Patent Grant
9328424
1. Field of the Invention
The present invention relates to an enamel coating method and an enamel coating apparatus using the same, and more particularly, to an enamel coating method and apparatus for a metal pin tube and a manhole cover in which a heat transfer pin is formed on the surface thereof.
2. Description of the Related Art
There are many cases in which a metal tube, a manhole cover, and the like are used in a highly humid environment, and therefore various types of coatings are applied to surfaces of the metal tube, the manhole cover, and the like in order to improve durability thereof. Among these, enamel coating has strong heat resistance and acid resistance characteristics, but is not widely used due to its difficult coating process such as requiring a firing process at a high temperature (750 to 1,000° C.).
In particular, since the firing process at the high temperature is required, it is difficult to secure economic efficiency when preparing a large scale firing chamber for the purpose of coating a long and bulky coating object with enamel. Thus, it is highly difficult to apply the enamel coating to the long and bulky coating object.
However, when coating a metal tube used in a harsh environment (when performing heat exchange using a gas containing acid components in a generator, a tube surface and a heat transfer pin are exposed to an acid dew point while the gas is cooled, and therefore a low temperature corrosion phenomenon occurs in a pin tube) such as a pin tube used as a heat exchanger for generator, with a general coating composition, the corroded metal tube should be replaced periodically, and therefore there are problems that cause inconvenience and high costs. In order to solve these problems, a metal tube made of a stainless steel or titanium-based material is used, but this requires high costs and cannot be the fundamental solution for acid corrosion even though the replacement cycle of the pin tube is increased. In addition, Teflon coating may be applied to the pin tube, but the Teflon material has a limitation in heat resistance. Accordingly, it can be desirable to apply the enamel coating to the metal tube, the manhole cover, and the like which are used in the harsh environment requiring heat resistance and acid resistance.
Coating the surfaces of the metal tube, the manhole cover, and the like with enamel is difficult for the following reasons.
First, as described above, a high-temperature firing chamber is required. In particular, when a length of the metal tube is large, a large-sized high temperature firing chamber is required.
Second, the metal tube is likely to be bent or distorted during coating while being subjected to the high temperature firing process. In this instance, as the length of the metal tube is increased, a frequency of the occurrence of this problem increases. Accordingly, a method for preventing such deformation of the metal tube when coating the metal tube is needed.
Third, oil-based components bonded to the surface of the metal tube in a preprocessing process hinder an aqueous enamel glaze from being bonded to the surface of the metal tube, and therefore it is necessary to remove the oil-based components before applying the enamel coating. However, through the conventional preprocessing processes, it is difficult to efficiently remove the oil-based components.
That is, a blasting process of the preprocessing process cannot efficiently remove the oil-based components, and when a wet process is introduced, the preprocessing process becomes complicated and causes deterioration in coating efficiency. Accordingly, there is a demand for a method for easily removing the oil-based components bonded to the surface of the metal tube.
Fourth, it is difficult to remove air bubbles formed within the coating film after coating with the enamel glaze. Removing the air bubbles formed in the coating film affects the coating quality, and is very important in the coating process. In particular, in a pin tube for a heat exchanger (see
Therefore, in order to take advantage of excellent properties of the enamel coating by applying the enamel coating to the metal tube, the above-described problems should be first solved.
The present invention is directed to an enamel coating method and apparatus in which a miniaturized firing chamber is adopted such that a long metal tube can be easily coated with an enamel glaze.
Also, the present invention is directed to an enamel coating method and apparatus which may heat a surface of a coating object such as a metal tube or a manhole cover to a temperature of 750 to 1,000° C. within a very short period of time, heat the whole surface of the coating object to a uniform temperature, minimize coating defects even in the case of a metal tube (for example, a metal pin tube) or a manhole cover having severe irregularities formed on a surface thereof, and apply coating with excellent durability to the whole coating object.
In particular, the present invention is directed to an enamel coating method and apparatus which may minimize coating defects and form uniform and solid coating by adopting a method in which the coating object is first heated and then the heat is transferred to the enamel glaze instead of adopting a method in which heat is transferred to the coating object through the enamel glaze applied to the surface of the coating object at the time of firing.
Also, the present invention is directed to an enamel coating method and apparatus which may prevent a long metal tube from being bent or distorted in a high temperature firing process.
Also, the present invention is directed to an enamel coating method and apparatus which may simplify a coating process of a metal tube and simplify the equipment.
According to an aspect of the present invention, there is provided an enamel coating method including: (a) preprocessing a surface of a conductive coating object by feeding the coating object into a preprocessing chamber by an in-feed conveyor; (b) coating the surface of the coating object with an enamel glaze supplied from an enamel glaze supply nozzle provided inside a coating chamber by feeding the preprocessed coating object into the coating chamber; and (c) firing the coated coating object by feeding the coated coating object into a firing chamber, wherein the firing chamber in the (c) firing includes a firing chamber conveyor having at least two transport rollers, and the firing chamber conveyor transports the coating object to an output conveyor while supporting a lower side of the coating object by the at least two transport rollers.
The transport roller is a rod with a circular cross-section, and has a tapered shape in which a diameter of the transport roller is gradually increased toward both end portions thereof from a central portion thereof.
An induction heater is provided in the firing chamber in the (c) firing, and the (c) firing includes heating the coated coating object to a temperature of 750 to 1,000° C. by the induction heater.
The induction heater is a high-frequency induction heater.
The coating object is a metal tube or a manhole cover.
The coating object is the metal tube, and the induction heater has a cylindrical or circular arc shape with a radius of curvature 5 to 150 mm larger than an external diameter of the metal tube and is provided in a movement direction of the metal tube so that a constant distance is maintained between an outer surface of the moved metal tube and an inner curved surface of the induction heater.
The metal tube advances while being rotated and is fed into the preprocessing chamber by the in-feed conveyor, and the fired metal tube is separated from the firing chamber by an out-feed conveyor.
The metal tube is a pin tube for a heat exchanger in which a heat transfer pin is formed on a surface of the tube.
The transport roller is provided on an axis forming an angle of 5° to 35° clockwise or counterclockwise with a lateral line perpendicular to a longitudinal direction of the firing chamber conveyor, and the firing chamber conveyor transports the coating object to the output conveyor by rotating and advancing the coating object while supporting the lower side of the coating object by the transport roller.
The transport roller includes a cooling liquid circulation path passing through a rotating shaft, and the (c) firing further includes circulating a cooling liquid through the cooling liquid circulation path.
According to another aspect of the present invention, there is provided an enamel coating apparatus including: a preprocessing chamber that preprocesses a surface of a conductive coating object fed from an in-feed conveyor; a coating chamber that coats the surface of the coating object with an enamel glaze supplied from an enamel glaze supply nozzle provided therein when the preprocessed coating object is fed; and a coating unit that includes a firing chamber for firing the coated coating object when the coated coating object is fed, wherein a firing chamber conveyor for transporting the coating object to an output conveyor while supporting a lower side of the coating object is provided in the firing chamber, and includes at least two transport rollers.
The transport roller is a rod with a circular cross-section, and has a tapered shape in which a diameter of the transport roller is gradually increased toward both end portions thereof from a central portion thereof.
An induction heater is provided in the firing chamber, and the induction heater heats the coated coating object to a temperature of 750 to 1,000° C.
The induction heater is a high-frequency induction heater.
The coating object is a metal tube or a manhole cover.
The coating object is the metal tube, and the induction heater has a cylindrical or circular arc shape with a radius of curvature 5 to 150 mm larger than an external diameter of the metal tube and is provided in a movement direction of the metal tube so that a constant distance is maintained between an outer surface of the moved metal tube and an inner curved surface of the induction heater.
The in-feed conveyor that feeds the metal tube into the preprocessing chamber by rotating and advancing the metal tube and an out-feed conveyor that feeds the coated metal tube out of the firing chamber.
The transport roller is provided on an axis forming an angle of 5° to 35° clockwise or counterclockwise with a lateral line perpendicular to a longitudinal direction of the firing chamber conveyor.
Each of the in-feed conveyor and the output conveyor includes at least two transport rollers, and the transport roller is provided on an axis forming an angle of 5° to 35° clockwise or counterclockwise with a lateral line perpendicular to a longitudinal direction of each of the in-feed conveyor and the output conveyor.
Additional aspects and/or advantages of the invention will be set forth in part in the description which follows and, in part, will be obvious from the description, or may be learned by practice of the invention.
The above and other objects, features and advantages of the present invention will become more apparent to those of ordinary skill in the art by describing in detail exemplary embodiments thereof with reference to the accompanying drawings, in which:
Exemplary embodiments of the present invention will be described in detail below with reference to the accompanying drawings. While the present invention is shown and described in connection with exemplary embodiments thereof, it will be apparent to those skilled in the art that various modifications can be made without departing from the spirit and scope of the invention. When it is determined that the detailed description of known art related to the present invention may obscure the gist of the present invention, the detailed description thereof will be omitted.
As shown in
As examples of the coating object 10, a conductive metal tube, a conductive manhole cover, and the like may be given.
In the (a) preprocessing, a heating means 111 is provided in the preprocessing chamber 110, and a preprocessing process of heating the metal tube 10 at a temperature of 300 to 600° C. for 10 seconds to 4 minutes using the heating means 111 is performed.
A preprocessing process of the metal tube in the (a) preprocessing may be performed by methods typically used in the related art, for example, a shot blasting method, a sand blasting method, a grit blasting method, and the like.
In addition, it is possible to preprocess the metal tube by wet preprocessing typically used in preprocessing of a metal, and it is possible to adopt a method of more efficiently remove foreign substances of the surface of the metal tube by generating ultrasound within a preprocessing solution at the time of the wet preprocessing.
However, oil-based components are not removed well by the blasting process, and when a wet process is adopted, the equipment is increased and the preprocessing process becomes complicated and causes deterioration in coating efficiency, and therefore the wet process is difficult to adopt for an automated enamel coating method according to an embodiment of the present invention.
Thus, in the enamel coating method according to an embodiment of the present invention, a method of burning and removing the oil-based components bonded to the surface of the metal tube 10 by heating the metal tube 10 at a high-temperature using the heating means 111 adopted in the preprocessing chamber 110 for a short period of time may be adopted.
The above-described high temperature heating process may be performed by the heating means 111 which is typically used. That is, as examples of the heating means, an electric furnace, a plasma heat treatment furnace, a heavy oil furnace, a light oil furnace, a gas furnace, a hydrogen heat treatment furnace, an induction heating furnace, and the like may be given.
In the enamel coating method according to an embodiment of the present invention, an induction heater 111 may be particularly used as the induction heating furnace as shown in
In the enamel coating method according to an embodiment of the present invention, the metal tube 10 is fed in while being rotated, and therefore the shape of the induction heater 111 is not an issue. That is, the metal tube 10 may be evenly heated regardless of what shape the induction heater 111 has, and therefore the shapes of the induction heater 111 known in the related art may all be used.
As the induction heater 111, as shown in
The high-temperature heat treatment in the preprocessing process is performed at a temperature of 300 to 600° C., more preferably at a temperature of 400 to 500° C., for 10 seconds to 4 minutes, more preferably for 10 seconds to 2 minutes.
When the high-temperature heat treatment is performed at a temperature less than 300° C., removal of oil-based components is very time-consuming, and when the high-temperature heat treatment is performed at a temperature exceeding 500° C., economical efficiency is reduced. In addition, at less than 10 seconds, it is difficult to reach a required high-temperature, and at 5 minutes or more, decrease in productivity may be caused.
When the above-described high temperature heat treatment is performed using the induction heater 111, it is possible to heat the metal tube 10 to a heat treatment temperature (300 to 600° C.) within approximately one minute, and therefore the preprocessing chamber 110 may be readily miniaturized, and preprocessing costs may be significantly reduced.
In addition, the induction heater 111 may be readily manufactured in a small size so as to conform to the metal tube 10 having a relatively small diameter compared to the conventional heating means, and have excellent energy efficiency because heating is performed in close proximity.
As shown in
As shown in
As can be seen from
In the (b) coating of the surface of the coating object 10, an air spray nozzle 123 is provided behind the enamel glaze supply nozzle 121 in an advancing direction of the metal tube 10 inside the coating chamber 120, and the (b) coating of the surface of the coating object 10 includes spraying air toward the metal tube 10 from the air spray nozzle 123 at a speed of 0.05 m/s to 1.5 m/s.
In the (b) coating of the surface of the metal tube 10, as shown in
In addition, by bringing the coating brush 122 provided behind the enamel glaze supply nozzle 121 in the advancing direction of the metal tube 10 into contact with the surface of the metal tube 10 which advances while being rotated, it is possible to simultaneously remove excessive enamel glaze applied to the surface of the metal tube 10 and air bubbles formed inside the coating film.
In addition, the air spray nozzle 123 is provided behind the enamel glaze supply nozzle 121, and therefore, by spraying air to the surface of the metal tube 10, which advances while being rotated, at a speed of preferably 0.05 m/s to 1.5 m/s, more preferably 0.1 m/s to 1.0 m/s, the excessive enamel glaze applied to the surface of the metal tube 10 and the air bubbles formed inside the coating film are simultaneously removed, and the applied enamel glaze is dried.
When the above-described spray speed of the air is less than 0.05 m/s, the effect of the air spray is difficult to ensure, and when the spray speed exceeds 1.5 m/s, the applied enamel glaze is excessively removed.
When performing the air spray process by the air spray nozzle 123, the excessive enamel glaze may be easily removed from the surface of the metal tube, the air bubbles formed inside the coating film may be efficiently removed, and by primarily drying the enamel glaze applied to the surface of the metal tube in the previous step of the firing, it is possible to prevent formation of an unsmooth coating surface formed in such a manner that the enamel glaze falls in the direction of gravity to be hardened in the firing processing.
In addition, by efficiently removing the air bubbles formed on the surface of the metal tube in the coating process of the enamel glaze, it is possible to form a uniform and solid coating film. In particular, when coating the metal tube (for example, metal pin tube) with severe irregularities formed thereon, it is possible to very easily remove the air bubbles which are unevenly formed and difficult to remove using the existing method.
The air spray nozzle 123 is constituted of a hot air spray nozzle, and it is more preferable that the air sprayed from the air spray nozzle 123 be hot air of 30 to 200° C. When spraying the hot air as described above, removal of the air bubbles may be more efficiently achieved, and drying the applied enamel glaze before the metal tube 10 enters the firing chamber 13 may be more efficiently achieved.
In addition, the air spray nozzle 123 may be provided behind the coating brush 122 provided behind the enamel glaze supply nozzle 121. In this case, the enamel glaze may be uniformly applied to the surface of the metal tube, and removal of the air bubbles may be more completely achieved.
As shown in
The installation position of the coating brush 122 is not limited as long as the coating brush 122 is provided behind the enamel glaze supply nozzle 121 in the advancing direction of the metal tube 10, and the type of the coating brush 122 is not limited as long as the coating brush 122 can simultaneously remove the excessive enamel glaze applied to the metal tube 10 and the air bubbles formed inside the coating film.
When the metal tube 10 is a pin tube in which a heat transfer pin 12 is formed on the surface of the tube, a single fiber constituting the coating brush 122 should have an appropriate strength and thickness in order for the enamel glaze to be uniformly applied to the heat transfer pin. Meanwhile, when the coating object is the manhole cover, the coating brush 122 may be provided in a position at which the coating brush 122 is brought into good contact with the manhole cover. For example, the coating brush 122 may be provided in at least one of a top surface, a bottom surface, and a side surface of the manhole cover, so that the manhole cover can be automatically brought into contact with the coating brush 122 while advancing.
The installation position of the air spray nozzle 123 is not limited as long as the air spray nozzle 123 is provided behind the enamel glaze supply nozzle 121 in the advancing direction of the metal tube 10, and the type of the air spray nozzle 123 is not limited as long as the air spray nozzle 123 can simultaneously remove the excessive enamel glaze applied to the metal tube 10 and the air bubbles formed inside the coating film.
Meanwhile, when the coating object is the manhole cover, the air spray nozzle 123 may be provided in a position at which the air spray nozzle 123 is brought into good contact with the manhole cover. For example, the air spray nozzle 123 may be provided in at least one of a top surface, a bottom surface, and a side surface of the manhole cover, so that the manhole cover can be automatically brought into contact with the sprayed air while advancing. In this case, in particular, the air spray nozzle is provided in such a manner that an angle between the surface of the manhole cover and the advancing direction of the manhole cover is 1 to 85 degrees, more preferably 1 to 45 degrees.
In particular, as shown in
As described above, when the sprayed air reaches the lowest end of the metal tube 10 which advances while being rotated, the excessive enamel glaze applied to the surface of the metal tube 10 is easily assembled to the bottom of the tube by the sprayed air, and easily falls downward to be removed by the action of gravity. In addition, spraying the air in the direction opposite to the rotating direction of the metal tube 10 is preferable to spraying the air in the same direction as the rotating direction of the metal tube 10 in that the removal of the excessive enamel glaze can be more efficiently achieved.
The enamel coating method according to an embodiment of the present invention has the coating brush 122 and/or the air spray nozzle 123, and therefore excellent effects may be achieved even when coating the metal tube having a complex surface shape such as a pin tube for heat exchanger (10 of
In the (c) firing, a heating means 131 is provided in the firing chamber 130, and the (c) firing includes heating the coated coating object to a temperature of 750 to 1,000° C. by the heating means 131.
It is more preferable that a high-temperature firing process of the metal tube in the (c) firing be performed at a temperature of 750 to 870° C. As the heating means 131, one which is typically used in the related art may be used without restriction, and for example, an electric furnace, a plasma heat treatment furnace, a heavy oil furnace, a light oil furnace, a gas furnace, a hydrogen heat treatment furnace, an induction heating furnace, or the like may be used.
According to an embodiment of the present invention, as the heating means 131, the induction heating furnace may be used. As the induction heating furnace, the induction heater 131 as shown in
In particular, the metal tube 10 is heated by an induction heating method, so that heat is generated only on the surface of the metal tube that is a conductor. Thus, the metal tube is first heated and the enamel glaze applied to the surface of the metal tube is heated by the generated heat, and therefore the enamel glaze is more uniformly and firmly bonded to the surface of the metal tube. In addition, coating defects may be reduced.
On the other hand, when the metal tube 10 is heated by the conventional heating means, heat is transferred to the metal tube through the enamel glaze applied to the outer surface of the metal tube, and therefore the enamel glaze is first heated to flow down in the direction of gravity before the metal tube is heated. As a result, coating defects may easily occur, and rigidity of the coating may be reduced compared to the induction heating method.
The metal tube 10 in the enamel coating method according to an embodiment of the present invention is fed in while being rotated, and therefore the shape of the induction heater 131 is not an issue. That is, the metal tube 10 may be evenly heated regardless of what shape the induction heater 131 has, and therefore the shapes of the induction heater 131 known in the related art may all be used.
The induction heater 131 may be the same as the induction heater 111 of the preprocessing chamber 110 as shown in
Meanwhile, when the manhole cover is coated, an induction heater capable of heating the top, the bottom, and/or the side surface of the manhole cover, that is, an induction heater having a rectangular tunnel shape, is preferably used.
As can be seen from
As the induction heater 131 in the enamel coating method according to an embodiment of the present invention, a high-frequency induction heater using a high-frequency current may be used.
In the (c) firing, the firing process of the metal tube is performed at a high temperature of 750 to 1,000° C. Thus, when the metal tubes 10 are connected with each other so that front and rear ends of the metal tubes are not mutually supported, bending or distortion may occur in portions of the metal tubes which are not supported while passing through the firing chamber 130. Thus, in the enamel coating method according to an embodiment of the present invention, the preprocessing process, the coating process, and the firing process are performed by connecting the rear end portion of the corresponding metal tube with another metal tube 10 before the rear end portions of the metal tubes 10 are fed into the preprocessing chamber 110, thereby minimizing occurrence of the bending or distortion.
The connection between the metal tubes 10 may be automatically or manually performed using various connection members which are known in the art. In the enamel coating method according to an embodiment of the present invention, rotational force and advancing power of the metal tube are transmitted through the above-described connection member, and therefore a connection member capable of achieving a strong bond between the metal tubes is preferably used.
In addition, according to the enamel coating method according to an embodiment of the present invention, in order to more completely prevent distortion of the metal tube 10 in the firing process, a firing chamber conveyor 600 for supporting, rotating, and advancing the metal tube 10 is further provided as shown in
As shown in
The transport roller 270 is a rod with a circular cross-section, and has a tapered shape in which a diameter of the transport roller 270 is gradually increased toward both end portions thereof from a central portion thereof.
When such a transport roller 270 is provided on the axis forming the angle of 5° to 35° clockwise or counterclockwise with the lateral line perpendicular to the longitudinal direction of the firing chamber conveyor 600 and is rotated by directly or indirectly supplied power, the transport roller 270 simultaneously rotates and advances the metal tube 10 placed thereon. The distorted angle of the axis of the transport roller 270 serves to determine the number of rotations of the metal tube 30. The number of rotations of the metal tube in the enamel coating method according to an embodiment of the present invention is, for example, 2 to 10 per minute, preferably 5 to 9 per minute, and the distorted angle of the axis of the transport roller 270 may be adjusted based on the number of rotations of the metal tube.
As the configuration of the firing chamber conveyor 600 except for the transport roller 270, a configuration typically used in the related art may be adopted. The power transmission by the transport roller 270 may be performed by a method typically used in the related art.
The material of the transport roller 270 is not limited as long as it can withstand a high temperature (750 to 1,000° C.), and a metal is preferably used as the material of the transport roller 270.
The firing process of the metal tube is performed at the high temperature, and therefore the firing chamber conveyor 600 provided in the firing chamber 130 should have excellent heat resistance. In particular, the transport roller 270 is brought into direct contact with the metal tube heated to the high temperature, and therefore should have heat resistance. However, materials having heat resistance capable of withstanding the temperature 750 to 1,000° C. are uncommon and expensive, and therefore in the enamel coating method according to an embodiment of the present invention, a method of cooling the transport roller 270 using a cooling solvent has been suggested.
That is, the transport roller 270 included in the firing chamber conveyor 600 in the enamel coating method according to an embodiment of the present invention includes a cooling liquid circulation path 271 that passes through a rotating shaft as shown in
The firing chamber conveyor 600 transports the metal tube to an out-feed conveyor 300 while rotating and advancing the metal tube 10 while supporting the lower portion of the heated metal tube by the transport roller 270.
That is, the firing process of the metal tube in the (c) firing is performed at the high temperature of 750 to 1,000° C. Thus, when the metal tubes 10 are connected with each other so that front and rear ends of the metal tubes are not mutually supported, bending or distortion may occur in portions of the metal tubes which are not supported while passing through the firing chamber 130. Thus, in the related art, the preprocessing process, the coating process, and the firing process were performed by connecting the corresponding metal tube with another metal tube 10 before the rear end portion of the metal tube 10 was fed into the preprocessing chamber 110. However, when the rear end portion of the corresponding metal tube 10 is connected with the front end portion of another metal tube 10 as described above, there is a disadvantage of requiring manpower capable of handling this. In addition, when the metal tubes are heated to the high temperature (750 to 1,000° C.) in the firing chamber 130 even in a state in which the metal tubes are connected with each other to be mutually supported, bending or distortion may commonly occur in the metal tube. Thus, the present invention has been suggested to solve these problems.
As described above, when the firing chamber conveyor 600 is provided in the firing chamber 130, bending or distortion of the metal tube does not occur in the firing process even without connecting the metal tubes 10 with each other, or even when the metal tubes 10 are connected with each other, the same effect may be achieved.
In the enamel coating method according to an embodiment of the present invention, the continued rotation and advancing of the metal tube 10 may be performed by a motor 220 provided in the in-feed conveyor 200 and/or the out-feed conveyor 300 and several pairs of rotation rollers 230 forming an alternate angle so that the metal tube advances while being rotated by the power received from the motor 220.
In addition, as shown in
When the above-described transport roller 270 is used in the conveyor, the roller is simplified, and therefore simplification of the entire apparatus may be achieved.
The number of rotations of the metal tube in the enamel coating method according to an embodiment of the present invention is, for example, 2 to 10 per minute, and preferably 5 to 9 per minute. The number of rotations of the metal tube may be adjusted by adjusting the alternate angle of the rotation roller (230 of
In the enamel coating method according to an embodiment of the present invention, when the in-feed conveyor 200 and the out-feed conveyor 300 are used as shown in
Meanwhile, when each of the metal tubes 10 is individually coated without performing the preprocessing process, the coating process, and the firing process by connecting the rear end portion of the corresponding metal tube 10 with another metal tube 10 before the metal tube 10 is fed into the preprocessing chamber 110, at least one of the preprocessing chamber conveyor 400, the coating chamber conveyor 500, and the firing chamber conveyor 600 may be required in order for each of the metal tubes 10 to have rotational force and advancing power in the preprocessing process, the coating process, and the firing process.
Meanwhile, according to an embodiment of the present invention, when the coating object is the manhole cover, the configuration for the rotation of the metal tube in the above descriptions is not applied. In particular, the transport roller 270 may be replaced with a cylindrical roller, and cooling of the cylindrical roller using a cooling liquid may be applied in the same manner as above.
In the related art, the firing chamber capable of receiving the metal tube is required for enamel coating of the metal tube, however, in an enamel coating apparatus according to an embodiment of the present invention, enamel coating may be easily performed with respect to even a long metal tube in the coating unit including the compact firing chamber. Thus, in the enamel coating method according to an embodiment of the present invention, when the length of the metal tube is 5 m or more, a greater economical advantage may be achieved than in the related art. For example, when coating is performed in the conventional method in a case in which a length of a pin tube for heat exchanger used in a generator is 18 m, the firing chamber having a space of 18 m or more is required, whereby uneconomical results are obtained in terms of energy efficiency and use of space. However, according to an embodiment of the present invention, the firing process may be easily and economically performed in the compact firing chamber (the overall length being approximately 4 m or less).
Hereinafter, the enamel coating apparatus according to an embodiment of the present invention will be described in detail with reference to
The enamel coating apparatus according to an embodiment of the present invention includes the preprocessing chamber 110 that preprocesses the surface of the coating object 10 that is fed from the in-feed conveyor 200 while being rotated, the coating chamber 120 that coats the surface of the coating object 10 with an enamel glaze supplied from the enamel glaze supply nozzle 121 provided therein when the preprocessed coating object 10 is fed, and the coating unit 100 that includes the firing chamber 130 performing firing when the coated coating object 10 is fed.
The induction heater 131 is provided in the firing chamber 130, and heats the coated coating object 10 to a temperature of 750 to 1,000° C.
In addition, the firing chamber conveyor 600 for transporting the heated metal tube 10 to the out-feed conveyor 300 while supporting the lower portion of the metal tube 10 is provided in the firing chamber 130, and includes at least two transport rollers 270.
All technical features described in the enamel coating method may be applied to the enamel coating apparatus, and repeated description thereof will be omitted.
The coating unit 100 is preferably provided in such a manner that the overall length of the metal tube is 5 m or less in a direction in which the metal tube is fed.
In the enamel coating apparatus, the preprocessing chamber 110 of the coating unit 100 is provided to have an overall length of 3 m or less, preferably 1 m or less in the direction in which the metal tube 10 is fed, the coating chamber 120 is provided to have an overall length of 2 m or less, preferably 1 m or less, and the firing chamber 130 is provided to have an overall length of 7 m or less, preferably 5 m or less, whereby miniaturization of the coating unit 100 may be achieved.
When the coating object 10 is the metal tube, the enamel coating apparatus according to an embodiment of the present invention further includes the in-feed conveyor 200 that feeds the metal tube 10 into the preprocessing chamber 110 by allowing the metal tube 10 to be rotated and advance, and the out-feed conveyor 300 that feeds the coated metal tube 10 out of the firing chamber 130.
In this instance, as shown in
In addition, the above-described configuration may be applied to the out-feed conveyor 300. In the out-feed conveyor 300, the coated metal tube 11 is transported from the metal tube loading unit 250 to the metal tube carrying unit 240.
When the coating object 10 is the manhole cover, the manhole cover advances by the in-feed conveyor 200 to be fed into the preprocessing chamber 110, and the fired manhole cover is separated from the firing chamber 130 by the out-feed conveyor 300, whereby enamel coating may be performed. In this case, the conveyor may be provided even in the coating unit 100.
As described above, according to the embodiments of the present invention, the induction heating method is adopted in the firing chamber, so that the surface of the coating object may be heated to the temperature of 750 to 1,000° C. within a significantly short period of time (within approximately two minutes), whereby the firing chamber may be miniaturized, and the whole surface of the coating object may be heated to the uniform temperature. As a result, even in a case of the metal tube (for example, metal pin tube) having severe irregularities formed thereon or the manhole cover, the coating defects may be minimized, whereby enamel coating having excellent durability may be applied to the whole coating object.
In particular, the coating object is first heated and then the heat is transmitted to the enamel glaze, rather than that the heat being transmitted to the coating object through the enamel glaze applied to the surface of the coating object at the time of firing, and therefore the coating defects may be minimized and the enamel glaze may be more uniformly and firmly bonded to the surface of the coating object to perform coating with excellent durability.
For example, when the heat is transmitted to the coating object through the enamel glaze, the enamel glaze is first heated to flow down in the direction of gravity before the coating object is heated, whereby the enamel glaze may receive the heat from the coating object to be immediately bonded to the surface of the coating object when the coating object is first heated according to an embodiment of the present invention, and therefore the coating defects may be significantly reduced and uniform and firm coating may be performed.
In addition, bending or distortion which commonly occurs in the long metal tube in the high-temperature firing process may be prevented, thereby providing the enamel coating metal tube having excellent quality.
In addition, the firing chamber conveyor is adopted, and therefore the firing may be performed without connecting the metal tubes with each other as in the conventional method in which the firing is performed by connecting the rear end portion of the corresponding metal tube with another metal tube before the metal tube is fed into the preprocessing chamber. As a result, the coating process may be simplified to improve the production efficiency of the enamel-coated metal tube.
In addition, when using the transport roller having the tapered shape in which the diameter of the transport roller is gradually increased toward both end portions thereof from the central portion thereof in place of a pair of rotation rollers, the equipment of the coating apparatus may be simplified.
It will be apparent to those skilled in the art that various modifications can be made to the above-described exemplary embodiments of the present invention without departing from the spirit or scope of the invention. Thus, it is intended that the present invention covers all such modifications provided they come within the scope of the appended claims and their equivalents.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4182782 | Scheiber | Jan 1980 | A |
| 5026451 | Trzecieski | Jun 1991 | A |
| 5207833 | Hart | May 1993 | A |
| 5585143 | Scharf | Dec 1996 | A |
| 20110248072 | Leiden | Oct 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 202461342 | Oct 2012 | CN |
| 20110010571 | Nov 2011 | KR |
| Number | Date | Country | |
|---|---|---|---|
| 20150354065 A1 | Dec 2015 | US |