Patent Application
20230279247
The present invention relates to a coating composition. In particular, the present invention relates to coating compositions comprising a polymeric coating binder, wherein the polymeric coating binder comprises an aqueous polymer latex of a film forming carboxylated polymer and a branched polyetheramine polyol. The invention also relates to the use such a coating composition as an interior and/or exterior wall masonry paint. The invention also relates substrate having applied thereon such a coating composition.
The drying speed of a paint or coating for outdoor use such as, for example, a masonry paint or a wood coating, is highly dependent on the weather conditions, in particular the atmospheric humidity, temperature and wind speed during application of the coating. For example, if the drying speed is too low, e.g. because of low temperature and/or high humidity, a sudden rainfall may spoil the coating. In contrast, a high drying speed, e.g. at elevated temperatures and/or low humidity conditions, may lead to problems when applying the coating under these conditions. The drying speed of a paint or coating for indoor use, such as for example a masonry paint or a wood coating, could be impacted by low temperature and high moisture in, for example, a new build where no heating system is operating. This may lead to delay in the time in which a second coat may be applied or may result in blistering due to inappropriate drying time between first and second layer. If the drying time required between two layers to achieve the desired final aesthetic and performance is too long, there may be a negative impact on the efficiency of the painter.
According to the present invention there is provided a coating composition comprising:
wherein the polymeric coating binder is present in the coating composition in an amount of 10 to 20 wt % (based on dry weight of the polymeric coating binder);
and wherein the total solids content of the coating composition is at least 60 wt %.
There is also provided the use of a coating composition as an interior and/or exterior wall masonry paint, wherein the coating composition comprises:
wherein the polymeric coating binder is present in the coating composition in an amount of 10 to 20 wt % (based on dry weight of the polymeric coating binder);
and wherein the total solids content of the coating composition is at least 60 wt %.
There is also provided a substrate coated on at least a portion thereof with a coating, the coating being derived from a coating composition comprising:
wherein the polymeric coating binder is present in the coating composition in an amount of 10 to 20 wt % (based on dry weight of the polymeric coating binder);
and wherein the total solids content of the coating composition is at least 60 wt %.
The coating composition comprises a polymeric coating binder. The polymeric coating binder comprises an aqueous polymer latex of a film forming carboxylated polymer.
By “film forming”, and like terms, as used herein in the context of the polymer latex is meant the ability of the carboxylated polymer of the polymer latex to form a film on surfaces upon drying under application conditions. The polymer may have a film forming temperature of at most 50° C., such as at most 30° C.
The carboxylated polymer may have any suitable glass transition temperature (Tg). The carboxylated polymer may have a Tg from −30 to 60° C., such as from −20 to 60° C., such as from 0 to 50° C., or even from 5 to 40° C. As reported herein, the Tg was measured according to NF EN ISO 1 1357-2 (2014), based on the definitions in NF EN ISO 1 1357-1 (2009). All values for Tg reported herein were measured in this way.
By “carboxylated polymer”, and like terms, as used herein is meant that the polymer of the latex bears carboxyl groups attached to the polymer backbone.
The carboxylated polymer may be formed from one more ethylenically unsaturated monomers having one or more carboxyl group. Suitable ethylenically unsaturated monomers include, but are not limited to, monoethylenically unsaturated monocarboxylic acids, such as C3-C6-monoethylenically unsaturated monocarboxylic acids monoethylenically unsaturated dicarboxylic acids, such as C4-C6-monoethylenically unsaturated dicarboxylic acids, esters, diesters and/or anhydrides of the aforementioned acids; and combinations thereof.
The ethylenically unsaturated monomers may comprise monoethylenically unsaturated monocarboxylic acids. Examples of suitable monoethylenically unsaturated monocarboxylic acids include, but are not limited to, acrylic acid, methacrylic acid, crotonic acid, 2-ethylpropenoic acid, 2-propylpropenoic acid, or combinations thereof.
The ethylenically unsaturated monomers may comprise monoethylenically unsaturated dicarboxylic acids. Examples of suitable monoethylenically unsaturated dicarboxylic acids include, but are not limited to, itaconic acid, fumaric acid or combinations thereof.
The ethylenically unsaturated monomers may comprise alkyl esters of monoethylenically unsaturated monomers. Examples of suitable alkyl esters of monoethylenically unsaturated monomers include, but are not limited to, C1-C20-alkyl esters of C3-C6 monoethylenically unsaturated monocarboxylic acids; di-C1-C20-alkyl esters of C3-C6 monoethylenically unsaturated dicarboxylic acids; C5-C20-cycloalkyl esters of C3-C6 monoethylenically unsaturated monocarboxylic acids, hydroxyalkyl esters of monoethylenically unsaturated C3-C6 monocarboxylic acids; vinylesters of C1-C20-alkanoic acids and combinations thereof.
Examples of suitable C1-C20-alkyl esters of C3-C6 monoethylenically unsaturated monocarboxylic acids include, but are not limited to, C1-C20-alkyl esters of acrylic acid, for example, methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl-acrylate, n-butyl acrylate, 2-butyl acrylate, isobutyl acrylate, n-pentyl acrylate, n-hexyl acrylate, n-octyl acrylate, 2-ethylhexyl acrylate, n-decyl acrylate, 2-propylheptyl acrylate, lauryl acrylate, C12/C14-alkyl acrylate or stearyl acrylate, C1-C20-alkylesters of methacrylic acid include, for example, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, 2-butyl methacrylate, isobutyl methacrylate, tert.-butyl methacrylate, n-pentyl methacrylate, n-hexyl methacrylate, n-octyl methacrylate, 2-ethylhexyl methacrylate, n-decyl methacrylate, 2-propylheptyl methacrylate, lauryl methacrylate, C12/C14-alkyl methacrylate or stearyl methacrylate and combinations thereof.
Examples of suitable di-C1-C20-alkyl esters of C3-C6 monoethylenically unsaturated dicarboxylic acids include, but are not limited to, di-C1-C20-alkyl esters of itaconic acid, di-C1-C20-alkyl esters of citraconic acid, di-C1-C20-alkyl esters of maleic acid, di-C1-C20-alkyl esters of fumaric acid and combinations thereof.
Examples of suitable C6-C20-cycloalkyl esters of C3-C6 monoethylenically unsaturated monocarboxylic acids include, but are not limited to, C6-C20-cycloalkyl esters of acrylic acid, C5-C20-cycloalkyl esters of methacrylic acid and combinations thereof.
Examples of suitable hydroxyalkyl esters of monoethylenically unsaturated C3-C6 monocarboxylic acids include, but are not limited to, hydroxyalkyl esters of acrylic acid (or hydroxyalkyl acrylates), such as hydroxy-C2-C4-alkylesters of acrylic acid, including 2-hydroxyethyl acrylate, 3-hydroxypropyl acrylate and 4-hydroxybutyl acrylate, for example; hydroxyalkyl esters of methacrylic acid (also referred to herein as hydroxyalkyl methacrylates), such as hydroxy-C2-C4-alkylesters of methacrylic acid, including 2-hydroxyethyl methacrylate, 3-hydroxypropyl methacrylate and 4-hydroxybutyl methacrylate, for example; and combinations thereof.
The ethylenically unsaturated monomers may comprise mono or diesters of monoethylenically unsaturated C3-C6 monocarboxylic acids. Monoesters of monoethylenically unsaturated C3-C6 monocarboxylic acids may comprise monoesters of monoethylenically unsaturated C3-C6 monocarboxylic acids with monoethylenically unsaturated aliphatic or cycloaliphatic monohydroxy compounds, such as the acrylates and the methacrylates of vinyl alcohol, allyl alcohol, 2-cyclohexen-1-ol or norbornenol. Diesters of monoethylenically unsaturated C3-C6 monocarboxylic acids may comprise diesters of monoethylenically unsaturated C3-C6 monocarboxylic acids with saturated aliphatic or cycloaliphatic diols, such as diesters of acrylic acid or methacrylic acid, including the diacrylates and the dimethacrylates of ethylene glycol, propylene glycol, 1,2-butanediol, 1,3-butanediol, neopentyl glycol and 1,2-cyclohexanediol.
The carboxylated polymer may be formed from one or more additional ethylenically unsaturated monomers. Suitable examples of additional ethylenically unsaturated monomers include, but are not limited to, vinyl aromatic monomers, such as mono-vinyl substituted aromatic hydrocarbons, including styrene, 2-methylstyrene, 4-methylstyrene, 2-n-butylstyrene, 4-n-butylstyrene, 4-n-decylstyrene and alpha-methylstyrene, for example; divinyl aromatic compounds, such as 1,3-divinyl benzene and 1,4-divinyl benzene, for example; C2-C6-monoolefines; butadiene; multiethylenically unsaturated monomers, such as monomers having at least 2 non-conjugated ethylenically unsaturated double bounds; primary amides of monoethylenically unsaturated monomers; monoethylenically unsaturated monomers bearing urea or keto groups; monoethylenically unsaturated monomers which bear at least one tri-C1-C4-alkoxysilane group; and combinations thereof.
Examples of suitable primary amides of monoethylenically unsaturated monomers include, but are not limited to, primary amides of monoethylenically unsaturated C3-C6 monocarboxylic acids, such as acrylamide and methacrylamide, N—C1-C10 alkyl amides of monoethylenically unsaturated C3-C6 monocarboxylic acids, such as N—C1-C10 alkyl amides of acrylic acid or methacrylic acid, N-methyl acrylamide, N-ethyl acrylamide, N-propyl acrylamide, N-isopropyl acrylamide, N-butyl acrylamide, N-methyl methacrylamide, N-ethyl methacrylamide, N-propyl methacrylamide, N-isopropyl methacrylamide and N-butyl methacrylamide and combinations thereof.
Examples of suitable monoethylenically unsaturated monomers bearing urea or keto groups include, but are not limited to, 2-(2-oxo-imidazolidin-1-yl)ethyl (meth)acrylate, 2-ureido (meth)acrylate, N-[2-(2-oxooxazolidin-3-yl)ethyl] methacrylate, acetoacetoxyethyl acrylate, acetoacetoxypropyl methacrylate, acetoacetoxybutyl methacrylate, 2-(acetoacetoxy)ethyl methacrylate, diacetoneacrylamide (DAAM) and diacetonemethacrylamide.
Examples of suitable monoethylenically unsaturated monomers which bear at least one tri-C1-C4-alkoxysilane group include, but are not limited to, vinyl trimethoxysilane, vinyl triethoxysilane, methacryloxyethyl trimethoxysilane, methacryloxyethyl triethoxysilane, and combinations thereof.
The carboxylated polymer may be formed from acrylic acid, methacrylic acid, crotonic acid, 2-ethylpropenoic acid, 2-propylpropenoic acid, itaconic acid, fumaric acid or combinations thereof.
The carboxylated polymer may be formed from (A) 70 to 99.95 w % of monomers selected from the group consisting of C1-C20-alkyl esters of C3-C6 monoethylenically unsaturated monocarboxylic acids, di-C1-C20-alkyl esters of C4-C6 monoethylenically unsaturated dicarboxylic acids, C6-C20-cycloalkyl esters of C3-C6 monoethylenically unsaturated monocarboxylic acids, vinylesters of C1-C20-alkanoic acids, vinyl aromatic monomers, C2-C6-monoolefines and butadiene, based on the total solid weight of the monomers from which the carboxylated polymer is formed, (B) 0.05 to 10 wt % of monomers selected from the group consisting of monoethylenically unsaturated C3-C6 monocarboxylic acids and monoethylenically unsaturated C4-C6 dicarboxylic acids, based on the total solid weight of the monomers from which the carboxylated polymer is formed; and (C) 0 to 20 wt % of one or more monomers selected from the group consisting of primary amides of monoethylenically unsaturated C3-C8 monocarboxylic acids, monoethylenically unsaturated monomers bearing urea or keto groups, hydroxyalkyl esters of monoethylenically unsaturated C3-C6 monocarboxylic acids, monoethylenically unsaturated monomers which bear at least one tri-C1-C4-alkoxysilane group and multiethylenically unsaturated monomers based on the total solid weight of the monomers from which the carboxylated polymer is formed. Component (C) may be different to component (A).
Component (A), as defined above, may comprise at least one monomer selected from C1-C20-alkyl esters of acrylic acid and C6-C20-alkylesters of methacrylic acid and at least one monomer selected from vinyl aromatic monomers, and C1-C4-alkyl esters of methacrylic acid and mixtures thereof.
Component (B), as defined above, may comprise acrylic acid, methacrylic acid and/or combinations thereof.
The ethylenically unsaturated monomers from which the carboxylated polymer is formed may have a solubility in deionized water of at most 50 g/l at 20° C.
The aqueous polymer latex of the carboxylated polymer may be obtained by radical emulsion polymerization. The aqueous polymer latex of the carboxylated polymer may be obtained by radical emulsion polymerization of one or more of the monomers defined above. Suitable radical emulsion polymerisation methods will be known to a person skilled in the art.
In the aqueous carboxylated polymer latex, the dispersed polymers may be in the form of polymer particles. The polymer particles may have an average diameter from 50 to 500 nanometers (nm), such as from 60 to 400 nm, or even from 80 to 300 nm. A reported herein, the average diameter of the polymer particles relates to the Z average particle diameter as determined by means of photon correlation spectroscopy (PCS), also known as quasielastic light scattering (QELS) or dynamic light scattering (DLS). The measurement method is described in the ISO 13321:1996 standard.
The polymers in the polymer dispersion may have a narrow particle size distribution as defined by the polydispersity index (Mw/Mn). The polydispersity index may be less than 0.2.
The polymeric coating binder may comprise any suitable amount of the film forming carboxylated polymer. The polymeric coating binder may comprise from 10 to 70 wt %, such as from 30 to 65 wt %, or even from 40 to 65 wt % of the of the film forming carboxylated polymer based on the total weight of the polymeric coating binder.
The polymeric coating binder comprises a branched polyetheramine polyol. The branched polyetheramine polyol is dissolved in the aqueous phase of the polymer latex. By “branched” and like terms as used herein is meant that the polyetheramine polyol does not have linear structure, but has an amount of branching points within the polymer backbone, which result in a branched polymer chain. Such branching points may be tri or tetra-substituted carbon atoms and/or tertiary amino groups. The branching points may be the tertiary amino groups.
The branched polyetheramine may have any suitable water solubility. The branched polyetheramine polyol may have a water solubility of at least 5 g/l, such as at least 10 g/l, such as at least 50 g/l, or even at least 100 g/l, at 20° C.
The branched polyetheramine polyol may be completely water miscible at 20° C.
In the branched polyetheramine polyol, essentially all of the amino groups in the branched polyetheramine polyol are tertiary amine groups. In this context, “essentially” means that at least 90%, such as at least 95%, such as at least 98%, or even at least 99% of the amino groups in the branched polyetheramine polyol are tertiary amine groups. The branched polyetheramine polyol may not have any detectable amounts of secondary and primary amino groups.
The branched polyetheramine polyol may contain on average less than 0.5 mol/kg of secondary and primary amino groups, if any. The polyetheramine polyol may contain on average less than 0.2 mol/kg, such as less than 0.1 mol/kg of secondary and primary amino groups, if any.
The branched polyetheramine polyol may contain on average from 4 to 8.2 mol/kg of tertiary amino groups. The polyetheramine polyol may contain on average from 5 to 8.0 mol/kg, such as from 5 to 7.9 mol/kg of tertiary amino groups.
The branched polyetheramine polyol may have any suitable amine number. The branched polyetheramine polyol may have an amine number from 100 to 700 mg KOH/g, such as from 200 to 500 mg KOH/g, determined according to the method described in DIN EN ISO 9702:1998. Besides determination of the total amine group content, this method allows for determination of the tertiary amine group content, the secondary amine group content, and the primary amine group content.
In addition to the amino groups, the branched polyetheramine polyol may contain hydroxyl groups. The branched polyetheramine polyol may have a hydroxyl number of at least 100 mg KOH/g, such as at least 200 mg KOH/g, or even at least 250 mg KOH/g. The branched polyetheramine polyol may have a hydroxyl number of up to 800 mg KOH/g, such as up to 700 mg KOH/g, or even up to 650 mg KOH/g. The branched polyetheramine polyol may have a hydroxyl number from 100 to 800 mg KOH/g, such as from 100 to 700 mg KOH/g, or even from 100 to 650 mg KOH/g. The branched polyetheramine polyol may have a hydroxyl number from 200 to 800 mg KOH/g, such as from 200 to 700 mg KOH/g, or even from 200 to 650 mg KOH/g. The branched polyetheramine polyol may have a hydroxyl number from 250 to 800 mg KOH/g, such as from 250 to 700 mg KOH/g, or even from 250 to 650 mg KOH/g.
As reported herein, the hydroxyl number was measured according to DIN 53240, part 2. All values for hydroxyl number reported herein were measured in this way.
The number of hydroxyl groups per molecule will depend on the number average molecular weight of the branched polyetheramine polyol and the degree of branching. The branched polyetheramine polyol may contain on average (number average) at least four, such as at least six, such as at least ten hydroxyl groups per molecule. However, in principle, there is no upper limit on the number of terminal or pendent functional groups. The branched polyetheramine polyol may contain on average (number average) at most 500, such as at most 200 terminal hydroxyl groups per molecule.
The branched polyetheramine polyol may have any suitable number average molecular weight (Mn). The branched polyetheramine polyol may have an Mn from 500 to 55,000 Daltons (Da=g/mol), such as from 1,000 to 40,000 Da. As reported herein, the Mn was determined by gel permeation chromatography using hexafluoroisopropanol as the mobile phase and polymethylmethacrylate as a standard.
The branched polyetheramine polyol may have any suitable weight average molecular weight (Mw). The branched polyetheramine polyol may have an Mw from 1,000 to 300,000 Daltons (Da=g/mol), such as from 2,000 to 200,000 Da, or even from 5,000 to 150,000 Da. As reported herein, the Mw was determined by gel permeation chromatography using hexafluoroisopropanol as the mobile phase and polymethylmethacrylate as a standard.
The branched polyetheramine polyol may have any suitable polydispersity, i.e. the ratio of Mw/Mn. The polyetheramine polyol may have a polydispersity from 1.1 to 25, such as from 1.5 to 20.
The branched polyetheramine polyol may have any suitable dynamic viscosity at 23° C. The branched polyetheramine polyol may have a dynamic viscosity at 23° C. from 5 to 200 Pa.s, such as from 8 to 150 Pa.s. As reported herein, the dynamic viscosity was determined according to ASTM D7042 at 23° C.
The branched polyetheramine polyol may have any suitable Hazen colour number. The branched polyetheramine polyol may have a Hazen colour number from 100 to 600 (APHA). As reported herein the Hazen colour number was determined according to DIN ISO 6271.
The branched polyetheramine polyol may have any suitable glass transition temperature (Tg). The branched polyetheramine polyol may have a Tg of up to 50° C., such as up to 30° C., or even up to 10° C. The branched polyetheramine polyol may have a Tg from −55 to 30° C., such as from −55 to 10° C.
The branched polyetheramine polyol may be formed from at least one trialkanolamine. For the avoidance of doubt, the trialkanolamine, and other components from which the branched polyetheramine polyol may be formed, are monomers which may undergo a polycondensation reaction to form the polyetheramine polyol polymer. Suitable trialkanolamines will be known to a person skilled in the art. Examples of suitable trialkanolamines include, but are not limited to, tri-C2-C8-alkanol amines, such as tri-C2-C4-alkanol amines, for example, triethanolamine, tri-n-propanolamine, triisopropanolamine, tri-n-butanolamine, triisobutanolamine and combinations thereof. The alkanol groups of the trialkanolamine may be different or may be identical, such as identical. Thus, the trialkanolamine may be selected from tri-C2-C8-alkanol amines, such as tri-C2-C4-alkanol amines, wherein the alkanol groups are identical.
The branched polyetheramine may be formed from triethanolamine, triisopropanolamine or a mixture thereof.
The branched polyetheramine polyol may comprise only monomers selected from trialkanolamines, such as tri-C2-C4-alkanolamines, for example, triethanolamine, triisopropanolamine and/or tri-n-propanolamine. Thus, the branched polyetheramine polyol may consist of only monomers selected from trialkanolamines, such as tri-C2-C4-alkanolamines, for example, triethanolamine, triisopropanolamine and/or tri-n-propanolamine.
However, the branched polyetheramine polyol may optionally be formed from at least one aliphatic or cycloaliphatic polyol. Thus, the branched polyetheramine polyol may be formed from at least one trialkanolamine and at least one aliphatic or cycloaliphatic polyol. Suitable examples of aliphatic or cycloaliphatic polyols include, but are not limited to, aliphatic diols, aliphatic polyols having more than 2 hydroxyl groups, cycloaliphatic diols, cycloaliphatic polyols having more than 2 hydroxyl groups and combinations thereof.
The aliphatic or cycloaliphatic polyols may comprise diols and aliphatic polyols having more than 2 hydroxyl groups. Examples of suitable aliphatic diols include C2-C20-diols, such as ethandiol, propandiol, butandiol, pentandiol, hexandiol, heptandiol, octandiol, and their structural isomers. Examples of suitable polyols having more than 2 hydroxyl groups are glycerol, pentaerythritol, trimethylolpropane, sorbitol, and the like. The polyols may also be alkoxylated, such as ethoxylated or propoxylated, for example. ethoxylated glycerol, propoxylated glycerol, ethylated pentaerythritol, propoxylated pentaerythritol, ethoxylated trimethylolpropane, propoxylated trimethylolpropane, ethoxylated sorbitol and propoxylated sorbitol. The degree of alkoxylation, i.e. the number average of alkyleneoxide moieties, may be up to 100, such as from 2 to 50.
Further examples of aliphatic diols include polyether diols of the general formula HO—((CH2)n—O)m—H, wherein n is 1 to 10, such as 2 to 4, and m is 2 to 100. Suitable examples of polyether diols include, but are not limited to, polyethylene glycol, polypropylene glycol, polytetramethylene glycol and copolymers thereof.
The aliphatic or cycloaliphatic polyol may comprise an aliphatic or cycloaliphatic C2-C8-polyol.
The branched polyetheramine polyol may be formed from monomers comprising at least one trialkanolamine or a mixture of at least one trialkanolamine with an aliphatic or cycloaliphatic polyol.
The branched polyetheramine polyol may be formed from monomers comprising at least one trialkanolamine, such as tri-C2-C4-alkanolamine, or even triethanolamine, triisopropanolamine or a mixture thereof, and at least one aliphatic or cycloaliphatic C2-C8-polyol.
The branched polyetheramine polyol may be formed from monomers comprising triethanolamine, triisopropanolamine or a mixture thereof and at least one further polyol, such as an aliphatic or cycloaliphatic C2-C8-polyol.
The branched polyetheramine polyol may comprise any suitable amount of trialkanolamine monomer. The branched polyetheramine polyol may comprise at least 50 wt %, such as at least 70 wt %, or even at least 80 wt % trialkanolamine(s), based on the total solid weight of the monomers from which the branched polyetheramine polyol is formed.
The branched polyetheramine polyol may be formed from monomers comprising from 50 to 100 mol % trialkanolamine(s) and 0 to 50 mol % aliphatic or cycloaliphatic polyol(s), such as from 70 to 100 mol % trialkanolamine(s) and 0 to 30 mol % aliphatic or cycloaliphatic polyol(s), or even from 80 to 100 mol % trialkanolamine(s) and 0 to 20 mol % aliphatic or cycloaliphatic polyol(s), based on the total molar amount of the monomers from which the branched polyetheramine polyol is formed.
The branched polyetheramine polyol may be stable at room temperature for a prolonged period, such as for at least 10 weeks, for example. The polyetheramine polyols may be stable without exhibiting instances of clouding, precipitation, and/or significant increase in viscosity.
The branched polyetheramine polyol may be used without chemical modification or derivatization. However, a derivative of the branched polyetheramine polyol can optionally be used. Derivatives include those obtained by alkoxylation of the hydroxyl end groups of the non-derivatized branched polyetheramine polyol. Likewise, it is possible to modify the non-derivatized branched polyetheramine polyol with hydrophobic groups or hydrophilic groups.
The polymeric coating binder may comprise any suitable amount of the branched polyetheramine polyol. The polymeric coating binder may comprise from 0.01 to 10 wt %, such as from 0.05 to 7.5 wt %, or even from 0.1 to 5 wt % of the branched polyetheramine polyol based on the total weight of the carboxylated polymer of the aqueous polymer latex.
The film forming carboxylated polymer and the branched polyetheramine polyol may be present in any suitable form. For example, the film forming carboxylated polymer and branched polyetheramine polyol may be blended together, the film forming carboxylated polymer and branched polyetheramine polyol may be in the form of a block copolymer and/or the film forming carboxylated polymer and branched polyetheramine polyol may be grafted together.
The polymeric coating binder comprises the aqueous polymer latex of a film forming carboxylated polymer as described herein, the branched polyetheramine polyol as described herein and water. The polymeric coating binder may optionally comprise further components such as, for example, dispersants, biocides, rheology modifiers, coalescing agents and/or defoamers. Suitable further components will be known to a person skilled in the art.
The coating composition comprises at least 10 wt % (percent by weight), such as at least 10.5 wt %, such as at least 11 wt %, such as at least 11.5 wt %, or even at least 12 wt % of the polymeric coating binder based on the total weight of the coating composition. The coating composition may comprise up to 20 wt %, such as up to 19 wt %, such as up to 18 wt %, such as up to 17 wt %, such as up to 16 wt %, or even up to 15 wt % of the polymeric coating binder based on the total weight of the coating composition. The coating composition may comprise from 10 to 19 wt %, such as from 10 to 18 wt %, such as from 10 to 17 wt %, such as from 10 to 16 wt %, or even from 10 to 15 wt % of the polymeric coating binder based on the total weight of the coating composition. The coating composition may comprise from 10.5 to 20 wt %, such as from 10.5 to 19 wt %, such as from 10.5 to 18 wt %, such as from 10.5 to 17 wt %, such as from 10.5 wt % to 16 wt % or even from 10.5 to 15 wt % of the polymeric coating binder based on the total weight of the coating composition. The coating composition may comprise from 11 to 20 wt %, such as from 11 to 19 wt %, such as from 11 to 18 wt %, such as from 11 to 17 wt %, such as from 11 wt % to 16 wt % or even from 11 to 15 wt % of the polymeric coating binder based on the total weight of the coating composition. The coating composition may comprise from 11.5 to 20 wt %, such as from 11.5 to 19 wt %, such as from 11.5 to 18 wt %, such as from 11.5 to 17 wt %, such as from 11.5 wt % to 16 wt % or even from 11.5 to 15 wt % of the polymeric coating binder based on the total weight of the coating composition. The coating composition may comprise from 12 to 20 wt %, such as from 12 to 19 wt %, such as from 12 to 18 wt %, such as from 12 to 17 wt %, such as from 12 wt % to 16 wt % or even from 12 to 15 wt % of the polymeric coating binder based on the total weight of the coating composition.
The coating composition may comprise a first filler and a second filler. The first filler may be different from the second filler (and both the first filler and the second filler may be different from the polymeric coating binder).
The first filler may comprise expanded polymeric microspheres. By “microsphere”, and like terms, as used herein is meant particles with an average (D50) particle size from 0.1 to 500 microns (μm), such as from 1 to 300 μm, such as from 5 to 200 μm, such as from 10 to 80 μm, or even from 10 to 50 μm. The microspheres may be generally spherical. The microspheres may be solid or may comprise a cavity. The microspheres may comprise a cavity. The cavity may be empty or may comprise a gas and/or a liquid. The cavity may be completely closed off for material exchange with the environment or may be open towards the environment.
As reported herein, the particle size was determined according to the International Standard ISO 13320:2009 (“Particle size analysis—Laser diffraction methods”) using laser diffraction analysis on a Malvern type analyser. Suitable Malvern systems include the Malvern 2000, Malvern MasterSizer (such as Mastersizer S), Malvern 2600 and Malvern 3600 series. All values for average particle size reported herein were measured in this way.
The first filler may comprise any suitable expanded polymeric microspheres. Suitable examples of expanded polymeric microspheres include, but are not limited to, expanded particles of a polymer selected from: a polyurethane, a polystyrene, a polyvinylidene chloride, a polyacrylate, a polymethyl methacrylate (PMMA), a polyacrylonitrile, or copolymers or combinations thereof.
The first filler may comprise expanded particles of a copolymer of vinylidene chloride and acrylonitrile.
The first filler may comprise pure polymeric particles.
The first filler may comprise a commercially available filler. Suitable commercially available fillers for the first filler include, but are not limited to, those sold under the trade name Micropearl (RTM) microspheres available from Lehmann & Voss, those sold under the trade name Expancel (RTM) available from AkzoNobel, those sold under the trade name Advancell (RTM) expandable microspheres available from Sekisui Chemical Co., those sold under the trade name Microsphere (RTM), such as Microsphere F-E and Microsphere F-DE, available from Matsumoto Yushi Seiyaku Co. and combinations thereof.
The first filler may have any suitable true density. The first filler may have a true density of at most 100 kg/m3, such as at most 75 kg/m3, such as at most 60 kg/m3, such as at most 50 kg/m3, or even at most 40 kg/m3 as determined according to ASTM D2840 (1969) using a gas displacement pycnometer.
The first filler may comprise expanded particles having a true density of up to 500 kg/m3 determined by gas displacement pycnometer according to ASTM D2840 (1969).
The coating composition may comprise a second filler. The second filler may comprise expanded glass particles. The second filler may comprise expanded perlite particles, expanded silica glass particles and/or combinations thereof. Examples of suitable expanded silica glass particles include, but are not limited to, borosilicate glass, fused borosilicate glass, soda-lime-borosilicate glass, natural volcanic ore and combinations thereof.
The second filler may comprise expanded perlite particles, expanded fused borosilicate glass particles or combinations thereof.
The second filler may comprise expanded fused borosilicate glass particles.
The second filler may have any suitable silica content. The second filler may have a silica content from 50 to 100 wt %, such as from 60 to 90 wt %, such as from 70 to 80 wt %, such as from 75 to 80 wt %, or even from 75 to 78 wt % based on the total solid weight of the second filler.
The second filler may have any suitable true density. The second filler may have a true density of up to 750 kg/m3, such as up to 600 kg/m3, such as up to 500 kg/m3, or even up to 400 kg/m3 as determined according to ASTM D2840 (1969) using a gas displacement pycnometer.
The second filler may comprise a commercially available filler. Suitable commercially available fillers include, but are not limited to, those sold under the trade names Poraver (RTM) available from Dennert Poraver, those sold under the trade name Sphericel (RTM) available from Potters Industries, those sold under the trade name Metapor (RTM) available from Dennert Poraver, Glass bubbles manufactured by 3M or combinations thereof.
The coating composition may comprise any suitable amount of the first filler and the second filler combined. The coating composition may comprise at least 0.1% by weight and at most 25% by weight of the first filler and the second filler combined based on the total weight of the coating composition, such as at least 0.5% by weight and at most 20% by weight, such as at least 1.5% by weight and at most 15% by weight, or even at least 3% by weight and at most 10% by weight.
The coating composition may comprise any suitable weight ratio of first filler to second filler. The weight ratio of first filler to second filler may be at least 1:40, such as at least 1:30, such as at least 1:20, such as at least 1:18, or even at least 1:15. The weight ratio of first filler to second filler may be up to 1:10, such as up to 1:5, such as up to 1:7, such as up to 1:10, such as up to 1:12, or even up to 1:14. The weight ratio of first filler to second filler may be from 1:40 to 1:1, such as from 1:30 to at most 1:5, such as from 1:20 to 1:7, such as from 1:18 to at most 1:10, such as from 1:15 to 1:12, or even from 1:15 to 1:14. The effect of the above mentioned weight ratios of first filler to the second filler may result in an optimal balance between low density and coating performance. Typically, the more first filler used compared to the second filler, the lower the density but the higher the impact on coating performances.
The first filler and the second filler combined may have a true density of at most 750 kg/m3, such as at most 600 kg/m3, such as at most 500 kg/m3, or even at most 400 kg/m3 as determined according to ASTM D2840 (1969) using a gas displacement pycnometer.
The coating composition may be substantially free from expanded polymeric microspheres. The coating composition may be substantially free from expanded perlite particles, expanded fused borosilicate glass particles or combinations thereof. The coating composition may be substantially free from i) expanded polymeric microspheres; and ii) expanded perlite particles, expanded fused borosilicate glass particles or combinations thereof.
By the term “substantially free from”, it is meant less than 0.1 wt % by dry weight of the coating composition.
The coating composition may be essentially free from expanded polymeric microspheres. The coating composition may be essentially free from expanded perlite particles, expanded fused borosilicate glass particles or combinations thereof. The coating composition may be essentially free from i) expanded polymeric microspheres; and ii) expanded perlite particles, expanded fused borosilicate glass particles or combinations thereof.
By the term “essentially free from”, it is meant less than 0.01 wt % by dry weight of the coating composition.
The coating composition may be completely free from expanded polymeric microspheres. The coating composition may be completely free from expanded perlite particles, expanded fused borosilicate glass particles or combinations thereof. The coating composition may be completely free from i) expanded polymeric microspheres; and ii) expanded perlite particles, expanded fused borosilicate glass particles or combinations thereof.
The coating compositions may optionally comprise at least one colourant. Suitable colourants will be known to a person skilled in the art. Examples of suitable colourants include, but are not limited to, inorganic pigments, organic pigments, transparent pigments, non-transparent pigments and combinations thereof. Examples of such pigments include, but are not limited to, titanium dioxide, iron oxides, mixed metal oxides, bismuth vanadate, chromium oxide green, ultramarine blue, carbon black, lampblack, monoazo and disazo pigments, anthraquinones, isoindolinones, isoindolines, quinophthalones, phthalocyanine blues and greens, dioxazines, phthalocyanines, thioindigos, quinacridones and diketo-pyrrolopyrroles; extender pigments including ground and crystalline silica, barium sulphate, magnesium silicate, calcium silicate, mica, micaceous iron oxide, calcium carbonate, zinc oxide, aluminium hydroxide, aluminium silicate and aluminium silicate, gypsum, feldspar, talcum, kaolin, and the like; and combinations thereof.
The coating compositions may comprise any suitable amount of colourant. It will be understood that the amount of colourant that is used may vary, depending on the particular end use of the coating composition and can be zero when a clear coating composition is desired.
The coating composition may comprise up to 50 wt %, for example from 5 to 40 wt %, or even up to 30 wt % colourant based on the total solid weight of the coating composition. Depending on the particular end use of the coating composition, the coating composition may comprise up to 20 wt %, or even up to 15 wt % colourant based on the total solid weight of the coating composition. The coating composition may comprise from 10 to 20 wt % colourant based on the total solid weight of the coating composition.
The coating composition may have any suitable ratio of pigment volume concentration (PVC) over critical pigment volume concentration (cPVC). The ratio of the pigment volume concentration (PVC) over the critical pigment volume concentration (cPVC) may be from 0.5 to 1.3, such as from 0.6 to 1.25, such as from 0.7 to 1.2, such as from 0.75 to 1.15, such as from 0.9 to 1.1.
For the avoidance of doubt, reference to the term “colourant” does not include fillers which may also act as pigments. For example, TiO2 in the base paint as a filler does not form part of the “colourant”.
The coating compositions may optionally comprise one or more further filler(s), such as expanded fillers, non-expanded fillers and/or combinations thereof. For the avoidance of doubt, the further filler may be different to the first and second fillers described above. Examples suitable non-expanded fillers include, but are not limited to: silica, such as precipitated silicas; clay; mica; dolomite; talc; zinc borate; magnesium carbonate; calcium oxide; calcium carbonate; calcium silicate; sodium aluminium silicate; calcium metasilicate; titanium dioxide; barium sulphate; and combinations thereof. The one or more further non-expanded filler may comprise a fibrous filler, such as milled glass fibres and/or milled carbon fibres. Examples of suitable expanded fillers are as described above in relation to the first filler and/or second filler, on the proviso that the one or more further filler(s) is different from the first filler and the second filler.
The coating composition may comprise any suitable amount of colourant and/or filler. For the avoidance of doubt, in this context, the amount of filler is calculated on the basis of the total amount of filler present in the coating composition (including the first filler, second filler and further filler(s)). The coating composition may comprise from 30 to 75 wt %, such as from 35 to 70 wt %, such as from 40 to 65 wt % of colourant and/or filler based on the total weight of the coating composition.
The first filler and second filler where present are expanded fillers and, as such, may be lightweight fillers. The one or more further filler(s) may comprise a lightweight filler. By “lightweight filler”, and like terms, as used herein is meant that the filler has a true density of at most 500 kg/m3, as determined according to ASTM D2840 (1969) using a gas displacement pycnometer. For the avoidance of doubt, a lightweight filler does not have to be an expanded filler so long as it has the required true density.
The coating composition may comprise any suitable total amount of lightweight filler (i.e. total amount of lightweight filler including the first filler, the second filler and any further lightweight filler). The coating composition may comprise from 1 to 70 wt %, such as from 5 to 50 wt %, such as from 10 to 35 wt %, such as from 15 to 30 wt %, or even from 20 to 25 wt % of the lightweight filler based on the total solid weight of the fillers present in the coating composition. In this context, titanium dioxide is seen as a filler, such as a non-expanded filler. Titanium dioxide is a filler that also functions as a colourant. For the avoidance of doubt, when taking the weight into account, titanium dioxide should be classed as a filler and not as a colourant or additive.
The coating composition of the present invention has a total solids content of at least 60 wt %. The coating composition may have a total solids content of at least 60.5 wt %, such as at least 61 wt %, such as at least 62 wt %, such as at least 63 wt %, or even at least 64 wt %. The coating composition may have a total solids content of up to 80 wt %, such as up to 79 wt %, or up to 77 wt %, such as up to 75 wt %. The coating composition may have a total solids content of up to 73 wt %, such as up to 70 wt %, or up to 69 wt %, such as up to 68 wt %.
The coating composition may have a total solids content of from 60 to 80 wt %, such as from 60 to 79 wt %, such as from 60 to 77 wt %, such as from 60 to 75 wt % or even from 60 to 73 wt %, such as from to 60 to 70 wt %, such as from 60 to 69 wt % or even from 60 to 68 wt % based on the total weight of the coating composition.
The coating composition may have a total solids content of from 60.5 to 80 wt %, such as from 60.5 to 79 wt %, such as from 60.5 to 77 wt %, such as from 60.5 to 75 wt % or even from 60.5 to 73 wt %, such as from to 60.5 to 70 wt %, such as from 60.5 to 69 wt % or even from 60.5 to 68 wt % based on the total weight of the coating composition.
The coating composition may have a total solids content of from 61 to 80 wt %, such as from 61 to 79 wt %, such as from 61 to 77 wt %, such as from 61 to 75 wt % or even from 61 to 73 wt %, such as from to 61 to 70 wt %, such as from 61 to 69 wt % or even 61 to 68 wt % based on the total weight of the coating composition.
The coating composition may have a total solids content of from 62 to 80 wt %, such as from 62 to 79 wt %, such as from 62 to 77 wt %, such as from 62 to 75 wt % or even from 62 to 73 wt %, such as from to 62 to 70 wt %, such as from 62 to 69 wt % or even 62 to 68 wt % based on the total weight of the coating composition.
The coating composition may have a total solids content of from 63 to 80 wt %, such as from 63 to 79 wt %, such as from 63 to 77 wt %, such as from 63 to 75 wt % or even from 63 to 73 wt %, such as from to 63 to 70 wt %, such as from 63 to 69 wt % or even 63 to 68 wt % based on the total weight of the coating composition.
The coating composition may have a total solids content of from 64 to 80 wt %, such as from 64 to 79 wt %, such as from 64 to 77 wt %, such as from 64 to 75 wt % or even from 64 to 73 wt %, such as from to 64 to 70 wt %, such as from 64 to 69 wt % or even 64 to 68 wt % based on the total weight of the coating composition.
As reported herein, the solid content was measured at 125° C. for two hours according to ISO 3251:2008. All values for solid content reported herein were measured in this way.
The coating composition may be water-borne, solvent-borne or a powder.
The coating composition may be a water-borne coating composition.
The water-borne coating composition may comprise any suitable amount of water. The water-borne coating composition may comprise up to 40 wt % water, such as from 10 to 40 wt % water based on the total weight of the coating composition. Water may be added to the coating composition as such, e.g. tap water, or may be added in combination with another component of the coating composition, such as the polymeric coating binder, which may be emulsified or suspended in water. For example, the polymeric coating binder may be added to the coating composition as suspension or emulsion, such as a 45 to 55 wt % suspension based on the total weight of the polymeric coating binder.
The coating compositions may optionally include one or more solvents, such as organic solvents. Suitable solvents will be known to a person skilled in the art. Examples of suitable solvents include, but are not limited to, aliphatic solvents, such as VM&P NAPTHA (available from Klean Strip); acetates, such as butyl acetate and hexyl acetate; mono and dialkyl ethers of ethylene, propylene and diethylene glycols, such as ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol diethyl ether, propylene glycol monomethyl ether, and dipropylene glycol ether; monoalkyl ethers of monoester glycols, such as ethylene glycol monoethylether acetate and propylene glycol monomethyl ether acetate; and combinations thereof. The coating composition may comprise any suitable amount of solvent. The coating composition may comprise up to 20 wt % solvent based on the total solid weight of the polymeric coating binder. The use of one or more solvent(s) may facilitate film forming, adjust drying properties and/or contribute to the application performances.
The coating composition may comprise up to 40 wt % of water and solvents (combined). For example, the coating composition may comprise up to 32 wt % or up to 35 wt % of water and solvents (combined).
It will be appreciated that the coating compositions may comprise the balance of the compositions that is not “total solids content” as “water and solids (combined)” to make 100 wt % total. For example, where the total solids content of the coating composition is, for example, from 61 wt % to 69 wt %, then the water and solids (combined) may be present in an amount of from 39 wt % to 31 wt %. Other balancing amounts where the total solids content is different will be readily understood by a person skilled in the art.
The coating compositions may optionally comprise other materials (or additives) well known in the art of formulating coatings. Examples of suitable additives that may be added to the composition may be found in Additives Guide, Paint & Coatings Magazine, May 2006, hereby incorporated by reference thereto. Suitable examples of additives include, but are not limited to, catalysts, other pigments and pigment pastes, dyes, surface active agents, stabilizers, wetting agents, thixotropic agents, anti-sagging agents, anti-oxidants, bactericides, fungicides, algaecides, anti-settling agents, insecticides, antifoaming agents, slip agents, flow and levelling agents, rheological modifiers, UV-absorbers, HALS-radical scavengers, matting agents, waxes, mineral oils, flame retardants, loss of dry inhibitors, optical brighteners, adhesion promoters, diluents, elastomers, plasticizers, air release agents, absorbents, anti-crater additives, coalescing agents, reinforcing agents, polymeric opacifier dispersing aids, plasticizers, thixotropes, substrate wetting agents, odorants, corrosion inhibitors and corrosion-inhibitive pigments, additional hardeners, additional curable compounds and combinations thereof. It will be appreciated by a person skilled in the art that the use of the aforementioned materials will typically depend on the particular end use of the coating composition.
Examples of suitable surface active agents include, but are not limited to, any of the well-known anionic, cationic or non-ionic surfactants or dispersing agents.
Examples of suitable antioxidants and UV light absorbers include, but are not limited to, those sold under the trademarks IRGANOX and TINUVIN (RTM) commercially available from BASF.
Examples of suitable thixotropes include, but are not limited to, fumed silica, bentonite, stearic acid-coated calcium carbonate, polyamide, fatty acid/oil derivatives and combinations thereof.
The additives may be selected from the group comprising: wetting agents, antifoaming agents, rheological modifiers, coalescing agents, dispersing aids and combinations thereof.
The coating compositions may comprise any suitable amount of the additives, when used. The coating composition may comprise up to 40 wt %, such as up to 30 wt %, such as up to 20 wt %, such as up to 15 wt %, or even up to 10 wt % of the additives based on total weight of the coating composition.
The coating composition may include a further polymeric coating binder, selected from the group comprising: (meth)acrylic coating binder, vinylic coating binder, silicone-based coating binder, siloxane-based binder, or any mixture thereof. The further polymeric coating binder may comprise a vinyl acetate ethylene (VAE) coating binder, a (meth)acrylic coating binder or a mixture thereof, such as a (meth)acrylic coating binder. The further coating binder may comprise a copolymer, such as a styrene (meth) acrylic copolymer. The further coating binder may include a copolymer of vinyl ester, ethylene and acrylic acid ester.
The further polymeric coating binder may have a weight average molecular weight (Mw) of at least 5,000 Da, such as at least 25,000 Da, at least 50,000 Da, or even at least 100,000 Da. The further polymeric coating binder may have a weight average molecular weight (Mw) of less than or equal to 1,000,000 Da, such as less than or equal to 750,000 Da, less than or equal to 600,000 Da or even less than or equal to 500,000 Da.
The coating compositions may be formulated as a 1K composition (also known as a one-component composition or one package composition). By “1K”, “one component composition”, “one package composition”, and like terms, as used herein is meant a stable one package composition. A 1K, one component or one package composition will be understood as referring to a composition wherein all of the components are maintained in the same container after manufacture, during storage etc. A 2K composition or a multi-component composition will be understood as referring to a composition wherein various components are maintained separately until just prior to application.
The coating compositions may provide any suitable finish upon curing. The coating composition may comprise a matt finish upon curing, an egg-shell finish upon curing or a semi-gloss finish upon curing. The coating compositions may provide a gloss level upon curing of up to 45%, such as up to 30%, such as up to 20%, such as up to 15%, such as up to 10%, such as up to 7%, such as up to 5%, or even up to 2.5%, as determined according to NF EN ISO 2813 (as measured using a gloss meter, under an angle of 60° and on a 2×200 μm cured layer of coating composition). It will be appreciated by a person skilled in the art that the gloss level will typically depend upon the particular finish, i.e. matt, egg-shell or semi-gloss, which is desired. For example, when a matt finish is desired, the gloss level of the cured coating composition may be up to 20%, such as up to 15%, such as up to 10%, such as up to 7%, such as up to 5%, or even up to 2.5%, as determined according to NF EN ISO 2813 (as measured using a gloss meter, under an angle of 85° and on a 2×200 μm cured layer of coating composition).
The coating compositions may have any suitable volatile organic compound (VOC) content. By “volatile organic compound”, and like terms, as used herein is meant to any organic compound having an initial boiling point less than or equal to 250° C. measured at a standard atmospheric pressure of 101.3 kPa. The coating compositions may have a VOC content of at most 150 g/l, such as at most 100 g/l, such as at most 75 g/l, such as at most 50 g/l, such as at most 40 g/l, or even at most 20 g/l, or even at most 10 g/l, or even at most 5 g/l, or even at most 1 g/l as determined according to ISO 1 1890-2 (2013).
The cured coating composition may have any suitable water-vapour diffusion-equivalent air layer thickness (Sd). The cured coating composition may have a water-vapour diffusion-equivalent air layer thickness (Sd) from 0.5 to 1.5 m, such as from 0.7 to 1.3 m, or even from 0.8 to 1.2 m, as determined according to ISO 7783-2 (201 1) 8.1.1. Suitably, the cured coating composition may have a water-vapour diffusion-equivalent air layer thickness (Sd) of 1.3 or lower, such as 1.2 or lower.
The cured coating compositions may have any suitable water-vapour transmission (V). The cured coating compositions may have a water-vapour transmission (V) from 30 to 420 g/m2, such as from 21 to 420 g/m2, such as from 35 to 300 g/m2, or even from 42 to 210 g/m2, as determined according to ISO 7783-2 (201 1) 8.1.1.
The coating compositions may be applied to various substrates. Suitable substrates include, but are not limited to: wood; paper; dry wall; synthetic materials, such as plastics, including elastomeric substrates; glass; ceramic; metals, such as iron, steel or aluminium; concrete; plasterboard; gypsum-board; mortar; brick; and the like; and combinations thereof.
The substrate may comprise concrete, dry walls, brick or combinations thereof.
Thus, there is also provided a substrate coated on at least a portion thereof with a coating, the coating being derived from a coating composition according to the present invention.
The substrates may be pre-treated before application of the coating composition. The substrates may be post-treated after application of the coating composition. The substrates may be post-treated after application of the coating composition with any other compositions (which will be known to a person skilled in the art).
The coating compositions of the present invention may be used and/or formulated as a coating, varnish, lacquer, paint, stain, enamel, printing ink and/or floor covering. Thus, there is also provided the use of the coating compositions of the present invention as a coating, varnish, lacquer, paint, stain, enamel, printing ink or floor covering.
The coating composition may be a wall paint, such as an interior wall paint or an exterior wall paint.
Wall paints typically differ from metal coatings, for example. A metal coating would typically use a polymeric binder that would be suitable for metal application that requires adhesion on metallic material, anti-flash rust additives, anticorrosive properties and low water vapour permeability. Wall paints typically have high water vapour permeability, which is too high for metal, have poor adhesion on metal and have no metal protection ability (i.e. have no anticorrosive properties).
The coating composition may be an interior wall masonry paint.
The coating composition may be an exterior wall masonry paint.
Thus, there is provided the use of the coating compositions of the present invention as an interior and/or exterior wall masonry paint.
The coating compositions may be applied to the substrate by any suitable methods. Methods of applying to coating compositions will be known to a person skilled in the art. Suitable application methods for the coating compositions include, but are not limited to, spreading (e.g., with paint pad or doctor blade, or by brushing or rolling), spraying (e.g., air-fed spray, airless spray, hot spray, and electrostatic spray), flow coating (e.g., dipping, curtain coating, roller coating, and reverse roller coating), electrodeposition and combinations thereof. Suitable application methods are described in R. Lambourne, Editor, Paint and Surface Coating: Theory and Practice, Eilis Horwood, 1987, page 39 et seq., for example.
The coating compositions may be applied to the substrate by spreading and/or spraying, such as by brushing, rolling or airless spraying.
The coating compositions may be applied to the substrate and cured. The coating compositions may be cured by any suitable method. For example, the coating compositions may be cured by heat curing or chemically curing. The coating compositions may be fully cured at ambient temperature conditions, for example in the range from 0 to 50° C., such as from 1 to 45° C., such as from 3 to 40° C., or even from 5 to 35° C. Curing of the coating compositions may proceed very rapidly at the aforementioned temperature ranges.
The coating compositions may be used as a single coating, a top coating, a base coating in a two-layered system, or one or more layers of a multi-layered system including a top coating composition, base coating composition, or as a primer layer. A typical opaque system may comprise: 1 layer of primer and 1 or 2 layers of top coat (a total of 2 to 3 layers), for example. Alternative opaque systems may comprise: 1 primer layer, 1 layer of mid coat and 1 layer top coat, for example.
As used herein, unless otherwise expressly specified, all numbers such as those expressing values, ranges, amounts or percentages may be read as if prefaced by the word “about”, even if the term does not expressly appear. Also, the recitation of numerical ranges by endpoints includes all integer numbers and, where appropriate, fractions subsumed within that range (e.g. 1 to 5 can include 1, 2, 3, 4 when referring to, for example, a number of elements, and can also include 1.5, 2, 2.75 and 3.80, when referring to, for example, measurements). The recitation of end points also includes the end point values themselves (e.g. from 1.0 to 5.0 includes both 1.0 and 5.0). Any numerical range recited herein is intended to include all sub-ranges subsumed therein.
Singular encompasses plural and vice versa. For example, although reference is made herein to “a” polyester imide poylmer, “a” crosslinker material, “an” imide containing moiety, “an” acid group, “an” alcohol group, and the like, one or more of each of these and any other components can be used. As used herein, the term “polymer” refers to oligomers and both homopolymers and copolymers, and the prefix “poly” refers to two or more.
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as is commonly understood by one of skill in the art. All publications referenced herein are incorporated by reference thereto.
The terms “comprising”, “comprises” and “comprised of” as used herein are synonymous with “including”, “includes” or “containing”, “contains”, and are inclusive or open-ended and do not exclude additional, non-recited members, elements or method steps. Additionally, although the present invention has been described in terms of “comprising”, the coating compositions detailed herein may also be described as “consisting essentially of” or “consisting of”.
As used herein, the term “and/or,” when used in a list of two or more items, means that any one of the listed items can be employed by itself or any combination of two or more of the listed items can be employed. For example, if a list is described as comprising group A, B, and/or C, the list can comprise A alone; B alone; C alone; A and B in combination; A and C in combination, B and C in combination; or A, B, and C in combination.
All of the features contained herein may be combined with any of the above aspects in any combination.
For a better understanding of the invention, and to show how embodiments of the same may be carried into effect, reference will now be made, by way of example, to the following examples.
Coating compositions according to the present invention, Examples 1, 2 and 3 were prepared according to the formulations in Table 1. All parts in Table 1 are given in parts by weight (pbw) unless specified otherwise.
Table 2 shows the dry wt % of the components of Examples 1, 2 and 3 and the solids content of the coating compositions in these examples.
Comparative coating compositions, Comparative Examples 1 to 5, were prepared according to the formulations in Table 1. All parts in Table 1 are given in parts by weight (pbw) unless specified otherwise.
Table 2 shows the dry wt % of the components of Comparative Examples 1 to 5 and the solids content of the coating compositions in these examples.
The coatings were tested for early rain resistance using the method disclosed below and for water-vapour diffusion-equivalent air layer thickness (Sd) according to ISO 7783-2 (201 1) 8.1.1. The results are shown in Table 3.
Paint is applied on fiber-cement panels primed with a quartz containing blue primer to create a surface roughness and colour contrast. The coating composition is applied to the blue panels at a given spreading rate and drying conditions are controlled (humidity and temperature). The coated panels are then washed (subjected to a water rinsing spray) at a given time interval. The results are given a score between 0 and 3, which is evaluated using the following scale:
Panels were prepared according to the Rain Resistance Test protocol and coatings applied thereto with a spreading rate of 7 m2/l The rain resistance test was undertaken under regular conditions (humidity of 50% and temperature of 23° C.). The panels were then subjected to a water rinsing spray after 10 minutes of applying the coating composition and the results graded 0 to 3, as discussed above.
Panels were prepared according to the Rain Resistance Test protocol and coatings applied thereto with a spreading rate of 7 m2/l. The rain resistance test was undertaken under severe conditions (humidity of 85% and temperature of 5° C.). The panels were the evaluated to give the drying time required to achieve a score of 3 on the Rain Resistance Test discussed above.
A measure of vapour transmissibility measured according to ISO 7783-2 (201 1) 8.1.1
A classification of the water vapour transmission rate of the coating system, measured according to EN 1062-1 [2004]. A higher V rating indicates a lower vapour permeability rating.
The results show that the coatings according to the present invention display improved early rain resistance properties under normal conditions and severe conditions compared to the comparative examples. The results also show that if the amount of polymeric coating binder is too high, it has an unacceptable detrimental effect on the water-vapour diffusion-equivalent air layer thickness (Sd), leading to a different V classification under EN 1062-1 [2004].
Attention is directed to all papers and documents which are filed concurrently with or previous to this specification in connection with this application and which are open to public inspection with this specification, and the contents of all such papers and documents are incorporated herein by reference.
All of the features disclosed in this specification (including any accompanying claims, abstract and drawings), and/or all of the steps of any method or process so disclosed, may be combined in any combination, except combinations where at least some of such features and/or steps are mutually exclusive.
Each feature disclosed in this specification (including any accompanying claims, abstract and drawings) may be replaced by alternative features serving the same, equivalent or similar purpose, unless expressly stated otherwise. Thus, unless expressly stated otherwise, each feature disclosed is one example only of a generic series of equivalent or similar features.
The invention is not restricted to the details of the foregoing embodiment(s). The invention extends to any novel one, or any novel combination, of the features disclosed in this specification (including any accompanying claims, abstract and drawings), or to any novel one, or any novel combination, of the steps of any method or process so disclosed.
| Number | Date | Country | Kind |
|---|---|---|---|
| 20188963.1 | Jul 2020 | EP | regional |