Patent Grant
8246735
The present invention relates to coating compositions for producing magnetically induced images. More specifically it relates to printing inks for producing magnetically induced images for use on security- or value-documents or on branded goods, to protect them against counterfeit or illegal reproduction.
Optically variable devices of various types are used as efficient anti-copying means on security- and value-documents. Among these, particularly important optically variable copy-protection means are the optically variable inks (OVI®; EP-A-0227423). Optically variable inks (OVI®) are used to print surfaces and/or indicia which exhibit a viewing angle dependent color (=color shift).
Said anti-copying inks are formulated on the basis of optically variable pigments (OVP); preferred types being the flake shaped thin-film optical interference pigments described in U.S. Pat. No. 4,705,300; U.S. Pat. No. 4,705,356; U.S. Pat. No. 4,721,271 and thereto related disclosures.
Other useful types of OVP for optically variable ink formulations comprise the interference coated particles described in U.S. Pat. No. 5,624,486 and U.S. Pat. No. 5,607,504, and the thin-film cholesteric (i.e. chiral-nematic) liquid crystal pigments described in U.S. Pat. No. 5,807,497 and U.S. Pat. No. 5,824,733.
Optically variable inks, coatings and paints are known in the art, e.g. from EP-A-0227423, U.S. Pat. No. 5,279,657, or WO 95/29140. Said optically variable inks can be used in various printing processes, such as copperplate (Intaglio) printing, gravure printing, flexographic printing or screen printing.
As known to the skilled person, the wet film thickness resulting from the said printing processes can vary to a large extent, form about 2 μm up to about 50 μm depending upon the process and the conditions used.
To achieve a high color-shifting effect of the optically variable ink or coating, the shape of the optically variable pigment (OVP) is preferably a platelet or a flake, as disclosed in the art.
The perceived optical characteristics and the color purity depend on the pigment's final orientation in the cured ink or coating layer on the substrate. Randomly oriented optically variable pigment flakes or platelets exhibit a poor color shift and low color purity. Maximum color shift and color purity requires the optically variable pigment flakes or platelets in the ink or coating to adopt a same particular orientation, e.g. coplanar to the surface of the substrate.
These optical effects are even more enhanced if the surface of the substrate has been previously smoothened through the application of a base coating. The optically variable pigment flakes can in this case arrange more readily in a flat plane, thus increasing the coverage on the substrate, the color purity and the color shift.
To obtain coatings having the optically variable pigment flakes arranged in a same flat plane on a substrate, an ink or coating formulation which allows for a reduction of the wet film thickness during the drying process to less than 10 μm is normally used. The gradual reduction of the film thickness during the drying process forces the optically variable pigment flakes to arrange in a single plane parallel to the surface of the substrate, providing for a maximum coverage and color shift on the substrate.
Magnetic optically variable pigments have been disclosed in WO 02/073250; U.S. Pat. No. 4,838,648; EP-A-686675; WO 03/00801 and U.S. Pat. No. 6,838,166 as an improvement to the optically variable pigments for inks on security-, value-documents and banknotes; these documents are incorporated herein by reference.
Magnetic optically variable pigments in printing inks or coatings allow for the production of magnetically induced images, designs and/or patterns through the application of a corresponding magnetic field, causing a local orientation of the magnetic optically variable pigment in the coating, followed by drying/curing the latter. The result is a fixed magnetically induced image, design or pattern in an optically variable ink.
Materials and technology for the orientation of magnetic particles in coating compositions and printing processes have been disclosed in U.S. Pat. No. 2,418,479; U.S. Pat. No. 2,570,856; U.S. Pat. No. 3,791,864; DE 2006848-A; U.S. Pat. No. 3,676,273; U.S. Pat. No. 5,364,689; U.S. Pat. No. 6,103,361; US 2004/0051297; US 2004/0009309; EP-A-710508, WO 02/090002; WO 03/000801; WO 2005/002866, and US 2002/0160194; these documents are incorporated herein by reference.
U.S. Pat. No. 2,418,479 and U.S. Pat. No. 2,570,856 disclose a process and a coating composition for the magnetic orientation of metallic pigments in paint films. Said films have a high degree of orientation and a low degree of brightness, as well as unusual reflectance and translucency properties. The metallic pigments comprise flakes of ferromagnetic material, preferably nickel, in amounts ranging from 0.1% to 95% by weight of the film forming binder; and volatile organic components are present in the composition in amounts ranging from 50% to 70% of the total weight. The wet film is applied in a thickness of 25 mils (635 μm), and subject to a magnetic field for orienting the metallic flakes, maintaining the field until the film is dry. These documents are not concerned with OVI® and disclose merely paint compositions comprising magnetic metal flake pigments and effect coatings based thereupon. No formulation rules are given as to the relationship of flake size, flake concentration and coating thickness for obtaining the best optical effect.
U.S. Pat. No. 3,791,864 and DE 2006848-A refer to stove-enamel compositions, nitro-cellulose compositions, and two-component compositions comprising magnetic components (e.g. lamellar or rod shaped iron pigments), for the production of magnetically oriented coatings. The documents are about a method and a process for the magnetic orientation of pigments in two layer coatings; the formulation aspects of the involved coating composition are not, however, contemplated.
U.S. Pat. No. 3,676,273 discloses a magnetically oriented coating, comprising highly reflective nickel flakes dispersed in an acrylic binder. The amount of magnetic pigment ranges form 0.1% to 95% by weight of the film forming material. Specific formulation aspects are not addressed in this document.
U.S. Pat. No. 5,364,689 discloses a painted product comprising magnetic non-spherical particles in a paint medium, wherein the said magnetic particles are oriented to yield a pattern of a three-dimensional optical appearance. The magnetic particles comprise one or more of nickel, cobalt, iron, and their alloys. The particles have a thickness of 0.1 to 1.0 μm and a length of 10 to 100 μm. The paint medium is selected from alkyd, polyester, acrylic, polyurethane, and vinyl resins. The particles are present in amounts between 1 and 60 parts per 100 parts by weight of the paint medium. No particular rules concerning the formulation of the paint medium are given, however.
U.S. Pat. No. 6,103,361 refers to heat resistant coating compositions containing fluoropolymers, such as PFTE (poly-tetrafluoroethylene) and magnetizable flakes, which allow for the magnetically inducing of a pattern in the coating of a frying pan.
US 2004/0051297 and US 2004/0009309 refer to a method and an apparatus for orienting magnetic flakes during a painting or printing process. Particles of a magnetic optically variable pigment are dispersed in a liquid paint or ink medium. The typical flake is about 20 μm large and about one μm thick. The flakes typically include a magnetic metal layer such as a thin film of ferromagnetic metal or alloy, such as cobalt, nickel or PERMALLOY (typically 80% Ni, 20% Fe) and an optical interference structure, such as an absorber-dielectric-reflector Fabry-Perot type structure on both sides of the metal layer. US 2004/0051297 contains a remark as to the influence of film thickness and the type of organic carrier used on the magnetic orientability of the pigments. However, no further details concerning the best formulation of the coating composition for the application purpose are disclosed.
WO 02/090002 refers to methods for producing imaged coated articles by using magnetic optically variable pigment, as well as to coated articles. The pigment consists of reflective magnetic flakes (RMF) of the type described in WO 03/000801 “Multi-Layered Magnetic Pigments and Foils” and has a magnetic core layer. No formulation rules are given, however, as to the coating composition which should be used.
WO 05/002866 refers to a method and means for producing a magnetically induced design in a coating containing magnetic particles. Said coating comprises preferably magnetic optically variable particles. The coating composition is preferably selected from the group of liquid inks, comprising screen-printing inks, gravure inks and flexographic inks. Liquid inks have low viscosity (in the range of 0.1 to 5 Pa*s at 20° C.) and allow for an easy orientation of the magnetic pigment. Drying/curing of the ink can be based on solvent or water evaporation, as well as on UV-crosslinking or on hybrid curing mechanisms, including evaporation of diluents, UV-curing and other reticulation reactions, such as oxypolymerization cross-linking reactions. None of the given ink formulas were optimized, however, with respect to the magnetic image/effect imprinted in the coating.
US 2002/0160194 refers to multi-layered magnetic pigments and foils. The disclosed pigment flakes can be interspersed within a binder medium to produce a colorant composition (ink) which can be applied to a wide variety of objects or papers. The binder medium contains a resin or mixtures of resins, and a solvent (organic solvent or water), and can be dried/cured by thermal processes such as thermal cross-linking, thermal setting, or thermal solvent evaporation, or by photochemical cross-linking.
The optically variable inks and coating compositions used in the art are aimed at exhibiting a bright color, a strong color shift and yielding a good substrate coverage using an as low as possible amount of optically variable pigment. A low pigment concentration is desirable to limit the raw material costs, as well as to obtain a good printability of the ink and durability of the print. These objectives are achieved by providing the printing inks with a relatively high amount of volatile components such as organic solvents, water or mixtures thereof, of the order of 50% or more, per weight of the composition, and a relatively low amount of non-volatile components, i.e. the binder medium and the OVP, of the order of 50% or less, per weight of the composition.
This particular formulation ensures a volume reduction of the coating layer during the drying process and a corresponding orientation of the OVP particles in the plane of the printed substrate. This is why most OVI formulations or coating formulations containing optical effect pigments are solvent or water based, with solid contents not exceeding 50%. The solid content represents the part of non-volatile compounds of a printed ink or coating layer after the drying/curing process.
In the case of magnetic optically variable pigments however, it has been found that this type of ink formulations, when used for the magnetic induction of images, patterns or designs in the printed ink layer, leads to poor visual effects.
The technical problem underlying the present invention was to find coating compositions and corresponding formulation rules which are particularly adapted for the magnetic orientation of magnetic optically variable pigment (MOVP) in a printed ink or coating layer, yielding an attractive visual effect. With conventional formulations, suited for printing OVI®, the magnetic images transferred into the wet ink film are noteworthy strongly diminished in resolution and contrast during the drying/curing process, due to the vertical shrinking of the printed ink or coating layer.
The resulting inks should be compatible with standard printing requirements such as drying speed and printing resolution, as well as with economical constraints to control cost by limiting the applied quantities. The printing techniques to be used to print MOVP particles should be (copperplate) intaglio-, flexography-, gravure-, screen-printing as well as roller coating.
According to the present invention, this problem has been solved by a coating composition as defined in the appended claims.
In particular, the present invention is related to a coating composition for producing a magnetically induced image according to the present invention therefore consists of volatile components (S) and non-volatile components, the latter consisting of an ink vehicle (I) and magnetically orientable optically variable interference pigment (P), characterized in that the ratio of the volume of the ink vehicle (V(I)) to the volume of the pigment (V(P)) is higher than 3.0, preferably higher than 4.0, and most preferably higher than 5.0.
The present invention is also related to a process for manufacturing a coating composition for producing a magnetically induced image, which comprises the step of mixing together volatile components (S), and non-volatile components, the latter consisting of an ink vehicle (I) and magnetically orientable optically variable interference pigment (P), characterized in that the ratio of the volume of the ink vehicle (V(I)) to the volume of the pigment (V(P)) is higher than 3.0, preferably higher than 4.0, and most preferably higher than 5.0.
According to the present invention, the term “magnetic optically variable pigment (MOVP)” refers to platelet or flake shaped magnetic pigment particles carrying an optical interference coating, as known in the art. The particular characteristic of MOVP with respect to OVP is that the MOVP particles can be oriented by an applied magnetic field. MOVP are thus “magnetically orientable optically variable interference pigments”. The MOVP comprised in the printing ink or coating composition of the present invention consists of flat platelet or flake shaped particles chosen from the group of vacuum deposited magnetic thin film interference pigments, interference coated metallic pigments, interference coated nonmetallic pigments, magnetic liquid crystal pigments as disclosed in PCT/EP2005/056260, and mixtures thereof. Particularly preferred are the five-layer or the seven-layer vacuum deposited thin film interference pigments of U.S. Pat. No. 4,838,648 and WO 02/73250.
The MOVP used in the present invention is also characterized by its average particle size. In order to get saturated colours and abrupt colour changes, the mean particle diameter (d50) should typically range from 5 to 40 μm, preferably from 15 to 25 μm, and have a thickness in the range of 0.1 to 6 μm, more preferably in the range of 0.5 to 3 μm.
According to the present invention, the term “Volatile components” refers to components having a boiling point below 300° C. at ambient pressure, i.e. everything which eventually evaporates after printing. The volatile components present in the coating/ink composition can be chosen from organic solvents, water and mixtures thereof, i.e. from solvents typically used for making printing inks.
According to the present invention, the term “non-volatile components” refers to components having a boiling point of at least 300° C. at ambient pressure, i.e. everything which remains after printing.
According to the present invention, the term “ink vehicle” refers to the non-volatile part of a printing ink or coating composition, except the magnetic optically variable interference pigment. The ink vehicle may, however, comprise other pigments. Thus, the ink vehicle according to the present invention may comprise components from the group consisting of varnishes (i.e. binders), oligomers, fillers, pigments, dyes, leveling agents, wetting agents, surfactants, corrosion inhibitors, drying catalysts, photo initiators, waxes, cross-linking agents, non-volatile diluents or monomers.
According to the present invention, the term “volume of the ink vehicle” refers to the volume of the dried/cured ink vehicle.
According to the present invention, by the term “drying”, three different mechanisms are commonly addressed in the art. Two merely physical drying processes refer to the evaporation of volatile components from the printed ink or coating, leaving back its solid resin and pigment components, and to the penetration/absorption of non-volatile ink or coating solvent into the substrate. A third, chemical drying process, also called hardening or curing, refers to the transformation of a liquid composition into a solid one through a chemical polymerization or cross-linking reaction initiated by UV radiation, electron beam or oxypolymerization (oxidative reticulation induced by the joint action of oxygen and catalysts, such as Co and Mn catalysts). One or more of these drying processes may be implied in the drying of a same particular printing ink or coating. Thus, curing is a specific embodiment of drying. “Dual Curing” means a combination of physical evaporation and/or penetration in the substrate of volatile components with UV curing or oxypolymerization or chemical polymerisation initiated with an appropriate additive; “UVOX” means a combination of UV curing and oxypolymerization.
The printing techniques which can be used to print MOVP particles are (copperplate) intaglio-, flexography-, gravure-, screen-printing as well as roller coating.
To achieve the printing requirements, the corresponding printing elements are selected so as to deposit typical average dry ink film thickness in the range of 2 to 50 μm, preferably of 5 (flexography) to 30 μm (intaglio- or screen-printing).
The average diameter of the pigment is selected in function of the layer thickness which can be typically obtained and of the technical constraints linked to a given printing application. Selecting too small pigments will, in all cases, result in poor colour shifting, strong light scattering and low chroma. This is well-known to the skilled man and will be taken into consideration by him when selecting the appropriate pigments.
It was found that a vertical shrinking of the printed ink or coating layer during the drying/curing process must be avoided, in order to prevent the oriented pigment particles from adopting a flat position, which significantly reduces or even completely destroys the orientation effect produced by the magnetization. This is achieved by providing a sufficiently thick layer of non-volatile ink vehicle which will remain after evaporation of the volatile components.
Thus, of paramount importance is the volume ratio V(I)/V(P) of the dried/cured ink vehicle (I) to that of the magnetic optically variable pigment (P) present in the ink vehicle. It was found that below a volume ratio V(I)/V(P) of 3.0 it was impossible to produce a satisfactory magnetically induced image in a coating of the present invention. According to the present invention, Volume ratios are calculated based on experimental data and known product characteristics, as disclosed hereinafter in the detailed description.
What has to be considered is the thickness of the dried/cured ink layer. Inventors have found that the dried/cured solid ink layer should not be less in thickness than d50/3, preferably not less than d50/2, in order to obtain an orientable coating layer yielding a satisfactory magnetically oriented image. The quantity d50 is the mean diameter of the magnetic optically variable pigment and determined as known in the art.
In coatings, which are significantly thinner than d50/2, the achievable orientation effect is poor.
The coating composition of the present invention for producing magnetic images may be a copperplate intaglio printing ink, a flexographic printing ink, a gravure printing ink, a silkscreen printing ink, or a roller coating ink, and can be correspondingly used in a copperplate intaglio-, a flexographic-, a gravure-, a silkscreen-printing or a roller-coating process.
The magnetic optically variable printing inks or coating compositions of the present invention are divided into three main constituents. The magnetic optically variable pigment (P), the solvents or volatile components (S), (i.e. everything which eventually evaporates after printing: organic solvents, water or mixtures thereof), and the ink vehicle (I), (i.e. everything which remains after printing, except the pigment: i.e. non-volatile components such as varnishes, oligomers, fillers, pigments, dyes, leveling agents, wetting agents, surfactants, corrosion inhibitors, drying catalysts, photo initiators, waxes, cross-linking agents, non-volatile diluents or monomers).
The magnetic pigment of the present invention is typically chosen such, that the platelet shaped particles have a mean diameter (d50) in the range of 5 to 40 μm, more preferably the diameter is in the range of 15 to 25 μm, and a thickness in the range of 0.1 to 6 μm, more preferably in the range of 0.5 to 3 μm.
The diameter of the platelet shaped particles is to be understood as the mean (d50) value, determined as known to the skilled man. Similarly, the thickness of the platelet shaped particles is to be understood as the mean of the distance between the platelets' upper and lower surfaces, determined as known to the skilled man.
It was found by the inventors, that, independent of the process used for applying the magnetic ink to the substrate, there is a lower limit to the volume ratio V(I)/V(P) of the ink vehicle (I) to the magnetic optically variable pigment (P) in the ink, under which the visual effect of the magnetically oriented images, patterns or designs fades away upon drying of the wet film. This lower limit was found to be at a volume ratio V(I)/V(P) of 3.0. Good results are obtained with a volume ratio V(I)/V(P) higher than 4.0, preferably higher than 5.0.
In other words, there must be sufficient volume of ink vehicle (I) per volume of pigment (P) in the dry ink film, in order to allow the pigment flakes to keep their orientations, if this latter is not in the plane of the substrate.
For calculating the volume ratio V(I)/V(P), the volume of the ink vehicle alone, and the volume of the pigment in the ink vehicle must be known. This will be outlined hereinafter with reference to example 2.
Three ink formulations according to example 2a to 2c (UV-curing silkscreen printing inks) served as a basis for correlating formulation parameters with the obtainable magnetic orientation effect. With respect to the details of those examples, reference is made to the experimental section below. The formula of example 2a showed excellent magnetic orientability; that of example 2b showed some degradation, as compared to example 2a, and that of example 2c showed serious degradation, as compared to example 2a. It can be inferred that formulas with a ratio V(I)/V(P) lower than 3.0 will no longer show any useful effect.
Experimental data determined from the base formula of example 2 (first column) showed that the specific weight (density) of the wet ink (Dinkw) is 1.24 g/cm3, (Dinkd 1.26 g/cm3 for the dry ink). The density of the magnetic optically variable pigment was determined to be 2.82 g/cm3 (the pigment density varies to a certain extent, depending on the ratio of dielectric material (MgF2 (optical properties)) and of magnetic material (Ni, Fe, Co or Ni alloy (magnetic properties)) in the pigment flake. The pigment used in the present example had an experimental density of 2.82 g/cm3), and the density of the solvent (Dowanol) is 0.967 g/cm3. The experimental densities were determined by means of a pycnometer. The use of a pycnometer for determining densities is well-known to the skilled man and needs not be discussed in detail here (cf. standard ISO 1183-1:2004).
The base wet ink formula can be approximately described as follows (wherein W=weight, V=volume before mixing, I=ink vehicle, P=MOVP, S=solvent, D=density):
Taking into account the per weight formulation ratio W(I)+W(S)=0.80 g/g and W(P)=0.20 g/g and the density of the pigment D(P)=2.82 g/cm3, the pigment volume V(P) per gram of ink is calculated by means of the known correlation d=m/V as 0.071 cm3 and the remainder volume of the wet ink vehicle is 0.735 cm3.
The dried/cured ink formulation can be approximately described as follows:
From the data above and the density of the solvent D(S)=0.967 g/cm3 (Dowanol), the quantity of evaporated solvent can be determined, and the weight of the ink vehicle results as 0.747 g/g of the original ink formulation; the corresponding volume V(I) being 0.68 cm3; this gives a density of the ink vehicle D(I) of 1.098 g/cm3. In the present example (base formulation), the volume ratio V(I)/V(P) is thus given as 9.58.
Referring to the magnetic orientation examples (formulations of examples 2a to 2c) the corresponding volume ratios were calculated in the same way, using the determined specific weights of the MOVP and the ink vehicle (I), and the corresponding weight percentages:
Ink vehicle, Pigment and solid content in %; V(I) and V(P) in cm3, dry film thickness in μm, the pigments used had a d50 of 22 μm.
In analogy the volume ratio V(I)/V(P) of example 1, which refers to an intaglio printing ink, was determined to 4.83. The densities of the dried/cured and the wet printing ink were determined as Dinkd=1.37 g/cm3 and Dinkw=1.236 g/cm3. The densities of the pigment and the solvent were determined as D(P)=2.82 g/cm3, and D(S)=0.805 g/cm3 (Ink solvent 27/29 Shell industrial chemicals). 0.3 g/g of pigment (P) were mixed with 0.7 g/g of (ink vehicle (I)+ink solvent (S)). The density of the ink vehicle D(I) was determined to 1.066 g/cm3.
A further point to consider for a successful ink formulation is the thickness of the dried/cured solid coating layer. The coating layer should be thicker than d50/3, preferably thicker than d50/2, wherein d50 is the mean diameter of the magnetic optically variable pigment flakes, determined as known in the art.
Coatings containing solvent must be correspondingly thicker upon application than coatings which are solvent free; considering that the thickness of the dry and solid layer, after evaporation of the solvent, must fulfill the given criteria. In the examples underlying
The amount of non-volatile components in the coating composition of the present invention is chosen between 50% and 100% per weight of the total composition, preferably between 80% and 100% per weight of the total composition.
The skilled person will recognize that the general concept outlined in present description is applicable to a series of printing ink formulations with different amounts of solid contents (with different amounts of MOVP), resulting in different volume ratio of V(I)/V(P).
Table 2 is one possible compilation out of many of a calculated matrix of formulations according to the inventive concept. Volume ratios range between around 0.6 and around 23.
Table 2 provides for an arbitrary selection based on different total solid contents and their respective composition. From a technical point of view, the skilled man knows that for producing satisfying results a minimal amount of pigment is required, and that a high amount of pigment present in the printing ink decreases the printability of the ink and increases the costs.
Therefore Table 2 provides for the selection of suitable coating compositions with respect to the limits of the solid contents as well as to the volume ratio of V(I)/V(P) according to the present invention. The highlighted examples correspond to the most preferred ratio V(I)/V(P) higher than 5.0 of example 2 and serve a mere illustrative purpose.
Printing inks having a volume ratio below 4.0 can be suitable as well for carrying out the present invention; however, the elevated amount of magnetic optically variable pigment with respect to the ink vehicle renders the magnetic orientation of the MOVP more difficult may adds unnecessary cost to the magnetic optically variable printing ink, if the printed ink layer is thick.
The process for manufacturing the printing ink or coating composition of the present invention for producing a magnetically induced image, comprises the step of mixing together volatile components (S), and non-volatile components, the latter consisting of an ink vehicle (I) and of magnetically orientable optically variable interference pigment (P), characterized in that the ratio of the volume of the ink vehicle (V(I)) to the volume of the pigment (V(P)) is higher than 3.0, preferably higher than 4.0, more preferably higher than 5.0.
The volatile components for the process of producing a printing ink or coating composition of the present invention are chosen from organic solvents, water, and mixtures thereof.
The present invention is furthermore related to a process of producing a magnetically induced image, which comprises the steps of a) applying a coating composition according to the present invention to a substrate surface, b) orienting the magnetic pigment particles in the applied coating composition of step a) by applying a magnetic field, and c) curing/drying the oriented coating composition of step b) to fix the particles in the oriented positions.
The coating process of step a) for applying the coating composition to a substrate surface is preferably chosen from engraved copperplate intaglio printing, flexographic printing, gravure printing, roller coating, and silkscreen printing. These processes are well-known to the skilled man.
Said printing processes allow for the deposit of a wet film-layer from about 2 μm to about 50 μm. The preferred wet film deposit is in the range from about 5 μm to about 30 μm. The resulting coating on the substrate has an average dry layer thickness comprised between 2 μm and less or equal than 50 μm, preferably between 5 μm and less or equal than 30 μm, more preferably between 10 μm and less or equal 20 μm.
The orienting step b) can be performed either simultaneously with the coating step a) or subsequently to the coating step a). Magnetic orientation of magnetic particles is described and known in the art. Reference is made in this respect to the prior art documents cited in the introductory portion of the present application.
The curing/drying step c) can be performed by physical evaporation of volatile compounds, UV-curing, oxidative reticulation, chemical cross-linking, electron beam curing, or by any combination thereof. Also this step is known in the art and does not have to be described here in detail.
The present invention is furthermore related to a magnetically induced image coating on a substrate which comprises magnetically oriented pigment (P) in a cured solid ink vehicle (I), characterized in that the ratio of the volume of the ink vehicle (V(I)) to the volume of the pigment (V(P)) is higher than 3.0, preferably higher than 4.0, and most preferably higher than 5.0, and that the coating layer is thicker than d50/3, preferably thicker than d50/2, wherein d50 is the mean diameter of the magnetically orientable optically variable interference pigment flakes. The amount of magnetically oriented pigments in the cured solid ink vehicle (I) ranges between 1% to 40% per weight, preferably between 5% to 30% per weight, more preferably between 10-20% per weight of the wet coating.
The printing ink or coating composition of the present invention can be used for producing magnetically induced images. Said magnetically induced images can be used as security elements for e.g. banks notes, credit cards, access cards, security badges, documents of value, rights or identity, transportation tickets, lottery tickets, event tickets, tax banderoles, security threads, labels, foils, strips or product security applications. Thus, the present invention is also related to the use of the herein disclosed coating compositions for the above applications, as well as to a security document comprising a magnetically induced image obtained with a coating composition of the present invention.
Said security element may further comprise additional marking means such as infrared markers, fluorescent markers, UV markers, phosphorescent markers, magnetic markers, forensic markers and mixtures thereof.
The invention can be practiced on any type of printable sheet or web material, in particular on materials used for producing e.g. banks notes, credit cards, access cards, security badges, documents of value, rights or identity, transportation tickets, lottery tickets, event tickets, tax banderoles, security threads, labels, foils, strips or product security applications. The printable sheet or web material may further comprise a single layer, as well as a plurality of layers.
The present invention will now be further described by reference to non-limiting examples and drawings. Unless indicated otherwise, all amounts are given as weight percents.
In this example, a formulation of an intaglio paper-wipe ink according to the present invention is given.
In this example, a formulation of a silkscreen ink according to the present invention is given.
The formulation of example 2a was applied on security paper. Prior to drying the wet ink was magnetized. The average dry film thickness was 19 μm. The solid content of the ink was 100%, wherein the magnetic optically variable pigment (P) was present in an amount of 20% per weight and the ink vehicle (I) was present in an amount of 80% per weight. The result is shown in
The formulation of example 2b was applied on security paper. Prior to drying the wet ink was magnetized. The average dry film thickness was 14 μm. The solid content of the ink was 80%, wherein the magnetic optically variable pigment (P) was present in an amount of 20% per weight, the ink vehicle (I) was present in an amount of 60% per weight, and the solvent (S) was present in an amount of 20% per weight. The result is shown in
The formulation of example 2c was applied on security paper. Prior to drying the wet ink was magnetized. The average dry film thickness was 11 μm. The solid content of the ink was 50%, wherein the magnetic optically variable pigment (P) was present in an amount of 20% per weight, the ink vehicle (I) was present in an amount of 30% per weight, and the solvent (S) was present in an amount of 50% per weight. The result is shown in
The formula of example 2a showed excellent magnetic orientability; that of example 2b showed some degradation, as compared to example 2a, and that of example 2c showed serious degradation, as compared to example 2a. It can be inferred that formulas with a ratio V(I)/V(P) lower than 3.0 will no longer show any useful effect.
It is evident from
In this example, a formulation of silkscreen ink according to the present invention is given.
In this example, a formulation of flexographic ink according to the present invention is given.
| Number | Date | Country | Kind |
|---|---|---|---|
| 06113891 | May 2006 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2007/052993 | 3/29/2007 | WO | 00 | 11/12/2008 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2007/131833 | 11/22/2007 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2418479 | Pratt et al. | Apr 1947 | A |
| 2570856 | Pratt et al. | Oct 1951 | A |
| 3676273 | Graves | Jul 1972 | A |
| 3791864 | Steingroever | Feb 1974 | A |
| 4705300 | Berning et al. | Nov 1987 | A |
| 4705356 | Berning et al. | Nov 1987 | A |
| 4721271 | Goldstein et al. | Jan 1988 | A |
| 4838648 | Phillips et al. | Jun 1989 | A |
| 5279657 | Phillips et al. | Jan 1994 | A |
| 5364689 | Kashiwagi et al. | Nov 1994 | A |
| 5607504 | Schmid et al. | Mar 1997 | A |
| 5624486 | Schmid et al. | Apr 1997 | A |
| 5807497 | Gailberger et al. | Sep 1998 | A |
| 5824733 | Dobert et al. | Oct 1998 | A |
| 6103361 | Batzar et al. | Aug 2000 | A |
| 6838166 | Phillips et al. | Jan 2005 | B2 |
| 7625632 | Argoitia | Dec 2009 | B2 |
| 20020160194 | Phillips et al. | Oct 2002 | A1 |
| 20040009309 | Raksha et al. | Jan 2004 | A1 |
| 20040051297 | Raksha et al. | Mar 2004 | A1 |
| 20060081151 | Raksha et al. | Apr 2006 | A1 |
| 20060150854 | Benninger et al. | Jul 2006 | A1 |
| Number | Date | Country |
|---|---|---|
| 2006848 | Sep 1971 | DE |
| 0227423 | Jul 1987 | EP |
| 0227423 | Jun 1992 | EP |
| 710508 | May 1996 | EP |
| 686675 | Feb 1998 | EP |
| 1650042 | Apr 2006 | EP |
| 9529140 | Nov 1995 | WO |
| 02073250 | Sep 2002 | WO |
| 02090002 | Nov 2002 | WO |
| 03000801 | Jan 2003 | WO |
| 2004101890 | Nov 2004 | WO |
| 2005002866 | Jan 2005 | WO |
| 2006063926 | Jun 2006 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20090184169 A1 | Jul 2009 | US |