Coating composition for controlling hydrogen absorption

Abstract

There is herein provided a coating composition for controlling hydrogen embrittlement of a steel which contains 1 to 500 percent by weight of a metal oxide selected from the group consisting of manganese dioxide, vanadium pentoxide and molybdenum trioxide based on 100 percent by weight of resin solids.

Description

FIELD OF THE INVENTION

The present invention relates to a coating composition for controlling hydrogen absorption of a steel, more particularly, a coating composition for preventing hydrogen embrittlement cracking which is the hydrogen induced cracking arising from the absorbed hydrogen atoms into the steel, formed by corrosion of the steel.

BACKGROUND OF THE INVENTION

A steel produces a stress corrosion cracking in the presence of hydrogen sulfide or carbonic acid gas. It is believed that a part of hydrogen formed from a reaction of hydrogen sulfide with the steel is absorbed and diffused into the steel in the form of the atomic state to result in the hydrogen embrittlement cracking.

In order to prevent the hydrogen embrittlement, a coating or a lining has been used, by which corrosive reagents such as hydrogen sulfide are prevented from contacting the steel. Typical examples are the method of adding a metallic powder (pigment) reactive with hydrogen sulfide to a coating composition and the method of adding an ion-exchange resin to a coating composition. The former prevents contact between hydrogen sulfide and the surface of the steel by the reaction of hydrogen sulfide with the metallic powder. The latter prevents contact between hydrogen sulfide and the surface of the steel by the reaction of hydrogen sulfide with the ion-exchange resin.

The above methods are based on the reaction of hydrogen sulfide with the additive such as the pigment or the ion-exchange resin. The reaction, however, can not continue forever, that is, the technical effect of the additive would reduce rapidly and the corrosion reaction would begin to increase if the reactivity of the additive decreases. According to the above methods, the corrosion reaction generally begins to increase after 30 hours to 100 days from an application of the coating composition. This term falls short of the actual service life of the steel (50-60 years).

SUMMARY OF THE INVENTION

The present invention provides a coating composition for controlling a hydrogen absorption which contains 1 to 500 percent by weight of a metal oxide selected from the group consisting of manganese dioxide, vanadium pentoxide and molybdenum trioxide based on 100 percent by weight of resin solids.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows change with time of reaction current to extraction of hydrogen.

FIG. 2 shows change with time of corrosion potential of the coated side of steel.

FIG. 3 shows an apparatus used to measure the change of corrosion potential of a steel plate coated with a gel containing oxides.

FIG. 4 shows the change in corrosion potential vs. immersion time for a steel panel coated with a composition of the present invention.

FIG. 5 shows the change in reaction current vs. immersion time for the metal oxide coating on a steel panel, in accordance with the present invention.

DETAILED DESCRIPTION OF THE INVENTION

Examples of manganese dioxide are natural manganese dioxide, electrolytic manganese dioxide, chemical synthesis manganese dioxide and a mixture thereof. Electrolytic manganese dioxide is generally prepared by an electrolysis of manganese sulfate or manganese chloride. Chemical manganese dioxide is prepared by a decomposition of a permanganate with hydrochloric acid, an oxidation of manganese sulfate or a thermal decomposition of manganese nitrate.

Vanadium pentoxide can be prepared by any conventional method such as the baking of lower oxides, nitrides or sulfides of vanadium.

Molybdenum trioxide can be prepared by any conventional method such as baking in air or a reaction with nitric acid of molybdenum metals, or lower oxides or sulfide of molybdenum metals. Also heating of phosphorus molybdate or heating of ammonium molybdate with nitric acid can be employed.

The particle size of the metal oxide is the same as a pigment. A bigger particle size gives insufficient film properties.

The vehicle used in the present invention is generally for a coating or a lining, for example a polymerized oil, a natural or synthetic resin, or a mixture thereof.

A typical example of the polymerized oil is the boiled oil. Examples of the natural or synthetic resin are an epoxy resin, an epoxy-urethane resin, an epoxy coal tar resin, a melamine resin, a rubber chloride, a phenol resin, a polyester resin, a polyurethane resin, a silicon resin, a fluororesin, and the like.

According to the present invention, the metal oxide is formulated into the coating composition in an amount of 1 to 500 percent by weight, preferably 5 to 100 percent by weight based on 100 percent by weight of resin solids. Amounts of more than 500 percent by weight are undesirable because of insufficient film properties. Amounts less than 1 percent by weight are undesirable because the technical effect of the present invention cannot be provided.

To the coating composition of the present invention is added water or another solvent to form a dispersion. Examples of solvents are those used in the usual coatings such as ketones, esters, glycols, alcohols, hydrocarbons. Also conventional type pigments or other additives can be added to the coating composition of the present invention, Examples of the additives are a plasticizer, a surfactant, a drying agent, a curing agent, a thickener, an anti-sagging agent, and the like.

The steel to be treated by the coating composition of the present invention is one which can form or easily forms stress corrosion, hydrogen embrittlement, hydrogen induced cracking, hydrogen blisters and the like. Typical examples of the steel are carbon steel, alloys, high tensile strength steel and the like which are used for oil field pipes, transfer line pipes, bolts, assembly of a ship and the like.

The process for coating can be any conventional process such as flow, dipping, spray, brush, or powder coating.

The substrate coated by the coating composition of the present invention hardly absorbs the atomic state hydrogen formed by the corrosion of the steel under the atmosphere containing hydrogen sulfate. Accordingly, the coating composition of the present invention effectively controls the hydrogen embrittlement. It is believed that the reason why the present coating composition prevents the hydrogen embrittlement is that the corrosion potential of the steel surface is kept noble by the metal oxide of the present invention (the absorption of the atomic state hydrogen would be accelerated if the corrosion potential of the steel surface is a less-noble potential).

The present invention is illustrated by the following examples, which, however, are not to be construed as limiting the invention to their details. All parts and percentages in the examples are by weight unless otherwise specified.

EXAMPLE I

A paint was prepared by the formulation as shown in Table-1 and was applied to a cold rolled steel (thickness 0.8 mm, JIS G 3141) under the condition as shown in Table-1. Instead of the cold rolled steel, the use of a high tensile steel is naturally required for an evaluation of the hydrogen embrittlement crack, but since the technical effect of the present invention can be evaluated by the degree of the hydrogen absorption is the steel, the cold rolled steel was used in the present example. The method of coating was a spray coating.

For the purpose of comparison, a paint was prepared by using the formulation outside the range of the present invention in the amount of manganese dioxide and was applied to the cold rolled steel.

In order to evaluate the controlling property of hydrogen absorption, a change on standing of the current caused by the reaction, H.fwdarw.H.sup.+ +e.sup.-, which is an extract reaction of hydrogen on the other side of the steel, was measured. The measuring process was based on the method described in Japanese Pat. No. 1018241, the portions of which are hereby incorporated by reference.

The method of the evaluation is illustrated with referring to FIG. 1. The curve X of FIG. 1 shows a change on standing of a reaction current to an extract of hydrogen with using the paint not containing manganase dioxide of the present invention, and the curve Y of FIG. 1 shows a change of standing of a reaction current to an extract of hydrogen with using the paint described in this example. Increase of the reaction current shows that the hydrogen was absorbed into the steel by a corrosion reaction of the steel surface under the film is extracted from the opposite side of the steel. Accordingly, the latter build up time of a curve shows the better corrosion control property. In FIG. 1, tx or ty indicates the build up time. The rate of this build up times between the curve X and the curve Y, i.e. ty/tx can indicate the technical effect of the present invention. The result and the condition of the corrosion is shown in Table 1.

TABLE 1__________________________________________________________________________ a type of manganese dioxide thicknessExample and loading (parts) based on of film ty/txnumber name of paint resin solids 100 parts drying condition (.mu.m) ratio corrosion__________________________________________________________________________ condition 1 SUPERLAC DIF, F-80, N-23 natural manganese dioxide.sup.(1) 190.degree. C./10 sec. 20 160 Hydrogen sulfide and (epoxy polyurethan paint) 100 parts carbonic acid were continuously blown into 3% NaCl solution. Temp. 50.degree. C. 2 COPON MASTIC PRIMER natural manganese dioxide natural drying 70 72 Hydrogen sulfide and (epoxy resin paint) 100 parts 10 days carbonic acid were continuously blown into 3% NaCl solution. Temp. 70.degree. C. 3 EPOTAR S (JIS K-566) natural manganese dioxide natural drying 40 21 Hydrogen sulfide and (epoxy coal tar paint) 100 parts 10 days carbonic acid were continuously blown into 3% NaCl solution. Temp. 50.degree. C. 4 Hi-RUBBER E PRIMER natural manganese dioxide natural drying 25 15 Hydrogen sulfide and (rubber chloride paint) 100 parts 10 days carbonic acid were continuously blown into 3% NaCl solution. Temp. 30.degree. C. 5 SULPHOTITE 10 natural manganese dioxide natural drying 25 120 Hydrogen sulfide gas (phenol resin paint) 100 parts 10 days of 100% relative humidity. Temp. 70.degree. C. 6 SUNFTAL (JIS K-5572) natural manganese dioxide natural drying 25 78 Hydrogen sulfide gas (phthalic acid paint) 100 parts 10 days of 100% relative humidity. Temp. 70.degree. C. 7 ORGA 100-2 natural manganese dioxide natural drying 20 34 Hydrogen sulfide gas (melamine resin paint) 100 parts 10 days of 100% relative humidity. Temp. 30.degree. C. 8 CYANAMID HELGON QD natural manganese dioxide natural drying 35 23 Hydrogen sulfide and (JIS K5625-2) 100 parts 10 days carbonic acid were continuously blown into 3% NaCl solution. Temp. 30.degree. C. 9 INTERGARD GLASS FLAKE natural manganese dioxide natural drying 2000 15 Hydrogen sulfide was (epoxy resin paint) 100 parts 10 days continuously blown into 3% NaCl solution. Temp. 60.degree. C.10 NIPPE ZINKY 1000P natural manganese dioxide natural drying 20 25 Hydrogen sulfide was (zinc powder containing 100 parts 10 days continuously blown paint) into 3% NaCl solution. Temp. 20.degree. C.11 Hi-CR PRIMER WHITE natural manganese dioxide natural drying 20 95 Hydrogen sulfide was (JIS K-5506) 100 parts 10 days continuously blown (synthetic resin paint) into 3% NaCl solution. Temp. 50.degree. C.12 POWDAX P natural manganese dioxide + 180.degree. C./30 min. 100 17 Hydrogen sulfide and (powder coating) electrolytic manganese carbonic acid were dioxide.sup.(2) 100 parts continuously blown into 3% NaCl solution. Temp. 70.degree. C.13 ORGA 100-2 electrolytic manganese natural drying 20 105 Hydrogen sulfide was (melamine resin paint) dioxide 10 parts 10 days continuously blown into 3% NaCl solution. Temp. 40.degree. C.14 ORGA 100-2 synthetic manganese dioxide.sup.(3) natural drying 20 175 Hydrogen sulfide was (melamine resin paint) 10 parts 10 days continuously blown into 3% NaCl solution. Temp. 40.degree. C.15 Hi-CR PRIMER WHITE synthetic manganese dioxide.sup.(4) natural drying 10 43 Hydrogen sulfide of (JIS K-5506) 1 parts more than 10 days 100% relative (synthetic resin paint) humidity. Temp. 60.degree. C.16 Hi-CR PRIMER WHITE synthetic manganese dioxide natural drying 10 120 Hydrogen sulfide gas (JIS K-5506) 10 parts more than 10 days of 100% relative (synthetic resin paint) humidity. Temp. 60.degree. C.17 Hi-CR PRIMER WHITE synthetic manganese dioxide natural drying 10 32 Hydrogen sulfide gas (JIS K-5506) 100 parts more than 10 days of 100% relative (synthetic resin paint) humidity. Temp. 60.degree. C.18 Hi-CR PRIMER WHITE synthetic manganese dioxide natural drying 10 14 Hydrogen sulfide gas (JIS K-5506) 500 parts more than 10 days of 100% relative (synthetic resin paint) humidity. Temp. 60.degree. C.Com- Hi-CR PRIMER WHITE synthetic manganese dioxide natural drying 10 3 Hydrogen sulfide gasparative (JIS K-5506) 0.1 parts more than 10 days of 100% relativeExample (synthetic resin paint) humidity. Temp.1 60.degree. C.Com- Hi-CR PRIMER WHITE synthetic manganese dioxide natural drying 10 2 Hydrogen sulfide gasparative (JIS K-5506) 1000 parts more than 10 days of 100% relativeExample (synthetic resin paint) humidity. Temp.2 60.degree. C.__________________________________________________________________________ .sup.(1) Use of .beta. MnO.sub.2 type pyrolusite .sup.(2) .gamma. MnO.sub.2 .sup.(3) .alpha. MnO.sub.2 .sup.(4) .beta. MnO.sub.2

Since this measurement is conducted by an electrochemical method, it is 100 times more sensitive than a conventional gas measurement. Accordingly, measuring time of ty is stopped at 1,000 hours, and ty is regarded as 1,000 unless the ty point is observed.

In Table 1, ty/tx of Example 9 was as small as 15, Example 9, however, was seemingly small, because it was a thick coating type (a kind of lining) which made ty more than 1,000 hours. Accordingly it seems that the technical effect is more than 15 times greater when manganese dioxide is present in the paint.

EXAMPLE II

A paint was prepared by the formulation as showed in Table-2 and was applied to a cold rolled steel (thickness 0.8 mm, JIS G 3141) under the condition as shown in Table-2.

For the purpose of comparison, a paint was prepared by using the formulation outside the range of the present invention in the amount of vanadium pentoxide and was applied to the cold rolled steel.

An evaluation was conducted as generally described in Example I. The result is shown in Table 2.

TABLE 2 loading of vanadium pentoxide thickness Example (parts) based on resin solids of film ty/tx number name of paint 100 parts drying condition (.mu.m) ratio corrosion condition 19 SUPERLAC DIF, F-80, N-23 30 parts 190.degree. C./10 sec. 20 310 Hydrogen sulfide and carbonic (epoxy polyurethan paint) acid were continuously blown into 3% NaCl solution. Temp. 50.degree. C. 20 COPON MASTIC PRIMER 30 parts natural drying 60 250 Hydrogen sulfide and carbonic (epoxy resin paint) 10 days acid were continuously blown into 3% NaCl solution. Temp. 70.degree. C. 21 EPOTAR S 30 parts natural drying 70 41 Hydrogen sulfide and carbonic (epoxy coal tar paint) 10 days acid were continuously blown into 3% NaCl solution. Temp. 50.degree. C. 22 Hi-RUBBER E PRIMER 30 parts natural drying 40 29 Hydrogen sulfide and carbonic (rubber chloride paint) 10 days acid were continuously blown into 3% NaCl solution. Temp. 30.degree. C. 23 SUPHOTITE 10 30 parts natural drying 25 270 Hydrogen sulfide gas of 100% (phenol resin paint) 10 days relative humidity. Temp. 70.degree. C. 24 SUNFTAL 20 (JIS K-5572) 30 parts natural drying 25 80 Hydrogen sulfide gas of 100% (phthalic acid paint) 10 days relative humidity. Temp. 70.degree. C. 25 ORGA 100-2 30 parts natural drying 20 50 Hydrogen sulfide gas of 100% (melamine resin paint) 10 days relative humidity. Temp. 30.degree. C. 26 CYANAMID HELGON QD PRIMER 30 parts natural drying 35 49 Hydrogen sulfide and carbonic (JIS K5625-2) 10 days acid were continuously blown into 3% NaCl solution. Temp. 30.degree. C. 27 INTERGARD GLASS FLAKE 30 parts natural drying 2000 38 Hydrogen sulfide was continu- (epoxy resin paint) 10 days ously blown into 3% NaCl solution. Temp. 60.degree. C. 28 NIPPE ZINKY 1000P 30 parts natural drying 20 90 Hydrogen sulfide was continu- (zinc powder containing 10 days ously blown into 3% NaCl paint) solution. Temp. 20.degree. C. 29 Hi-CR PRIMER WHITE 30 parts natural drying 20 152 Hydrogen sulfide was continu- (JIS K-5506) 10 days ously blown into 3% NaCl (synthetic resin paint) solution. Temp. 50.degree. C. 30 POWDAX P 30 parts 180.degree. C./30 min. 100 31 Hydrogen sulfide and carbonic (powder coating) acid were continuousl y blown into 3% NaCl solution. Temp. 70.degree. C. 31 Hi-CR PRIMER WHITE 1 parts natural drying 10 81 Hydrogen sulfide was continu- (JIS K-5506) more than 10 days ously blown into 3% NaCl (synthetic resin paint) solution. Temp. 40.degree. C. 32 Hi-CR PRIMER WHITE 10 parts natural drying 10 370 Hydrogen sulfide was continu- (JIS K-5506) more than 10 days ously blown into 3% NaCl (synthetic resin paint) solution. Temp. 40.degree. C. 33 Hi-CR PRIMER WHITE 100 parts natural drying 10 102 Hydrogen sulfide of 100% (JIS K-5506) more than 10 days relative humidity. Temp. 60.degree. C. (synthetic resin paint) 34 Hi-CR PRIMER WHITE 500 parts natural drying 10 21 Hydrogen sulfide gas of 100% (JIS K-5506) more than 10 days relative humidity. Temp. 60.degree. C. (synthetic resin paint) Comparative Hi-CR PRIMER WHITE 0.1 parts natural drying 10 7 Hydrogen sulfide gas of 100% Example (JIS K-5506) more than 10 days relative humidity. Temp. 60.degree. C. 3 (synthetic resin paint) Comparative Hi-CR PRIMER WHITE 1000 parts natural drying 10 5 Hydrogen sulfide gas of 100% Example (JIS K-5506) more than 10 days relative humidity. Temp. 60.degree. C. 4 (synthetic resin paint)

Since this measurement is conducted by an electrochemical method, it is 100 times more sensitive than a conventional gas measurement. Accordingly, the measuring time of ty is stopped at 3,000 hours, ty is regarded as 3,000 unless the ty point exists.

In Table 2, ty/tx of Example 27 was as small as 38, Example 27, however, was seemingly small, because it was a thick coating type (a kind of lining) which made ty more than 3,000 hours. Accordingly it seems that the technical effect is more than 38 times greater when vanadium pentoxide is present in the paint.

EXAMPLE III

A paint was prepared by the formulation as showed in Table-3 and was applied to a cold rolled steel (thickness 0.8 mm, JIS G 3141) under the condition as shown in Table-3.

For the purpose of comparison, a paint was prepared by using the formulation outside the range of the present invention in the amount of molybdenum trioxide and was applied to the cold rolled steel.

An evaluation was conducted as generally described in Example I. The result is shown in Table 3.

TABLE 3 loading or molybdenum trioxide thickness Example (parts) based on resin solids of film ty/tx number name of paint 100 parts drying condition (.mu.m) ratio corrosion condition 35 SUPERLAC DIF, F-80, N-23 30 parts 190.degree. C./10 sec. 20 260 Hydrogen sulfide and carbonic (epoxy polyurethan paint) acid were continuously blown into 3% NaCl solution. Temp. 50.degree. C. 36 COPON MASTIC PRIMER 30 parts natural drying 60 180 Hydrogen sulfide and carbonic (epoxy resin paint) 10 days acid were continuously blown into 3% NaCl solution. Temp. 70.degree. C. 37 EPOTAR S 30 parts natural drying 70 38 Hydrogen sulfide and carbonic (epoxy coal tar paint) 10 days acid were continuously blown into 3% NaCl solution. Temp. 50.degree. C. 38 Hi-RUBBER E PRIMER 30 parts natural drying 40 23 Hydrogen sulfide and carbonic (rubber chloride paint) 10 days acid were continuously blown into 3% NaCl solution. Temp. 30.degree. C. 39 SULPHOTITE 10 30 parts natural drying 25 232 Hydrogen sulfide gas of 100% (phenol resin paint) 10 days relative humidity. Temp. 70.degree. C. 40 SUNFTAL 20 JIS K-5572) 30 parts natural drying 25 43 Hydrogen sulfide gas of 100% (phthalic acid paint) 10 days relative humidity. Temp. 70.degree. C. 41 ORGA 100-2 30 parts natural drying 20 29 Hydrogen sulfide gas of 100% (melamine resin paint) 10 days relative humidity. Temp. 30.degree. C. 42 CYANAMID HELGON QD PRIMER 30 parts natural drying 35 31 Hydrogen sulfide and carbonic (JIS K5625-2) 10 days acid were continuously blown into 3% NaCl solution. Temp. 30.degree. C. 43 INTERGARD GLASS FLAKE 30 parts natural drying 2000 18 Hydrogen sulfide was continu- (epoxy resin paint) 10 days ously blown into 3% NaCl solution. Temp. 60.degree. C. 44 NIPPE ZINKY 1000P 30 parts natural drying 20 21 Hydrogen sulfide was continu- (zinc powder containing 10 days ously blown into 3% NaCl paint) solution. Temp. 20.degree. C. 45 Hi-CR PRIMER WHITE 30 parts natural drying 20 98 Hydrogen sulfide was continu- (JIS K-5506) 10 days ously blown into 3% NaCl (synthetic resin paint) solution. Temp. 50.degree. C. 46 POWDAX P 30 parts 180.degree. C./30 min. 100 22 Hydrogen sulfide and carbonic (powder coating) acid were continuousl y blown into 3% NaCl solution. Temp. 70.degree. C. 47 Hi-CR PRIMER WHITE 1 parts natural drying 10 42 Hydrogen sulfide was continu- (JIS K-5506) more than 10 days ously blown into 3% NaCl (synthetic resin paint) solution. Temp. 40.degree. C. 48 Hi-CR PRIMER WHITE 10 parts natural drying 10 210 Hydrogen sulfide was continu- (JIS K-5506) more than 10 days ously blown into 3% NaCl (synthetic resin paint) solution. Temp. 40.degree. C. 49 Hi-CR PRIMER WHITE 100 parts natural drying 10 45 Hydrogen sulfide of 100% (JIS K-5506) more than 10 days relative humidity. Temp. 60.degree. C. (synthetic resin paint) 50 Hi-CR PRIMER WHITE 500 parts natural drying 10 19 Hydrogen sulfide gas of 100% (JIS K-5506) more than 10 days relative humidity. Temp. 60.degree. C. (synthetic resin paint) Comparative Hi-CR PRIMER WHITE 0.1 parts natural drying 10 4 Hydrogen sulfide gas of 100% Example (JIS K-5506) more than 10 days relative humidity. Temp. 60.degree. C. 5 (synthetic resin paint) Comparative Hi-CR PRIMER WHITE 1000 parts natural drying 10 3 Hydrogen sulfide gas of 100% Example (JIS K-5506) more than 10 days relative humidity. Temp. 60.degree. C. 6 (synthetic resin paint)

Since this measurement is conducted by an electrochemical method, it is 100 times more sensitive than a conventional gas measurement. Accordingly, the measuring time of ty is stopped at 3,000 hours, ty is regarded as 3,000 unless the ty point exists.

In Table 3, ty/tx of Example 43 was as small as 18, Example 43, however, was seemingly small, because it was a thick coating type (a kind of lining) which made ty more than 3,000 hours. Accordingly it seems that the technical effect is more than 18 times greater when molybdenum trioxide is present in the paint.

EXAMPLE IV

This example indicates that the coating composition of the present invention holds the potential of the steel surface noble by measuring a corrosion potential on the side of the coating.

One hundred parts by weight of melamine alkyd resin was mixed with 10 parts of a metal oxide of the present invention (Y-1), 10 parts of titanium oxide(X-1) and 10 parts of iron oxide red(X-2) to form a paint. The paint was applied to the cold rolled steel as described in Example 1. A saturated solution of 3% NaCl+H.sub.2 S(gas) was contacted with the coated film. A silver-silver chloride reference electrode was put into the saturated solution through a salt bridge. The corrosion potential of the steel is measured on a basis of the silver-silver chloride electrode. The result is shown in FIG. 2.

As indicated in FIG. 2, when the paint did not contain the metal oxide of the present invention or when the paint contained the substance which can react with hydrogen sulfide, the corrosion potential of the steel was not kept noble and changed to less-noble with time. On the other hand, when the paint prepared according to the present invention was used, the corrosion potential was held noble to control hydrogen absorption by an electrochemical reaction.

EXAMPLE V

This example illustrates the reactivity between various oxides and H.sub.2 S.

A particular amount of V.sub.2 O.sub.5 was put in a petri dish and placed in an atmosphere containing a H.sub.2 S gas saturated with water, for 500 hours. The saturated H.sub.2 S gas was introduced by blowing H.sub.2 S gas into water at 30.degree. C. and collecting the bubbled gas. The reacted V.sub.2 O.sub.5 with H.sub.2 S was then dried in vacuum and weighed. The weight increase was obtained in terms of percentage by weight and shown in Table 4 hereinafter.

MoO.sub.3, electrolytic MnO.sub.2, .beta.-MnO.sub.2 and TiO.sub.2 were treated as mentioned above and the results are shown in Table 4.

EXAMPLE VI

This example illustrates the change of corrosion potential (Ecorr.) in respect to a steel panel coated with an agar gel containing the oxides mentioned in Example V.

The measurement was carried out using an apparatus shown in FIG. 3. In FIG. 3, a steel panel 2 was positioned on a substrate 1 and an agar gel containing V.sub.2 O.sub.5 at 5% by weight was coated on the steel panel 2 to form an agar layer 3. A 3% NaCl solution 5 was poured in an electrolysis cell 4 as a typical corrosion condition to allow to polarization. The agar gel 3 was connected to an Ag-AgCl reference electrode 9 immersed in 3.33N KCl solution 8 in a glass container 7 through a salt bridge (3.33N solution gelled with agar) in a rugin tube 6. The Ag-AgCl reference electrode 9 was connected to a potentiostat. The steel panel 2 was also connected to the potentiostat, of which a C terminal was connected to a Pt counter-electrode 11 around the rugin tube 6. Corrosion potential (Ecorr.) before and after blowing an H.sub.2 S was measured by a polarization curve method. The H.sub.2 S gas was continuously blown into the NaCl solution 5 at 25.degree. C. for one day. The same test were applied to MoO.sub.3, electrolytic MnO.sub.2, .beta.-MnO.sub.2 and TiO.sub.2. The result was shown in Table 4.

TABLE 4______________________________________ Ecorr. (mV) Weight Before Aftermetal oxides increase H.sub.2 S blow H.sub.2 S blow Difference______________________________________V.sub.2 O.sub.5 +5% -615 -610 +5MoO.sub.3 +12 -620 -610 +10EMD (electro- +30 -590 -700 -110lytic MnO).beta.MnO.sub.2 +25 -620 -690 -70TiO.sub.2 +1 -640 -660 -20______________________________________

As appears from Table 4, V.sub.2 O.sub.5 and MoO.sub.3 have less weight increase in Example V and maintain noble corrosion potential after finishing the reaction with H.sub.2 S in Example VI.

EXAMPLE VII

This example shows how the metal oxide of the present invention provides the capability of maintaining noble Ecorr. in the presence of H.sub.2 S.

A melamine alkyd coating composition was formulated with .beta.-MnO.sub.2, V.sub.2 O.sub.5 and MoO.sub.3, respectively, in an amount of 50 parts by weight based on 100 parts by weight of resin solids to form three compositions. The compositions were applied to steel panels in a thickness of 30 to 35 .mu.m and were baked for 30 minutes at 140.degree. C. The corrosion potential was measured using the apparatus mentioned in Example VI. H.sub.2 S gas was continuously blown into the three NaCl solutions 5 at 40.degree. C. The result is shown in FIG. 4.

As apparent from FIG. 4, corrosion potential is maintained noble with V.sub.2 O.sub.5 and MoO.sub.3, but not with MnO.sub.2. It is indicated that MnO.sub.2 is rapidly changed by reacting with H.sub.2 S.

EXAMPLE VIII

Coating compositions were made and coated on steel panels as generally described in Example VII. Reaction current to extract the permeated hydrogen was measured as generally described in Example 1. The result is shown in FIG. 5.

As apparent from FIG. 5, the rise up time of the reaction current curve for MoO.sub.3 and V.sub.2 O.sub.5 is longer than that of MnO.sub.2. Though the rise up time of the reaction current curve of MnO.sub.2 does not correspond to the shift to be less noble of corrosion potential, it can be understood as follows: MnO.sub.2 prevents absorption of hydrogen by a similar mechanism to MoO.sub.3 and V.sub.2 O.sub.5 up to 100 hours and after 100 hours the control of hydrogen absorption is probably carried out by a different mechanism which has been unknown. This mechanism does not work sufficiently after 500 hours. It has thus been found that MoO.sub.3 and V.sub.2 O.sub.5 are superior to MnO.sub.2.

Claims

1. A method for controlling hydrogen absorption of steel which consists essentially of directly coating the surface of said steel with a composition containing resin solids and a metal oxide, with said metal oxide being selected from the group consisting of vanadium pentoxide and molybdenum trioxide and being employed at 1 to 500 percent by weight, based on 100 percent by weight of said resin solids.