Claims
- 1. A solvent borne coating composition comprising:
- (A) at least one component which contains hydroxyl groups, comprising
- (A1) from 20 to 60% by weight of at least one polyester having an OH number of 90 to 130, a molecular weight of 1300 to 3500 and a polydispersity of from 5 to 50, and
- (A2) from 40 to 80% by weight of at least one polyacrylate resin which contains hydroxyl groups and has been prepared, at least partially, in the presence of component (A1), from
- (a) from 5 to 50% by weight of one or more monomers selected from the group consisting of 4-hydroxy-n-butyl acrylate, 4-hydroxy-n-butyl methacrylate, 3-hydroxy-n-butyl acrylate, 3-hydroxy-n-butyl methacrylate and hydroxyethyl methacrylate,
- and monomers selected from the group consisting of
- (b) ethylenically unsaturated, copolymerizable monomers containing hydroxyl groups and different from (a) and mixtures of such monomers,
- (c) aliphatic and cycloaliphatic esters of methacrylic acid, aliphatic and cycloaliphatic esters of acrylic acid which are different from (a) and (b), and mixtures of such monomers,
- (d) copolymerizable vinyl esters different from (a), (b) and (c), and mixtures of such monomers,
- (e) aromatic vinyl hydrocarbons different from (a), (b), (c) and (d) and mixtures of such monomers, and
- (f) additional ethylenically unsaturated monomer which is different from (a), (b), (c), (d) and (e) or a mixture of such monomers, the sum of the proportions by weight of monomers (a) to (f) being in each case 100% by weight,
- (B) at least one crosslinking agent, and
- (C) a compound selected from the group consisting of aromatic mono-and polycarboxylic acids, anhdyrides of aromatic polycarboxylic acids and mixtures thereof, wherein said compound (C) is added to component (A) after its preparation or to the coating composition.
- 2. Coating composition according to claim 1, characterized in that component (A) comprises
- (A1) from 30 to 50% by weight of at least one polyester (A1) and
- (A2) from 50 to 70% by weight of at least one polyacrylate resin (A2).
- 3. Coating composition according to claims 1 or 2 wherein the polyester (A1) has an OH number of from 90 to 130 mg of KOH/g, an acid number of less than 10 mg of KOH/g, a number-average molecular weight of from 1300 to 3500 and a polydispersity of from 5 to 50.
- 4. Coating composition according to claim 1, wherein the polyester (A1) has an OH number of from 90 to 110 mg of KOH/g, an acid number of from 1 to 8 mg of KOH/g, a number-average molecular weight of from 1350 to 2000 and a polydispersity of from 5 to 10.
- 5. A coating composition according to claim 1 or 4 wherein the acrylate resin (A2) has an OH number from 70 to 105 mg of KOH/g and an acid number of from 0 to 8 mg KOH/g.
- 6. A coating composition according to claim 1 or 4 wherein component (A) has an OH number of from 80 to 150, and an acid number of from 0.1 to 10 mg KOH/g.
- 7. A coating composition according to claim 1 or 4 wherein component (A) has an OH number of from 85 to 105 mg KOH/g and an acid number of from 4 to 8 mg KOH/g.
- 8. Coating composition according to claim 1, wherein C comprises from 0.4 to 0.9% by weight, based on the weight of component (A) without solvent.
- 9. Coating composition according to claim 1, wherein a compound C is selected from the group consisting of benzoic acid, alkyl-substituted benzoic acid, alkoxy-substituted benzoic acid, and phthalic anhydride, and is added to component (A) after its preparation.
- 10. Coating composition according to claim 1 wherein at least 40% by weight of component (A2) has been prepared in the presence of component (A1).
- 11. Coating composition according to claim 1, comprising as component (B) compounds selected from the group consisting of diisocyanates, polyisocyanates and mixtures thereof.
- 12. Coating composition according to claim 1, wherein the polyacrylate resin (A2) comprises
- a) from 5 to 50% by weight of one or more monomers selected from the group consisting of 4-hydroxy-n-butyl acrylate, 4-hydroxy-n-butyl methacrylate, 3-hydroxy-n-butyl acrylate, 3-hydroxy-n-butyl methacrylate and hydroxyethyl methacrylate, together with
- (c) from 5 to 95% by weight of aliphatic and cycloaliphatic esters of methacrylic acid, aliphatic and cycloaliphatic esters of acrylic acid which are different from (a) and (e), and mixtures of such monomers,
- (d) from 0.5 to 30% by weight, of a copolymerizable vinyl ester monomer which is different from (a), (b) and (e), and mixtures of such monomers, and
- (e) from 15 to 80% by weight, of an aromatic vinyl hydrocarbon monomer which is different from (a), (c), (d) and mixtures of such monomers.
- 13. A coating composition according to claim 12, further comprising
- (b) additional monomers selected from the group consisting of (i) ethylenically unsaturated, copolymerizable monomers containing hydroxyl groups and different from (a), (c) and (d), and mixtures of such monomers, and (f) ethylenically unsaturated monomers different from (a)-(e) and mixtures of such monomers, where the sum of (a)-(f) is 100% by weight.
- 14. A process for the production of a coating on a substrate surface, comprising the step of applying to a substrate a coating composition according to claim 1.
- 15. A process according to claim 14 wherein the coating composition applied to the substrate is applied as the topcoat layer.
- 16. A process according to claim 14 wherein the coating applied to the substrate is a refinish coating composition.
- 17. A process according to claim 14 wherein the coating applied to the substrate is a solid color topcoat composition.
Parent Case Info
This application is a continuation of application Ser. No. 08/396,027, filed Feb. 28, 1995, which is now abandoned.
US Referenced Citations (2)
Foreign Referenced Citations (1)
Number |
Date |
Country |
9201757 |
Feb 1992 |
WOX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
396027 |
Feb 1995 |
|