1. Field of the Invention
This invention generally relates to substrates with surface coatings, in particular to a coated substrate having one or more cross-linked interfacial zones formed to improve coating adhesion.
2. Description of the Related Art
Various coating systems have been developed to protect surfaces such as that of building materials from the detrimental effects of handling and environmental exposure. Protective and decorative coatings such as sealers, primers, tie coats, topcoats, color coats, and clear coats are well known. Typically, coatings are applied to solid substrates as liquids or powders and subsequently cured by moisture, heat, light, irradiation and/or chemical initiators. The coatings are usually applied in multiple layers, with each of the layers often having different chemical compositions and properties.
Disadvantageously, conventional coating systems for building materials often suffer from drawbacks such as poor adhesion. For example, the interfacial bond strength between paint and a cementitious building article is often less than ideal, which can result in overall paint failure. Moreover, the adhesion between adjacent coating layers on a building article is also often weak, which can cause paint layer separation. It is thus an object of the present invention to provide a system and method of manufacturing a coated substrate which overcomes or ameliorates one or more of the disadvantages of the prior art.
In one aspect, the preferred embodiments of the present invention provide a composite building article comprising a substrate containing hydroxyl functional groups, a first composition coated over at least a portion of the substrate, wherein a portion of the first composition extends into a subsurface region of the substrate. Preferably, the first composition comprises a plurality of cross-linking molecules wherein each molecule has at least two reactive functional groups, each functional group being capable of forming chemical bonds with the hydroxyl functional groups in the substrate. The building article further includes a cross-linked interfacial zone comprising an interlocking matrix formed in the subsurface region of the substrate. Preferably, the interlocking matrix is comprised of hydroxyl functional groups in the subsurface region bonded to and cross-linked by the cross-linking molecules in the portion of the first composition extending into the subsurface region. In one embodiment, the cross-linking molecule in the composition can be selected from the group consisting of vinylalkoxy silane, epoxy-tertiary amine, epoxy, metal complexity compounds, glycidoxypropyltrimethoxysilane, carboxylic acid, hydroxyl-carboxylic acid, and combinations thereof. In another embodiment, the building article further includes a second composition coated over at least a portion of the first composition. Preferably, a second cross-linked interfacial zone is formed between the first and second compositions wherein molecules in the second composition are bonded to and cross-linked by the cross-linking molecules in the first composition.
In another aspect, the preferred embodiments of the present invention provide a composite building article having a first zone which comprises predominantly cement, a second zone which comprises predominantly a coating material, and an interfacial zone interposed therebetween. The interfacial zone preferably comprises an interlocking matrix formed of the coating material and the cement. Preferably, the coating material comprises molecules, each having at least two functional groups, wherein the functional groups on the molecules bond with hydroxyl functional groups in the cement to form cross-linked bonds in the cement. In one embodiment, the coating material further comprises at least one secondary functional group which forms cross-linking bonds with subsequent coating layers. In another embodiment, the coating material comprises a basecoat and a topcoat.
In yet another aspect, the preferred embodiments of the present invention provide a method of forming a building article. The method comprises applying a coating material to a hydroxyl-group containing substrate, wherein the coating material extends into the substrate in a controlled manner, and curing the coating material in the substrate to as to form a three-dimensional network of hydroxyl groups cross-linked by the coating material. The hydroxyl group containing substrate includes fiber reinforced cement composite building products such as siding, roofing, fencing, trim, fascia, pipes, decking, and tile underlayment.
As used herein, the term “cross-linked” shall refer to two or more molecules or functional groups that are linked together by bonding to cross-linking agents which extend between the molecules or functional groups. The cross-linked functional groups could be on neighboring molecules or on the same molecule. The term “cross-linking agent” or “cross-linking molecule” shall refer to a molecule having at least two reactive functional groups, whereby each functional group bonds to a different molecule or functional group to link together the molecules or functional groups.
Certain preferred embodiments of the present invention provide a coated composite building article having one or more cross-linked interfacial zones formed to improve coating adhesion. In one embodiment, a first cross-linked interfacial zone is formed at the interface between the substrate of the building article and a basecoat layer. In the first cross-linked interfacial zone, a portion of the molecules in the substrate are bonded to and cross-linked by components in the basecoat. In another embodiment, a second cross-linked interfacial zone is formed at the interface between the basecoat layer and a topcoat layer. In the second cross-linked interfacial zone, a portion of the molecules in the topcoat layer are bonded to and cross-linked by components in the basecoat layer.
The building article substrate can include a variety of different materials, including but not limited to, organic polymers, inorganic polymers, woods, papers, cardboards, cements, fiber reinforced cement composite materials, and the like. In some preferred embodiments, the building article substrate contains hydroxyl functional groups and the basecoat components have primary functional groups which form covalent bonds with the hydroxyl functional groups in the substrate, thereby linking together neighboring hydroxyl groups. In one embodiment, the basecoat components contain at least two, preferably three or more, chemical functional groups per molecule that are capable of reacting with hydroxyl groups in the substrate. The basecoat-substrate reaction can be a condensation or an addition reaction, and the reaction can proceed at ambient conditions, and/or under heat, and/or under irradiation, and/or with catalysts. The basecoat-substrate reaction enhances not only the adhesion and durability of the basecoat, but also the structural integrity of the topcoat layer on the solid substrate.
In practice, a portion of the basecoat preferably extends into the pores and interstices of the substrate so that the components contained therein can react with molecules in the substrate. In some embodiments, the basecoat contains small particles that can penetrate into the substrate to also form a mechanical interlocking after curing. The cross-linking reaction between the basecoat and the substrate plus the mechanical interlocking can significantly increase the interfacial bond strength between the basecoat and the substrate.
In other embodiments, the components in the basecoat may also contain at least one, preferably two or more, secondary functional groups per molecule that are capable of reacting with molecules in the topcoat. The topcoat may or may not contain functional group(s) reactive with the hydroxyl groups of the substrate. Examples of the top-basecoat reaction include a radical graft polymerization reaction, a condensation-type reaction or an addition-type reaction.
In certain implementations, the cross-linked interfacial zones provide an interlocking matrix extending between the basecoat layer and the substrate and between the basecoat and the topcoat layers. The resultant coating is one unified, three-dimensional network from the bulk solid substrate to the top coating layer that demonstrates superior adhesion and durability.
The substrate 102 of the composite building article 100 in
In the first cross-linked interfacial zone 110, the basecoat 106 illustrated in
As
As will be described in greater detail below, the cross-linked interfacial zones in the fiber cement article can be formed by a number of different methods including but not limited to applying in a controlled manner a coating as a dispersion or solution into a cured fiber cement matrix.
The cement is typically ordinary Portland cement type 1 and the silica can be milled quartz, preferably around 200 mesh, or any suitable siliceous material that alone, or in combination, yields properties substantially equivalent thereto. Examples of suitable siliceous materials include, but are not limited to, amorphous silica, diatomaceous earth, rice hull ash, blast furnace slag, granulated slag, steel slag, mineral oxides, mineral hydroxides, clays, magnasite or dolomite, polymeric beads, metal oxides and hydroxides, or mixtures thereof.
Preferred fibers include various forms of cellulose fibers including Kraft and sulfite pulps, bleached and unbleached wood and non-wood cellulosic fibers, pulps in rolls, bales, fiberized (by hammermilled or refining). However, it will be appreciated that other forms of fibers may be used. In a particularly preferred embodiment, the fiber is cellulose wood pulp. Other examples of suitable fibers are ceramic fiber, glass fiber, mineral wool, steel fiber, and synthetic polymer fibers such as polyamides, polyester, polypropylene, polymethylpentene, polyacrylonitrile, polyacrylamide, viscose, nylon, PVC, PVA, rayon, glass ceramic, carbon, or any mixtures thereof. The fibers can also include engineered cellulose fibers such as those disclosed in PCT Patent Application WO 0228796 and WO 0228795, which are hereby incorporated by reference in their entirety.
It should also be noted that additional additives can be optionally incorporated into the fiber cement composition including but not limited to density modifiers, dispersing agents, silica fume, geothermal silica, fire retardant, biocides, thickeners, pigments, colorants, dispersants, foaming agents, flocculating agents, water-proofing agents, organic density modifiers, aluminum powder, kaolin, alumina trihydrate, mica, metakaolin, calcium carbonate, wollastonite, polymeric resin emulsions, or mixtures thereof.
In one preferred method, the sheets are produced using the Hatschek process. As it is generally known in the art, the Hatschek process uses a rotating drum sieve arrangement to deposit a plurality of zones of de-watered slurry onto an absorbent conveyer until the desired sheet thickness has been achieved. However, it will be appreciated that the greens sheets can also be produced using other known methods such as extrusion, mazza, magnani and roll pressed processes. The green sheets are subsequently cured in Step 204. The curing can be carried out in an autoclave or using any number of other conventional techniques including air curing.
When curing has been completed, the sheets are typically cut to size in Step 206 and in certain implementations, the edges are finished by passing through a conventional sheet finishing line in where they are optionally trimmed to size with an edge router to exact dimensions. The finished fiber-cement sheets are placed in a stack as they come off the sheet finishing line.
In Step 208, a basecoat composition is applied to an exterior surface of each fiber-cement sheet. A portion of the basecoat composition extends from the exterior surface into the fiber cement matrix, fills the voids and interstices therein, and directly contacts the fiber cement. In some preferred forms of the invention, the basecoat composition is applied to all six sides of the finished fiber-cement sheet (the front face and mounting face being the two major faces, and the four edges). This may be done by first manually roll coating or spraying the basecoat on the edges of the stack of fiber-cement sheets and then individually roll coating the basecoat on the face and back of an fiber-cement sheet using a conventional roll coater. Alternatively, the basecoat composition may be applied by other conventional methods such as spraying, vacuum, direct roller coating, flood coating, brush coating, curtain coating or powder coating. Preferably, the coating thickness is in the range of about 5 to 50 microns.
In one embodiment, the basecoat composition comprises a vinylalkoxy silane sealer and a water-based acrylic latex topcoat. In another embodiment, the basecoat composition consists essentially of a vinylalkoxy silane sealer and a water-based acrylic latex topcoat. In yet another embodiment, the basecoat composition comprises a dilute citric acid pre-sealer and a styrene-acrylic latex sealer. In certain embodiments, the basecoat composition consists essentially of a dilute citric acid pre-sealer and a styrene-acrylic latex sealer. In other embodiment, the basecoat composite can comprise a carboxylic acid pre-sealer and/or a citric acid pre-sealer.
In preferred embodiments, the basecoat composition is applied directly to the fiber cement surface and allowed to migrate in a controlled manner into the fiber-cement sheet or substrate to form the cross-linked interfacial zone. In certain embodiments, a continuous, defect free film is applied to the fiber cement in a single pass. In other embodiments, the surface of the fiber-cement sheet is further treated to facilitate controlled migration of the basecoat composition. Mechanical and chemical treatments can also be applied to affect the porosity of the substrate which in turn affects the migration of the basecoat component into the substrate. The surface of the fiber cement can be sanded, machined, chemically etched prior to application of the cross-linking agent, which can have the effect of increasing the thickness and improving the uniformity of the cross-linked interfacial zone.
As also shown in
In certain preferred embodiments, the process 200 continues with Step 212 in which a topcoat is applied to the basecoat composition using methods know in the art. In one embodiment, a paint layer is applied to an upper surface of the basecoat composition using methods such as spraying, vacuum, direct roller coating, flood coating, brush coating, curtain coating or roll coating. Preferably, the topcoat contains molecules or functional groups that can be cross-linked by cross-linking agents in the basecoat composition. In one embodiment, a portion of the topcoat extends into the basecoat and molecules therein are cross-linked in step 214 by cross-linking agents present in the basecoat, thus forming a second cross-linked interfacial region. In certain embodiments, Steps 210 and 214 can be performed simultaneously after both the basecoat composition and topcoat have been applied to the FRC substrate.
The preferred embodiments of the present invention will be further described with reference to the following illustrative Examples.
Example 1 illustrates a coating composition of one preferred embodiment cross-linkable to fiber reinforced cement composites and also a method of applying the cross-linkable coating composition onto fiber cement substrates. The coating composition comprised a vinylalkoxy silane sealer and a water-based acrylic latex topcoat. The vinylalkoxy silane sealer was vinyltriethoxymethoxy silane at about 100% solids obtained from Gelest, Inc. The water-based acrylic latex topcoat was acrylic ColorPlus obtained from Valspar Corporation with the addition of a 2,5-dimethyl-2,5-di-(2-ethylhexanoylperoxy) hexane liquid radical initiator, Trigonox 141 obtained from Akzo Nobel Polymer Chemicals LLC. Trigonox 141 was added at about 1-2% relative to the acrylic latex resin, which contained about 50-54% solids. The acrylic topcoat also contained about 2-4% of a polycarbodiimide crosslinker.
Fiber reinforced cement sample boards precut to 3″ by 3″, pre-equilibrated to a board moisture content of about 18-22% and preheated to a board temperature of about 130-140 F, were sealed with vinyltriethoxymethoxy silane at a film thickness of about 0.7-1.0 mils. The amount of sealer was adjusted on an analytical balance with a precision of ±0.01 g. Subsequently, sealed samples were cured at room conditions for 24 hours to bond/crosslink vinyltriethoxymethoxy silane to the fiber cement substrate. After the 24-hour period, vinyltriethoxymethoxy silane sealed fiber cement boards were then top coated with two layers of acrylic coating to achieve a dry film thickness of about 1 mil. The first topcoat layer was cured in a fanned oven until the board surface temperature reached about 120-140 F, whereas the second topcoat layer was cured until the board surface temperature reached about 170-180 F. Heat cure was employed to speed up the self cross-linking reaction between acrylic polymer chain and also to facilitate the radical graft co-polymerization reaction between the vinyltriethoxymethoxy silane sealer and the acrylic topcoat. Once the coating was completed, coated boards were allowed to further equilibrate/cure at room temperature conditions for and additional 24 hours between inspections/tests.
24 hours after curing the coatings were fully dry and non-tacky. Under a microscope at a magnification of 100×, the coatings appeared smooth with no pinholes, no mud-cracks and no blisters. Tape adhesion tests (using 3M Scotch Flat Back 1″ wide masking tape) on dry coated boards resulted in no paint peeling, which suggests an excellent adhesion of the films to the fiber cement substrate through the cross-linking reaction. The same tape-adhesion tests on damp coated boards (after soaking in tap water for 24 hours at room temperature conditions) confirmed the excellent adhesion with paint pickings of only about 0-5% (per total paint area tested). In addition, surprisingly, the tape-adhesion pickings of damp coated boards were only about 10-15% even after 50 cycles of freeze thaw. The control samples coated with sealers without the cross-linking agent would peel 20% and 40% of the paint in the dry and wet tape adhesion test, respectively. 50 to 70% of the paint would be peeled off after 50 cycles of freeze/thaw testing. Table 1 shows the paint adhesion results of one embodiment compared against paint adhesion of a control sealer.
Example 2 provides a coating composition of another preferred embodiment suitable for cross-linking fiber cement substrates and a method of coating the composition containing cross-linking agents onto fiber cement substrates. The coating composition comprised an epoxy-tertiary amine emulsion sealer and an acrylic latex topcoat. The water-based sealer mixture was prepared by mixing a tertiary polyamine catalyst, POLYCAT 41 obtained from Air Products into an epoxy emulsion resin, ANCAREZ AR550 obtained from Air Products. The POLYCAT 41 catalyst was usually added at 2-10% to the ANCAREZ AR 550 resin, containing about 57% solids epoxy. The topcoat was an acrylic latex coating, containing about 50-54% solids with about 2-4% of a polycarbodiimide cross-linking agent. The acrylic polymer chains also possessed carboxylic acid end groups cross-linkable to the epoxy sealer.
A preferred procedure for creating coatings cross-linking fiber cement substrates using epoxy-tertiary amine sealer and acrylic latex topcoat can be proceeded as follow. First, the emulsion mixture of ANCAREZ AR550 and POLYCAT 41 was brushed onto the fiber cement boards precut to 3″ by 3″, presoaked to about 20% moisture content and preheated to about 130-140 F to achieve a dry film thickness of about 0.6 to 0.8 mils. The sealer was allowed to soak in for about 20-30 seconds, and then cured until board surface temperature reached about 170-180 F. Subsequently, sealed samples were cooled to room temperature under ambient conditions, followed by the application of two layers of acrylic topcoat similar to those shown in Example 1. Heat cure was used to speed up the self cross-linking reaction of the topcoat, and also to facilitate the bond/cross-linking reaction between the epoxy sealer and the acrylic topcoat. Once the coating was completed, coated boards were allowed to further equilibrate/cure at room temperature conditions for an additional one week before inspection/analysis.
Inspections revealed smooth and non-tacky paint films on the fiber cement substrates. In addition, no pinholes, mud-cracks, or blisters were detected.
Tape adhesion tests indicated a superb adhesion of the cross-linking coating to the fiber cement substrate. No paint pickings were observed for both dry and damp boards before freeze thaw. Surprisingly, there were no picking even after 100 cycles of freeze thaw. Table 2 illustrates the paint adhesion results of one embodiment as compared against paint adhesion results of a control sealer.
Example 3 presents yet another preferred embodiment of cross-linkable coating composition based on a different water-based epoxy sealer and the acrylic topcoat. In this example, the water-based epoxy sealer was prepared by adding about 2-5% of a glycidoxypropyltrimethoxysilane DYNASYLAN obtained from Degussa and about 1-3% of a polyamine curing agent, ANQUAMINE 401 obtained from Air Products to the ANCAREZ AR5550 epoxy resin. The acrylic topcoat used in this example was identical to that used in Example 2. The coating and testing procedures were conducted similarly as those illustrated in Example 2.
Smooth, non-tacky, and defect-free films were also obtained similar to those in Example 2. However, noticeable that the current cross-linking coatings on damp fiber cement substrates completely passed the tape-adhesion test with no pickings even after 260 cycles of freeze thaw. Table 3 illustrates the paint adhesion results of one embodiment as compared against paint adhesion of a control sealer.
Example 4 discloses yet another preferred coating composition cross-linkable to cement in general, and to fiber reinforced cement composites in specific. The coating composition comprised a dilute aqueous solution of citric acid as the pre-sealer and a styrene modified acrylic latex as the sealer. The coating composition further comprised an acrylic coating as the topcoat. The aqueous citric acid sealer was prepared by dissolving about 7-12% of an anhydrous solid citric acid obtained from EMD chemicals in tap water. The styrene modified acrylic sealer was diluted with tap water to achieve 15-25% solids. The topcoat used in this example was similar to that used in Example 2.
The cross-linkable coating was produced by first pre-sealing the fiber cement samples with the aqueous acid sealer and curing the pre-sealed samples in a convection air over at about 350 F for 45 minutes. The typical dry film thickness of citric acid was about 0.25-0.45 mils. After the heat cure period, citric acid was expected to completely react/cross-link with the fiber cement materials via an acid-base reaction and/or a carboxylic acid-hydroxyl condensation reaction. Once pre-sealed boards had cooled to about 130-140 F, the sealer was brushed on at a dry film thickness of about 0.6-0.8 mils and allowed to soak in for about 1-2 minutes. Subsequently, two coats of acrylic topcoat were applied and cured similar to the procedure shown in Example 2.
The resultant coatings were smooth, non-tacky and free of film defects. The crosslinking coatings adhere strongly to the fiber cement substrates with no tape-adhesion pickings on both dry and damp coated boards. More superbly, the coatings showed no wet-adhesion pickings (tape-adhesion test on a damp board) even after 75 cycles of freeze thaw. Table 4 illustrates paint adhesion test results of one embodiment using citric acid pre-sealer as compared to test results using a control sealer.
The citric acid in this example serves as the cross-linking agent between the fiber reinforced cement substrate and the styrenated acrylic sealer. In certain preferred embodiments, the application of the citric acid pre-sealer as a cross-linkable composition advantageously provides excellent paint adhesion to sanded fiber cement substrates in particular.
The presence of the cross-linked interfacial zone correlates with improved adhesion of coatings to the substrate following freeze/thaw cycles. The coating also contains cross-linking agents which can form bonds with polymers in subsequent coating layers. Advantageously, the coated composite building products of the preferred embodiments of the present invention, as compared with similar sheets prepared using traditional surface coatings, present an improved adhesion between coatings and substrate and also between coating layers. The addition of a cross-linked interfacial zone imparts to the composite article superior dry and wet coating adhesion, a reduced propensity to weathering, especially freeze/thaw damage, when compared to existing fiber cement products, improved heat resistance, toughness, scratch and impact resistance, excellent acid and alkaline and chemical resistance.
Although the foregoing description of the preferred embodiments of the present invention has shown, described and pointed out the fundamental novel features of the invention, it will be understood that various omissions, substitutions, and changes in the form of the detail of the invention as illustrated as well as the uses thereof, may be made by those skilled in the art, without departing from the spirit of the invention. Particularly, it will be appreciated that the preferred embodiments of the invention may manifest itself in other shapes and configurations as appropriate for the end use of the article made thereby.
Number | Name | Date | Kind |
---|---|---|---|
3931448 | Parkinson | Jan 1976 | A |
4143188 | Huber-Nuesch et al. | Mar 1979 | A |
4226277 | Matalon | Oct 1980 | A |
4246148 | Shimp et al. | Jan 1981 | A |
4759961 | Kato et al. | Jul 1988 | A |
5059264 | Sheets | Oct 1991 | A |
5087405 | Maker | Feb 1992 | A |
5162407 | Turner | Nov 1992 | A |
5445754 | Nelson | Aug 1995 | A |
5681877 | Hosotte-Filbert et al. | Oct 1997 | A |
5688642 | Chrisey et al. | Nov 1997 | A |
6068885 | Hartman et al. | May 2000 | A |
6069217 | Nae et al. | May 2000 | A |
6376570 | Zhao et al. | Apr 2002 | B1 |
6376579 | Mishra et al. | Apr 2002 | B1 |
6395804 | Rao et al. | May 2002 | B1 |
6420479 | Phan et al. | Jul 2002 | B1 |
6572927 | Pleyers et al. | Jun 2003 | B1 |
6680111 | Leibler et al. | Jan 2004 | B1 |
6710112 | Sandor et al. | Mar 2004 | B1 |
6933415 | Zhao et al. | Aug 2005 | B2 |
7041727 | Kubicek et al. | May 2006 | B2 |
7235595 | Hermes et al. | Jun 2007 | B2 |
20010051227 | Jung et al. | Dec 2001 | A1 |
20010053449 | Parekh et al. | Dec 2001 | A1 |
20020061940 | Lach et al. | May 2002 | A1 |
20020072562 | Asthana | Jun 2002 | A1 |
20020077397 | Karuga et al. | Jun 2002 | A1 |
20020081437 | Dargontina et al. | Jun 2002 | A1 |
20020136900 | Mallen | Sep 2002 | A1 |
20020150689 | Seibel et al. | Oct 2002 | A1 |
20020156163 | Brandenburger et al. | Oct 2002 | A1 |
20020169271 | Peng et al. | Nov 2002 | A1 |
20020171170 | DeMasi et al. | Nov 2002 | A1 |
20030054176 | Pantano et al. | Mar 2003 | A1 |
20030088014 | Edwards et al. | May 2003 | A1 |
20030158351 | Smith et al. | Aug 2003 | A1 |
20030207035 | Schmid et al. | Nov 2003 | A1 |
20030236340 | Kubicek et al. | Dec 2003 | A1 |
20040005455 | Stephenson et al. | Jan 2004 | A1 |
20040081706 | Trainer et al. | Apr 2004 | A1 |
20050043446 | Bochan et al. | Feb 2005 | A1 |
20050058689 | McDaniel | Mar 2005 | A1 |
20050192400 | Killilea et al. | Sep 2005 | A1 |
20050196629 | Bariatinsky et al. | Sep 2005 | A1 |
20050214550 | Kawamura | Sep 2005 | A1 |
20050215708 | Robertson | Sep 2005 | A1 |
20050227100 | Brandenburger et al. | Oct 2005 | A1 |
20050238898 | Wind et al. | Oct 2005 | A1 |
20060003159 | Hayes et al. | Jan 2006 | A1 |
20060029825 | Chen et al. | Feb 2006 | A1 |
20060036056 | Wu et al. | Feb 2006 | A1 |
20060105161 | Brandenburger et al. | May 2006 | A1 |
20060111503 | Killilea et al. | May 2006 | A1 |
20060122330 | Wu et al. | Jun 2006 | A1 |
20060135684 | Killilea | Jun 2006 | A1 |
20060135686 | Killilea et al. | Jun 2006 | A1 |
20060141261 | Wind et al. | Jun 2006 | A1 |
20060167208 | Garner et al. | Jul 2006 | A1 |
20060182946 | Zarb et al. | Aug 2006 | A1 |
20060202161 | Share et al. | Sep 2006 | A1 |
20060207476 | Coward et al. | Sep 2006 | A1 |
20060210153 | Sara et al. | Sep 2006 | A1 |
20070001343 | Pulman et al. | Jan 2007 | A1 |
20070010612 | Rouge et al. | Jan 2007 | A1 |
20070027249 | Killilea | Feb 2007 | A1 |
20070036903 | Mayr et al. | Feb 2007 | A1 |
20070045891 | Martinoni et al. | Mar 2007 | A1 |
20070054140 | Mayr et al. | Mar 2007 | A1 |
20070065608 | Niederst | Mar 2007 | A1 |
20070087146 | Evans et al. | Apr 2007 | A1 |
20070110933 | Share et al. | May 2007 | A1 |
20070110981 | Killilea et al. | May 2007 | A1 |
20070117928 | O'Brien et al. | May 2007 | A1 |
20070132158 | Martinoni et al. | Jun 2007 | A1 |
20070154643 | Schmid et al. | Jul 2007 | A1 |
20070169843 | Henderleiter | Jul 2007 | A1 |
20070178239 | Kestell et al. | Aug 2007 | A1 |
20070178294 | Dargontina et al. | Aug 2007 | A1 |
20070259166 | Killilea et al. | Nov 2007 | A1 |
20070259188 | Wu et al. | Nov 2007 | A1 |
20070269660 | Killilea et al. | Nov 2007 | A1 |
20070269668 | Hayes et al. | Nov 2007 | A1 |
20070275198 | Share et al. | Nov 2007 | A1 |
20070282046 | Killilea et al. | Dec 2007 | A1 |
20080008895 | Garner et al. | Jan 2008 | A1 |
20080009601 | Killilea et al. | Jan 2008 | A1 |
20080041003 | Nowak et al. | Feb 2008 | A1 |
20080096024 | Cavallin | Apr 2008 | A1 |
20090004468 | Chen et al. | Jan 2009 | A1 |
20090005484 | Lazarus et al. | Jan 2009 | A1 |
Number | Date | Country |
---|---|---|
515151 | Mar 1981 | AU |
1958706 | Nov 1969 | DE |
469 295 | May 1992 | EP |
10-279831 | Oct 1998 | JP |
2000-327453 | Nov 2000 | JP |
2000327453 | Nov 2000 | JP |
WO-9845222 | Oct 1998 | WO |
WO-0168547 | Sep 2001 | WO |
WO-0228795 | Apr 2002 | WO |
WO-0228796 | Apr 2002 | WO |
WO 2004087412 | Oct 2004 | WO |
WO-2007022449 | Feb 2007 | WO |
WO-2009006304 | Jan 2009 | WO |
WO-2009006324 | Jan 2009 | WO |
WO-2009006333 | Jan 2009 | WO |
Number | Date | Country | |
---|---|---|---|
20070042192 A1 | Feb 2007 | US |