Coated electrode

Abstract

A coated electrode having a flux formulation that is a function of the diameter of the electrode wire. The electrode wire is made from a nickel-chromium-cobalt-molybdenum-aluminum alloy. The flux coating contains differing amounts of manganese, iron and columbium depending on the diameter of the core wire.

Description

TECHNICAL FIELD

This invention relates to the art of welding in general and more particularly to a coated welding electrode especially adapted for nickel based alloy welding.

BACKGROUND ART

Nickel base alloys have long enjoyed considerable usage as structural materials and have been found to be particularly advantageous when employed in high temperature environments such as those associated with nuclear reactors, jet engines and the like. These nickel alloys exhibit excellent high temperature strength characteristics as well as high resistance to the fluctuating stresses and shock experienced at elevated temperatures. Moreover, many nickel base alloys are highly resistant to corrosion normally associated with a wide variety of hot gases and corrosive liquids.

In particular, the assignee of this invention, produces a patented solid-solution nickel-chromium-cobalt-molybdenum-aluminum alloy called INCONEL alloy 617. (INCONEL is a trademark of Huntington Alloys, Inc. Huntington, W. Va.). See U.S. Pat. No. 3,859,060. This alloy exhibits an excellent combination of high temperature strength and oxidation resistance characteristics. INCONEL alloy 617 also has excellent resistance to a wide range of corrosive environments and it is readily formed and welded by conventional techniques.

Inasmuch as this alloy (as well as other alloys) is ultimately joined to something, we attempted to develop a welding electrode using the alloy itself as the core wire. Accordingly, we initially employed standard production INCONEL alloy 617 as the core wire for the electrode. In this manner, the problems of introducing and producing a new and different electrode solely for welding electrodes were to be eliminated.

Our goal was to develop a welding electrode having a deposit that exhibited the same tensile stress, rupture and oxidation properties as those of the wrought alloy product. Moreover, it was expected that the electrode would exhibit good operability and produce sound weldments.

Initially, it was determined that such an electrode could be produced. However, as developmental work proceeded, it was discovered that an exact duplication of the alloy composition when used in electrode form did not produce defect-free weldments when the electrode was used out of position. Indeed, close examinations of the resulting deposit disclosed evidence of undesirable microfissuring. Since this problem occurs more often than not, an electrode capable of producing defect-free weldments had to be developed.

SUMMARY OF THE INVENTION

There is provided a coated electrode having two slightly dissimilar flux formations; the composition of the flux coating being a function of the diameter of the core wire.

As was discussed previously, the core wire is made from a nickel-chromium-cobalt-molybdenum-aluminum alloy. The flux composition is similar to but not identical to the composition of the core wire. In particular, the percentage of two elements included in the flux, manganese and columbium, is adjusted to reflect the diameter of the core wire. The smaller diameter electrode will have a correspondingly higher percentage of manganese and columbium to combat the debilitating effects of microfissuring.

PREFERRED MODE FOR CARRYING OUT THE INVENTION

Broadly stated, the present invention contemplates the provision of a flux-coated welding rod having a core wire of a nickel base alloy and in combination therewith a special flux coating containing controlled amounts of columbium (niobium) and manganese. An important feature of the present invention is that the coated welding rod contains controlled amounts of columbium and manganese in a special balance with the other constituents of the coated welding rod together with a special control of aluminum in the core wire to produce an arc welding electrode having good arc behavior, slagging characteristics and resistance to hot weld cracking. In general, the columbium and manganese is present partly in the flux and partly in the core. The columbium may be replaced in part by tantalum. Indeed, most commercial sources of columbium usually contain tantalum.

The nominal chemical composition of the nickel base alloy welding wire (INCONEL alloy 617) is given in Table 1.

TABLE 1______________________________________(% by weight)______________________________________ Nickel 52.0 Chromium 22.0 Cobalt 12.5 Molybdenum 9.0 Aluminum 1.2 Carbon 0.07 Iron 1.5 Manganese 0.5 Silicon 0.5 Sulfur 0.008 Titanium 0.3 Copper 0.2______________________________________

It was found that it was possible to produce an electrode that met the requirements discussed above. A first deposit composition developed is that given in Table 2 for 5/32" (0.41 cm) and 3/16" (0.48 cm) diameter electrodes. However, later we found that this composition was not capable of producing defect-free weldments when used out of position. To remedy this situation columbium and higher levels of manganese were added to the deposit (via the flux coating) of the smaller diameter electrodes (3/32" [0.23 cm] and 1/8" [0.32 cm]--sizes that may ordinarily be used out of position). Thus, it was necessary to produce two slightly dissimilar flux formulations, one for the larger diameter electrodes and another with a higher manganese and columbian content for the smaller diameters.

The chemical analyses of deposits of the four sizes of electrodes are presented in Table 2. As can be seen, the difference in the larger and smaller sizes is in the levels of manganese and columbium. Iron content also differs because the columbium is added in the form of ferrocolumbium. Otherwise, the composition of the deposits are quite similar.

TABLE 2______________________________________AVERAGE CHEMICAL ANALYSIS - WELDINGELECTRODE DEPOSIT (IN WEIGHT PERCENT) 3/32"(.24 cm) and 5/32"(.41 cm) andElement 1/8"(.32 cm) 3/16"(.48 cm)______________________________________Carbon (C) .1 .1Manganese (Mn) 1.42 .64Iron (Fe) 1.16 .87Sulfur (S) .005 .004Silicon (Si) .5 .47Copper (Cu) .05 .05Nickel (Ni) Bal BalChrome (Cr) 23.1 23.20Aluminum (Al) .21 .24Titanium (Ti) .09 .13Magnesium (Mg) <.001 <.001Cobalt (Co) 11.47 11.73Molybdenum (Mo) 9.24 9.32Columbium-Tantalum (Cb + Ta) .52 .02Boron (B) <.002 .001Phosphorous (P) .005 .004______________________________________

A silicate type binder is used with the flux composition to provide a durable and hard coating after drying and baking. This silicate type binder may be a solution of sodium silicate and/or potassium silicate. A preferred binder formulation is given in Table 3.

TABLE 3______________________________________BINDER FORMULATION RangeIngredient Broad (%) Preferred (%)______________________________________Sodium Silicate 40-98 95Potassium Silicate 0-50Lithium Silicate 0-4 4Water 0-6 1______________________________________

In preparing the flux coating from the dry ingredients and binder, the binder is added to the mixture of dry ingredients, together with additional water as needed to obtain a consistency suitable for extrusion on the core wire. The flux coating can be applied to the core wire in any suitable manner, e.g., by an extrusion process and then dried on the wire surface by suitable drying and/or baking. This results in a hard adherent coating of high mechanical strength relatively free from impairment under normal handling conditions. A satisfactory drying or baking treatment of the flux and binder mixture comprises raising the temperature gradually up to about 600.degree. F. (316.degree. C.), and holding at that temperature for about 2 hours.

A flux coating formulation is shown in Table 4.

TABLE 4______________________________________FLUX COATING FORMULATION Range Pre-Ingredient Broad (%) Ferred (%)______________________________________Calcium Carbonate 10-50 28Cryolite 10-50 28Titania 5-35 9Silica 0-30 3Wollastonite 0-15 3*Chromium Metal 5-20 10***Manganese Metal 2-15 3***Molybdenum Metal 0-8 4**Nickel-Carbon Composite 0-2 1Collodial Clays & Extrusion Aids 0-8 3High Melting Oxides (e.g., MgO orZrO.sub.2) 0-12 4*Columbium Metal 0-8 4______________________________________ *May be added as pure metals or in ferroalloy form. **Depends on form of material used. Number given is for pure metal.

Tensile results from longitudinal, all-weld-metal specimens of deposits of the two formulations are presented in Table 5. It should be appreciated that there appears to be very little difference in properties of the deposits of the two formulations.

TABLE 5______________________________________WELDING ELECTRODE 3/32" (.24 cm) &1/8" (.32 cm) DIAMETERS; ALL-WELD-METAL SPECIMENSTest Tensile Yield Elonga- ReductionTemperature Strength Strength tion of Area.degree.F. (.degree.C.) ksi (MPa) ksi (MPa) % %______________________________________RoomTemperature 119.4 (823) 72.6 (500) 34 26.8RoomTemperature 118.0 (813) 75.0 (517) 35 27RoomTemperature 118.7 (818) 73.7 (508) 34 28RoomTemperature 119.9 (827) 73.7 (508) 37 38 1000 (538) 92.2 (636) 55.4 (382) 38.3 45.9 1200 (649) 85.8 (591) 51.6 (356) 34.9 26.1 1400 (760) 72.3 (498) 55.1 (379) 33.6 41.3 1600 (871) 37.9 (261) 36.5 (252) 36.6 38.9 1800 (982) 23.0 (158) 22.8 (157) 26.4 28.8 2000 (1093) 12.7 (87.5) 12.7 (87.5) 12.8 23.3______________________________________WELDING ELECTRODE 5/32" (.41 cm) &3/16" (.48 cm) DIAMETERS; ALL-WELD-METAL SPECIMENSRoomTemperature 116.7 (804) 72.5 (499) 40 39.8RoomTemperature 118.7 (818) 72.9 (503) 39 35.7 1000 (538) 92.1 (635) 56.8 (391) 40.0 44 1200 (649) 89.3 (615) 56.3 (388) 38.0 45 1400 (760) 75.2 (518) 58.7 (405) 23.6 19 1600 (871) 45.5 (314) 41.3 (285) 28.0 31 1800 (982) 24.7 (170) 23.3 (161) 33.0 36 2000 (1093) 16.6 (114) 16.6 (114) 13.5 12.2______________________________________

Results of stress rupture tests from the two formulations are presented in Table 6. As before, no consistent differences between the two formulations are evident. It should be observed that the stress to rupture the electrode is slightly less than that of the base metal at all temperatures except 1600.degree. F. However, these differences are small. It is felt that the rupture strength of the electrode should be adequate for most applications. Joint efficiencies calculated from this data are presented in Table 7.

TABLE 6______________________________________STRESS RUPTURE DATA WELDING ELECTRODE 3/32"(.24 cm) & 1/8" (.32 cm) DIAMETERS;ALL-WELD-METAL SPECIMENS Rupture Elonga- ReductionTest Temp. Stress Life tion of Area.degree.F. (.degree.C.) psi (MPa) hrs. % %______________________________________1200 (649) 58,000 (399) 41.7 16.2 17.0 50,000 (345) 107.7 11.3 23.81400 (760) 30,000 (206) 21.0 15.2 18.3 24,000 (165) 81.8 0.2 10.71600 (871) 13,000 (89.6) 177.1 17.5 21.0 13,000 (89.6) 170.1 11.5 16.0 13,000 (89.6) 166.9 6.5 14.0 9,700 (66.9) 1036.3 9.3 13.8 9,600 (66.1) 1137.2 5.8 8.31800 (982) 5,900 (40.7) 143.1 3.9 10.5 4,300 (29.6) 498.8 7.5 7.51832 (1000) 3,000 (20.6) 651.8 11.7 7.0 5,000 (34.5) 125.8 10.9 0.8 5,000 (34.5) 130.2 5.4 4.42000 (1093) 2,700 (18.6) 42.9 7.3 2.5 1,800 (12.4) 108.2 8.9 1.0______________________________________WELDING ELECTRODE 5/32" (.41 cm) &3/16" (.48 cm) DIAMETERS; ALL-WELD-METAL SPECIMENS Rupture Elonga- ReductionTest Temp. Stress Life tion of Area.degree.F. (.degree.C.) psi (MPa) hrs. % %______________________________________1200 (649) 58,000 (399) 19.5 10.5 19.5 50,000 (345) 59.8 7.5 8.5 47,000 (324) 108.6 6.6 5.0 42,000 (289) 211.4 7.1 8.01400 (760) 30,000 (306) 24.0 11.6 7.0 24,000 (165) 95.3 10.1 14.5 22,000 (152) 148.8 7.4 7.0 18,000 (124) 594.0 2.6 2.51600 (871) 13,000 (89.6) 131.9 4.7 6.0 13,000 (89.6) 165.3 5.4 2.3 9,700 (66.9) 803.1 3.7 7.6 8,500 (58.5) 824.4 10.7 7.01800 (982) 5,900 (40.7) 75.2 5.7 3.3 4,300 (29.6) 324.3 6.3 3.0 3,600 (24.8) 509.0 6.1 1.5 2,500 (17.2) 1602.1 5.8 0.91832 (1000) 3,000 (20.6) 406.1 9.0 0.5 5,000 (34.5) 94.8 2.7 3.02000 (1093) 2,700 (18.6) 28.8 7.4 2.5 1,800 (12.4) 69.5 0.8 0.1 1,500 (10.3) 138.6 5.0 1.5 1,000 (6.89) 354.8 9.6 1.5______________________________________ TABLE 7______________________________________CALCULATION OF JOINT EFFICIENCYStress to Rupturein 1000 hrs Welding INCONEL Joint EfficiencyTemp. Electrode alloy 617 Weld in INCONEL.degree.F. (.degree.C.) psi (MPa) psi (MPa) alloy 617______________________________________1200 (649) 40,000 (276) 48,000 (331) 831400 (760) 17,500 (121) 22,000 (151) 801600 (871) 8,600 (59.2) 8,400 (57.9) 1021800 (982) 3,400 (23.4) 3,600 (24.8) 942000 (1093) 680 (4.68) 1,500 (10.3) 45______________________________________

The stability of the deposit of the electrode is shown in Table 8. It is observed that while the weld material does show a loss of ductility and impact strength the loss is not of an extent that would render the weldment unserviceable.

TABLE 8______________________________________STABILITY DATA ROOM TEMPERATURE IMPACTSTRENGTH (CVN) AFTER EXPOSURE TO VARIOUSELEVATED TEMPERATURES Average Impact Strength Weld Deposit Base MetalExposure Exposure Small .phi.* Large .phi.* INCONELTemperature Time Electrode Electrode alloy 617.degree.F. (.degree.C.) hrs ft/lb (J) ft/lb (J) ft/lb (J)______________________________________As Welded- 39 (52) 49 (66) 187 (252)1200 (649) 500 21 (28) 27 (36) 49 (66) 1000 20 (27) 24 (32) 40 (54) 2000 17 (23) 20 (27) 43 (58)1400 (760) 500 16 (22) 19 (26) 64 (86) 1000 15 (20) 17 (23) 61 (82) 2000 15 (20) 17 (23) 55 (74)1625 (885) 500 15 (20) 23 (31) 75 (101) 1000 17 (21) 18 (24) 65 (88)1800 (987) 500 20 (27) 21 (18) N/A______________________________________ *Small Diameters 3/32" & 1/8" (.24 & .32 *Large Diameters 5/32" & 3/16" (.41 & .48 cm)

INCONEL alloy 617 derives much of its excellent oxidation resistance from the approximately 1% aluminum in its composition. However, very little of this aluminum will transfer across a welding arc during shielded metal arc welding. Thus, the weld deposits of the instant electrode normally contain less than 0.25% aluminum. For this reason, it was expected that the oxidation resistance of the weld deposits would be less than that of the wrought alloy. Indeed, this was found to be the case. Since it is impractical from an operability standpoint to add aluminum to the deposit via the coating, it is doubtful that the oxidation resistance of the deposit can be significantly increased without a major alloy composition change.

Accordingly, by adding manganese, chromium and columbium to the electrode coating, the oxidation resistance of the weld deposit is improved. Moreover by modifying the nickel-carbon composition of the flux, we have been able to improve the stress rupture characteristics of the weld deposit as well.

The physical characteristics of the experimental electrodes are presented in Table 10. The deposition efficiency values were calculated as follows: ##EQU1## where the "Weight of Metal Deposited" is defined as the weight of the deposit (with slag removed) from one electrode which was burned to a 2-inch (5.08 cm) stub. Thus, it is seen that from 10 pounds (4.5 kg) of 5/32-inch (0.41 cm) diameter electrodes, a welder will deposit approximately 61/2 pounds (2.9 kg) of weld metal.

TABLE 10__________________________________________________________________________PHYSICAL CHARACTERISTICS OF THE ELECTRODE__________________________________________________________________________Diameter 3/32"(.24 cm) 1/8"(.32 cm) 5/32"(.41 cm) 3/16"(.48 cm)Length 9"(22.8 cm) 12"(30.5 cm) 14"(35.6 cm) 14"(35.6 cm)Electrode/Pound (kg) 41(91) 16(35) 9(20) 7(15.5)Die Size .145"(.37 cm) .200"(.5 cm) .235"(.64 cm) .270"(.67 cm)*Deposition Efficiency (%) 66 63 65 67Electrode Coating (%) 24.5 29.0 24.5 21.3__________________________________________________________________________ *Calculated with 2" (5.08 cm) stub.

The recommended current ranges for the electrodes are presented in Table 11. These ranges were determined to be "optimum". Operating the electrodes below the minimum results in arc instability, poor wetting and trapped slag. Above the maximum amperage the welder may experience overheating, loss of arc stability and arc force, porosity and cracking.

TABLE 11______________________________________CURRENT RANGES WELDING ELECTRODEElectrodeDiameter Minimum* Maximum**in. (cm) (Amps) (Amps)______________________________________3/32 (.24) 40 651/8 (.32) 60 955/32 (.41) 90 1303/16 (.48) 120 175______________________________________ *Lowest amperage at which the electrode could be used with a reasonable amount of arc stability. **Highest amperage at which the entire electrode (2inch [5.08 cm] stub) could be used without overheating and loss of stability.

It is to be observed that the present invention provides a unique, flux-coated arc-welding electrode, containing a nickel alloy core of special composition for producing improved, sound, ductile welds having substantial freedom from hot cracking together with an easily removable slag. In the present invention substantial benefits are obtained by combining in special electrodes a columbium and manganese content together with a controlled aluminum content in the core wire of the electrode and further by incorporating it with the flux to provide an electrode which will produce satisfactory strong welds in joining or overlaying a variety of metals, especially in joining similar or dissimilar metals, and which will have improved arc stability and good slag characteristics and will deposit metal having good weld soundness and ductility and good freedom from hot cracking, and microfissuring. Furthermore, in accordance with the invention, the special electrodes hereinbefore described contain controlled amounts of the essential metals columbium and manganese together with a controlled aluminum content in the core wire. These new electrodes reduce weld porosity and hot weld cracking tendencies and further incorporate sufficient calcium carbonate in the flux to keep the carbon content of the weld low. The flux also contains a suitable binder material to produce a flux coating of high mechanical strength and a coating capable of rough handling without cracking and chipping.

While in accordance with the provisions of the statutes, there is illustrated and described herein specific embodiments of the invention, those skilled in the art will understand that changes may be made in the form of the invention covered by the claims and that certain features of the invention may sometimes be used to advantage without a corresponding use of the other features.

Claims

1. A coated welding electrode having a core wire comprising about 22% chromium, about 12.5% cobalt, 9% molybdenum, about 1.2% aluminum, about 0.07% carbon, about 1.5% iron, about 0.5% silicon, about 0.5% manganese, about 0.008% sulfur, about 0.3% titanium, about 0.2% copper, the balance being nickel and a flux coating disposed about the electrode including about 10-50% calcium carbonate, about 10-50% cryolite, about 5-35% titania, up to 30% silica, up to 15% wollastonite, about 5-20% chrome, about 2-15% manganese, up to 8% molybdenum, up to 2% nickel-carbon composite, up to 8% colloidal clay, up to 12% high melting oxide, up to 8% columbium and a silicate type binder.

2. The electrode according to claim 1 wherein the flux coating comprises about 28% calcium carbonate, about 28% cryolite, about 9% titania, about 3% silica, about 3% wollastonite, about 10% chromium metal, about 3% manganese metal, about 4% molybdenum metal, about 1% nickel-carbon composite, about 3% collodial clays and extrusion aids, about 4% high melting oxides and about 4% columbium metal.

3. The electrode according to claim 1 wherein a weld deposit of the electrode includes about 0.1% carbon, about 1.4% manganese, about 1.2% iron, about 0.005% sulfur, about 0.5% silica, about 0.05% copper, about 23.1% chrome, about 0.2% aluminum, about 0.09% titanium, up to 0.001% magnesium, about 11.5% cobalt, about 9.2% molybdenum, about 0.5% columbium-tantalum, up to 0.002% boron, about 0.005% phosphorous, and the balance nickel.

4. The electrode according to claim 2 wherein the diameter of the electrode is less than or equal to 1/8 inch (0.32 centimeters).

5. The electrode according to claim 1 wherein a weld deposit of the electrode includes about 0.1% carbon, about 0.6% manganese, about 0.8% iron, about 0.004% sulfur, about 0.5% silicon, about 0.05% copper, about 23.2% chrome, about 0.2% aluminum, about 0.1% titanium, up to 0.001% magnesium, about 11.7% cobalt, about 9.3% molybdenum, about 0.02% columbium-tantalum, about 0.001% boron, about 0.005% phosphorous and the balance nickel.

6. The electrode according to claim 5 wherein the diameter of the electrode is greater than 1/8 inch (0.32 centimeters).

7. The electrode according to claim 1 wherein the binder comprises 40-98% sodium silicate, up to 50% potassium silicate, up to 4% lithium silicate and up to 6% water.

8. The electrode according to claim 7 wherein the binder comprises about 95% sodium silicate, about 4% lithium silicate and about 1% water.