Patent Application
20060078738
1) Field of the Invention
The present invention relates to a technology for extending a life-span of a member that is used under a severe condition, such as a coating formed on a surface of a base metal, a heat-resistant machinery part, a nozzle for a processing machine, and a contact tip for welding.
2) Description of the Related Art
Conventionally, as for a discharge surface treatment technique for generating a pulsed electric discharge between an electrode and a workpiece in an oil-based processing fluid using a green compact obtained by compression-molding ceramic powders or a green compact obtained by heat treating the green compact as the electrode, and for forming a coating, which consists of an electrode material or a matter obtained by provoking a reaction of the electrode material by a discharge energy, on a surface of the workpiece using the discharge energy, there has been established a technique for forming, for example, a hard carbide coating on the surface of the workpiece (see, for example, International Publication No. 99/58744 Pamphlet, International Publication No. 01/05545 Pamphlet, and International Publication No. 01/23640 Pamphlet).
Further, as inventions relating to a welding nozzle or a contact tip for welding that are heat-resistant machinery parts used under high temperature, there have been proposed techniques for lengthening a life-span of the nozzle or the contact tip (see, for example, Japanese Patent Application Laid-open No. H3-291169, Japanese Patent Application Laid-open No. S61-266189, Japanese Patent Application Laid-open No. S63-188477, and Japanese Patent Application Laid-open No. S61-111783).
Members such as a laser processing nozzle, a thermal spraying nozzle, a welding nozzle, and a contact tip for welding have only a short life-span, since they are used under severe conditions of exposure to heat and sputtering of a molten material. These members, therefore, need to be replaced frequently. Namely, they need to be replaced normally at several days' intervals or sometimes at several hours' intervals for members with short life-span.
The techniques disclosed in the literatures are intended to extend the life-spans of these members. The techniques disclosed in the literatures have, however, a disadvantage in that a sufficient effect cannot be achieved in improvement of the life-spans of such members. That is, it leaves much room for improvements on extending the life-span of such members used under these severe conditions.
It is an object of the present invention to solve at least the above problems in the conventional technology.
A coating formed on a surface of a base metal according to one aspect of the present invention has a hard ceramic coating formed on the surface of the base metal. A metal-based coating mainly consisting of at least one metal element selected from a group consisting of Cr, Ni, Fe, W, and Mo is formed on the hard ceramic coating.
A heat-resistant machinery part used under high temperature according to another aspect of the present invention has a body having a metal surface and a coating formed on the metal surface of the body. A hard ceramic coating is formed on the metal surface of the body, and a metal-based coating mainly consisting of at least one metal element selected from a group consisting of Cr, Ni, Fe, W, and Mo is formed on the hard ceramic coating.
A nozzle for a processing machine according to still another aspect of the present invention has a body having a metal surface and a coating formed on the metal surface of the body. A hard ceramic coating is formed on the metal surface of the body, and a metal-based coating mainly consisting of at least one metal element selected from a group consisting of Cr, Ni, Fe, W, and Mo is formed on the hard ceramic coating.
A contact tip for welding according to still another aspect of the present invention has a body having a metal surface and a coating formed on the metal surface of the body. A hard ceramic coating is formed on the metal surface of the body, and a metal-based coating mainly consisting of at least one metal element selected from a group consisting of Cr, Ni, Fe, W, and Mo is formed on the hard ceramic coating.
A method of forming a coating according to still another aspect of the present invention, includes forming a hard ceramic coating on a surface of a base metal; and forming a metal-based coating on the hard ceramic coating, the metal-based coating mainly consisting of at least one metal element selected from a group consisting of Cr, Ni, Fe, W, and Mo.
A method of manufacturing a heat-resistant machinery part used under high temperature according to still another aspect of the present invention, includes manufacturing a body of the heat-resistant machinery part, the body having a metal surface; forming a hard ceramic coating on the metal surface of the body; and forming a metal-based coating on the hard ceramic coating, the metal-based coating mainly consisting of at least one metal element selected from a group consisting of Cr, Ni, Fe, W, and Mo.
A method of manufacturing a nozzle for a processing machine according to still another aspect of the present invention, includes manufacturing a body of the nozzle, the body having a metal surface; forming a hard ceramic coating on the metal surface of the body; and forming a metal-based coating on the hard ceramic coating, the metal-based coating mainly consisting of at least one metal element selected from a group consisting of Cr, Ni, Fe, W, and Mo.
A method of manufacturing a contact tip for welding according to still another aspect of the present invention, includes manufacturing a body of the contact tip, the body having a metal surface; forming a hard ceramic coating on the metal surface of the body; and forming a metal-based coating on the hard ceramic coating, the metal-based coating mainly consisting of at least one metal element selected from a group consisting of Cr, Ni, Fe, W, and Mo.
Exemplary embodiments according to the present invention will be explained below in detail with reference to the accompanying drawings. The present invention is not limited by the embodiments, and various modifications can be made without departing from the spirits of the invention. In the accompanying drawings, respective members are sometimes not shown to scale to facilitate understanding.
Conventionally, it is common to make a laser processing nozzle of a material that mainly consists of Cu (copper). However, the conventional laser processing nozzle has a disadvantage of a short life-span resulting from a flaw that occurs when a workpiece contacts with a burr during a laser processing, a heat-related deformation, a deformation caused by adhesion and separation of a sputtering material, a hole clogging, or the like.
Considering the conventional disadvantage, the laser processing nozzle 10 according to the present embodiment includes the laser processing nozzle main unit 1 that mainly consists of the base metal such as copper, iron, or aluminum, the TiC (chromium carbide) coating 2 that is the hard ceramic coating formed on the surface of the laser processing nozzle main unit 1, and the nickel chromium plating 3 that is the metal coating formed on the Tic (titanium carbide) coating 2.
By thus constituting the laser processing nozzle 10 according to the present embodiment, the surface of the laser processing nozzle 10 is made flaw-resistant, the nozzle 10 has strong resistance to heat, and the nozzle 10 is made sputter-resistant. It is thereby possible to prevent the life-span of the nozzle 10 from being shortened due to occurrence of a flaw caused by contact of the workpiece 5 with a burr during the laser processing, the heat-related deformation, the deformation caused by adhesion and separation of the sputtering material, the hole clogging or the like. It is, therefore, ensured that the life-span of the nozzle 10 is extended.
Namely, the laser processing nozzle 10 according to the present embodiment enjoys a remarkably long life-span and can be used continuously for a long time. A considerable reduction in replacement operation and a cost reduction can be thereby realized.
The hard ceramic coating is made of a ceramic material having a Vickers hardness of 1,000 or more. As the material other than titanium carbide (TiC) for such a hard ceramic coating, titanium nitride (TiN), silicon carbide (SiC), boron carbide (B4C), chromium carbide (e.g., Cr3C2), vanadium carbide (VC), zirconium carbide (ZrC), niobium carbide (e.g., NbC), molybdenum carbide (e.g., MoC), tungsten carbide (WC) or the like can be used. Among these, when titanium carbide (TiC) is used as hard ceramics, a greatest effect of extending the life-span of the laser processing nozzle 10 is obtained according to a result of an experiment conducted by the inventor of the present invention.
Furthermore, a similar effect can be recognized even when the metallic coating formed on the hard ceramic coating is made of a metallic material, other than nickel chromium, manly consisting of a metallic element such as Cr (chromium), Ni (nickel), Fe (iron), W (tungsten), or Mo (molybdenum). These metallic elements exhibit a common property of having a relatively high melting point over a thousand degrees Celsius.
Among these metallic elements, Cr, Mo, and W are materials that form oxides at high temperature and exhibit lubricity. By using the metallic coating mainly consisting of one of these elements, adhesion of the sputtering material to the nozzle 10 can be effectively prevented.
As a method for forming the metallic coating (nickel chromium plating in the present embodiment) on an outermost surface of the laser processing nozzle 10, various methods including plating and evaporation are available. In addition, even when this metallic coating is formed by different methods, no great difference is recognized in extension of the life-span of the laser processing nozzle 10.
Meanwhile, the experiment conducted by the inventor of the present invention has discovered that the hard ceramic coating that is an intermediate layer between the laser processing nozzle main unit 1 and the metallic coating has the greatest effect of extending the life-span of the nozzle 10 when a discharge surface treatment method to be explained hereafter is used for forming the hard ceramic coating.
The discharge surface treatment is the method disclosed in pamphlets of International Publication Nos. 99/55744, 01/05545, 01/23640, and the like. According to the discharge surface treatment, a voltage is applied between a green compact obtained by compression-molding metallic powders that are easily carbonated or a green compact obtained by heat-treating the green compact and a workpiece to generate a pulsed electric discharge, thereby forming a coating made of a metallic carbide obtained by carbonating the electrode material and formed on the workpiece.
The hard carbide coating formed by this discharge surface treatment has properties of being excellent in adhesiveness and being hard to separate. A possible reason is because a gradient property of the coating that the surface of the coating contains many hard carbides, and a ratio of a base material is higher at apposition nearer to a center of the coating.
By way of example, a photograph of a cross section when the TiC coating is formed on the workpiece made of a steel material is shown in
The analysis is performed on the intensities of the characteristic curves Fe—Kα and Ti-kα along the line L-L of
As can be seen from
The present invention will be explained more specifically based on a result of an evaluation test. An instance of conducting a life-span evaluation test to a copper laser processing nozzle obtained by forming a TiC coating on a laser processing nozzle main unit made of copper by the discharge surface treatment, and by further forming a nickel chromium plating on the TiC coating will be explained herein.
The evaluation test is conducted using the following four types of samples.
<Laser Processing Nozzles>
(Sample 1)
A copper laser processing nozzle (conventional nozzle)
(Sample 2)
A copper laser processing nozzle having a nickel chromium plating formed on the surface of the nozzle
(Sample 3)
A copper laser processing nozzle having a TiC coating formed on the surface of the nozzle by the discharge surface treatment
(Sample 4)
A copper laser processing nozzle having a TiC coating formed on the surface of the nozzle by the discharge surface treatment, and having a nickel chromium plating further formed on the TiC coating
Contents of the evaluation and sample life-spans (in comparison with a life-span of the sample 1 that is assumed as 1) are shown in Table 1.
As shown in the Table 1, the life-spans of even the sample 2 (the copper laser processing nozzle having the nickel chromium plating formed on the surface of the nozzle) and the sample 3 (the copper laser processing nozzle having the TiC coating formed on the nozzle by the discharge surface treatment) can be slightly extended. As the samples 2 and 3 are compared, the sample 3 exhibits a greater life-span extending effect. Namely, it can be said that when the TiC coating is formed on the copper laser processing nozzle by the discharge surface treatment, a certain degree of favorable life-span extension effect can be obtained.
Meanwhile, the sample 4 (the copper laser processing nozzle having the TiC coating formed on the surface of the nozzle by the discharge surface treatment, and having the nickel chromium plating further formed on the TiC coating) exhibits a far greater effect than those of the samples 2 and 3. Causes for remarkably extending the life-span of the sample 4 are supposed as follows.
Copper has good heat conductivity but has a high melting point. Conversely, TiC has inferior heat conductivity and has a high melting point. When the heat conductivity is low, temperature tends to rise locally. Due to this, the sputtering material tends to adhere to the nozzle, which possibly causes a damage on the coating. However, the coating formed by the discharge surface treatment is the coating that has the gradient property, and the hard TiC coating is the coating that is promptly blended with a copper component having the excellent heat conductivity. Accordingly, it is considered that the coating is formed into an ideal coating that can prevent melting by the heat using the TiC component having the high melting point and formed on the surface of the nozzle, and that can promptly release the heat entering the laser processing nozzle using the copper component having the good heat conductivity and formed just under the coating.
The hard ceramic coating formed by the discharge surface treatment has a surface roughness as high as 10 micrometers and a thickness of the coating has a large fluctuation. For these reasons, the life-span extending effect can be achieved only by using the hard ceramic coating. However, it is considered that the effect of extending the life-span of the laser processing nozzle is restricted when only the hard ceramic coating is formed. To compensate for the restricted effect, the surface of the hard ceramic coating formed by the discharge surface treatment is covered with the metallic coating of nickel chromium or the like that has relatively a high melting point. This is the concept of the present invention.
While the instance of using the copper laser processing nozzle main unit as the laser processing nozzle main unit in the evaluation test has been explained, it is confirmed by an experiment that a similar effect can be achieved even when a laser processing nozzle main unit made of iron (Fe) or made of aluminum (Al) is used.
According to the present invention, therefore, it is possible to provide the laser processing nozzle which is far more flaw-resistant, to which the less sputtering material adheres, and which enjoys a long life-span, as compared with the conventional laser processing nozzle.
The test is conducted by continuous processing for cutting a sheet metal by a laser. It is also confirmed that the life-span of even the nozzle in the form of the sample 3 can be sufficiently extended in a processing in which the heat does not intensively enter the nozzle such as piecing. This is because a damage caused by the burr generated by the processing contacts with the nozzle is greater than a damage caused by the heat, in the processing such as piecing. The nozzle can sufficiently resist such a damage only by the hardness of the coating.
Welding also has the same disadvantage as that in the laser processing explained in the first embodiment. Namely, life-spans of a nozzle and a contact tip for welding are shortened due to heat or adhesion of a sputtering material.
Therefore, a hard ceramic coating is formed on a surface of the welding nozzle and that of the contact tip for welding, whereby the life-spans of the nozzle and tip can be extended. Further, a predetermined metallic coating is formed on each hard ceramic coating, whereby the life-span of each of the welding nozzle and the contact tip for welding can be advantageously extended more effectively. Thanks to these, the welding nozzle and the contact tip for welding can be used continuously for a long time, thereby making it possible to provide a welding nozzle and a contact tip for welding that realize a great reduction in replacement operation and a cost reduction.
Further, as shown in
A penetrating hole that penetrates a central portion of the contact tip for welding 21 in a longitudinal direction is formed in the contact tip for welding 21. A welding rod 25 is arranged in the penetrating hole. During welding, a shield gas 31 is supplied to a region between the welding nozzle 11 and the contact tip for welding 21.
By thus constituting the welding nozzle 11 and the contact tip for welding 21 according to the present embodiment, the welding nozzle 11 and the contact tip for welding 21 have strong heat resistance during the welding, and the welding nozzle 11 and the contact tip for welding 21 are made sputter-resistant. It is thereby possible to prevent the life-spans of the welding nozzle 11 and the contact tip for welding 21 from being shortened due to a heat-related deformation during the welding, a deformation caused by adhesion and separation of the sputtering material, or the like. It is thus ensured that the life-spans of the welding nozzle 11 and the contact tip for welding 21 are extended.
Namely, the welding nozzle 11 and the contact tip for welding 21 according to the present embodiment have remarkably long life-spans and can be used continuously for a long time. The considerable reduction in replacement operation and the cost reduction are, therefore, realized.
Similarly to the first embodiment, as the material for the hard ceramic coating, titanium carbide (TiC), titanium nitride (TiN), silicon carbide (SiC), boron carbide (B4C), chromium carbide (e.g., Cr3C2), vanadium carbide (VC), zirconium carbide (ZrC), niobium carbide (e.g., NbC), molybdenum carbide (e.g., MoC), tungsten carbide (WC) or the like can be used.
Furthermore, the metallic coating formed on the hard ceramic coating can be a coating made of a metallic material, other than nickel chromium, manly consisting of a metallic element such as Cr (chromium), Ni (nickel), Fe (iron), W (tungsten), or Mo (molybdenum). Among these metallic elements, when the metallic coating mainly consisting of one of Cr, Mo, or W, adhesion of the sputtering material to the welding nozzle 11 and the contact tip for welding 21 can be effectively prevented.
The present invention will be explained more specifically based on a result of an evaluation test. An instance of conducting a life-span evaluation test to a copper welding nozzle obtained by forming a TiC coating on a welding nozzle main unit made of copper by the discharge surface treatment, and by further forming a nickel chromium plating on the TiC coating will be explained herein.
In addition, an instance of conducting a life-span evaluation test to a copper contact tip for welding obtained by forming a TiC coating on a contact tip for welding main unit made of copper by the discharge surface treatment, and by further forming a nickel chromium plating on the TiC coating will be explained herein.
Each evaluation test is conducted using the following four types of samples.
<Welding Nozzles>
(Sample 5)
A copper welding nozzle (conventional nozzle)
(Sample 6)
A copper welding nozzle having a nickel chromium plating formed on the surface of the nozzle
(Sample 7)
A copper welding nozzle having a TiC coating formed on the surface of the nozzle by the discharge surface treatment
(Sample 8)
A copper welding nozzle having a TiC coating formed on the surface of the nozzle by the discharge surface treatment, and having a nickel chromium plating further formed on the TiC coating
Contents of the evaluation and sample life-spans (in comparison with a life-span of the sample 5 that is assumed as 1) are shown in Table 2.
<Contact Tip for Welding>
(Sample 9)
A copper contact tip for welding (conventional nozzle)
(Sample 10)
A copper contact tip for welding having a nickel chromium plating formed on the surface of the tip
(Sample 11)
A copper contact tip for welding having a TiC coating formed on the surface of the tip by the discharge surface treatment
(Sample 12)
A copper contact tip for welding having a TiC coating formed on the surface of the tip by the discharge surface treatment, and having a nickel chromium plating further formed on the TiC coating
Contents of the evaluation and sample life-spans (in comparison with a life-span of the sample 9 that is assumed as 1) are shown in Table 3.
As shown in the Table 2, the life-spans of even the sample 6 (the copper welding nozzle having the nickel chromium plating formed on the surface of the nozzle) and the sample 7 (the copper welding nozzle having the TiC coating formed on the nozzle) can be slightly extended. As the samples 6 and 7 are compared, the sample 7 exhibits a greater life-span extending effect. Namely, it can be said that when the TiC coating is formed on the copper welding nozzle by the discharge surface treatment, a certain degree of favorable life-span extension effect can be obtained.
Meanwhile, the sample 8 (the copper welding nozzle having the TiC coating formed on the surface of the nozzle by the discharge surface treatment, and having the nickel chromium plating further formed on the TiC coating) exhibits a greater effect than those of the samples 6 and 7, although the effect is not so greater than that of the laser nozzle.
As shown in the Table 3, the life-spans of even the sample 10 (the copper contact tip for welding having the nickel chromium plating formed on the surface of the tip) and the sample 11 (the copper contact tip for welding having the TiC coating formed on the tip) can be slightly extended. When the samples 10 and 11 are compared, the sample 11 exhibits a greater life-span extending effect. Namely, it can be said that when the TiC coating is formed on the copper contact tip for welding by the discharge surface treatment, a certain degree of favorable life-span extension effect can be obtained.
Meanwhile, the sample 12 (the copper contact tip for welding having the TiC coating formed on the surface of the tip by the discharge surface treatment, and having the nickel chromium plating further formed on the TiC coating) exhibits a greater effect than those of the samples 10 and 11.
Causes for remarkably extending the life-spans of the samples 8 and 12 are supposed as follows.
Copper has good heat conductivity but has a high melting point. Conversely, TiC has inferior heat conductivity and has a high melting point. When the heat conductivity is low, temperature tends to rise locally. Due to this, the sputtering material tends to adhere to the nozzle, which possibly causes a damage on the coating. However, the coating formed by the discharge surface treatment is the coating that has the gradient property, and the hard TiC coating is the coating that is promptly blended with a copper component having the good heat conductivity. Accordingly, it is considered that the coating is formed into an ideal coating that can prevent melting by the heat using the TiC component having the high melting point and formed on the surface of the nozzle or contact tip, and that can promptly release the heat entering the welding nozzle and the contact tip for welding using the copper component having the good heat conductivity and formed just under the coating.
The hard ceramic coating formed by the discharge surface treatment has a surface roughness as high as 10 micrometers and a thickness of the coating has a large fluctuation. The life-span extending effect can be achieved only by using the hard ceramic coating. However, it is considered that the effect of extending the life-span of the welding nozzle or the contact tip for welding is restricted when only the hard ceramic coating is formed. To compensate for the restricted effect, the surface of the hard ceramic coating formed by the discharge surface treatment is covered with the metallic coating of nickel chromium or the like that has relatively a high melting point. This is the concept of the present invention.
A temperature of the contact tip for welding, in particular, is as high as several hundreds of degrees Celsius because of direct conduction of a welding heat. When the temperature of the contact tip for welding is high, Cr (chromium) contained in the nickel chromium plated coating is oxidized into Cr2O3 (chromium oxide), which exhibit lubricity. It is, therefore, supposed that the surface of the contact tip for welding is advantageously made deposit-resistant.
While the instances of using the copper welding nozzle main unit and the copper contact tip for welding main unit as the welding nozzle main unit and the contact tip for welding main unit, respectively, in the evaluation tests have been explained, it is confirmed by an experiment that a similar effect can be achieved even when a welding nozzle main unit made of iron (Fe) or made of aluminum (Al), or a contact tip for welding main unit made of iron (Fe) or made of aluminum (Al) is used.
According to the present invention, therefore, it is possible to achieve the welding nozzle and the contact tip for welding that enjoy long life-spans, as compared with the conventional welding nozzle and the conventional contact tip for welding. It is thereby possible to provide the welding nozzle and the contact tip for welding that can be used continuously for a long time, which can realize a considerable reduction in replacement operation and a cost reduction.
Thermal spraying is a method for spraying a molten material from a nozzle and for causing the material to adhere to a surface of a workpiece. The thermal spraying also has the same disadvantage as that in the laser processing explained in the first embodiment.
Therefore, a hard ceramic coating is formed on a surface of a thermal spraying nozzle, whereby a life-span of the thermal spraying nozzle can be extended. Further, a predetermined metallic coating is formed on the hard ceramic coating, whereby the life-span of the thermal spraying nozzle can be advantageously extended more effectively. Thanks to these, the thermal spraying nozzle can be used continuously for a long time, thereby making it possible to provide a thermal spraying nozzle that realizes a great reduction in replacement operation and a cost reduction.
By thus constituting the thermal spraying nozzle 51 according to the present embodiment, the thermal spraying nozzle 51 has strong heat resistance during the welding and the thermal spraying nozzle 51 is made sputter-resistant. It is thereby possible to prevent the life-span of the thermal spraying nozzle 51 from being shortened due to a heat-related deformation during the welding, a deformation caused by adhesion and separation of the sputtering material, or the like. It is thus ensured that the life-span of the thermal spraying nozzle 51 is extended.
Namely, the thermal spraying nozzle 51 according to the present embodiment has a remarkably long life-span and can be used continuously for a long time. The considerable reduction in replacement operation and the cost reduction are, therefore, realized.
As the material for the hard ceramic coating and the metallic coating formed on the hard ceramic coating according to the present embodiment, the same materials as those according to the first embodiment can be used.
The present invention will be explained more specifically based on a result of an evaluation test. An instance of conducting a life-span evaluation test to a copper thermal spraying nozzle obtained by forming a TiC coating on a thermal spraying nozzle main unit made of copper by the discharge surface treatment, and by further forming a nickel chromium plating on the TiC coating will be explained herein.
The evaluation test is conducted using the following four types of samples.
<Thermal Spraying Nozzles>
(Sample 13)
A copper thermal spraying nozzle (conventional nozzle)
(Sample 14)
A copper thermal spraying nozzle having a nickel chromium plating formed on the surface of the nozzle
(Sample 15)
A copper thermal spraying nozzle having a TiC coating formed on the surface of the nozzle by the discharge surface treatment
(Sample 16)
A copper thermal spraying nozzle having a TiC coating formed on the surface of the nozzle by the discharge surface treatment, and having a nickel chromium plating further formed on the TiC coating
Contents of the evaluation and sample life-spans (in comparison with a life-span of the sample 13 that is assumed as 1) are shown in Table 4.
As shown in the Table 4, the life-spans of even the sample 14 (the copper thermal spraying nozzle having the nickel chromium plating formed on the surface of the nozzle) and the sample 15 (the copper thermal spraying nozzle having the TiC coating formed on the nozzle) can be slightly extended. When the samples 14 and 15 are compared, the sample 15 exhibits a greater life-span extending effect. Namely, it can be said that when the TiC coating is formed on the copper thermal spraying nozzle by the discharge surface treatment, a certain degree of favorable life-span extension effect can be obtained.
Meanwhile, the sample 16 (the copper thermal spraying nozzle having the TiC coating formed on the surface of the nozzle by the discharge surface treatment, and having the nickel chromium plating further formed on the TiC coating) exhibits a greater effect than those of the samples 14 and 15.
Causes for remarkably extending the life-span of the sample 16 are supposed as follows.
Copper has good heat conductivity but has a high melting point. Conversely, TiC has inferior heat conductivity and has a high melting point. When the heat conductivity is low, temperature tends to rise locally. Due to this, the sputtering material tends to adhere to the nozzle, which possibly causes a damage on the coating. However, the coating formed by the discharge surface treatment is the coating that has the gradient property, and the hard TiC coating is the coating that is promptly blended with a copper component having the excellent heat conductivity. Accordingly, it is considered that the coating is formed into an ideal coating that can prevent melting by the heat using the TiC component having the high melting point and formed on the surface of the nozzle, and that can promptly release the heat entering the thermal spraying nozzle using the copper component having the good heat conductivity and formed just under the coating.
The hard ceramic coating formed by the discharge surface treatment has a surface roughness as high as 10 micrometers and a thickness of the coating has a large fluctuation. The life-span extending effect can be achieved only by using the hard ceramic coating. However, it is considered that the effect of extending the life-span of the thermal spraying nozzle is restricted when only the hard ceramic coating is formed. To compensate for the restricted effect, the surface of the hard ceramic coating formed by the discharge surface treatment is covered with the metallic coating of nickel chromium or the like that has relatively a high melting point. This is the concept of the present invention.
A temperature of the thermal spraying nozzle, in particular, is as high as several hundreds of degrees Celsius because of direct conduction of a welding heat. When the temperature of the thermal spraying nozzle is high, Cr (chromium) contained in the nickel chromium plated coating is oxidized into Cr2O3 (chromium oxide), which exhibit lubricity. It is, therefore, supposed that the surface of the thermal spraying nozzle is advantageously made deposit-resistant.
The instance of using the copper thermal spraying nozzle main unit as the thermal spraying nozzle main unit in the evaluation test has been explained. However, it is confirmed by an experiment that a similar effect can be achieved even when a thermal spraying nozzle main unit made of iron (Fe) or made of aluminum (Al) is used.
According to the present invention, therefore, it is possible to achieve the thermal spraying nozzle which enjoys a long life-span, as compared with the conventional thermal spraying nozzle. It is thereby possible to provide the thermal spraying nozzle that can be used continuously for a long time, which can realize a considerable reduction in replacement operation and a cost reduction.
The nozzle for the processing machine and the contact tip for welding are taken as examples for describing the present invention. However, the present invention is not limited to these examples, and is applicable to a broad range of heat-resistant machinery parts that are used under severe conditions, such as high temperature.
Although the invention has been described with respect to a specific embodiment for a complete and clear disclosure, the appended claims are not to be thus limited but are to be construed as embodying all modifications and alternative constructions that may occur to one skilled in the art which fairly fall within the basic teaching herein set forth.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-158895 | Jun 2003 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP04/00803 | Jan 2004 | US |
| Child | 11291989 | Dec 2005 | US |