The invention relates to an improved coating comprising layers of diamond like nanocomposite and diamond like carbon.
It is well known in the art to use diamond like carbon coatings or diamond like nanocomposite coatings to increase the hardness or the wear resistance of a substrate.
WO98/33948 describes a layered coating comprising two layered structures, each layered structure comprising a diamond like nanocomposite layer and a diamond like carbon layer.
For some applications, the wear resistance of such a layered coating is insufficient. Therefore, there is a need to develop coatings having increased wear resistance.
It is an object of the present invention to provide an improved coating comprising layers of diamond like carbon and diamond like nanocomposite.
It is another object of the invention to provide a coating having increased wear resistances and reduced internal stresses.
According to a first aspect of the present invention a coating comprising layers of diamond like nanocomposite and diamond like carbon is provided.
The coating comprises a number of layered structures. Each layered structure comprises
The number of layered structures is higher than 4 and is preferably between 5 and 100. More preferably, the number of layered structures is between 10 and 30, as for example 12 or 15.
The coating according to the present invention is characterized by a high wear resistance.
For the purpose of this invention, the number of rotations to wear through the coating divided by the thickness of the coating is used as a measure of the wear resistance of the coating.
The number of rotations to wear through the coating is determined by a ball crater test. In this test a steel ball covered with an abrasive fluid is rotating against the sample and is wearing a crater into the coating under investigation.
In the ball crater test 3 ball craters are formed, a first crater not through the coating, a second crater through the coating and a third crater as close as possible to the coating—substrate interphase.
The number of rotations is 80 rpm, the load is 0.25 N and the abrasive particles have a size of 1 μm.
The number of rotations to wear through the coating is determined by a linear fit of the crater depth versus the number of rotations.
Preferably, the wear resistance of the coating according to the present invention is higher than 1000 rotations/μm, for example 1020 rotations/μm. More preferably, the wear resistance of the coating is higher than 1200 rotations/μm as for example 1400 rotations/μm.
Surprisingly, it has been found that by increasing the number of layered structures, the wear resistance of the coating is improved.
The wear resistance of two coatings having the same total thickness is compared: the first coating has a high number of layered structures; the second coating has a low number of layered structures.
It has been found that the wear resistance of the coating having a high number of layered structures is much higher than the wear resistance of the coating having a low number of layered structures.
Although the applicant does not want to be bound to any theory, it seems that by increasing the number of layered structures, the internal stresses within the coating are better distributed over the thickness of the coating.
The thickness of the first layer comprising a diamond like nanocomposite layer is preferably between 0.05 and 1 μm, more preferably the thickness is between 0.05 and 0.5 μm as for example 0.1 or 0.3 μm.
The thickness of the second layer comprising a diamond like carbon layer is preferably between 0.05 and 1 μm, more preferably the thickness is between 0.05 and 0.5 μm as for example 0.1 or 0.3 μm.
The thickness of the second layer t2 is preferably larger than the thickness of the first layer t1.
Preferably, the ratio of the thickness t2 over the thickness t1, t2/t1, is between 1 and 3, as for example between 1 and 1.5.
The coating may comprise a first intermediate layer between the first layer and the second layer. The first intermediate layer has a composition that is gradually changing from a diamond like nanocomposite composition to a diamond like carbon composition.
The coating according to the present invention may comprise a second intermediate layer between two consecutive layered structures. The composition of the second intermediate layer is gradually changing from a diamond like carbon composition to a diamond like nanocomposite composition.
With diamond like carbon (DLC) is meant any hard carbon-based coating such as hydrogenated amorphous carbon (a-C:H) coatings and metal containing hydrogenated amorphous carbon coatings.
With diamond like nanocomposite is meant any hard carbon coating comprising C, H, Si and O.
Preferably, the diamond like nanocomposite layer preferably comprises in proportion to the sum of C, Si and O in at %, 40 to 90% C, 5 to 40% Si, and 5 to 25% O.
The diamond like nanocomposite layer comprises preferably two interpenetrating networks, one network being an a-C:H diamond like network and the other an a-Si:O glass-like network.
To influence the properties of the coating such as the electrical conductivity one or more layers of the coating, such as the diamond like carbon layer, the diamond like nanocomposite layer or one or more of the intermediate layers, can be doped with one or more transition metal such as Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Re, Fe, Co, Ir, Ni, Pd and Pt.
Other dopants may comprise B, Li, Na, Si, Ge, Te, O, Mg, Cu, Al, Ag and Au.
Preferred dopants are W, Zr and Ti.
Any of the layers of the coating can contain 0.5 to 5 at % of an inert gas such as Ne, Ar or Kr.
According to a second aspect of the present invention a substrate coated with a coating layer as described above is provided.
The coating according to the present invention is in particular suitable to coat substrates requiring a high wear resistance.
Preferred substrates to be coated are parts of an injection mould, such as the mirror and/or stamper of injection moulds for the manufacturing of disc-like information carriers and the venting ring of an injection mould.
According to a third aspect of the present invention a method to manufacture a coated substrate is provided.
The method comprises the steps of
Preferably, the number of layered structures is between 5 and 100. More preferably, the number of layered structures is between 10 and 30.
Before the deposition of the coating, the substrate can be subjected to a pretreatment process such as an ion etching process.
The ion etching process may for example comprise the bombardment of the substrate by ions of an inert gas such as argon.
The invention will now be described into more detail with reference to the accompanying drawings wherein
The coating 12 comprises a number of layered structures 13, each layered structure 13 comprising
The first layer 14 is located closest to the substrate 10.
The coating 12 may comprise a first intermediate layer 16 between the first layer 14 and the second layer 15. The first intermediate layer 16 has a composition that is gradually changing from a diamond like nanocomposite composition to a diamond like carbon composition.
Possibly, the coating 12 may comprise a second intermediate layer 17 between two consecutive layered structures 13. The composition of the second intermediate layer is gradually changing from a diamond like carbon composition to a diamond like nanocomposite composition.
On top of the outermost layered structure 13 a top layer can be deposited. The top layer can be chosen in order to influence the properties of the coating 12. Possible top layers comprise diamond like nanocomposite coatings or antisticking coatings.
To evaluate the coating according to the present invention, some different coatings are compared.
Coating 1 is a reference coating comprising 3 layered structures; coating 2 is a coating according to the present invention comprising 10 layered structures; coating 3 is a coating according to the present invention comprising 12 layered structures and coating 4 is a coating according to the present invention comprising 15 layered structures.
The thickness of the different layers of coatings 1 to 4 is given in table 1 to table 4.
The 1st layered structure is the layered structure located closest to the substrate.
The wear resistance of the different coatings is given in table 5.
From table 5 can be concluded that the wear resistance of a coating having a high number of layered structures (as for example 10 layered structures (example 2), 12 layered structures (example 3) or 15 layered structures (example 4)) is considerably higher than the wear resistance of a coating having 3 layered structures (example 1).
Furthermore, the wear resistance of a coating can be improved by increasing the thickness or the second layer compared to the thickness of the first layer.
The wear resistance of two different coatings (coating 5 and coating 6) is compared. Each coating comprises 10 layered structures; for coating 5, the ratio of the thickness of the second layer over the thickness of the first layer, t2/t1 is ⅓; for coating 6, the ratio of the thickness of the second layer over the thickness of the first layer, t2/t1 is 3.
Test results showed that the wear resistance of the coating of example 6 is 50% higher than the wear resistance of the coating of example 5.
| Number | Date | Country | Kind |
|---|---|---|---|
| 05104514 | May 2005 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2006/004912 | 5/24/2006 | WO | 00 | 12/27/2007 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2006/125613 | 11/30/2006 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4619865 | Keem et al. | Oct 1986 | A |
| 5352493 | Dorfman et al. | Oct 1994 | A |
| 5508368 | Knapp et al. | Apr 1996 | A |
| 6200675 | Neerinck et al. | Mar 2001 | B1 |
| 6228471 | Neerinck et al. | May 2001 | B1 |
| Number | Date | Country |
|---|---|---|
| 0 651 069 | May 1995 | EP |
| 0 856 592 | Aug 1998 | EP |
| WO 9833948 | Aug 1998 | WO |
| 0075394 | Dec 2000 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20080193649 A1 | Aug 2008 | US |