Coatings comprising an organosilane solution polymer and a crosslink functional dispersed polymer

BACKGROUND OF THE INVENTION
This invention is directed to a coating composition useful for providing a finish on a variety of substrates. In particular, this invention is directed to an organosilane composition which may be used for finishing automobiles and trucks.
It is well known that consumers prefer automobiles and trucks with an exterior finish having an attractive aesthetic appearance, including high gloss and excellent DOI (distinctness of image). While ever more aesthetically attractive finishes have been obtained, deterioration of the finish over time, whereby the exterior finish of an automobile or truck loses its luster or other aspects of its aesthetic appearance, may be all the more noticeable. An increasingly observed cause of this deterioration of the finish is etching of the finish caused by exposure to environmental chemical attack. Chemicals that may cause etching of a finish include pollutants such as acid rain and chemical smog.
In order to protect and preserve the aesthetic qualities of the finish on a vehicle, it is generally known to provide a clear (unpigmented) topcoat over a colored (pigmented) basecoat, so that the basecoat remains unaffected even on prolonged exposure to the environment or weathering. It is also generally known that alkoxysilane polymers, due to strong silane bonding when cured, exhibit excellent chemical resistance. Exemplary of prior art patents disclosing silane polymers for coating are U.S. Pat. Nos. 4,368,297; 4,518,726; 4,049,954, and Japanese Kokai 57-12058.
However, to applicants, knowledge, none of the previously disclosed alkoxysilane compositions for finishing automobiles or trucks have ever been placed into commercial use. It is believed that heretofore known or patented alkoxysilane coatings suffer from certain unsolved problems or deficiencies. In particular, previously disclosed alkoxysilane coatings have a strong tendency to cracking. Such cracking may result from either stress or degradation from ultraviolent radiation. Such cracking could seriously and adversely affect long term durability and weatherability.
There is a need for a commercially practical clearcoat finish having excellent appearance, including high gloss and DOI, that is also resistant to etching caused by chemical attack. To be commercially practical, such a clearcoat must not be prone to cracking. It is also desirable that such a clearcoat should be capable of being applied over a variety of basecoats and have excellent adhesion.
SUMMARY OF THE INVENTION
The invention is directed to a coating composition useful for finishing the exterior of automobiles and trucks and other substrates. The composition comprises:
(a) from about 20 to 90% by weight, based on the weight of the binder solids, of a film-forming organosilane polymer having a weight average molecular weight of about 500-30,000 comprising
(i) from about 30 to 95% by weight, based on the weight of the organosilane polymer, of ethylenically unsaturated monomers which do not contain a silane functionality and about 3 to 70% by weight ethylenically unsaturated monomers which contain a silane functionality; and
(b) from about 10 to 60%, based on the weight of the binder solids, of particles of a non-aqueous dispersed polymer comprising:
(i) a macromolecular core having a weight average molecular weight of about 50,000 to 500,000; and
(ii) attached to the macromolecular core, a plurality of macromonomer chains having a weight average molecular weight of about 1,000 to 30,0000, comprising 5 to 30% by weight, based on the weight of the macromonomer, of polymerized ethylenically unsaturated monomers which comprise a functionality, the same or different, selected from the group consisting of an epoxide, anhydride, isocyanate, silane, acid, hydroxy, amide or combinations thereof; and about 70 to 95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without a crosslink functionality; and
(c) from about 25 to 50% by weight, based on the weight of the composition, of a liquid organic carrier;
such that when the composition is applied to a substrate, covalent bonding between crosslinking functionalities in said non-aqueous dispersion polymer and silane functionalities in said organosilane polymer reduces the tendency of the coating so produced to exhibit cracking.
Optionally, the composition may further comprise one or more non-silane containing film-forming solution polymers, preferably about 0 to 30%, more preferably about 0 to 20% by weight, based on the weight of binder solids of the composition.
The invention also includes a process for coating a substrate with the above coating composition. The claimed invention further includes a substrate having adhered thereto a coating according to the above composition.
The composition of the present invention is especially useful for forming a clear topcoat over a pigmented basecoat. Such a clear topcoat can be applied over a variety of colorcoats, such as water or organic solvent based colorcoats or powder colorcoats.

DETAILED DESCRIPTION OF THE INVENTION
This invention provides a coating composition useful for finishing the exterior of automobile and truck bodies. Depending on its use, the present composition is capable of providing a coating which is durable, has excellent adhesion to basecoats, does not crack, does not deteriorate in terms of transparency under prolonged exposure to weather conditions, and imparts a superior glossy appearance for an extended period. Also, the coating composition offers a significant improvement over conventionally used coating compositions in terms of resistance to etching caused by environmental chemical attack.
A typical automobile steel panel or substrate has several layers of coatings. The substrate is typically first coated with an inorganic rust-proofing zinc or iron phosphate layer over which is provided a primer which can be an electrocoated primer or a repair primer. A typical electrocoated primer comprises a cathodically deposited epoxy modified resin. A typical repair primer comprises an alkyd resin. Optionally, a primer surfacer can be applied over the primer coating to provide for better appearance and/or improved adhesion of the basecoat to the primer coat. A pigmented basecoat or colorcoat is next applied over the primer surfacer. A typical basecoat comprises a pigment, which may include metallic flakes in the case of a metallic finish, and polyester or acrylourethane as a film-forming binder. A clear topcoat (clearcoat) is then applied to the pigmented basecoat (colorcoat). The colorcoat and clearcoat are preferably deposited to have thicknesses of about 0.1-2.5 mils and 1.0-3.0 mils, respectively. A composition according to the present invention, depending on the presence of pigments or other conventional components, may be used as a basecoat, clearcoat, or primer. However, a particularly preferred composition is useful as a clear topcoat to prevent environmental chemical attack to the entire finish. A clearcoat composition of the present invention may be applied over a basecoat composition of the present invention.
The film-forming portion of the present coating composition, comprising polymeric components, is referred to as the "binder" or "binder solids" and is dissolved, emulsified or otherwise dispersed in an organic solvent or liquid carrier. The binder solids generally include all the normally solid polymeric non-liquid components of the total composition. Generally, catalysts, pigments, and non-polymeric chemical additives such as stabilizers are not considered part of the binder solids. Non-binder solids other than pigments usually do not amount to more than about 5% by weight of the composition. In this disclosure, the term binder includes the organosilane polymer, the dispersed polymer, and all other optional film-forming polymers.
The applied coating composition suitably contains about 50-75% by weight of the binder and about 25-50% by weight of the organic solvent carrier. The binder of the coating composition contains about 20-90%, preferably 40-80%, by weight of a film-forming silane containing polymer, hereafter also referred to as the silane polymer.
The silane polymer portion of the binder has a weight average molecular weight of about 1000-30,000, a number average molecular weight of about 500-10,000. All molecular weights disclosed herein are determined by gel permeation chromatography using a polystyrene standard.
The silane polymer is the polymerization product of about 30-95%, preferably 40-60%, by weight ethylenically unsaturated non-silane containing monomers and about 5-70%, preferably 40-60% by weight ethylenically unsaturated silane containing monomers, based on the weight of the organosilane polymer. Suitable ethylenically unsaturated non-silane containing monomers are alkyl acrylates, alkyl methacrylates and any mixtures thereof, where the alkyl groups have 1-12 carbon atoms, preferably 3-8 carbon atoms.
Suitable alkyl methacrylate monomers used to form the organosilane polymer are methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, isobutyl methacrylate, pentyl methacrylate, hexyl methacrylate, octyl methacrylate, nonyl methacrylate, lauryl methacrylate and the like. Similarly, suitable alkyl acrylate momomers include methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, isobutyl acrylate, pentyl acrylate, hexyl acrylate, octyl acrylate, nonyl acrylate, lauryl acrylate and the like. Cycloaliphatic methacrylates and acrylates also can be used, for example, such as trimethylcyclohlexyl methacrylate, trimethylcyclohexl acrylate, iso-butyl methacrylate, t-butyl cyclohexyl acrylate, or t-butyl cyclohexyl methacrylate. Aryl acrylate and aryl methacrylates also can be used, for example, such as benzyl acrylate and benzyl methacrylate. Of course, mixtures of the two or more of the above mentioned monomers are also suitable.
In addition to alkyl acrylates or methacrylates, other non-silane containing polymerizable monomers, up to about 50% by weight of the polymer, can be used in the acrylosilane polymer for the purpose of achieving the desired properties such as hardness, appearance, mar resistance, and the like. Exemplary of such other monomers are styrene, methyl styrene, acrylamide, acrylonitrile, methacrylonitrile, and the like. Styrene can be used in the range of 0-50% by weight.
A suitable silane containing monomer useful in forming the acrylosilane polymer is an alkoxysilane having the following structural formula: ##STR1## wherein R is either CH.sub.3, CH.sub.3 CH.sub.2, CH.sub.3 O, or CH.sub.3 CH.sub.2 O; R.sub.1 and R.sub.2 are CH.sub.3 or CH.sub.3 CH.sub.2 ; and R.sub.3 is either H, CH.sub.3, or CH.sub.3 CH.sub.2 ; and n is 0 or a positive integer from 1 to 10. Preferably, R is CH.sub.3 O or CH.sub.3 CH.sub.2 O and n is 1.
Typical examples of such alkoxysilanes are the acrylatoalkoxy silanes, such as gamma-acryloxypropyltrimethoxy silane and the methacrylatoalkoxy silanes, such as gamma-methacryloxypropyltrimethoxy silane, and gamma-methacryloxypropyltris(2-methoxyethoxy) silane.
Other suitable alkoxy silane monomers have the following structural formula: ##STR2## wherein R, R.sub.1 and R.sub.2 are as described above and n is a positive integer from 1 to 10.
Examples of such alkoxysilanes are the vinylalkoxy silanes, such as vinyl trimethoxy silane, vinyl triethoxy silane and vinyl tris(2-methoxyethoxy)silane.
Other suitable silane containing monomers are ethylenically unsaturated acyloxysilanes, including acrylatoxy silane, methacrylatoxy silane and vinylacetoxy silanes, such as vinylmethyldiacetoxy silane, acrylatopropyl triacetoxy silane, and methacrylatopropyltriacetoxy silane. Of course, mixtures of the above-mentioned silane containing monomers are also suitable.
Consistent with the above mentioned components of the silane polymer, an example of an organosilane polymer useful in the coating composition of this invention may contain the following constituents: about 15-25% by weight styrene, about 30-60% by weight methacryloxypropyltrimethoxy silane, and about 25-50% by weight trimethylcyclohexyl methacrylate.
One preferred acrylosilane polymer contains about 30% by weight styrene, about 50% by weight methacryloxypropyl trimethoxy silane, and about 20% by weight of nonfunctional acrylates or methacrylates such as trimethylcyclohexyl methacrylate, butyl acrylate, and iso-butyl methacrylate and any mixtures thereof.
Silane functional macromonomers also can be used in forming the silane polymer. These macromonomers are the reaction product of a silane containing compound, having a reactive group such as epoxide or isocyanate, with an ethylenically unsaturated non-silane containing monomer having a reactive group, typically a hydroxyl or an epoxide group, that is co-reactive with the silane monomer. An example of a useful macromonomer is the reaction product of a hydroxy functional ethylenically unsaturated monomer such as a hydroxyalkyl acrylate or methacrylate having 1-4 carbon atoms in the alkyl group and an isocyanatoalkyl alkoxysilane such as isocyanatopropyl triethoxysilane.
Typical of such above mentioned silane functional macromonomers are those having the following structural formula: ##STR3## wherein R, R.sub.1, and R.sub.2 are as described above; R.sub.4 is H or CH.sub.3, R.sub.5 is an alkylene group having 1-8 carbon atoms and n is a positive integer from 1-8.
Additional to the organosilane polymer, other film-forming and/or crosslinking solution polymers may be included in the present application. Examples include conventionally known acrylics, cellulosics, aminoplasts, urethanes, polyesters, epoxides or mixtures thereof. One preferred optional film-forming polymer is a polyol, for example an acrylic polyol solution polymer of polymerized monomers. Such monomers may include any of the aforementioned alkyl acrylates and/or methacrylates and, in addition, hydroxy alkyl acrylates or methacrylates. The polyol polymer preferably has a hydroxyl number of about 50-200 and a weight average molecular weight of about 1,000-200,000 and preferably about 1,000-20,000.
To provide the hydroxy functionality in the polyol, up to about 90% by weight, preferably 20 to 50%, of the polyol comprises hydroxy functional polymerized monomers. Suitable monomers include hydroxy alkyl acrylates and methacrylates, for example, hydroxy ethyl acrylate, hydroxy propyl acrylate, hydroxy isopropyl acrylate, hydroxy butyl acrylate, hydroxy ethyl methacrylate, hydroxy propyl methacrylate, hydroxy isopropyl methacrylate, hydroxy butyl methacrylate, and the like, and mixtures thereof.
Other polymerizable non-hydroxy containing monomers may be included in the polyol polymer, in an amount up to about 90% by weight, preferably 50 to 80%. Such polymerizable monomers include, for example, styrene, methylstyrene, acrylamide, acrylonitrile, methacrylonitrile, methacrylamide, methylol methacrylamide, methylol acrylamide, and the like, and mixtures thereof.
One example of an acrylic polyol polymer comprises about 10-20% by weight of styrene, 40-60% by weight of alkyl methacrylate or acrylate having 1-6 carbon atoms in the alkyl group, and 10-50% by weight of hydroxy alkyl acrylate or methacrylate having 1-4 carbon atoms in the alkyl group. One such polymer contains about 15% by weight styrene, about 29% by weight iso-butyl methacrylate, about 20% by weight 2-ethylhexyl acrylate, and about 36% by weight hydroxy propylacrylate.
A key component of the coating composition of the present invention is, in addition to the above polymeric components, a dispersed polymer. Polymers dispersed in an organic (substantially non-aqueous) medium have been variously referred to, in the art, as a non-aqueous dispersion (NAD) polymer, a microgel, a non-aqueous latex, or a polymer colloid. See generally, Poehlin et al., editor, SCIENCE AND TECHNOLOGY OF POLYMER COLLOIDS, Volume 1, pages 40-50 (1983); El-Asser, editor, FUTURE DIRECTIONS IN POLYMER COLLOIDS, pages 191-227 (1987); Barrett, DISPERSION POLYMERIZATION IN ORGANIC MEDIA (John Wiley 1975). See also U.S. Pat. Nos. 4,147,688; 4,180,489; 4,075,141; 4,415, 681; and 4,591,533, hereby incorporated by reference. Microgel particles, necessarily cross-linked, have been used for years as impact modifiers for plastics, as rheology controllers for coatings, and in basecoats, to permit wet-on-wet application of paints.
In general, the dispersed polymer of the present invention is characterized as a polymer particle dispersed in an organic media, which particle is stabilized by what is known as steric stabilization. According to the prior art, steric stabilization is accomplished by the attachment, commonly by adsorption, of a solvated polymeric or oligomeric layer at the particle medium interface. The problem of providing a steric barrier has been considered in two parts: first, the selection of the soluble polymer which comprises the solvate sheath surrounding each particle and, secondly, the method of attaching or anchoring this polymer to the particle surface. The most widely known type of stabilizer used in dispersed polymers had been based on block or graft copolymers, one component of which is the soluble stabilizing portion and the other portion, often termed the anchor, is insoluble in the continuous phase and is adsorbed on or is absorbed into the disperse phase. It is also known that to increase the stability of the a dispersed polymer, particularly to strong solvents, or to ensure that the stabilizer is not desorbed or displaced, the anchor group may be covalently linked to the particle. This has been achieved by incorporating into the anchor group a reactive group, for example a glycidal group which can react with a complementary group in the dispersed polymer, for example a carboxylic acid.
In the dispersed polymers of the present composition, the dispersed phase or particle, sheathed by a steric barrier, will be referred to as the "macromolecular polymer" or "core." The stabilizer forming the steric barrier, attached to this core, will be referred to as the "macromonomer chains" or "arms."
The dispersed polymers of the present invention solve the problem of cracking heretofor associated with silane coatings. These dispersed polymers, to reduce cracking to the desired minimum, must be used in higher amounts than dispersed polymers are typically used for other purposes. For example, while microgels have been used in basecoats for flow control at levels of not more than about 5%, the present dispersed polymers are used in an amount varying from about 10 to 60% by weight, preferably about 15 to 40%, more preferably about 20 to 30%, of the total solids binder in the composition. The ratio of the silane polymer component of the composition suitably ranges from 5:1 to 1:2, preferably 4:1 to 1:1. These relatively high concentrations of dispersed polymers, in the present composition, is made possible by the presence of reactive groups on the arms of the dispersed polymer, which reactive groups make the polymers compatible with the continuous phase of the system.
The dispersed polymer contains about 10-90% by weight, preferably 50-80%, based on the weight of the dispersed polymer, of a high molecular weight core having a weight average molecular weight of about 50,000-500,000. The preferred average particle size is 0.1 to 0.5 microns. The arms, attached to the core, make up about 90-10% by weight, preferably 20-50%, of the dispersed polymer, and have a weight average molecular weight of about 1,000-30,000, preferably 1000-10,000.
Preferably, the macromolecular core of the dispersed polymer is comprised of polymerized ethylenically unsaturated monomers. Suitable monomers include styrene, alkyl acrylate or methacrylate, ethylenically unsaturated monocarboxylic acid, and/or silane containing monomers. Such monomers as methyl methacrylate contribute to a high Tg (transition glass temperature) dispersed polymer, whereas such "softening" monomers as butyl acrylate or 2-ethylhexylacrylate contribute to a low Tg dispersed polymer. Other optional monomers are hydroxyalkyl acrylates or methacrylates or acrylonitrile. It is noted that such functional groups as hydroxy can react with silane groups in the organosilane polymer to produce more bonding in the composition. If the core is crosslinked, allyl acrylate or allyl methacrylate, which crosslink with each other, can be used or an epoxy functional monomer such as glycidyl acrylate or methacrylate can be used, which can react with a monocarboxylic acid functional ethylenically unsaturated monomer to crosslink the core.
Preferably, there is silane functionality, for crosslinking purposes, in the core, which functionality may be provided by a small amount of one or more of the silane containing monomers mentioned above with respect to the film forming organosilane polymer. Suitably, the silane functionality is the primary or major means, preferably the sole means, of crosslinking in the core. Suitably about 2 to 10%, preferably about less than 5% of the monomers making up the macromolecular core are silane monomers capable of crosslinking between themselves. Thus, crosslinking occurs by siloxane bonding (--Si--O--Si--). This silane crosslinking enables the core to behave as a non-crosslinked polymer before cure for good flow during application, resulting in improved appearance. The core can crosslink during and after curing, upon exposure to humidity and heat during curing and/or exposure to humidity in the environment after curing. A further advantage of silane being present in the core is that the cured film does not blush when exposed to humidity, which blushing was found to occur without the presence of silane. If the case is pre-crosslinked (before curing) by other means, such as acid/epoxy or diacrylates, then humidity sensitivity may be eliminated but the system may have poor flow and appearance.
The reason that the dispersed polymer in the present coating composition eliminates the cracking problem which silane-containing film forming polymers are otherwise prone is not known for certain. Although not wishing to be bound by theory, one hypothesis is that the dispersed polymer provides high density, high molecular weight reinforcement, which reinforcement is integrated with the matrix of the film coating. This enables the coating to better withstand stress and/or U.V. degradation. Another hypothesis is that the dispersed polymer is that the dispersed polymer, with its macromolecular coil or core, provides a certain amount of sponginess and flexibilty to the coating, that is, the macromolecular core may be able to contract and expand, especially with low volatile organic content. This so-called sponginess may compensate to some extent for the points, or concentrated areas, of silane bonding. Silane bonding tends to become tightly bound, since each silane moiety or group potentially can be crosslinked at three sites and a number of silane moieties can become extended in a silane matrix. Without the dispersed polymer, an overconcentration of silane crosslinking may result in stress cracking.
As mentioned above, it is preferred that the macromolecular core of the dispersed polymer has a low amount of crosslinking within the macromolecular core and, most preferably, the core has zero pre-crosslinking. This means there is no crosslinking in solution, before the composition is cured or baked. The more the core is crosslinked, the less its sponginess. Also, without crosslinking, the macromolecular core is capable of uncoiling to some extent and therefore has a better tendency to flow, an advantage in spray appplication of the coating composition. Some degree of crosslinking may be desirable, for example, in order to derive the macromolecular core polymer from shorter chains. However, in general, the greater the crosslinking, the more tightly bound together the polymer and the less its ability to prevent cracking of the coating. Because limited or no pre-crosslinking in the macromolecular core of the dispersed polymer is desired, dispersed polymers which are highly crosslinked, such as structured Star polymers, with reactive arms, while useful to some extent may be less preferred. Star Polymers, such as disclosed in U.S. Pat. No. 4,810,756 to Spinnelli, but which have relatively highly crosslinked cores, relatively small in size, compared to the preferred dispersed polymers.
A distinctive feature of the dispersed polymers of the present invention is the presence of macromonomer arms which are reactive, that is these arms have numerous reactive groups, referred to a "crosslinking functionalities," which are adapted to react with the organosilane polymer of the present composition. It is not known with certainty what portion of the these functional groups do, in fact, react with the organosilane polymer, because of the numerous and complicated sets of reactions which may occur during baking and curing of the composition, especially if additional film-forming binders are present. However, it may be said that a substantial portion of these functionalities in the arms, preferably the majority thereof, do in actuality react and crosslink with the film-former of the composition, which in some cases may exclusively consist of an organosilane polymer. Of course, if additional film-forming polymers are present, for example, a polyol, then the arms may react with film-formers other than the organosilane polymer. Suitably, about 3 to 30% of the monomers which make up the macromonomer arms have reactive crosslinking functional groups. Preferably about 10 to 20% of the monomers have such reactive groups. Dispersed polymers having reactive arms have been disclosed in U.S. Pat. No. 4,591,533 to Antonelli et al.
The arms of the dispersed polymer, should be anchored securely to the macromolecular core. For this reason, the arms preferably are anchored by covalent bonds. The anchoring must be sufficient to hold the arms to the dispersed polymer after they react with the film-former polymer. For this reason, the conventional method of anchoring by adsorption of the backbone portion of a graft polymer may provide insufficient anchoring.
As indicated above, the arms or macromonomers of the dispersed polymer serve to prevent the core from flocculating by forming what is referred to in the art as a steric barrier. The arms, typically in contrast to the macromolecular core, are believed capable, at least temporarily, of being solvated in the organic solvent carrier or media of the composition. They may therefore be in a chain-extended configuration and their crosslinking functional groups are therefore relatively readily available to reaction with the silane groups of the film forming silane containing polymer. Such arms suitably comprise about 3 to 30% by weight, preferably 10 to 20%, based on the weight of macromonomer, of polymerized ethylenically unsaturated hydroxy, epoxide, silane, acid, anhydride, isocyanate, amide, or other crosslinking functionality containing monomers, or combinations thereof, and about 70-95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without such crosslinking functionality. Preferably the crosslinking functionality is a hydroxy, silane or epoxy containing monomer, since such reactive groups can be utilized in one package systems. When the crosslinking functionality is an acid, anhydride, or isocyanate, then a two package system, with the dispersed polymer in a first package and the organosilane in a second package, is generally required. Combinations of the above-mentioned crosslinking functional groups are also suitable, although it is noted that hydroxy and silane groups have limited compatibility and are preferably not on the same macromonomer chain.
As an example, the macromonomer arms attached to the core may contain polymerized monomers of alkyl methacrylate, alkyl acrylate, each having 1-12 carbon atoms in the alkyl group, as well as glycidyl acrylate or glycidyl methacrylate or ethylenically unsaturated monocarboxylic acid containing monomers for anchoring and/or crosslinking. Typically useful hydroxy containing monomers are hydroxy alkyl acrylates or methacrylates as described above.
A preferred composition for a dispersed polymer that has hydroxy functionality comprises a core consisting of about 25% by weight hydroxy ethyl acrylate, about 4% by weight methacrylic acid, about 46.5% by weight methyl methacrylate, about 18% by weight methyl acrylate, about 1.5% by weight glycidyl methacrylate and about 5% styrene. The macromonomer attached to the core contains 97.3% by weight prepolymer and about 2.7% by weight glycidyl methacrylate, the latter for crosslinking or anchoring. A preferred prepolymer contains about 28% by weight butyl methacrylate, about 15% by weight ethyl methacrylate, about 30% by weight butyl acrylate, about 10% by weight hydroxyethyl acrylate, about 2% by weight acrylic acid, and about 15% by weight styrene.
The dispersed polymer may be produced by conventionally known procedures. For example, it has been disclosed that such polymers may be produced by a process of dispersion free radical polymerization of monomers, in an organic solvent, in the presence of a steric stabilizer for the particles. The procedure has been described as basically one of polymerizing the monomers in an inert solvent in which the monomers are soluble but the resulting polymer is not soluble, in the presence of a dissolved amphiteric stabilizing agent. Such procedures have been extensively disclosed in both the patent and non-patent literature, for example, see the above cited references regarding dispersed polymers in general, or U.S. Pat. No. 4,220,679 and PAINT AND SURFACE COATING: THEORY AND PRACTICE, ed. R. Lambourne (Ellis Horwood Limited 1987). As illustrated in the examples below, the macromonomer arms can be prepared by cobalt catalyzed special chain transfer (SCT) polymerization, group transfer polymerization (GTP), or free radical polymerization.
Optionally, the present coating composition may optionally further include, particularly in conjunction with an optional polyol polymer, an additional crosslinking agent, for example conventionally known monomeric or polymeric alkylated melamine formaldehyde resin that is partially or fully alkylated. One preferred crosslinking agent is a methylated and butylated or isobutylated melamine formaldehyde resin that has a degree of polymerization of about 1-3. Generally, this melamine formaldehyde resin contains about 50% butylated groups or isobutylated groups and 50% methylated groups. Such crosslinking agents typically have a number average molecular weight of about 300-600 and a weight average molecular weight of about 500-1500. Examples of commercially available resins are "Cymel" 1168, "Cymel" 1161, "Cymel" 1158, "Resimine" 4514 and "Resimine" 354. Preferably, the crosslinking agent is used in the amount of about 5-50% by weight, based on the weight of the binder of the composition. Other crosslinking agents are urea formaldehyde, benzoquanamine formaldeyde and blocked polyisocyanates.
A catalyst is typically added to catalyze the crosslinking of the silane moieties of the silane polymer with itself and with other components of the composition, including the dispersed polymer. Typical of such catalysts are dibutyl tin dilaurate, dibutyl tin diacetate, dibutyl tin dioxide, dibutyl tin dioctoate, tin octoate, aluminum titanate, aluminum chelates, zirconium chelate and the like. Tertiary amines and acids or combinations thereof are also useful for catalyzing silane bonding. Preferably, these catalysts are used in the amount of about 0.1 to 5.0% by weight of the composition.
In addition, the coating composition may include a structured polymer, a STAR polymer, or a solvent reversible polymer (SRP).
To improve weatherability of a clear finish produced by the present coating composition, an ultraviolet light stabilizer or a combination of ultraviolet light stabilizers can be added in the amount of about 0.1-5% by weight, based on the weight of the binder. Such stabilizers include ultraviolet light absorbers, screeners, quenchers, and specific hindered amine light stabilizers. Also, an anitoxidant can be added, in the about 0.1-5% by weight, based on the weight of the binder.
Typical ultraviolet light stabilizers that are useful include benzophenones, triazoles, triazines, benzoates, hindered amines and mixtures thereof. Specific examples of ultraviolet stabilizers are disclosed in U.S. Pat. No. 4,591,533, the entire disclosure of which is incorporated herein by reference.
The composition may also include other conventional formulation additives such as flow control agents, for example, such as Resiflow.RTM. S (polybutylacrylate), BYK 320 and 325 (high molecular weight polyacrylates); rheology control agents, such as fumed silica; water scavengers such as tetrasilicate, trimethyl orthoformate, triethyl orthoformate and the like.
When the present composition is used as a clearcoat (topcoat) over a pigmented colorcoat (basecoat) to provide a colorcoat/clearcoat finish, small amounts of pigment can be added to the clear coat to eliminate undesirable color in the finish such as yellowing.
The present composition also can be pigmented and used as the colorcoat, or as a monocoat or even as a primer or primer surfacer. The composition has excellent adhesion to a variety of substrates, such as previously painted substrates, cold rolled steel, phosphatized steel, and steel coated with conventional primers by electrodeposition. The present composition exhibits excellent adhesion to primers, for example, those that comprise crosslinked epoxy polyester and various epoxy resins, as well as alkyd resin repair primers. The present compositon can be used to coat plastic substrates such as polyester reinforced fiberglass, reaction injection-molded urethanes and partially crystalline polyamides.
When the present coating composition is used as a basecoat, typical pigments that can be added to the composition include the following: metallic oxides such as titanium dioxide, zinc oxide, iron oxides of various colors, carbon black, filler pigments such as talc, china clay, barytes, carbonates, silicates and a wide variety of organic colored pigments such as quinacridones, copper phthalocyanines, perylenes, azo pigments, indanthrone blues, carbazoles such as carbozole violet, isoindolinones, isoindolones, thioindigo reds, benzimidazolinones, metallic flake pigments such as aluminum flake and the like.
The pigments can be introduced into the coating composition by first forming a mill base or pigment dispersion with any of the aforementioned polymers used in the coating composition or with another compatable polymer or dispersant by conventional techniques, such as high speed mixing, sand grinding, ball milling, attritor grinding or two roll milling. The mill base is then blended with the other constituents used in the coating composition.
Conventional solvents and diluents are used to disperse and/or dilute the above mentioned polymers to obtain the present coating composition. Typical solvents and diluents include toluene, xylene, butyl acetate, acetone, methyl isobutyl ketone, methyl ethyl ketone, methanol, isopropanol, butanol, hexane, acetone, ethylene glycol, monoethyl ether, VM and P naptha, mineral spirits, heptane and other aliphatic, cycloaliphatic, aromatic hydrocarbons, esters, ethers and ketones and the like.
The coating composition can be applied by conventional techniques such as spraying, electrostatic spraying, dipping, brushing, flowcoating and the like. The preferred techniques are spraying and electrostatic spraying. After application, the composition is typically baked at 100.degree.-150.degree. C. for about 5-30 minutes to form a coating about 0.1-3.0 mils thick. When the composition is used as a clearcoat, it is applied over the colorcoat which may be dried to a tack-free state and cured or preferably flash dried for a short period before the clearcoat is applied. The colorcoat/clearcoat finish is then baked as mentioned above to provide a dried and cured finish.
It is customary to apply a clear topcoat over a basecoat by means of a "wet-on-wet" application, i.e., the topcoat is applied to the basecoat without curing or completely drying the basecoat. The coated substrate is then heated for a predetermined time period to allow simultaneous curing of the base and clear coats.
Upon curing of clear topcoat compositions of the present invention, a portion of the silane containing polymer may migrates and stratifies to the top of the clearcoat, particularly when the organosilane polymer is used in combination with a polyol, so as to produce a durable, weather-resistant clearcoat. Such stratification has been shown by electron scanning chemical analysis (ESCA) of a cross section of the cured layer of topcoat.
The coating composition can be formulated as a one-package system that has an extended shelf life.
The following examples illustrate the invention. All parts and percentages are on a weight basis unless otherwise indicated.
EXAMPLE 1
An organosilane polymer solution A is prepared by charging the following constituents into a polymerization reactor equipped with a heat source and a reflux condensor:
______________________________________ Parts by Weight______________________________________Portion I"Solvesso" 100 75.00Portion IIMethacryloxypropyltrimethoxy silane 300.00Styrene monomer 173.00Isobutyl methacrylate monomer 103.86"Solvesso" 100 45.02Portion III2,2-(2-methyl butane nitrile) 57.32"Solvesso" 100 85.80Total 840.00______________________________________
The "Solvesso" 100 is a conventional aromatic hydrocarbon solvent. Portion I is charged into the reactor and heated to its reflux temperature. Portion II, containing the monomers for the organosilane polymer, and Portion III, containing the polymerization initiator, are each premixed and then added simultaneously to the reactor while the reaction mixture is held at its reflux temperature. Portion II is added at a uniform rate over a 6 hour period and Portion II is added at a uniform rate over a 7 hour period. After Portion II is added, the reaction mixture is held at its reflux temperature for an additional hour. The resulting acrylosilane polymer solution is cooled at room temperature and filtered.
The resulting acrylosilane polymer solution has a polymer solids content of about 70%, the polymer has a weight average molecular weight of about 3,000, and has the following constituents: 30% styrene, 18% isobutyl methacrylate, and 52% methacryloxypropyl trimethoxysilane.
EXAMPLE 2
A hydroxy functional non-aqueous sterically stabilized dispersed polymer is prepared by charging the following components into a reactor:
______________________________________ Parts by Weight______________________________________Portion IIsopropanol 179.26Acrylic polymer solution 2254.05(52% solids of an acrylic polymerof 15% styrene, 28% butyl methacrylate,30% butyl acrylate, 10% hydroxy ethylacrylate, 2% acrylic acid and 15% ethylmethacrylate having a weight averagemolecular weight of 10,000 in a solventmixture of 82.2% xylene and 17.8% butanol)Mineral spirits 255.65Heptane 1912.46Portion IIHeptane 28.75t-Butyl peroctoate 4.68Portion IIIMethyl methacrylate monomer 1459.69Hydroxyethyl acrylate monomer 784.81Styrene monomer 156.97Portion IVAcrylic polymer solution 1126.52(53% solids of an acrylic polymerof 15% styrene, 28% butyl methacrylate,30% butyl acrylate, 10% hydroxy ethylacrylate, 2% acrylic acid and 15% ethylmethacrylate, 2.7% glycidyl methacrylatehaving a weight average molecular weightof 10,000 in a solvent mixture of 82.2%xylene and 17.8% butanol)Methyl methacrylate monomer 125.57Methyl acrylate monomer 565.06Glycidyl methacrylate monomer 47.05Heptane 17.25Portion VMineral Spirits 638.63t-Butyl peroctoate 47.14Isobutanol 127.31Portion VIt-Butyl peroctoate 30.96Isobutanol 255.65Portion VIIHeptane 167.25Total 10,184.71______________________________________
Portion I is charged into the reaction vessel and heated to its reflux temperature. Then Portion II is added to the reaction vessel mixed and held at reflux temperature for 2 minutes. Then Portions III and IV are added simultaneously with Portion V, over a 210 minute period, to the reaction vessel while maintaining the resulting reaction mixture at its reflux temperature. Then the mixture is held at its reflux temperature for an additional 45 minutes. Portion VI is added over a 90 minute period while maintaining the reaction mixture at its reflux temperature and then held at this temperature for an additional 90 minutes. Portion VII is added and excess solvent is stripped off to give a 60% solids dispersion.
The resulting polyester dispersed polymer has a core having a weight average molecular weight of about 100,000-200,000 and arms attached to the core having a weight average molecular weight of about 10,000-15,000.
EXAMPLE 3
An acrylic polyol resin solution is prepared by charging the following constituents into a polymerization reactor equipped with a heat source and a reflux condenser:
______________________________________ Parts by Weight______________________________________Portion In-Pentyl propionate 501.00Portion IIStyrene 360.00Isobutyl methacrylate 696.002-Ethylhexyl acrylate 480.00Hydroxypropyl acrylate 864.00n-Pentylpropionate 285.00Portion IIIt-Butyl peroctoate 60.00n-Pentyl propionate 60.00Total 3306.00______________________________________
Portion I is charged into the reactor and is heated to its reflux temperature of about (160.degree.-163.degree. C.). Portions II and III are each premixed and then added simultaneously to the reactor while the reaction mixture is held at its reflux temperature. Portion II is added at a uniform rate over a 6 hour period and Portion III is added at a uniform rate over a 7 hour period. After Portion III is added, the reaction mixture is held at its reflux temperature for an additional hour. The resulting acrylic polyol resin solution is cooled at room temperature and filtered.
The resulting acrylic polyol resin solution is 70% by weight of polymer solids. The polymer has a weight average molecular weight of about 6,000 and a hydroxyl number of about 150-160. It constitutes the following: 15% styrene, 29% isobutyl methacrylate, 20% 2-ethylhexyl methacrylate, and 36% hydroxypropyl acrylate.
EXAMPLE 4
A coating composition is prepared by blending together the following constituents:
______________________________________ Parts by Weight______________________________________Portion IXylene 163.002(3-hydroxy-3,5'-ditertamylphenyl 113.20amylphenyl) benzotriazoleHindered amine U.V. light stabilizer 147.80solution (40% solution in xylene of8-acetyl-3-dodecyl - 7, 7, 9, 9-tetramethyl-2, 3, 8-triazaspiro (4,5)-decane-2,4 dione)Baysilon Oil Solution 4.10(72.8 parts Baysilone Fluid OL and655.2 parts xylene)Portion IIMethylated/butylated melamine 2068.50formaldehyde resin (fully butylatedand methylated melamine formaldehyderesin having a butoxy/methoxy ratioof 1:1 and a degree of polymerizationof about 1-1.2)Acrylic polyol resin solution 4054.30Blocked sulfonic acid solution 236.40(33% solids in methanol of dodecyl benzenesulfonic acid blocked with dimethyloxazolidine, molar ratio of acid: dimethyloxazolidine is 1.52:1)Dispersed polymer (prepared above) 985.40Acrylosilane polymer solution A 3439.00(prepared above)Dibutyl tin dilaurate 65.00Portion IIIMethanol 203.80"Solvesso" 100 - hydrocarbon solvent 458.50Total 11,939.00______________________________________
The constituents of Portion I are added in the order shown to a mixing vessel and agitated until solution is complete. Portion II is added to the vessel and mixed for 30 minutes. Portion III is added and mixed for 30 minutes. The resulting clear coating composition has 70% solids content.
The resulting composition is sprayed onto primer coated phosphatized steel panels that were coated with a solvent base pigmented acrylic polymer basecoating composition. The composition is sprayed onto the panels before the basecoating is baked. The panels are baked at 120.degree. C. for 30 minutes and a clear coat about 2 mils thick is formed on each panel. The clear coating has a hardness of 8 knoops, a gloss measured at 20.degree. C. of 95. The coating has excellent outdoor weatherability and resistance to environmental attack, good mar and scratch resistance, good humidity resistance as determined by the Cleveland Humidity test and good chip resistance as determined by a gravelometer test.
EXAMPLE 5
An acrylosilane polymer solution B is prepared by first forming a silane containing macromonomer and then reacting the macromonomer with acrylic monomers.
The macromonomer is prepared by charging the following constituents into a reactor equipped as above:
______________________________________ Parts by Weight______________________________________Portion IY-9030 (isocyanatopropylmethoxy 750.0silane)Xylene 300.0Portion IIHydroxyethyl acrylate monomer 340.0Total 1390.0______________________________________
Portion I is heated to about 120.degree. C. and Portion II is slowly added over a 1 hour period with constant mixing. The reaction mixture is held at the above temperature for about 1 hour and the isocyanate level is checked by infrared analysis. When the isocyanate level reaches zero, the reaction is stopped and the resulting macromonomer solution is cooled to room temperature.
Acrylosilane polymer solution B is prepared by charging the following constituents into a reactor as equipped above:
______________________________________ Parts by Weight______________________________________Portion I"Solvesso" 100 430.0Portion IIMacromonomer solution (prepared above) 1826.0Styrene monomer 765.0Methyl methacrylate monomer 153.0Butyl methacrylate monomer 153.02-Ethylhexyl methacrylate monomer 153.0"Solvesso" 100 170.0Portion III2,2-(2 methyl butane nitrile) 100.0"Solvesso" 100 300.0Total 4050.0______________________________________
Portion I is charged into the reactor and heated to its reflux temperature. Portions II and III are premixed and slowly added to the reactor while maintaining the reaction mixture at its reflux temperature. Portion II is a added over a 6 hour period and Portion III is added over a 7 hour period. The reaction mixture is held at its reflux temperature for an additional hour and then cooled to room temperature.
The resulting acrylosilane polymer solution has a polymer solids content of about 66%. The polymer has a weight average molecular weight of about 6,000, and has the following constituents: 53% macromonomer, 29% styrene, 6% methyl methacrylate, 6% butyl methacrylate, and 6% 2-ethylhexyl methacrylate.
EXAMPLE 6
An acrylosilane polymer solution C is prepared by cobalt special chain transfer (SCT) by charging the following constituents into a heated reactor flask of five liter volume fitted with a water cooled condensor, stirred, 2 feed metering pumps and a thermometer:
______________________________________ Parts by Weight______________________________________Portion I"Solvesso" 100 120.00Ethylene Glycol Monobutyl Ether Acetate 120.00Xylene 150.00Portion IIgamma-methacryloxypropyltrimethoxy 39.67silaneStyrene 28.33Isobutyl methacrylate 45.33Co(DMG-BF.sub.2).sub.2 0.05VAZO 67 2.74Portion IIIgamma-methacryloxypropyltrimethoxy 847.83silaneStyrene 605.42Isobutyl methacrylate 968.67Portion IVVAZO 67 17.25"Solvesso" 100.00Ethylene glycol monobutyl ether acetate 100.00Xylene 100.00Portion Vt-Butyl Peroxyacetate 10.00Xylene 60.00______________________________________
Portion I, containing organic solvents, is charged into the reactor flask and heated under a nitrogen atmosphere to its reflux temperature. Portion II, containing the acrylosilane monomers and an initiator (a cobalt chelate of dimethylglycol and boron difluoride), is added to the refluxing solvent over a 10 minute period. After the 10 minute period, Portion III, containing additional monomers, and Portion IV, containing additional solvent, are each premixed and then added simultaneously to the reactor while the reaction mixture is held at its reflux temperature. Portion III is added at a uniform rate over a period of 360 minutes and Portion IV is added at a uniform rate over a period of 390 minutes. Then, Portion V, containing an initiator to kill the cobalt chain transfer, is fed over a 20 minute period. After Portion V is added, the reaction mixture is held at its reflux temperature for an additional 30 minutes. The resulting acrylosilane polymer solution is cooled at room temperature and filtered. The polymer has a weight average molecular weight of about 10,000-12,000 and constitutes 29% styrene, 30% isobutyl methacrylate and 41% methacryloxypropyltrimethoxy silane.
EXAMPLE 7
An acrylosilane polymer solution D is prepared by a group transfer process (GTP) as follows. To a four neck 3 liter flask, fitted with a stirrer, condenser, two feed pumps, thermometer and nitrogen inlet is added 950 g toluene, 136 g methyl methacrylate, 106 g butyl methacrylate, 118 g trimethoxysilylpropyl methacrylate and 46.2 g trimethoxysilylpropyl dimethyl ketene. The reaction mixture is cooled to 5.degree. C. and 4 ml of tetrabutyl ammonium m-chlorobenzoate catalyst is added over 90 minutes. The catalyst feed is temporarily interrupted during the reaction exotherm. When the exotherm subsides, the catalyst feed is resumed together with a monomer feed, over 40 minutes, of 220 g methyl methacrylate, 212 g butyl methacrylate and 237 g trimethoxysilylpropyl methacrylate. After completing all the addition, the reaction mixture is held for an additional half hour, after which 45 g methanol, for killing the ketene initiator, is added to the reaction mixture. The resulting polymer solution constitutes 35% methyl methacrylate, 31% butyl methacrylate, and 34% methacryloxypropyltrimethoxy silane.
EXAMPLE 8
The following components are used in preparing an acrylosilane solution polymer by free radical polymerization.
______________________________________ Parts by Weight______________________________________Portion I"Solvesso" 100 726.4 gPortion IIMethacryloxypropyltrimethoxy silane 1380.3 gStyrene 500. gMethyl methacrylate monomer 424.7 g2-Ethylhexyl acrylate 159.2 gButyl methacrylate monomer 159.2 gHydrocarbon ("Napoleum" 145A) 81.8 gPortion III"Lupersol" 70 70. gHydrocarbon ("Napoleum" 145A) 199.3 gPortion IVHydrocarbon ("Napoleum" 145A) 27.2 gPortion VHydrocarbon ("Napoleum" 145A) 9.1 g______________________________________
Portion I, containing organic solvent, is charged to the reaction flask and heated to reflux. Portion II, containing the monomers for the acrylosilane polymer, and Portion III, containing a t-butyl peroxyacetate initiator, are added simultaneously. Portion II is added over a 6 hour period, and Portion III is added over a 7 hour period. After Portion II is added, Portion IV is added immediately. After Portion III is added, Portion V is added immediately. Heating is continued at reflux for one additional hour after all the portions have been added. The reaction mixture is then cooled and filtered.
EXAMPLE 9
A dispersed (NAD) polymer A is prepared as follows. The macromonomer portion is prepared by a group transfer procedure.
Macromonomer A: To a four neck 3 liter flask, is fitted a stirrer, condenser, two feed pumps, thermometer and nitrogen inlet. To the flask is added 840 g of toluene, 100.3 g 2-ethylhexyl methacrylate, 75.4 g isobutyl methacrylate, 16.4 g hydroxyethyl methacrylate and 38.6 g trimethoxysilylpropyl dimethylketene. The reaction mixture is cooled to 5.degree. C. and the addition of 6.0 g tetrabutylammonium m-chlorobenzoate catalyst over 90 minutes is started. The catalyst feed is temporarily interrupted during the reaction exotherm. When the exotherm subsides, the catalyst feed is resumed together with a monomer feed over 40 minutes, comprising 202.1 g 2-ethylhexyl methacrylate, 136.7 g isobutyl methacrylate and 29.7 g hydroxyethyl methacrylate. A second monomer feed of 23.0 g allyl methacrylate is then added to the reactor. After completing all the additions, the reaction mixture is held for an additional 30 min., after which 3.0 g methanol is added to the reaction mixture.
Macromolecular Core: A reactor is charged with 248.3 g of macromonomer A above and 251.94 g heptane and heated to reflux under N.sub.2. At reflux is added 0.41 g tert-butylperoctoate, an initiator, followed with monomer and initiator feeds added over 210 minutes. The monomer feed is as follows: 20.6 heptane, 41.58 g stryrene, 54.25 g Methyl acrylate, 138.61 g methyl methacrylate, 13.86 g methacryloxypropyl trimethoxysilane, 27.12 g acrylonitrile, 133.7 g macromonomer A. The initiator feed is as follows: 48.38 g heptane and 4.16 g TBPO (tertiary butyl peroxide). The reaction is held at reflux for 45 minutes. A scavenger mix of 18.04 g heptane and 2.72 g TBPO is then added over 90 minutes. The reaction is held at reflux for 60 minutes and then distilled to 55% solids.
EXAMPLE 10
This example illustrates a dispersed or NAD Polymer B, in which the macromonomer is prepared by special chain transfer:
Macromonomer B: To a reactor is added 100.92 g butyl acrylate, 100.92 g isobutyl methacrylate, 600.62 g 2-ethylhexyl methacrylate, 110.24 g hydroxyethyl methacrylate and 611.94 g toluene. The mixture is heated to reflux under N.sub.2. At reflux is added a mixture of 178.43 g butyl acrylate, 178.45 g isobutylmethacrylate, 42.93 g toluene, 1.17 g VAZO 88 (a nitrile initiator) and 30 ppm Co(DMG-BF2)2 catalyst over 10 minutes. To the reactor is then fed a mixture of 190.61 g isobutylmethacrylate, 621.93 g 2-ethylhexyl methacrylate, 120.66 g methacryloxypropyl trimethoxysilane, 4.13 g VAZO 88 and 86.08 g toluene over a period of 240 minutes. This is followed with a scavenger feed of 108.01 g toluene and 2.01 g VAZO 88 for 60 minutes. The reaction is the held at reflux for 90 minutes. Finally, 251.21 g toluene is added.
Macromolecular Core: To a reactor is charged 142.4 g of macromonomer B as prepared above and 251.94 g heptane. This is heated to reflux under N.sub.2. At reflux is added 0.41 g tert-butylperoctoate, followed with monomer and initiator feeds added over 210 minutes. The monomer feed is as follows: 20.6 g heptane, 41.58 g styrene, 54.25 g methyl methacrylate, 138.61 g methyl acrylate, 13.86 g methacryloxypropyl trimethoxysilane, 27.12 g acrylonitrile, 76.68 g of macromonomer B. The initiator feed is as follows: 48.38 g heptane and 4.16 g TBPO. The reaction feed is held at reflux for 45 minutes and then a scavenger mix is started of 18.04 g heptane and 2.72 g TBPO over 90 minutes. The reaction mixture is held at reflux for 60 minutes and distilled to 55% solids.
EXAMPLE 11
This example illustrates a dispersed (NAD) Polymer C prepared by a free radical procedure:
Macromonomer C: To a reactor is added 195.91 g xylene which is heated to reflux under N.sub.2. At reflux is added a mixture of 213.0 g butylmethacrylate, 221.21 g butyl acrylate, 49.54 g hydroxyethyl acrylate, 11.6 g methyl methacrylate, and 6.0 g xylene over 240 mins. with the initiator feed. The initiator feed consists of 30.0 g xylene, 41.55 g butanol and 37.18 g TBPO and is fed to the reactor with monomer feed over 270 mins. To the reactor is added a mix of 0.02 g butyl catechol, 0.21 g isopropanol, 8.8 g glycidyl methacrylate and 3.0 g xylene. A mix of 0.12 g dimethylethylamine and 0.5 g xylene is added to the reactor, held for 90 mins. and cooled quickly to below 176.degree. F.
Macromolecular core C: To a reactor is charged 142.4 g macromonomer C prepared as above and 251.94 g heptane. The mixture is heated to reflux under N.sub.2. At reflux is added 0.41 g tert-butylperoctoate, followed with monomer and initiator feeds added over 210 minutes. The monomer feed consists of the following: 20.6 g heptane, 41.58 g styrene, 68.11 g methyl methacrylate, 138.61g methyl acrylate, 27.12 g acrylonitrile, and 76.68 g of macromonomer C as prepared above. The initiator feed consisted of the following: 48.38 g heptane and 4.16 g TBPO. The reaction is held at reflux for 45 minutes and then is added a scavenger mix of 18.04 g heptane and 2.72 g TBPO over 90 minutes. The reaction is held at reflux for 60 minutes and then distilled to 55% solids.
EXAMPLE 12
This example illustrates the preparation of a star polymer by a group transfer procedure (GTP).
Macromonomer 1: To a four neck 3 liter flask, fitted with a stirrer, condenser, two feed pumps, thermometer and nitrogen inlet is added 840 g toluene, 100.3 g 2-ethylhexyl methacrylate, 75.4 g isobutyl methacrylate, 16.4 g methacryloxypropyl trimethoxysilane and 38.6 g trimethoxysilylpropyl dimethylketene. The reaction mixture is cooled to 5.degree. C. and 6.0 g tetrabutylammonium m-chlorobenzoate catalyst over 90 minutes is added. This catalyst feed is temporarily interrupted during the reaction exotherm. When the exotherm subsides, the catalyst feed is resumed together with a monomer feed over 40 minutes, comprising 202.1 g 2-ethylhexyl methacrylate, 136.7 g isobutyl methacrylate and 29.7 g methacryloxypropyl trimethoxysilane. A second monomer feed of 23.0 g allyl methacrylate is then added to the reactor. After completing all the additions the reaction mixture is held for an additional 30 mins., after which 3.0 g methanol is added to the reaction mixture.
Star 1: To the reactor is charged 20.95 g 1,4-Butanediol diacrylate, 400.0 g macromonomer and 311.42 g xylene. At reflux is added a mix of 1.00 g tert-butyl peroctoate and 9.0 xylene, followed with monomer and initiator feeds added over 120 minutes. The monomer feed consists of the following: 30 g xylene and 41.89 g 1,4-butanediol diacrylate. The initiator feed consists of the following: 32.84 g xylene and 6.0 g TBPO. The reaction is held at reflux for 60 minutes.
EXAMPLE 13
This example illustrates another star polymer 2 in which the macromonomer is prepared by special chain transfer (SCT).
Macromonomer 2: To the reactor is added 100.92 g butyl acrylate, 100.92 g isobutyl methacrylate, 600.62 g 2-ethylhexyl methacrylate, 110.24 g methacryloxypropyl trimethoxysilane and 611.94 g toluene. The mixture is heated to reflux and then is added a mixture of 178.43 g butyl acrylate, 178.45 g isobutyl methacrylate, 42.93 g toluene, 1.17 g VAZO 88 and 30 ppm Co(DMG-BF2).sub.2 catalyst over a period of 10 minutes. Then is fed a mixture of 190.61 g isobutyl methacrylate, 621.93 g 2-ethylhexyl methacrylate, 120.66 g methacryloxypropyl trimethoxysilane, 4.13 g VAZO 88 and 86.08 g toluene to the reactor over a period for 240 minutes. This feed is followed by a scavenger feed of 108.01 g toluene and 2.01 g VAZO 88 for 60 minutes. The reaction is then held at reflux for 90 minutes. Finally, 251.21 g of toluene is added.
Star 2: To a reactor is charged 20.95 g 1,4-butanediol diacrylate, 400.0 g macromonomer 2 and 311.42 g xylene. At reflux is added a mix of 1.00 g tert-butyl peroctoate and 9.0 g xylene, followed with monomer and initiator feeds added over 120 minutes. The monomer feed consists of the following: 30 g xylene and 41.89 g 1,4-butanediol diacrylate. The initiator feed consists of the following: 32.84 g xylene and 6.0 g TBPO. The reaction is held at reflux for 60 minutes.
EXAMPLE 14
This example illustrates another star polymer in which the macromonomer is prepared by a free radical procedure.
Macromonomer 3: To a reactor is added 195.91 g xylene. The mixture is heated to reflux under N.sub.2. At reflux is added a mixture of 213.0 g butyl methacrylate, 221.21 g butyl acrylate, 49.54 g methacryloxypropyl trimethoxysilane, 11.6 g methacrylic acid, and 6.0 g xylene over 240 mins. with the initiator feed. The initiator feed consists of 30.0 g xylene, 41.55 g butanol and 37.18 g TBPO and is fed to the reactor with the monomer feed over 270 mins. Then to the reactor is added a mix of 0.02 g butyl catechol, 0.21 g isopropanol, 8.8 g glycidyl methacrylate and 3.0 g xylene, followed by a mix of 0.12 g dimethylethylamine and 0.5 g xylene. The reaction is held for 90 mins. and cooled quickly to below 176.degree. F.
Star 3: To the reactor is charged 20.95 g 1,4 butanediol diacrylate, 400.0 g macromonomer 3 prepared as above and 311.42 g xylene. Then the monomer and initiator feeds are added over 120 minutes. The monomer feed consists of 30 g xylene and 41.89 g 1,4 butanediol diacrylate. The initiator feed consists of 32.84 g xylene and 6.0 g TBPO. The reaction is held at reflux for 60 minutes.
EXAMPLE 15
This example illustrates a clearcoat composition according to the present invention. The following ingredients were added with mixing and a nitrogen blanket:
______________________________________Polymer B 320.00 gmNAD A 162.00 gmTin 1130 7.50 gmTin 440 (40% sol. in Xylene) 7.50 gm"Byk" 325 0.60 gmTrimethyl orthoformate 1.00 gm"Fascat" 4020 6.00 gm"Solvesso" 100 35.00 gm______________________________________
In the above list, tin 1130 and tin 440 are U.V. screeners, "Byk" 325 is a flow agent, trimethylorthoformate is a stabilizer to prevent gelling, "Fascat" 4020 is a disbutyl tin dilaurate curing catalyst, and "Solvesso" 100 is an aromatic solvent. The clearcoat composition is sprayed at a viscosity of 35" Fisher #2 cup. It is sprayed over clearcoat wet on wet at 1.8-2.0 mil thickness and baked 30 min. at 265.degree. F. The clearcoat typically exhibits an out of oven hardness of 3-4 Knoop, a gloss of 85-95 at 20.degree. and a DOI of 80-90. The clearcoat had excellent durability and crack resistance.
The above examples of dispersed polymers illustrate the preparation of dispersed polymers with hydroxy functionalities in the macromonomer arms attached to the core. Analogous dispersed polymers may be prepared analogously, with epoxide, anhydride, isocyanate, silane, or amine functionalities in the macromonomers, respectively, by the substitution, as will be appreciated by those skilled in the art, of the hydroxy-containing monomer in the above example, with a corresponding amount, respectively of an epoxide-containing monomer such as glycidyl methacrylate, an anhydride-containing monomer such as itaconic anhydride, an isocyanate containing monomer such as benzene, 1-(1-isocyanto-1-methylethyl)-3-(1-methylethenyl) a,a-Dimethyl meta-isopropenyl benzyl isocyanate ("TMI" metal vinyl isocyanate available from American Cyanamid in Wayne, N.J.), a silane-containing monomer such as gamma-methacryloxypropyltrimethoxy silane, or an amine-containing monomer such as methacrylamide.
Various modifications, alterations, additions, or substitutions of the components of the composition and process of this invention will be apparent to those skilled in the art without departing from the scope and spirit of this invention and it should be understood that this invention is not unduly limited to the illustrative embodiments set forth herein.

Number	Name	Date
4025474	Porter, Jr. et al.	May 1977
4055607	Sullivan et al.	Oct 1977
4075141	Porter, Jr. et al.	Feb 1978
4115472	Porter, Jr. et al.	Sep 1978
4147688	Makklouf et al.	Apr 1979
4180489	Andrew et al.	Dec 1979
4220679	Backhouse	Sep 1980
4242384	Andrew et al.	Dec 1980
4268547	Backhouse	May 1981
4290932	Wright et al.	Sep 1981
4415681	Howath	Nov 1983
4491650	Rizk et al.	Jan 1985
4499150	Dowbenko et al.	Feb 1985
4518726	Kato et al.	May 1985
4591533	Antonelli et al.	May 1986
4603064	Kania	Jul 1986
4810756	Spinelli	Mar 1989
4908397	Barsotti et al.	Mar 1990
4972027	Isozaki et al.	Nov 1990
5003004	Simms	Mar 1991
5010140	Antonelli et al.	Apr 1991
5063114	Nambu et al.	Nov 1991

Number	Date	Country
55-8028	Jul 1980	JPX
9100559	Dec 1991	JPX
2192399	Jan 1987	GBX

Coatings comprising an organosilane solution polymer and a crosslink functional dispersed polymer

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims