---|
4599281 | Schintlmeister et al. | Jul 1986 | A |
4984940 | Bryant et al. | Jan 1991 | A |
5700569 | Ruppi | Dec 1997 | A |
Number | Date | Country |
---|---|---|
0127416 | Dec 1984 | EP |
0298729 | Jan 1989 | EP |
0683244 | Nov 1995 | EP |
0693574 | Jan 1996 | EP |
1103635 | May 2001 | EP |
1209255 | May 2002 | EP |
1245698 | Oct 2002 | EP |
1245700 | Oct 2002 | EP |
2048960 | Dec 1980 | GB |
WO9958738 | Nov 1999 | WO |
Number | Date | Country | |
---|---|---|---|
20040180241 A1 | Sep 2004 | US |